Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Sustaining metal–organic frameworks for water–gas shift catalysis by non-thermal plasma

Abstract

The limited thermal and water stability of metal–organic frameworks (MOFs) often restricts their applications in conventional catalysis that involve thermal treatment and/or use of water. Non-thermal plasma (NTP) is a promising technique that can overcome barriers in conventional catalysis. Here we report an example of an NTP-activated water–gas shift reaction (WGSR) over a MOF (HKUST-1). Significantly, the exceptional stability of HKUST-1 was sustained under NTP activation and in the presence of water, which led to a high specific rate of 8.8 h−1. We found that NTP-induced water dissociation has a twofold promotion effect in WGSR, as it facilitates WGSR by supplying OH and sustains the stability and hence activity of HKUST-1. In situ characterization of HKUST-1 revealed the critical role of open Cu sites in the binding of substrate molecules. This study paves the way to utilize MOFs for a wider range of catalysis.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Effect of Ar NTP treatment on HKUST-1.
Fig. 2: Catalytic WGSR by thermal and NTP activation.
Fig. 3: In situ DRIFTS characterization.
Fig. 4: Comparison of the pristine and used HKUST-1 by power XRD and N2 physisorption.

Similar content being viewed by others

Data availability

All the figures presented in this paper are associated with raw data. The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.

References

  1. Yaghi, O. M. & Li, H. Hydrothermal synthesis of a metal–organic framework containing large rectangular channels. J. Am. Chem. Soc. 117, 10401–10402 (1995).

    Article  CAS  Google Scholar 

  2. Corma, A. et al. Engineering metal organic frameworks for heterogeneous catalysis. Chem. Rev. 110, 4606–4655 (2010).

    Article  CAS  Google Scholar 

  3. Rowsell, J. L. C. & Yaghi, O. M. Metal–organic frameworks: a new class of porous materials. Microporous Mesoporous Mater. 73, 3–14 (2004).

    Article  CAS  Google Scholar 

  4. Peterson, V. K. et al. Neutron powder diffraction study of D2 sorption in Cu3(1,3,5-benzenetricarboxylate)2. J. Am. Chem. Soc. 128, 15578–15579 (2006).

    Article  CAS  Google Scholar 

  5. Chui, S. S. et al. A chemically functionalizable nanoporous material [Cu3(TMA)2(H2O)3]n. Science 283, 1148–1150 (1999).

    Article  CAS  Google Scholar 

  6. Al-Janabi, N. et al. Mapping the Cu-BTC metal–organic framework (HKUST-1) stability envelope in the presence of water vapour for CO2 adsorption from flue gases. Chem. Eng. J. 281, 669–677 (2015).

    Article  CAS  Google Scholar 

  7. Alaerts, L. et al. Probing the Lewis acidity and catalytic activity of the metal–organic framework [Cu3(btc)2] (btc = benzene-1,3,5-tricarboxylate). Chem. Eur. J. 12, 7353–7363 (2006).

    Article  CAS  Google Scholar 

  8. Luz, I. et al. Bridging homogeneous and heterogeneous catalysis with MOFs: Cu-MOFs as solid catalysts for three-component coupling and cyclization reactions for the synthesis of propargylamines, indoles and imidazopyridines. J. Catal. 285, 285–291 (2012).

    Article  CAS  Google Scholar 

  9. Al-Janabi, N. et al. Underlying mechanism of the hydrothermal instability of Cu3(BTC)2 metal–organic framework. Front. Chem. Sci. Eng. 10, 103–107 (2016).

    Article  CAS  Google Scholar 

  10. Al-Janabi, N. et al. Cyclic adsorption of water vapour on CuBTC MOF: sustaining the hydrothermal stability under non-equilibrium conditions. Chem. Eng. J. 333, 594–602 (2018).

    Article  CAS  Google Scholar 

  11. Mehta, P. et al. Overcoming ammonia synthesis scaling relations with plasma-enabled catalysis. Nat. Catal. 1, 269–275 (2018).

    Article  Google Scholar 

  12. Stere, C. E. et al. Non-thermal plasma activation of gold-based catalysts for low-temperature water–gas shift catalysis. Angew. Chem. Int. Ed. 56, 5579–5583 (2017).

    Article  CAS  Google Scholar 

  13. Gibson, E. K. et al. Probing the role of a non-thermal plasma (NTP) in the hybrid NTP catalytic oxidation of methane. Angew. Chem. Int. Ed. 56, 9351–9355 (2017).

    Article  CAS  Google Scholar 

  14. Ashford, B. & Tu, X. Non-thermal plasma technology for the conversion of CO2. Curr. Opin. Green Sustainable Chem. 3, 45–49 (2017).

    Article  Google Scholar 

  15. Bae, J. et al. Oxygen plasma treatment of HKUST-1 for porosity retention upon exposure to moisture. Chem. Commun. 53, 12100–12103 (2017).

    Article  CAS  Google Scholar 

  16. Luo, J. et al. Water splitting in low-temperature ac plasmas at atmospheric pressure. Res. Chem. Intermed. 26, 849–874 (2000).

    Article  CAS  Google Scholar 

  17. Decoste, J. B. et al. Enhanced stability of Cu-BTC MOF via perfluorohexane plasma-enhanced chemical vapor deposition. J. Am. Chem. Soc. 134, 1486–1489 (2012).

    Article  CAS  Google Scholar 

  18. Decoste, J. B. et al. Hierarchical pore development by plasma etching of Zr-based metal–organic frameworks. Chem. Eur. J. 21, 18029–18032 (2015).

    Article  CAS  Google Scholar 

  19. Sadakiyo, M. et al. A new approach for the facile preparation of metal–organic framework composites directly contacting with metal nanoparticles through arc plasma deposition. Chem. Commun. 52, 8385–8388 (2016).

    Article  CAS  Google Scholar 

  20. Tao, L. et al. Creating coordinatively unsaturated metal sites in metal–organic frameworks as efficient electrocatalysts for the oxygen evolution reaction: insights into the active centers. Nano Energy 41, 417–425 (2017).

    Article  CAS  Google Scholar 

  21. Bahri, M. et al. Metal organic frameworks for gas-phase VOCs removal in a NTP-catalytic reactor. Chem. Eng. J. 320, 308–318 (2017).

    Article  CAS  Google Scholar 

  22. Junliang, W. et al. Chromium-based metal–organic framework MIL-101 as a highly effective catalyst in plasma for toluene removal. J. Phys. D. 50, 475202 (2017).

    Article  CAS  Google Scholar 

  23. Xu, S. et al. CO2 conversion in a non-thermal, barium titanate packed bed plasma reactor: The effect of dilution by Ar and N2. Chem. Eng. J. 327, 764–773 (2017).

    Article  CAS  Google Scholar 

  24. Drenchev, N. et al. CO as an IR probe molecule for characterization of copper ions in a basolite C300 MOF sample. Phys. Chem. Chem. Phys. 12, 6423–6427 (2010).

    Article  CAS  Google Scholar 

  25. Al-Janabi, N. et al. Assessment of MOF’s quality: quantifying defect content in crystalline porous materials. J. Phys. Chem. Lett. 7, 1490–1494 (2016).

    Article  CAS  Google Scholar 

  26. Cheetham, A. K. et al. Defects and disorder in metal organic frameworks. Dalton. Trans. 45, 4113–4126 (2016).

    Article  CAS  Google Scholar 

  27. Holzer, F. et al. Combination of non-thermal plasma and heterogeneous catalysis for oxidation of volatile organic compounds: Part 1. Accessibility of the intra-particle volume. Appl. Catal. B 38, 163–181 (2002).

    Article  CAS  Google Scholar 

  28. Roland, U. et al. Combination of non-thermal plasma and heterogeneous catalysis for oxidation of volatile organic compounds: Part 2. Ozone decomposition and deactivation of γ-Al2O3. Appl. Catal. B 58, 217–226 (2005).

    Article  CAS  Google Scholar 

  29. Zhang, Y. R. et al. Can plasma be formed in catalyst pores? A modeling investigation. Appl. Catal. B 2016(185), 56–67 (2016).

    Google Scholar 

  30. Karra, J. R. & Walton, K. S. Effect of open metal sites on adsorption of polar and nonpolar molecules in metal–organic framework Cu-BTC. Langmuir 24, 8620–8626 (2008).

    Article  CAS  Google Scholar 

  31. Jeong, D.-W. et al. Low-temperature water–gas shift reaction over supported Cu catalysts. Renew. Energy 65, 102–107 (2014).

    Article  CAS  Google Scholar 

  32. Tanaka, Y. et al. Water gas shift reaction over Cu-based mixed oxides for CO removal from the reformed fuels. Appl. Catal. A 242, 287–295 (2003).

    Article  CAS  Google Scholar 

  33. Gokhale, A. A. et al. On the mechanism of low-temperature water gas shift reaction on copper. J. Am. Chem. Soc. 130, 1402–1414 (2008).

    Article  CAS  Google Scholar 

  34. Aranifard, S. et al. On the importance of the associative carboxyl mechanism for the water–gas shift reaction at Pt/CeO2 interface sites. J. Phys. Chem. C 118, 6314–6323 (2014).

    Article  CAS  Google Scholar 

  35. Burch, R. Gold catalysts for pure hydrogen production in the water-gas shift reaction: activity, structure and reaction mechanism. Phys. Chem. Chem. Phys. 8, 5483–5500 (2006).

    Article  CAS  Google Scholar 

  36. Szanyi, J. Well-studied Cu-BTC still serves surprises: evidence for facile Cu2+/Cu+ interchange. Phys. Chem. Chem. Phys. 14, 4383–4390 (2012).

    Article  CAS  Google Scholar 

  37. Chen, C.-S. et al. Active sites on Cu/SiO2 prepared using the atomic layer epitaxy technique for a low-temperature water–gas shift reaction. J. Catal. 263, 155–166 (2009).

    Article  CAS  Google Scholar 

  38. Ilinich, O. et al. Cu–Al2O3–CuAl2O4 water–gas shift catalyst for hydrogen production in fuel cell applications: mechanism of deactivation under start–stop operating conditions. J. Catal. 247, 112–118 (2007).

    Article  CAS  Google Scholar 

  39. Wang, X. et al. In situ studies of the active sites for the water gas shift reaction over Cu−CeO2 catalysts: complex interaction between metallic copper and oxygen vacancies of ceria. J. Phys. Chem. B 110, 428–434 (2006).

    Article  CAS  Google Scholar 

  40. Du, H. et al. In situ FTIR spectroscopic analysis of carbonate transformations during adsorption and desorption of CO2 in K-promoted HTlc. Chem. Mater. 22, 3519–3526 (2010).

    Article  CAS  Google Scholar 

  41. Campbell, C. T. & Daube, K. A. A surface science investigation of the water–gas shift reaction on Cu(111). J. Catal. 104, 109–119 (1987).

    Article  CAS  Google Scholar 

  42. Zhang, Z. et al. The most active Cu facet for low-temperature water gas shift reaction. Nat. Commun. 8, 488 (2017).

  43. Baier, T. & Kolb, G. Temperature control of the water gas shift reaction in microstructured reactors. Chem. Eng. Sci. 62, 4602–4611 (2007).

    Article  CAS  Google Scholar 

  44. Łaniecki, M. et al. Water–gas shift reaction over sulfided molybdenum catalysts. Appl. Catal. A 196, 293–303 (2000).

    Article  Google Scholar 

Download references

Acknowledgements

X.F. thanks The Royal Society (RG160031) for financial support. P.A.M. and S.X. acknowledge the support from the European Community’s Seventh Framework (FP7)/People-Marie Curie Actions Programme (RAPID under Marie Curie Grant agreement no. 606889). The UK Catalysis Hub is thanked for resources and support provided via our membership of the UK Catalysis Hub Consortium and funded by EPSRC (Portfolio Grant nos EP/K014706/2, EP/K014668/1, EP/K014854/1, EP/K014714/1 and EP/I019693/1). We thank S. Yang, A. Walton, R. Saunders and T. Vetter for their advice and help in improving the manuscript.

Author information

Authors and Affiliations

Authors

Contributions

X.F. and S.X. conceived the idea. S.X. designed the NTP reactor under the guidance of P.A.M., carried out the catalytic tests and characterization of the materials using N2 sorption, XRD, scanning electron microscopy and FTIR spectroscopy under the guidance of X.F., performed in situ DRIFTS experiments and data analysis and took part in the initial discussion of the data under the guidance of X.F. and P.A.M. C.S. and S.C. designed and performed the in situ DRIFTS experiments and discussed the data with S.X. under the guidance of C.H. and X.F. K.W., B.I. and A.G. developed the in situ DRIFTS flow cell in collaboration with C.H. S.F.R.T. performed the XPS characterization and analysis under the guidance of C.H. N.A.-J. helped with the dynamic water vapour adsorption experiments under the guidance of X.F. X.F wrote the manuscript. All the authors contributed to the preparation of the manuscript.

Corresponding authors

Correspondence to Christopher Hardacre, Philip A. Martin or Xiaolei Fan.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Methods; Supplementary Figures 1–34; Supplementary Tables 1–5; Supplementary Notes 1–6; Supplementary References

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Xu, S., Chansai, S., Stere, C. et al. Sustaining metal–organic frameworks for water–gas shift catalysis by non-thermal plasma. Nat Catal 2, 142–148 (2019). https://doi.org/10.1038/s41929-018-0206-2

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41929-018-0206-2

This article is cited by

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing