Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Sustainable polymer coating for stainproof fabrics

Abstract

The excessive use of synthetic detergents in laundry operations is an important source of environmental pollution. As a result, sustainability-driven innovations are receiving increasing attention to enable eco-friendly textiles characterized by properties that allow for minimized consumption of detergents. Here we propose a coating-at-will (CAW) strategy to create an extra layer on top of a textile fabric to introduce stain resistance. The coated layer is based on conjugated polymers from lysozyme (Lyz) and zwitterionic poly(sulfobetaine methacrylate) (pSBMA), which, once exposed to the fabric, form a robust nanofilm on the surface. Remarkably, this hydrophilic layer exhibits excellent underwater superoleophobicity, and the coated fabrics can be cleaned simply with water without detergents. Optically transparent and biocompatible, this polymer nanofilm does not compromise the clothing comfort of the fabric and reduces the carbon footprint by more than 50% compared with detergents, according to a life cycle analysis. Moreover, our CAW strategy can be applied to the surfaces of various materials, including metals, glasses, plastics and ceramics, suggesting a versatile solution to the environmental risks posed by cleaning products.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Synthesis of PTL-pSBMA nanofilm and its rapid adhesion to substrates.
Fig. 2: Antifouling property of the PTL-pSBMA nanofilm.
Fig. 3: Surface modification of fabrics by PTL-pSBMA.
Fig. 4: Stain resistance of PTL-pSBMA-modified fabrics.
Fig. 5: CAW concept enabling regeneration of PTL-pSBMA for reuse.
Fig. 6: LCA of PTL-pSBMA.

Similar content being viewed by others

Data availability

The data that support the findings of this study are available from the corresponding author upon reasonable request. Correspondence and requests for materials should be addressed to P.Y. Source data are provided with this paper.

References

  1. Malkapuram, S. et al. A review on recent advances in the application of biosurfactants in wastewater treatment. Sustain. Energy Techn. 48, 101576 (2021).

    Google Scholar 

  2. Johnson, P., Trybala, A., Starov, V. & Pinfield, V. J. Effect of synthetic surfactants on the environment and the potential for substitution by biosurfactants. Adv. Colloid Interface Sci. 288, 102340 (2021).

    Article  CAS  Google Scholar 

  3. Joseph, C. G. et al. Ozonation treatment processes for the remediation of detergent wastewater: a comprehensive review. J. Environ. Chem. Eng. 9, 106099 (2021).

    Article  CAS  Google Scholar 

  4. Jardak, K., Drogui, P. & Daghrir, R. Surfactants in aquatic and terrestrial environment: occurrence, behavior, and treatment processes. Environ. Sci. Pollut. Res. 23, 3195–3216 (2016).

    Article  CAS  Google Scholar 

  5. Yan, P. et al. Net-zero-energy model for sustainable wastewater treatment. Environ. Sci. Technol. 51, 1017–1023 (2017).

    Article  CAS  Google Scholar 

  6. Maktabifard, M., Zaborowska, E. & Makinia, J. Achieving energy neutrality in wastewater treatment plants through energy savings and enhancing renewable energy production. Rev. Environ. Sci. Biotechnol. 17, 655–689 (2018).

    Article  Google Scholar 

  7. Hardie, A. G., Madubela, N., Clarke, C. E. & Lategan, E. L. Impact of powdered and liquid laundry detergent greywater on soil degradation. J. Hydrol. 595, 126059 (2021).

    Article  CAS  Google Scholar 

  8. Rebello, S., Asok, A. K., Mundayoor, S. & Jisha, M. S. Surfactants: toxicity, remediation and green surfactants. Environ. Chem. Lett. 12, 275–287 (2014).

    Article  CAS  Google Scholar 

  9. Yu, X. L. & He, Y. Tea saponins: effective natural surfactants beneficial for soil remediation, from preparation to application. RSC Adv. 8, 24312–24321 (2018).

    Article  CAS  Google Scholar 

  10. Liu, B. et al. Corncob cellulose nanosphere as an eco-friendly detergent. Nat. Sustain. 3, 448–458 (2020).

    Article  Google Scholar 

  11. Singh, A., Sharma, A., Bansal, S. & Sharma, P. Comparative interaction study of amylase and surfactants for potential detergent formulation. J. Mol. Liq. 261, 397–401 (2018).

    Article  CAS  Google Scholar 

  12. Delorme, V. et al. Effects of surfactants on lipase structure, activity, and inhibition. Pharm. Res. 28, 1831–1842 (2011).

    Article  CAS  Google Scholar 

  13. Fenibo, E. O., Ijoma, G. N., Selvarajan, R. & Chikere, C. B. Microbial surfactants: the next generation multifunctional biomolecules for applications in the petroleum industry and its associated environmental remediation. Microorganisms 7, 581 (2019).

    Article  CAS  Google Scholar 

  14. Wisetkomolmat, J., Suppakittpaisarn, P. & Sommano, S. R. Detergent plants of northern Thailand: potential sources of natural saponins. Resources 8, 10 (2019).

    Article  Google Scholar 

  15. Liu, P. et al. Zwitterionic modification of polyurethane membranes for enhancing the anti-fouling property. J. Colloid Interface Sci. 480, 91–101 (2016).

    Article  CAS  Google Scholar 

  16. Liu, P., Domingue, E., Ayers, D. C. & Song, J. Modification of Ti6Al4V substrates with well-defined zwitterionic polysulfobetaine brushes for improved surface mineralization. ACS Appl. Mater. Interfaces 6, 7141–7152 (2014).

    Article  CAS  Google Scholar 

  17. Chen, S. et al. Durable antibacterial and nonfouling cotton textiles with enhanced comfort via zwitterionic sulfopropylbetaine coating. Small 12, 3516–3521 (2016).

    Article  CAS  Google Scholar 

  18. Li, Q. et al. Zwitterionic biomaterials. Chem. Rev. 122, 17073–17154 (2022).

    Article  CAS  Google Scholar 

  19. Cheng, Y. et al. Zwitterionic polymer-grafted superhydrophilic and superoleophobic silk fabrics for anti-oil applications. Macromol. Rapid Commun. 41, 2000162 (2020).

    Article  CAS  Google Scholar 

  20. Lee, H., Dellatore, S. M., Miller, W. M. & Messersmith, P. B. Mussel-inspired surface chemistry for multifunctional coatings. Science 318, 426–430 (2007).

    Article  CAS  Google Scholar 

  21. Ejima, H. et al. One-step assembly of coordination complexes for versatile film and particle engineering. Science 341, 154–157 (2013).

    Article  CAS  Google Scholar 

  22. Wang, D. et al. 2D protein supramolecular nanofilm with exceptionally large area and emergent functions. Adv. Mater. 28, 7414–7423 (2016).

    Article  CAS  Google Scholar 

  23. Li, C., Qin, R., Liu, R., Miao, S. & Yang, P. Functional amyloid materials at surfaces/interfaces. Biomater. Sci. 6, 462–472 (2018).

    Article  CAS  Google Scholar 

  24. Tao, F., Han, Q., Liu, K. & Yang, P. Tuning crystallization pathways through the mesoscale assembly of biomacromolecular nanocrystals. Angew. Chem. Int. Ed. 56, 13440–13444 (2017).

    Article  CAS  Google Scholar 

  25. Gu, J., Miao, S., Yan, Z. & Yang, P. Multiplex binding of amyloid-like protein nanofilm to different material surfaces. Colloid Interface Sci. Commun. 22, 42–48 (2018).

    Article  CAS  Google Scholar 

  26. Li, C., Lu, D., Deng, J., Zhang, X. & Yang, P. Amyloid-like rapid surface modification for antifouling and in-depth remineralization of dentine tubules to treat dental hypersensitivity. Adv. Mater. 31, 1903973 (2019).

    Article  CAS  Google Scholar 

  27. Hu, X. et al. Amyloid-like protein aggregates: a new class of bioinspired materials merging an interfacial anchor with antifouling. Adv. Mater. 32, 2000128 (2020).

    Article  CAS  Google Scholar 

  28. Tian, J. et al. Amyloid-like protein aggregates combining antifouling with antibacterial activity. Biomater. Sci. 8, 6903–6911 (2020).

    Article  CAS  Google Scholar 

  29. Wang, Y. et al. Mussel-inspired design of a self-adhesive agent for durable moisture management and bacterial inhibition on PET fabric. Adv. Mater. 33, 2100140 (2021).

    Article  CAS  Google Scholar 

  30. Lee, H., Scherer, N. F. & Messersmith, P. B. Single-molecule mechanics of mussel adhesion. Proc. Natl Acad. Sci. USA 103, 12999–13003 (2006).

    Article  CAS  Google Scholar 

  31. Li, Y. et al. Molecular design principles of lysine-DOPA wet adhesion. Nat. Commun. 11, 3895 (2020).

    Article  CAS  Google Scholar 

  32. Qiu, Q. et al. Silane-functionalized polyionenes-coated cotton fabrics with potent antimicrobial and antiviral activities. Biomaterials 284, 121470 (2022).

    Article  CAS  Google Scholar 

  33. Giagnorio, M., Amelio, A., Grüttner, H. & Tiraferri, A. Environmental impacts of detergents and benefits of their recovery in the laundering industry. J. Clean. Prod. 154, 593–601 (2017).

    Article  Google Scholar 

  34. Baumgartner, M. et al. Resilient yet entirely degradable gelatin-based biogels for soft robots and electronics. Nat. Mater. 19, 1102–1109 (2020).

    Article  CAS  Google Scholar 

  35. Knoth, D. et al. Evaluation of a biosurfactant extract obtained from corn for dermal application. Int. J. Pharm. 564, 225–236 (2019).

    Article  CAS  Google Scholar 

  36. Doncom, K. E., Warren, N. J. & Armes, S. P. Polysulfobetaine-based diblock copolymer nano-objects via polymerization-induced self-assembly. Polym. Chem. 6, 7264–7273 (2015).

    Article  CAS  Google Scholar 

  37. Li, H., Bapat, A. P., Li, M. & Sumerlin, B. S. Protein conjugation of thermoresponsive amine-reactive polymers prepared by RAFT. Polym. Chem. 2, 323–327 (2011).

    Article  CAS  Google Scholar 

  38. Lucius, M. et al. Investigating the impact of polymer functional groups on the stability and activity of lysozyme-polymer conjugates. Biomacromolecules 17, 1123–1134 (2016).

    Article  CAS  Google Scholar 

  39. Li, C. et al. Amphiphilic antifogging/anti-icing coatings containing POSS-PDMAEMA-b-PSBMA. ACS Appl. Mater. Interfaces 9, 22959–22969 (2017).

    Article  CAS  Google Scholar 

  40. Yandi, W. et al. Polyampholytic poly(AEMA-co-SPMA) thin films and their potential for antifouling applications. ACS Appl. Polym. Mater. 3, 5361–5372 (2021).

    Article  CAS  Google Scholar 

  41. Kalak, T., Gąsior, K., Wieczorek, D. & Cierpiszewski, R. Improvement of washing properties of liquid laundry detergents by modification with N-hexadecyl-N, N-dimethyl-3-ammonio-1-propanesulfonate sulfobetaine. Text. Res. J. 91, 115–129 (2021).

    Article  CAS  Google Scholar 

  42. Yang, X. et al. Green detergent made of halloysite nanotubes. Chem. Eng. J. 425, 130623 (2021).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

P.Y. acknowledges funding support from the National Science Foundation through Distinguished Young Scholars (No. 52225301), the National Key R&D Program of China (Nos. 2020YFA0710400, 2020YFA0710402), the 111 Project (No. B14041), the Innovation Capability Support Program of Shaanxi (No. 2020TD-024) and the International Science and Technology Cooperation Program of Shaanxi Province (No. 2022KWZ-24). J. Zhao was funded by the National Key R&D Program of China (Nos. 2020YFA0710400 and 2020YFA0710403), the Fundamental Research Funds for Central Universities (No. GK202205017), the National Natural Science Foundation of China (No. 51903146) and the Natural Science Foundation of Shaanxi Province (No. 2020JQ-420). Y.L. was supported by the National Natural Science Foundation of China (No. 51903147).

Author information

Authors and Affiliations

Authors

Contributions

P.Y. managed the entire project, providing experimental space, expenditures, ideas, designs and article revisions. C.F. completed the experimental preparation, characterization, data processing, project design and article revision. Z.W. provided ideas for experiments. Y.G. assisted in materials characterization. J. Zhao and Y.L. revised the article. X. Zhou and R.Q. proofread the article. Y.P. and X. Zhang directed animal experiments. Y.Z. guided in situ AFM characterization. B.H., J. Zhang, J.W. and S.N. assisted with field experiments. F.F. assisted with image design. Q.T. and X.L. guided the LCA analysis.

Corresponding author

Correspondence to Peng Yang.

Ethics declarations

Competing interests

The authors declare no competing interests.

Peer review

Peer review information

Nature Sustainability thanks Xi Yao, Simeon Stoyanov and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data

Extended Data Fig. 1 Basic characterization of the PTL-pSBMA nanofilm.

a, FTIR characterization of the Lyz-pSBMA and PTL-pSBMA powders and the corresponding deconvolution of the amide I regions. b,c, AFM (b) and TEM (c) images of the PTL-pSBMA coating. The scale bar of AFM is 160 nm and TEM is 100 nm. d, S2p XPS test on the surface of the PTL-pSBMA nanofilm. e, f, C/N ratio (e) and WCA (f) of the PTL-pSBMA coatings on various substrates. Error bars show the mean ± SD (n = 3).

Source data

Extended Data Fig. 2 Characterization of the antifouling properties of nanofilms.

a, Laser scanning confocal microscopy (LSCM) images showing the patterned adherence of S. aureus. Scale bars are 400 μm and 20 μm respectively. b, E. coli cultured on bare glass and PTL-pSBMA@glass. Scale bars, 20 μm. c,d, Field emission-scanning electron microscopy (FE-SEM) images showing S. aureus (c) and E. coli (d) adherence to a bare silicon wafer (left, scale bars, 3 μm) and the PTL-pSBMA nanofilm (right, scale bars, 10 μm). e, Optical microscopy images showing A. flavus adherence to the PS culture dish (left) and PTL-pSBMA nanofilm (right). Scale bars, 50 μm. f,g, FE-SEM images (f) showing the platelets adhered to the bare glass (left) and PTL-pSBMA nanofilm (right), and LSCM images (g) showing L929 cells adhered to the bare glass (left) and PTL-pSBMA nanofilm (right). Scale bars are 20 μm (f) and 300 μm (g) respectively.

Extended Data Fig. 3 Underwater superoleophobic properties of the PTL-pSBMA nanofilm.

a,b, Optical images showing PTL-pSBMA modified on various fabrics (silk, linen, polyester, flannel, vinylon, cotton, and modal) (a), and the corresponding underwater oil contact angle (OCA) (b). Scale bar, 2 cm.

Extended Data Fig. 4 The stain resistance of PTL-pSBMA-modified fabrics.

a, Optical images showing removal of grass stains from white polyester, vinylon, silk and cotton fabrics in the groups of blank, PTL-pSBMA, conventional DWL and LP. b,c, The corresponding detergency (b) and whiteness retention (c). Error bars show the mean ± SD (n = 3).

Source data

Extended Data Fig. 5 Stain resistance of PTL-pPSBMA-modified kitchenware.

a, Optical images showing the cleaning effect of PTL-pSBMA relative to DWL to remove chili oil from plastic, stainless steel, ceramic, and glass plates (a). b,c, The corresponding cleaning efficiency values (b, c). Error bars show the mean ± SD (n = 3).

Source data

Extended Data Fig. 6 Safety evaluation of PTL-pSBMA.

a,b, Haemolysis assay of PTL-pSBMA coated on a bandage. Optical photographs of positive (H2O), negative control (PBS), pristine bandage and PTL-pSBMA nanofilm (a, b). Error bars show the mean ± SD (n = 3). c, Cytotoxicity test of the PTL-pSBMA nanofilm. Error bars show the mean ± SD (n = 3). d, Mortality tests of zebrafish for PTL-pSBMA, LP and DWL. e,f, Photosynthetic rates of hydroponic lettuce treated with PTL-pSBMA, LP and DWL after 48 h of cultivation at 1 and 2 mg ml-1, respectively (e, f). Error bars show the mean ± SD (n = 3). g,h, Optical and H&E staining images showing mouse back contact with the blank and PTL-pSBMA@fabrics for 1–5 d (g,h). Scale bars are 2 mm (g) and 200 μm (h) respectively.

Source data

Supplementary information

Supplementary Information

Supplementary Methods, Figs. 1–69 and Tables 1–3.

Supplementary Data 1

LCA of PTL-pSBMA.

Supplementary Video 1

In situ AFM images of the film formation process of PTL-pSBMA solution on mica substrate.

Supplementary Video 2

Comparison of pristine silk and PTL-pSBMA@silk on cleaning chili oil.

Supplementary Video 3

Large-scale modification of fabrics by PTL-pSBMA and cleaning of chili oil stain.

Supplementary Video 4

PTL-pSBMA nanofilm cleans chili oil on dish surface.

Supplementary Video 5

Comparison of washing pristine dish and PTL-pSBMA@dish with water at a rate of 25 ml s−1.

Source data

Source Data Fig. 1

Unprocessed CD and T% and processed ANS data.

Source Data Fig. 2

Calculated QCM data.

Source Data Fig. 3

Unprocessed air and moisture permeability data.

Source Data Fig. 4

Calculated data for resistance to chili oil.

Source Data Fig. 5

Calculated data for coating regeneration cycles.

Source Data Fig. 6

Fig. 6b,c are unprocessed data, and the specific data can be viewed in the Supplementary Information. Fig. 6d,e are calculated data.

Source Data Extended Data Fig. 1

Extended Fig. 1a,d,f are unprocessed data, and Extended Data Fig. 1e is processed data.

Source Data Extended Data Fig. 4

Calculated data for resistance to grass stains.

Source Data Extended Data Fig. 5

Calculated data for resistance to chili oil.

Source Data Extended Data Fig. 6

Extended Data Fig. 6b–d are processed data, and Extended Data Fig. 6f are unprocessed data.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Fu, C., Wang, Z., Gao, Y. et al. Sustainable polymer coating for stainproof fabrics. Nat Sustain 6, 984–994 (2023). https://doi.org/10.1038/s41893-023-01121-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41893-023-01121-9

This article is cited by

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing