Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

A strong, biodegradable and recyclable lignocellulosic bioplastic

An Author Correction to this article was published on 20 August 2021


Renewable and biodegradable materials derived from biomass are attractive candidates to replace non-biodegradable petrochemical plastics. However, the mechanical performance and wet stability of biomass are generally insufficient for practical applications. Herein, we report a facile in situ lignin regeneration strategy to synthesize a high-performance bioplastic from lignocellulosic resources (for example, wood). In this process, the porous matrix of natural wood is deconstructed to form a homogeneous cellulose–lignin slurry that features nanoscale entanglement and hydrogen bonding between the regenerated lignin and cellulose micro/nanofibrils. The resulting lignocellulosic bioplastic shows high mechanical strength, excellent water stability, ultraviolet-light resistance and improved thermal stability. Furthermore, the lignocellulosic bioplastic has a lower environmental impact as it can be easily recycled or safely biodegraded in the natural environment. This in situ lignin regeneration strategy involving only green and recyclable chemicals provides a promising route to producing strong, biodegradable and sustainable lignocellulosic bioplastic as a promising alternative to petrochemical plastics.

This is a preview of subscription content, access via your institution

Access options

Buy this article

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: The preparation of high-performance lignocellulosic bioplastic.
Fig. 2: The fabrication process of the lignocellulosic bioplastic by the in situ lignin regeneration method.
Fig. 3: Structural and compositional characterization of the lignocellulosic bioplastic.
Fig. 4: The structure of the regenerated lignin and the interaction between the regenerated lignin and cellulose.
Fig. 5: The biodegradability, recyclability and environmental impacts of the lignocellulosic bioplastic.

Similar content being viewed by others

Data availability

Data are available on reasonable request from the authors, according to their contributions.


  1. Yun, X. & Dong, T. in Food Packaging (ed. Grumezescu, A. M.) 147–184 (Academic Press, 2017).

  2. Záleská, M. et al. Structural, mechanical and hygrothermal properties of lightweight concrete based on the application of waste plastics. Constr. Build. Mater. 180, 1–11 (2018).

    Article  Google Scholar 

  3. Someya, T., Bao, Z. & Malliaras, G. G. The rise of plastic bioelectronics. Nature 540, 379–385 (2016).

    Article  CAS  Google Scholar 

  4. Kudrin, A. M., Gabriel’s, K. S. & Karaeva, O. A. The temperature effect on mechanical properties of carbon fiber reinforced plastics for aviation purposes. Inorg. Mater. 9, 763–766 (2018).

    Article  Google Scholar 

  5. Rochman, C. M. et al. Classify plastic waste as hazardous. Nature 494, 169–171 (2013).

    Article  CAS  Google Scholar 

  6. Brahney, J., Hallerud, M., Heim, E., Hahnenbergeret, M. & Sukumaran, S. Plastic rain in protected areas of the United States. Science 368, 1257–1260 (2020).

    Article  CAS  Google Scholar 

  7. Law, K. L. et al. The United States’ contribution of plastic waste to land and ocean. Sci. Adv. 6, eabd0288 (2020).

    Article  Google Scholar 

  8. Zhu, Y., Romain, C. & Williams, C. K. Sustainable polymers from renewable resources. Nature 540, 354–362 (2016).

    Article  CAS  Google Scholar 

  9. Lambert, S. & Wagner, M. Environmental performance of bio-based and biodegradable plastics: the road ahead. Chem. Soc. Rev. 46, 6855–6871 (2017).

    Article  CAS  Google Scholar 

  10. Chen, C. et al. Structure–property–function relationships of natural and engineered wood. Nat. Rev. Mater. 5, 642–666 (2020).

    Article  CAS  Google Scholar 

  11. Yang, J., Ching, Y. C. & Chuah, C. H. Applications of lignocellulosic fibers and lignin in bioplastics: a review. Polymers 11, 751 (2019).

    Article  CAS  Google Scholar 

  12. Balaguer, M. P., Gomez-Estaca, J., Gavara, R. & Hernandez-Munoz, P. Biochemical properties of bioplastics made from wheat gliadins cross-linked with cinnamaldehyde. J. Agric. Food Chem. 59, 13212–13220 (2011).

    Article  CAS  Google Scholar 

  13. Yue, H. B., Cui, Y. D., Shuttleworth, P. S. & Clark, J. H. Preparation and characterisation of bioplastics made from cottonseed protein. Green. Chem. 14, 2009–2016 (2012).

    Article  CAS  Google Scholar 

  14. Herres-Pawlis, S. New stereocontrol on the block. Nat. Chem. 12, 107–109 (2020).

    Article  CAS  Google Scholar 

  15. Venkateshaiah, A. et al. Recycling non-food-grade tree gum wastes into nanoporous carbon for sustainable energy harvesting. Green. Chem. 22, 1198–1208 (2020).

    Article  CAS  Google Scholar 

  16. Yang, Y., Tilman, D., Lehman, C. & Trost, J. J. Sustainable intensification of high-diversity biomass production for optimal biofuel benefits. Nat. Sustain. 1, 686–692 (2018).

    Article  Google Scholar 

  17. Isogai, A., Saito, T. & Fukuzumi, H. TEMPO-oxidized cellulose nanofibers. Nanoscale 3, 71–85 (2011).

    Article  CAS  Google Scholar 

  18. Arnodo, D., Ghinato, S., Nejrotti, S., Blangetti, M. & Prandi, C. Lateral lithiation in deep eutectic solvents: regioselective functionalization of substituted toluene derivatives. Chem. Commun. 56, 2391–2394 (2020).

    Article  CAS  Google Scholar 

  19. Hong, S. et al. In-depth interpretation of the structural changes of lignin and formation of diketones during acidic deep eutectic solvent pretreatment. Green. Chem. 22, 1851–1858 (2020).

    Article  CAS  Google Scholar 

  20. Hammond, O. S., Edler, K. J., Bowron, D. T. & Torrente-Murciano, L. Deep eutectic-solvothermal synthesis of nanostructured ceria. Nat. Commun. 8, 14150 (2017).

    Article  CAS  Google Scholar 

  21. Tan, X., Zhao, W. & Mu, T. Controllable exfoliation of natural silk fibers into nanofibrils by protein denaturant deep eutectic solvent: nanofibrous strategy for multifunctional membranes. Green. Chem. 20, 3625–3633 (2018).

    Article  CAS  Google Scholar 

  22. Sirvio, J. A., Visanko, M. & Liimatainen, H. Acidic deep eutectic solvents as hydrolytic media for cellulose nanocrystal production. Biomacromolecules 17, 3025–3032 (2016).

    Article  CAS  Google Scholar 

  23. Wang, M. et al. Highly stretchable, transparent, and conductive wood fabricated by in situ photopolymerization with polymerizable deep eutectic solvents. ACS Appl. Mater. Interfaces 11, 14313–14321 (2019).

    Article  CAS  Google Scholar 

  24. Xia, Q. et al. Multiple hydrogen bond coordination in three-constituent deep eutectic solvents enhances lignin fractionation from biomass. Green. Chem. 20, 2711–2721 (2018).

    Article  CAS  Google Scholar 

  25. Liu, Q. et al. Novel deep eutectic solvents with different functional groups towards highly efficient dissolution of lignin. Green. Chem. 21, 5291–5297 (2019).

    Article  CAS  Google Scholar 

  26. Zhao, D. et al. A dynamic gel with reversible and tunable topological networks and performances. Matter 2, 390–403 (2020).

    Article  Google Scholar 

  27. Li, Y. et al. Facile extraction of cellulose nanocrystals from wood using ethanol and peroxide solvothermal pretreatment followed by ultrasonic nanofibrillation. Green. Chem. 18, 1010–1018 (2016).

    Article  CAS  Google Scholar 

  28. Wang, H. et al. Extraction of cellulose nanocrystals using a recyclable deep eutectic solvent. Cellulose 27, 1301–1314 (2019).

    Article  CAS  Google Scholar 

  29. Zhu, M. et al. Highly anisotropic, highly transparent wood composites. Adv. Mater. 28, 5181–5187 (2016).

    Article  CAS  Google Scholar 

  30. Moon, R. J., Martini, A., Nairn, J., Simonsen, J. & Youngblood, J. Cellulose nanomaterials review: structure, properties and nanocomposites. Chem. Soc. Rev. 40, 3941–3994 (2011).

    Article  CAS  Google Scholar 

  31. Alvarez-Vasco, C. et al. Unique low-molecular-weight lignin with high purity extracted from wood by deep eutectic solvents (DES): a source of lignin for valorization. Green. Chem. 18, 5133–5141 (2016).

    Article  CAS  Google Scholar 

  32. Wu, X. et al. Lignin‐derived electrochemical energy materials and systems. Biofuel. Bioprod. Birefin. 14, 650–672 (2020).

    Article  CAS  Google Scholar 

  33. Iravani, S. & Varma, R. S. Greener synthesis of lignin nanoparticles and their applications. Green. Chem. 22, 612–636 (2020).

    Article  CAS  Google Scholar 

  34. Ragauskas, A. J. et al. Lignin valorization: improving lignin processing in the biorefinery. Science 344, 1246843 (2014).

    Article  Google Scholar 

  35. Wu, X. et al. Solar energy-driven lignin-first approach to full utilization of lignocellulosic biomass under mild conditions. Nat. Catal. 1, 772–780 (2018).

    Article  CAS  Google Scholar 

  36. Fraile, JoséM., Zoel Hormigón, J. I. G., Mayoral, J. A., Saavedra, C. J., & Salvatella, L. Role of substituents in the solid acid-catalyzed cleavage of the β-O-4 linkage in lignin models. ACS Sustain. Chem. Eng. 6, 1837–1847 (2018).

    Article  CAS  Google Scholar 

  37. Sanderson, K. Lignocellulose: a chewy problem. Nature 474, S12–S14 (2011).

    Article  CAS  Google Scholar 

  38. Jung, Y. H. et al. High-performance green flexible electronics based on biodegradable cellulose nanofibril paper. Nat. Commun. 6, 7170 (2015).

    Article  Google Scholar 

  39. Ashter, S. A. in Thermoforming of Single and Multilayer Laminates Ch. 10 (William Andrew, 2013).

Download references


We acknowledge the support of the Maryland Nanocenter, its Surface Analysis Center and AIMLab. We acknowledge J. Gao for his experimental suggestions.

Author information

Authors and Affiliations



L.H., Q.X. and C.C. designed the experiments. Q.X. carried out experiments. Y.G.Y. and S.H. analysed the mechanical data. Y.Z. helped with the preparation of the large-scale bioplastic film. Q.X. and J.L. fabricated the lignocellulosic bioplastic parts by compression moulding. T.L. and X.P. provided some useful suggestions. Y.Y. provided the LCAs. L.H., Q.X. and C.C. collaboratively analysed the data and wrote the paper. All authors commented on the final manuscript.

Corresponding authors

Correspondence to Yuan Yao or Liangbing Hu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Sustainability thanks Robert Allen, Eun Yeol Lee and Tong-Qi Yuan for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data

Extended Data Fig. 1 The fabrication mechanism of the lignocellulosic bioplastic.

Loose and porous wood powder, composed of cellulose, lignin and hemicellulose, serves as the starting material. After DES (ChCl/oxalic acid) treatment, the cellulose fibres are fibrillated into micro/nanofibrils while DES dissolves the lignin. Water can interact with the hydrophobic DES through hydrogen bonding interactions. Thus, water can be added as a green antisolvent in the system, causing the hydrophobic lignin to regenerate. After filtering, we obtain a cellulose–lignin slurry, the solid content of which we can control by varying the water content. The lignocellulosic bioplastic film can then be obtained by casting the slurry at room temperature.

Extended Data Fig. 2 The structure of the wood powder.

a-d, Photograph (a), SEM image (b), magnified SEM image (c) and SAXS pattern (d) of the wood powder. Compared to the isotropic structure of lignocellulosic bioplastic, the wood powder shows more structural inhomogeneity.

Extended Data Fig. 3 The tensile strength and fracture surfaces of the lignocellulosic bioplastic.

a, The tensile stress-strain curves of the cellulose film and lignocellulosic bioplastic. b, The strength and toughness of the cellulose film and lignocellulosic bioplastic. The lignocellulosic bioplastic demonstrates excellent mechanical properties with a high tensile strength of 128 MPa and toughness of 2.8 MJ·m3, which are 7- and 8-times higher than cellulose film (18 MPa and 0.35 MJ·m3), respectively. c-d, Digital and SEM images of the fracture surfaces of the (c) lignocellulosic bioplastic and (d) cellulose film after tensile testing. The samples have ~1 wt.% water content. The cellulose film fractured by macro-fibre slippage from the loose fibre network structure, in which most fibres were not broken, indicating the binding strength between the cellulose fibres in the film is weaker than the strength of the fibres themselves. In contrast, broken fibres appear in the fracture zone of the lignocellulosic bioplastic, suggesting its binding strength is greater than the strength of its constituent fibres due to the intertwining cellulose micro/nanofibrils and lignin network. Such entangled interaction between the micro/nanofibrils and high adhesion mediated by the in situ regenerated lignin matrix with abundant hydrogen bonding and van der Waals forces contribute to the outstanding mechanical properties of the lignocellulosic bioplastic.

Extended Data Fig. 4 The excellent mechanical strength of the lignocellulosic bioplastic.

a, Photographs of the lignocellulosic bioplastic (8 cm×3.5 cm×0.1 cm), b, including under a heavy load (200 g). c-d, The excellent foldability of the lignocellulosic bioplastic. e, The unfolded lignocellulosic bioplastic features a sharp crease. f, Photograph of the unfolded lignocellulosic bioplastic bearing a heavy load (200 g). Although the lignocellulosic bioplastic had undergone folding, the creased material can still easily bear the applied weight without failing.

Extended Data Fig. 5 The water stability of the lignocellulosic bioplastic.

a. Photographs of water droplets on the cellulose film and lignocellulosic bioplastic surfaces over time (0–10 min). The lignocellulosic bioplastic has a higher water contact angle (90.0 ± 8°) than that of pure cellulose film (78.7 ± 10°), demonstrating its slightly greater tendency to repel water. After 10 minutes, the water droplet gradually spreads out and adheres to the cellulose film (28.2 ± 6°), whereas the shape of the droplet on the lignocellulosic bioplastic surface remains relatively stable (71.8 ± 7°). b, Water absorption of the cellulose film and lignocellulosic bioplastic over 140 min. The inset shows photographs of water droplets on a sloping lignocellulosic bioplastic surface (right), demonstrating the material’s excellent water stability, while the water is quickly absorbed on the cellulose film (left). The lignocellulosic bioplastic has exceptionally lower water absorption (~30%) than that of the cellulose film (~100%). In contrast, water droplets easily permeate into the hydrophilic cellulose film even on inclined surfaces. c, Water stability test of cellulose film and lignocellulosic bioplastic in water for 30 days. The cellulose film disintegrates while the lignocellulosic bioplastic film maintains its shape. We immersed the cellulose film and lignocellulosic bioplastic in water for thirty days. After this time, we found the cellulose film completely disintegrated into microfibers, while the lignocellulosic bioplastic showed good stability in the wet environment, retaining its shape without any fractures.

Extended Data Fig. 6 The degradability tests of the lignocellulosic bioplastic and PVC materials.

Direct outdoor exposure was carried out to evaluate the degradability of the lignocellulosic bioplastic, which was placed on grass and exposed to the sun, wind and rain (College Park, Maryland, U.S., from October 20, 2019 to March 10, 2020). After three months, the dimensions of the lignocellulosic bioplastic increased as it became more swollen. After ~4 months, the lignocellulosic bioplastic became cracked and fragmented and its original structure completely degraded after five months. Meanwhile, the PVC remained almost the same as on the first day, demonstrating it cannot be degraded under natural conditions.

Extended Data Fig. 7 Flow diagram for continuous in situ lignin regeneration treatment and the recycling of the DES.

After mixing and heating of the wood powder and DES, followed by the addition of water to in situ regenerate the lignin, we can use an in-line filter to separate the cellulose–lignin slurry and solvent, in which the DES and water make up the filter liquor. DES can then be purified by heating the mixture to remove water. The recovered DES can be recycled in the system to treat new lignocellulosic starting materials. Water can also be collected using a condenser and recycled again to serve as the antisolvent for lignin regeneration.

Extended Data Fig. 8 The universality of in situ lignin regeneration approach.

The lignocellulosic bioplastic can be derived from various lignocellulosic biomass sources, including wood, wheat straw, grass and bagasse, demonstrating the strong universality of this approach.

Extended Data Fig. 9 The life cycle impact assessment results of lignocellulosic and other biodegradable plastics per cm3/MPa.

Across most environmental impact categories, the lignocellulosic bioplastic developed in this work is more environmentally favourable than PHA, PLA, PBS, PCL and PBAT. There are a few exceptions. Compared with PBAT, the lignocellulosic bioplastic has higher impacts in three categories, including eutrophication, human health - carcinogenics and respiratory effects. For all three categories, the impacts of lignocellulosic bioplastics are driven by electricity consumption, which accounted for 71–86% of the results based on the contribution analysis. The electricity was assumed to be the U.S. average grid in this study. The environmental impacts could be lower if renewable energy were used. To estimate the impacts of using renewable energy, a scenario using electricity generated from wind was evaluated and the results are shown in Extended Data Fig. 9 as triangles. The Life Cycle Inventory (LCI) of wind energy was obtained from Ecoinvent database for onshore generation in the U.S. The environmental impacts of the lignocellulosic bioplastic using wind energy are the lowest across all the impact categories except fossil fuel depletion (close to the upper bounds of the results of PLA and PBAT).

Extended Data Fig. 10 Environmental impacts of the moulded lignocellulosic bioplastic compared to PP, PET and ABS.

Compared to PP and ABS, the lignocellulosic bioplastic is at the lower end across all environmental impact categories. Compared to PET, the lignocellulosic bioplastic has lower environmental impacts in categories such as ecotoxicity, eutrophication and human health. For other categories, the lignocellulosic bioplastic has comparable results with PET and close to the higher bounds of PET’s impacts in ozone depletion, smog formation and fossil fuel depletion. Similar to the LCAs for plastic films, we included a renewable energy scenario to investigate the impacts of using wind and the results are shown as triangles (Extended Data Fig. 10). Compared with PP, PET and ABS, the environmental impacts of the lignocellulosic bioplastic using wind energy were the lowest across all the impact categories, except for fossil fuel depletion (which was close to the upper bound of PET’s results).

Supplementary information

Supplementary Information

Supplementary Notes 1–8, Figs. 1–19, Tables 1–3 and refs. 1–60.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Xia, Q., Chen, C., Yao, Y. et al. A strong, biodegradable and recyclable lignocellulosic bioplastic. Nat Sustain 4, 627–635 (2021).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

This article is cited by


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing