Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Tuning OH binding energy enables selective electrochemical oxidation of ethylene to ethylene glycol


There is significant interest in developing efficient electrochemical processes for commodity chemical manufacturing, all directly powered by renewable electricity. A vital chemical is ethylene glycol, with an annual consumption of around 20 million tonnes due to its use as antifreeze and as a polymer precursor. Here we report a one-step electrochemical route at ambient temperature and pressure in aqueous media to the selective partial oxidation of ethylene to ethylene glycol. Tuning of the catalyst OH binding energy was hypothesized to be crucial for facilitating the transfer of OH to *C2H4OH to form ethylene glycol. Computational studies suggested that a gold-doped palladium catalyst could perform this step efficiently, and experimentally we found it to exhibit an approximate 80% Faradaic efficiency to ethylene glycol, retaining its performance for 100 hours of continuous operation. These findings represent a significant advance in the development of selective anodic partial oxidation reactions in aqueous media under mild conditions.

This is a preview of subscription content, access via your institution

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: An electrochemical route to ethylene glycol.
Fig. 2: Electron microscopy characterization and ethylene oxidation using the Pd DNT and commercial Pd/C catalysts.
Fig. 3: Investigation of the activation process involving the Pd DNT catalyst.
Fig. 4: Cyclic voltammetry experiments.
Fig. 5: Density functional theory calculations for ethylene oxidation to ethylene glycol.
Fig. 6: Characterization and bulk electrolysis testing of PdAu DNT catalyst.

Data availability

The data that support the findings of this study are available from the corresponding author on reasonable request.


  1. Annual Energy Review 2011 (U.S. Energy Information Administration, 2012).

  2. IPCC Climate Change 2014: Synthesis Report (eds Core Writing Team, Pachauri, R. K. & Meyer L. A.) (IPCC, 2014).

  3. Chu, S., Cui, Y. & Liu, N. The path towards sustainable energy. Nat. Mater. 16, 16–22 (2017).

    Article  Google Scholar 

  4. Davidson, D. J. Exnovating for a renewable energy transition. Nat. Energy 4, 254–256 (2019).

    Article  Google Scholar 

  5. Tackett, B. M., Gomez, E. & Chen, J. G. Net reduction of CO2 via its thermocatalytic and electrocatalytic transformation reactions in standard and hybrid processes. Nat. Catal. 2, 381–386 (2019).

    Article  CAS  Google Scholar 

  6. Vogt, C., Monai, M., Kramer, G. J. & Weckhuysen, B. M. The renaissance of the Sabatier reaction and its applications on Earth and in space. Nat. Catal. 2, 188–197 (2019).

    Article  CAS  Google Scholar 

  7. De Luna, P. et al. What would it take for renewably powered electrosynthesis to displace petrochemical processes? Science 364, eaav3506 (2019).

    Article  Google Scholar 

  8. Orella, M. J., Román-Leshkov, Y. & Brushett, F. R. Emerging opportunities for electrochemical processing to enable sustainable chemical manufacturing. Curr. Opin. Chem. Eng. 20, 159–167 (2018).

    Article  Google Scholar 

  9. Sherbo, R. S., Delima, R. S., Chiykowski, V. A., MacLeod, B. P. & Berlinguette, C. P. Complete electron economy by pairing electrolysis with hydrogenation. Nat. Catal. 1, 501–507 (2018).

    Article  CAS  Google Scholar 

  10. Bondue, C. J., Calle-Vallejo, F., Figueiredo, M. C. & Koper, M. T. M. Structural principles to steer the selectivity of the electrocatalytic reduction of aliphatic ketones on platinum. Nat. Catal. 2, 243–250 (2019).

    Article  CAS  Google Scholar 

  11. Winiwarter, A. et al. Towards an atomistic understanding of electrocatalytic partial hydrocarbon oxidation: propene on palladium. Energy Environ. Sci. 12, 1055–1067 (2019).

    Article  CAS  Google Scholar 

  12. Huang, X., Zhang, Q., Lin, J., Harms, K. & Meggers, E. Electricity-driven asymmetric Lewis acid catalysis. Nat. Catal. 2, 34–40 (2019).

    Article  CAS  Google Scholar 

  13. Wang, A. & Zhang, T. One-pot conversion of cellulose to ethylene glycol with multifunctional tungsten-based catalysts. Acc. Chem. Res. 46, 1377–1386 (2013).

    Article  CAS  Google Scholar 

  14. Rebsdat, S. & Mayer, D. in Ullmann’s Encyclopedia of Industrial Chemistry (Wiley-VCH, 2000).

  15. Bio-Mono Ethylene Glycol (MEG) from Renewable Source An India Glycols Limited Case StudyInternational Council of Chemical Associations, 2017);

  16. Verma, S., Lu, S. & Kenis, P. J. A. Co-electrolysis of CO2 and glycerol as a pathway to carbon chemicals with improved technoeconomics due to low electricity consumption. Nat. Energy 4, 466–474 (2019).

  17. Jirkovský, J. S., Busch, M., Ahlberg, E., Panas, I. & Krtil, P. Switching on the electrocatalytic ehene epoxidation on nanocrystalline RuO2. J. Am. Chem. Soc. 133, 5882–5892 (2011).

    Article  Google Scholar 

  18. Goodridge, F. & King, C. J. H. Oxidation of ethylene at a palladium electrode. Trans. Faraday Soc. 66, 2889–2896 (1970).

    Article  CAS  Google Scholar 

  19. Šebera, J., Hoffmannová, H., Krtil, P., Samec, Z. & Záliš, S. Electrochemical and density functional studies of the catalytic ethylene oxidation on nanostructured Au electrodes. Catal. Today 158, 29–34 (2010).

    Article  Google Scholar 

  20. Holbrook, L. L. & Wise, H. Electrooxidation of olefins at a silver electrode. J. Catal. 38, 294–298 (1975).

    Article  CAS  Google Scholar 

  21. Calle-Vallejo, F., Loffreda, D., Koper, M. T. M. & Sautet, P. Introducing structural sensitivity into adsorption–energy scaling relations by means of coordination numbers. Nat. Chem. 7, 403–410 (2015).

    Article  CAS  Google Scholar 

  22. Huang, Y.-F., Kooyman, P. J. & Koper, M. T. M. Intermediate stages of electrochemical oxidation of single-crystalline platinum revealed by in situ Raman spectroscopy. Nat. Commun. 7, 12440 (2016).

    Article  CAS  Google Scholar 

  23. D’Acapito, F., Davoli, I., Ghigna, P. & Mobilio, S. The refiEXAFS station at the GILDA beamline (BM08) of ESRF. J. Synchrotron Radiat. 10, 260–264 (2003).

    Article  Google Scholar 

  24. Long, N. V. et al. The development of mixture, alloy, and core-shell nanocatalysts with nanomaterial supports for energy conversion in low-temperature fuel cells. Nano Energy 2, 636–676 (2013).

    Article  Google Scholar 

  25. Chen, C.-H. et al. Architecture of Pd–Au bimetallic nanoparticles in sodium bis(2-ethylhexyl)sulfosuccinate reverse micelles as investigated by X-ray absorption spectroscopy. ACS Nano 1, 114–125 (2007).

    Article  CAS  Google Scholar 

  26. Kaiser, J. et al. The structure of AuPd nanoalloys anchored on spherical polyelectrolyte brushes determined by X-ray absorption spectroscopy. Faraday Discuss. 162, 45–55 (2013).

    Article  CAS  Google Scholar 

  27. Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synch. Rad. 12, 537–541 (2005).

    Article  CAS  Google Scholar 

  28. Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).

    Article  CAS  Google Scholar 

  29. Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).

    Article  CAS  Google Scholar 

  30. Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).

    Article  CAS  Google Scholar 

  31. Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal–amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251–14269 (1994).

    Article  CAS  Google Scholar 

  32. Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    Article  CAS  Google Scholar 

  33. Mathew, K., Sundararaman, R., Letchworth-Weaver, K., Arias, T. A. & Hennig, R. G. Implicit solvation model for density-functional study of nanocrystal surfaces and reaction pathways. J. Chem. Phys. 140, 084106 (2014).

    Article  Google Scholar 

  34. Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).

    Article  Google Scholar 

  35. Nørskov, J. K. et al. Origin of the overpotential for oxygen reduction at a fuel-cell cathode. J. Phys. Chem. B 108, 17886–17892 (2004).

    Article  Google Scholar 

Download references


This material is based upon work supported by the Ontario Research Fund Research Excellence Program, the Natural Sciences and Engineering Research Council (NSERC) of Canada and the CIFAR Bio-Inspired Solar Energy program. The authors thank Z. Finfrock and D. M. Meira for technical support at the 20BM beamline of the Advanced Photon Source (Lemont, IL). This research used resources of the Advanced Photon Source, an Office of Science User Facility operated for the US Department of Energy (DOE) Office of Science by Argonne National Laboratory and was supported by the US DOE under Contract No. DE-AC02-06CH11357 and the Canadian Light Source and its funding partners. We acknowledge S. Fakra and the use of Beamline 10.3.2 at the Advanced Light Source for the collection of XAS data. The authors thank C. Andrei of the Canadian Centre for Electron Microscopy (CCEM) for TEM analysis. D.S. acknowledges the NSERC for an E. W. R. Steacie Memorial Fellowship. J.L. acknowledges the Banting Postdoctoral Fellowships program. All DFT computations were performed on the IBM BlueGene/Q supercomputer with support from the Southern Ontario Smart Computing Innovation Platform (SOSCIP) and Niagara supercomputer at the SciNet HPC Consortium. SOSCIP is funded by the Federal Economic Development Agency of Southern Ontario, the Province of Ontario, IBM Canada Ltd, Ontario Centres of Excellence, Mitacs and 15 Ontario academic member institutions. SciNet is funded by: the Canada Foundation for Innovation, the Government of Ontario, Ontario Research Fund—Research Excellence and the University of Toronto. We acknowledge the Ontario Centre for the Characterization of Advanced Materials (OCCAM) for characterization facilities.

Author information

Authors and Affiliations



E.H.S. supervised the project. Y.L. and E.H.S. conceived the idea and designed the experiments. Y.L. and J.E.H. carried out all the experimental work. Y.L. performed the DFT calculations. Z.W. supervised the DFT calculations. Y.L. and W.R.L. performed the TEA. M.L. carried out some of the TEM measurements. B.C. analysed the TEM results. Y.L. and D.H.N. carried out XAS measurements. Y.L. and J.L. analysed the XAS data. J.W. performed the XPS measurements. D.H.N carried out PXRD measurements. Y.C.L. and Y.W. performed SEM measurements. C.-T.D., T.-T.Z., F.L., T.-K.S. and D.S. contributed to data analysis and manuscript editing. Y.L. and E.H.S. co-wrote the manuscript. All authors discussed the results and assisted during the manuscript preparation.

Corresponding author

Correspondence to Edward H. Sargent.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figures 1–39, Tables 1–5, Notes 1–3 and references.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Lum, Y., Huang, J.E., Wang, Z. et al. Tuning OH binding energy enables selective electrochemical oxidation of ethylene to ethylene glycol. Nat Catal 3, 14–22 (2020).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing