Abstract
In this work, the electronic properties of phosphorene nanoribbons with different width and edge configurations are studied by using density functional theory. It is found that the armchair phosphorene nanoribbons are semiconducting while the zigzag nanoribbons are metallic. The band gaps of armchair nanoribbons decrease monotonically with increasing ribbon width. By passivating the edge phosphorus atoms with hydrogen, the zigzag series also become semiconducting, while the armchair series exhibit a larger band gap than their pristine counterpart. The electronic transport properties of these phosphorene nanoribbons are then investigated using Boltzmann theory and relaxation time approximation. We find that all the semiconducting nanoribbons exhibit very large values of Seebeck coefficient and can be further enhanced by hydrogen passivation at the edge. Taking pristine armchair nanoribbons and hydrogenpassivated zigzag naoribbons with width N = 7, 8, 9 as examples, we calculate the lattice thermal conductivity with the help of phonon Boltzmann transport equation and evaluate the widthdependent thermoelectric performance. Due to significantly enhanced Seebeck coefficient and decreased thermal conductivity, we find that at least one type of phosphorene nanoribbons can be optimized to exhibit very high figure of merit (ZT values) at room temperature, which suggests their appealing thermoelectric applications.
Similar content being viewed by others
Introduction
Recently, the black phosphorous has become the focus of science community due to the synthesis^{1,2,3,4} of its twodimensional form, namely, the phosphorene. Preliminary but exciting results indicate that phosphorene has potential application in nanoelectronics and optoelectronics^{1,3,5}. As known, black phosphorus (BP) is the most stable phosphorus allotrope under normal condition and owns a direct band gap of about 0.3 eV^{6,7}, which can be easily turned into both ptype and ntype configuration. What's more, BP was found to have high carrier mobility in the order of 10^{5} cm^{2}/V/s at low temperature^{8,9}. Such superior electronic and transport properties suggest that BP may have potential thermoelectric applications. Indeed, recent theoretical work of Lv et al. showed that the power factor of BP can reach as high as 118.4 μWcm^{−1}K^{−2} by appropriate doping. However, due to relatively higher lattice thermal conductivity (12.1 W/mK), the maximum ZT value of BP can only reach 0.22 at room temperature^{10}. At the same time, Qin et al. investigated the strain effect on the thermoelectric properties of BP^{11}. They found that applying strain is a practical way to enhance the thermoelectric performance of BP and the largest ZT value of 0.87 can be achieved at 800 K with a tensile strain of 7%. Although these works suggest the possibility to use BP as a new kind of thermoelectric material, the ZT values obtained are very small and can not competitive with typical thermoelectric materials such as Bi_{2}Te_{3} and CoSb_{3}. Another efficient method to improve the thermoelectric performance is using lowdimensional structures. As theoretically predicated by Hicks and Dresselhaus^{12,13}, lowdimensional systems could have dramatically larger ZT values than the corresponding bulk materials because of decreased thermal conductivity caused by phonon boundary scattering and improved power factors on account of quantum confinement. Indeed, Fei et al. showed that the ZT value of twodimensional phosphorene (similar to graphene) is greater than 1.0 at room temperature and can reach 2.5 at 500 K^{14}, which can be traced to a large ration of electrical conductance to thermal conductance with orthogonally preferred conducting directions. Lv et al. demonstrated that strain induced band convergence in twodimensional phosphorene can significantly increase the Seebeck coefficient and electrical conductivity at the same time, which leads to a room temperature ZT value of about 2.1 in the armchair direction^{15}. If the dimension can be further reduced, say, considering the socalled phosphorene nanoribbons (in analogy with graphene nanoribbons), one may expect even better thermoelectric performance. It is thus of both fundamental and practical interests to discuss the thermoelectric properties of the onedimensional phosphorene nanoribbons.
In this work, we show by firstprinciples calculations that phosphorene nanoribbons (PNRs) with zigzag (ZPNRs) and armchair (APNRs) edges have distinct electronic properties, which can be further tuned by hydrogen passivation. Using the Boltzmann theory for both electrons and phonons, the transport coefficients of the PNRs are calculated. As a quick understanding of the thermoelectric performance of such kind of lowdimensional system, the ZT value of APNRs and Hpassivated ZPNRs with several typical width are evaluated. Our results indicate that the ZT values of APNRs can be optimized to as high as 6.4 at room temperature, which suggests that phosphorene nanoribbons could be very promising candidates for highperformance thermoelectric applications.
