Abstract
Co-doping of lanthanum and phosphorus in CaFe2As2 induces superconductivity at 45 K. This superconducting transition temperature is higher than the 38 K transition in Ba1−xKxFe2As2, which is the maximum found thus far among the 122 phases. Superconductivity with a substantial shielding volume fraction was observed at 0.12 ≤ x ≤ 0.18 and y = 0.06 in Ca1−xLaxFe2(As1−yPy)2. The superconducting phase of the present system seems to be not adjacent to an antiferromagnetic phase.
Similar content being viewed by others
Introduction
Iron arsenide superconductors seem to occur in close proximity to an antiferromagnetic (AF) phase1,2,3. Density functional theory calculations have pointed out the importance of spin fluctuations, resulting from Fermi surface nesting between hole and electron pockets, for the emergence of superconductivity4,5. The superconducting transition temperature Tc has exceeded 50 K in doped REFeAsO, where RE corresponds to a rare earth element6,7,8.
However, recent reports by Iimura et al.9 and Sun et al.10 suggest that the fascinating superconducting phase is also found separated from the AF phase in this class of materials. Iimura et al.9 reported that two domes appear in Tc versus x for LaFeAsO1−xHx. The first dome exhibits Tc = 26 K in the vicinity of the AF phase, which was recognized as the maximum Tc of the electron-doped LaFeAsO11. Surprisingly, a much higher Tc = 36 K emerges in the second dome, far from the AF phase. Moreover, Sun et al.10 reported the re-emergence of high temperature superconductivity in Tl0.6Rb0.4Fe1.67Se2, K0.8Fe1.7Se2 and K0.8Fe1.78Se2 as a function of pressure. At low pressures, superconductivity in those compounds coexists with AF order, as reported by Guo et al.12 With increasing pressure, Tc decreases from a maximum of 32 K at 1 GPa to zero at 9.8 GPa10, above which AF order disappears12. Upon further increase in pressure, a second superconducting phase with Tc = 48 K suddenly emerges above 11.5 GPa in the paramagnetic phase10. These results suggest a greater flexibility in developing iron-based superconductors. A similar superconducting phase that is separated from the AF phase is expected in systems other than LaFeAsO1−xHx9 and (Tl,Rb,K)1−xFe2−ySe210.
We focus on the RE-doped CaFe2As2 (abbreviated to 122) system as a candidate material with a superconducting phase separated from an AF phase. Very recently, in the vicinity of the AF phase, a superconducting phase with Tc = 40–49 K was suggested in RE-doped CaFe2As213,14,15. Though bulk superconductivity has not yet been confirmed, the results strongly suggest that the 122 phase may exhibit a Tc as high as 50 K. This value is higher than Tc = 38 K in Ba1−xKxFe2As216 which is the highest value yet reported among the 122-type bulk superconductors. Similar results were almost simultaneously reported by three groups: Saha et al. reported Tc = 47 K in Ca1−xPrxFe2As213; Gao et al. reported Tc = 42.7 K in Ca1−xLaxFe2As214; and Lv et al. reported Tc = 49 K in Ca1−xPrxFe2As215. These values of Tc were determined from the onset of the resistive transition.
In the reports by Saha et al.13 and Gao et al.14, diamagnetic behavior is not clearly observed in the temperature dependence of the magnetization M around Tc. Instead, a visible drop in M occurs below ~20 K, suggesting that a minority phase possesses a high Tc. On the other hand, Lv et al.15 showed a clear diamagnetic signal around 40 K in a magnetic field of 1 Oe, in addition to a subsequent transition at 20 K. However, the signal around 40 K was completely suppressed by the application of a tiny magnetic field of 20 Oe. Lv et al.15 proposed that interfacial superconductivity with Tc = 49 K occurs at the grain boundary.
In this paper, we report the emergence of superconductivity at 45 K by La and P co-doping of CaFe2As2. Tc = 45 K is higher than 38 K in Ba1−xKxFe2As216. A substantial shielding volume fraction was observed at 0.12 ≤ x ≤ 0.18 with y = 0.06 in Ca1−xLaxFe2(As1−yPy)2. The superconducting phase of the present system seems to be far from the AF phase in the electronic phase diagram.
Results
Lattice parameters and cell volume
In the phosphorus-free Ca1−xLaxFe2As2, the a parameter gently increases and the c parameter slightly decreases with increasing x, as shown in Figure 1. This result is consistent with Saha et al.13 Upon phosphorus doping of Ca1−xLaxFe2As2, the a parameter increases and the c parameter decreases, resulting in a reduced cell volume. This decrease in cell volume is expected since the ionic radius of P is smaller than As. Kasahara et al.17 have shown in CaFe2(As1−xPx)2 that the reduction in volume leads to successive phase transitions in which the AF phase, the superconducting phase and the non-superconducting phase appear, in this order. Thus, isovalent phosphorus doping separates the system from the AF phase. This same effect is also expected in Ca1−xLaxFe2(As1−yPy)2.
Superconductivity
In fact, phosphorus-doped Ca1−xLaxFe2(As0.94P0.06)2 does not show an AF transition. As shown in the inset of Figure 2, phosphorus-free Ca1−xLaxFe2As2 (x = 0.12) exhibits a jump in the temperature dependence of the electrical resistivity, characteristic of an AF transition19,20. On the other hand, no jump was observed in phosphorus-doped Ca1−xLaxFe2(As0.94P0.06)2 (x = 0.12). Instead, the electrical resistivity exhibits superconductivity with Tc as high as 40 K. A maximum Tc of 45 K was observed around x = 0.15 – 0.18 with y = 0.06. Figure 2 shows the temperature dependence of the electrical resistivity for Ca1−xLaxFe2(As0.94P0.06)2 (x = 0.17). The resistivity decreases with decreasing temperature, starts to drop sharply at 48 K and becomes negligibly small below 45 K. This result suggests that the sample becomes superconducting below 45 K.
Superconductivity at 45 K was also evident from the temperature dependence of the magnetization, shown in Figure 3. Ca1−xLaxFe2(As0.94P0.06)2 (x = 0.17) shows clear diamagnetic behavior below 45 K. The estimated shielding volume fraction, VF, is as large as 23% at 20 K and 75% at 5 K. Contrary to previous reports13,14,15, there is no second transition at 20 K and the VF is robust against any increase in magnetic field, as shown in the inset of Figure 3. These results do not entirely ensure the occurrence of bulk superconductivity at 45 K because the transition is broad and the magnetization continues to decrease with decreasing temperature. Nonetheless, the present data strongly suggest the existence of a bulk superconducting phase with Tc = 45 K in Ca1−xLaxFe2(As0.94P0.06)2.
Phase diagram
Figure 4a shows the T-x-y phase diagram of Ca1−xLaxFe2(As1−yPy)2 for y = 0.00, 0.03 and 0.06, derived from electrical resistivity and magnetization measurements. The AF phase is almost suppressed by 3% phosphorus doping. It is found that the superconducting phase (colored in blue) seems to be not adjacent to the AF phase. Superconductivity at 40–45 K was observed at 0.12 ≤ x ≤ 0.18 with y = 0.06 in Ca1−xLaxFe2(As1−yPy)2. The substantial VF in these samples can be seen in Figure 4b. On the other hand, near the AF phase, phosphorus-free Ca1−xLaxFe2As2 and Ca1−xLaxFe2(As0.97P0.03)2 with less phosphorus exhibit traces of superconductivity, with a zero resistivity accompanied by a quite small VF.
Discussion
At x < 0.12, Ca1−xLaxFe2(As0.94P0.06)2 exhibits trace superconductivity. A superconducting phase with a large VF suddenly emerges at x ≥ 0.12 and is narrow in width (Δx = 0.06). Here, the question of the origin for the sudden cut-off of the superconducting phase arises. The lattice collapse transition in CaFe2As217,18,21,22 might provide a clue. CaFe2As2 undergoes a lattice collapse transition from an uncollapsed tetragonal (ucT) to a collapsed tetragonal (cT) phase along with a 10% decrease in c with the application of pressure or chemical doping. It is well known that superconductivity abruptly disappears with the appearance of the ucT-cT transition17,18,21,22. The sudden cut-off of the superconducting phase at x < 0.12 might be explained in terms of the ucT-cT transition. Structural studies are thus necessary in the present system.
Another question that arises is on the origin of the emergence of high Tc superconductivity separate from the AF phase. The second dome in Tc in the T-x phase diagram of LaFeAsO1−xHx may provide a hint9. Based on density functional theory calculations, Iimura et al.9 have shown that the three Fe 3d bands (xy, yz and zx) become degenerate when Tc exhibits a maximum in the second dome, whereas Fermi surface nesting is weakened there. They have implied that band degeneracy is a key ingredient to induce high Tc in the second dome, while spin fluctuations are important in the first dome. A similar scenario may be active in Ca1−xLaxFe2(As1−yPy)2. Further angle-resolved photoemission spectroscopy measurements and band structure calculations are expected to be useful for understanding superconductivity in the present system.
So far, systematic chemical substitutions have been conducted in the 122 type AEFe2As2 (AE = alkaline earth elements). It has been found that bulk superconductivity appears upon substituting alkali metals for AE (hole doping)16, the RE element La for AE ( = Sr) (electron doping)23, transition metal elements such as Co24,25 and Ni26,27 for Fe (electron doping) and P for As (isovalent doping)17,28,29,30,31. The highest resulting Tc is 38 K in Ba1−xKxFe2As216. There seems to be no further variety of chemical doping in the 122 phase. However, there is still some room left for improvement in terms of co-doping. Sole P doping of the As site shrinks the cell volume, resulting in bulk superconductivity at 15 K in CaFe2(As1−xPx)217. Sole La doping of the Ca site induces electron carriers, leading to trace superconductivity at 40 K in Ca1−xLaxFe2As213,14. In this study, La and P co-doped Ca1−xLaxFe2(As1−yPy)2 exhibits Tc = 45 K, which is higher than 38 K. It is considered that the simultaneous tuning of the concentration of electron carriers and the reduction in cell volume optimizes superconductivity. Our result suggests that the co-doping technique will lead to higher superconducting transition temperatures in the iron-based pnictides.
In conclusion, we demonstrate the emergence of superconductivity at 45 K by La and P co-doping of CaFe2As2. Tc = 45 K is higher than the value of 38 K found in Ba1−xKxFe2As2. The magnetization shows a substantial shielding volume fraction at 0.12 ≤ x ≤ 0.18 with y = 0.06 in Ca1−xLaxFe2(As1−yPy)2. The superconducting phase in the present system looks to be separated from the antiferromagnetic phase.
Methods
Preparation and characterization of samples
Single crystals of Ca1−xLaxFe2(As1−yPy)2 were grown using a self-flux method18. A mixture with a ratio of Ca:La:FeAs:Fe:P = 1−x : x : 4−4y : 4y : 4y′ was placed in an alumina crucible, sealed in an evacuated quartz tube, slowly heated to 1100°C and cooled to 1050°C at a rate of 1.25°C/h followed by furnace cooling. Single crystals with a typical dimension of 1.5 × 1.5 × 0.05 mm3 were mechanically isolated from the flux. The results of powder X-ray diffraction at room temperature, performed using a Rigaku RINT-TTR III X-ray diffractometer with Cu Kα radiation, showed that all specimens are single phase and possess the CaFe2As2 structure. Energy dispersive X-ray spectrometry (EDS) was used to determine the lanthanum content x and the phosphorus content y. The lattice parameters a and c were estimated at room temperature using a Rigaku Single Crystal X-ray Structural Analyzer (Varimax with Saturn).
Electrical resistivity and magnetization measurements
The electrical resistivity ρab (parallel to the ab-plane) measurements were carried out by a standard DC four-terminal method in a Quantum Design PPMS. The magnetization M was measured using a SQUID magnetometer (Quantum Design MPMS SQUID-VSM).
References
Ishida, K., Nakai, Y. & Hosono, H. To What Extent Iron-Pnictide New Superconductors Have Been Clarified: A Progress Report. J. Phys. Soc. Jpn. 78, 062001 (2009).
Paglione, J. & Greene, R. L. High-temperature superconductivity in iron-based materials. Nat. Phys. 6, 645–658 (2010).
Johnston, D. C. The puzzle of high temperature superconductivity in layered iron pnictides and chalcogenides. Adv. Phys. 59, 803–1061 (2010).
Mazin, I. I., Singh, D. J., Johannes, M. D. & Du, M. H. Unconventional Superconductivity with a Sign Reversal in the Order Parameter of LaFeAsO1−xFx . Phys. Rev. Lett. 101, 057003 (2008).
Kuroki, K. et al. Unconventional Pairing Originating from the Disconnected Fermi Surfaces of Superconducting LaFeAsO1−xFx . Phys. Rev. Lett. 101, 087004 (2008).
Ren, Z.-A. et al. Superconductivity at 55 K in Iron-Based F-Doped Layered Quaternary Compound Sm[O1−xFx]FeAs. Chin. Phys. Lett. 25, 2215–2216 (2008).
Kito, H., Eisaki, H. & Iyo, A. Superconductivity at 54 K in F-Free NdFeAsO1-y . J. Phys. Soc. Jpn. 77, 063707 (2008).
Ren, Z.-A. et al. Superconductivity and phase diagram in iron-based arsenic-oxides ReFeAsO1−δ (Re = rare-earth metal) without fluorine doping. Europhys. Lett. 83, 17002 (2008).
Iimura, S. et al. Two-dome structure in electron-doped iron arsenide superconductors. Nat. Commun. 3, 943 (2012).
Sun, L. et al. Re-emerging superconductivity at 48 kelvin in iron chalcogenides. Nature 483, 67–69 (2012).
Kamihara, Y., Watanabe, T., Hirano, M. & Hosono, H. Iron-Based Layered Superconductor La[O1-xFx]FeAs (x = 0.05 – 0.12) with Tc = 26 K. J. Am. Chem. Soc. 130, 3296–3297 (2008).
Guo, J. et al. Pressure-Driven Quantum Criticality in Iron-Selenide Superconductors. Phys. Rev. Lett. 108, 197001 (2012).
Saha, S. R. et al. Structural collapse and superconductivity in rare-earth-doped CaFe2As2 . Phys. Rev. B 85, 024525 (2012).
Gao, Z. et al. Synthesis and properties of La-doped CaFe2As2 single crystals with Tc = 42.7 K. Europhys. Lett. 95, 67002 (2011).
Lv, B. et al. Unusual superconducting state at 49 K in electron-doped CaFe2As2 at ambient pressure. Proc. Natl. Acad. Sci. USA 108, 15705–15709 (2011).
Rotter, M., Tegel, M. & Johrendt, D. Superconductivity at 38 K in the Iron Arsenide (Ba1−xKx)Fe2As2 . Phys. Rev. Lett. 101, 107006 (2008).
Kasahara, S. et al. Abrupt recovery of Fermi-liquid transport following the collapse of the c axis in CaFe2(As1−xPx)2 single crystals. Phys. Rev. B 83, 060505(R) (2011).
Danura, M. et al. Interplay of Superconductivity and Fermi-Liquid Transport in Rh-Doped CaFe2As2 with Lattice-Collapse Transition. J. Phys. Soc. Jpn. 80, 103701 (2011).
Harnagea, L. et al. Phase diagram of the iron arsenide superconductors Ca(Fe1−xCox)2As2 (0 ≤ x ≤ 0.2). Phys. Rev. B 83, 094523 (2011).
Pratt, D. K. et al. Coexistence of Competing Antiferromagnetic and Superconducting Phases in the Underdoped Ba(Fe0.953Co0.047)2As2 Compound Using X-ray and Neutron Scattering Techniques. Phys. Rev. Lett. 103, 087001 (2009).
Kreyssig, A. et al. Pressure-induced volume-collapsed tetragonal phase of CaFe2As2 as seen via neutron scattering. Phys. Rev. B 78, 184517 (2008).
Goldman, A. I. et al. Lattice collapse and quenching of magnetism in CaFe2As2 under pressure: A single-crystal neutron and x-ray diffraction investigation. Phys. Rev. B 79, 024513 (2009).
Muraba, Y. et al. High-pressure synthesis of the indirectly electron-doped iron pnictide superconductor Sr1−xLaxFe2As2 with maximum Tc = 22 K. Phys. Rev. B 82, 180512(R) (2010).
Leithe-Jasper, A., Schnelle, W., Geibel, C. & Rosner, H. Superconducting State in SrFe2−xCoxAs2 by Internal Doping of the Iron Arsenide Layers. Phys. Rev. Lett. 101, 207004 (2008).
Chu, J.-H., Analytis, J. G., Kucharczyk, C. & Fisher, I. R. Determination of the phase diagram of the electron-doped superconductor Ba(Fe1−xCox)2As2 . Phys. Rev. B 79, 014506 (2009).
Saha, S. R., Butch, N. P., Kirshenbaum, K. & Paglione, J. Evolution of bulk superconductivity in SrFe2As2 with Ni substitution. Phys. Rev. B 79, 224519 (2009).
Li, L. J. et al. Superconductivity induced by Ni doping in BaFe2As2 single crystals. New J. Phys. 11, 025008 (2009).
Ren, Z. et al. Superconductivity Induced by Phosphorus Doping and Its Coexistence with Ferromagnetism in EuFe2(As0.7P0.3)2 . Phys. Rev. Lett. 102, 137002 (2009).
Jiang, S. et al. Superconductivity up to 30 K in the vicinity of the quantum critical point in BaFe2(As1−xPx)2 . J. Phys. Condens. Matter 21, 382203 (2009).
Shi, H. L. et al. Structural properties and superconductivity of SrFe2As2−xPx (0.0 ≤ x ≤ 1.0) and CaFe2As2−yPy (0.0 ≤ y ≤ 0.3). J. Phys. Condens. Matter 22, 125702 (2010).
Kasahara, S. et al. Evolution from non-Fermi- to Fermi-liquid transport via isovalent doping in BaFe2(As1−xPx)2 superconductors. Phys. Rev. B 81, 184519 (2010).
Acknowledgements
Part of this work was performed at the Advanced Science Research Center, Okayama University. This work was partially supported by a Grant-in-Aid for Young Scientists (B) (23740274) from the Japan Society for the Promotion of Science (JSPS) and the Funding Program for World-Leading Innovative R&D on Science and Technology (FIRST Program) from JSPS.
Author information
Authors and Affiliations
Contributions
K.K. and M.N. conceived and planed the research. K.I., Y.K., J.M. and K.K. synthesized single crystals. K.I., M.T., M.D. and K.K. carried out electrical resistivity and magnetization measurements. K.K., K.I., M.T. and Y.N. characterized single crystals using X-ray diffraction. K.K. and M.N. discussed the results and wrote the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 3.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/3.0/
About this article
Cite this article
Kudo, K., Iba, K., Takasuga, M. et al. Emergence of superconductivity at 45 K by lanthanum and phosphorus co-doping of CaFe2As2. Sci Rep 3, 1478 (2013). https://doi.org/10.1038/srep01478
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep01478
This article is cited by
-
A Nanoindentation Study of the Plastic Deformation and Fracture Mechanisms in Single-Crystalline CaFe2As2
JOM (2018)
-
Phase diagram and transport properties of Sb-doped Ca0.88La0.12Fe2As2 single crystals
Frontiers of Physics (2017)
-
Iron arsenides with three-dimensional FeAs layer networks: Can(n+1)/2(Fe1−xPtx)(2+3n)Ptn(n−1)/2As(n+1)(n+2)/2 (n = 2, 3)
Scientific Reports (2016)
-
Characteristic two-dimensional Fermi surface topology of high-Tc iron-based superconductors
Scientific Reports (2014)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.