Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Synthesis and Verification of Biobased Terephthalic Acid from Furfural


Exploiting biomass as an alternative to petrochemicals for the production of commodity plastics is vitally important if we are to become a more sustainable society. Here, we report a synthetic route for the production of terephthalic acid (TPA), the monomer of the widely used thermoplastic polymer poly(ethylene terephthalate) (PET), from the biomass-derived starting material furfural. Biobased furfural was oxidised and dehydrated to give maleic anhydride, which was further reacted with biobased furan to give its Diels-Alder (DA) adduct. The dehydration of the DA adduct gave phthalic anhydride, which was converted via phthalic acid and dipotassium phthalate to TPA. The biobased carbon content of the TPA was measured by accelerator mass spectroscopy and the TPA was found to be made of 100% biobased carbon.


As social demand for renewable sources of commodity plastics has increased, biomass has attracted much attention as a promising alternative to petrochemicals1,2,3. The resources used to produce biobased plastics should be inedible, waste and abundant. Furfural is an ideal biomass resource, as it is traditionally produced from cellulosic and waste biomass such as corncob, corn stock and rice hull. Furthermore, it is extremely abundant, with a global output of 500,000–1,000,000 tonne/year4,5. The US Department of Energy (DOE) has stated that it is one of the most value-added chemicals derived from biomass6.

Another advantage of using furfural is that it can be readily converted to other useful chemicals due to its high reactivity7. Furfural is industrially converted to furan via decarboxylation and has been used as a source of bio-fuels7,8,9,10. In previous works, we have synthesised succinic acid and 1,4-butanediol from furfural and polymerised them to the biodegradable thermoplastic resin poly(butylene succinate)11,12,13. We have further used it to produce biobased acid anhydrides and polymerised them with diols to polyoxabicyclates, which are a potential alternative to commercially available transparent elastic polymers14.

In this work, we have focused on producing biobased poly(ethylene terephthalate) (PET). PET resin is a widely used commodity plastic with applications in fibre manufacture, packaging and electric devices. Coca-Cola Ltd. and other beverage companies have adopted biobased-PET since 2009 when they announced that their containers would change from petroleum-based PET to biobased PET1,15,16. However, this commercially available biobased PET is composed of bio-ethylene glycol derived from bio-ethanol and petroleum-based terephthalic acid (TPA) made from p-xylene produced by fractional distillation of naphtha. Consequently, its percentage biomass carbon content, as defined below, is a mere 20%.

The development of a route to biobased TPA would allow the synthesis of fully biobased PET, an extremely attractive prospect from both economic and environmental viewpoints. Consequently, many researchers have attempted to develop a viable method to produce biobased TPA and its precursors. p-Xylene, a precursor of TPA, has been obtained from two different biomass resources: glyceride, supplied as a by-product of commercially available chemicals such as bio-diesel; and 5-hydroxymethyl-2-furfural, derived from cellulosic waste17. The monoterpene p-cymene has been directly oxidised to TPA18 and ethylene, which can be produced from bio-ethanol, has been converted to p-xylene19. The conversion of biomass chemicals such as ethylene, isobutene, furan and dimethylfurfural to p-xylene using heterogeneous catalysts has also been investigated20,21,22,23,24. Furthermore, Toray industries Inc. launched the production of a fully biobased PET fibre with biobased TPA derived from isobutene in 201225,26.

In this work, we propose a viable synthetic route, shown in Figure 1, for the preparation of biobased TPA from furfural alone, which is produced industrially from inedible cellulosic biomass. In addition, we verified that the TPA obtained was indeed biobased, as determined by the measurement of the biobased carbon content. Biobased carbon content has been adopted as a criterion for biomass-sourced chemicals in several international standards such as ISO, ASTM and EN as it is the most practical and effective method for verifying that a material contains carbon derived from biomass27,28,29. It is determined by measuring the value of the 14C/12C ratio in the material and is based on the assumption that this ratio for petroleum-derived (or ‘ancient’) carbon is 0, while the ratio for biobased (or ‘modern’) carbon is 1 × 10−12. In our work, this ratio was measured using accelerator mass spectroscopy (AMS) according to guidelines listed in ISO 16620-2. The details of the measurement procedure have been previously reported in the literature28.

Figure 1
figure 1

Synthetic route to biobased TPA from biomass-derived furfural.

The furan used to produce the DA adduct is processed from the same biomass-derived furfural employed at the beginning of the route, making the product entirely biobased.

Results and Discussion

Oxidation of furfural to fumaric acid and maleic acid

The oxidisation of furfural with NaClO4 as an oxidant and V2O5 as a catalyst, gave a mixture of fumaric acid and maleic acid in 58% yield, lower than the 72% yield reported in the literature30. This lower yield could be caused by vigorous oxidation, which is difficult to control. The oxidation of furfural to maleic acid and fumaric acid has been performed by other means with improved yields and better selectivity for the products, either maleic acid or fumaric acid, elsewhere in the literature31,32. However, the oxidation with NaClO4 is, for our purposes, a more practical laboratory process, and, therefore, we adopted this traditional oxidation method in this study.

Dehydration of fumaric acid and maleic acid to maleic anhydride

The dehydration of the mixture of maleic acid and fumaric acid to maleic anhydride was performed using P2O5 as a dehydration agent. As the ratio of maleic acid and fumaric acid, determined by 1H NMR, was 1:7, the yield of maleic anhydride could potentially be less than 30%. However, once maleic acid was dehydrated to give maleic anhydride, phosphoric acid, produced by the reaction of P2O5 and water, could isomerise fumaric acid to maleic acid33. Consequently, the mixture of maleic acid and fumaric acid was quantitatively converted to maleic anhydride.

Diels-Alder (DA) reaction of anhydrous maleic acid and furan to the exo-DA adduct

The synthesis of furan from furfural could have been demonstrated in this study. However, commercially available furan is a biobased chemical and has been verified as such in previous work13. The biobased carbon contents of the furan and furfural used in this study are shown below. Therefore, although we have not performed the process ourselves, for the purposes of this work, commercially available furan is assumed to be biobased.

The DA reaction of maleic anhydride and furan readily gave the DA adduct. At the beginning of the reaction, the regioselectivity of DA cyclisation is for the endo-adduct due to its kinetic stability. However, the DA reaction is reversible and, after some time, the product is converted to the more thermally stable exo-DA adduct34,35,36. Consequently, the reaction was carried out for 12 h at room temperature, yielding the DA adduct in almost quantitative yield. Melting point analysis showed the m.p. of the product to be 127–129°C, corresponding to the exo adduct.

Dehydration of the exo-DA adduct to phthalic anhydride

The oxabicyclo moiety in the exo-DA adduct is readily dehydrated with an acid. We attempted to dehydrate the exo-DA adduct using sulfonic acid, phosphoric acid and P2O5, but the yield and purity of the phthalic anhydride produced were not high enough to isolate it. However, a more effective protocol for the dehydration of the exo-DA adduct has been recently developed in which it is treated with a mixture of trifluoromethane sulfonic acid and acetic anhydride37. We employed this new method and obtained phthalic anhydride in 84% yield.

Hydrolysis of phthalic anhydride to dipotassium phthalate

Phthalic acid was readily hydrolysed with aqueous potassium hydroxide to give dipotassium phthalate quantitatively.

Transfer reaction and acidification of dipotassium phthalate to TPA

Half a century ago, a transfer reaction known as the Henkel method, which converts dipotassium phthalate to dipotassium terephthalate at high temperature (above 400°C) with CdI2 as a catalyst, was the most common industrial process for the production of TPA38,39. The development of an alternative method involving the oxidation of p-xylene to TPA led to the Henkel method losing its competitive advantage and falling out of favour. Consequently, it is rarely used industrially. However, in this study, we adopted the Henkel method to convert biobased phthalate to biobased TPA, as we found it to be a practical method for obtaining biobased TPA from furfural. The reaction was carried out with CdI2 at 420°C and the resulting mixture was acidified to give biobased TPA. At 44%, the yield of TPA obtained in this study is not sufficient. However, this figure is obtained at the milligram scale, but the process was optimised industrially, so, therefore, it is reasonable to expect that the yield would increase for industrial production. Additionally, the Henkel method is proven as an industrial process, and, therefore, the commercial viability of this synthetic route from furfural to TPA is already established.

Biobased carbon content

The biobased carbon contents of the reagents and products are summarised in Table 1. The synthesis of fully biobased TPA is verified by the fact that the values of furfural, furan and TPA were almost 100%. Thus, we can conclude that both the starting materials and product are fully biobased chemicals.

Table 1 Biobased carbon content of biobased chemicals calculated from Δ 14C measured by accelerated mass spectrometry (AMS), in accordance with ISO 16620-2

On the other hand, the values for furfural and furan reported previously were 100.8 and 105.0%11,13 and slightly higher than those measured in this study. These values were obtained in 2010, while those in this study were obtained in 2014. Since the lot numbers of furfural and furan used in this study are different from those used in the previous study, the actual value of the 14C/12C ratio could be slightly different. This difference could be explained by the difference in the definition of biobased carbon content between ISO 16620-2 and ASTM D6866 and the manufacturing year of furfural and furan. In principle, the percentage of modern carbon (pMC) calculated from the 14C/12C concentration ratios, is the biobased carbon content. However, the pMC for biomass produced by fixation of CO2 in the atmosphere by photosynthesis was 108–110% in 200227,28,29. The pMC is possibly slightly higher than 100% because of the continuing but diminishing effects of nuclear testing in the atmosphere in the 1950s, during which large amounts of 14C were emitted into the atmosphere. Because the 14C in all the samples is referenced to a “prebomb” standard, i.e., modern carbon-based oxalic acid radiocarbon [Standard reference material (SRM) 4990c, National Institute of Standards, USA], all pMC values must be multiplied by a cofactor to correct for the bomb carbon and to obtain the true biobased carbon content of the sample. In our previous study, the biobased carbon contents were calculated using a strong cofactor of 0.93, that being the old value based on ASTM D6866 (2008) because the furfural and furan used were purchased before 2009. Nevertheless, the reason why the value of furan was above 105% is that it was produced before 2008. In this study, as the reagents used were purchased in 2013, the biobased carbon contents were calculated using the new value for the weak cofactor of 0.95 based on ISO 16620-2. These indicate that the nuclear testing effect on the old reagents was strong and the biobased carbon content was above 100%, even though the strong cofactor 0.93 was used, while the effect on the new reagents was weaker, giving a biobased carbon content of almost 100%. Therefore, the biobased carbon contents of furan and furfural in this study were slightly different from the values measured in the previous study.

The precise method for the measurement of biobased carbon content is detailed in ISO 16620-2 and ASTM D6866 and is an industrially indispensable verification procedure29,40. It is important, not just to prevent mistakes by researchers, but also to detect whether supposedly biobased materials have undergone some contamination from, or carbon exchange with, petrochemical sources such as other reaction reagents or non-biobased solvents. For example, in the case of the Henkel method, the transfer reaction could involve the incorporation of a carbonyl carbon from carbon dioxide, produced as a by-product of a petrochemical process38,41. In addition, biobased carbon content measurement is also an invaluable method for identifying materials mistakenly or falsely supplied as biobased. Therefore, we propose that the measurement of biobased carbon content should be necessary when biobased chemicals are used, especially when the products can be synthesised from commercially available petroleum-derived starting materials or involve the use of non-biobased reagents or solvents.

In summary

We successfully synthesised biobased TPA from furfural and furan using viable and proven organic synthetic procedures. Furthermore, the biobased carbon content of the TPA that we synthesised confirmed that it is a truly biobased product. Using furfural as a single resource is a novel and interesting concept, since furfural can be produced from inedible cellulosic biomass.

The aim of this study was to propose a viable synthetic route from furfural alone to TPA and we have succeeded in this. It is our hope that more research, conducted by both ourselves and, perhaps, other groups, will optimise this process so that it may be industrialised.

We finally propose that the measurement of biobased carbon content is indispensable as a verification method in the research area of biobased synthesis.



Furan, sodium chlorate, vanadium pentoxide, phosphorus pentoxide, methane sulfonic acid, acetic anhydride, cadmium iodide, toluene and diethyl ether were purchased from Wako Pure Chemical Industries (Osaka, Japan). Furfural, potassium hydroxide and hydrochloric acid were purchased from Kanto Kagaku Co., Inc (Tokyo, Japan). Phosphorus pentoxide was purchased from Kishida Chemical Co., Ltd (Osaka, Japan). Furfural, trifluoromethane sulfonic acid and acetic anhydride were used after distillation under reduced pressure. All other chemicals were of reagent grade and used without further purification.


1H NMR spectra were recorded on a 400 MHz NMR spectrometer (JNM-ECX400; JEOL, Tokyo, Japan) using deuterated chloroform or deuterated dimethyl sulfoxide as a solvent and tetramethylsilane as an internal standard.

Measurement of biobased carbon content28

Measurements of the ratios of the three carbon isotopes (14C, 13C and 12C) using AMS were performed at the Institute of Accelerator Analysis Ltd (IAA) (Fukushima, Japan) using a 3-MV tandem accelerator (National Electrostatics Co., Middleton, WI, USA, Pelletron 9SDH-2). The pMC was calculated from the 14C/12C concentration ratios for the sample. The biobased carbon content was determined from the ratio of 14C/12C concentrations of the sample according to ISO 16620-2. Δ 14C is the isotope differential ratio of 14C between the sample and reference material. Reference materials were also analysed using AMS. The biobased carbon content was calculated as follows:

Oxidation of furfural to fumaric acid and maleic acid30

Furfural (36 g, 367 mmol) was carefully added dropwise to a solution of sodium chlorate (80 g, 751 mmol) and vanadium pentoxide (360 mg, 1.98 mmol) in water (10 mL) at 90°C over 3 h and the mixture was stirred at 80°C for a further 10 h. The mixture was allowed to stand at room temperature for 11 h, affording a white crystalline precipitate. The precipitate was filtered and dried to give 42.3 g (58%) of a mixture of fumaric acid and maleic acid as white crystals. 1H NMR (400 MHz, DMSO-d6) δ 6.61 (2H, s, –CH = of fumaric acid), 6.01 (2H, s, –CH = of maleic acid) ppm.

Dehydration of fumaric acid and maleic acid to maleic anhydride42

The mixture of fumaric acid and maleic acid prepared above (3.00 g, 25.8 mmol) was mixed with diphosphorus pentoxide (5.00 g, 35.2 mmol) using a pestle and mortar. The resulting mixture was added to a sublimation apparatus and sublimated at 140°C and 0.4 kPa for 3 h. The resulting sublimate was collected to give 2.41 g (95%) of maleic anhydride as white crystals. 1H NMR (400 MHz, CDCl3) δ 7.46 (2H, s) ppm.

Diels–Alder (DA) reaction of anhydrous maleic acid and furan to exo-DA adduct34

Maleic anhydride (4.65 g, 47.4 mmol) was dissolved in diethyl ether (50 mL). Furan (18 mL, 278 mmol) was added and the reaction mixture was allowed to stir at room temperature for 12 h. The resulting precipitate was collected by filtration to give 7.77 g (98%) of white crystals. The melting point of white crystals was 127–129°C. This indicates that the white crystals obtained is exo-DA adduct. 1H NMR (400 MHz, DMSO-d6) δ 6.58 (2H, s), 5.46 (2H, s), 3.18 (2H, s) ppm.

Dehydration of exo-DA adduct to phthalic anhydride37

The exo-DA adduct (1.00 g, 6.02 mmol) was added to a mixture of methane sulfonic acid (10.0 mL, 154 mmol) and acetic anhydride (2.0 mL, 21 mmol) under a N2 atmosphere at 0°C. The reaction mixture was allowed to warm to room temperature and stirred for 2 h. It was then heated to 80°C and stirred for 4 h. After cooling to room temperature, the reaction mixture was extracted with toluene (3 × 20 mL). The combined toluene extract was washed with saturated sodium hydrogen carbonate solution and saturated sodium chloride solution before being dried over anhydrous sodium sulfonate. After filtration, the organic layer was evaporated in vacuo to give 746 mg (84%) of phthalic anhydride as white crystals. 1H NMR (400 MHz, CDCl3) δ 8.08–7.95 (2H, m), 7.65–7.52 (2H, m) ppm.

