Lithography provides the precision to pattern large arrays of metallic nanostructures with varying geometries, enabling systematic studies and discoveries of new phenomena in plasmonics. However, surface plasmon resonances experience more damping in lithographically–defined structures than in chemically–synthesized nanoparticles of comparable geometries. Grain boundaries, surface roughness, substrate effects and adhesion layers have been reported as causes of plasmon damping, but it is difficult to isolate these effects. Using monochromated electron energy–loss spectroscopy (EELS) and numerical analysis, we demonstrate an experimental technique that allows the study of these effects individually, to significantly reduce the plasmon damping in lithographically–defined structures. We introduce a method of encapsulated annealing that preserves the shape of polycrystalline gold nanostructures, while their grain-boundary density is reduced. We demonstrate enhanced Q–factors in lithographically–defined nanostructures, with intrinsic damping that matches the theoretical Drude damping limit.
Why do plasmonic structures have poorer performance when they are fabricated with top–down techniques compared to those fabricated with bottom–up approaches?
Surface plasmon resonances produce strong electric fields within sub–diffraction–limited volumes that can be applied in various nanophotonic devices. Using top–down lithographic approaches such as electron–beam lithography (EBL), these resonators can be patterned deterministically over large arrays with sub–10 nanometer dimensional control1,2,3. As a universal damping parameter for resonators, the quality–factor (Q–factor) has been extensively studied with different plasmonic nanostructures4,5. Unfortunately, in addition to damping due to the intrinsic properties of the material, extrinsic sources such as grain boundaries, surface roughness and adhesion layers6,7,8,9,10 also introduce damping and suppress Q–factors in lithographically–defined nanostructures. In contrast, wet–chemically–synthesized metal nanoparticles can be monocrystalline and atomically smooth11,12 and possess higher Q–factors. However, due to the challenges in precise placement of these particles, lithography provides an acceptable compromise for plasmonic device applications. To enhance Q–factors of lithographically–defined structures, thermal annealing7,13,14 and substituting metal adhesion layers with organic ligands9,15 have shown promise. However, more detailed studies are needed, e.g. to anneal–out grain boundaries without shape change and suppress Rayleigh instabilities that break up long and narrow nanostructures16,17. As high Q–factor plasmonic resonators are useful in practical applications such as surface–enhanced Raman scattering (SERS)18, color printing19 and light extraction from quantum emitters20, efforts to improve Q–factors are relevant.
In this work, we present a readily–applicable method21 that combines the design freedom of top–down lithography and the high Q–factors of chemically–synthesized nanoparticles, where the intrinsic damping is at the Drude limit7,11,22. By incorporating a thermally–stable but easily removable encapsulation layer, the EBL–defined nanostructures can be annealed to reduce grain boundaries without changing the geometry or surface roughness of the nanostructures. We applied this method to isolate and analyze the contributions of the various damping sources in plasmonic nanostructures. Ensemble–averaging effects were avoided in our analysis by studying single nanostructures with monochromated electron energy–loss spectroscopy (EELS) in a transmission electron microscopy (TEM)23,24,25,26,27,28. Interestingly, our results show that despite the incomplete removal of grain boundaries, annealed nanostructures have damping parameters close to those of monocrystalline nanoparticles, matching the Drude damping parameter of bulk metal. We also show the importance of a hitherto unexamined parameter, i.e. the contact area between the nanostructure and a dielectric substrate.
Figure 1 shows the process flow for reducing the grain boundary density of nanostructures. Au nanostructures with a thickness of 25 nm were fabricated directly onto 30 nm thick, free–standing Si3N4 TEM support membranes29,30. A 30 nm thick layer of hydrogen silsesquioxane (HSQ, XR–1541 2% solids) was then spin–coated onto the samples. Thermal annealing was performed in a Jipelek rapid thermal processor under nitrogen environment at 400°C for 10 minutes. After annealing, the HSQ encapsulation was removed by immersing the sample in a 2% vol. solution of hydrofluoric acid (HF) for 15 s. The shape and surface roughness of the nanostructures were preserved due to the encapsulation. In contrast, control samples without encapsulation experienced changes in shape, size and surface roughness16 as can be seen in Fig. S1 of the Supplementary Information (SI).
The nanostructures were fabricated onto Si3N4 membranes to enable the direct high–resolution imaging of the grain boundaries. Figure 2 shows TEM images of ring– and rod–shaped nanostructures with a 1 nm Cr adhesion layer, before and after annealing. The highly-polycrystalline nature of the gold nanostructures prior to annealing is seen in the TEM image of Fig. 2(a) with grain sizes of ∼10 nm. Grain boundaries are marked by dashed, yellow lines in the close–up panels. As shown in Fig. 2(b), the same region after annealing had fewer grain boundaries, likely due to grain–boundary migration and Ostwald ripening at elevated temperatures31. The average diameter of the grains increased to ∼20 nm, leading to a significant reduction of the total number of crystals, as evidenced by the reduced number of bright spots in the electron diffraction patterns (bottom panels, Fig. 2(a) and (b)).
Shape preservation was afforded by HSQ encapsulation and not by adhesion layer pinning. An example of a structure fabricated without Cr is shown in Fig. 2(c). The length of this nanorod was 454 nm before and 446 nm after annealing, a reduction in length of ∼2%. The edge profiles of the nanorod were still preserved by the encapsulation, confirming the minimal effect of the process on the shape and surface roughness of the nanostructures.
EELS measurements were done on the same structures both before and after they were annealed; the experimental procedures are described in the SI. EELS results for the nanorod of Fig. 2(c) are presented in Fig. 3(a). Up to four peaks corresponding to different resonant harmonic modes are evident and their corresponding plasmon maps are shown beneath the respective peaks. The effects of annealing are evident in the enhanced intensity and narrowed full–width at half maximum (FWHM) of the resonant peaks. Q–factors were extracted from the spectra by using a previously-described method32. The blue shift of the plasmon peaks observed in Fig. 3(a) after annealing is likely caused by a combination of factors, including the reduction of the rod length during annealing and possibly the thinning of the substrate during etching, as is shown in more detail in Fig. S3 in the SI.
Numerical calculations using FDTD were performed to extract the Q–factors and field distributions of the nanostructures, as described in the Methods section. The relative permittivity for bulk Au was described using the Drude–Lorentz model7, expressed as follows:
Here ωp is the plasma frequency, Γp is the damping parameter for the Drude term, ωm and Γm are the resonant frequency and the damping parameter of the mth Lorentz oscillator, respectively. The increase in damping due to factors such as grain boundaries and impurities is accounted for by an increase in the Drude damping parameter. Following the work of Liu et al.10, a damping factor α was introduced to quantify this increase relative to bulk Au, where α = 1 is defined to be at the Drude limit. By fitting experimental permittivity data33 with two Lorentzian terms, we obtained the following parameters: ωp = 9 eV, α = 1, Γp = 0.07 eV, f1 = 0.3, ω1 = 2.7 eV, Γ1 = 0.3 eV, f2 = 0.8, ω2 = 3.05 eV and Γ2 = 0.5 eV, as shown in Fig. S2 in the SI. Figure 3(b) shows spectra for the fundamental mode of a 100 nm long gold rod with α = 1, 1.3 and 1.8. Q–factors were extracted from fitted Lorentzian functions to the simulated spectra4.
Experimental Q–factors extracted from three sets of gold nanostructures are shown in Fig. 3(c) as a function of resonance energy. To verify the effects of the adhesion layer and grain boundaries on the damping process, we compared these experimental results with simulated Q–factors of nanostructures with lengths from 40 to 275 nm and square cross sections 25 nm wide. Structures with Cr adhesion have the lowest Q–factors and could be fitted with a damping factor of α = 1.8. Without Cr, Q–factors immediately improved by ∼25%. Notably, samples with Cr adhesion did not show a significant increase in Q–factor (<10%) after annealing, though it was evident that they experienced a reduction in grain boundary densities, as seen in Fig. 2. It is likely that Cr diffuses into the gold during annealing, to form Cr–rich crystallites34, creating new scattering sites that compensate the reduction in damping from grain boundaries. Conversely, the samples without Cr exhibited an improvement in Q–factor by as much as ∼40% after annealing (Fig. 3(c) inset). The as–fabricated structures without Cr could be fitted with α = 1.3, which reduced to α = 1 after annealing.
Annealing strongly enhances the Q–factors for plasmons with resonance energies below ∼1.7 eV. This effect can be understood from the relatively low–frequency Drude damping parameter in Au, Γp ∼ 0.1 eV. Therefore, only resonances that occur at low frequencies are most strongly affected by a modification to this parameter. Consistently, Fig. S2 in the SI illustrates that the damping factor affects only the imaginary part of the permittivity at energies below ∼1.7 eV. The decrease in Q–factors >1.7 eV is due to damping from interband transitions in Au4.
Figure 4(a) shows that the wet–chemically synthesized nanorods have comparable but systematically higher Q–factors than the annealed, EBL–patterned nanostructures. We identified two main reasons for this observation: (1) smaller physical cross sections and volumes of the rounded single–crystal nanorods11,35,36 and (2) the smaller contact area of these nanorods with the substrate. The widths of the measured wet–chemically synthesized nanorods were in the range of 17 to 32 nm while the EBL patterned nanostructures were systematically wider, ranging from 23 to 32 nm. To enhance mutual comparison, the simulations used 25 nm as the lateral widths for all the simulated structures. As shown in Fig. 4(a), numerical simulations using α = 1 for structures with a pentagonal cross section (blue line) agree well with experimental data for the single–crystal nanorods. In reality, the cross sections of our wet–chemically synthesized particles are neither pentagonal nor perfectly circular37, but somewhere in–between, see for example Fig. S4 in the SI. As a result, their Q–factors would fall between the blue and black solid lines in Fig. 4(b), the latter of which simulates nanostructures with rounded corners.
The normalized E–field magnitude distributions of gold nanostructures with two different lengths for points I–IV are simulated in the panels on the right of Fig. 4. For resonances around 1 eV (panels I, II), the field distributions are comparable for both the square and pentagonal cross sections. At these low energies, radiative damping dominates. As a consequence, their relatively smaller volume leads to a somewhat higher Q–factor for pentagonal nanorods32. This effect is confirmed in Fig. 4(b), where at low energies, structures with smaller cross–sectional areas (i.e. smaller volumes) have higher Q–factors. Conversely, for high–energy resonances around 2.1 eV (panels III, IV), absorptive damping dominates and the stronger field localization at the metal–substrate interface dictates that structures with the smallest contact areas have the highest Q–factors, as seen in Fig. 4(b).
The effect of the substrate is further studied by comparing Q–factors for structures with and without substrates, also plotted in Fig. 4(b). For a given cross section, the presence of a substrate improves the Q–factor at low energies, but strongly reduces the Q–factor at high energies. The different effects of the substrate arise again from the interplay between radiative and absorptive damping. The presence of a substrate reduces radiative damping at low energies, by localizing fields at the metal-substrate interface and leads to an overall increase in Q–factor, see also Figures S5 and S6 in the SI. On the other hand, this substrate effect leads to a decrease in Q-factor at high energies due to the enhanced absorptive damping at the metal–substrate interface. The sensitive dependence on the metal–substrate contact area can also explain the scatter in the data of Fig. 4(a) for single–crystal nanorods: Some of these rods are likely to contact the substrate only at localized points, unlike the conformal contact in lithographically–defined structures.
It is worth pointing out that even though grain boundaries remain after annealing, the damping factors of the annealed structures still match those of single–crystal nanorods. We predict that the effect still of grain boundaries on damping strongly depends on their orientation, their position along the particle length with respect to the plasmon resonance nodes and whether low– or high–angle grain boundaries are present38. The crystallographic defect density can vary greatly between different types of grain boundaries. For an isotropic material such as gold, defect–free twin boundaries potentially introduce less damping than high–angle grain boundaries (having grain misorientations >10°) loaded with crystallographic defects that act as scattering centers for electrons31. We therefore hypothesize that the large plasmon damping in as–deposited samples is predominantly due to the presence of high–angle grain boundaries. As grain-boundary mobility increases with the degree of misorientation, these high–angle grain boundaries are also most easily removed by annealing. Our results suggest that the boundaries that remain are predominantly low–angled ones that have little effect on plasmon damping. The annealed structures, while polycrystalline, are therefore optically indistinguishable from a single crystal. Finally, over the entire energy range that was investigated, surface roughness of the nanostructures was found to have very little effect on the Q–factor4,7, as can be seen in Fig. S7 in the SI.
In answer to our introductory question, we demonstrated that lithographically–defined nanostructures experience more plasmon damping than wet–chemically synthesized metal nanoparticles due to the combined effect of grain boundaries, the larger metal–substrate interface and metal adhesion layers. We presented a facile process to improve the Q–factors of nanostructures that are fabricated using top–down lithography. Encapsulation by HSQ, followed by annealing and HSQ removal resulted in polycrystalline gold nanostructures with Q–factors comparable to those of single–crystal nanorods. Both structures could be modelled using damping parameters of bulk gold. Our results provide design guidelines that indicate the dominant source(s) of damping for a given energy range and will enable the fabrication of high Q–factor plasmonic resonators and antennas. If left intact, the HSQ encapsulation could also prevent degradation of metal resonators operating at elevated temperatures, such as in near–field transducers for heat–assisted magnetic recording and photoelectron–emission cathodes.
EELS experiments were performed in scanning TEM (STEM) mode using an FEI Titan TEM with a Schottky electron source. The microscope was operated at 80 kV, using a STEM probe with a diameter around 1 nm. With a Wien–type monochromator, an energy resolution with typical FWHM values of 70 meV was obtained. Mapping and spectroscopy was done with a Gatan Tridiem ER EELS detector, applying a 7 mrad collection semiangle using STEM–based spectrum imaging and a modified binned gain averaging acquisition routine39. The EELS spectra in Fig. 3 were taken by summing all EELS spectra from the spectrum image in the first 5 nm off the surface of the whole nanostructure. The resulting summed EELS spectra are therefore representative of the nanostructure as a whole. The spectra were normalized at the ‘zero–loss peak’ maximum, making it possible to mutually compare the spectral intensity before and after annealing. The background signal was measured from a bare amorphous Si3N4 TEM support membrane, fitted to– and subtracted from the experimental EELS plasmon spectra. EELS maps show the loss signal integrated over an energy window of 0.1 eV energy around the plasmon peaks of interest. Q–factors were calculated from the first and—when possible—higher-order plasmon modes40 in the EELS spectra, as described in detail elsewhere32, by applying Olivero and Longbothum's accurate empirical approach41. Q–factors were extracted from the most prominent peaks for a given nanostructure, up to the third–order harmonic.
Synthesis of gold nanorods
Gold(III) chloride trihydrate (HAuCl4·3H2O, ≥99.9% trace metals basis), Sodium citrate dihydrate (≥99%), hexadecyltrimethylammonium bromide (CTAB, ≥99%, powder) and L–ascorbic acid (Biotra, ≥99.0%) were purchased from Sigma–Aldrich Singapore Pte Ltd. Ultra–pure deionized water (ELGA pure lab water systems) was used to prepare all aqueous solutions. The preparation of seeds ∼3.5 nm in diameter was done following the three–step seed–mediated method introduced by Jana et al42. A 20 ml of gold seeds aqueous solution containing HAuCl4·3H2O (2.5 × 10−4 M) and tri–sodium citrate (2.5 × 10−4 M) was prepared in a 22 ml glass vial. Then, 0.6 ml of an aqueous ice–cold NaBH4 (0.1 M) was added at once into the growth solution. The solution was allowed to stir for 2 hours before proceeding to the next step. A 30 ml of growth solution containing CTAB (0.1 M) and HAuCl4·3H2O (2.5 × 10−4 M) was prepared. This growth solution was distributed into three polypropylene tubes (labeled A, B and C) with 9 ml each. Next, 0.05 ml of ascorbic acid (0.1 M) was added into each tube followed by gentle inversion mixing. Then, 1.0 ml of the gold seeds solution was added into tube A. After 15 s, 1.0 ml from tube A was transferred into tube B. After another 15 s, 1.0 ml from tube B was transferred from tube B into tube C. Solution in tube C which contained gold nanorods, spheres and plates, was subjected to centrifugation for shape separation. Typically, 1.5 ml of the particle solution was centrifuged at 2000 rpm for 6 min repeatedly. The supernatant was poured off and the solid part containing nanorods and plates was re–dispersed in about 0.1 ml of deionized water, from which a droplet was dried on a Si3N4 TEM support membrane.
The commercial finite–difference time–domain (FDTD) code from LUMERICAL was used to simulate the damping parameters and field distributions. A plane wave with the electric field polarized along the long axis of the nanorod illuminates a nanorod at normal incident angle. Perfectly matched layer (PML) boundary conditions encompass one isolated nanorod. For samples fabricated by EBL, a square cross section, 25 nm wide, was set for all the relevant simulations regardless of annealing condition or adhesion layer, while for the wet–chemically synthesized particles, a 25 nm wide pentagonal cross section was applied. Electric field plots were normalized to their maxima. Q–factors were obtained by fitting the fundamental mode of the extinction spectra with a Lorentzian function, using nanorods with lengths varying from 40 to 275 nm. The relative permittivity for Si3N4 was set to be 4.
Im, H., Bantz, K. C., Lindquist, N. C., Haynes, C. L. & Oh, S.-H. Vertically oriented sub-10-nm plasmonic nanogap arrays. Nano Lett. 10, 2231–2236 (2010).
Duan, H., Hu, H., Kumar, K., Shen, Z. & Yang, J. K. W. Direct and reliable patterning of plasmonic nanostructures with sub-10-nm gaps. ACS Nano 5, 7593–7600 (2011).
Duan, H., Hu, H., Hui, H. K., Shen, Z. & Yang, J. K. W. Free-standing sub-10 nm nanostencils for the definition of gaps in plasmonic antennas. Nanotechnology 24, 185301 (2013).
Sönnichsen, C. et al. Drastic reduction of plasmon damping in gold nanorods. Phys. Rev. Lett. 88, 077402 (2002).
Zhang, L., Chan, C. Y., Li, J. & Ong, H. C. Rational design of high performance surface plasmon resonance sensors based on two-dimensional metallic hole arrays. Opt. Express 20, 12610–12621 (2012).
Nagpal, P., Lindquist, N. C., Oh, S.-H. & Norris, D. J. Ultrasmooth patterned metals for plasmonics and metamaterials. Science 325, 594–597 (2009).
Chen, K.-P., Drachev, V. P., Borneman, J. D., Kildishev, A. V. & Shalaev, V. M. Drude relaxation rate in grained gold nanoantennas. Nano Lett. 10, 916–922 (2010).
Sambles, J. R. Grain-boundary scattering and surface plasmon attenuation in noble metal films. Solid State Commun. 49, 343–345 (1984).
Habteyes, T. G. et al. Metallic adhesion layer induced plasmon damping and molecular linker as a nondamping alternative. ACS Nano 6, 5702–5709 (2012).
Liu, Z. et al. Plasmonic nanoantenna arrays for the visible. Metamaterials 2, 45–51 (2008).
Critchley, K. et al. Near-bulk conductivity of gold nanowires as nanoscale interconnects and the role of atomically smooth interface. Adv. Mater. 22, 2338–2342 (2010).
Huang, J.-S. et al. Atomically flat single-crystalline gold nanostructures for plasmonic nanocircuitry. Nat. Commun. 1, 150 (2010).
Jung, Y. S., Sun, Z., Kim, H. K. & Blachere, J. Blueshift of surface plasmon resonance spectra in anneal-treated silver nanoslit arrays. Appl. Phys. Lett. 87, 263116 (2005).
Tinguely, J.-C. et al. Gold nanoparticles for plasmonic biosensing: the role of metal crystallinity and nanoscale roughness. BioNanoSci. 1, 128–135 (2011).
Liu, H. et al. Enhanced surface plasmon resonance on a smooth silver film with a seed growth layer. ACS Nano 4, 3139–3146 (2010).
Karakouz, T. et al. Mechanism of morphology transformation during annealing of nanostructured gold films on glass. Phys. Chem. Chem. Phys. 15, 4656–4665 (2013).
Karim, S. et al. Influence of crystallinity on the Rayleigh instability of gold nanowires. J. Phys. D Appl. Phys. 40, 3767 (2007).
Nie, S. & Emory, S. R. Probing single molecules and single nanoparticles by surface-enhanced Raman scattering. Science 275, 1102–1106 (1997).
Kumar, K. et al. Printing colour at the optical diffraction limit. Nat. Nanotechnol. 7, 557–561 (2012).
Curto, A. G. et al. Unidirectional emission of a quantum dot coupled to a nanoantenna. Science 329, 930–933 (2010).
Yang, J. K. W., Bosman, M., Duan, H., Kumar, K. & Phang, I. Y. Process for creating lithographically-defined plasmonic structures with enhanced Q-factors. US Patent Application no. US 20130243947 A1. (2013).
Liu, N. et al. Plasmonic analogue of electromagnetically induced transparency at the Drude damping limit. Nat. Mater. 8, 758–762 (2009).
Bosman, M., Keast, V. J., Watanabe, M., Maaroof, A. I. & Cortie, M. B. Mapping surface plasmons at the nanometre scale with an electron beam. Nanotechnology 18, 165505 (2007).
Nelayah, J. et al. Direct imaging of surface plasmon resonances on single triangular silver nanoprisms at optical wavelength using low-loss EFTEM imaging. Opt. Lett. 34, 1003–1005 (2009).
Rossouw, D., Couillard, M., Vickery, J., Kumacheva, E. & Botton, G. A. Multipolar plasmonic resonances in silver nanowire antennas imaged with a subnanometer electron probe. Nano Lett. 11, 1499–1504 (2011).
Duan, H., Fernández-Domínguez, A. I., Bosman, M., Maier, S. A. & Yang, J. K. W. Nanoplasmonics: classical down to the nanometer scale. Nano Lett. 12, 1683–1689 (2012).
Kociak, M. & Stéphan, O. Mapping plasmons at the nanometer scale in an electron microscope. Chem. Soc. Rev. 43, 3865–3883 (2014).
Tan, S. F. et al. Quantum plasmon resonances controlled by molecular tunnel junctions. Science 343, 1496–1499 (2014).
Koh, A. L., McComb, D. W., Maier, S. A., Low, H. Y. & Yang, J. K. W. Sub-10 nm patterning of gold nanostructures on silicon-nitride membranes for plasmon mapping with electron energy-loss spectroscopy. J. Vac. Sci. Technol. B 28, C6O45–C46O49 (2010).
Koh, A. L., Fernández-Domínguez, A. I., McComb, D. W., Maier, S. A. & Yang, J. K. W. High-resolution mapping of electron-beam-excited plasmon modes in lithographically defined gold nanostructures. Nano Lett. 11, 1323–1330 (2011).
Humphreys, F. J. & Hatherly, M. Recrystallization and related annealing phenomena. (Pergamon, 2004).
Bosman, M. et al. Surface plasmon damping quantified with an electron nanoprobe. Sci. Rep. 3, 1312 (2013).
Palik, E. D. Handbook of optical constants, Vol. III. (Academic Press, San Diego; 1998).
Moody, N. R. et al. Effects of diffusion on interfacial fracture of gold-chromium hybrid microcircuit films. Int. J.Fracture 120, 407–419 (2003).
Johnson, C. J., Dujardin, E., Davis, S. A., Murphy, C. J. & Mann, S. Growth and form of gold nanorods prepared by seed-mediated, surfactant-directed synthesis. J. Mater. Chem. 12, 1765–1770 (2002).
Hu, H. et al. Photoluminescence via gap plasmons between single silver nanowires and a thin gold film. Nanoscale 5, 12086–12091 (2013).
Katz-Boon, H. et al. Three-dimensional morphology and crystallography of gold nanorods. Nano Lett. 11, 273–278 (2011).
Bietsch, A. & Michel, B. Size and grain-boundary effects of a gold nanowire measured by conducting atomic force microscopy. Appl. Phys. Lett. 80, 3346–3348 (2002).
Bosman, M. & Keast, V. J. Optimizing EELS acquisition. Ultramicroscopy 108, 837–846 (2008).
Schmidt, F.-P. et al. Universal dispersion of surface plasmons in flat nanostructures. Nat. Commun. 5, 3604 (2014).
Olivero, J. J. & Longbothum, R. L. Empirical fits to the Voigt line width: A brief review. J. Quant. Spectrosc. Radiat. Transfer 17, 233–236 (1977).
Jana, N. R., Gearheart, L. & Murphy, C. J. Wet chemical synthesis of high aspect ratio cylindrical gold nanorods. J. Phys.Chem. B 105, 4065–4067 (2001).
This work was supported by the Agency for Science, Technology and Research (A*STAR) in Singapore and made use of the SnFPC facilities in IMRE. J.K.W.Y. kindly acknowledges support from the Singapore National Research Foundation (NRF) under the CRP program (Award Nos. NRF–2011, NRF–CRP 001–126) and the NRF is acknowledged by J.K.W.Y., M.B. and C.A.N. for support via NRF–CRP 8–2011–07). L.Z. and C.-W.Q. acknowledge financial support from the National University of Singapore (Grant No R–263–000–688–112). H.D. acknowledges financial support from the National Science Foundation of China (Grant Nos 1274107 and 61204109).
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Bosman, M., Zhang, L., Duan, H. et al. Encapsulated Annealing: Enhancing the Plasmon Quality Factor in Lithographically–Defined Nanostructures. Sci Rep 4, 5537 (2014). https://doi.org/10.1038/srep05537
This article is cited by
Comparative study of plasmonic antennas fabricated by electron beam and focused ion beam lithography
Scientific Reports (2018)
Single-Crystalline Gold Nanowires Synthesized from Light-Driven Oriented Attachment and Plasmon-Mediated Self-Assembly of Gold Nanorods or Nanoparticles
Scientific Reports (2017)
Frontiers of Physics (2017)