The PNRs can be obtained by cutting a monolayer phosphorene along armchair or zigzag directions. Following the conventional notation for graphene nanoribbon^{16}, the armchair phosphorene nanoribbons (APNRs) or zigzag phosphorene nanoribbons (ZPNRs) can be identified by the number of dimer lines or the zigzag chains across the ribbon width and are labeled as NAPNRs or NZPNRs, respectively. Figure 1(a) and 1(c) show the ballandstick model of NAPNRs and NZPNRs, respectively. Here we consider N = 7 ~ 12 for both armchair and zigzag nanoribbons and the width varies from about 10 Å to 26 Å. Upon structure relaxations, we see from Figure 1(b) and 1(d) there are some edge reconstructions for both APNRs and ZPNRs. Take N = 9 as an example, For the APNR, we find that the bond length between the edge atoms on the translation direction decreases from 2.26 Å to 2.06 Å. The corresponding bond angles at edge increase from 96.9° to 111.0° for α and from 103.7° to 119.5° for β. In the case of ZPNR, the bond length at the edge decreases from 2.23 Å to 2.14 Å and the corresponding edge angles γ and θ increase from 96.9° to 100.7° and from 103.7° to 108.9°, respectively. Similar edge reconstructions have been also found in previous calculations^{17}. It should be mentioned that the reconstructed motifs at the opposite edges are symmetrically arranged, which is different from those found in the BiSb nanoribbon^{18} with similar atomic configurations.
To investigate the relative stability of pristine phosphorene nanoribbons, we have computed the formation energy of both APNRs and ZPNRs. Here the formation energy E_{FE} is defined as:
where E_{PNR} is the calculated total energy of a given PNR, E_{P} is the energy per atom of a phosphorene sheet and n is the number of P atoms in the PNR. Figure 2(a) plots the formation energies of APNRs and ZPNRs as a function of the ribbon width. The small but positive formation energies indicate that the onedimensional phosphorene nanoribbons are energetically less favorable than the twodimensional phosphorene. Compared with the wellknown graphene nanoribbons^{19}, we find that both armchair and zigzag phosphorene nanoribbons have much smaller formation energies, suggesting that it is quite accessible to synthesize the PNRs experimentally. On the other hand, we see that the ZPNRs are energetically more favorable than the APNRs. The formation energies of both systems decrease monotonically with increasing ribbons width and converge to zero, indicating that the wider nanoribbon has relatively higher stability. To further confirm the stability of the phosphorene nanoribbons, we have performed abinitio molecular dynamics (MD). The starting temperature is 300 K and a microcanonical ensemble has been used. The MD runs for 2000 steps with a time step of 0.5 fs. Taking 7APNR and 7ZPNR as an example, we show in Figure 2(b) the nearest PP distance at the edge in the whole MD running time. We see there are only slight fluctuations around the PP bond length of 2.06 Å for 7APNR and 2.14 Å for 7ZPNR, which indicates that the phosphorene nanoribbons considered in our work are rather stable.
It is known that monolayer phosphorene is semiconducting with a direct band gap of 1.51 eV^{5}. By cutting the monolayer into nanoribbons, however, we find that the ZPNRs become metallic while APNRs remain semiconducting but exhibit an indirect band gap. As indicated in Figure 3, the band gaps of APNRs decrease with increasing ribbon width, which can be attributed to the wellknown quantum confinement effect^{20}. If the edge phosphorus atoms are passivated by hydrogen atoms, our calculated results indicate that the abovementioned edge reconstructions disappear and the band gaps of Hsaturated APNRs become direct. Moreover, there are obvious increases of the corresponding band gaps (Fig. 3). Such effect is more pronounced for the ZPNRs, where a transition from metal to indirect band gap semiconductor is observed and the Hpassivated ZPNRs exhibit the largest band gaps among the four kinds of phosphorene nanoribbons. Our results are consistent with previous works^{17,21} and further confirm the reliability of our calculations.
We next consider the electronic transport properties of these nanoribbons by using the semiclassical Boltzmann theory and rigidband approach^{22}. Within this method, the chemical potential μ indicates the doping level (or carrier concentration) of the system and the positive and negative μ correspond to ntype and ptype, respectively. The optimal carrier concentration can be obtained by integrating the density of states (DOS) of the system from the desired chemical potential to the Fermi level (μ = 0). The Seebeck coefficient S and the electrical conductivity σ are given by integration of the socalled transport distribution :
where f_{0} is the equilibrium Fermi function, k_{B} is the Boltzmann's constant and μ is the chemical potential. and is the group velocity and relaxation time at state , respectively.
Figure 4(a) and 4(b) show the calculated Seebeck coefficients S for the APNRs and Hpassivated APNRs as a function of chemical potential at room temperature, respectively. We see that by optimizing the carrier concentration, the phosphorene nanoribbons can exhibit very large value of Seebeck coefficients. As the definition of crosssectional area has some arbitrariness for lowdimensional systems such as our phosphorene nanoribbons, in the following we will calculate the carrier concentration with respect to the interlayer distance of bulk phosphorus (3.07 Å) and the real ribbon width. For example, the pristine 7APNR has a maximum Seebeck coefficient of 1.36 mV/K at μ = 0.056 eV. Upon edge passivation, the maximum Seebeck coefficient can further enhanced 1.75 mV/K, which is significantly higher than most of previous results^{23,24,25,26}. As all the investigated ZPNRs in their pristine form are metallic, we see from Figure 4(c) that their Seebeck coefficients are very small around the Fermi level. However, we observe a much higher Seebeck coefficient for the Hpassivated ZPNRs (Figure 4(d)), which can be optimized to 2.6 mV/K for the ZPNRs with width of N = 7. Such giant Seebeck coefficients of phosphorene nanoribbons are very beneficial for their thermoelectric applications and we will come back to this point later. On the other hand, we find from Figure 4 that the Seebeck coefficients of three kinds of semiconducting nanoribbons exhibit obvious edge dependence, which is the largest for the Hpassivated ZPNRs, the smallest for the pristine APNRs, with Hpassivated APNRs in between. Such an order of Seebeck coefficients is a consequence of their distinct energy gaps. As shown in Figure 5, the Seebeck coefficient at the peak shows linear dependence with the band gap and has no trend towards to saturation. This implies that the structures which have larger band gaps would have higher Seebeck coefficients. Similar relation has also been found in the graphene/hBN superlattice nanoribbons^{27}.
Within the semiclassical Boltzmann theory, the electrical conductivity σ can only be calculated with the relaxation time τ inserted as a parameter. This means that what we actually obtained is σ/τ. To figure out the electronic relaxation time of phosphorene nanoribbons, we apply the deformation potential (DP) theory proposed by Bardeen and Shockley^{28}, where the relaxation time τ of 1D system at temperature T can be expressed as:
In this formula, m* and μ_{c} are the effective mass and carrier mobility along the transport direction, respectively. The deformation potential constant E_{1} = ΔE/(Δl/l) is determined by changing the lattice constant l along the transport direction. The elastic modular can be obtained by C = [∂^{2}E/∂δ^{2}]/l, where E is the total energy of the system, δ is the applied uniaxial strain along the ribbon direction.
As the Hpassivated zigzag ribbon has the largest Seebeck coefficient while it is the smallest for the pristine armchair ribbon, for simplicity, in the following we take the APNRs and Hpassivated ZPNRs with width N = 7, 8, 9 as examples to discuss the thermoelectric performance of phosphorene nanoribbons. Table I lists the calculated room temperature carrier mobility μ_{c}, the relaxation time (τ) and all the related parameters indicated in Eq. (4) for the pristine armchair and Hpassivated zigzag ribbons. Note that the calculated mobility for the electron can reach as high as 740 cm^{2}/V/s at room temperature, which is higher than the experiment values of twodimensional phosphorene FET^{1,2} and monolayer MoS_{2}^{29}. The relaxation time for electron is higher than that for hole in APNRs, but it is just reversed for the Hpassivated ZPNRs.
Figure 6 (a) shows the calculated electrical conductivity σ of 7, 8, 9APNR as a function of chemical potential μ at 300 K. We see that σ of ntype is usually larger than that of ptype, especially for the 9APNR which has a much larger electron relaxation time. For both 7APNR and 8APNR, we see that σ increases gradually with increasing absolute μ. However, the electrical conductivity is very small at the chemical potential where the Seebeck coefficient approach its peak value (See Fig. 4(a)). This implies that there should be a certain compromise between the Seebeck coefficient and the electrical conductivity. Indeed, we see from the Figure 6(b) that the maximum power factor (denoted by S^{2}σ) appears at a particular chemical potential where neither the Seebeck coefficient nor the electrical conductivity reach the maximum. Among the investigated 7, 8, 9APNR, we find that the 9APNR exhibit the smallest Seebeck coefficient but the largest power factor (ntype), which results from its much larger electrical conductivity as discussed above. The calculated electronic thermal conductivity (κ_{e}) shown in Figure 6(c) has the same behavior as that of electrical conductivity since κ_{e} is calculated by the WiedemannFranz law^{30}
where the Lorentz number is set to 2.45 × 10^{−8} WΩK^{−2}^{31,32,33}.
To estimate the lattice thermal conductivity (κ_{p}) of phosphorene nanoribbons, the phonon Boltzmann transport equation for the phonons are adopted^{47,48,49}. The calculated lattice thermal conductivity of 7, 8, 9APNR and Hpassivated 7, 8, 9ZPNR are list in the Table II. We find that the lattice thermal conductivity of both series increase with the ribbon width, which is consistent with those found in graphene nanoribbons and silicene nanoribbons^{34,35}. In the case of APNRs, the lattice thermal conductivity are much smaller than that of bulk value (12.1 W/mK)^{36}, implying that pristine armchair phosphorene nanoribbons may have better thermoelectric performance than their bulk counterpart. The reduced lattice thermal conductivity can be attributed to the fact that phonons in the armchair nanoribbons are different from those in bulk phosphorus because the dispersion relations will be significantly modified due to confinements in two directions. The phononphonon interactions can be changed and boundary scattering is much stronger in nanoribbons than in bulk system. Compared with the electronic lattice thermal conductivity (see the inset of Fig. 6(c)), the lattice part of APNRs is relatively higher in a certain chemical potential range around the Fermi level. However, the electronic part becomes dominative and increases rapidly beyond this range.
With all the transport coefficients available to us, we can now evaluate the ZT value of phosphorene nanoribbons, which is given by:
Figure 6(d) shows the calculated ZT value of 7, 8, 9APNR as a function of chemical potential at room temperature. We see that ntype APNRs exhibit larger ZT value than the ptype systems, which is mainly caused by relatively larger electrical conductivity and Seebeck coefficient of the former. Moreover, the peak ZT values of ptype systems decrease with increasing ribbon width, but the behavior is reversed for the ntype systems. Among the investigated APNRs, the 7APNR shows the largest ptype ZT value of 2.3 at chemical potential μ = −0.36 eV, while the 9APNR exhibits the largest ntype ZT value of 6.4 with μ = 0.21 eV. Such ZT values significantly exceeds the performance of most laboratory results reported and are comparable to the efficiency of traditional energy conversion method, which makes armchair phosphorene nanoribbon a very promising candidate for thermoelectric applications. As summarized in Table II, the effectiveness of the phosphorene nanoribbon is mainly due to its very large Seebeck coefficient and much lower thermal conductivity (especially the lattice part) compared with the bulk phosphorous^{10}.
We next consider the Hpassivated ZPNRs which have the largest Seebeck coefficients among the four nanoribbon series (see Fig. 4). The calculated electronic conductivity σ of 7, 8, 9ZPNR as a function of chemical potential μ is shown in Figure 7(a). Compared with the APNRs, the obvious difference is that the ptype σ of Hpassivated ZPNRs is obviously larger than that of ntype, which also leads to much larger power factor S^{2}σ of the former (see Figure 7(b)). However, we see from Table II that Hpassivated ZPNRs have obviously larger lattice thermal conductivity compared with APNRs. Similar to those observed in graphene nanoribbons^{34} and silicene nanoribbons^{35}, such strong anisotropy of thermal conductivity is mainly caused by different phonon scattering rates at the zigzag and armchair edges^{37} and low frequency phonon bands of zigzag nanoribbons are in general more dispersive than those of the armchair nanoribbons^{38,39}. As a result, the optimized ZT values of Hpassivated ZPNRs are rather small, which is only 0.7 for the case of ptype and 0.1 for the ntype system.
In summary, we have demonstrated that at least one type of phosphorene nanoribbons (APNRs) could be optimized to exhibit very good thermoelectric performance with a ZT value as high as 6.4 at room temperature. Our theoretical calculations are selfconsistent within the framework of density functional theory and Boltzmann theory and there are no adjustable parameters. We want to mention that the phosphorous thin films and fewlayer or even monolayer phosphorene were recently fabricated by using mechanical exfoliation method^{1,2,3,4}. It is reasonable to expect that by cutting monolayer phosphorene or by patterning epitaxially grown phosphorene, one can obtain the phosphorene nanoribbons with controllable width and/or edge and thus realize their possible thermoelectric applications.
Methods
The electronic structure properties of PNRs are performed by using the firstprinciples planewave pseudopotential formulation^{40,41,42} as implemented in the Vienna abinitio Simulation Package (VASP)^{43}. The exchangecorrelation energy is in the form of PerdewBurkeErnzerhof (PBE)^{44} with generalized gradient approximation (GGA). The cutoff energy for the wave function is set to 400 eV. For the geometry optimization, a 1 × 1 × 15 MonkhorsePack kmeshes^{45} is adopted for the Brillouin zone integration. The atomic positions are fully relaxed until the force on all atoms become less than 0.05 eV/Å. A vacuum distance of 14 Å is used for the directions of both width and thicknesses, so that the nanoribbons can be treated as independent entities. Based on the calculated energy band structure, the electronic transport properties are determined by using the semiclassical Boltzmann theory within the relaxation time approximation^{46}. Such a method has been successfully used to predict some known thermoelectric materials and the theoretical calculations agree well with the experimental results^{23,24,25,26}. In order to obtain reliable transport coefficients, a denser MonkhorsePack kmesh up to 125 points in the irreducible Brillouin zone (IBZ) is used. To estimate the lattice thermal conductivity of PNRs, we use the phonon Boltzmann transport equation as implemented in the socalled ShengBTE code^{47,48,49}. For the calculations of the secondorder and thirdorder interatomic force constant matrix, we use a 1 × 1 × 6 and 1 × 1 × 3 supercell, respectively. The interactions up to the third nearest neighbors are considered when dealing with the anharmonic one. The qpoint grid and scale parameter for Gaussian smearing are set as 1 × 1 × 35 and 1.0, respectively.
Change history
10 July 2015
A correction has been published and is appended to both the HTML and PDF versions of this paper. The error has not been fixed in the paper.
References
Liu, H. et al. Phosphorene: An Unexplored 2D Semiconductor with a High Hole Mobility. ACS nano 8, 4033 (2014).
Koenig, S. P., Doganov, R. A., Schmidt, H., Neto, A. H. C. & Özyilmaz, B. Electric field effect in ultrathin black phosphorus. Appl. Phys. Lett. 104, 103106 (2014).
Li, L. et al. Black phosphorus fieldeffect transistors. Nature Nanotech. 9, 372 (2014).
Lu, W. L. et al. Plasmaassisted fabrication of monolayer phosphorene and its Raman characterization. Nano Res. 7, 853 (2014).
Qiao, J. S., Kong, X. H., Hu, Z. X., Yang, F. & Ji, W. Highmobility transport anisotropy and linear dichroism in fewlayer black phosphorus. Nature Commun. 5, 4475 (2014).
Keyes, R. W. The electrical properties of black phosphorus. Phys. Rev. 92, 580 (1953).
Warschauer, D. Electrical and optical properties of crystalline black phosphorus. J. Appl. Phys. 34, 1853 (1963).
Akahama, Y., Endo, S. & Narita, S.i. Electrical properties of black phosphorus single crystals. J. Phys. Soc. Jpn. 52, 2148 (1983).
Morita, A. Semiconducting Black Phosphorus. Appl. Phys. A: Mater. Sci. Process. 39, 227 (1986).
Lv, H. Y., Lu, W. J., Shao, D. F. & Sun, Y. P. Large thermoelectric power factors in black phosphorus and phosphorene. arXiv:1404.5171 (2014).
Qin, G. Z. et al. Strain enhanced anisotropic thermoelectric performance of Black Phosphorus. arXiv:1406.0261 (2014).
Hicks, L. D. & Dresselhaus, M. S. Effect of quantumwell structures on the thermoelectric figure of merit. Phys. Rev. B 47, 12727 (1993).
Hicks, L. D. & Dresselhaus, M. S. Thermoelectric figure of merit of a onedimensional conductor. Phys. Rev. B 47, 16631 (1993).
Fei, R. X. et al. Enhanced Thermoelectric Efficiency via Orthogonal Electrical and Thermal Conductances in Phosphorene. arXiv:1405.2836 (2014).
Lv, H. Y., Lu, W. J., Shao, D. F. & Sun, Y. P. Enhanced thermoelectric performance of phosphorene by straininduced band convergence. arXiv:1406.5272 (2014).
Son, Y. W., Cohen, M. L. & Louie, S. G. Energy Gaps in Graphene Nanoribbons. Phys. Rev. Lett. 97, 216803 (2006).
Peng, X. H., Wei, Q. & Copple, A. Edge effects on the electronic properties of phosphorene nanoribbons. arXiv:1404.5995 (2014).
Lv, H. Y. et al. The properties of BiSb nanoribbons from firstprinciples calculations. Nanoscale 4, 511 (2012).
Barone, V., Hod, O. & Scuseria, G. E. Electronic Structure and Stability of Semiconducting Graphene Nanoribbons. Nano Lett. 6, 2748 (2006).
Ploog, K. & Döhler, G. H. Compositional and doping superlattices in IIIV semiconductors. Adv. Phys. 32, 285 (1983).
Tran, V. & Yang, L. Scaling laws for the band gap and optical response of phosphorene nanoribbons. Phys. Rev. B 89, 245407 (2014).
Holland, M. G. Analysis of Lattice Thermal Conductivity. Phys. Rev. 132, 2461 (1963).
Singh, D. J. & Mazin, I. I. Calculated thermoelectric properties of Lafilled skutterudites. Phys. Rev. B 56, R1650 (1997).
Madsen, G. K. H., Schwarz, K., Blaha, P. & Singh, D. J. Electronic structure and transport in typeI and typeVIII clathrates containing strontium, barium and europium. Phys. Rev. B 68, 125212 (2003).
Singh, D. J. Dopingdependent thermopower of PbTe from Boltzmann transport calculations. Phys. Rev. B 81, 195217 (2010).
Parker, D. & Singh, D. J. Thermoelectric properties of AgGaTe2 and related chalcopyrite structure materials. Phys. Rev. B 85, 125209 (2012).
Yokomizo, Y. & Nakamura, J. Giant Seebeck coefficient of the graphene/hBN superlattices. Appl. Phys. Lett. 103, 113901 (2013).
Bardeen, J. & Shockley, W. Deformation Potentials and Mobilities in NonPolar Crystals. Phys. Rev. 80, 72 (1950).
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. SingleLayer MoS2 Transistors. Nature. Nanotech. 6, 147 (2011).
Bejan, A. & Allan, A. D. Heat Transfer Handbook (Wiley, New York, 2003), p. 1338.
Zhou, J. H., Jin, C. G., Seol, J. H., Li, X. G. & Shi, L. Thermoelectric properties of individual electrodeposited bismuth telluride nanowires. Appl. Phys. Lett. 87, 133109 (2005).
Chatterjee, K., Mitra, M., Kargupta, K., Ganguly, S. & Banerjee, D. Synthesis, characterization and enhanced thermoelectric performance of structurally ordered cablelike novel polyanilinebismuth telluride nanocomposite. Nanotechnology 24, 215703 (2013).
Sumithra, S. et al. Enhancement in Thermoelectric Figure of Merit in Nanostructured Bi2Te3 with Semimetal Nanoinclusions. Adv. Energy Mater. 1, 1141 (2011).
Zheng, H. et al. Enhanced thermoelectric performance of graphene nanoribbons. Appl. Phys. Lett. 100, 093104 (2012).
Pan, L. et al. Thermoelectric properties of armchair and zigzag silicene nanoribbons. Phys. Chem. Chem. Phys. 14, 13588 (2012).
Slack, G. Thermal Conductivity of Elements with Complex Lattices: B, P, S. Phys. Rev. 139, A507 (1965).
Hu, J. N., Ruan, X. L. & Chen, Y. P. Thermal Conductivity and Thermal Rectification in Graphene Nanoribbons: A Molecular Dynamics Study. Nano Lett. 7, 2730 (2009).
Xu, Y., Chen, X. B., Gu, B. L. & Duan, W. H. Intrinsic anisotropy of thermal conductance in graphene nanoribbon. Appl. Phys. Lett. 95, 233116 (2009).
Tan, Z. W., Wang, J. S. & Gan, C. K. FirstPrinciples Study of Heat Transport Properties of Graphene Nanoribbons. Nano Lett. 11, 214 (2011).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558 (1993).
Kresse, G. & Hafner, J. Ab initio moleculardynamics simulation of the liquidmetalamorphoussemiconductor transition in germanium. Phys. Rev. B 49, 14251 (1994).
Kresse, G. & Furthmüller, J. Efficiency of abinitio total energy calculations for metals and semiconductors using a planewave basis set. Comput. Mater. Sci. 6, 15 (1996).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio totalenergy calculations using a planewave basis set. Phys. Rev. B 54, 11169 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized Gradient Approximation Made Simple. Phys. Rev. Lett. 77, 3865 (1996).
Monkhorst, H. J. & Pack, J. D. Special points for Brilloninzone integrations. Phys. Rev. B 13, 5188 (1976).
Madsen, G. K. H. & Singh, D. J. BoltzTraP. A code for calculating bandstructure dependent quantities. Comput. Phys. Commun. 175, 67 (2006).
Li, W., Carrete, J., Katcho, N. A. & Mingo, N. ShengBTE: A solver of the Boltzmann transport equation for phonons. Comput. Phys. Commun. 185, 1747 (2014).
Li, W. et al. Thermal conductivity of diamond nanowires from first principles. Phys. Rev. B 85, 195436 (2012).
Li, W., Lindsay, L., Broido, D. A., Stewart, D. A. & Mingo, N. Thermal conductivity of bulk and nanowire Mg2SixSn1−x alloys from first principles. Phys. Rev. B 86, 174307 (2012).
Acknowledgements
We thank financial support from the National Natural Science Foundation (Grant No. 51172167 and J1210061) and the “973 Program” of China (Grant No. 2013CB632502).
Author information
Authors and Affiliations
Contributions
H.J.L. and J.S. conceived and initiated the study. J.Z. performed the calculations with helps from L.C., J.W., J.H.L. and D.D.F. J.Z. and H.J.L. analyzed the calculated results and wrote the manuscript. J.S., X.F.T. and Q.J.Z. discussed the related experimental work. All authors reviewed the paper.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons AttributionNonCommercialNoDerivs 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/byncnd/4.0/
About this article
Cite this article
Zhang, J., Liu, H., Cheng, L. et al. Phosphorene nanoribbon as a promising candidate for thermoelectric applications. Sci Rep 4, 6452 (2014). https://doi.org/10.1038/srep06452
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep06452
This article is cited by

Progress of microscopic thermoelectric effects studied by micro and nanothermometric techniques
Frontiers of Physics (2022)

Oxidationenhanced thermoelectric efficiency in a twodimensional phosphorene oxide
Scientific Reports (2021)

Flat epitaxial quasi1D phosphorene chains
Nature Communications (2021)

Thermoelectric Potential of OsAl2 Chimney LadderCompound: a Theoretical Investigation
Journal of Superconductivity and Novel Magnetism (2021)

Developments in stability and passivation strategies for black phosphorus
Nano Research (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.