Hydrolysis to phthalic anhydride to dipotassium phthalate43

Phthalic anhydride (500 mg, 3.38 mmol) was dispersed in a solution of potassium hydroxide (1.00 g, 17.8 mmol) in water (10 mL). The reaction mixture was allowed to stir at 80°C for 2 h. The resulting solution was poured into ethanol (150 mL) affording a white precipitate which was filtered to give 802 mg (98%) of dipotassium phthalate as white crystals. 1H NMR (400 MHz, D2O) δ 7.36–7.25 (4H, m, –CH = ) ppm.

Conversion and acidification of dipotassium phthalate to TPA43

A mixture of dipotassium phthalate (800 mg, 3.30 mmol) and cadmium iodide (40 mg, 0.11 mmol) was ground in a pestle and mortar. The mixture was placed in a sealing tube and sealed in vacuo. After heating to 420°C for 2 h, the resulting solid was placed into hot water (30 mL). The dispersion was refluxed for 10 min and the remaining precipitate was removed by filtration. The filtrate was acidified with 1 M HCl and the resulting solid was filtered off to give 242 mg (44%) of a white solid. 1H NMR (400 MHz, CDCl3) δ 8.03 (4H, s, –CH = ) ppm.


  • Mülhaupt, R. Green polymer chemistry and bio-based plastics: dreams and reality. Macromol. Chem. Phys. 214, 159–174 (2013).

    Article  Google Scholar 

  • Queiroz, A. U. B. & Collares-Queiroz, F. P. Innovation and industrial trends in bioplastics. Polym. Rev. 49, 65–78 (2009).

    CAS  Article  Google Scholar 

  • Chen, G.-Q. & Patel, M. K. Plastics derived from biological sources: present and future: a technical and environmental review. Chem. Rev. 112, 2082–2099 (2012).

    CAS  ADS  Article  Google Scholar 

  • Hong, J., Zhang, Y., Xu, X. & Li, X. Life cycle assessment of corn- and cassava-based ethylene production. Biomass and Bioenergy 67, 304–11 (2014).

    CAS  Article  Google Scholar 

  • Mao, L., Zhang, L., Gao, N. & Li, A. FeCl3 and acetic acid co-catalyzed hydrolysis of corncob for improving furfural production and lignin removal from residue. Bioresour. Technol. 123, 324–331 (2012).

    CAS  Article  Google Scholar 

  • Bozell, J. J. & Petersen, G. R. Technology development for the production of biobased products from biorefinery carbohydrates—the US Department of Energy's ‘Top 10’ revisited. Green Chem. 12, 539–554 (2010).

    CAS  Article  Google Scholar 

  • Cai, C. M., Zhang, T., Kumar, R. & Wyman, C. E. Integrated furfural production as a renewable fuel and chemical platform from lignocellulosic biomass. J. Chem. Technol. Biotechnol. 89, 2–10 (2014).

    CAS  Article  Google Scholar 

  • Brownlee, H. J. & Miner, C. S. Industrial development of furfural. Ind. Eng. Chem. 40, 201–204 (1948).

    CAS  Article  Google Scholar 

  • Cass, O. W. Chemical intermediates from furfural. Ind. Eng. Chem. 40, 216–219 (1948).

    CAS  Article  Google Scholar 

  • Dutta, S., De, S., Saha, B. & Alam, M. I. Advances in conversion of hemicellulosic biomass to furfural and upgrading to biofuels. Catal. Sci. Technol. 2, 2025 (2012).

    CAS  Article  Google Scholar 

  • Tachibana, Y., Masuda, T., Funabashi, M. & Kunioka, M. Chemical synthesis of fully biomass-based poly(butylene succinate) from inedible-biomass-based furfural and evaluation of its biomass carbon ratio. Biomacromolecules 11, 2760–2765 (2010).

    CAS  Article  Google Scholar 

  • Kunioka, M., Masuda, T., Tachibana, Y., Funabashi, M. & Oishi, A. Highly selective synthesis of biomass-based 1,4-butanediol monomer by alcoholysis of 1,4-diacetoxybutane derived from furan. Polym. Degrad. Stab. (2014) 10.1016/j.polymdegradstab.2014.05.011

  • Tachibana, Y., Masuda, T., Funabashi, M., Kasuya, K. & Kunioka, M. Synthesis of biomass-based monomers from biomass-based furfural for polyesters and evaluation of their biomass carbon ratios. In Biobased Monomers, Polymers and Materials, Smith, P. and Gross, R. Eds., ACS Symp. Ser., Press 1105, 91–110 (American Chemical Society 2012).

    CAS  Article  Google Scholar 

  • Tachibana, Y., Yamahata, M. & Kasuya, K. Synthesis and characterization of renewable polyester containing oxabicyclic dicarboxylate derived from furfural. Green Chem. 15, 1318–1325 (2013).

    CAS  Article  Google Scholar 

  • Johansson, C. et al. Renewable fibers and bio-based materials for packaging applications - a review of recent developments. BioResources 7, 2506–2552 (2012).

    Article  Google Scholar 

  • Miller, S. A. Sustainable polymers: opportunities for the next decade. ACS Macro Lett. 2, 550–554 (2013).

    CAS  Article  Google Scholar 

  • Shiramizu, M. & Toste, F. D. On the Diels-Alder approach to solely biomass-derived polyethylene terephthalate (PET): conversion of 2,5-dimethylfuran and acrolein into p-xylene. Chem. Eur. J. 17, 12452–12457 (2011).

    CAS  Article  Google Scholar 

  • Colonna, M. et al. Synthesis and radiocarbon evidence of terephthalate polyesters completely prepared from renewable resources. Green Chem. 13, 2543–2549 (2011).

    CAS  Article  Google Scholar 

  • Lyons, T. W., Guironnet, D., Findlater, M. & Brookhart, M. Synthesis of p-xylene from ethylene. J. Am. Chem. Soc. 134, 15708–15711 (2012).

    CAS  Article  Google Scholar 

  • Cheng, Y.-T., Wang, Z., Gilbert, C. J., Fan, W. & Huber, G. W. Production of p-xylene from biomass by catalytic fast pyrolysis using ZSM-5 catalysts with reduced pore openings. Angew. Chem. Int. Ed. Engl. 51, 11097–11100 (2012).

    CAS  Article  Google Scholar 

  • Williams, C. L. et al. Cycloaddition of biomass-derived furans for catalytic production of renewable p-xylene. ACS Catal. 2, 935–939 (2012).

    CAS  Article  Google Scholar 

  • Do, P. T. M., McAtee, J. R., Watson, D. A. & Lobo, R. F. Elucidation of Diels-Alder reaction network of 2,5-dimethylfuran and ethylene on HY zeolite catalyst. ACS Catal. 3, 41–46 (2013).

    CAS  Article  Google Scholar 

  • Lin, Z., Ierapetritou, M. & Nikolakis, V. Aromatics from lignocellulosic biomass: economic analysis of the production of p-xylene from 5-hydroxymethylfurfural. AIChE J. 59, 2079–2087 (2013).

    CAS  Article  Google Scholar 

  • Agirrezabal-Telleria, I., Gandarias, I. & Arias, P. L. Heterogeneous acid-catalysts for the production of furan-derived compounds (furfural and hydroxymethylfurfural) from renewable carbohydrates: a review. Catal. Today 234, 42–58 (2014).

    CAS  Article  Google Scholar 

  • Toray Industries, Inc (2012) Toray and Gevo Sign Bio-Paraxylene Offtake Agreement for the World's 1st Pilot-scale Fully Renewable, Bio-based Polyethylene Terephthalate (PET) Production. Available at Accessed October 7, 2014.

  • Yoshizawa, M. Toray's activities on bio-based polymers, Proceedings of Inno BioPlast 2013, Bangkok Thailand, 28 (2013).

  • Narayan, R. Biobased and biodegradable polymer materials: rationale, drivers and technology exemplars. In Degradable Polymers and Materials. Khemani. K. and Schols C Eds., ACS Symp. Ser., Press 939, 282–306 (American Chemical Society 2006).

  • Funabashi, M., Ninomiya, F., Kunioka, M. & Ohara, K. Biomass carbon ratio of biomass chemicals measured by accelerator mass spectrometry. Bull. Chem. Soc. Jpn. 82, 1538–1547 (2009).

    CAS  Article  Google Scholar 

  • Kunioka, M. et al. Biobased contents of natural rubber model compound and its separated constituents. Polymers (Basel). 6, 423–442 (2014).

    Article  Google Scholar 

  • Milas, N. A. Catalytic oxidations in aqueous solutions I. The oxidation of furfural. J. Am. Chem. Soc. 49, 2005–2011 (1927).

    CAS  Article  Google Scholar 

  • Guo, H. & Yin, G. Catalytic aerobic oxidation of renewable furfural with phosphomolybdic acid catalyst: an alternative route to maleic acid. J. Phys. Chem. C 115, 17516–17522 (2011).

    CAS  Article  Google Scholar 

  • Choudhary, H., Nishimura, S. & Ebitani, K. Highly efficient aqueous oxidation of furfural to succinic acid using reusable heterogeneous acid catalyst with hydrogen peroxide. Chem. Lett. 41, 409–411 (2012).

    CAS  Article  Google Scholar 

  • Terry, E. M. & Eichelberger, L. Catalytic transmutation of maleic acid into fumaric acid. J. Am. Chem. Soc. 47, 1402–1412 (1925).

    CAS  Article  Google Scholar 

  • Schmart, I. M. & Knot-Tso, M. E. Endo- vs. Exo-Selectivity in Diels-Alder reactions of maleic anhydride. J. Chem. Educ. 36, 81–82 (2004).

    Google Scholar 

  • Sauer, J. Diels-Alder reactions II: the reaction mechanism. Angew. Chemie Int. Ed. 6, 16–33 (1967).

    CAS  Article  Google Scholar 

  • Sauer, J. & Sustmann, R. Mechanistic aspects of Diels-Alder reactions: a critical survey. Angew. Chemie Int. Ed. 19, 779–807 (1980).

    Article  Google Scholar 

  • Mahmoud, E., Watson, D. A. & Lobo, R. F. Renewable production of phthalic anhydride from biomass-derived furan and maleic anhydride. Green Chem. 16, 167 (2014).

    CAS  Article  Google Scholar 

  • Raecke, B. Synthese von di- und tricarbonsäuren aromatischer ringsysteme durch verschiebung von carboxyl-gruppen. Angew. Chemie 70, 1–5 (1958).

    CAS  Article  Google Scholar 

  • Dozen, Y. Synthesis of aromatic dicarboxylic acids by Henkel and Cie process. J. Synth. Org. Chem. Japan 19, 570–581 (1961).

    CAS  Article  Google Scholar 

  • ISO 16620-2. Plastics -- biobased content -- part 2: determination of biobased carbon content. Available at: (Accessed: October 7, 2014)

  • Yoshiro, O. & Masaru Hojo, M. M. Further studies on the preparation of terephthalic acid from phthalic or benzoic acid. J. Org. Chem. 25, 2082–2087 (1960).

    Article  Google Scholar 

  • Nystrom, R. F., Loo, Y. H. & Leak, J. C. Synthesis of fumaric acid-2-C 14 and maleic anhydride-2-C 14 1. J. Am. Chem. Soc. 74, 3434–3435 (1952).

    CAS  Article  Google Scholar 

  • Raecke, B. & Schirp, H. 2,6-Naphthalenedicarboxylic acid. Org. Synth. 40, 71 (1960).

    CAS  Article  Google Scholar 

Download references


This work, under the project ‘Creation of essential technologies to utilise carbon dioxide as a resource through the enhancement of plant productivity and the exploitation of plant products,’ was supported by the Precursory Research for Embryonic Science and Technology (PRESTO) program of the Japan Science and Technology Agency (JST). We are thankful for valuable discussions with Masao Kunioka concerning biobased carbon content based on ISO 16620-2.

Author information

Authors and Affiliations



Y.T. and K.K designed this work and wrote the paper. Y.T. and S.K. carried out the synthetic experiments. All the authors participated in analysis and discussion of the results.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Tachibana, Y., Kimura, S. & Kasuya, Ki. Synthesis and Verification of Biobased Terephthalic Acid from Furfural. Sci Rep 5, 8249 (2015).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing