Walkable Dual Emissions

Walkable dual emissions, in which the emission bands of the walker reversibly cross or leave those of the stationary ones depending on temperature and concentration, have been demonstrated in cyclic dimeric lanthanide complexes [Ln(hfac)3(PAnPO2)]2 (Ln = EuIII, TbIII; hfac− = hexafluoroacetylacetonate; PAnPO2 = 9,10-bis(diphenylphosphino) anthracene dioxide), providing a concept model for signals exchanging and dispatching. Additionally, good linear relationships are observed between the maximum emission bands of the walker vs the concentrations {lg(M)} and the measurement temperatures (K), implying such materials could be served as potential concentration and temperature sensors.

M olecular information process, operative in molecular system with reversibly switchable states, is a hot topic 1,2 . These processes are commonly controlled by stimuli, such as by chemical 3 or electrical 4 energies, as well as by light 5 . Like bead shuttling back and forth along the thread in rotaxane 6 , one emission bands reversibly crossing or leaving the static ones in single molecule depending on experimental conditions named as ''Walkable Dual Emissions'' (WDE), may be potential application in signal transmission.
We consider that a model with a typical ''WDE'' should match the following two criteria: 1) There are at least two types of luminophores in a molecule, one is the stationary, the emission bands of which are not affected by peripheral environment, such as the lanthanide subunits in its complex 7 . While the other is the walker, the emission behavior of the walker, such as the aromatic ligands, is sensitive to the external environment 8 . 2) The two chromophores are assembled in a cyclic structure. Given the two prerequisite conditions are warranted, the parallel conjugate aromatic ligands (the walkers) can easily suffer from p???p stacking interactions 8,9 , inducing the emission bands of the walker moving toward or backward those of the lanthanide ones (the stationary). When the emissions (signals) meet with each other, a possibility to exchange information is present. If the walker leaves the stationary, dispatching information becomes possible.

Results
Synthesis and structure. The cyclic lanthanide complexes could be afforded by two methods, one is in situ oxidation PAnP into PAnPO 2 by O 2 , the other one is by prior addition of H 2 O 2 , then reaction of equal molar ratio of PAnPO 2 with Ln(hfac) 3 (H 2 O) 2 affords orange crystals of 1. We found that the former method is better than the latter in the yields. As depicted in Figure 1, the crystal structure of 1?Eu can be viewed as two Eu(hfac) 3 subunits bridged by PAnPO 2 into a cyclic structure. The Eu III ion is encapsulated by eight oxygen atoms including six from hfac 2 , and two from the P5O groups to furnish a distorted square-antiprism. The bridging ligand PAnPO 2 exhibits a ''W'' arrangement with a linear P-O-M angle (176.5(3)u and 178.0(3)u), comparable to those found in the phosphine oxide lanthanide complexes 10  , assigned as the low-energy 1 p R p* transition of the anthracenyl rings 11 . Noticeably, the vibronic bands are extended from 450 nm in the free PAnPO 2 to 500 nm in the cyclic 1?Eu owing to the two coplanar anthracenes. Upon excitation with l ex 5 384 nm, PAnPO 2 exhibits a broad emission band centered at ca. 470 nm in an aerated dichloromethane solution at 298 K, ascribed to the low energy 1 p R p* transitions in the anthracenyl ring 11 . Upon illumination at 350 nm, 1?Eu (10 25 M) exhibits a broad luminescence band centered at ca. 475 nm as well as a narrow line-like emission at 613 nm, featured distinctly from PAnPO 2 chromophore and Eu III center, respectively ( Figure 2).
White-light emission. It has been demonstrated that white-light emission is accessible by mixing pure red, green, and blue emissions 14 or at least two complementary color emissions 15  Energy transfer procedure. Due to the internal heavy atom effect, and lacking of energy transfer from the sensitizer triplet states, 1?Gd is a suitable candidate for evaluating ligand triplet energy levels, so as to assess its efficiency in the energy-transfer process to the lanthanides. As shown in Figure S3, 1?Gd exhibits ligand phosphorescence as a broad band centered at ca. 472 nm with vibrational structure after excitation at 380 nm in degassed methanol at 77 K. The calculated triplet-state energy level (21300 cm 21 ) is favorable for energy transfer into those of Eu 31 ( 5 D 0 , 17300 cm 21 ), and Tb 31 ( 5 D 4 , 20500 cm 21 ) 7 . And the excitation spectra of 1?Eu ( Figure S4) and 1?Tb monitored at the strongest f-f' transition at 613 nm and 545 nm resemble the profile of the absorption spectrum. All of these facts demonstrate an energy transfer from the PAnPO 2 to the lanthanide. The calculated energy transfer rates (k ET ) of 1?Eu and 1?Tb, estimated by the equation of k ET 5 1/t 2 1/t 0 12,13 with 1?Gd complex as the reference, are beyond 10 8 s 21 , indicating an efficient energy transfer from PAnPO 2 to the lanthanide acceptors. And the Dexter energy transfer mechanism is operative in 1?Eu and 1?Tb based on the Calculations of donor/acceptor spectrosocpic overlap with PhotoChemCAD version 2.1 13 .
Processivity studies on forward and backward walking. As depicted in Figure 2, by increasing its solution concentrations from 1 3 10 26 M to 1 3 10 23 M (the maximum limited concentration is about 10 23 M), the distances between the maximum emission bands of the walker (PAnPO 2 ) and those of the stationary (Eu IIIbased subunit) shorten from 146 to 98 nm by ca. 48 nm. When   the concentration reaches its highest value in the solid state, the distance remains only 28 nm eventually. These phenomena can be simply viewed as the walker approaches the stationary gradually with concentrations increasing, shielding almost the stationary in the solid state. We have verified that these phenomena are reversible, diluting the solution concentrations from 1 3 10 23 M to 1 3 10 26 M, the walker leaves the stationary from 98 nm to 146 nm. Due to the nondestructive physical cycle, these phenomena are completely reversible and reliable.
Since cooling can also fortify the restriction of the intramolecular breathing vibration process of the walkers, we thus studied the temperature effect on the emission behaviors of 1?Eu. As shown in Figure 3, by successively decreasing the measurement temperature, the walker approaches the stationary gradually. When the dilute solution of 1?Eu (1.5 3 10 25 M) is cooled to 198 K, the emission peak (l max 5 474 nm) of the walker is divided into two vibration peaks (l max 5 450 and 478 nm) with a frequency of ca. 1300 cm 21 . Further dropping the temperature to 148 K, the two vibration peaks are splitted into three vibration ones (l max 5 450, 485 and 511 nm) with the vibronic spacings ca. 1600 and 1050 cm 21 , compared to those of the free PAnPO 2 ( Figure S6, two vibronic shoulders with l max 5 450 and 475 nm with a frequency of ca. 1170 cm 21 ), assigned as the low energy 1 p R p* transitions in the anthracenyl ring 11 . Noticeably, the third vibration peak of the walker at 77 K approaches the stationary closer ca. 37 nm (139-102) than the distance between the walker and the stationary at 298 K. Warming up the solution from 77 K to 298 K, the single emission band recovers from three vibration peaks with the distance from the stationary ca. 139 nm.
Interestingly, by increasing the concentration of 1?Eu up to 5 3  Figure S8, ESI), we find that not only the emission profiles of the walker change from three vibration peaks (l max 5 450, 485 and 511 nm) to a broad emission band (l max 5 511 nm), but also the walker approaches the stationary from 163 to 102 nm (ca. 61 nm). This value is larger than that at room temperature (ca. 48 nm), indicating low temperature (77 K, ca. 61 nm) with more effect than high temperature (298 K, ca. 48 nm) on the walking distance.
Although similar to dimers, two bridging parallel anthracenyl rings in 1?Eu experience a strong p???p stacking interactions (Figure 1), different emission behaviors of excimers with red-shift and the absence of vibronic structures 8,9 , forming by aromatic conjugate molecules in aggregation, are found. Such as, the emission bands of the PAnPO 2 in 1?Eu exhibit red shift with vibronic structures (l max 5 450, 485 and 511 nm) in diluted solution (1.5 3 10 25 M), but without vibronic structures (a broad emission band centred at ca. 510 nm) in concentrated solution (5 3 10 24 M) at 77 K. And the vibronic structures (l max 5 450 and 488 nm) in concentrated solution (5 3 10 24 M) rather than in diluted solution (1.5 3 10 25 M) (l max 5 474 nm) are observed at 298 K. Therefore, the vibronic structures of 1?Eu appear to be dependent on the measurement concentrations and temperatures.
Taking advantage of such unique properties that the measurement temperatures and concentrations have significant effect on the walking distance of the walker, such materials displays some potential applications on concentration or temperature sensors. Pleasantly, there are good linear relationships between the maximum emission bands of the walker vs the concentrations {lg(M)} and the measurement temperatures based on some limitations. As shown in Figure 4 and Figures S9-S10 (ESI), we could find that the linear relationships between the maximum emission bands of the walker vs the concentrations {lg(M)} (R 2 5 0.99) is slightly better than it vs the measurement temperatures (R 2 5 0.98).

Discussion
As the measurement temperatures and concentrations have critical effect on the walking distance of the walker in 1?Eu, it can be concluded that it is the aggregation effect induces such walkable dual emissions. As shown in Figure 5, 1?Eu displays (a) configuration with a long distance between the two bridging anthracenyl rings in isolated state. However, in the aggregated state, the separation becomes shorter and shorter, due to the p???p stacking interactions ( Figure 5(b)). Crystallographic evidence does confirm a short  intramolecular p???p separation between the two bridging coplanar anthracenyl rings of 3.4 Å . In addition, various emission behaviors of the temperature-dependent vibronic structure also indirectly support the above hypothesis.
Based on the above possible mechanism, asides from acting as sensors of concentration and temperature, such kind of cyclic dimeric lanthanide may be promising in other relative applications 18,19 , such as in information gateway or molecular electronics 19 , by elaborately modulating the distance between the two bridging anthracenyl rings.
In order to realize the walker crossing the stationary, two approaches may be practicable. One is blue-shifting the emission bands of the stationary, such as using Tb(hfac) 3 instead of Eu(hfac) 3 to fix the central emission band of the stationary from 613 nm to 543 nm. The other one is using more conjugate luminophores than PAnPO 2 as the walker. As expected, with the former approach, we have realized the crossing dual emission bands in 1?Tb. As shown in Figure 6, 1?Tb exhibits dual emissions at ca. 475 nm and 543 nm in dilute solution (1.5 3 10 25 M) from both the walker (PAnPO 2 ) and the stationary (Tb III -centred emitters), respectively. When the concentration reaches its highest value in the solid state, the walker crosses the stationary (543 nm) with a beyond distance of 42 nm. Similarly, under dilute conditions, the walker moves backward about 110 nm (68 1 42) to recover its initial state. These phenomena could thus be simply viewed as: there is a small island in a gulf, when the tide rises, seawater climbs across and drowns the island; once the tide ebbs away, the island would stand out again.
Noteworthily, it is the first case that emission bands from the sensitizer could reversibly cross or leave the fixed Ln III -based emissions depending on temperature and concentration, although dual emissions arising from both the sensitizers and lanthanide ions always could be observed in a hybrid lanthanide due to a part energy transfer 15,16 . On the other hand, if other metallic blocks complexed with the same ligand, dual emissions may also be provided 20,21 . However, as the energy levels of metallic blocks and the aromatic ligands are susceptible to the external environment, the two emissions are active during altering experimental conditions 22 .
In summary, walkable dual emissions in the cyclic 1 have been found, and the emission bands of the walker are able to pass through and reverse back those of the stationary depending on temperature and concentration. Due to the non-destructive physical cycle, these phenomena are verified to be completely reversible and reliable. This work establishes a model that the information between the walker and the stationary could be exchanged and dispatched by the ''WDE'', through switching the intramolecular interactions in dimeric complexes. Additionally, our results demonstrated that such materials are promising for potential application as sensors of concentration and temperature.

Methods
Sample preparation. All manipulations were performed under dry argon atmosphere using Schlenk techniques and a vacuum-line system. The solvents were dried, distilled, and degassed prior to use, except those for spectroscopic measurements were of spectroscopic grade. Hexafluoroacetylacetone (Hhfac) were commercially available. Ln(hfac) 3 (H 2 O) 2 (Ln 5 Eu, Gd, Tb) 23 , and 9,10bis(diphenylphosphino)anthracene (PAnP) 11 were prepared by the literature procedures.
Synthesis of PAnPO 2 . A mixture of diphosphine (1040 mg for PAnP), hydrogen peroxide (0.5 mL, 30%), and absolute ethanol (40 ml) was refluxed for 30 min. The solution was poured into water (ca. 100 mL) and extracted with chloroform. The organic extract was dried over magnesium sulfate, filtered, and concentrated to afford diphosphine dioxides powder as a yellowish green solid, ESI-MS (CH 3    Physical measurements. Elemental analyses (C, H, N) were carried out on a Perkin-Elmer model 240C elemental analyzer. Electrospray ion mass spectra (ESI-MS) were performed on a Finnigan LCQ mass spectrometer using dichloromethane-methanol mixture as mobile phases. UV-vis absorption spectra were measured on a Perkin-Elmer Lambda 35 UV-vis spectrophotometer. Infrared (IR) spectra were recorded on a Magna750 FT-IR spectrophotometer with KBr pellet. Emission, excitation spectra and emission lifetimes were recorded on an Edinburgh Instrument (FLS 920 spectrometer). Low temperature emission and excitation spectra were carried out in an oxford instrument liquid nitrogen cryostat, Optistat DN . The instrument response function at the excitation wavelength was deconvolved from the luminescence decay. The quantum yields of 1?Eu with white-light emission was determined relative to that of [Ru(bpy) 3 ]Cl 2 (W em 5 0.028) in H 2 O. All the quantum yields were calculated by W s 5 W r (A r /A s )(I r /I s )(n s /n r ) 2 (D s /D r ) 24 , where the subscripts r and s denote reference standard and the sample solution, respectively; and A, n, I, D and W are the absorbance of a sample at excitation wavelength l, the refractive index of the solvents, the relative intensity of excitation light at wavelength l, the integrated intensity and the luminescence quantum yield, respectively. All the solutions used for determination of emission lifetimes and quantum yields were prepared under vacuum in a 10 cm round bottom flask equipped with a side arm 1 cm fluorescence cuvette and sealed from the atmosphere by a quick-release teflon stopper. Solutions used for luminescence determination were prepared after rigorous removal of oxygen by three successive freeze-pump-thaw cycles. Calculations of the chromaticity coordinates (CIE) of 1?Eu with ColorCoordinate. exe version 1.0 was carried out with the concentration of 1.5 3 10 25 M in dichloromethane solutions under irradiation with 350 nm in dichloromethane at ambient temperature.
Crystal structural determination. Single crystal of 1?Eu?H 2 O suitable for X-ray diffraction was grown by layering n-hexane onto the corresponding dichloromethane solutions. Crystals coated with epoxy resin or sealed in capillaries with mother liquors were measured on a SIEMENS SMART CCD diffractometer by v scan technique at room temperature using graphite-monochromated Mo-Ka radiation (l 5 0.71073 Å ). Lp corrections were carried out in the reflection reduction process. The structures were solved by direct method and the heavy atoms were located from E-map. The remaining non-hydrogen atoms were determined from the successive difference Fourier syntheses. The non-hydrogen atoms were refined anisotropically except for the F atoms, and the hydrogen atoms were generated geometrically with isotropic thermal parameters. The structures were refined on F 2 by full-matrix least-squares methods using the SHELXTL-97 program package 25 , the refinements were carried out by fixing the C-F distances (1.32 6 0.01 Å ) with the occupancy factors of F1-F36 and