Sustainable conversion of polyethylene plastic bottles into terephthalic acid, synthesis of coated MIL-101 metal–organic framework and catalytic degradation of pollutant dyes

Persistent environmental colored compounds, resistant to biodegradation, accumulate and harm eco-systems. Developing effective methods to break down these pollutants is crucial. This study introduces Ag-MIL-101 (Ag-MIL-101) as a composite and reusable catalyst that efficiently degrades specific colored organic pollutants (COPs) like Methylene blue (MB), 4-Nitrophenol (4-NP), and 4-Nitroaniline (4-NA) using sodium borohydride at room temperature. The MIL-101 was synthesized using Terephthalic acid (TPA) derived from the degradation of Polyethylene Terephthalate (PET) plastic waste, with the assistance of zinc chloride. To further investigation, the kinetics of degradation reaction was studied under optimized conditions in the presence of Ag-MIL-101 as catalyst. Our results demonstrated the remarkable efficiency of the degradation process, with over 93% degradation achieved within just 8 min. The catalyst was characterized using FTIR, XRD, FESEM, and TEM. In this study, the average particle size of Ag-MIL-101 was determined using SEM and XRD analysis. These methods allow us to accurately and precisely determine the particle size. We determined the reaction rate constants for the degradation of each COP using a pseudo first-order kinetic equation, with values of 0.585, 0.597 and 0.302 min−1 for MB, 4-NP, and 4-NA, respectively. We also evaluated the recyclability of the catalyst and found that it could be reused for up to three cycles with only a slight decrease in efficiency (10–15%). Overall, our findings highlight the promising application of Ag-MIL-101 as an effective catalyst for the degradation of COPs, emphasizing the importance of optimizing reaction conditions to achieve enhanced efficiency.


Chemicals and materials
We obtained all the chemicals (Cr(NO 3 ) 3 •9H 2 O, ZnCl 2 •H 2 O, Urea, Ethylene glycol (EG), Dimethyl formamide (DMF), Ethanol (EtOH), Methylene blue (MB), 4-Nitrophenol (4-NP), and 4-Nitroaniline (4-NA)) from Merck and Sigma-Aldrich Chemical companies.These chemicals were of analytical grade and used without any further purification.The used plastic waste bottles in this study were obtained from a public recycling center.TPA, a crucial component, was derived from the degradation of discarded plastic bottles.

Catalytic depolymerization of PET
With slight modifications, the described methods were utilized to prepare the required terephthalic acid for MIL-101 synthesis 56,57 .Obtained PET water bottles from recycling facilities were washed, dried, and divided into 5 × 5 mm fragments (total weight: 5 g).The fragments were placed in a 50 mL glass flask with 20 g of ethylene glycol, equipped with a reflux condenser and a thermometer.A catalyst of 0.25 g ZnCl 2 : Urea (molar ratio 1:6) was added.Glycolysis of PET was conducted for 30 min at 170 ± 3 °C under atmospheric pressure, using a magnetic stirrer and an oil bath.After cooling to room temperature, 1000 mL of cold distilled water was added, the pH was adjusted to 3-4 using H 2 SO 4 (2 M) to obtain a white slurry, and the resulting product (TPA) was filtered to separate it from the residual PET pellets.The residual PET was dried at 70 °C until constant weight was achieved.PET conversion was calculated as 87% using the formula.

Preparation of MIL-101
Obtained TPA from the degradation of plastic waste bottles (the previous step) was used and MIL-101 was synthesized using the hydrothermal method 58,59 .Initially, terephthalic acid (3.32 g), Cr(NO 3 ) 3 •9H 2 O (8.0 g), and hydrofluoric acid (0.8 mL) were added to 100 mL of deionized water.The resulting mixture was stirred for 0.5 h using a magnetic stirrer.Subsequently, the mixture was transferred into a Teflon-lined autoclave and heated at 220 ± 5 °C for 8 h, followed by slow cooling to room temperature (5 °C/min).The produced green-solid was separated by centrifugation at 4000 rpm and washed with hot water until the supernatant became colorless.After vacuum drying at 80 °C, crude MIL-101 was obtained.To further purify the product and remove any remaining TPA and Cr(NO 3 ) 3 •9H 2 O, the crude MIL-101 was refluxed in dimethyl formamide (DMF) solvent for 12 h.The product was then thoroughly washed with ethanol at 40 °C for 2 h.Finally, after drying in an oven at 80 °C for 10 h, pure MIL-101 powder was obtained.

Preparation of Ag-MIL-101 composite
According to the literature, Ag-MIL-101 composite was synthesized using an in-situ precipitation method 58 .In order to achieve Ag-MIL-101 with maximum silver immobilization on its surface while minimizing losses during washing procedures, MIL-101 (10 g) were mixed with different concentrations of silver nitrate (2-25 mL, 0.3 M).The degree of silver loss was assessed through atomic absorption analysis, and eventually, the ideal conditions were employed for fabricating the optimized ratio of Ag on MIL-101.In optimized conditions, pre-synthesized MIL-101 (10 g) was added to deionized water (50 mL) and mixed at room temperature for 0.5 h.Subsequently, a solution of AgNO 3 (10 mL, 0. 12 h.The resulting product was thoroughly washed with deionized water (3 × 50 mL), ethanol (3 × 50 mL) and subsequently dried under vacuum at 80 °C overnight.The resulting Ag-MIL-101 composite, exhibiting green color, was designated as Ag-MIL-101.

Characterization methods
In this study, the monomer TPA, derived from PET decomposition, 4-NP, and 4-aminophenol (4-AP) were characterized using 1 H-NMR spectroscopy.The spectra were recorded in DMSO-d 6 (or CDCl 3 ) with a Bruker Avance DRX-400 MHz spectrometer, using tetramethylsilane (TMS = 0.00 ppm) as the internal standard.Also, FT-IR spectroscopy was employed to identify the linkages and functional groups present in the MOFs.The spectra were recorded using a JASCO 6300 spectrophotometer in the wavenumber range of 400-4000 cm −1 , with KBr as the matrix.The crystal structure of MOFs were investigated using the D8-ADVANCE XRD instrument (Bruker, Germany) and Cu-Kα radiation.The scanning range was set from 10 to 90° at a rate of 2°/min.The surface morphology, average particle size and elemental composition of the synthesized samples were analyzed using the TESCAN BRNO field-emission scanning electron microscope (FE-SEM) at 15.0 kv, along with energy-dispersive X-ray spectroscopy (EDS).Transmission electron microscopy (TEM) images obtained from the Philips EM 208S instrument were used to further examine the sample morphology.Additionally, the progress of COP reduction reactions was monitored using a UV-Vis spectrophotometer equipped with a quartz cell, and absorption measurements were recorded to evaluate changes over time.

Catalytic degradation of COPs
To assess the effectiveness of the synthesized Ag-MIL-101 catalyst, a catalytic degradation test was performed using MB, 4-NP and 4-NA as model COPs.In the experimental procedure, 1 × 10 -3 -15 × 10 -3 g of Ag-MIL-101 were added to a 50 mL aqueous solution containing 50 ppm of COP (MB, 4-NP or 4-NA).In an effort to diminish the surface adsorption impact of COPs by the catalyst, the solution underwent agitation using a magnetic stirrer, allowing for a thorough examination of changes in adsorption intensity.The results indicated a marginal reduction in the magnitude of adsorption changes, with the intensity remaining unchanged following 20 min of agitation.Therefore, in each reaction, the reaction mixture was initially stirred for 30 min to ensure effective interaction between the catalyst and the COP, thereby establishing an adsorption-desorption equilibrium between them.Then, a 0.1 M NaBH 4 solution (15-40 mL) was added to the reaction mixture.The reaction mixture was continuously stirred using a magnetic stirrer at room temperature throughout the duration.At regular intervals, 2.5 mL samples of the reaction solution were taken and rapidly diluted with 5 mL of water.The catalyst was subsequently separated from the mixture by centrifugation.The progress of color degradation was quantified using UV-Vis spectroscopy, specifically by measuring absorbance changes at the corresponding maximum wavelength (Table 1).The objective was to optimize the degradation conditions of the COPs catalyst by investigating factors such as reaction time, sodium borohydride dosage, catalyst efficiency, recovery, and reusability.

Molecular structure
The TPA produced in this study was purified and its identity was confirmed using the 1 H-NMR technique.The 1 H-NMR spectrum (400 MHz, DMSO-d 6 ) showed peaks at δ = 13.28 ppm (for -OH) and 8.05 ppm (for aromatic C-H).Also, the structural identity of 4-NP and 4-aminophenol (4-AP) (the reduced product of 4-NP) were determined and compared using 1 H-NMR spectroscopy (Fig. 2).After the completion of the reduction reaction, the reaction solution was transferred to a separating funnel and extracted with diethyl ether.Subsequently, the resulting mixture underwent purification via packed column chromatography; 4-NP: The samples were analyzed using FT-IR spectroscopy.To facilitate a better and easier comparison, the results of the infrared analyses for the two compounds investigated in this research, MIL-101 and Ag-MIL-101, were placed side by side (Fig. 3).Considering the presence of similar functional groups in these two compounds, it is expected that the IR spectra of MIL-101 and Ag-MIL-101 would show significant similarities.The comparison of the two IR analyses in the image confirms this expectation.Furthermore, the results indicate that the incorporation of Ag 3 PO 4 onto the surface of MIL-101 did not significantly alter the structure and bonds of MIL-101.A more detailed examination of the IR spectra of MIL-101 and Ag-MIL-101 reveals overlapping absorption bands at wavelengths of 3460, 1595, 1389, 1125, 920, 815, 750, 612, and 549 cm −1 .The broad band near 3460 cm suggests the presence of crystalline water in the sample 59 .An intense band at around 1389 cm −1 indicates O-C-O symmetry.Additionally, the absorption band at 1595 cm −1 is related to the vibrational anisotropy of the dicarboxylate organic ligand 58,59 .The absorption at 750 and 920 cm −1 are associated with the C-H bands 60 .The characteristic band at 612 cm −1 corresponds to Cr-O stretching 58 .Importantly, compared to MIL-101, the absorption spectrum of the Ag-MIL-101 compound exhibits two additional and novel absorption bands at wavelengths of 1031 and www.nature.com/scientificreports/549 cm −1 , which can be attributed to the presence of the phosphate functional group.The absorption bands near 1031 and 549 cm −1 correspond to P-O stretching and O-P-O bending vibrations of PO 4 3− , respectively 58,61 .The presence of these bands indicates the successful manufacturing process of the Ag-MIL-101 composite.Moreover, the production process of the Ag-MIL-101 composite did not cause any noticeable changes in the preexisting bonds and functional groups.
In conclusion, the samples were analyzed using FT-IR spectroscopy.The IR spectra of MIL-101 and Ag-MIL-101 show significant similarities, confirming the presence of similar functional groups.The addition of Ag  www.nature.com/scientificreports/ the phosphate functional group, confirming the successful manufacturing process without causing noticeable changes to the preexisting bonds and functional groups.

Crystalline and phase structure
XRD analysis has proven to be a valuable tool for confirming the formation and stability of NPs in MOFs.In this study, the representative XRD pattern of Ag-MIL-101 was compared to that of MIL-101, as shown in Fig. 4. Despite the adsorption of Ag 3 PO 4 and subsequent reduction to Ag NPs, the crystallinity of MIL-101 remained intact.However, there was a noticeable shift in the peak positions following the adsorption of Ag 3 PO 4 .Fortunately, the XRD analysis confirmed that the as-synthesized Ag-MIL-101 possesses a structural arrangement similar to that of MIF-101 (Fig. 4).The crystal structures of MIL-101 and Ag-MIL-101 were found to be isostructural to each other and exhibited similar porosity.In these structures, the equatorial or axial sites of each Cr 3+ ion are coordinated by O atoms from TPA unit linkers resulting in the formation of 3D MOFs.The addition of Ag 3 PO 4 to MIL-101 leads to a noticeable darkening of its green color, while the crystalline structure remains unaffected, signifying the compatibility between these two materials.The slight displacement of diffraction peaks corresponding to MIL-101 can be attributed to the presence of Ag 3 PO 4 .To investigate the crystal structure and phase composition of the samples, X-ray diffraction (XRD) analysis was employed.The XRD pattern of the MIL-101 sample is depicted in Fig. 4. The obtained XRD peaks at 2θ angles of 5.

Morphology and elemental composition
In this study, morphological and elemental analysis of the prepared Ag-MIL-101 compound samples was carried out using SEM, EDS, and TEM techniques.The SEM image (Fig. 5a www.nature.com/scientificreports/ the presence of silver nanoparticles (Fig. 6).These silver nanoparticles facilitate efficient electron transfer between energy levels, thereby improving the speed and efficiency of the catalytic reaction.

Optical properties
The optical properties of materials are essential for their photocatalytic performance.Using UV-vis absorption spectroscopy, we investigated these properties in our study.Comparing the Ag-MIL-101 composite to The smaller band gap of the composite suggests more efficient utilization of visible light, highlighting its potential for photocatalytic applications (Fig. 7).

Optimal conditions for the degradation of COPs
The use of catalysts in chemical processes is crucial for enhancing speed and reaction efficiency.Increasing the catalyst dosage does not always improve efficiency and can lead to economic wastage.Therefore, optimizing catalyst dosage is crucial for environmental protection and cost-effectiveness.Initially, we investigated the importance of key compounds in the degradation of COP to determine the optimal reaction conditions (Table 2).Each type of COP (MB, 4-NP and 4-NA) was individually evaluated to establish the most appropriate conditions.The degradation of an equal amount of COP (50 mL, 50 ppm) was measured and assessed in all reactions.Initially, the degradation of the COP was examined in the presence of MOF and NaBH 4 separately or simultaneously.
The photocatalytic degradation reaction of the desired COPs was investigated in the presence of the Ag-MIL-101 composite, and the results are reported in Table 2 (entry 8).The photocatalytic capability of Ag-MIL-101 composite in degrading COP compounds was investigated under light radiation at room temperature.A solution containing COP compound (50 mL, 50 ppm) and Ag-MIL-101 composite (5 × 10 -3 g) was exposed to sunlight, and the change in UV-vis absorption of COPs was measured.Results demonstrated that, while the photocatalytic reaction had its advantages, the efficiency of the composite in the presence of NaBH 4 far exceeded the degradation of COPs under light radiation (Table 2, entry 8).To examine the impact of light absorption on the photodegradation of the desired COPs, photolysis of these compounds was investigated using sunlight without catalyst.However, after 120 min, no significant alteration in the absorption intensity at the maximum wavelength of the COPs was observed.
The results demonstrated a significant decrease in COP degradation in the absence of either NaBH 4 or Ag-MIL-101, particularly with prolonged reaction time.These findings highlight the necessity of both compounds (NaBH 4 and Ag-MIL-101) for achieving satisfactory efficiency in the degradation of COPs.Furthermore, it can  www.nature.com/scientificreports/be concluded that silver metal plays a crucial catalytic role in the COP degradation reaction.In the absence of catalyst, the COP degradation reaction fails to occur, potentially due to a significant discrepancy between the energy level of the reducing agent (NaBH 4 ) and the acceptor (COP compound).The energy levels of these species remain distant, and the absorption intensity at λ max remains relatively constant, suggesting limited color reduction and degradation.However, the inclusion of the Ag-MIL-101 composite as a catalyst in the reaction mixture creates an intermediate electronic level through the presence of silver metal.This enables the facilitation of electron transfer between energy levels by reducing the necessary distance for electron transfers.As evident from the obtained results in Table 2 (Entries 6 and 7), the Ag 3 PO 4 compound can serve as an efficient catalyst for the degradation of COPs.Comparison of Entries 6 and 7 reveals that while Ag 3 PO 4 has limited capability in degrading COPs, the addition of NaBH 4 greatly enhances reaction efficiency and degradation rate.Sodium borohydride is thought to induce the reduction of silver ions and formation of Ag nanoparticles, enabling them to effectively catalyze the degradation of the desired COP compounds 9,64 .Considering our primary objective of conducting environmentally friendly processes and degrading environmental pollutants, we have overlooked application of Ag-MIL-101 composite as catalyst for the COP degradation reaction in the presence of NaBH 4 .Subsequently, all remaining reactions to find optimized conditions were conducted with the simultaneous presence of NaBH 4 and Ag-MIL-101 (Table 3).The degradation of desired COPs (50 mL, 50 ppm) was conducted and examined in the presence of various doses of Ag-MIL-101 (1 × 10 -3 -15 × 10 -3 g) and NaBH 4 (0.1 M, 10-40 mL).The experimental results demonstrate the positive impact of increasing the dosage of Ag-MIL-101 and NaBH 4 on the reaction rate and efficiency, confirming our initial expectations.Increasing the dosage of the Ag-MIL-101 and NaBH 4 leads to an increase in the number of reaction sites on the surface, resulting in improved overall efficiency of COP degradation and apparent reaction rate.The results, indicate that the degradation efficiency of the investigated COPs is not significantly  www.nature.com/scientificreports/affected by the use of doses higher than 5 × 10 -3 g of catalyst in each reaction.However, it should be noted that once the catalyst (or NaBH 4 ) dosage surpasses a certain threshold, the catalytic degradation efficiency of COPs reaches a saturation point.The obtained results, which can be found in Table 3, provide valuable insights.
The obtained results demonstrate a clear correlation between the degradation of the target COP and the decrease in intensity of its maximum absorption wavelength.Notably, the maximum absorption wavelengths for MB, 4-NP, and 4-NA COPs are measured at 663, 400, and 380 nm, respectively.It is noteworthy that the 4-NP exhibited a maximum absorption at 317 nm.However, when combined with NaBH 4 , the maximum absorption peak of 4-NP shifted to 400 nm.This shift in absorption wavelength is attributed to the inherent bathochromic properties of the 4-NP compound 65 .Consequently, in the evaluation and assessment of the catalytic degradation reaction of 4-NP, the alterations in absorption intensity at 400 nm wavelength were utilized as the primary parameter.Table 3 presents a summarized overview of the specific values of Ag-MIL-101 and NaBH 4 that were utilized to determine the optimal reaction conditions for the degradation of MB, 4-NP, and 4-NA COPs.
The results indicate that the degradation of the investigated COPs can be efficiently achieved within a short time (6-8 min) under optimized conditions, with an exceptional efficiency exceeding 93%.Also, it can be concluded that the Ag-MIL-101 composite can serve as a highly suitable catalyst for the efficient degradation of COPs present in real wastewater samples.
Subsequently, the reaction kinetics of each COP were evaluated under the identified optimal degradation conditions.In this study, we have concentrated on examining the kinetics of COP degradation reactions by specifically focusing on the reduction of absorption intensity at the corresponding maximum wavelengths.This choice was made based on the direct relationship between the change in absorption intensity and the percentage of degradation reaction progress.The following equation has been utilized in this study to determine the reaction efficiency of COP degradation in the presence of Ag-MIL-101: To analyze the degradation reaction kinetics of COPs, a concentration-time graph was prepared for the COPs.Due to the significantly higher concentration of NaBH 4 (0.1 M) compared to COPs, the reduction process was investigated as a pseudo-first-order reaction.[C o ] and [A o ] represented the initial concentration and absorbance intensity, respectively.Similarly, [C t ] and [A t ] represented the concentration and absorbance intensity during the reaction.Using the equation and the absorbance-concentration relationship, a ln ([C o ]/[C t ]) vs. time graph was plotted.The data were fitted to a linear trend line to obtain the reaction rate constant (k app , min −1 ).so: Under optimized conditions, the degradation reactions of COPs were examined with a specific emphasis on their kinetic behavior.The study revealed distinct rate constants for the degradation of various COPs: MB, 4-NP, and 4-NA exhibited rate constants of 0.58, 0.60, and 0.32 min −1 , respectively (Fig. 8).

Selective degradation of OPDs
The study aimed to examine the degradation behavior of COPs under specific experimental conditions.Equal quantities of two distinct COPs were introduced into a single batch and subjected to degradation under similar conditions at room temperature.The outcomes are detailed in Table 4.The findings indicate that the degradation process of MB and 4-NP lacks significant selectivity.However, when each of these pollutants is investigated alongside 4-NA, a substantial enhancement in the reaction's selectivity is observed.www.nature.com/scientificreports/

Proposed mechanism of COP degradation
While a comprehensive investigation into the degradation mechanism remains outstanding, existing literature posits a potential mechanism for the reduction of COPs (MB and 4-NP), illustrated in Fig. 9 39,66,67 .Studies suggest that the incorporation of doped silver metal sites onto the MIL-101 framework initiates a reduction in energy band gaps, thereby narrowing the energy level gap between the lowest unoccupied molecular orbital (LUMO) and highest occupied molecular orbital (HOMO) levels.Consequently, this facilitates active interactions between the metal active sites and the dye pollutants, leading to a notable acceleration in the reaction rate.
In this study, our objective was to utilize Ag-MIL-101 as a novel and efficient catalyst in catalytic degradation of COPs in the presence of NaBH 4 solution.The acquired outcomes were subsequently juxtaposed against the findings reported in comparable investigations, thereby elucidating the outstanding efficacy of the catalyst.It exhibited a notably elevated level of degradation progress, an accelerated reaction rate, and a reduced catalyst dosage-to-COP ratio.These findings underscore the superior benefits provided by this catalyst in comparison to alternative catalysts employed in prior studies (Table 5).
Furthermore, a comparison was made between the photocatalytic degradation results of methylene blue using various photocatalysts (Table 6).From an environmental perspective, catalysts that have better chemical stability, recyclability, and reusability are particularly important and also hold economic significance.These properties are crucial for the practical utilization of catalysts.Although the main objective of researchers in this study is the removal of pollutants and the presentation of efficient conditions for water treatment, it should be noted that the importance of catalyst recyclability in environmental preservation, waste reduction, and energy consumption cannot be underestimated.Therefore, in this study, we investigated the recoverability and reusability of the used catalyst.After the completion of the COP degradation reaction, the used catalysts were collected using filtration, centrifugation, washed, and dried overnight.The catalyst's efficiency in this study is directly impacted by the concentration of silver particles in its structure.Our findings indicate that the recycled catalyst significantly decreases in efficiency by approximately 10-15% after three recovery steps (Fig. 10a).These results emphasize the strong interactions between the silver component and the MOF matrix, which effectively prevent silver leaching during the recycling and cleaning processes.Consequently, this improves the stability and longevity of the catalyst, emphasizing its substantial implications in the respective domain.In addition, FT-IR analysis was performed on the catalyst before and after three cycles of experiments.Surprisingly, minimal differences were observed in the FT-IR pattern of the Ag-MIL-101 composite compared to the unreacted and fresh composite, suggesting that the functional groups remained unchanged throughout the three cycles (Fig. 10b).

Conclusion
In this study, TPA was synthesized from PET bottles through solvothermal catalytic degradation, aiming to reduce plastic waste.The Ag-MIL-101 composite, synthesized using chromium and silver salts, was selected as the optimal catalyst for COP degradation based on factors such as degradation efficiency, reaction conditions, and catalyst recoverability.The catalytic ability of Ag-MIL-101 in the degradation of COPs (MB, 4-NP, and 4-NA) in the presence of NaBH 4 was investigated.The results showed that under optimal conditions, the degradation of the examined COPs was achieved within 5-10 min with an efficiency of over 93%.The kinetics of the degradation reaction were evaluated, and the reaction rate constants for each COP was calculated.The Ag-MIL-101 catalyst demonstrated not only efficient COP degradation but also good recyclability and reusability, indicating its stability and excellent performance.Based on the advantages of the Ag-MIL-101 composite, its use in other catalytic reactions is recommended.This study presents an innovative approach to reducing environmental pollutants by utilizing plastic waste as a raw material for the production of a stable and recyclable catalyst.Further research is needed to optimize the process and evaluate its feasibility in large-scale applications.The study emphasizes the importance of using waste materials for sustainable solutions and provides an effective method  to address environmental challenges.Our future research will focus on investigating photocatalytic degradation using MIL-101 composites for the degradation of COPs and pharmaceutical pollutants.This research not only highlights the significant role of MOF composites in water treatment but also opens new perspectives for the development of highly efficient catalytic systems based on MOFs.The preparation conditions of the Ag-MIL-101 composite could be evaluated in future research to enhance its photocatalytic efficiency for the degradation of COPs.By doing so, the photocatalytic properties and effectiveness of the composite in the photodegradation reaction can be improved.

100 Figure 1 .
Figure 1.Synthesis of MOF composite derived from depolymerized PET as an efficient catalyst for the degradation of colored organic pollutants.

Table 2 .
The key role and simultaneous presence of Ag-MIL-101 and NaBH 4 in the catalytic degradation of COPs.Conditions: All reaction efficiencies were determined by measuring the degradation of COP solution (50 mL, 50 ppm) after 2 h of reaction time.a Deg.: Degradation.b The degradation of COPs was conducted under sunlight radiation, and the results were measured after 2 h reaction time.

Figure 9 .
Figure 9.The proposed mechanism for the reduction of MB and 4-NP in the presence of Ag-MIL-101.

Figure 10 .
Figure 10.(a) Catalytic efficiency of recycled catalyst, (b) FT-IR spectra of catalyst before and after three catalytic cycles.

Table 1 .
The maximum wavelength of each COP used in catalytic degradation reactions in the presence of NaBH 4 and Ag-MIL-101 catalyst.
Vol.:(0123456789) Scientific Reports | (2024) 14:12832 | https://doi.org/10.1038/s41598-024-60363-5 58,62,639.1,10.3, and 16.5° are in agreement with the literature, which confirms the presence of MIL-101 in the samples58,62,63.Moreover, the XRD pattern of the synthesized MIL-101 indicates its highly crystalline nature.The combined XRD patterns of MIL-101 and Ag-MIL-101 show distinctive peaks from MIL-101, Ag 3 PO 4 , and Ag nanoparticles, confirming successful synthesis of the composite.Comparative analysis reveals similar XRD patterns, except for the appearance of novel peaks at 2θ = 46.1 and 47.7, attributed to Ag nanoparticles, and peaks at 2θ = 52.6,55.0, and 57.2, attributed to Ag 3 PO 4 .Importantly, no significant shifts in MIL-101 peaks are observed in the XRD patterns of composites with Ag, Ag 3 PO 4 , and MIL-101.This suggests that incorporating Ag 3 PO 4 does not affect the crystal structure of MIL-101.

Table 3 .
Optimization of catalytic degradation conditions of COPs in the simultaneous presence of Ag-MIL-101 and NaBH 4 .
a Optimum conditions are bolded.

Table 4 .
The catalytic and selective degradation of COPs in the presence of Ag-MIL-101.Conditions: All reaction efficiencies were determined by measuring the degradation of COP solution (50 mL, 50 ppm), NaBH 4 (20 mL, 0.1 M) and Ag-MIL-101 (4 × 10 -3 g) after 20 min of reaction time.

Table 5 .
Comparison of catalytic reduction of MB and 4-NP in the presence of various catalysts.

Table 6 .
Comparison of photocatalytic reduction of MB in the presence of various catalysts.