Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Single artificial atoms in silicon emitting at telecom wavelengths


Given its potential for integration and scalability, silicon is likely to be a key platform for large-scale quantum technologies. Individual electron-encoded artificial atoms, formed by either impurities or quantum dots, have emerged as a promising solution for silicon-based integrated quantum circuits. However, single qubits featuring an optical interface, which is needed for long-distance exchange of information, have not yet been isolated in silicon. Here we report the isolation of single optically active point defects in a commercial silicon-on-insulator wafer implanted with carbon atoms. These artificial atoms exhibit a bright, linearly polarized single-photon emission with a quantum efficiency of the order of unity. This single-photon emission occurs at telecom wavelengths suitable for long-distance propagation in optical fibres. Our results show that silicon can accommodate single isolated optical point defects like in wide-bandgap semiconductors, despite a small bandgap (1.1 eV) that is unfavourable for such observations.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Single optically active artificial atoms in silicon.
Fig. 2: Photophysics of single G-centres in silicon.
Fig. 3: Dynamics of optical cycles.

Similar content being viewed by others

Data availability

Source data are provided with this paper. All other results are available from the corresponding author upon reasonable request.


  1. He, Y. et al. A two-qubit gate between phosphorus donor electrons in silicon. Nature 571, 371–375 (2019).

    Article  Google Scholar 

  2. Watson, T. et al. A programmable two-qubit quantum processor in silicon. Nature 555, 633–637 (2018).

    Article  Google Scholar 

  3. Maurand, R. et al. A CMOS silicon spin qubit. Nat. Commun. 7, 13575 (2016).

    Article  Google Scholar 

  4. Qiang, X. et al. Large-scale silicon quantum photonics implementing arbitrary two-qubit processing. Nat. Photon. 12, 534–539 (2018).

    Article  Google Scholar 

  5. Silverstone, J., Bonneau, D., O’Brien, J. & Thompson, M. Silicon quantum photonics. IEEE J. Sel. Top. Quantum Electron. 22, 390–402 (2016).

    Article  Google Scholar 

  6. Awschalom, D., Hanson, R., Wrachtrup, J. & Zhou, B. Quantum technologies with optically interfaced solid-state spins. Nat. Photon. 12, 516–527 (2018).

    Article  Google Scholar 

  7. Aharonovich, I., Englund, D. & Toth, M. Solid-state single-photon emitters. Nat. Photon. 10, 631–641 (2016).

    Article  Google Scholar 

  8. Gruber, A. et al. Scanning confocal optical microscopy and magnetic resonance on single defect centers. Science 276, 2012–2014 (1997).

    Article  Google Scholar 

  9. Beveratos, A. et al. Single photon quantum cryptography. Phys. Rev. Lett. 89, 187901 (2002).

    Article  Google Scholar 

  10. Hensen, B. et al. Loophole-free Bell inequality violation using electron spins separated by 1.3 kilometres. Nature 526, 682–686 (2015).

    Article  Google Scholar 

  11. Gross, I. et al. Real-space imaging of non-collinear antiferromagnetic order with a single-spin magnetometer. Nature 549, 252–256 (2017).

    Article  Google Scholar 

  12. Weber, J. et al. Quantum computing with defects. Proc. Natl Acad. Sci. USA 107, 8513–8518 (2010).

    Article  Google Scholar 

  13. Davies, G. The optical properties of luminescence centres in silicon. Phys. Rep. 176, 83–188 (1989).

    Article  Google Scholar 

  14. Beaufils, C. et al. Optical properties of an ensemble of G-centers in silicon. Phys. Rev. B 97, 035303 (2018).

    Article  Google Scholar 

  15. Beveratos, A. et al. Room temperature stable single-photon source. Eur. Phys. J. D 18, 191–196 (2002).

    Google Scholar 

  16. Chartrand, C. et al. Highly enriched 28Si reveals remarkable optical linewidths and fine structure for well-known damage centers. Phys. Rev. B 98, 195201 (2018).

    Article  Google Scholar 

  17. Docaj, A. & Estreicher, S. Three carbon pairs in Si. Physica B 407, 2981–2984 (2012).

    Article  Google Scholar 

  18. Wang, H., Chroneos, A., Londos, C., Sgourou, E. & Schwingenschlegl, U. G-centers in irradiated silicon revisited: a screened hybrid density functional theory approach. J. Appl. Phys. 115, 183509 (2014).

