Abstract
The exploration of promising nonlinear optical materials, which allows for the construction of high-performance optical devices in fundamental and industrial applications, has become one of the fastest-evolving research interests in recent decades and plays a key role in the development and innovation of optics in the future. Here, by utilizing the optical nonlinearity of a recently synthesized, two dimensional material AuTe2Se4/3 prepared by the self-flux method, a passively mode-locked fiber laser operating at 1557.53 nm is achieved with 147.7 fs pulse duration as well as impressive stability (up to 91 dB). The proposed mode-locked fiber laser reveals superior overall performance compared with previously reported lasers which are more widely studied in the same band. Our work not only investigates the optical nonlinearity of AuTe2Se4/3, but also demonstrates its ultrafast photonics application. These results may stimulate further innovation and advancement in the field of nonlinear optics and ultrafast photonics.
Similar content being viewed by others
Introduction
Nonlinear optics, as an important discipline describing the interaction between light and material, has become one of the fastest-evolving scientific fields in recent decades1. In this discipline, the nonlinear response of materials to external electromagnetic field under linear field amplitude has been studied in depth. Optical nonlinearity is also the intrinsic cause of some interesting optical phenomena, such as optical rectification, Kerr effect, higher harmonics and saturable absorption2,3,4,5. It is believed that the explorations of promising nonlinear optical materials for fundamental and industrial applications play a key role in the development and innovation of optics in the future.
In recent years, femtosecond lasers, which are widely applied in micromachining6, medical operation7,8, molecular spectroscopy9,10, and optical communications11, have become good platforms for nonlinear materials to be applied effectively. After the early use of semiconductor saturable absorber mirrors, the nonlinear proof and experimental observation of graphene have aroused the upsurge of research on two dimensional (2D) materials12,13,14,15,16. Subsequently, black phosphorus17,18,19, topological insulators20,21,22 and transition metal dichalcogenides23,24,25 have been extensively studied. The high third-order optical nonlinearity, simplicity of fabrication and ultrafast excited state carrier dynamics of mentioned 2D materials have endowed them unique advantages in laser applications. Meanwhile, the research and attempt on new materials are still going on26,27,28.
Recently, a new 2D material AuTe2Se4/3 has been successfully prepared by Guo et al.29. Through the introduction of Se element, they have successfully transformed the three-dimensional disordered cubic AuTe2 phase into a 2D layered structure, and have proved that the 2D state of AuTe2Se4/3 comes from the Berezinsky-Kosterlitz-Thouless topological transition. As the main nonlinear source of optical modulators, 2D materials have a huge impact on the performance of lasers. Thus, AuTe2Se4/3 may bring about new breakthroughs and opportunities in ultrafast photonics. However, the potential applications of AuTe2Se4/3 in ultrafast photonics have not been explored yet.
In this paper, the possibility of generating mode-locked pulses by AuTe2Se4/3 is investigated by a combination of experiments and calculations, in which AuTe2Se4/3 is used as a saturable absorber (SA). By utilizing the optical nonlinearity of AuTe2Se4/3 prepared by the self-flux method, a passively mode-locked fiber laser operating at 1557.53 nm has been demonstrated, which features ultrafast pulse duration (147.7 fs) as well as impressive stability (up to 91 dB). From the comparison with previously reported lasers which are more widely studied in the same band, the overall performance of the proposed lasers is highlighted. Experimental results suggest that AuTe2Se4/3 is a kind of excellent nonlinear optical materials, and has advantages in ultrafast photonics application.
Results
Preparation and characterization
The band structure and total energy calculations of AuTe2Se4/3 are presented in Supplementary Note 1, which indicates the AuTe2Se4/3 is a metallic material with environmental stability. The process of preparation and transfer of AuTe2Se4/3 is described in Fig. 1. The detailed operation process is discussed in “Methods” section. Figure 2a shows powder x-ray diffraction pattern of AuTe2Se4/3 single crystal. Only (00 l) Bragg peaks show up, suggesting that the crystallographic c-axis is perpendicular to the plane of the single crystal. The peaks are sharp and well-defined, indicating good crystallized quality. A transmission electron microscope (TEM) image of exfoliated thin flake of AuTe2Se4/3 shows a good 2D layer of ab plane in Fig. 2b. Besides, Fig. 2c displays the high resolution TEM (HRTEM) image, and the corresponding selected-area electron diffraction (SAED) pattern is presented. The atomic intra-spacing of two perpendicular direct is about 2.8 Å, which corresponds to the interlayer spacing of (310) or (031) plane29. The chemical composition is further investigated by x-ray photoelectron spectroscopy (XPS). The Te peaks (3d5/2 at 573.30 eV, 3d3/2 at 483.74 eV), Au peaks (3f7/2 at 84.37 eV, 3f5/2 at 88.03 eV) and Se peaks (2d5/2 at 53.59 eV, 2d3/2 at 54.31 eV) can be observed in Fig. 2d. The atomic force microscopy (AFM) image of ultrasonically exfoliated thin-flake with the 5 nm thickness, which equates to the 5 layers of AuTe2Se4/3, is shown in Fig. 2e.
a the self-flux method. b the transfer process of AuTe2Se4/3.
a X-ray diffraction (XRD) pattern. b Transmission electron microscope (TEM) images. c High resolution TEM (HR-TEM) and selected-area electron diffraction (SAED) (inset) images. d x-ray photoelectron spectroscopy (XPS) of Te 3d, Au 4 f and Se 3d of the AuTe2Se4/3 crystal. e Atomic force microscopy (AFM) images of AuTe2Se4/3 saturable absorber (SA) and typical height profiles.
By using the balanced twin-detector measurement system, the saturable absorption property of the AuTe2Se4/3 SA is investigated. The schematic diagram of the balanced twin-detector measurement system is shown in Fig. 3a. The incident optical pulses come from a home-made mode-locked laser with the pulse duration of 700 fs and repetition rate of 120 MHz. The source light from the mode-locked laser is divided into two parts by a 50:50 output coupler (OC). It is worth noting that by adjusting the variable optical attenuator (VOA) before OC, the power of light passing through OC in the total channel can be changed. Half of the light divided by OC is measured directly by the detector of the power meter for reference. The other half is received by the detector after the saturable absorption of the AuTe2Se4/3 SA. Saturable absorption at a given power can be obtained by the ratio of two power channels. With the adjustment of VOA, the whole process of the SA from light absorption to light saturation in wide power range can be obtained, as shown in Fig. 3b. From the fitted absorption curves, the modulation depth of the AuTe2Se4/3 SA is about 65.58%.
a Schematic diagram of saturable absorption measurement. VOA: variable optical attenuators; OC: optical coupler. b Nonlinear transmission of the AuTe2Se4/3 saturable absorber (SA). The error of the power is ± 5% due to the uncertainty of the power monitors.
Mode-locked fiber laser
The experimental schematic design of the proposed laser, which is used to prove the optical nonlinearity of the AuTe2Se4/3 SA, is shown in Fig. 4. The erbium-doped fiber (EDF) laser is formed by the 0.6 m-long EDF (Liekki 110-4/125), a 20:80 OC, an isolator (ISO) and a polarization controller (PC). The main function of the PC is to adjust the polarization state and optimize the laser state. The AuTe2Se4/3 SA is successively placed between ISO and PC. The standard SMF-28 fibers are commonly used to make up the pigtails of all optical elements. The whole system is pumped by a commercial stabilized laser diode (LD), which operates at 980 nm and owns the maximum output power of 630 mW. The wavelength division multiplexor (WDM) is the key interface unit for guiding pumped light into the cavity. With 20% of the light output from the cavity, the working status of the laser can be observed on the oscilloscope (Tektronix DPO3054) in time. The corresponding spectra and radio frequency (RF) spectrum can be measured with the help of spectrum analyzer (Yokogawa AQ6370C) and RF spectrum analyzer (Agilent E4402B).
LD: laser diode; WDM: wavelength division multiplexor; EDF: erbium-doped fiber; OC: output coupler; PC: polarization controller; ISO: isolator.
With the coordination of the gradual increase of pump power and proper adjustment of PC, the mode-locked pulses are generated. At the pump power of 93 mW, the stable mode-locked pulses are successfully observed on oscilloscope. The round-trip time of pulses shown in Fig. 5a conforms to the fundamental frequency of 69.9 MHz. From the optical spectrum in Fig. 5b, the center wavelength of the mode-locked pulse is 1557.53 nm with the 3-dB bandwidth of 30.26 nm. As shown in Fig. 5c, the pulse duration of the mode-locked pulse is as short as 147.7 fs after the sech2 fitting. Further, the time-bandwidth product of the system is calculated as 0.5523. The RF spectrum of the pulse is shown in Fig. 5d. The signal-to-noise ratio (SNR) of the fundamental repetition rate is measured as 91 dB. Moreover, no significant interference peaks are observed in the illustrations in Fig. 5d with the wide band of 1 GHz. In other words, the mode-locked system works well with good stability. The output power of the proposed mode-locked laser versus pump power are provided in Fig. 6. The average output power of the proposed laser is 21.4 mW. When the AuTe2Se4/3 SA is removed, the mode-locked pulses could not be obtained at the same cavity. This result indicates that the optical nonlinearity of the AuTe2Se4/3 SA is the main cause of the mode-locking phenomenon. The optical damage threshold of AuTe2Se4/3 SA is about 0.169 J cm−2.
a Stable mode-locked pulse train. b Long-term monitoring for mode-locked spectrum. c Autocorrelation traces of mode-locked pulses. The error of the pulse duration is ±7 fs due to the uncertainty of the autocorrelation instrument. d Radio frequency (RF) spectrum of mode-locked pulses with resolution bandwidth of 10 Hz (the illustrations is the RF spectrum with the wide band of 1 GHz).
The error of the power is ±5% due to the uncertainty of the power monitors.
Discussion
The overall performance of the proposed laser based on the AuTe2Se4/3 SA and previously reported lasers which are more widely studied in the same band are summarized in Table 1. Modulation depth, as an important parameter reflecting the regulation ability of materials for light, has an important reference role in evaluating SA ability. It has reported that materials with large modulation depth are conducive to the formation of ultrashort pulses39. In Table 1, the modulation depth of AuTe2Se4/3 SA is up to 65.58%, which is the largest. The output power of 21. 4 mW is the highest. The SNR up to 91 dB reveals the stability of the whole mode-locked system, which is proved to be superior by comparison. In terms of the pulse duration, the proposed laser is only inferior to that of the carbon nanotube (CNT). However, considering that the absorption wavelength of the CNT is related to its diameter, it is necessary to select CNTs with different diameters in different wavelength bands. This property is not conducive to broadband applications. AuTe2Se4/3 is considered to be a metallic material after the theoretical calculation, which indicates that it has great potential in broadband absorption application. Therefore, in terms of broadband absorption characteristics and overall performance, AuTe2Se4/3 can be a strong candidate for a new generation of SAs.
In summary, the 2D material AuTe2Se4/3 has shown good prospects for saturable absorption applications in theory and experiment. The DFT calculations of AuTe2Se4/3 indicates that it is a metallic material with environmental stability. Based on the AuTe2Se4/3 SA, the mode-locked pulses have been realized in the fiber laser based on the nonlinear optical properties of AuTe2Se4/3. Besides, compared with previously reported lasers which are widely studied in the same band, the 147.7 fs pulse duration and 91 dB SNR of the proposed laser are the best. Moreover, the proposed AuTe2Se4/3 has better results in overall performance, especially in the ultrafast photonics application. This potential in ultrafast optics may stimulate further innovation and progress in related nonlinear optics and photonic applications.
Methods
Sample fabrication
By the self-flux method, AuTe2Se4/3 was successfully grown as shown in Fig. 1a. The detailed operation process is as follows. At first, three high-quality powders including Se powder (99.99%, Sigma Aldrich), Te powder (99.999%, Sigma Aldrich) and Au powder (99.99%, Sigma Aldrich) were prepared. After the stoichiometric weighting, the starting materials with a weight of 2–4 g were sealed in the evacuated silica tube with a vacuum of 10−5 mbar. Then, the sealed materials were loaded into the muffle furnace. When the materials were ready, the temperature in the furnace was increased to 800 °C and remained for 10 h. After that, the temperature in the furnace was dropped to 450 °C uniformly within 4 days, and then the furnace was turned off. As shown in Fig. 1b, 60 mg of AuTe2Se4/3 was added to 20 mL of ethanol and treated with ultrasonic for 20 min until it was completely dispersed in ethanol. Subsequently, 40 μL of the dispersion was dropped on the end face of fiber. After drying at room temperature, the AuTe2Se4/3 SA was fabricated.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request. The DOI of the data is https://doi.org/10.6084/m9.figshare.11363099.v4.
References
Boyd, R. W. in Nonlinear Optics, 3rd edn., (Academic Press, Cambridge, MA, USA, 2008).
Franken, P. A., Hill, A. E., Peters, C. W. & Weinreich, G. Generation of optical harmonics. Phys. Rev. Lett. 7, 118 (1961).
Kerr, J. L. A new relation between electricity and light: Dielectrified media birefringent. Philos. Mag. 50, 337–348 (1875).
Bass, M., Franken, P. A., Ward, J. F. & Weinreich, G. Optical rectification. Phys. Rev. Lett. 9, 446 (1962).
Colin, S., Contesse, E., Le Boudec, P., Stephan, G. & Sanchez, F. Evidence of a saturable-absorption effect in heavily erbium-doped fibers. Opt. Lett. 21, 1987–1989 (1996).
Gattass, R. R. & Mazur, E. Femtosecond laser micromachining in transparent materials. Nat. Photon. 2, 219–225 (2008).
Merker, M., Ackermann, R., Kammel, R. & Kunert, K. S. An in vitro study on focusing fs-laser pulses into ocular media for ophthalmic surgery. Laser Surg. Med. 45, 589–596 (2013).
Morin, F., Druon, F., Hanna, M. & Georges, P. Microjoule femtosecond fiber laser at 1.6 μm for corneal surgery applications. Opt. Lett. 34, 1991–1993 (2009).
Diddams, S. A., Hollberg, L. & Mbele, V. Molecular fingerprinting with the resolved modes of a femtosecond laser frequency comb. Nature 445, 627–630 (2007).
Xu, C. & Wise, F. W. Recent advances in fibre lasers for nonlinear microscopy. Nat. Photon. 7, 875–882 (2013).
De Vivie-Riedle, R. & Troppmann, U. Femtosecond lasers for quantum information technology. Chem. Rev. 107, 5082–5100 (2007).
Liverini, V. et al. Low-loss GaInNAs saturable absorber mode locking a 1.3-μm solid-state laser. Appl. Phys. Lett. 84, 4002–4004 (2004).
Keller, U. Recent developments in compact ultrafast lasers. Nature 424, 831–838 (2003).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Bao, Q. et al. Atomic-layer graphene as a saturable absorber for ultrafast pulsed lasers. Adv. Funct. Mater. 19, 3077–3083 (2009).
Sun, Z. et al. Graphene mode-locked ultrafast laser. ACS Nano 4, 803–810 (2010).
Na, D. et al. Passivation of black phosphorus saturable absorbers for reliable pulse formation of fiber lasers. Nanotechnology 28, 475207 (2017).
Rodin, A. S., Carvalho, A. & Neto, A. H. C. Strain-induced gap modification in black phosphorus. Phys. Rev. Lett. 112, 176801 (2014).
Han, C. Q. et al. Electronic structure of black phosphorus studied by angle-resolved photoemission spectroscopy. Phys. Rev. B. 90, 085101 (2014).
Yan, P., Lin, R., Ruan, S., Liu, A. J. & Chen, H. A 2.95 GHz, femtosecond passive harmonic mode-locked fiber laser based on evanescent field interaction with topological insulator film. Opt. Express 23, 154–164 (2015).
Lin, Y. H. et al. Soliton compression of the erbium-doped fiber laser weakly started mode-locking by nanoscale p-type Bi2Te3 topological insulator particles. Laser Phys. Lett. 11, 055107 (2014).
Zhang, H. et al. Topological insulators in Bi2Se3, Bi2Te3 and Sb2Te3 with a single Dirac cone on the surface. Nat. Phys. 5, 438–442 (2009).
Sotor, J. et al. Mode-locking in Er-doped fiber laser based on mechanically exfoliated Sb2Te3 saturable absorber. Opt. Mater. Express 4, 1–6 (2014).
Zhao, C. et al. Ultra-short pulse generation by a topological insulator based saturable absorber. Appl. Phys. Lett. 101, 211106 (2012).
Luo, Z. et al. 1-, 1.5-, and 2-μm fiber lasers Q-switched by a broadband few-layer MoS2 saturable absorber. J. Lightwave Technol. 32, 4077–4084 (2014).
Xu, Y. et al. Solvothermal synthesis and ultrafast photonics of black phosphorus quantum dots. Adv. Opt. Mater. 4, 1223–1229 (2016).
Jiang, X. et al. Broadband nonlinear photonics in few-layer MXene Ti3C2Tx (T = F, O, or OH). Laser Photonics Rev. 12, 1700229 (2018).
Yang, L. et al. Gold nanostars as a Q-switcher for the mid-infrared erbium-doped fluoride fiber laser. Opt. Lett. 21, 5459–5462 (2018).
Guo, J. G. et al. Quasi-two-dimensional superconductivity from dimerization of atomically ordered AuTe2Se4/3 cubes. Nat. Commun. 8, 871 (2017).
Sobon, G., Sotor, J. & Abramski, K. M. All-polarization maintaining femtosecond Er-doped fiber laser mode-locked by graphene saturable absorber. Laser Phys. Lett. 9, 581 (2012).
Wang, J. et al. Pulse dynamics in carbon nanotube mode-locked fiber lasers near zero cavity dispersion. Opt. Express 23, 9947–9958 (2015).
Chen, Y. et al. Mechanically exfoliated black phosphorus as a new saturable absorber for both Q-switching and mode-locking laser operation. Opt. Express 23, 12823–12833 (2015).
Boguslawski, J. et al. Mode-locked Er-doped fiber laser based on liquid phase exfoliated Sb2Te3 topological insulator. Laser Phys. 24, 105111 (2014).
Liu, H. et al. Femtosecond pulse generation from a topological insulator mode-locked fiber laser. Opt. Express 6, 6868–6873 (2014).
Wu, K., Zhang, X. Y., Wang, J., Li, X. & Chen, J. P. WS2 as a saturable absorber for ultrafast photonic applications of mode-locked and Q-switched lasers. Opt. Express 23, 11453–11461 (2015).
Liu, H. et al. Femtosecond pulse erbium-doped fiber laser by a few-layer MoS2 saturable absorber. Opt. Lett. 39, 4591–4594 (2014).
Luo, Z. et al. Nonlinear optical absorption of few-layer molybdenum diselenide (MoSe2) for passively mode-locked soliton fiber laser. Photonics Res. 3, A79–A86 (2015).
Mao, D. et al. Erbium-doped fiber laser passively mode locked with few-layer WSe2/MoSe2 nanosheets. Sci. Rep. 6, 23583 (2016).
Jeon, J., Lee, J. & Lee, J. H. Numerical study on the minimum modulation depth of a saturable absorber for stable fiber laser mode locking. J. Opt. Soc. Am. B. 32, 31–37 (2015).
Acknowledgements
We acknowledge the financial support from the National Natural Science Foundation of China (NSFC) (11674036; 11875008; 91850209); Beijing Youth Top-Notch Talent Support Program (2017000026833ZK08); Fund of State Key Laboratory of Information Photonics and Optical Communications (Beijing University of Posts and Telecommunications, IPOC2019ZZ01); The Fundamental Research Funds for the Central Universities (500419305); State Key Laboratory of Advanced Optical Communication Systems and Networks, Shanghai Jiao Tong University (2019GZKF03007); Beijing University of Posts and Telecommunications Excellent Ph.D. Students Foundation (CX2019202).
Author information
Authors and Affiliations
Contributions
W.L., M.Liu, X.C., and J.G. fabricated the samples. W.L., M.Liu, X.C., M.Lei and J.G. performed the measurements. X.C., M.Lei, and J.G. performed the TEM results. W.L., T.S., H.D., W.Z., C.D., and X.Z. developed the theory. W.L. and Z.W. designed the project. All authors discussed the result, and contributed to the writing of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, W., Liu, M., Chen, X. et al. Ultrafast photonics of two dimensional AuTe2Se4/3 in fiber lasers. Commun Phys 3, 15 (2020). https://doi.org/10.1038/s42005-020-0283-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s42005-020-0283-9
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.