Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Confinement of poly(allylamine) in Preyssler-type polyoxometalate and potassium ion framework for enhanced proton conductivity


Polyoxometalate based solids are promising candidates of proton-conducting solid electrolytes. In this work, a Preyssler-type polyoxometalate is crystallized with potassium ions and poly(allylamine), which is also a good proton conductor, from aqueous solutions. Here we show that the hygroscopicity induced low durability of polyoxometalate and poly(allylamine) can be circumvented by the electrostatic interaction between the polyoxometalate and protonated amine moieties in the solid state. Crystalline compounds are synthesized with poly(allylamine) of different average molecular weights, and all compounds achieve proton conductivities of 10−2 S cm−1 under mild-humidity and low-temperature conditions. Spectroscopic studies reveal that the side-chain mobility of poly(allylamine) and hydrogen-bonding network rearrangement contribute to the proton conduction of compounds with poly(allylamine) of low and high average molecular weights, respectively. While numbers of proton-conducting amorphous polyoxometalate-polymer composites are reported previously, these results show both structure-property relationship and high functionality in crystalline composites.


The performance of cation-conducting solid polymer electrolytes is key to improving the efficiency of fuel cells and secondary batteries. Nafions, which are sulfonated fluorocarbon polymers, have achieved great success commercially in polymer electrolyte fuel cells (PEFCs): Nafions show high proton conductivity (>10−2 S cm−1) under high-humidity (relative humidity (RH) 100%) and low-temperature (<373 K) conditions1. Another example is polyethylene oxides (i.e., high-molecular-weight poly(ethylene glycol)s, PEGs), which can transport cations efficiently (10−4 S cm−1) at room temperature (rt) in next-generation Li- and Na-ion secondary batteries2,3,4. However, these polymers show low durability especially at elevated temperatures, so that composites of polymers with inorganic or carbon-based materials have been fabricated and utilized5.

Polyoxometalates (POMs), which are nano-sized anionic metal-oxygen clusters of early transition metals6,7,8,9,10,11, can efficiently transport protons12,13,14,15,16 since smearing of the negative charge over the external surface oxygens makes the effective surface charge density small. In fact, it has been well known for a long time that Keggin-type acidic POMs (e.g., H3[PW12O40], H4[SiW12O40]) show high proton conductivities close to Nafions17,18,19. However, application is limited because the structural stability is low and proton conductivity largely decreases upon slight decrease in RH. To solve these problems, POMs have been hybridized with polymers20,21,22,23,24 especially with those containing amine groups, which serve as protonation sites. While these POM-polymer composites are promising candidates of future solid electrolytes, it is rather difficult to obtain relationship among composition, structure, and property because of the amorphous nature.

We have recently reported that crystalline composites of Keggin-type POMs with PEGs (POM-PEGs) show moderate proton conductivities under non-humidified and intermediate-temperature conditions25. Furthermore, we utilized a Preyssler-type [Na(H2O)P5W30O110]14− POM26, which is known to show higher acidity as acid salts than Keggin-type POMs, and the POM-PEGs showed proton conductivities of 10−4 S cm−1 under non-humidified and low-temperature conditions27. Recently, neutron diffraction and scattering measurements have revealed that a single PEG chain stays as a distorted helix in the channels of POM-PEGs, and that protons are conducted via the PEG chain performing a longitudinal motion along the channel28. The longitudinal motion of PEG is localized by the electrostatic interaction with Cs+ in the channel28. Confinement effects of PEG in nano-channels of metal-organic frameworks (MOFs) have received great attention, and it has been revealed that chemical or physical properties such as transition temperatures of confined PEGs are different from those of the bulk polymer29.

Here we show that a Preyssler-type [Bi(H2O)P5W30O110]12− POM30 with a low anion charge facilitates the migration of protons by decreasing the electrostatic interactions between POM and protons. In addition, poly(allylamine) (PAA) is utilized as a polymer because (1) amine groups contribute to increase the number of protonation sites and to extend the hydrogen-bonding network, which results in efficient proton transport and (2) PAA would be positively charged by protonation, and structural stability may improve via electrostatic interaction with POM. Isostructural crystalline composites of Preyssler-type POM with PAAs of different average molecular weights (PAA5000, 3000, and 1600) are synthesized, and the compounds show proton conductivity of 10−2 S cm−1 under mildly-humidified (RH 75%) and low-temperature (368 K) conditions. The compounds with PAA of high average molecular weights (PAA5000 and 3000) show low activation energies in proton conduction (0.16 eV and 0.24 eV) suggesting that protons conduct via rearrangement of the hydrogen-bonding network composed of water molecules and PAA (i.e., Grotthuss mechanism). On the other hand, the compound with PAA of low average molecular weight (PAA1600) shows a much higher activation energy (0.41 eV) suggesting that the side-chain mobility of PAA contributes to the proton conduction, which is confirmed by NMR spectroscopy. The importance of this work can be summarized as follows: Highly proton conductive but hygroscopic POM and PAA are stabilized via electrostatic interaction in the solid state. While there is a large number of proton-conducting amorphous POM-polymer composites exist, these crystalline composites realize both structure-property relationship and high functionality.


Crystal structure

A composite of POM and PAA5000 was crystallized in an aqueous solution. IR spectroscopy showed that the crystal contained both components (Supplementary Figure 1). The chemical formula of the crystal was determined as K8H4[Bi(H2O)P5W30O110]•0.03PAA5000•19H2O [I] by inductively coupled plasma optical emission spectrometry (ICP-OES), atomic absorption spectrometry (AAS), CHN combustion analysis, and thermogravimetry (TG) (Supplementary Figure 2). Elemental analysis of more than three different lots synthesized with different concentrations of the components in the synthetic solution well agreed with this chemical formula, showing that the chemical formula is uniquely determined and that the amounts of PAA and K+ in I is not controllable.

Single-crystal X-ray diffraction (SXRD) analysis showed that the structure of Preyssler-type POM in I agrees with the previous report (Fig. 1a, Supplementary Data 1 and Supplementary Figure 3)30: A bismuth atom (Bi(III)) with a coordination water, which are disordered between two positions, exists on the principal axis of the doughnut-shape POM with pseudo-D5h symmetry. The Bi(III) is coordinated by five phosphate oxygens (Bi-O = 2.50−2.73 Å).

Fig. 1

Schematic illustration of the synthesis and structures. a Molecular structure of Preyssler-type [Bi(H2O)P5W30O110]12− POM, and schematic illustration of the synthesis of IIII. Crystal structure (b) and void analysis (c) of I in the ab-plane. Crystal structure (d) and void analysis (e) of I in the bc-plane. Pink and purple spheres in (a), (b), and (d) show the bismuth and potassium atoms (ions), respectively. Green and gray polyhedra show the [WO6] and [PO4] units, respectively. K-O bonds within bonding distances of 3.2 Å are shown in (d). Plausible positions of PAA are shown in (c) and (e), and molecular and ionic components are omitted for the clarity. Void analysis was carried out by a Mercury structure visualization software (CCDC), and surface of the voids are shown in yellow. Black bold lines and blue spheres show the PAA backbone and amine units, respectively. Red, green, and blue lines in (c) and (e) indicate the unit cell along the a, b, and c-axis, respectively. Black broken lines in (be) are used to display multiple unit cells

Figure 1b–d show the crystal structure of I in the ab and bc-plane, respectively. Eight K+ per chemical formula (K1-K12, where K1-K4 and K5-K12 have site occupancies of 1.0 and 0.5, respectively) were located with SXRD analysis as counter cations of POM. K+ connects adjacent POMs: K1 has four bonds with POMs (K-O: 2.82−3.01 Å) and links three adjacent POMs. K2 has four bonds with POMs (K-O: 2.88−3.07 Å) and links two adjacent POMs. K3 has four bonds with POMs (K-O: 2.79−3.10 Å) and links two adjacent POMs. K4 has six bonds with POMs (K-O: 2.86−3.08 Å) and links two adjacent POMs. See Supplementary Table 2 and Supplementary Figures 3 and 4 for the details of the local arrangements of POMs with K+. POMs are arranged three-dimensionally in the crystal lattice by the aid of K+, which results in an all-inorganic framework. Void analysis (Fig. 1c, e ) shows that three-dimensional channels with a minimum aperture of ca. 4 Å were formed. The void volume of I without the water of crystallization and PAA was 14% (995 Å3, Z = 2) of the crystal lattice.

The powder X-ray diffraction (PXRD) pattern (Fig. 2b) well agreed with that calculated from the SXRD data (Fig. 2a), confirming that the crystal structure shown in Fig. 1 represents the whole bulk solid. Besides, the PXRD pattern of K12[Bi(H2O)P5W30O110]·26H2O (Fig. 2c) was different from that of I, showing that structure change occurs when PAA is accommodated in the crystal lattice. Notably, the use of allylamine monomer instead of PAA resulted in the crystallization of a solid with a different PXRD pattern (Fig. 2d), and this compound was highly soluble in water so that it is not realistic to use it as a solid electrolyte.

Fig. 2

PXRD patterns. a I (calc) with Miller indices, b I, c K12[Bi(H2O)P5W30O110]·26H2O, and d the composite of POM with allylamine monomer

States of PAA in the crystal lattice

While the position of PAA could not be resolved by SXRD, considering the size of the channel aperture, PAA probably resides along the [111] direction with the water of crystallization (see Fig. 1c–e). Packing ratio of PAA in the void was estimated with the void volume (995 Å3, Z = 2) and number of monomer units of PAA in the unit cell (5.3): Assuming that the volume of PAA monomer unit is ca. 65 Å3.31, the packing ratio is 35% (=5.3 × 65/995). Considering that water of crystallization are also contained in the channel, this estimation suggests single-chain accommodation of PAA. In addition, PLATON SQUEEZE32 has shown that there are 773 electrons per unit cell in the void. Considering that PAA (monomer unit: 57 g mol−1) amounts to 302 electrons (=5.3 × 57) per unit cell, PAA accounts for 39% (=302/773) of the electrons in the unit cell, which fairly agrees with the packing ratio. These results suggest that PAA occupies 35–40% of the contents and/or space in the void.

The number of acidic protons (H+) per chemical formula was estimated as 4 according to the number of potassium ions (8) and anion charge of POM (−12). Since the number of acidic protons (4) is larger than the number of monomer units of PAA per chemical formula (2.6), it can be reasonably assumed that the amine groups of PAA are completely protonated and PAA has become cationic, contributing to stabilize the crystal structure via electrostatic interactions.

In order to confirm the existence of PAA in the crystal lattice, Raman spectra of a single crystal of I at different vertical positions (0–30 μm beneath the crystal surface) were measured (Fig. 3)29. Bulk poly(allylamine hydrochloride) showed bands at ca. 1450 and 1350 cm−1, which can be assigned to C–N stretch and C–H deformation, respectively (Fig. 3b)33. Note that POM did not show any bands in this region (Fig. 3a). The Raman spectrum of the surface of a single crystal (= axial depth of the focal spot is 0 μm from the surface) of I showed several high-intensity bands below 1000 cm−1 and a broad band at 1300–1500 cm−1 due to POM and PAA, respectively (Fig. 3c). When the focal spot was set to 10 μm beneath the surface (Fig. 3d), the relative intensity of the broad band at 1300–1500 cm−1 increased, and this band was clearly observed when the focal spots were set deeper (Fig. 3e, f ). These results confirm the existence of PAA in the crystal lattice.

Fig. 3

Raman spectra and optical microscopic image. Raman spectra of a K12[Bi(H2O)P5W30O110]·26H2O, b poly(allylamine hydrochloride), and cf I at different vertical positions at the yellow spot of the optical microscopic image. Yellow bar shows the scale (1 mm). The axial depths of the focal spots are c 0 μm, d 10 μm, e 20 μm, and f 30 μm from the crystal surface. The intensities of (a) and (cf) were normalized with the band at ca. 970 cm−1. Note that the increase in relative intensity of the band assignable to PAA (1350–1450 cm−1) from (c) to (df) is probably due to the washing of the crystal with water prior to measurement to remove the PAA which adsorbed from the synthetic solution onto the crystal surface

Differential scanning calorimetry (DSC) measurements were performed to investigate the states of PAA in I. The DSC curve of the bulk poly(allylamine hydrochloride) showed a small endothermic peak around 380 K, which is in-line with the reported glass transition temperature (Supplementary Figure 5a, b)34. On the other hand, no obvious glass transition was observed for I (Supplementary Figure 5c). Such a phenomenon was also observed in the case of a single-chain PEG confined in the channel of a POM-PEG composite28 or a MOF29. Generally, temperature dependent glass transitions are molecular cooperative phenomena that a single polymer chain is incapable of displaying.

Proton conductivity

Figure 4a (inset) shows the Nyquist plot of the impedance spectrum at 308 K and RH 75%. The bulk proton conductivity was calculated by fitting the Nyquist plot with an electrical equivalent circuit (see Supplementary Methods). The proton conductivity of I increased with the temperature (298−368 K, Supplementary Figure 6a) and reached a very high proton conductivity of 8.5 × 10−3 S cm−1 at 368 K and RH 75%. The activation energy calculated from the Arrhenius plot of the temperature dependent proton conductivities was 0.16 eV (Fig. 4a). It is well known that the activation energy of proton conduction via hydrogen-bonding network rearrangement (Grotthuss mechanism), is about 0.2 eV or less35, and proton conduction in Nafions1 occurs by this mechanism. Notably, the proton conductivity of K12[Bi(H2O)P5W30O110]·26H2O was 3.8 × 10−3 S cm−1 (368 K and RH 75%) and smaller than that of I, and the proton conductivity of poly(allylamine hydrochloride) could not be measured because of the hygroscopicity.

Fig. 4

Proton conductivities. Arrhenius plots of the proton conductivities of a I, b II, and c III at (298–368 K and RH 75%). Nyquist plot of the impedance spectrum at 308 K (as a representative) is shown under each Arrhenius plot

Compounds with PAA of different molecular weights

Next, compounds with POM and PAA of different average molecular weights (PAA3000 and 1600) were synthesized. The chemical formula of the compounds were determined as K5H7[Bi(H2O)P5W30O110]•0.11PAA3000•16H2O [II] and K5H7[Bi(H2O)P5W30O110]•0.25PAA1600•15H2O [III]. The PXRD patterns of II (Supplementary Figure 7b) and III (Supplementary Figure 7c) fairy agreed with that of I (Fig. 2a and Supplementary Figure 7a), suggesting that the crystal structure is not affected by the average molecular weights of PAA. The amounts of PAA monomer units per chemical formula were estimated as 2.6, 5.8, and 7.0 for I, II, and III, respectively, which increased with the decrease in average molecular weights of PAA. This is probably because accommodation in the crystal lattice becomes more difficult with PAA of longer chains.

Figure 4b, c (inset) show the Nyquist plots of the impedance spectra of II and III, respectively, at 308 K and RH 75%. The proton conductivities increased with the temperature (298−368 K, Supplementary Figure 6b, c) and reached very high proton conductivities of 9.7 × 10−3 and 8.3 × 10−3 S cm−1 for II and III, respectively, at 368 K and RH 75%. The proton conductivities of IIII at 368 K and RH 75% were within 8.3–9.7 × 10−3 S cm−1, and did not depend much on the average molecular weights of PAA. However, the activation energies estimated from the Arrhenius plots were 0.24 and 0.41 eV for II and III, respectively (Fig. 4b, c), and showed large differences. According to these results, it can be reasonably assumed that proton conduction in I and II are based on Grotthuss mechanism, while that of III is probably based on vehicle mechanism, or more specifically, segmental motion of the polymer moiety (see below)25,27,28. The PXRD patterns before and after the impedance measurement were essentially the same (Supplementary Figure 8), confirming that the crystal structure is stable under this condition.

States of PAA investigated with NMR spectroscopy

Solid state magic angle spinning (MAS) NMR spectroscopy was utilized to gain insight into the states of PAA in IIII. 1H-MASNMR spectrum of I is shown in Fig. 5a. The signal at 4.3 ppm fairly agrees with the positions of protons of bulk water36 and PAA backbone (SDBSWeb #4258 allylamine:, National Institute of Advanced Industrial Science and Technology, Dec. 19th, 2018). The signal at 7.3 ppm agrees with the position of methylene protons of the PAA side-chain (SDBSWeb #4258 allylamine:, National Institute of Advanced Industrial Science and Technology, Dec. 19th, 2018). Compounds II and III gave 1H-MASNMR spectra similar to that of I (Supplementary Figure 9). Then, in order to compare the local mobility of PAA, variable contact time 13C cross-polarization MAS (13C-CPMAS) NMR spectroscopy was used. Time constants for magnetization buildup (TCH) and subsequent decay (T1ρ(H)) can be obtained according to the following equation,

$$I(t) = I_0(1 - T_{{\mathrm{CH}}}/T_{1\rho ({\mathrm{H}})})^{ - 1}\{ \exp ( - t/T_{1\rho ({\mathrm{H}})}) - \exp ( - t/T_{{\mathrm{CH}}})\}$$

where I(t) shows the intensity of the signal at contact time t, and I0 shows the theoretical maximum intensity37. T1ρ(H) can be used to semi-quantify the local mobility, which is longer if the polymer chain is more mobile38.

Fig. 5

Solid state MASNMR spectroscopy. a 1H-MASNMR (MAS = 10 KHz) and b 13C-CPMASNMR (MAS = 5 kHz, contact time = 2 ms) of I at rt. Changes in the intensities of the side-chain methylene carbon signal (44 ppm) of c I, d II, and e III with variation of contact time. In (b), (i) and (ii) show the tertiary and secondary carbons of PAA backbone, respectively, and (iii) shows the methylene carbon of PAA side-chain. Experimental and calculated (eq. 1) data are shown by the circles and solid lines, respectively. Intensities are normalized by the largest signal in each plot. Note that T(H) of poly(allylamine hydrochloride) (m = 120,000, Alfa Aesar) measured and calculated under the same experimental conditions was 3.4 ms

Figure 5b shows the solid-state 13C-CPMASNMR spectrum of I, and each signal can be reasonably assigned to each carbon moiety of PAA (SDBSWeb #4258 allylamine:, National Institute of Advanced Industrial Science and Technology, Dec. 19th, 2018). Compounds II and III gave 13C-CPMASNMR spectra similar to that of I. Figure 5ce show the changes in intensities of the methylene side-chain carbon signal of PAA in IIII, respectively, with variations of contact time (see Supplementary Figure 10 for the raw data). The intensities of the signals increased, reached maximum, and then decreased. The magnetization decay of III was much slower than those of I and II, showing that T1ρ(H) is longer and thus mobility of the methylene side-chain carbon of PAA is higher. T1ρ(H) values were estimated as 3.5, 3.6, and 9.5 ms for I, II, and III, respectively, with eq. (1). This result suggests that side-chain mobility of III with the lowest average molecular weight of PAA (i.e., PAA1600) is faster than those of higher molecular weights. It has been reported that activation energies for the side-chain mobility of polymers in the solid state are at least 0.2 eV and sometimes larger than 1 eV depending on the backbone and side-chain structures39,40. Considering that the protonated amine group resides on the side-chain of PAA and the trend in activation energies of proton conduction (I: 0.16 eV ≈ II: 0.24 eV < III: 0.41 eV), it can be concluded that the side-chain mobility of PAA is crucial to the proton conduction in III. Notably, the difference among the T1ρ(H) values of carbon atoms of PAA backbone were not so large, probably because the longitudinal motion of PAA is localized by the electrostatic interactions with K+ and POM in the channel, as in the case of POM-PEGs28.

States of water molecules investigated with IR spectroscopy

Finally, the states of water molecules in IIII were investigated with the ν(OH) bands of the in situ IR spectra under water vapor at rt (Fig. 6, see Supplementary Figures 1113 for the details). Note that the proton conductivities were in the order of 5.6 × 10−4 S cm−1 (III) < 2.1 × 10−3 S cm−1 (II) ≈ 3.3 × 10−3 S cm−1 (I) around rt (308 K) and RH 75%. Upon the introduction of water vapor, a broad band appeared around 3600–3000 cm−1 for all compounds. The band was rather sharp and a maximum was observed around 3400 cm−1 for III. On the other hand, the band extended toward the higher frequency (wavenumber) (3500–3600 cm−1) for I and II, and also toward the lower frequency (3200 cm−1) for I. Previous reports by us and other groups have shown that the bands at high (3500–3600 cm−1) and low (3200–3400 cm−1) frequencies can be attributed to unperturbed (free) water molecules at the outside of a water cluster and to perturbed hydrogen-bonded water molecules inside the cluster, respectively41,42. Therefore, it can be reasonably stated that I possesses an extensive hydrogen-bonding network of water molecules and PAA, which agrees with the relatively large number of the water of crystallization (19 (I) > 16 (II), 15 (III)), and free water molecules (protons) at the periphery of the hydrogen-bonding network.

Fig. 6

IR spectra of IIII under a water vapor pressure of 1 × 103 Pa at room temperature. a I, b II, and c III. Double-headed arrow along the y-axis shows the scale of absorbance (0.005)


According to these results, the relationship between proton conductivity and states of water molecules and PAA in the compounds can be interpreted as follows. The mobile water molecules (protons) as well as the extensive hydrogen-bonding network probably contribute to the efficient proton conduction and low activation energy of I (0.16 eV). Both the relative intensities of the IR bands at high frequencies and proton conductivities (308 K and RH 75%) were in the order of I ≈ II > III, and activation energies of proton conduction was in the order of I (0.16 eV) ≈ II (0.24 eV) < III (0.41 eV). Therefore, it can be concluded that mobile water molecules (protons) largely contribute to the efficient proton conduction and low activation energies of I and II, while water molecules are rather fixed and the side-chain mobility of PAA is crucial to the proton conduction in III.

In summary, we have shown that the low durability of POM and PAA due to hygroscopicity was circumvented by the electrostatic interaction between the POM and protonated amine moieties in the solid state, and proton conductivities of 10−2 S cm−1 were achieved under mild-humidity (RH 75%) and low-temperature (368 K) conditions. Spectroscopic studies have revealed that the side-chain mobility of PAA and hydrogen-bonding network rearrangement contribute to the proton conduction in compounds with PAA of low and high average molecular weights, respectively. We will report the states and dynamics of protons, water, and polymers in the near future.



Potassium salt of Preyssler-type POM (K12[Bi(H2O)P5W30O110]·26H2O) was synthesized according to a previously reported method30. Forty percent aqueous poly(allylamine hydrochloride) solution (m= 5000, 3000, or 1600) was provided from Nittobo Medical Co., Ltd. Allylamine hydrochloride and poly(allylamine hydrochloride) (m = 120,000) were purchased from Kanto Chemical Co. and Alfa Aesar, respectively, and used as received.


Compounds IIII were synthesized as follows: 1.0 g of K12[Bi(H2O)P5W30O110]·26H2O (0.12 mmol) was dissolved in 20 mL of H2O (solution A). Six milliliters of H2O was added to 3.0 g of 40% aqueous poly(allylamine hydrochloride) solution (m= 5000, 3000, or 1600) (solution B). Solution B was added to solution A, and the solution was left for 1 week at 278 K. Colorless crystals of IIII were obtained in ca. 70% yield. As for the synthesis of the compound with allylamine (i.e., monomer), equal amount of monomer in mole was used instead of PAA. Elemental analysis (calcd) for K8H4[Bi(H2O)P5W30O110]•0.03PAA5000•19H2O [I]: C 1.23 (1.25), H 0.59 (0.77), N 0.63 (0.48), K 3.6 (3.7), Bi 2.6 (2.5), P 2.1 (1.8), W 63 (65). Elemental analysis (calcd) for K5H7[Bi(H2O)P5W30O110]•0.11PAA3000•16H2O [II]: C 2.38 (2.50), H 0.47 (0.95), N 1.19 (0.97), K 2.3 (2.3), Bi 2.1 (2.4), P 2.1 (1.8), W 62 (64). Elemental analysis (calcd) for K5H7[Bi(H2O)P5W30O110]•0.25PAA1600•15H2O [III] C 2.98 (2.87), H 0.74 (1.04), N 1.67 (1.11), K 2.3 (2.3), Bi 2.3 (2.4), P 1.8 (1.8), W 61 (63). Elemental analysis of more than 3 different lots for each compound well agreed with these formulae.

SXRD analysis

X-ray diffraction data of I was collected at 93 K with a CCD 2-D detector by using Rigaku Saturn diffractometer with graphite monochromated Mo Kα radiation. Structures were solved by direct methods (SHELX97), expanded using Fourier techniques, and refined by full-matrix least squares against F2 with the SHELXL-2014 package. Tungsten atoms and part of the potassium atoms were refined anisotropically. Phosphorus, oxygen, bismuth, and other potassium atoms were refined isotropically. Hydrogen atoms, PAA, and water of crystallization were not included in the model. Bismuth atom was disordered between two positions with site occupancies of 0.8 and 0.2. Such disordering of central metal ions (Na+, K+, Tb3+, Eu3+) with a water molecule has been observed for several Preyssler-type POMs43,44,45. Void analysis was carried out by a Mercury structure visualization software (CCDC) with a probe radius of 2.0 Å and approximate grid spacing of 0.7 Å and PLATON SQUEEZE32. Crystal data for I: triclinic P-1 (No. 2), a = 17.80(2) Å, b = 18.018(19) Å, c = 24.68(3) Å, α = 75.28(8), β = 78.97(8), γ = 67.75(6), V = 7046(14), Z = 2, R1 = 0.1100, wR2 = 0.2880, GOF = 1.122.


Combustion analysis (Elementar, vario MICRO cube) was used for the quantitative analysis of C, H, and N. ICP-OES (Agilent Technologies, ICP-OES720) was used for the quantitative analysis of Bi, P and W. AAS (Hitachi, ZA3000) was used for the quantitative analysis of K. Prior to the ICP-OES and AAS analysis, ca. 10 mg of the solid (accurately weighed) was dispersed in 10 mL of H2O with NaOH (0.2 g) to dissolve the solid completely, conc. HNO3 (0.3 mL) was added, and the solution was diluted up to exactly 100 mL. PXRD patterns were measured with a New advance D8 X-ray diffractometer (Bruker) by using Cu Kα radiation (λ = 1.54056 Å, 40 kV−40 mA) at 2θ = 3 −20° and 1.8° min−1. Solid-state MASNMR spectra (MAS rate = 5 and 10 kHz for 13C and 1H, respectively) were recorded with an AVANCE 400WB spectrometer (Bruker), and the resonance frequencies were 100.6 and 400.2 MHz for 13C and 1H, respectively. Adamantane (1H 1.91 ppm, 13C 28.8 and 38.3 ppm) was used as an external standard for the calibration of chemical shifts. Single-pulse excitation (1H) or cross-polarization (CP) with contact times of 0.05−7.5 ms (13C) were used for the NMR measurements. Micro-Raman measurements were performed using a JASCO NRS-4500 spectrometer with an excitation wavelength of 785 nm. The beam was focused onto the sample using an optical microscope (×100 magnification), which allowed us to focus the laser beam with a 1 μm lateral resolution and an axial depth resolution of 1.5 μm. Alternating current (AC) impedance measurements: About 0.3 g of each compound was compressed at 150 kgf cm−2 into pellets of 10 mm in diameter and ca. 1.0 mm in thickness. The pellets were cut into fourths, and one-fourth of the pellet was used for the AC impedance measurement. AC impedance measurements were carried out in a temperature and humidity chamber with a BioLogic VMP3 multichannel potentiostat/galvanostat (Science Instruments) over the frequency range of 2 Hz to 2 MHz and AC amplitude of 500 mV. Gold electrodes with copper wire were attached on both faces of the pellets. Bulk conductivities were estimated by a semicircle fitting of Nyquist plots. An electrical equivalent circuit, which consists of a series of inductance (H, representing the effect of the external circuit) and three blocks of a resistance (R) and constant phase element (CPE, used for imperfect capacitors) in parallel, standing for bulk, grain boundary, and electrode interface, was used to fit the impedance spectra (see Supplementary Methods for the details). In situ IR spectra under water vapor were measured as follows: Each powder sample was deposited on a CaF2 plate (20 mm diameter), which was placed inclined at the center of an IR cell, and treated in vacuo at 298 K for 0.5 h. IR spectra were obtained at a resolution of 4 cm−1 by averaging 64 scans using a Jasco 6100 FT-IR spectrometer equipped with an MCT detector. The IR spectra of the sample in vacuum were recorded as background spectra. IR spectra of adsorbed water were measured by increasing the water vapor pressure from 5 to 1 × 103 Pa at rt, and background-subtracted IR spectra showing adsorbed water are presented throughout this paper.

Data availability

The X-ray crystallographic coordinates for the structure of compound I is available as Supplementary Tables 1 and 2. The data has also been deposited at the Cambridge Crystallographic Data Centre (CCDC) under deposition number 1856730. The data can be obtained free of charge from the CCDC via The other data that support the findings of this study are available from the corresponding author upon reasonable request.


  1. 1.

    Mauritz, K. A. & Moore, R. B. State of understanding of Nafion. Chem. Rev. 104, 4535–4546 (2004).

    CAS  Article  Google Scholar 

  2. 2.

    Quartarone, E., Mustarelli, P. & Magistris, A. PEO-based composite polymer electrolytes. Solid State Ion. 110, 1–14 (1998).

    CAS  Article  Google Scholar 

  3. 3.

    Gadjourova, Z., Andreev, Y. G., Tunstall, D. P. & Bruce, P. G. Ionic conductivity in crystalline polymer electrolytes. Nature 412, 520–523 (2001).

    CAS  Article  Google Scholar 

  4. 4.

    Li, Y. et al. Enhancing sodium-ion battery performance with interlayer-expanded MoS2-PEO nanocomposites. Nano Energy 15, 453–461 (2015).

    Article  Google Scholar 

  5. 5.

    Meng, X., Wang, H. -N., Song, S. -Y. & Zhang, H. -J. Proton-conducting crystalline porous materials. Chem. Soc. Rev. 46, 464–480 (2017).

    CAS  Article  Google Scholar 

  6. 6.

    Pope, M. T. & Müller, A. Polyoxometalate chemistry: an old field with new dimensions in several disciplines. Angew. Chem. Int. Ed. 30, 34–48 (1991).

    Article  Google Scholar 

  7. 7.

    Hill, C. L. Stable, self-assembling, equilibrating catalysts for green chemistry. Angew. Chem. Int. Ed. 43, 402–404 (2004).

    CAS  Article  Google Scholar 

  8. 8.

    Izarova, N. V., Pope, M. T. & Kortz, U. Noble metals in polyoxometalates. Angew. Chem. Int. Ed. 51, 9492–9510 (2012).

    CAS  Article  Google Scholar 

  9. 9.

    Busche, C. et al. Design and fabrication of memory devices based on nanoscale polyoxometalate clusters. Nature 515, 545–549 (2014).

    CAS  Article  Google Scholar 

  10. 10.

    Zhang, Z. et al. Ultrathin inorganic molecular nanowire based on polyoxometalates. Nat. Commun. 6, 7731 (2015).

    Article  Google Scholar 

  11. 11.

    Seino, S., Kawahara, R., Ogasawara, Y., Mizuno, N. & Uchida, S. Reduction-induced highly selective uptake of cesium ions by an ionic crystal based on silicododecamolybdate. Angew. Chem. Int. Ed. 55, 3987–3991 (2016).

    CAS  Article  Google Scholar 

  12. 12.

    Ma, H. et al. Cationic covalent organic frameworks: a simple platform of anionic exchange for porosity tuning and proton conduction. J. Am. Chem. Soc. 138, 5897–5903 (2016).

    CAS  Article  Google Scholar 

  13. 13.

    Ye, Y. et al. Straightforward loading of imidazole molecules into metal–organic framework for high proton conduction. J. Am. Chem. Soc. 139, 15604–15607 (2017).

    CAS  Article  Google Scholar 

  14. 14.

    Cao, X. -L. et al. A well-established POM-based single-crystal proton-conducting model incorporating multiple weak interactions. Chem. Eur. J. 24, 2365–2369 (2018).

    CAS  Article  Google Scholar 

  15. 15.

    Liu, J. -C. et al. Aggregation of giant cerium-bismuth tungstate clusters into a 3D porous framework with high proton conductivity. Angew. Chem. Int. Ed. 57, 8416–8420 (2018).

    CAS  Article  Google Scholar 

  16. 16.

    Yang, P., Alsufyani, M., Emwas, A. -H., Chen, C. & Khashab, N. M. Lewis acid guests in a {P8W48} archetypal polyoxotungstate host: enhanced proton conductivity via metal-oxocluster within cluster assemblies. Angew. Chem. Int. Ed. 57, 13046–13051 (2018).

    CAS  Article  Google Scholar 

  17. 17.

    Nakamura, O., Kodama, T., Ogino, I. & Miyake, Y. High-conductivity solid proton conductors: dodecamolybdophosphoric acid and dodecatungstophosphoric acid crystals. Chem. Lett. 8, 17–18 (1979).

  18. 18.

    Xie, Z., Wu, H., Wu., Q. & Ai, L. Synthesis and performance of solid proton conductor molybdovanadosilicic acid. RSC Adv. 8, 13984–13988 (2018).

    CAS  Article  Google Scholar 

  19. 19.

    Xie, Z., Wu, Q., He, F. & Ai, L. Synthesis and conductive performance of quaternary heteropoly acid H5SiW9Mo2VO40•13H2O. Funct. Mater. Lett. 11, 1850065 (2018).

    CAS  Article  Google Scholar 

  20. 20.

    Tong, X. et al. Preparation and electrochemical performance of tungstovanadophosphoric heteropoly acid and its hybrid materials. J. Phys. Chem. C. 117, 3258–3263 (2013).

    CAS  Article  Google Scholar 

  21. 21.

    Zhang, L. et al. Inorganic-macroion-induced formation of bicontinuous block copolymer nanocomposites with enhanced conductivity and modulus. Angew. Chem. Int. Ed. 56, 9013–9017 (2017).

    CAS  Article  Google Scholar 

  22. 22.

    Lai, X. et al. Controllable proton-conducting pathways via situating polyoxometalates in targeting pores of a metal-organic framework. J. Mater. Chem. A 5, 9611–9617 (2017).

    CAS  Article  Google Scholar 

  23. 23.

    Miao, J. et al. Proton conducting polyoxometalate/polypyrrole films and their humidity sensing performances. ACS Appl. Nano Mater. 1, 564–571 (2018).

    CAS  Article  Google Scholar 

  24. 24.

    Wu, H., Wu, X., Wu, Q. & Yan, W. High performance proton-conducting composite based on vanadium-substituted Dawson-type heteropoly acid for proton exchange membranes. Compos. Sci. Technol. 162, 1–6 (2018).

    CAS  Article  Google Scholar 

  25. 25.

    Tsuboi, M., Hibino, M., Mizuno, N. & Uchida, S. Crystalline polyoxometalate (POM)–polyethylene glycol (PEG) composites aimed as non-humidified intermediate-temperature proton conductors. J. Solid State Chem. 234, 9–14 (2016).

    CAS  Article  Google Scholar 

  26. 26.

    Sadakane, M., Ichi, Y., Ide, Y. & Sano, T. Thermal stability and acid strength of Preyssler-type phosphotungstic acid, H14[P5W30O110Na] and it’s catalytic activity for hydroxylation of alkyl acetate. Z. Anorg. Allg. Chem. 637, 2120–2124 (2011).

    CAS  Article  Google Scholar 

  27. 27.

    Niinomi, K., Miyazawa, S., Hibino, M., Mizuno, N. & Uchida, S. High proton conduction in crystalline composites based on Preyssler-type polyoxometalates and polymers under non-humidified or humidified conditions. Inorg. Chem. 56, 15187–15193 (2017).

    CAS  Article  Google Scholar 

  28. 28.

    Wu, H. et al. Spatial-temporal characteristics of confined PEG motion determine proton conduction of polyoxometalate-PEG hybrid nanocomposites. J. Phys. Chem. Lett. 9, 5572–5777 (2018).

    Google Scholar 

  29. 29.

    Uemura, T. et al. Unveiling thermal transitions of polymers in subnanometre pores. Nat. Commun. 1, 83 (2010).

    PubMed  Google Scholar 

  30. 30.

    Hayashi, A. et al. Cation effect on formation of Preyssler-type 30-tungsto-5-phosphate: enhanced yield of Na-encapsulated derivative and direct synthesis of Ca- and Bi-encapsulated derivatives. Z. Anorg. Allg. Chem. 641, 2670–2676 (2015).

    CAS  Article  Google Scholar 

  31. 31.

    Zhao, Y. H., Abraham, M. H. & Zissimos, A. M. Fast calculation of van der Waals volume as a sum of atomic and bond contributions and its application to drug compounds. J. Org. Chem. 68, 7368–7373 (2003).

    CAS  Article  Google Scholar 

  32. 32.

    Spek, A. L. PLATON SQUEEZE: a tool for the calculation of the disordered solvent contribution to the calculated structure factors. Acta Cryst. C. 71, 9–18 (2015).

    CAS  Article  Google Scholar 

  33. 33.

    Zucolotto, V. et al. Unusual interactions binding iron tetrasulfonated phthalocyanine and poly(allylamine hydrochloride) in layer-by-layer films. J. Phys. Chem. B 107, 3733–3737 (2003).

    CAS  Article  Google Scholar 

  34. 34.

    Shao, L. & Lutkenhaus, J. L. Thermochemical properties of free-standing electrostatic layer-by-layer assemblies containing poly(allylamine hydrochloride) and poly(acrylic acid). Soft Matter 6, 3363–3369 (2010).

    CAS  Article  Google Scholar 

  35. 35.

    Kreuer, K. D. Proton conductivity: materials and applications. Chem. Mater. 8, 610–641 (1996).

    CAS  Article  Google Scholar 

  36. 36.

    Gottlieb, H. E., Kotlyar, V. & Nudelman, A. NMR chemical shifts of common laboratory solvents as trace impurities. J. Org. Chem. 62, 7512–7515 (1997).

    CAS  Article  Google Scholar 

  37. 37.

    Fyfe, C. A., Diaz, A. C., Grondey, H., Lewis, A. R. & Förster, H. Solid state NMR method for the determination of 3D zeolite framework/sorbate structures:1H/29Si CP MAS NMR study of the high-loaded form of p-xylene in ZSM-5 and determination of the unknown structure of the low-loaded form. J. Am. Chem. Soc. 127, 7543–7558 (2005).

    CAS  Article  Google Scholar 

  38. 38.

    Naik, V. V. & Vasudevan, S. Effect of alkyl chain arrangement on conformation and dynamics in a surfactant intercalated layered double hydroxide: spectroscopic measurements and MD simulations. J. Phys. Chem. C. 115, 8221–8232 (2011).

    CAS  Article  Google Scholar 

  39. 39.

    Mccreight, K. W. et al. Phase structures and transition behaviors in polymers containing rigid rodlike backbones with flexible side chains. V. Methylene side-chain effects on structure and molecular motion in a series of polyimides. J. Polym. Sci. B Polym. Phys. 37, 1633–1646 (1999).

    CAS  Article  Google Scholar 

  40. 40.

    Ryu, S. -Y., Chung, J. W. & Kwak, S. -Y. Probing the role of side-chain interconnecting groups in the structural hydrophobicity of comblike fluorinated polystyrene by solid state NMR spectroscopy. Langmuir 31, 9473–9482 (2015).

    CAS  Article  Google Scholar 

  41. 41.

    Jentys, A., Warecka, G., Derewinski, M. & Lercher, J. A. Adsorption of water on ZSM 5 zeolites. J. Phys. Chem. 93, 4837–4843 (1989).

    CAS  Article  Google Scholar 

  42. 42.

    Uchida, S. et al. Proton conduction in alkali metal ion-exchanged porous ionic crystals. Phys. Chem. Chem. Phys. 19, 29077–29083 (2017).

    CAS  Article  Google Scholar 

  43. 43.

    Lu, Y., Li, Y., Wang, E., Xu, X. & Ma, Y. A new family of polyoxometalate compounds built up of Preyssler anions and trivalent lanthanide cations. Inorg. Chim. Acta 360, 2063–2070 (2007).

    CAS  Article  Google Scholar 

  44. 44.

    Hu, T.-P. et al. Four hybrid materials based on Preyssler P5W30 polyoxometalate and first-row transition-metal complex. Inorg. Chem. 54, 7415–7423 (2015).

    CAS  Article  Google Scholar 

  45. 45.

    Kato, C. et al. Giant Hysteretic Single-Molecule Electric Polarisation Switching above Room Temperature. Angew. Chem. Int. Ed. 57, 13429–13432 (2018).

    CAS  Article  Google Scholar 

Download references


This work was supported by JST-PRESTO (JPMJPR1312) and grant-in-aids for scientific research JP16K05742 and JP17H05356 (Coordination Asymmetry) from MEXT of Japan. Prof. M. Matsuo and Dr. K. Shozugawa (Univ. of Tokyo) are acknowledged for providing access to the ICP instrument.

Author information




T.I., S.M., and S.U. designed and carried out the experiments, and wrote the manuscript. R.O. and J.N.K. designed and performed the in situ IR measurements. K.H., T.K., and T.U. designed and performed the DSC and Raman measurements.

Corresponding author

Correspondence to Sayaka Uchida.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Iwano, T., Miyazawa, S., Osuga, R. et al. Confinement of poly(allylamine) in Preyssler-type polyoxometalate and potassium ion framework for enhanced proton conductivity. Commun Chem 2, 9 (2019).

Download citation


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.