Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Structural selectivity of supported Pd nanoparticles for catalytic NH3 oxidation resolved using combined operando spectroscopy


The selective catalytic oxidation of NH3 to N2 presents a promising solution for the abatement of unused NH3-based reductants from diesel exhaust after treatment. Supported Pd nanoparticle catalysts show selectivity to N2 rather than NOx, which is investigated in this work. The link between Pd nanoparticle structure and surface reactivity was found using operando X-ray absorption fine structure spectroscopy, diffuse reflectance infrared Fourier-transformed spectroscopy and on-line mass spectrometry. Nitrogen insertion into the metallic Pd nanoparticle structure at low temperatures (<200 °C) was found to be responsible for high N2 selectivity, whereas the unfavourable formation of NO is linked to adsorbed nitrates, which form at the surface of bulk PdO nanoparticles at high temperatures (>280 °C). Our work demonstrates the ability of combined operando spectroscopy and density functional theory calculations to characterize a previously unidentified PdNx species, and clarify the selectivity-directing structure of supported Pd catalysts for the selective catalytic oxidation of NH3 to N2.

Access options

Rent or Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: Catalytic activity of supported Pd catalysts for NH3 oxidation at increasing temperatures.
Fig. 2: In situ Pd L3-edge XANES spectra of 1.5 wt% Pd/γ-Al2O3 in different gas environments.
Fig. 3: Operando Pd K-edge XANES and EXAFS spectra of Pd/γ-Al2O3 under different reaction conditions.
Fig. 4: Operando Pd K-edge XANES spectra of 1.5 wt% Pd/γ-Al2O3 under different reaction conditions.
Fig. 5: Operando DRIFTS spectrum of 1.5 wt% Pd/γ-Al2O3 during NH3 oxidation.

Data availability

The data that support the findings of this study are available from the University of Southampton repository with the identifier, or from the authors upon reasonable request.


  1. 1.

    Sobczyk, D. P., Hensen, E. J. M., de Jong, A. M. & van Santen, R. A. Low-temperature ammonia oxidation over Pt/γ-alumina: the influence of the alumina support. Top. Catal. 23, 109–117 (2003).

    CAS  Article  Google Scholar 

  2. 2.

    Weststrate, C. J., Bakker, J. W., Gluhoi, A. C., Ludwig, W. & Nieuwenhuys, B. E. Ammonia oxidation on Ir(1 1 1): why Ir is more selective to N2 than Pt. Catal. Today 154, 46–52 (2010).

    CAS  Article  Google Scholar 

  3. 3.

    Hung, C.-M. Characterization and performance of Pt–Pd–Rh cordierite monolith catalyst for selectivity catalytic oxidation of ammonia. J. Hazard. Mat. 180, 561–565 (2010).

    CAS  Article  Google Scholar 

  4. 4.

    Gang, L., Anderson, B. G., van Grondelle, J. & van Santen, R. A. Low temperature selective oxidation of ammonia to nitrogen on silver-based catalysts. Appl. Catal. B 40, 101–110 (2003).

    CAS  Article  Google Scholar 

  5. 5.

    Burch, R. & Southward, B. W. L. The nature of the active metal surface of catalysts for the clean combustion of biogas containing ammonia. J. Catal. 198, 286–295 (2001).

    CAS  Article  Google Scholar 

  6. 6.

    Carabineiro, S. A. C., Matveev, A. V., Gorodetskii, V. V. & Nieuwenhuys, B. E. Selective oxidation of ammonia over Ru(0 0 0 1). Surf. Sci. 555, 83–93 (2004).

    CAS  Article  Google Scholar 

  7. 7.

    Carabineiro, S. A. C. & Nieuwenhuys, B. E. Selective oxidation of ammonia over Ir(5 1 0). Comparison with Ir(1 1 0). Surf. Sci. 532–535, 87–95 (2003).

    Article  Google Scholar 

  8. 8.

    Qi, G., Gatt, J. E. & Yang, R. T. Selective catalytic oxidation (SCO) of ammonia to nitrogen over Fe-exchanged zeolites prepared by sublimation of FeCl3. J. Catal. 226, 120–128 (2004).

    CAS  Article  Google Scholar 

  9. 9.

    Qi, G. & Yang, R. T. Selective catalytic oxidation (SCO) of ammonia to nitrogen over Fe/ZSM-5 catalysts. Appl. Catal. A 287, 25–33 (2005).

    CAS  Article  Google Scholar 

  10. 10.

    Long, R. Q. & Yang, R. T. Superior ion-exchanged ZSM-5 catalysts for selective catalytic oxidation of ammonia to nitrogen. Chem. Commun. 0, 1651–1652 (2000).

    CAS  Article  Google Scholar 

  11. 11.

    Gang, L., van Grondelle, J., Anderson, B. G. & van Santen, R. A. Selective low temperature NH3 oxidation to N2 on copper-based catalysts. J. Catal. 186, 100–109 (1999).

    CAS  Article  Google Scholar 

  12. 12.

    Chmielarz, L., Kuśtrowski, P., Rafalska-Łasocha, A. & Dziembaj, R. Selective oxidation of ammonia to nitrogen on transition metal containing mixed metal oxides. Appl. Catal. B 58, 235–244 (2005).

    CAS  Article  Google Scholar 

  13. 13.

    Lee, S. M. & Hong, S. C. Promotional effect of vanadium on the selective catalytic oxidation of NH3 to N2 over Ce/V/TiO2 catalyst. Appl. Catal. B 163, 30–39 (2015).

    CAS  Article  Google Scholar 

  14. 14.

    Il‘chenko, N. I. Catalytic oxidation of ammonia. Russ. Chem. Rev. 45, 1119 (1976).

    Article  Google Scholar 

  15. 15.

    Chmielarz, L. & Jablonska, M. Advances in selective catalytic oxidation of ammonia to dinitrogen: a review. RSC Adv. 5, 43408–43431 (2015).

    CAS  Article  Google Scholar 

  16. 16.

    Barbier, J. Jr, Oliviero, L., Renard, B. & Duprez, D. Catalytic wet air oxidation of ammonia over M/CeO2 catalysts in the treatment of nitrogen-containing pollutants. Catal. Today 75, 29–34 (2002).

    CAS  Article  Google Scholar 

  17. 17.

    Li, P., Zhang, R., Liu, N. & Royer, S. Efficiency of Cu and Pd substitution in Fe-based perovskites to promote N2 formation during NH3 selective catalytic oxidation (NH3-SCO). Appl. Catal. B 203, 174–188 (2017).

    CAS  Article  Google Scholar 

  18. 18.

    Lousteau, C., Besson, M. & Descorme, C. Catalytic wet air oxidation of ammonia over supported noble metals. Catal. Today 241, 80–85 (2015).

    CAS  Article  Google Scholar 

  19. 19.

    Jabłońska, M. et al. Zeolite Y modified with palladium as effective catalyst for selective catalytic oxidation of ammonia to nitrogen. J. Catal. 316, 36–46 (2014).

    Article  Google Scholar 

  20. 20.

    Li, Y. & Armor, J. N. Selective NH3 oxidation to N2 in a wet stream. Appl. Catal. B. 13, 131–139 (1997).

    Article  Google Scholar 

  21. 21.

    Nilsson, J. et al. Chemistry of supported palladium nanoparticles during methane oxidation. ACS Catal. 5, 2481–2489 (2015).

    CAS  Article  Google Scholar 

  22. 22.

    Tew, M. W., Janousch, M., Huthwelker, T. & van Bokhoven, J. A. The roles of carbide and hydride in oxide-supported palladium nanoparticles for alkyne hydrogenation. J. Catal. 283, 45–54 (2011).

    CAS  Article  Google Scholar 

  23. 23.

    Khan, N. A., Shaikhutdinov, S. & Freund, H. J. Acetylene and ethylene hydrogenation on alumina supported Pd–Ag model catalysts. Catal. Lett. 108, 159–164 (2006).

    CAS  Article  Google Scholar 

  24. 24.

    Tew, M. W., Nachtegaal, M., Janousch, M., Huthwelker, T. & van Bokhoven, J. A. The irreversible formation of palladium carbide during hydrogenation of 1-pentyne over silica-supported palladium nanoparticles: in situ Pd K and L3 edge XAS. Phys. Chem. Chem. Phys. 14, 5761–5768 (2012).

    CAS  PubMed  Article  Google Scholar 

  25. 25.

    Zhang, L., Zhang, C. & He, H. The role of silver species on Ag/Al2O3 catalysts for the selective catalytic oxidation of ammonia to nitrogen. J. Catal. 261, 101–109 (2009).

    CAS  Article  Google Scholar 

  26. 26.

    Bugaev, A. L. et al. In situ formation of hydrides and carbides in palladium catalyst: when XANES is better than EXAFS and XRD. Catal. Today 283, 119–126 (2017).

    CAS  Article  Google Scholar 

  27. 27.

    Lin, C.-M. et al. Size-dependent lattice structure of palladium studied by X-ray absorption spectroscopy. Phys. Rev. B 75, 125426 (2007).

    Article  Google Scholar 

  28. 28.

    Beale, A. M. & Weckhuysen, B. M. EXAFS as a tool to interrogate the size and shape of mono and bimetallic catalyst nanoparticles. Phys. Chem. Chem. Phys. 12, 5562–5574 (2010).

    CAS  PubMed  Article  Google Scholar 

  29. 29.

    Soldatov, A. V., Della Longa, S. & Bianconi, A. Relevant role of hydrogen atoms in the XANES of Pd hydride: evidence of hydrogen induced unoccupied states. Solid State Commun. 85, 863–868 (1993).

    CAS  Article  Google Scholar 

  30. 30.

    Ruckman, M. W. et al. XANES study of hydrogen incorporation in a Pd-capped Nb thin film. Phys. Rev. B 57, 3881–3886 (1998).

    CAS  Article  Google Scholar 

  31. 31.

    Tew, M. W., Miller, J. T. & van Bokhoven, J. A. Particle size effect of hydride formation and surface hydrogen adsorption of nanosized palladium catalysts: L3 edge vs K edge X-ray absorption spectroscopy. J. Phys. Chem. C 113, 15140–15147 (2009).

    CAS  Article  Google Scholar 

  32. 32.

    Veith, G. M. et al. Evidence for the formation of nitrogen-rich platinum and palladium nitride nanoparticles. Chem. Mater. 25, 4936–4945 (2013).

    CAS  Article  Google Scholar 

  33. 33.

    Briggs, D. Book Review: Handbook of X-ray spectroscopy. Surf. Interface Anal. 3, 190 (1981).

    Google Scholar 

  34. 34.

    Rogers, S. M. et al. Tandem site- and size-controlled Pd nanoparticles for the directed hydrogenation of furfural. ACS Catal. 7, 2266–2274 (2017).

    CAS  Article  Google Scholar 

  35. 35.

    Wang, H. & Agmon, N. Complete assignment of the infrared spectrum of the gas-phase protonated ammonia dimer. J. Phys. Chem. A 120, 3117–3135 (2016).

    CAS  PubMed  Article  Google Scholar 

  36. 36.

    Liu, F. et al. Novel MnWOx catalyst with remarkable performance for low temperature NH3-SCR of NOx. Catal. Sci. Technol. 3, 2699–2707 (2013).

    CAS  Article  Google Scholar 

  37. 37.

    Zhang, L. & He, H. Mechanism of selective catalytic oxidation of ammonia to nitrogen over Ag/Al2O3. J. Catal. 268, 18–25 (2009).

    CAS  Article  Google Scholar 

  38. 38.

    Amores, J. G., Escribano, V. S., Ramis, G. & Busca, G. An FT-IR study of ammonia adsorption and oxidation over anatase-supported metal oxides. Appl. Catal. B 13, 45–58 (1997).

    Article  Google Scholar 

  39. 39.

    Carré, S., Dujardin, C. & Granger, P. Operando infrared spectroscopy of the reduction of NO by H2 over rhodium based catalysts. Catal. Today 191, 59–64 (2012).

    Article  Google Scholar 

  40. 40.

    Zhanpeisov, N. U. et al. Interaction of N2O with Ag+ ion-exchanged zeolites: an FT-IR spectroscopy and quantum chemical ab initio and DFT studies. J. Mol. Catal. A 201, 237–246 (2003).

    CAS  Article  Google Scholar 

  41. 41.

    Wcław, A., Nowińska, K., Schwieger, W. & Zielińska, A. N2O decomposition over iron modified zeolites ZSM-5. Catal. Today 90, 21–25 (2004).

    Article  Google Scholar 

  42. 42.

    Zhang, X., He, H., Gao, H. & Yu, Y. Experimental and theoretical studies of surface nitrate species on Ag/Al2O3 using DRIFTS and DFT. Spectrochim. Acta A 71, 1446–1451 (2008).

    Article  Google Scholar 

  43. 43.

    Müslehiddinoğlu, J. & Vannice, M. A. Adsorption of NO on promoted Ag/α-Al2O3 catalysts. J. Catal. 217, 442–456 (2003).

    Article  Google Scholar 

  44. 44.

    Underwood, G. M., Miller, T. M. & Grassian, V. H. Transmission FT-IR and Knudsen cell study of the heterogeneous reactivity of gaseous nitrogen dioxide on mineral oxide particles. J. Phys. Chem. A 103, 6184–6190 (1999).

    CAS  Article  Google Scholar 

  45. 45.

    Caravaggio, G., Nossova, L. & Burich, R. Influence of supports on Pd catalysts for the selective catalytic reduction of NOxwith H2 and CO. Emiss. Control Sci. Technol. 2, 10–19 (2016).

    CAS  Article  Google Scholar 

  46. 46.

    Thompson, P. B. J. et al. X-ray spectroscopy for chemistry in the 2-4 keV energy regime at the XMaS beamline: ionic liquids, Rh and Pd catalysts in gas and liquid environments, and Cl contamination in [gamma]-Al2O3. J. Synchotron. Radiat. 22, 1426–1439 (2015).

    Article  Google Scholar 

  47. 47.

    Gibson, E. K. et al. Restructuring of AuPd nanoparticles studied by a combined XAFS/DRIFTS approach. Chem. Mater. 27, 3714–3720 (2015).

    CAS  Article  Google Scholar 

  48. 48.

    Dann, E. K. et al. Combined in situ XAFS/DRIFTS studies of the evolution of nanoparticle structures from molecular precursors. Chem. Mater. 29, 7515–7523 (2017).

    CAS  Article  Google Scholar 

  49. 49.

    Marinkovic, N. S. et al. Combined in situ X-ray absorption and diffuse reflectance infrared spectroscopy: an attractive tool for catalytic investigations. Nucl. Instrum. Methods Phys. Res. A 649, 204–206 (2011).

    CAS  Article  Google Scholar 

  50. 50.

    Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).

    CAS  Article  Google Scholar 

  51. 51.

    Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal–amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251–14269 (1994).

    CAS  Article  Google Scholar 

  52. 52.

    Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).

    CAS  Article  Google Scholar 

  53. 53.

    Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).

    Article  Google Scholar 

  54. 54.

    Kresse, G., Marsman, M. & Furthmuller, J. Vienna ab initio simulation package (VASP) (2018)

  55. 55.

    Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    CAS  PubMed  Article  Google Scholar 

  56. 56.

    Makov, G. & Payne, M. Periodic boundary conditions in ab initio calculations. Phys. Rev. B 51, 4014–4022 (1995).

    CAS  Article  Google Scholar 

  57. 57.

    Neugebauer, J. & Scheffler, M. Adsorbate–substrate and adsorbate–adsorbate interactions of Na and K adlayers on Al(111). Phys. Rev. B 46, 16067–16080 (1992).

    CAS  Article  Google Scholar 

  58. 58.

    Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).

    PubMed  Article  Google Scholar 

  59. 59.

    Henkelman, G., Uberuaga, B. P. & Jónsson, H. Climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).

    CAS  Article  Google Scholar 

  60. 60.

    Henkelman, G. & Jónsson, H. Improved tangent estimate in the nudged elastic band method for finding minimum energy paths and saddle points. J. Chem. Phys. 113, 9978–9985 (2000).

    CAS  Article  Google Scholar 

Download references


We acknowledge UCL and the EPSRC for the iCASE studentship of E.K.D; the beamline scientists at the Swiss Light Source and staff at the Paul Scherrer Institut for the provision of beamtime (proposal 20160396); and the beamline scientists at XMaS, European Synchrotron Radiation Facility, for the provision of beamtime (experiment 28-01-1213). XMaS is a UK national facility supported by EPSRC. We recognize staff at the University of Warwick and University of Liverpool for support in facilitating the beamtime. We also acknowledge the RCaH for the use of facilities, and Johnson Matthey for providing catalyst precursor materials and testing facilities. We thank the UK Catalysis Hub for resources and support provided via our membership of the UK Catalysis Hub Consortium (portfolio grants EP/K014706/1, EP/K014668/1, EP/K014854/1, EP/K014714/1 and EP/I019693/1). Via our membership of the UK’s HEC Materials Chemistry Consortium, which is funded by the EPSRC (EP/L000202), this work used the ARCHER UK National Supercomputing service ( We acknowledge the use of Athena at HPC Midlands+, which was funded by the EPSRC (grant EP/P020232/1), in this research, via the EPSRC RAP call of spring 2018. We also thank HPC Wales for the computing time.

Author information




The experiments on SuperXAS were performed by P.P.W., E.K.D., E.K.G., R.H.B., M.N. and A.G. The experiments on XMaS at the European Synchrotron Radiation Facility were performed by P.P.W., E.K.D., G.F.T., P.T. and S.M.R. The catalysts were prepared by E.K.D. and A.R., with routine characterization performed by E.K.D. The X-ray absorption spectroscopy data were interpreted by P.P.W., E.K.D., A.K. and E.K.G. XPS measurements were performed and analysed by E.K.D., S.F.R.T. and T.E.E. The computational work was performed by A.C. and C.D.Z.-Y. The work was conceived and designed by P.P.W., C.R.A.C., A.G., P.C. and C.H. The manuscript was written by P.P.W., E.K.D., A.C. and A.G.

Corresponding authors

Correspondence to Alexandre Goguet or Peter P. Wells.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figures 1–22; Supplementary Tables 1–10; Supplementary Note 1

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Dann, E.K., Gibson, E.K., Blackmore, R.H. et al. Structural selectivity of supported Pd nanoparticles for catalytic NH3 oxidation resolved using combined operando spectroscopy. Nat Catal 2, 157–163 (2019).

Download citation

Further reading


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing