The extraction of water from air is a promising way to supply fresh water, especially in remote, arid regions. This process can be supported by desiccant materials such as zeolites, metal−organic frameworks, or hygroscopic salts. Here we present a composite material that is able to absorb 660 kg of water per cubic meter of bulk material from air at 10 mbar water vapor pressure and 28 °C. The material consists of calcium chloride incorporated into an alginate-derived matrix. A simple synthesis route leads to spherical beads of the composite with a diameter of approximately 2 mm. This macroscopic structure allows for good vapor permeability through packed beds. The collected water can be released at 100 °C, potentially enabling a solar-driven application. In addition, the synthetic route uses cheap, non-toxic, and easily accessible materials allowing for widespread application.
It is estimated that around four billion people on the globe suffer from water scarcity1. Distribution and production of fresh water and the control over water sources are a potential cause for conflicts. Therefore, new ways of fresh water production and improvement of existing techniques are the focus of current research. The utilization of water from lakes and rivers, the exploitation of rainfall runoff and the desalination of salt water are being used extensively to cover the demand of fresh water2. Particularly, the desalination of seawater requires high initial investment cost and is mainly feasible on large scale in coastal areas, making it inaccessible for remote regions and decentralized allocation. The use of atmospheric water as source of fresh water has been investigated extensively, but is still underdeveloped3,4,5,6,7,8,9,10,11,12,13,14,15,16,17. There are two general options for water harvesting from air: 1) Ambient air can be cooled below its dew point and the condensed liquid water can be collected. Large volumes of air and low temperatures at the condenser are required, especially in regions of low relative humidity (r.h.). The cooling of the heat sink for the condensation can be energy consumptive, since a difference in temperature between the condensation unit and the ambience has to be maintained. Additionally, the heat of condensation of the collected water has to be discharged. 2) Humidity can be adsorbed or absorbed (taken up) by desiccant materials, and in a second step desorbed at elevated temperatures followed by condensation of the hot water vapor at ambient conditions. Usually water is taken up during the colder nighttime when the relative humidity is higher and desorbed during daytime. The necessary heat for desorption is ideally provided by solar radiation. The resulting heated water vapor can be brought below its dew point and condensed at ambient temperatures, making an energy expansive auxiliary heat sink redundant. When the ambient air is used as coolant, a sufficient airstream has to be maintained to reject the heat of condensation. Applications for dew point water collection and fog capturing have been presented, but they require high relative humidities, usually above 50%3,4,5,6,7,8,9. Those conditions are usually found in regions that offer other possibilities for fresh water production such as water extraction from lakes, rivers or oceans. Only a few applications have been presented that are able to harvest water from air at relative humidity below 30%. These conditions are especially interesting because regions where the relative humidity is low usually offer no efficient ways for fresh water production. Hygroscopic salts10,11,12, zeolites13, porous silica-based materials14 like MCM-4115, carbon based composites16 or metal-organic frameworks17, such as MOF-80118, are capable of taking up water at relative humidities below 25%. The adsorption of water on zeolite surfaces at low humidities is accompanied by high adsorption enthalpies of more than 70 kJ mol−1, requiring temperatures above 150 °C for the desorption, making this process energy consumptive17,19. MOFs, such as MOF-801, can readily absorb water from air at around 10% relative humidity and are able to release it at temperatures below 100 °C. The major problem of materials that harvest water through adsorption on the material surface is the low gravimetric water uptake of around 25 wt.%18,20. However, there are exceptions such as a MOF based on cobalt ions and a bis(1H-1,2,3-triazolo[4,5-b],[4’,5’-i])dibenzo[1,4]dioxin) (BTDD) linker that, shows a water uptake of around 80 wt.% at 25 °C and 30% relative humidity21. Up untill now, it has been proven difficult to synthesize most of the suitable MOFs on a scale that allows for significant, cost-efficient water production. Apart from water harvesting through adsorption on the surface, it is possible to harvest water through absorption, e.g., hydration of salts. One of the most promising salts is calcium chloride because of its excellent water sorption properties in combination with a natural and industrial abundance. The salt is able to absorb more than 95% of its own weight in water for the reaction of the anhydrous salt to the hexahydrate. However, hygroscopic salts face the problem of particle agglomeration during hydration, which reduces the gas permeability. Additionally, passivation layers can be formed on the surface of the salt particles, which reduces the absorption capability. Composites of matrix materials that can adsorb water on their surface and hygroscopic salts that absorb water through hydration reactions have shown promising results15,16,22,23. The salt is distributed within the matrix to prevent agglomeration while at the same time increasing the amount of water that can be taken up by the composite. A general problem for pristine, as well as composite materials is the macroscopic structuring. Ideally, a material should be prepared, which can be packed in beds or columns that are penetrable by air with a low pressure loss and high volumetric, as well as gravimetric water sorption capacity.
Here, we present an approach for the encapsulation of CaCl2 into a polymer-based matrix for water harvesting purposes. A facile ionotropic gelation method is used to synthesize composite beads in the size of around 2 mm. Sodium alginic acid is chosen as basis for the matrix because of the excellent features of alginate-based hydrogels in terms of macroscopic shaping24. In addition, alginates are a cheap, as well as non-toxic biomaterial that has been utilized in various applications25,26,27,28.
Synthesis and characterization
In the present approach, a CaCl2 solution is used as a Ca2+ source for the ionotropic gelation of a sodium alginic acid solution (see Fig. 1). Droplets of the alginate solution form spherical hydrogel beads upon contact with the gelation solution that contains Ca2+ ions. After the initial hydrogel formation, Ca2+ and Cl− ions from the gelation solution diffuse into the hydrogel spheres until an equilibrium of the salt concentration between the CaCl2 solution and the hydrogel is reached. Upon drying of the hydrogel, CaCl2 precipitates within the alginate-derived matrix and a composite is formed. The spherical shape of the hydrogel can be maintained throughout the drying process leading to the generation of spherical beads of an alginate-derived matrix with incorporated CaCl2. The size of the composite beads can be altered by the droplet size. The amount of incorporated salt can be adjusted by the concentration of the CaCl2 solution. Here we used beads in the size of around 2 mm in diameter to obtain a balance between high packing density, easy vapor transport through the packed bed, and limited diffusion length within the individual beads. The final composite, referred to as Alg-CaCl2, contains 76 wt.% of salt. This is higher than the amount of salt that can be incorporated through conventional impregnation of matrices, which usually ranges from 30 to 58 wt.-% in the case of silica-based materials15,18,22, and can reach up to 68 wt.% in the case of MOFs29.
Figure 2 shows scanning electron microscope (SEM) images of the dried composite. A porous structure was obtained with pores in the range from 1 µm to more than 10 µm in diameter. The performed cyclisation experiments indicate that the hydration of the incorporated salt is possible in a timeframe of 12 h. This leads to the conclusion, that the pores allow diffusion of water vapor within the individual beads. Salt particles cannot be observed in the SEM, indicating a fine distribution of the salt within the matrix. The presence of CaCl2 within the composite was proven by energy dispersive X-Ray spectroscopy (EDX) and X-Ray diffraction (XRD) measurements (see Supplementary Fig. 1 and Supplementary Fig. 2).
Water sorption performance
Three aspects are of major importance for water harvesting materials: 1) The material has to adsorb or absorb large amounts of water with respect to weight and/or volume, 2) the harvesting of water should be possible at low relative humidities, and 3) the water should be released at low temperatures. Different experiments were performed to investigate the absorption and desorption behavior of the composite. Additionally, the material was subjected to multiple cycles of water uptake and release to prove the stability of the composite.
Figure 3a shows water sorption isotherms of the fully dehydrated material at 28, 65, and 85 °C. The water vapor pressure was stepwise increased. The hydration to the hexahydrate is directly followed by the deliquescence (formation of a solution) of the salt above around 10 mbar water vapor pressure at 28 °C. At 65 °C and 30 mbar of water vapor pressure a water uptake of 17 wt.% was observed. No mentionable water uptake could be observed at 85 °C. Equilibration times for the data points were set to 600 min below 13 mbar and to 150 min above 13 mbar. The equilibration time for the desorption is set to 150 min throughout the whole measurement. The hysteresis between absorption and desorption is attributed to the short equilibration times that do not allow the system to reach the equilibrium state during desorption. The gain in mass at 10 mbar of 100% translates to a bulk capacity of 0.66 g cm−3 (grams of water per volume composite) in a packed bed at 28 °C. Even at 7.5 mbar water vapor pressure, the material is able to absorb 70% of its own weight in water. Under comparable conditions, MOF-80118 is only able to adsorb approx. 30% of its own weight in water, and zeolite 13X17 adsorbs approx. 38% of its own weight. Pristine CaCl2 is theoretically able to absorb 97% of its own weight in water for the hydration to the hexahydrate. However, this is accompanied by agglomeration and a poor permeability of packed beds when the salt is used as bulk.
There are several interesting composite materials with good gravimetric water harvesting capacity as shown in Table 1. The highest water uptake of almost 200 wt.% was achieved with the MOF Cr-soc-MOF-1, however the material only absorbs water above 50% relative humidity, making it unsuitable for water harvesting in arid climates30. A very promising candidate for water harvesting has recently been published by Rieth et al. A Cobalt based MOF with a BTDD linker showed water uptake of around 80 wt.% at 25 °C and 30% relative humidity (9.5 mbar water vapor pressure)21. It was presented that the harvested water can be released at 45 °C making a solar driven application feasible. A volumetric capacity of 0.60 g cm−3 (grams of water per volume MOF) was calculated from the crystal density. This value is expected to be reduced significantly in a packed bed. In addition, the MOF incorporates a cobalt salt and a dioxin linker, which might be reason for concern regarding fresh water quality. Moreover, it has to be considered that the synthetic approach is more complicated and the price of the cobalt based MOF is significantly higher than the CaCl2 based material presented here.
The dry composite beads of Alg-CaCl2 exhibit a bulk density of 0.66 g cm−3. Figure 3a shows that 1.0 g of water are absorbed per gram of composite at 10 mbar water vapor pressure at 28 °C. It is, therefore, possible to harvest 660 kg of water per cubic meter of the composite material in a packed bed in one cycle.
Figure 3b shows the thermogravimetric analysis (TGA) of the fully hydrated material with a heating rate of 1 °C min−1. The dehydration behavior of Alg-CaCl2 is almost identical to the dehydration behavior of pure CaCl2⋅6H2O. Dehydration under the investigated conditions is complete at 150 °C and results in the formation of anhydrous CaCl2. The temperature that is required for the desorption of the water from the desiccant material has a major influence on the energy demand of the application. The required temperature directly influences the capital expenditure and the engineering complexity to build a solar system to provide the heat. A lower desorption temperature usually goes along with a cheaper setup.
The composite Alg-CaCl2 was hydrated and dehydrated repeatedly to investigate cyclisation behavior (see Fig. 4). One hydration/dehydration cycle consists of 4 steps: 1) Absorption of water at 30 °C and 25% relative humidity (10.6 mbar water vapor pressure) for 12 h, 2) heating to the desorption temperature under dry nitrogen with a heating rate of 2 °C min−1, 3) holding time at the desorption temperature for 12 h and 4) cooling down to 30 °C with a cooling rate of approx. 1 °C min−1 and equilibration for 2 h. The dehydration of the composite after the first cycle is not complete. Approx. 6% of the adsorbed water cannot be desorbed under the investigated conditions. The second cycle proves that the absorbed amount of water is still extremely high and that cyclisation is possible with approx. 75 wt.% of water taken up by the material. The experiment has been repeated with slightly different conditions to prove the stability over 8 cycles (see Supplementary Fig. 3).
It has to be noted that the desorption process was performed in dry nitrogen, which does not fully represent application conditions, where ambient air is heated up to desorb the water. In an open system, the desorption behavior is dependent on ambient air temperature and humidity, and has to be investigated according to the respective climate of the intended location of the application.
A composite material for water harvesting consisting of an alginate-derived matrix and large amounts of incorporated CaCl2 was presented, which can be obtained as spherical beads through a facile synthesis route. The spherical structure promotes good gas permeability of packed beds. The presented material is able to adsorb 100% of its own weight in water from air at a water vapor pressure of 10 mbar, which makes it promising for application in arid climate zones. The high water uptake indicated that the incorporated salt is accessible for water vapor, which is attributed to the micro pores of the matrix. More than 90% of the adsorbed water can be released at 100 °C and complete desorption can be achieved at 150 °C. These temperatures can be provided by solar radiation, e.g., vacuum solar tubes. The results show that the presented material is an interesting candidate for water harvesting applications.
The macroscopic structure may allow an application in packed columns. Ambient air can be lead through the material at night to allow for water absorption with a low pressure loss and therefore little energy consumption. At daytime, the temperature of the packed bed can be increased by solar heat and the released water can be condensed at ambient temperature. Calculations from the bulk density of the material and the water uptake indicate that 660 kg of water could be harvested per cubic meter of composite material in a packed bed. We believe that this work may inspire researchers to use the presented material for prototype development to advance in the field of water harvesting from air towards large-scale application.
TGA was performed on a Jupiter STA 449 F3 from Netzsch GmbH and Co KG with a STA/DTA sample holder and Al2O3 crucibles. Water sorption isotherms were recorded on a SPSx-1µ Advanced from proUmid GmbH and Co. KG at 23 °C. SEM Images were taken on NTS LEO-1525 from Carl Zeiss company. The samples were coated with a carbon layer by vapor deposition. All experiments were conducted with samples that were dried at 130 °C.
Analysis of the salt content
The ground composite was dried at 130 °C, extracted with water and filtered. The filtrate was subjected to ICP-OES (inductively coupled plasma optical emission spectrometry) to investigate the salt content. The concentration of Ca2+ and Cl− in the filtrate is measured and the amount of CaCl2 in the composite calculated.
Cyclisation of the composites
The material was stored at 130 °C and loaded into a Jupiter STA 449 F3 from Netzsch GmbH and Co KG equipped with a humidity generator from proumid GmbH and Co. KG in a modified Al2O3 crucible (see Supplementary Fig. 4). The airflow was set to 100 ml min−1 of nitrogen for all steps. The material was heated to 100 °C for 5 h for full dehydration prior to the experiment. The resulting mass at 30 °C was defined as starting mass.
Analysis of the water sorption and desorption
The material was stored at 130 °C and loaded into a Jupiter STA 449 F3 from Netzsch GmbH & Co KG equipped with a humidity generator from proumid GmbH and Co. KG in a modified Al2O3 crucible (see Supplementary Fig. 4). The airflow was set to 100 ml min−1 of nitrogen for all steps. The material was heated to the respective temperature (28 or 85 °C) and the humidity was stepwise increased. Equilibration times were set to 600 min below 13 mbar water vapor pressure and to 150 min above 13 mbar water vapor pressure for the absorption. The equilibration time was set to 150 min for the desorption.
Synthesis of the composites
Alg-CaCl2 was synthesized using a solution of sodium alginic acid (4.00 g in 200 mL of water) that was added to a solution of CaCl2 (290.00 g in 400 mL water) dropwise. Droplets were produced with an Encapsulator B390 from Büchi Labortechnik GmbH using a 1000 µm nozzle. The hydrogel spheres were left in the CaCl2 solution for 12 h, filtered, washed with water and dried at 140 °C for 20 h to obtain the final composite Alg-CaCl2.
The data that support the findings of this study are available from the corresponding author on reasonable request.
Mekonnen, M. M. & Hoekstra, A. Y. Four billion people facing severe water scarcity. Sci. Adv. 2, e1500323 (2016).
Shatat, M. & Riffat, S. B. Water desalination technologies utilizing conventional and renewable energy sources. Int. J. Low. Carbon Technol. 9, 1–19 (2014).
Wahlgren, R. V. Atmospheric water vapour processor designs for portable water production: a review. Water Res. 35, 1–22 (2001).
Muselli, M. et al. Dew water collector for portable water in Ajaccio (Corsica Island, France). Atmos. Res. 64, 297–312 (2002).
Clus, O., Ortega, P., Muselli, M., Milimouk, I. & Beysens, D. Study of dew water collection in humid tropical islands. J. Hydrol. 361, 159–171 (2008).
Lee, A., Moon, M. W., Lim, H., Kim, W. D. & Kim, H. Y. Water harvest via dewing. Langmuir 28, 10183–10191 (2012).
Schemenauer, R. S. & Cereceda, P. A Proposed standard fog collector for use in high-elevation regions. J. Appl. Meteorol. 33, 1313–1322 (1994).
Klemm, O. et al. Fog as a fresh-water resource: overview and perspectives. Ambio 41, 221–234 (2012).
Park, K. C., Chhatre, S. S., Srinivasan, S., Cohen, R. E. & McKinley, G. H. Optimal design of permeable fibre network structure for fog harvesting. Langmuir 29, 13269–13277 (2013).
Kabeel, A. E. Water production from air using multi-shelves solar glass pyramid system. Renew. Energy 32, 157–172 (2007).
Gad, H. E., Hamed, A. M. & El-Sharkawy, I. I. Application of a solar desiccant/collector system for water recovery from atmospheric air. Renew. Energy 22, 541–556 (2001).
William, G. E., Mohamed, M. H. & Fatouh, M. Desiccant system for water production from humid air using solar energy. Energy 90, 1707–1720 (2015).
Casey, S. P., Elvins, J., Riffat, S. & Robinson, A. Salt impregnated desiccant matrices for ‘open’ thermochemical energy storage–selection, synthesis and characterization of candidate materials. Energ. Build. 84, 412–425 (2014).
Courbon, E. et al. A new composite sorbent based on SrBr2 and silica gel for solar energy storage application with high energy storage density and stability. Appl. Energy 190, 1184–1194 (2017).
Ji, J. G., Wang, R. Z. & Li, L. X. New composite adsorbent for solar-driven fresh water production from the atmosphere. Desalination 212, 176–182 (2007).
Wang, J. Y., Liu, J. Y., Wang, R. Z. & Wang, L. W. Experimental research of composite solid sorbents for fresh water production driven by solar energy. Appl. Therm. Eng. 121, 941–950 (2017).
Furukawa, H. et al. Water adsorption in porous metal-oragnic frameworks and related materials. J. Am. Chem. Soc. 136, 4369–4381 (2014).
Kim, H. et al. Water harvesting from air with metal-organic frameworks powered by natural sunlight. Science 365, 430–434 (2017).
Barreneche, C., Fernández, A. I., Cabeza, L. F. & Cuypers, R. Thermophysical charcterizastion of sorption TCM. Energy Procedia 48, 273–279 (2014).
Whiting, G. T., Grondin, D., Stosic, D., Bennici, S. & Auroux, A. Zeolite-MgCl2 composites as potential long-term heat storage materials: influence of zeolite properties on heat of water sorption. Sol. Energy Mater. Sol. Cells 128, 289–295 (2014).
Rieth, A. J., Yang, S., Wang, E. N. & Dincǎ, M. Record atmospheric fresh water capture and heat transfer with a material operating at the water uptake reversibility limit. ACS Cent. Sci. 3, 668–672 (2017).
Aristov, Y. I., Tokarev, M. M., Gordeeva, L. G., Snytnikov, V. N. & Parmon, V. N. New composite sorbent for solar-driven technology of fresh water production from the atmosphere. Sol. Energy 66, 165–168 (1999).
Gordeeva, L. G., Tokarev, M. M., Parmon, V. N. & Aristov, Y. I. Selective water sorbents for multiple application, 6. freshwater production from the atmosphere. React. Kinet. Catal. Lett. 65, 153–159 (1998).
Braccini, I. & Pérez, S. Molecular basis of Ca2+-induced gelation in alginates and pectins: the egg-box model revisited. Biomacromolecules 2, 1089–1096 (2001).
Gibbs, B. F., Kermasha, S., Alli, I. & Mulligan, C. N. Encapsulation in the food industry: a review. Int. J. Food Sci. Nutr. 50, 213–224 (1999).
George, M. & Abraham, T. E. Polyionic hydrocolloids for the intestinal delivery of protein drugs: Alginate and chitosan - a review. J. Control. Release 114, 1–14 (2006).
Lee, K. Y. & Mooney, D. J. Alginate: properties and biomedical applications. Prog. Polym. Sci. 37, 106–126 (2012).
Augst, A. D., Kong, H. J. & Mooney, D. J. Alginate hydrogels as biomaterials. Macromol. Biosci. 6, 623–633 (2006).
Permyakova, A. et al. Design of salt–metal organic framework composites for seasonal heat storage applications. J. Mater. Chem. A 5, 12889–12898 (2017).
Abtab, S. M. T. et al. Reticular chemistry in action: a hydrolytically stable MOF capturing twice its weight in adsorbed water. Chem 4, 94–105 (2017).
Tso, C. Y. & Chao, C. Y. H. Activated carbon, silica-gel and calcium chloride composite adsorbents for energy efficient solar adsorption cooling and dehumidification systems. Int. J. Refrig. 35, 1626–1638 (2012).
Many thanks to Renate Walter and Dr. Frank Friedrich from the University of Hamburg for taking numerous SEM images of our samples. We also thank Uta Sazama, Isabelle Nevoigt, and Kirsten Linnow from the University of Hamburg for the TGA, XRD, and water sorption measurements. Furthermore, we would like to thank Dr. Frank Hoffmann for the helpful discussions and the scientific support. This study is financed by the BMBF (Bundesministerium für Bildung und Forschung), as part of the project ThessaPor in Germany (Förderkennzeichen: 03EK3019A and 03EK3019B).
P.A.K., M.F., Michael Steiger, Felix Brieler, Konrad Posern, the University of Weimar and the University of Hamburg filed a German patent application (Kompositmaterial zur Speicherung von Wasser und/oder Wärme, DE 10 2017 109 618.3) pertaining to the presented synthesis and materials.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
About this article
Cite this article
Kallenberger, P.A., Fröba, M. Water harvesting from air with a hygroscopic salt in a hydrogel–derived matrix. Commun Chem 1, 28 (2018). https://doi.org/10.1038/s42004-018-0028-9
Environmentally adaptive MOF-based device enables continuous self-optimizing atmospheric water harvesting
Nature Communications (2022)
Scientific Reports (2022)
Topics in Current Chemistry (2022)
Effect of the composition stoichiometry and salt on the ammonia sensing properties of curcumin-loaded polyelectrolyte complex membranes
Polymer Bulletin (2022)
Fabrication of magnetic multi-template molecularly imprinted polymer composite for the selective and efficient removal of tetracyclines from water
Frontiers of Environmental Science & Engineering (2021)