Abstract
Twodimensional (2D) transition metal oxides (TMOs) are an emerging class of nanomaterials. Using density functional theory and ab initio molecular dynamics (AIMD) simulations, we carried out a systematic study of atomically thin metal oxide phases with compositions MO, M_{2}O_{3}, and MO_{2}, for transition metal elements Sc, Ti, V, Cr, and Mn. We identified nine thermally stable structures that may be realized as freestanding nanosheets: hexagonal hSc_{2}O_{3}, hV_{2}O_{3}, and hMn_{2}O_{3}; hexagonal tVO, tCrO, and tMnO; and square sqTiO, sqVO, and sqMnO. The tMO phases are novel hexagonal structures which emerged naturally from phase transformations observed during AIMD simulations. The 2D TMOs were found to exhibit a wide range of remarkable electronic and magnetic properties, indicating that they are bright candidates for electronic and spintronic applications. Most exceptional in this regard is hV_{2}O_{3}, that is the only phase that has been experimentally realized so far, and was found to be a ferromagnetic halfmetal with Diracconelike bands.
Introduction
The discovery of graphene and its fascinating properties^{1} has incited a whole new field of research dedicated to the exploration of twodimensional (2D) nanomaterials. Using top–down approaches, where monolayers are isolated from layered bulk structures, and bottomup approaches, where thin films are obtained through deposition of molecules on substrates, added to graphene is now a wide range of 2D materials consisting of elements other than carbon, such as hBN, the monoelemental 2D semiconductors silicene, phosphorene, and germanene, Mxenes, i.e., transition metal carbides, nitrides, and carbonitrides, and transition metal dichalcogenides (TMDs), such as MoS_{2}.^{2,3} The exploration of 2D nanomaterials has only started little over a decade ago, but is rapidly progressing.
Bulk phase transition metal oxides (TMOs) are known to have unique properties originating from their itinerant and strongly correlated transition metal (TM) d electrons. This strong electron correlation, where the TM d electrons experience a strong Coulomb repulsion from one another, leads to physical phenomena such as the metal–insulator transition^{4,5} (MIT), where, upon tuning parameters such as temperature, pressure, and chemical composition, and often along with a structural and magnetic phase transition, the electronic structure of a system will undergo a MIT (for VO_{2}, for example, see Refs. ^{6,7,8}). In addition, TM d orbitals can be either fully or partially occupied, giving rise to multivalence states of TM atoms and allowing numerous stoichiometries; vanadium oxide, for example, existing in the four principle phases VO, V_{2}O_{3}, VO_{2}, and V_{2}O_{5}, in the Wadsley phases^{9} V_{n}O_{2n+1} (1 ≤ n ≤ 3), and in the Magnéli phases^{10} V_{n}O_{2n−1} (3 ≤ n ≤ 9). A TMO can furthermore exist as various stable polymorphs, stoichiometrically identical but crystallographically different phases, that for MnO_{2}, for example, add up to a total number of six stable phases found so far^{11} and may transform into one another with energy barriers as low as 0.2–0.3 eV/f.u.^{12} Their diversity makes TMOs versatile in a wide range of applications, including energy storage, catalysis, molecular sieving, functional magnetic and optical materials, and biosensors.
With the popularity of 2D materials and the unique properties of bulk TMOs in mind, 2D TMOs are being actively investigated as well, and recently, the first thin film and nanosheet 2D TMOs have been realized experimentally. Limiting ourselves to the scope of our study, i.e., the early 3d transition metal (Sc, Ti, V, Cr, and Mn) oxides, and just naming a few works with no intention of a complete review: via chemical vapor deposition, Chang et al. prepared rutile TiO_{2} and monoclinic VO_{2} thin films on αAl_{2}O_{3} surfaces;^{13} with the same technique, epitaxial rutile and monoclinic VO_{2} films were grown on a rAl_{2}O_{3} substrate by Makarevich et al.;^{14} monolayered (ML) V_{2}O_{3} thin films have been synthesized on a Pd(111) surface by Surnev at al.^{15,16} Exfoliation of a layered manganese oxide by Omomo et al. resulted in ML nanosheets of MnO_{2} in the T phase.^{17} A generalized approach to molecular selfassembly synthesis of ultrathin 2D nanosheets of transition metal oxides was developed by Sun et al., and resulted in the successful synthesis of, among others, ~3.3 nmthick TiO_{2} nanosheets containing 4–5 MLs of anatase TiO_{2}.^{18} The preparation of 2D TMOs on temporary, watersoluble salt templates resulted in ~1 nmthick cubic MnO nanolayers and was reported by Xiao et al.^{19}
Comprehensive computational studies using density functional theory (DFT) and the more advanced quasiparticle GW approach^{20} (G: Green’s function; W: screened Coulomb interaction) on monolayered MX_{2} transition metal dichalcogenides and oxides (TMDs and TMOs) in the T and H phases were performed by Ataca et al. and Rasmussen et al.,^{21,22} and included ScO_{2} and MnO_{2}, which are stable in both phases, TiO_{2}, which is unstable in either phase, and VO_{2} and CrO_{2}, which only have a stable H phase.^{21} The monolayered V_{2}O_{3} synthesized on a Pd(111) surface, mentioned in the previous paragraph, was characterized by DFT simulations by Kresse et al.^{23} DFT calculations by Vittadini et al. on 1–6 monolayer (ML) thick films derived from the main lowindex surfaces of anatase TiO_{2} revealed two anomalously stable films that are a restructuring of anatase TiO_{2} into a lepidocrociteTiO_{2} nanosheet (derived from the 2 ML (001) film) and a novel TiO_{2} phase (derived from the 4 ML (101) film).^{24} By DFT+U^{25} (Hubbard U parameter) and hybrid HSE06^{26} (Heyd–Scuseria–Ernzerhof) calculations, Kan et al. identified the experimentally realized monolayered Tphase MnO_{2} nanosheets mentioned in the paragraph above to be an intrinsic ferromagnetic 2D material.^{27} Graphitic, hexagonal MnO layers were further predicted by means of DFT+U by Kan et al. to be more stable than the corresponding wurtzite wzMnO(0001) surface, when the number of layers is less than four.^{28} Along this line, Wang et al. performed DFT calculations and suggested that semiconductor wz structures transform into planar hexagonal structures upon a planar stretching force.^{29}
To the best of our knowledge, a systematic firstprinciples’ study of singleatomically thin 2D TMO structures has not been conducted yet. Inspired by the successful synthesis of 2D hexagonal V_{2}O_{3} on a substrate and the predicted stability of 2D hexagonal MnO, we designed four different 2D TMO phases: hexagonal MO (hMO) and square MO (sqMO), which both have an equivalent bulk phase, namely wurtzite MO (wzMO) and rocksalt MO (rsMO), that can be built up directly from the 2D counterparts; and hexagonal M_{2}O_{3} (hM_{2}O_{3}) and square MO_{2} (sqMO_{2}), for which no direct 2D bulk connection exists. Using planewave DFT and hybrid HSE06 calculations, we systematically disclosed the energetic and thermal stability, and novel electronic and magnetic properties, of these atomically thin 2D TMOs for the five early 3d transition metals Sc, Ti, V, Cr, and Mn. Except for hV_{2}O_{3} and hMnO, all these structures are at this moment undiscovered.
Results and discussion
Computational methodology
The four planar hMO, sqMO, hM_{2}O_{3}, and sqMO input geometries considered in this study for the five TMs, Sc, Ti, V, Cr, and Mn, are shown in Fig. 1. For each of the 2D TMO input geometries, nonmagnetic (NM), ferromagnetic (FM), and various antiferromagnetic (AFM) orderings of the TM atoms were investigated, including for hMO, the ferrimagnetic (FiM) configuration that is the groundstate magnetic ordering of halfhydrated graphene (graphone).^{30} The number of (planar) structuralmagnetic input configurations adds up to 20 for hMO, 20 for sqMO, 15 for hM_{2}O_{3}, and 20 for sqMO_{2}. Inspired by the experimentally synthesized buckled structure of hV_{2}O_{3},^{15,16,23} we also examined the stability of buckled 2D TMO phases, rerunning all simulations with buckled instead of planar input geometries, with the Osublayer shifted 0.5 Å away from the TMsublayer, bringing the total number of structural and magnetic input configurations considered in this study for the hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} phases to 150.
The DFT calculations were performed using the first principles’ Vienna Ab initio Simulation Package^{31,32,33} (VASP). Within the projectoraugmented wave (PAW) framework,^{34,35} the exchange and correlation energy terms were described using the Perdew–Burke–Ernzerhof (PBE) generalized gradient approximation (GGA) functional.^{36,37} Computational details are given in the Methods section. To obtain groundstate geometries and magnetic arrangements, the simulation cells were structurally and magnetically optimized, relaxing lattice parameters, atomic positions, and magnetic moments. To study the charges of the atoms, a Bader charge analysis^{38} was carried out using the approach by Henkelman et al.^{39,40}
The enormous amount of calculations involved in our study prevented us from relaxing the structures with the more advanced Hartree–Fock (HF)/DFT hybrid Heyd–Scuseria–Ernzerhof functional^{26} (HSE06). Previous studies have shown, however, that using HSE for 2D materials such as graphene halides^{41} and MoS_{2}^{42} results in geometries that are almost identical to PBErelaxed geometries. In addition, studies of bulk TMOs have found, at the same time, that, while giving very similar results for structural relaxation and relative stability and indicating that the nonlocal HF exchange has little effect on the structure and total energy of strongly correlated systems, the description of the electronic structure of such a system, in particular of its d states, greatly improves when using a hybrid functional.^{11,43,44,45,46,47} To obtain a more accurate description of the electronic structure of our 2D TMOs, we therefore performed HSE06 calculations on the PBErelaxed structures that were found to be the 2D TMOs’ structural and magnetic groundstate configurations. Employing the popular and computationally less expensive DFT + U method was not considered in this study, as we are investigating a wide range of elements, and various physical properties such as energy, geometry, electronic structure, and magnetism, and the DFT + U approach depends on the Hubbard U parameter, the value of which differs for different elements and different properties, and may lead to unwanted inconsistencies in our results.^{44,48}
To assess the thermal stability of the 2D TMOs, we performed ab initio molecular dynamics (AIMD) simulations for each of the 20 structural and magnetic groundstate configurations, using 72atom 6 × 6 supercells for the hMO phases, 100atom 5 × 5 supercells for the sqMO phases, 80atom 4 × 4 supercells for the hM_{2}O_{3} phases, and 72atom 5 × 5 supercells for each of the sqMO_{2} phases, except sqMnO_{2}, which was simulated using a 108atom 6 × 6 supercell to accommodate its magnetic ordering. For each of the structures, with a time step of 1 fs, a 2 ps initial equilibration and a 5 ps subsequent canonical (NVT) ensemble simulation using a Nosé thermostat^{49,50,51} was carried out, at simulation temperatures of 300 and 700 K. After the AIMD simulations, AIMD supercell output configurations were relaxed at high accuracy at 0 K again, to see if the structures had remained topologically equivalent.
Energetic stability of the hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} phases
To assess the relative stability of the 2D TMO phases, we define their formation energy per atom, E_{f}, relative to their elemental transition metal bulk phases TM and the paramagnetic oxygen molecule O_{2}:
where E(MO_{x}) is the calculated total energy of a 2D TMO with x = 1, 1.5, or 2; E(TM) is the energy per atom of the TMs in their elemental phase; and E(O_{2}) is the energy of an O_{2} molecule in its paramagnetic ground state.
Table S1 in the Supplementary Information (SI) lists the calculated energies of lowestenergy and higherenergy magnetic and nonmagnetic configurations for all 2D TMO phases considered in this study. This table includes tMO phases, which were found from the AIMD simulations and which will be discussed separately below. A summary of the formation energy E_{f} of the most stable magnetic groundstate configurations can be found in Table 1. For the latter, a concavehull plot is included as well (see Fig. 2). In general, a system will be unstable and decompose into its two neighboring compositions if its energy lies above the concavehull line, i.e., the common tangent constructed connecting line. In the concavehull plot for the 2D TMOs, for each of the phases the formation energy is located below the straight line connecting the two adjacent data points. This suggests that all considered 2D TMO phases are energetically stable at the respective stoichiometries.
Comparing the formation energies of the hMO and sqMO polymorphs, the sqMO phase was found to be energetically more favorable than the hMO phase for all considered TMs except Mn, sqMnO being less stable than hMnO by 39 meV/atom. The relative stability of the sqMO phases over hMO may be due to the bonding network, for which sqMO, where each TM atom is coordinated by four oxygen atoms, resembles that of its 3D rs counterpart. In general, rs compounds have a stronger ionic nature than corresponding wz phases. The stronger ionicity of the TM–O bonds in sqMOs is indeed evidenced by the Bader charge analysis of the 2D structures: as can be seen from Table 1, for all TMs except Mn, the TM atoms were found to have a Bader charge that is ~0.2e higher in the sqMO phase than in the corresponding hMO phase; for MnO, the Bader charge on the Mn atoms was found to be similar in magnitude in both phases. TM and O atom coordination numbers and TM–O bond lengths in the 2D TMOs (listed in Table S2) can be correlated with the calculated atomic Bader charges (listed in Table 1): In sqMO, the coordination number of all atoms is 4, whereas for hMO this number is 3. The larger number of bonds correlates with an increased ionicity for sqMO structures, while at the same time the bond lengths in the latter are slightly larger than those in corresponding hMO structures. Comparing MO, M_{2}O_{3}, and MO_{2} structures, it can be observed that the Bader charge on the TM atoms is dominated by the difference in stoichiometry, and increases when going from MO to M_{2}O_{3} to MO_{2}. For the latter two structures, the bond lengths are considerably smaller than those in hMO and sqMO phases, by up to 10%, which is likely related to the fact that the O atoms have only two TM nearest neighbor atoms in M_{2}O_{3} and MO_{2}.
For further analysis of the structural buckling, we define the buckling energy E_{b} as the energy difference between a d_{b} buckled structure and its planar counterpart:
where a negative E_{b} indicates that a buckled structure is energetically more stable than the corresponding planar structure, and d_{b} is simply the perpendicular separation between the TM and Osublayer.
Relaxation of the 150 input configurations for the hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} phases resulted in 24 stable and metastable buckled structures. Of these, 15 were found to have E_{b} ≤ 20 meV/atom and d_{b} ≥ 0.02 Å (see Table S1), implying that these 2D TMO phases have a rather flat potential energy surface (PES), where the energies of planar and buckled geometries are two nearby local minima. Five buckled structures, namely AFM hScO, NM hTiO, FM hVO, AFM1 sqCrO, and AFM hTi_{2}O_{3}, were found to be structural and magnetic groundstate configurations, with buckling ranging from 0.14 to 0.71 Å (see Table 1). The reason for the energetic stability of these buckled 2D phases may be the pseudoJahn–Teller effect^{52} (PJTE), which states that if the excitedstate geometry of a polyatomic system is very close in energy (nearly degenerate) to its groundstate geometry, then these two states will be mixed via vibronic coupling, resulting in a symmetrybreaking distortion which stabilizes the system. The PJTE has been commonly seen in other 2D systems, such as groupIV^{53,54} and groupV^{55} nanosheets.
Energetic stability with respect to bulk TMOs
The stability of the hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} phases with respect to their 3D counterparts is evaluated by comparing their total energies per atom directly:
This simple formula has been used to evaluate the stability of cadmium chalcogenide monolayers^{56} and other 2D materials^{57} with respect to their bulk counterparts. A negative ΔE means that a 2D monolayer is energetically more favorable than its corresponding 3D bulk phase, indicating that a material would grow into a 2D slab rather than into a 3D nanocrystal. Furthermore, Singh et al. calculated the formation energies of a range of 2D ML materials, and came to the conclusion that all 2D materials that have been synthesized experimentally in the freestanding form, have a ΔE smaller than 200 meV/atom,^{58} suggesting that this could be a first selection criterion for assessing stability.
When choosing the 2D TMOs’ corresponding 3D phases, in addition to having the same stoichiometry as the 2D phases, two criteria were applied to make the chosen bulk structures as relevant as possible: (1) bulk structures that can be built up directly from the 2D counterparts are preferred. This is the case for the 3D rsMO and wzMO phases, which can be built up directly from the 2D sqMO and hMO phases. (2) Bulk structures that are relatively stable at low temperatures are preferred. This is to avoid possible structural and magnetic phase transitions at higher temperatures; and it makes more sense to compare lower energy structures rather than higherenergy structures with the 2D phases, which were calculated at 0 K.
The phases that were selected as the 2D TMOs’ corresponding bulk phases are listed in Table S2. Five bulk phases that have not been experimentally realized yet and remain hypothetical were still chosen because of their close similarity to the 2D TMO phases. The structural and magnetic ground states for these phases, i.e., wzScO, wzTiO, wzVO, wzCrO, and rsScO, were calculated and can be found in Table S2. The magnetic ground state for rsCrO and bixbyite Sc_{2}O_{3}, whose magnetic orderings were not found in literature, was investigated as well. No bulk phase was chosen for ScO_{2}: ScO_{2} has neither been experimentally realized nor theoretically predicted, and there is not a clear structural connection between the 3D rutile or anatase MO_{2} phase and the 2D sqMO_{2} phase. For readers’ information, all bond lengths and coordination numbers for the hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} phases, and their corresponding 3D phases are given in Table S2 as well.
Table 2 lists the calculated values for ΔE. For all 2D TMOs except three, the calculations resulted in a ΔE larger than 200 meV/atom. The three 2D TMOs that do meet the 200 meV/atom criterion, however, were found to even have a negative ΔE. These phases are 2D sqTiO, sqCrO, and sqMnO, and that they are energetically more favorable than 3D \({\it{\epsilon }}\)TiO, rsCrO, and rsMnO, indicates that they may be synthesized as stable freestanding slabs. To further understand the underlying reason for the energetic stability of these sqMO phases over their corresponding bulk phases, we compared the orbitalresolved densityofstates (DOS) of these 2D TMOs to the DOS of their 3D counterparts. This analysis is included as Supplementary Discussion in the SI.
Thermal stability of the 2D TMO phases
The thermal stability of the 20 structural and magnetic groundstate configurations was examined by means of AIMD simulation at temperatures of 300 and 700 K, and subsequent 0 K relaxation of AIMD output configurations to see if the structures had remained topologically equivalent. For the structures that did not show bond breaking during AIMD simulation, average bond lengths are listed in Table 3. Graphs showing minimum, average, and maximum bond lengths during 300 and 700 K AIMD simulation can be found in Fig. S1. All 300 and 700 K AIMD output configurations, and all postAIMD relaxed structures obtained from the 300 K AIMD output configurations, can be found in Fig. S1 as well. Figure 3 shows a selection, and includes for a number of structures perspective views and postAIMD relaxed structures obtained from 700 K AIMD output configurations, not shown in Fig. S1.
For the sqMO phases, the AIMD and postAIMD simulations indicate that planar sqTiO and sqVO are thermally stable structures. These phases show nice undulation during 300 and 700 K AIMD simulation, bond lengths increasing with increasing temperature and layers exhibiting outofplane displacement of atoms and wavelike vibration of the entire structure, but clearly remain the same: the 0 K relaxed AIMD output configurations for these phases are very smoothly corrugated 2D square structures that are energetically as favorable as their planar counterparts. Planar sqScO and monosided buckled sqCrO were found to be thermally unstable: postAIMD relaxation for these phases resulted in energetically more favorable doublesided oxygen terminated (and for sqScO: highly corrugated) structures that are no longer atomically thin (see Fig. 3c). Metastable sqMnO is thermally stable at 300 K and thermally unstable at 700 K: at 300 K, this structure remained the same, its AIMD output configuration at 0 K relaxing into a very smoothly corrugated square structure (see Fig. 3b, d) that is energetically as stable as planar sqMnO; at 700 K, sqMnO transformed into a hexagonal phase (see Fig. 3a). The 2D square MnO→2D hexagonal MnO phase transition will be further described below.
The planar sqMO_{2} phases are relatively open structures, the number of bonds per atom being two for O and four for TM atoms in sqMO_{2}, versus four bonds for each atom in sqMO. An open structure could cause a layer to rupture more easily; or to be more resilient to stress, due to increased flexibility. For all sqMO_{2} phases except sqScO_{2}, it has resulted in the former: during 300 K simulation, sqTiO_{2}, sqVO_{2}, sqCrO_{2}, and sqMnO_{2}, were all found to disintegrate and partly restructure into phases that are no longer atomically thin. sqScO_{2}, however, was found to retain structural integrity and square character during 300 K simulation (bond lengths increasing by ~3%, though); and after 700 K simulation, sqScO_{2} showed only the onset of the disintegration and partial restructuring, which for the other sqMO_{2} phases, was already and to a larger extent observed during 300 K simulation (see Fig. 3e–i). Relaxing at 0 K again, the sqScO_{2} 300 K AIMD output configuration was found to restructure into a phase that is no longer square and no longer atomically thin (see Fig. S1), indicating that sqScO_{2} too is thermally unstable.
For the hM_{2}O_{3} phases, the AIMD simulations and postAIMD relaxations show that planar hSc_{2}O_{3} and hV_{2}O_{3} are thermally stable: the 0 K relaxed output configurations for these phases are very smoothly corrugated atomically thin 2D structures (see Fig. 3j) that are energetically as favorable as their planar counterparts. The buckled hTi_{2}O_{3} and planar hCr_{2}O_{3} phases were found to be unstable; during postAIMD relaxation, the supercells for these phases restructured into phases that are no longer atomically thin (see Fig. 3l). The hMn_{2}O_{3} phase is thermally stable. Both the 300 and 700 K AIMD output configurations for this phase were found to restructure into arrangements of smoothly tilted hexagons (see Fig. 3k, m) that are only slightly more favorable than planar hMn_{2}O_{3}, by 1 meV/atom, which is at the accuracy limit of the calculations. This indicates that the hMn_{2}O_{3} structure preserves its hexagonal and atomically thin 2D character, i.e., is thermally stable at 300 and 700 K, but will exist as a smoothly corrugated structure rather than as a planar structure.
The hMO phases were all found to be thermally unstable. Buckled hScO and hTiO retained structural integrity during AIMD simulation; at 0 K, their AIMD output configurations relaxed, however, into structures that are no longer atomically thin (see Fig. 3n) and energetically more favorable than buckled hScO and hTiO. Buckled hVO, and planar hCrO and hMnO, also retained structural integrity during AIMD simulation and subsequently relaxed into energetically more favorable configurations; the AIMD output configurations for these three phases, however, were found to have restructured upon postAIMD relaxation into atomically thin supercells of hexagonal “tMO” phases displaying trigonal rotation symmetry (see Fig. 3o–q) that are thermally stable. (These three tMO phases will be further discussed below.)
In summary (see also Table 1), of the 20 hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} structural and magnetic groundstate configurations, 5 were found to be thermally stable, 1 to be thermally stable at 300 K and thermally unstable at 700 K, and 14 to be unstable. The unstable configurations include all buckled structures, all sqMO_{2} phases, and all hMO phases. From the AIMD and postAIMD simulations, another 2D hexagonal (“tMO”) phase was found, however, that is thermally stable for V, Cr, and Mn. This brings the total number of 2D TMOs identified in this study that may be realized as freestanding nanosheets to nine. These phases are: sqTiO, sqVO, and sqMnO; hSc_{2}O_{3}, hV_{2}O_{3}, and hMn_{2}O_{3}; and tVO, tCrO, and tMnO.
2D square MnO→2D hexagonal MnO phase transition
The sqMnO phase was found to be metastable, hexagonal hMnO and tMnO being more favorable than square sqMnO by 39 and 110 meV/atom, respectively (see the sections on the energetic stability of the 2D TMO phases above and below). During 700 K AIMD simulation, sqMnO was found to transform into a hexagonal phase (see Fig. 3a); this transformation already starts during equilibration. The mechanism of this 2D to 2D phase transformation consists of bond breaking resulting in rectangles with four atoms at the corners and two atoms halfway the long edges, and subsequent relaxation of these rectangles into hexagons (see Fig. 4; Supplementary Video 1). Already at the end of the 2 ps equilibration, the honeycomb phase has become the dominant phase, spanning the entire width of the simulation cell, while smaller patches with square MnO remain. A rough estimate of 400 K for the transformation temperature was obtained: continuing the 300 K simulation for another 50 ps, still no transformation of sqMnO was observed; while during a 10 ps simulation at 400 K after initial 2 ps equilibration, transformation into hexagonal MnO did take place.
Energetic stability of the tMO phases
The hVO, hCrO, and hMnO AIMD output configurations were found to restructure, upon postAIMD relaxation, into atomically thin supercells of hexagonal “tMO” phases. As can be seen from Fig. S2, the postAIMD relaxed hMnO supercell has an antiferromagnetic ordering corresponding to the AFM ordering found for hMnO. The postAIMDrelaxed hVO output configuration was found to be FM ordered, just like hVO, with the exception of one small domain. The postAIMD relaxation output configuration obtained for antiferromagnetic hCrO was found to have antiferromagnetic ordering of a type, however, that was not considered for the hMOs.
To check the structural and magnetic ground state of the three tMOs, totalenergy calculations were performed, considering NM, FM, AFM1, and AFM2 magnetic ordering, planar and buckled input configurations, and two types of atomic arrangements (labeled “(a)” and “(b)” as in Fig. 5) for each of the tMOs, bringing the total number of input configurations considered for the tMO phases to 48 (and the total number of input configurations considered in our study to 198). Unit cell geometries and considered AFM orderings are illustrated in Fig. 5. Note that the tMO phase is a \(\sqrt 3\) × \(\sqrt 3\) reconstruction of the hMO phase, lowering the p3m1 symmetry for perfect hMO to p31m symmetry for perfect tMO.
The results of the totalenergy calculations can be found in Table S1. Structural parameters for the structural and magnetic groundstate configurations are listed in Table 4. The groundstate configurations for tVO and tCrO were found to be atomic arrangements as depicted in Fig. 5a; the groundstate configuration for tMnO was found to be an atomic arrangement as depicted in Fig. 5b. tCrO and tMnO are planar structures. The lowestenergy configuration for tVO, however, was found to be a buckled phase, of a type where only onethird of the oxygen atoms (i.e., the oxygen atoms at the x = y mirror plane) are located at the buckling distance of 0.44 Å (see Table 4; Fig. S2). The tMnO phase was found to have an AFM1 ordering corresponding to its hMO precursor’s magnetic ground state. tCrO was found to have an antiferromagnetic ordering of a type (AFM2) that was not considered for the hMOs (hCrO has an antiferromagnetic ordering as well, of the AFM1 type, however). tVO is also AFM2 ordered; in contrast to its hVO precursor, which has FM ordering.
Comparing the formation energies of the tMO phases and their corresponding hMO and sqMO phases, it can be observed from Table 1 and Fig. 2, that just like their corresponding hMO phases, tVO and tCrO are energetically less favorable, and tMnO is energetically more favorable, than the corresponding sqMO phase. tVO, tCrO, and tMnO, are all energetically more favorable than their corresponding hMO phases, by 74, 155, and 71 meV/atom, respectively. The (latter) energetic stability of the tMO phases over the hMO phases may be due to the PJTE (for a brief discussion of the PJTE: see the section on the energetic stability of the hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} phases above).
Discussion of stability and methodology
The AIMD simulations and postAIMD relaxations indicate that nine of the 2D TMO structural and magnetic groundstate configurations identified in this study are thermally stable (see Table 1). These phases not only retained structural integrity, i.e., did not break at elevated temperatures, but also preserved their atomically thin, and hexagonal or square, 2D character. Our findings suggest that these structures may all be synthesized as freestanding atomically thin nanosheets showing smooth corrugation upon realization. The thermally unstable 2D TMO phases can most likely not exist as freestanding slabs. These phases, however, may be stabilized using an appropriate support: substrate stabilization of 2D materials can be as large as 8.84 kJ/molatom (91.6 meV/atom);^{59} and substrates can be chosen to interact with the synthesized 2D TMO thin film via only a weak van der Waals force, which would stabilize the film without much interference with its electronic structure.^{60} The thermally stable phases were found to include 2D TMOs that do not meet the 200 meV criterion (see the section on the energetic stability of 2D TMO phases with respect to bulk); and sqCrO, which does meet the 200 meV criterion, was found to be thermally unstable. This merely indicates, however, that comparing 2D TMOs with corresponding bulk phases is not that straightforward, and that for a number of 2D TMO phases perhaps the corresponding bulk phase has not been chosen properly.
The AIMD as performed, imposing periodic boundary conditions on the structures, tends to overestimate structural stability: lateral periodicity mitigates outofplane movements of the atoms and artificially enhances structural integrity, and may result in structural integrity for structures that would otherwise curl up or even disintegrate. Furthermore, the results presented here are the outcome of 7 ps simulations; prolonged simulations might yield different results with respect to the stability of the structures. We are confident about our approach consisting of AIMD simulation and subsequent relaxation of AIMD output configurations, though, because of the proper prediction of hV_{2}O_{3}: of all the structural and magnetic groundstate 2D TMO configurations identified in this study, only hV_{2}O_{3} has been experimentally realized so far,^{15,16,23} and our simulations indeed resulted in thermal stability for this phase. That hV_{2}O_{3} has been realized in a buckled form while our simulations indicate that the planar configuration is the energetically more favorable configuration for this phase, does not detract from this: our calculations suggest that hV_{2}O_{3} may be realized as freestanding smoothly corrugated planar nanosheets; the reported buckling of hV_{2}O_{3} may be due to its realization on a Pd(111) support.
Our method of AIMD simulation and subsequent relaxation of AIMD output configurations yields more reliable stability results than approaches that depend on AIMD simulation alone: Of all the 2D TMO phases identified in this study, other than hV_{2}O_{3}, only hMnO has been found reported on before, in a study that based on AIMD simulation only and finding no structure destruction concluded hMnO to be thermally stable up to temperatures of at least 500 K.^{28} Our method, however, indicates that hMnO is thermally unstable at 300 K, already, and that any future experimental realization of an atomically thin 2D hexagonal MnO will more likely be of MnO in the tMO configuration. Besides hMnO, 15 more of the hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} groundstate configurations were found to show no structure destruction during 300 K AIMD simulation; only six of these, however, were also found to be thermally stable at 300 K. The discovery of the thermally stable tMO phases in addition shows that postAIMD relaxation of AIMD output configurations may also reveal new phases that otherwise would have remained undisclosed.
Electronic and magnetic properties of the 2D TMOs
To further investigate the magnetic properties of the 2D TMOs and to disclose their electronic structure, we calculated the electronic band structures and determined the bandgaps and atomic magnetic moments and Bader charges of the magnetic groundstate configurations, using the PBE and HSE06 functionals. A summary of the HSEobtained results can be found in Table 1 and Fig. 6. Table S4 and Fig. S3 include the PBE results and orbitalresolved band structures.
From the comparison made in Table S4 and Fig. S3 between PBE and HSEcalculated electronic and magnetic properties, it can be seen that, in terms of an enlarged bandgap, HSE gives a better description of the strongly correlated d electrons than PBE. In particular, HSE opened bandgaps for sqMnO, hCr_{2}O_{3}, sqTiO_{2}, sqVO_{2}, and sqMnO_{2}, making these phases no longer metals as predicted by PBE, but semiconductors, semimetals, and halfmetals instead. The qualitative discrepancy between PBE and HSE occurs only when describing the electronic ground state of the 2D TMOs. For the magnetic ground state, the two approaches (i.e., PBE and HSE bandstructure calculation of an identical PBErelaxed atomic configuration) always give the same results. Regarding the Bader analysis: HSE always gives values for the atomic partial charges that are slightly larger (by 0.1–0.3e) than PBEcalculated values. Similar to the electronic charges, the magnetic moments on the atoms (that were obtained by evaluating spinup and spindown electron densities inside Bader volumes) were also found to be slightly higher (by 0.2–0.5 μ_{B}) when using HSE in comparison with PBEcalculated values. Our results therefore suggest that for obtaining a qualitative description of the magnetism and charge distribution of the 2D TMOs, DFT calculations suffice. Gaining a qualitatively correct picture of the electronic structure, however, requires more advanced methods such as using the hybrid HSE06 functional that incorporates a contribution of HF exchange. The effect of this HF correction on a particular TMO phases depends on the elements, their valence states, the levels of the atomic orbitals, as well as on the crystal geometry. The general trend, however, is that the HF correction lowers the energy levels of occupied states and lifts the levels of unoccupied states, and has a strong impact on the energy levels of the itinerant d electrons. The partial atomic charges and the magnetic moments on the atoms are determined from (total, and spinup and spindown) electron densities inside Bader atomic volumes. As the main effect of the HF correction is on the eigenvalues of the states rather than on the electrondensity distribution, the partial charges and the local magnetic moments obtained from HSE calculations are quite similar to those obtained by PBE calculations (and result in quite similar structural properties as well), while the impact on the electronic band structure is in general very significant.
Using the hybrid HSE06 functional, we found a rich variety of electronic properties among the 2D TMO phases. As can be seen from Table 1 and Fig. 6, of the 23 groundstate configurations, fifteen structures are predicted to be semiconductors and three to be metals with various magnetic orderings; sqMnO was found to be an antiferromagnetic semimetal; and hV_{2}O_{3}, sqScO_{2}, sqCrO_{2}, and sqMnO_{2}, are halfmetals that are either ferromagnets (hV_{2}O_{3}, sqScO_{2}, and sqCrO_{2}) or antiferromagnets (sqMnO_{2}). The magnetic moments on the atoms were evaluated from the spinup and spindown electron densities within Bader atomic volumes, and vary up to values of 4.6 μ_{B} for the transition metal atoms. Besides the four halfmetals, four semiconductors were also found to have nonoverlapping spinup and spindown bands and different bandgaps for spinup and spindown electrons; these semiconductors are: ferromagnetic hVO, hCr_{2}O_{3}, and sqVO_{2}, and ferrimagnetic hMn_{2}O_{3}. For the ferromagnetic halfmetal hV_{2}O_{3}, and for the nonmagnetic semiconductor hTiO, Diracconelike shaped dispersion curves were found. All these remarkable properties indicate that the 2D TMOs are bright candidates for electronic, magnetic, and spintronic applications. Exceptionally remarkable in this regard is hV_{2}O_{3}, that was found to be thermally stable up to temperatures of 700 K, and combines magnetism and a massless behavior of spinup electrons along with a wide bandgap of 6.2 eV for spindown electrons.
To understand the halfmetallic property of hV_{2}O_{3}, sqScO_{2}, sqCrO_{2}, and sqMnO_{2} in more detail, we performed a spinpolarization analysis of their densityofstates (DOS) at the Fermi level. The spin polarization P is defined as
where D(E_{F}) is the magnitude of the DOS at the Fermi level for spinup (↑) and spindown (↓) states. The spin polarization serves as a criterion to determine the extent of spin polarization, hence the degree of halfmetallicity, of a material.^{61,62,63} P = ±1 indicates that a system is halfmetallic, whereas P = 0 shows that a system has an equal amount of spinup and spindown states at the Fermi level. DOS analysis indeed showed that for hV_{2}O_{3}, sqScO_{2}, sqCrO_{2}, and sqMnO_{2}, the spin polarization is equal to the ideal value of 1.
We have presented the results from our systematic firstprinciples study of atomically thin 2D TMOs. For the five early 3d transition metals Sc, Ti, V, Cr, and Mn, four different 2D TMO phases were designed, namely hMO, sqMO, hM_{2}O_{3}, and sqMO_{2}, and we investigated their structural and magnetic groundstate configurations, considering various magnetic orderings and planar and monosided buckled configurations. The 20 structural and magnetic groundstate configurations for these phases were all found to have negative formation energies with respect to the elemental transition metal bulk phases and the paramagnetic oxygen molecule. The concavehull plot of these formation energies indicates that all the 2D TMOs are energetically stable at their respective stoichiometries.
AIMD simulation at temperatures of 300 and 700 K, and subsequent 0 K relaxation of AIMD output configurations, were carried out to examine the thermal stability of the 2D TMO phases. Of the 20 hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} groundstate configurations, 5 were found to be thermally stable; metastable sqMnO was found to be thermally stable at 300 K and thermally unstable at 700 K, 2D square sqMnO transforming into a 2D hexagonal MnO phase at temperatures of 400 K and higher; and 14 configurations were found to be thermally unstable. The unstable configurations include all sqMO_{2} phases, and all hMO phases. The postAIMD relaxations revealed a 2D hexagonal tMO phase that is a \(\sqrt 3\) × \(\sqrt 3\) reconstruction of the hMO phase; however, that is thermally stable for V, Cr, and Mn. This brings the total number of 2D TMOs identified in this study that may be realized as freestanding nanosheets to nine. These phases are: sqTiO, sqVO, and sqMnO; hSc_{2}O_{3}, hV_{2}O_{3}, and hMn_{2}O_{3}; and tVO, tCrO, and tMnO; of all these, only hV_{2}O_{3} has been experimentally realized so far. Our method of AIMD simulation and subsequent relaxation of AIMD output configurations yields more reliable results than approaches that depend on AIMD simulation alone: Of all the 2D TMO phases identified in this study, other than hV_{2}O_{3}, only hMnO was found reported on before, in a study that, based on AIMD simulation only, predicts hMnO to be thermally stable. Our method, however, indicates that hMnO is thermally unstable, and that any future experimental realization of atomically thin 2D hexagonal MnO will more likely be of MnO in the tMO phase. Our findings furthermore suggest that all thermally stable phases will show smooth corrugation upon realization. The thermally unstable 2D TMO phases can most likely not exist as freestanding slabs but may very well be stabilized when using an appropriate support.
A rich variety of electronic and magnetic properties was discovered for the 2D TMOs identified in this study, using the HSE06 hybrid functional. In particular, sqMnO is predicted to be a semimetal with antiferromagnetic ordering; hV_{2}O_{3}, sqScO_{2}, and sqCrO_{2} were found to be ferromagnetic halfmetals, while sqMnO_{2} is an antiferromagnetic halfmetal; and Diracconelike bands were found for the nonmagnetic semiconductor hTiO and the ferromagnetic halfmetal hV_{2}O_{3}. The magnetic moments on the transition metal atoms vary up to values of 4.6 μ_{B}. All these remarkable properties indicate that the 2D TMOs are bright candidates for electronic, magnetic, and spintronic applications. Exceptionally remarkable in this regard is planar hV_{2}O_{3}, that combines magnetism and a massless behavior of spinup electrons along with a wide bandgap of 6.2 eV for spindown electrons, and was found to be thermally stable up to temperatures of 700 K. The hybrid HSE06 functional gives a scenario of the electronic properties for the 2D TMOs that significantly differs from the one obtained using DFT: in general, HSE successfully opened up a bandgap for materials which were predicted to be metals by traditional DFT. This shows the necessity of using more advanced electronic structure methods to treat these strongly correlated systems correctly.
The current study assessed the stability of the 2D TMO phases and highlighted their remarkable electronic and magnetic properties, presenting an opportunity for experimentalists of targeted synthesis of these novel 2D TMO materials, which hold great potential for electronic and spintronic applications. For future work, a thorough study of the growth process and substrate effects is crucial to the successful realization of these 2D nanomaterials. Furthermore, a comprehensive study of point defects such as monovacancies, interstitials, antisites, and dopants, and the mutual interaction between these different kinds of defects, will open up the possibility of successful defect engineering in these 2D TMOs.
Methods
Totalenergy calculations
The DFT calculations were performed using the first principles’ Vienna Ab initio Simulation Package^{31,32,33} (VASP). Within the projectoraugmented wave (PAW) framework,^{34,35} the exchange and correlation energy terms were described using the PBE generalized gradient approximation (GGA) functional.^{36,37} The cutoff energy of the wave functions was set to 700 eV, and the cutoff energy of the augmentation functions to 850 eV. All calculations were carried out using conventional unit cells or 2 × 2 supercells, dependent on the input configurations’ magnetic ordering; except for hMO, which requires a 3 × 3 supercell to accommodate the FiM ordering. Figure 1 illustrates the considered antiferromagnetic orderings for the four 2D TMO input geometries and their corresponding simulation cell sizes. Different starting values for the magnitudes of the magnetic moments on the TM atoms were considered as well, with input values of 0.0 μ_{B} for nonmagnetic calculations, and input values of 1.0, 2.0, 3.0, 4.0, and 5.0 μ_{B} for magnetic calculations. To avoid spurious interactions between layers, a vacuum slab that is larger than 20 Å was included in all simulation cells. The electronic wave functions were sampled on grids in inverse proportion to simulation cell size, using a 16 × 16 × 1 Γcentered kmesh for the conventional unit cells. Cutoff energies, kmesh, and height of the vacuum slab were all tested to ensure energy convergence within 1 meV/atom. The structures were structurally and magnetically optimized, keeping the cell volume fixed to avoid collapse of the vacuum slab separating the model layers, and using energy and atomic force convergence criteria of 10^{6} eV and 10^{2} eV/Å, respectively. The calculations are valid for a temperature of 0 K and a pressure of 0 GPa. Zeropoint vibration contributions have been neglected. Noncollinear magnetism and spin–orbit coupling have not been considered.
Bandstructure analysis
The electronic structure of the PBErelaxed configurations was evaluated using the hybrid HSE06 functional.^{26} The fraction of HF exchange for these calculations was set to 0.25, resulting in a \(\frac{1}{4}\) : \(\frac{3}{4}\) hybridization of the HF exchange energy and PBE exchange energy, and the cutoff energy of the wave functions and the augmentation functions to 500 and 600 eV, respectively. Electronic band structures obtained from supercells were unfolded using the method by Tomić et al.^{64}
AIMD simulations
The AIMD simulations were performed using 72atom 6 × 6 supercells for the hMO phases, 100atom 5 × 5 supercells for the sqMO phases, 80atom 4 × 4 supercells for the hM_{2}O_{3} phases, and 72atom 5 × 5 supercells for each of the sqMO_{2} phases, except sqMnO_{2}, which was simulated using a 108atom 6 × 6 supercell to accommodate its magnetic ordering. For each of the structures, with a time step of 1 fs, a 2 ps initial equilibration and a 5 ps subsequent canonical (NVT) ensemble simulation using a Nosé thermostat^{49,50,51} was carried out, at simulation temperatures of 300 and 700 K. The AIMD calculations were performed including the Γpoint only and using a cutoff energy of 400 eV for the wave functions and a cutoff energy of 560 eV for the augmentation functions. After the AIMD simulations, AIMD supercell output configurations were relaxed at high accuracy at 0 K again, to see if the structures had remained topologically equivalent.
Data availability
Details on the crystal structures and calculation settings are provided here and the Supplementary Information. The calculation data will be stored in the Data Repository of Utrecht University, and are available from the authors upon request.
References
Novoselov, S. K. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Butler, S. Z. et al. Progress, challenges, and opportunities in twodimensional materials beyond graphene. ACS Nano 7, 2898–2926 (2013).
Bhimanapati, G. R. et al. Recent advances in twodimensional materials beyond graphene. ACS Nano 9, 11509–11539 (2015).
Mott, N. F. Metal–insulator transition. Rev. Mod. Phys. 40, 677–683 (1968).
Imada, M., Fujimori, A. & Tokura, Y. Metalinsulator transitions. Rev. Mod. Phys. 70, 1039–1263 (1998).
Xu, S., Shen, X., Hallman, K. A., Haglund, R. F. Jr. & Pantelides, S. T. Unified bandtheoretic description of structural, electronic, and magnetic properties of vanadium dioxide phases. Phys. Rev. B 95, 125105 (2017).
Park, J. H. et al. Measurement of a solidstate triple point at the metal–insulator transition in VO_{2}. Nature 500, 431–434 (2013).
Wegkamp, D. et al. Instantaneous band gap collapse in photoexcited monoclinic VO_{2} due to photocarrier doping. Phys. Rev. Lett. 113, 216401 (2014).
Bahlawane, N. & Lenoble, D. Vanadium oxide compounds: structure, properties, and growth from the gas phase. Chem. Vap. Depos. 20, 299–311 (2014).
Schwingenschlögl, U. & Eyert, V. The vanadium Magnéli phases V_{n}O_{2n−1}. Ann. Phys. (Leipz.) 13, 475–510 (2004).
Kitchaev, D. A. et al. Energetics of MnO_{2} polymorphs in density functional theory. Phys. Rev. B 93, 045132 (2016).
Li, Y.F., Zhu, S.C. & Liu, Z.P. Reaction network of layertotunnel transition of MnO_{2}. J. Am. Chem. Soc. 138, 5371–5379 (2016).
Chang, H. L. M., You, H., Guo, J. & Lain, D. J. Epitaxial TiO_{2} and VO_{2} films prepared by MOCVD. Appl. Surf. Sci. 48/49, 12–18 (1991).
Makarevich, A. M. et al. Chemical synthesis of high quality epitaxial vanadium dioxide films with sharp electrical and optical switch properties. J. Mater. Chem. C. 3, 9197–9205 (2015).
Surnev, S. et al. Growth and structure of ultrathin vanadium oxide layers on Pd(111). Phys. Rev. B 61, 13945–13954 (2000).
Surnev, S., Kresse, G., Ramsey, M. G. & Netzer, F. P. Novel interfacemediated metastable oxide phases: vanadium oxides on Pd(111). Phys. Rev. Lett. 87, 086102 (2001).
Omomo, Y., Sasaki, T., Wang, L. & Watanabe, M. Redoxable nanosheet crystallites of MnO_{2} derived via delamination of a layered manganese oxide. J. Am. Chem. Soc. 125, 3568–3575 (2003).
Sun, Z. et al. Generalized selfassembly of scalable twodimensional transition metal oxide nanosheets. Nat. Commun. 5, 3813 (2014).
Xiao, X. et al. Scalable salttemplated synthesis of twodimensional transition metal oxides. Nat. Commun. 7, 11296 (2016).
Aryasetiawan, F. & Gunnarsson, O. The GW method. Rep. Prog. Phys. 61, 237–312 (1998).
Ataca, C., Şahin, H. & Ciraci, S. Stable, singlelayer MX_{2} transitionmetal oxides and dichalcogenides in a honeycomblike structure. J. Phys. Chem. C. 116, 8983–8999 (2012).
Rasmussen, F. A. & Thygesen, K. S. Computational 2D materials database: electronic structure of transitionmetal dichalcogenides and oxides. J. Phys. Chem. C. 119, 13169–13183 (2015).
Kresse, G., Surnev, S., Ramsey, M. G. & Netzer, F. P. Firstprinciples calculations for V_{x}O_{y} Grown on Pd(111). Surf. Sci. 492, 329–344 (2001).
Vittadini, A. & Casarin, M. Ab Initio modeling of TiO_{2} nanosheets. Theor. Chem. Acc. 120, 551–556 (2008).
Dudarev, S. L., Botton, G. A., Savrasov, S. Y., Humphreys, C. J. & Sutton, A. P. Electronenergyloss spectra and the structural stability of nickel oxide: an LSDA+U study. Phys. Rev. B 57, 1505–1509 (1998).
Krukau, A. V., Vydrov, O. A., Izmaylov, A. F. & Scuseria, G. E. Influence of the exchange screening parameter on the performance of screened hybrid functionals. J. Chem. Phys. 125, 224106 (2006).
Kan, M., Zhou, J., Sun, Q., Kawazoe, Y. & Jena, P. The intrinsic ferromagnetism in a MnO_{2} monolayer. J. Phys. Chem. Lett. 4, 3382–3386 (2013).
Kan, E. et al. Twodimensional hexagonal transitionmetal oxide for spintronics. J. Phys. Chem. Lett. 4, 1120–1125 (2013).
Wang, J. & Zhang, Y. Topologic connection between 2D layered structures and 3D diamond structures for conventional semiconductors. Sci. Rep. 6, 24660 (2016).
Boukhvalov, D. W. Stable antiferromagnetic graphone. Phys. E 43, 199–201 (2010).
Kresse, G. & Hafner, J. Ab initio moleculardynamics simulation of the liquidmetalamorphoussemiconductor transition in germanium. Phys. Rev. B 49, 14251–14269 (1994).
Kresse, G. & Furthmüller, J. Efficiency of AbInitio total energy calculations for metals and semiconductors using a planewave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for Ab Initio totalenergy calculations using a planewave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Blöchl, P. E. Projector AugmentedWave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector AugmentedWave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple – errata. Phys. Rev. Lett. 78, 1396 (1997).
Bader, R. F. W. Atoms in Molecules: A Quantum Theory. (Oxford University Press, Oxford, 1990).
Henkelman, G., Arnaldsson, A. & Jónsson, H. A fast and robust algorithm for Bader decomposition of charge density. Comput. Mater. Sci. 36, 354–360 (2006).
Yu, M. & Trinkle, D. R. Accurate and efficient algorithm for Bader charge integration. J. Chem. Phys. 134, 064111 (2011).
Karlický, F., Zbořil, R. & Otyepka, M. Band gaps and structural properties of graphene halides and their derivates: a hybrid functional study with localized orbital basis sets. J. Chem. Phys. 137, 034709 (2012).
Komsa, H.P. & Krasheninnikov, A. V. Native defects in bulk and monolayer MoS_{2} from first principles. Phys. Rev. B 91, 125304 (2015).
Mackrodt, W. C., Middlemiss, D. S. & Owens, T. G. Hybrid density functional theory study of vanadium monoxide. Phys. Rev. B 69, 115119 (2004).
Franchini, C., Podloucky, R., Paier, J., Marsman, M. & Kresse, G. Groundstate properties of multivalent manganese oxides: density functional and hybrid density functional calculations. Phys. Rev. B 75, 195128 (2007).
Schrön, A., Rödl, C. & Bechstedt, F. Energetic stability and magnetic properties of MnO in the rocksalt, wurtzite, and zincblende structures: influence of exchange and correlation. Phys. Rev. B 82, 165109 (2010).
Guo, Y., Clark, S. J. & Robertson, J. Electronic and magnetic properties of Ti_{2}O_{3}, Cr_{2}O_{3}, and Fe_{2}O_{3} calculated by the screened exchange hybrid density functional. J. Phys.: Condens. Matter 24, 325504 (2012).
Zhu, L., Zhou, J., Guo, Z. & Sun, Z. Metal−metal bonding stabilized ground state structure of early transition metal monoxide TM−MO (TM=Ti, Hf, V, Ta). J. Phys. Chem. C. 120, 10009–10014 (2016).
Fang, C. M., Van Huis, M. A., Sluiter, M. H. F. & Zandbergen, H. W. Stability, structure and electronic properties of γFe_{23}C_{6} from firstprinciples theory. Acta Mater. 58, 2968–2977 (2010).
Nosé, S. A. Unified formulation of the constant temperature molecular dynamics methods. J. Chem. Phys. 81, 511–519 (1984).
Nosé, S. Constant temperature molecular dynamics methods. Prog. Theor. Phys. Suppl. 103, 1–46 (1991).
Bylander, D. M. & Kleinman, L. Energy fluctuations induced by the Nosé thermostat. Phys. Rev. B 46, 13756–13761 (1992).
Bersuker, I. B. PseudoJahn–Teller Effect—a twostate paradigm in formation, deformation, and transformation of molecular systems and solids. Chem. Rev. 113, 1351–1390 (2013).
Jose, D. & Datta, A. Understanding of the buckling distortions in silicene. J. Phys. Chem. C. 116, 24639–24648 (2012).
Nijamudheen, A., Bhattacharjee, R., Choudhury, S. & Datta, A. Electronic and chemical properties of germanene: the crucial role of buckling. J. Phys. Chem. C. 119, 3802–3809 (2015).
Wang, Y. & Ding, Y. Unexpected buckled structures and tunable electronic properties in arsenic nanosheets: insights from firstprinciples calculations. J. Phys.: Condens. Matter 27, 225304 (2015).
Wang, J., Meng, J., Li, Q. & Yang, J. Singlelayer cadmium chalcogenides: promising visiblelight driven photocatalysts for water splitting. Phys. Chem. Chem. Phys. 18, 17029–17036 (2016).
Revard, B. C., Tipton, W. W., Yesypenko, A. & Hennig, R. G. Grandcanonical evolutionary algorithm for the prediction of twodimensional materials. Phys. Rev. B 93, 054117 (2016).
Singh, A. K., Mathew, K., Zhuang, H. L. & Hennig, R. G. Computational screening of 2D materials for photocatalysis. J. Phys. Chem. Lett. 6, 1087–1098 (2015).
Shang, S.L. et al. Lateral versus vertical growth of twodimensional layered transitionmetal dichalcogenides: thermodynamic insight into MoS_{2}. Nano Lett. 16, 5742–5750 (2016).
Fu, B., Ge, Y., Su, W., Guo, W. & Liu, C.C. A new kind of 2D topological insulators BiCN with a giant gap and its substrate effects. Sci. Rep. 6, 30003 (2016).
De Groot, R. A., Mueller, F. M., Van Engen, P. G. & Buschow, K. H. J. New class of materials: halfmetallic ferromagnets. Phys. Rev. Lett. 50, 2024–2027 (1983).
Fang, C. M., De Wijs, G. A. & De Groot, R. A. Spinpolarization in halfmetals. J. Appl. Phys. 91, 8340–8344 (2002).
Katsnelson, M. I. et al. Halfmetallic ferromagnets: from band structure to manybody effects. Rev. Mod. Phys. 80, 315–378 (2008).
Tomić, M., Jeschke, H. O. & Valentí, R. Unfolding of electronic structure through induced representations of space groups: application to Febased superconductors. Phys. Rev. B 90, 195121 (2014).
Momma, K. & Izumi, F. VESTA 3 for threedimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).
Acknowledgements
This project is financially supported by the Dutch science foundation NWO via a VIDI grant (grant no. 723.012.006) and by the European Research Council through an ERC Consolidator Grant (grant no. 683076). This work was carried out on the Dutch national einfrastructure with the support of SURF Cooperative and NWO Rekentijd (grant no. 16905). Figures of atomic structural models were produced using VESTA.^{65} W.F.L. gratefully acknowledges J.P. Chou and S. S. Gupta for valuable discussions. The authors furthermore appreciate the careful reading and helpful comments on the paper from A. van Blaaderen.
Author information
Authors and Affiliations
Contributions
H.v.G. performed the AIMD and postAIMD calculations, including the totalenergy calculations and bandstructure analysis for the tMO phases. W.F.L., M.A.v.H., and H.v.G. performed the totalenergy calculations and bandstructure analysis for the hMO, sqMO, hM_{2}O_{3}, and sqMO_{2} phases. H.v.G. wrote the paper, incorporating an early version of the paper by W.F.L. All authors contributed to discussions and commented on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
van Gog, H., Li, WF., Fang, C. et al. Thermal stability and electronic and magnetic properties of atomically thin 2D transition metal oxides. npj 2D Mater Appl 3, 18 (2019). https://doi.org/10.1038/s416990190100z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s416990190100z
This article is cited by

2D honeycomb transformation into dodecagonal quasicrystals driven by electrostatic forces
Nature Communications (2022)

XANES Investigations on Electronic Structure and Magnetic Properties of GaFeO3 Nanocrystals
Journal of Electronic Materials (2022)

Firstprinciples Investigations on the Magnetic, Electronic, and Optical Properties of HoneycombKagomeStructured Fe$$_{2}$$O$$_3$$ Monolayer
Journal of Superconductivity and Novel Magnetism (2022)

Density Functional Theory Study on Magnetic character and Mn Crystal Field Split Levels in Mndoped SnO Monolayer
Journal of Superconductivity and Novel Magnetism (2022)

Unsupervised discovery of thinfilm photovoltaic materials from unlabeled data
npj Computational Materials (2021)