Vertically aligned single-walled carbon nanotubes (VASWCNTs) have been successfully transferred onto transparent conducting oxide glass and implemented as efficient low-cost, platinum-free counter electrode in sulfide –mediated dye-sensitized solar cells (DSCs), featuring notably improved electrocatalytic activity toward thiolate/disulfide redox shuttle over conventional Pt counter electrodes. Impressively, device with VASWCNTs counter electrode demonstrates a high fill factor of 0.68 and power conversion efficiency up to 5.25%, which is significantly higher than 0.56 and 3.49% for that with a conventional Pt electrode. Moreover, VASWCNTs counter electrode produces a charge transfer resistance of only 21.22 Ω towards aqueous polysulfide electrolyte commonly applied in quantum dots-sensitized solar cells (QDSCs), which is several orders of magnitude lower than that of a typical Pt electrode. Therefore, VASWCNTs counter electrodes are believed to be a versatile candidate for further improvement of the power conversion efficiency of other iodine-free redox couple based DSCs and polysulfide electrolyte based QDSCs.
One of the greatest challenges in the twenty-first century is undoubtedly the energy conversion and storage1. In response to the urgent renewable energy needs of modern society and emerging ecological concerns, it is now essential to develop novel inexpensive and environmentally friendly energy conversion and storage systems. Mesoscopic dye-sensitized solar cells (DSCs) have recently emerged as a credible alternative to solid-state p-n junction photovoltaic devices, primarily due to its potential to generate electricity on resource-abundant raw materials and energy-saving device processing2. Currently, certified power conversion efficiency (PCE) up to 11% has been achieved in conjunction with a polypyridyl ruthenium complexes based sensitizer and an organic solvent containing I−/I3− redox couple3. Nevertheless, there are substantial drawbacks of this benchmark I−/I3− redox shuttle hindering its practical applications4, such as large energy loss of dye regeneration process, visible light absorption and corrosiveness towards most current-collecting metal grids. Clearly, it would be highly desirable to identify alternative, noncorrosive and weakly absorbing redox couples5,6,7. This will not only further boost up the PCE but also promote the practical implementation of this promising low-cost photovoltaic technology.
Recently, Wang et al. reported a promising disulfide/thiolate (T−/T2) redox couple that has negligible absorption in the visible spectral range. Using this novel noncorrosive redox electrolyte in conjunction with a Z-907Na sensitized heterojunction, a PCE up to 6.4% was achieved under standard illumination conditions6. However, conventional planar platinum counter electrode showed poor catalytic activity towards this iodine-free redox couple, thus resulting in a poor fill factor (FF) and relatively moderate PCE. The phenomenon of a low FF with sulfur-functionalized redox mediators most likely results from the slow catalytic reduction of the oxidized species at the platinum counter electrode6,8,9. The slow electron transfer thus leads to a high interfacial charge transfer resistance limiting the FF of the device10. Therefore, it is imperative to seek suitable platinum-free catalysts that exhibit fast electron transfer kinetics for the disulfide-to-thiolate reduction, especially taking into account the low abundance (0.0037 ppm) and high cost (US$50/gram) of the platinum resources11.
Additionally, semiconductor quantum dots (QDs) such as CdS, CdSe, PbS, InAs and InP constitute reliable alternative light absorbers12,13 due to their intrinsic properties (i.e., size-dependent band gap14, high extinction coefficients15, and large intrinsic dipole moment16). More importantly, demonstration of the multiple exciton generation by impact ionization in colloidal QDs17 could push the thermodynamic efficiency limit of these devices up to 44%18 instead of the current 31% of the Shockley-Queisser detailed balance limit19. However, most QDs suffer from photodegradation when used in conjunction with the I−/I3− redox couple20. Consequently, quantum dot-sensitized solar cells (QDSCs) are often based on aqueous polysulfide electrolyte with minor use of the Fe(CN)63−/Fe(CN)64− couple21 and various cobalt-based electrolytes22 featuring notable attenuated corrosiveness, as well as, adjustable redox potential. Normally, in conjunction with such polysulfide electrolytes, Pt and other noble metals like Au are poor catalysts, and generate considerable overpotentials for the electrolyte regeneration. This is reflected in a reduction of the fill factors and thus PCE of the solar cell23. Therefore, alternative catalytic materials for polysulfide solution have been investigated such as CoS, Cu2S, NiS, and carbon materials24,25,26. However, low electrocatalytic activities were observed for carbon, Au, and Pt, followed by NiS, while the best results were obtained for CoS and Cu2S recently. Nevertheless, stability measurements in the presence of a photoanode indicated that CoS and Cu2S electrodes may contaminate the electrolyte and subsequently the photoanode24. Therefore, it would be of high importance to identify alternative highly-active catalytic counter electrode materials for further progress of this polysulfide electrolytes widely utilized in QDSCs.
To this end, efforts have been made to replace Pt with abundant low-cost alternatives in these iodine-free electrolyte systems, including tungsten carbide embedded into the ordered mesoporous carbon8, mesoporous carbon nanofibers27, niobium oxide28, Cu2S reduced graphene oxide composite29, and PbS23. It is worth mentioning that carbon nanotube (CNT) has recently attracted numerous attentions as practical Pt-free counter electrodes material in iodine electrolyte based DSCs and exhibited reasonable performance30,31,32,33. Specifically, aligned multi-walled carbon nanotube (MWCNT) arrays have been widely used to replace the platinum counter electrodes to catalyze the reduction of triiodide in DSCs with the target of better performance and lower material cost34,35,36,37,38,39. In 2011, Peng's group developed a new fabrication method for aligned CNTs/polymer film as the electrode material36 and reported an efficiency of 6.6%40. It is noted that Cheng's team successfully obtained a PCE of 6.05% in the iodine electrolyte system by utilizing a hybrid carbon structure, VACNTs grown on graphene paper38.
Single-walled carbon nanotubes (SWCNTs) can provide much higher surface area than MWCNTs due to their single graphitic layer structure and small diameter. Most recently, the efficiency of gel-coated SWCNTs-DSC reached 8% in conjunction with iodine electrolyte35. According to the high surface area to volume ratio in the vertically aligned 3D structure, even higher available catalytic surface area can be achieved in the vertically aligned single-wall carbon nanotubes (VASWCNTs). Moreover, electrons can directly transfer through individual tubes, instead of hopping between the different carbon structures within this film. As the result, VASWCNTs have been applied as low-cost counter electrode material for DSCs in our recent work32 and demonstrated comparable PCE with iodine electrolyte to the conventional Pt analogue. However, to the best of our knowledge, these promising three-dimensional electrocatalysts have not been employed in the iodine-free electrolyte up to date. Such results motivated us to explore the implementation of VASWCNTs as potential electrocatalyst for the aforementioned sulfide-mediated electrolytes.
Herein, we present for the first time, VASWCNTs that have been successfully transferred onto transparent conducting oxide glass and implemented as efficient low-cost, platinum-free counter electrode in iodine-free DSCs, featuring notably improved electrocatalytic activity toward thiolate/disulfide redox shuttle6 and aqueous polysulfide electrolyte over that of conventional planar Pt counter electrode. Impressively, The charge-transfer resistance (Rct) of VASWCNTs-counter electrode is only 21.22 Ω towards aqueous polysulfide electrolyte commonly applied in QDSCs. This value is several orders of magnitude lower than that of a Pt electrode. DSCs devices incorporating VASWCNTs counter electrodes and thiolate/disulfide redox electrolytes also show a significant gain in FF and short-circuit photocurrent density with respect to that of Pt electrodes.
As depicted in Figure 1, high quality VASWCNTs arrays were firstly grown in a water-assisted thermal chemical vapor deposition (CVD) system at 750°C (Process 1 in Figure 1)41, and then dry-transferred onto FTO glass substrates to produce robust counter electrodes (Process 2 and 3 in Figure 1). When compared with wet processing methods, the dry-transfer method is simple, reproducible and easy to control, offering high packing density of the obtained VASWCNTs arrays. Such VASWCNTs offer strong van Der Waals interfacial adhesion with a contacting surface, compared to the interaction with the growth substrate. According to this, a simple dry contact transfer can be achieved following the principle of the “gecko-effect” in a fully dry state42. Figure 2a presents a representative cross-sectional scanning electron microscope (SEM) image of the as-grown VASWCNTs arrays with a length around 30 μm, demonstrating the vertical alignment of these SWCNTs. As depicted in Figure 2b, following the dry-transfer process, the lengths of the SWCNTs arrays are observed to be approximately 6 μm due to the compression by an applied shear-force placed on the SWCNTs arrays, which is in line with our previous study of the compression effect on the VASWCNTs arrays' lengths32. Top surface morphology from Figure 2c clearly demonstrates the large interstices around the CNTs bundles. Such a geometrical structure of the VASWCNTs possesses double-functional merits of direct electron transport through individual vertically aligned tubes as well as rapid redox diffusion in the open structure around tubes. Figure 2d shows a typical transmission electron microscopy (TEM) image of the SWCNTs material, after sonication in ethanol and drop casting onto a TEM grid. It is evident from these images that SWCNTs have a diameter range of 2~4 nm, giving rise to a significant high surface area of the CNTs arrays. Due to its repeatability and simplicity, the dry contact transfer printing is highly scalable. This technique can be applied in a roll-to-roll, or large-scale industrial manufacturing settings.
Raman spectroscopy was further applied to characterize the quality of the VASWCNTs arrays. From the Raman characterization (633 nm excitation) of Figure 3, it is obvious that the VASWCNTs are of high quality with a G/D ratio around 9. This suggests a very low amount of defects, such as amorphous carbon in the nanotubes, as indicated by the red circles in Figure S1. At the same time, radial breathing modes (RBM) can be observed from the Raman spectra of the materials.
To assess the potential applications of the VASWCNTs counter electrodes in DSCs, devices were assembled with N719 sensitized TiO2 electrodes with a thickness of 14 μm and an active area of 0.16 cm2 in conjunction with the VASWCNTs electrodes (Process 4 in Figure 1) or conventional sputtered Pt counter electrodes. Figure 4 demonstrates the characteristic J-V performance for devices with VASWCNTs and reference Pt counter electrodes measured under Air Mass 1.5G illumination and the detailed photovoltaic parameters are tabulated in Table 1. Device A with Pt electrode in conjunction with T−/T2 electrolyte exhibits an open-circuit voltage (Voc) of 612 mV, a short-circuit photocurrent density (Jsc) of 10.26 mA cm−2, an FF of 0.56, yielding an overall PCE of 3.49%. It is remarkable that device B with VASWCNTs displays a Jsc enhancement up to 12.66 mA cm−2, a considerable increase in FF up to 0.68, and produces a PCE of 5.25%. Apparently, the enhancement of the PCE is directly originated from the Jsc and FF increase.
It is important to note that the FF of a DSC device is attenuated by the total series resistance of the cell, including the sheet resistances of the substrate and counter electrode, electron transport resistance through the photoanode, ion transport resistance, and Rct at the counter electrode43. Therefore, the FF enrichment in the current work is mainly a result of the superior electrocatalytic activity of the VASWCNTs and consequent significantly reduced charge-transfer resistance across the counter electrode/electrolyte interface. Significant improvement in charge transfer at the counter electrode/electrolyte interface not only reduces internal resistances, but also attenuates the recombination rates and concentration gradients in the electrolyte, which have been proved to affect Jsc strongly23. The obtained FF and PCE is of great advantage when compared to that with other catalyst materials, such as tungsten carbide embedded ordered mesoporous carbon8, as well as graphite9. Efforts to further enhance the PCE are currently in progress in our laboratory, which include optimizing the photoanode structure and employment of other sensitizers with strong hydrophobicity to inhibit charge recombination between the photoelectrode and electrolyte.
The electrocatalytic activity of the as-fabricated VASWCNTs counter electrodes towards thiolate/disulfide redox shuttle6 was first investigated by electrochemical impedance spectroscopy (EIS)44,45. Figure 5a presents the corresponding Nyquist spectra of symmetrical dummy cells with VASWCNTs counter electrodes and conventional sputtered Pt counter electrodes as the reference. It is generally recognized that in the order of increasing frequency, the response can be attributed to the Warburg diffusion processes in the electrolyte and charge transfer at the counter electrode/electrolyte interface45. Apparently, incorporation of the VASWCNTs promotes a significantly reduced diameter of the high-frequency semicircles. By fitting with the Randles equivalent circuit shown in Figure S2, the Rct of the VASWCNTs as shown in Table 1 is only 12.66 Ω, a value almost six-fold lower than that of conventional Pt counter electrode (76.28 Ω) under similar measurement conditions, highlighting the superior electrocatalytic activity of the VASWCNTs towards thiolate/disulfide redox couples. Furthermore, obvious high-frequency shift of the characteristic response peaks in the high-frequency regime of Bode plot shown in Figure 5b demonstrates a faster electron transfer at the interface between VASWCNTs and electrolyte with respect to conventional Pt counter electrode. In addition, it is also observed that the VASWCNTs electrodes exhibit a notably larger double-layer capacitance (Cdl) than the planar Pt electrodes do, suggesting a higher specific surface area in the former counter electrodes. This is in agreement with the results from other nanostructured counter electrodes with a high porosity46,47. Noteworthy is that our VASWCNTs do not increase the redox diffusion resistance in the electrolyte, probably arising from the relative open structure as characterized by the SEM image in Figure 2c.
The superior electrocatalytic activity of VASWCNTs electrodes towards T−/T2 electrolyte inspired us to the implementation of this encouraging counter electrode in other electrolyte systems, such as the aqueous polysulfide electrolyte commonly applied in QDSCs. Similar to the aforementioned experimental conditions, symmetrical dummy cells were fabricated in combination with the aqueous polysulfide electrolyte with a recipe of 1 M sulfur, 1 M Na2S·9H2O, and 0.1 M NaOH in deionized water. Figure 6 displays the corresponding Nyquist plots (a), Bode plots (b) and Tafel curves (c) of the symmetrical dummy cells measured under the similar conditions. Dramatic reduction in the Rct of VASWCNTs electrode is observed in comparison with that of Pt electrode as summarized in Table S1. In parallel with previous studies on the catalytic activity for polysulfide solutions24,25,26,48,49,50, planar Pt electrode exhibits a huge Rct in the order of 105 Ω, mainly due to the poor catalytic activity. Encouragingly, utilization of the VASWCNTs greatly enhances the electrocatalytic activity, yielding a small Rct value of only 21.22 Ω, as seen from the inset of Figure 6a. To the best of our knowledge, such an Rct value is the lowest ever seen in the polysulfide electrolyte, even compared with recently reported PbS23 and Cu2S19 counter electrodes. Complementally, significant high-frequency shift of the characteristic response peaks in the Bode plot shown in Figure 6b, further confirms the superior catalytic activity of the VASWCNTs electrodes to polysulfide electrolytes.
Tafel polarization measurement was further employed to study the interfacial charge-transfer properties of the polysulfide redox couples on the counter electrode surface. Figure 6c shows the logarithmic current density as a function of applied voltage of the symmetrical dummy cells. The exchange current density (J0) is obtained as the intercept of the extrapolated linear region of the curve when the overpotential is zero. In the curve at high potential (horizontal part), the limiting diffusion current density (Jlim) can be derived. These two parameters are closely related with the electrochemical activity of the catalysts51. Evidently, the anodic and cathodic branches of the VASWCNTs electrodes exhibit an obvious larger slope than the conventional Pt counter electrodes do, indicating the presence of a large exchange current density (J0) on the electrode surfaces. Moreover, a higher Jlim is noted in conjunction with VASWCNTs counter electrode, which suggests a higher diffusion coefficient of the polysufide redox couple in the electrolyte compared to that of Pt electrode according to Equation (1):where D is the diffusion coefficient of the polysulfide, l is the electrolyte thickness, n is the number of electrons involved in the reduction of disulphide at the counter electrode, F is the Faraday constant, and C is the polysulfide concentration52. These results confirm that the catalytic activity towards polysulfide redox shuttle of VASWCNTs is superior to that of conventional Pt counter electrodes. Furthermore, studies on the photovoltaic implementation of VASWCNTs counter electrodes in QDSCs are in progress in our laboratory.
In summary, we have developed VASWCNTs as efficient low-cost counter electrode material in iodine-free DSCs, featuring notably improved electrocatalytic activity towards thiolate/disulfide redox shuttle. Spectacularly, device in conjunction with VASWCNTs counter electrode demonstrates a high FF of 0.68 and PCE up to 5.25%, which is significant higher than 0.56 and 3.49% for that with a conventional Pt counter electrode. Moreover, in QDSCs system, the Rct of VASWCNTs counter electrode is as low as 21.22 Ω towards aqueous polysulfide electrolyte. This is several orders of magnitude lower than that for Pt electrode. In comparison with alternative counter electrode materials previous reported such as Au, CoS, Cu2S or PbS, to the best of our knowledge, such a Rct value is the lowest ever seen in the polysulfide electrolyte system. Therefore, the highly catalytic VASWCNTs counter electrodes are believed to be a versatile candidate for further improvement of the PCE of other iodine-free redox couple based DSCs and polysulfide electrolyte based QDSCs.
Similar to our previous work32, 10 nm thick Al2O3 film and subsequent 1 nm thick Fe film are deposited onto Si substrate. VASWCNTs growth was carried out in a water-assisted thermal CVD system at 750°C. After a quick cooling treatment, the post-growth H2/H2O vapor etch took 3~5 min at 750°C. This etch would release the chemical bonds between the nanotubes and the catalyst particles. And then the VASWCNTs were transferred onto FTO substrate by simple dry contact transfer printing53.
Conventional sputtered Pt counter electrode was prepared by an ion sputtering coater (SBC-12, KYKY Technology Development Ltd., China) for comparison. The thickness of the obtained Pt film was approximately 50 nm. DSCs devices were fabricated according to our previous reports54. Briefly, TiO2 paste composed of 18% commercial P25 nanoparticles and 9% ethyl cellulose in terpineol was used to screen printing porous TiO2 films (approximately 14 μm thick) on FTO substrate (sheet resistance: 12 Ω/square, Nippon Sheet Glass, Co., Ltd.). The obtained TiO2 electrodes were dipped into dry ethanol solution containing 5×10−4 M cis-bis(isothiocyanato) bis(2, 2′-bipyridyl-4,4′-dicarboxylato) ruthenium(II) bistetrabuyl-ammonium (N719, ruthenium TBA535, Solaronix, Switzerland) for 20 h. The dye-sensitized TiO2 electrodes, VASWCNTs and Pt counter electrodes were assembled to form DSCs by sandwiching a redox couple (T−/T2) electrolyte solution composed of 0.4 M T−, 0.4 M T2, 0.5 M 4-tertbutylpyridine, and 0.05 M LiOCl4 in acetonitrile:ethylene carbonate = 6:4, V:V). The organic redox couple (T−/T2) was synthesized by the literature method6. Aqueous polysulfide electrolyte was composed of 1 M sulfur, 1 M Na2S 9H2O, and 0.1 M NaOH in deionized water.
The morphologies of the obtained VASWCNTs were characterized by field emission scanning electron microscopy (FEI Quanta 400 ESEM, FEI, USA) and transmission electron microscopy (TEM, JEOL 2010, JEOL, Japan). Raman characterization (633 nm excitation) was performed by a Renishaw inVia Raman Microscope. To assess the corresponding catalytic performance of different counter electrodes, the Rct across the counter electrode/electrolyte interface was investigated by means of EIS with the symmetrical thin-layer cells method. The frequency range was set from 100 mHz to 1 MHz, and the amplitude of the alternating current was set to 10 mV. Tafel measurements were performed with a scanning rate of 10 mV s−1 in the potential range of 0.6 V to −0.6 V. The photocurrent-voltage (J-V) characteristics of DSCs were measured with a digital source meter (2400, Keithley Instruments, USA) under AM 1.5G illumination (100 mW cm−2), which was realized by a solar simulator (91192, Oriel, USA, calibrated with a standard crystalline silicon solar cell).
Financial Supports from the National High Technology Research and Development Program of China (863 Program, 2011AA050522), the International Cooperation S&T Cooperation Program of China (2010DFA64360), and the Welch Foundation (C-1716) are greatly appreciated. The authors thank Dr Y. Zhu for help with catalyst preparation and TEM imaging.