    Article  Google Scholar 

  19. Timerkaeva, D., Attaccalite, C., Brenet, G., Caliste, D. & Pochet, P. Structural, electronic, and optical properties of the C–C complex in bulk silicon from first principles. J. Appl. Phys. 123, 161421 (2018).

    Article  Google Scholar 

  20. Song, L., Zhan, X., Benson, B. & Watkins, G. Bistable defect in silicon: the interstitial-carbon–substitutional-carbon pair. Phys. Rev. Lett. 60, 460–463 (1988).

    Article  Google Scholar 

  21. Capaz, R., Dal Pino, A. & Joannopoulos, J. Theory of carbon–carbon pairs in silicon. Phys. Rev. B 58, 9845–9850 (1998).

    Article  Google Scholar 

  22. Tkachev, V. & Mudryi, A. Piezospectroscopic effect on zero-phonon luminescence lines of silicon. J. Appl. Spectrosc. 29, 1485–1491 (1978).

    Article  Google Scholar 

  23. Schmitt, S., Sarau, G. & Christiansen, S. Observation of strongly enhanced photoluminescence from inverted cone-shaped silicon nanostructures. Sci. Rep. 5, 17089 (2015).

    Article  Google Scholar 

  24. Cueff, S. et al. Tailoring the local density of optical states and directionality of light emission by symmetry breaking. IEEE J. Sel. Top. Quantum Electron. 25, 4700807 (2019).

  25. Gérard, J. et al. Enhanced spontaneous emission by quantum boxes in a monolithic optical microcavity. Phys. Rev. Lett. 81, 1110–1113 (1998).

    Article  Google Scholar 

  26. Lee, K., O’Donnell, K., Weber, J., Cavenett, B. & Watkins, G. Optical detection of magnetic resonance for a deep-level defect in silicon. Phys. Rev. Lett. 48, 37–40 (1982).

    Article  Google Scholar 

  27. Manson, N. et al. NV–N+ pair centre in 1b diamond. New J. Phys. 20, 113037 (2018).

    Article  Google Scholar 

  28. Lohrmann, A. et al. Diamond based light-emitting diode for visible single-photon emission at room temperature. Appl. Phys. Lett. 99, 251106 (2011).

    Article  Google Scholar 

  29. Anderson, C. et al. Electrical and optical control of single spins integrated in scalable semiconductor devices. Science 366, 1225–1230 (2019).

    Article  Google Scholar 

  30. Bernien, H. et al. Two-photon quantum interference from separate nitrogen vacancy centers in diamond. Phys. Rev. Lett. 108, 043604 (2012).

    Article  Google Scholar 

  31. Riedinger, R. et al. Remote quantum entanglement between two micromechanical oscillators. Nature 556, 473–477 (2018).

    Article  Google Scholar 

  32. Lee, S.-Y. et al. Readout and control of a single nuclear spin with a metastable electron spin ancilla. Nat. Nanotechnol. 8, 487–492 (2013).

    Article  Google Scholar 

  33. Wehner, S., Elkouss, D. & Hanson, R. Quantum internet: a vision for the road ahead. Science 362, eaam9288 (2018).

    Article  MathSciNet  Google Scholar 

  34. Tait, A. et al. Microring resonator-coupled photoluminescence from silicon W centers. J. Phys. Photonics 2, 045001 (2020).

    Article  Google Scholar 

  35. Ziegler, J. F. SRIM-2003. Nucl. Instrum. Methods Phys. Res. B 219/220, 1027–1036 (2004).

    Article  Google Scholar 

  36. Binder, J. et al. Qudi: a modular Python suite for experiment control and data processing. SoftwareX 6, 85–90 (2017).

    Article  Google Scholar 

  37. Martínez, L. et al. Efficient single photon emission from a high-purity hexagonal boron nitride crystal. Phys. Rev. B 94, 121405 (2016).

    Article  Google Scholar 

  38. Kitson, S. C., Jonsson, P., Rarity, J. & Tapster, P. Intensity fluctuation spectroscopy of small numbers of dye molecules in a microcavity. Phys. Rev. A 58, 620–627 (1998).

    Article  Google Scholar 

  39. Beveratos, A., Brouri, R., Poizat, J.-P. & Grangier, P. in Quantum Communication, Computing, and Measurement 3 (eds Tombesi, P. & Hirota, O.) 261–267 (Springer, 2002).

  40. Benisty, H., Stanley, R. & Mayer, M. Method of source terms for dipole emission modification in modes of arbitrary planar structures. J. Opt. Soc. Am. A 15, 1192–1201 (1998).

    Article  Google Scholar 

  41. Genovese, L. et al. Daubechies wavelets as a basis set for density functional pseudopotential calculations. J. Chem. Phys. 129, 014109 (2008).

    Article  Google Scholar 

Download references


We thank P. Valvin for his technical support and fruitful discussions, and C. L’Henoret for his technical support at the mechanics workshop. We acknowledge support from the French National Research Agency (ANR) through the PRCI projects ULYSSES (no. ANR-15-CE24-0027-01) and OCTOPUS (no. ANR-18-CE47-0013-01), the German Research Foundation (DFG) through the ULYSSES project and the European Union’s Horizon 2020 research and innovation programme through the FET-OPEN project NARCISO (no. 828890). P.P. and D.C. acknowledge GENCI for the use of French computational resources in CCRT and IDRIS supercomputer centres (grant no. 6107). A. Durand acknowledges support from the French DGA.

Author information

Authors and Affiliations



A. Durand, I.R.-P., V.J., A. Dréau and G.C. designed the experimental set-up. T.H., A.B., S.P., J.M. and A.Y.K. prepared the samples. W.R., A. Durand and A. Dréau carried out the experiments. J.-M.G., D.C. and P.P. performed numerical simulations. W.R., A. Durand, J.-M.G., I.R.-P., B.G., M.A., V.J., A. Dréau and G.C. analysed the data. A. Dréau prepared the manuscript with contributions from I.R.-P., V.J. and G.C. All authors discussed the results and commented on the manuscript.

Corresponding author

Correspondence to A. Dréau.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data

Extended Data Fig. 1 Analysis of the photodynamics of the G-center.

a, Simplified three-level model of the G-center under optical excitation. b, Second-order autocorrelation function \({g}_{{\rm{cor}}}^{(2)}(\tau )\) with increasing laser excitation power (from bottom to top). Data are corrected from background counts (see Eq. (1)) and fitted with equation (3). c, Evolution of the rates Λ0 and Λ1 with increasing optical power. The dashed lines correspond to data fitting excluding the last point at 30 μW. d, The bunching amplitude decreases with increasing optical power. The dotted line is a guide to the eye. Error bars represent the standard error resulting from data fitting of b with Python lmfit package.

Source data

Extended Data Fig. 2 Time-resolved PL counts recorded under pulsed laser excitation.

Histogram of the PL counts measured on a single defect under a 50-ps pulse laser excitation at 532 nm, with a periodicity of 270 ns. The measurement sequence was repeated 2.8 billion times. Counts are integrated in the window [0, 150] ns (shaded area), subtracted from noise counts (gray shaded area), and finally divided by the number of sweeps to get the probability to detect a photon per optical excitation Pphoton 4.1 10−4.

Source data

Extended Data Fig. 3 Calculations of the photon collection efficiency by a NA=0.85 objective.

a, Scheme of the simulated structure. The emitter dipole is assumed to be lying in the plane perpendicular to the surface, as this configuration maximizes photon collection. b, Evolution of the collection efficiency ηcoll as a function of the depth d of the embedded emitter.

Source data

Source data

Source Data Fig. 1

Source data of the plots in Fig. 1.

Source Data Fig. 2

Source data of the plots in Fig. 2.

Source Data Fig. 3

Source data of the plots in Fig. 3.

Source Data Extended Data Fig. 1

Source data of the plots in Extended Data Fig. 1.

Source Data Extended Data Fig. 2

Source data of the plots in Extended Data Fig. 2.

Source Data Extended Data Fig. 3

Source data of the plots in Extended Data Fig. 3.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Redjem, W., Durand, A., Herzig, T. et al. Single artificial atoms in silicon emitting at telecom wavelengths. Nat Electron 3, 738–743 (2020).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing