Experimental study of the bond behavior of 400MPa grade hot-rolled ribbed steel bars in steel fibre reinforced concrete

Present studies show that steel fibres can improve the bond of steel bar in steel fibre reinforced concrete (SFRC) with a correlation to the fibre factor and the fibre distribution uniformity. As a foundation of high-flowability SFRC working together with 400 MPa grade hot-rolled ribbed (HRB400) steel bar in reinforced structures, the bond between them was evaluated through a series of pull-out testing on 48 specimens with a central arranged steel bar. The bond behaviours of steel bar were estimated with a constant bond length of 5d (d is the diameter of steel bar) embedded in high-flowability SFRC, the main research parameters included the ingot mill steel fibres with a fibre volume fraction varied from 0.8 to 2.0%, the strength grade C40 and C50 of SFRC or referenced conventional concrete, and the diameter of steel bars varied from 14 to 20 mm. Results showed that the high-flowability SFRC compacted with a slight vibration is beneficial to improve the bond failure pattern since steel fibres effectively eliminate the crack appeared on the SFRC blocks during the pulling out of steel bar, leading to all specimens failed with the steel bar pull out of SFRC blocks. The bond strength was dominant by the SFRC strength, and obviously strengthened with the increase of fibre volume fraction, while the peak-slip was slightly influenced by the diameter of steel bar. By conducting analyses of test data, equations for calculating the bond strength and the peak-slip are proposed accounting for the effect of steel fibres. Then the predicting method for the anchorage length is suggested linking with different design codes for concrete structures. Compared with test results of this study, a little shorter anchorage length of steel bar in SFRC is obtained from the specification of Chinese code JGJ/T46, which should be noticed to ensure a rational anchorage of ribbed steel bar in SFRC with ingot mill steel fibres.


List of symbols
Trial no.CsH4/d-v f Cs-strength grade, C4 expresses C40, and C5 expresses C50; H4-400 MPa grade hotrolled ribbed steel bar; d-diameter of steel bar (mm); v f -volume fraction of steel fibre (%) P The pull-out force (N) τ The average bond stress (MPa) τ u The bond strength of steel bar with SFRC (MPa) τ u0 The bond strength of steel bar embedded in concrete with the same matrix of SFRC (MPa) f t The tensile strength of SFRC (MPa) f t0 The tensile strength of concrete with the same matrix of SFRC (MPa) f y The yield strength of steel bar (MPa) d The diameter of steel bar (mm) l b The bonding length of steel bar (mm) The aspect ratio of steel fibre v f The volume fraction of steel fibre F The fibre factor near the steel bars, and stiffer of these fibers.Therefore, it is necessary to correctly evaluate the bond of highflowability SFRC with steel bars to ensure their working together in reinforced concrete structures.In this paper, an experimental study was carried out for the bond performance of the 400 MPa grade hotrolled ribbed (HRB400) steel bar embedded in high-flowability SFRC.Forty-eight specimens, divided into 24 groups, with a centrally arranged steel bar were prepared and tested using a central pull-out test method.The volume fraction of ingot mill steel fibre with a varying from 0.8 to 2.0% was considered to evaluate the contribution of high-flowability SFRC to the bond with HRB400 steel bars.Meanwhile, the influences of the strength of SFRC and the conventional concrete, and the diameter of steel bar, on the bond of HRB400 steel bars embedded in high-flowability SFRC were also experimentally studied.The loads and displacements were measured to determine the complete bond stress-slip curve of each specimen.And then the test results are analyzed on the failure pattern of specimens, and the effects of test factors on the bond behaviour of HRB400 steel bar embedded in high-flowability SFRC.Equations for predicting bond strength and slip accounting for the effect of steel fibres are proposed.Finally, linked with the specifications in codes 23,32,33 , a prediction equation for the anchorage length of steel bar embedded in high-flowability SFRC is suggested.

Experiment work Preparation of high-flowability SFRC
Raw materials used in this study included Grade 42.5 common Portland cement, Class-II fly ash, natural river sand, continuous grading crushed limestones, ingot mill steel fibre, and superplasticizer (water reducing agent).Physical and mechanical property of each material were tested according to related Chinese codes 34 .The cement was 3040 kg/m 3 in density, with an initial setting time of 170 min and a compressive strength of 44.2 MPa at a curing age of 28 days, which met the requirement of common Portland cement specified in Chinese code GB 175 35 .The fly ash was , which met the requirement of fly ash for concrete specified in Chinese code GB/T 1596 36 .The river sand was 2610 kg/m 3 in apparent density and 1653 kg/m 3 in closed volume density; the crushed limestone was continuous grading with a maximum particle size of 10 mm, 2800 kg/m 3 in apparent density, 1615 kg/m 3 in closed volume density, and a crushed index of 10.8%.They met the requirement of sand and crushed stone for concrete specified in Chinese code JGJ52 37 .The ingot mill steel fibre was produced with an average length l f = 32 mm, an equivalent diameter d f = 0.8 mm, and an aspect ratio l f /d f = 40.As shown in Fig. 1, it met the requirement of Chinese code JG 472 38 .
The SFRC mix design was developed based on volumetric method similar to the mix design of conventional concrete 38,39 .A direct mix design method was used, in which the coarse aggregate was replaced by an equalvolume of steel fibre, and the mass of steel fibre was considered in the calculation of sand ratio 40 .The slump of fresh mix was designed over 150 mm.A water reducing agent was used to increase the slump of the mixture without changing w/b and the amount of water used.The volume fraction of steel fiber v f = 0, 0.8%, 1.2%, 1.6% or 2.0% was used for producing the high-flowability SFRC.
A horizontal shaft mixer was used to mix the fresh SFRC.Crushed limestones, sand followed by adding cement and fly ash was mixed for 1 min, then water was added for continue mixing of 50 s.Finally, the remaining water and the water reducing agent were added for mixing of 3 min.Special attention was paid to the state of the fresh mix during the mixing process, steel fibres must be evenly spread into the stirred concrete, and the mixing time was strictly controlled to limit the early hydration of cement.The working performance of fresh mixes was timely measured after mixing, using the slump cone method specified in Chinese code GB50080 41 .As shown in Fig. 2, the slump of fresh SFRC appeared a decrease from 200 to 160 mm when the fibre volume fraction increased from 0.8% to 2.0%.This corresponds to the high-flowing concrete with a slump over 160 mm as specified in Chinese code JGJ55 39 .Therefore, the fresh SFRC in this study has a characteristic of high-flowability that distinguishes from that with low slump.Actually, a flowing feature of the fresh SFRC was apparent when compacted with a slight vibration.Therefore, the fresh mixes could meet the designed compaction quality of specimens with uniformly distributed fibres.In order to obtain the actual mechanical properties of SFRC for the bonding specimens, the basic mechanical properties of the accompanied specimens were tested first in accordance with the Chinese code GB/T50081 9 .For each test category, three ϕ150 mm × 300 mm cylinders were casted for axial-compressive strength test, three ϕ150 mm × 300 mm cylinders for elasticity modulus test, three cubes with a dimension of 150 mm for cubic compressive strength test, and three cubes with a dimension of 150 mm for splitting-tensile strength test.Test results are presented in Table 1.It can be seen that all the mechanical properties of SFRC including the compressive strength, the splitting tensile strength, and the modulus of elasticity, increased with the fibre content.This is consistent to previous studies of high-flowability SFRC 29,30 .As shown in Fig. 3, a linear relationship is built for the splitting tensile strength with a fibre factor by a fitness of test data, and can be predicted using the following equations,  www.nature.com/scientificreports/ In which the fibre bonding factor η f = 1.0 for ingot mill steel fibre 34 .

Steel bars
The HRB400 hot-rolled ribbed steel bars of 400 MPa grade was used in this test, the measured mechanical properties and physical dimensions are summarized in Table 2.

Specimens for pull-out tests
To eliminate the boundary influence at the free and tension ends of SFRC block on the bond behavior of ribbed steel bar, the bond length was set at the central of specimens in this study.As shown in Fig. 4, the bond length l b = 5d, the free length was 50 mm at the free and tension ends sheathed by a PVC tube, and the length of the SFRC block for bonding test was 5d + 100 mm.A square section with a dimension over 13d (d = diameter of steel bar) was designed for the SFRC block, which was set to prevent a splitting failure of block with a sufficient thickness of concrete cover over 6d 4,9 .Therefore, the specimens, with the steel bar of a diameter of 14 mm, 16 mm, and 20 mm, had a length of 170 mm, 180 mm, and 200 mm, with a sectional dimension of 200 mm, 300 mm, and 300 mm, respectively.Correspondingly, the bond length was 70 mm, 80 mm, and 100 mm, respectively.Two same specimens were made for each group.Forty-eight specimens for 24 groups in total were prepared for testing.Details are presented in Table 3.
Due to the specimen dimensions changed with the diameter of steel bars, the assembly of steel and wood formworks were used for the moulds of specimens.The wood plate was customized according to the size of the height and width of the block with a hole drilled in the center to penetrate the PVC sleeve for the steel bar.As the length of the bonding block was different with different diameters of steel bar, the distance between the wood plates was changed to meet the test requirements.A pair of bolts were used on the top to fix the distance of plates, while the corners at the bottom of the plates were all fixed.The blocks were compacted on a vibration platform with a slight vibration, smoothed with a spatula for its surface, and covered with the plastic film.The (1)  demould was carried out after 1 to 2 days.And then, the wet quilt was covered on the specimens to ensure a wet curing condition for 28 days.

Pull-out test method
In this study, the pull-out test was carried out on a horizontal tensioning device 9,42 .The composition of test device is exhibited in Fig. 5, two lift platforms on pedestal were used to support the load sensor and jack.The lift platforms could adjust the centers of load sensor and jack to be on the same axis, as per the required height of loading point fitted to different specimen sizes.Meanwhile, a steel connector was used with one convex side inserted in the jack, and the other groove side to fix the load sensor.This ensures the close link of the jack with the load sensor without tilt.A steel subplate was fitted on the contact surface of bonding block to ensure no local deformation in the process of loading.The inner diameter of the holes of jack, load sensor and subplate ensured that the steel bar could be passed smoothly.In general, the test device is able to adjust the platform with  www.nature.com/scientificreports/fine-tuning to improve the test efficiency, and reduce the possible errors of the test results generated in the test operation process.The data acquisition system used in this test category was Donghua DH-3821 static strain test system.Four channels were needed to respectively connect the load sensor, the steel bar displacement meter and the concrete displacement meters on both sides of the steel bar, as shown in Fig. 6.
The following steps were used to carry out the tests: (1) Put the bonding specimen on the loading platform.Pass the load sensor, connector, jack and anchorage through the steel bar in turn.Adjust the lifting platform and fine-tuning platform to ensure the sensor and hollow self-reset hydraulic jack in the same horizontal axis.And then, use the jack to pre-tensioning the specimen with a magnitude of 3-5 kN to make a close contact among the components of loading device.(2) Install the displacement meters at the predetermined position.Balance the data collector to ensure the success of assembling of each link.(3) Apply the tensile force on steel bar, collect and save testing data.Observe and record carefully about any abnormality during the test.(4) Unscrew the oil pump valve first after the test, then remove the displacement meters and the loading device.
In the end, collect the bonding specimen to observe the surface and take photos for future reference.
The average bond-stress was calculated as follows: The peak bond-stress was the bond strength, while the slip was the peak-slip at the bond-slip curve.Since the bond length of this test was relatively short, the bond-slip was regarded as the slip amount of the free end of the steel bar 9 .Because the rib spacing is different for the steel bar with different diameters, a reliable bond-slip was taken as one time of the diameter of the steel bar in this test category.

Failure pattern of bonding specimens
At the early stage of tensioning, the first response of bonding surface between steel bar and SFRC or conventional concrete was to overcome the cementation cohesiveness, while the sliding hardly changed.With the increase of tensile force, a small displacement increased at the free end when the steel bar began to slide, and the slip of steel bar could be measured by the displacement meters.After that, the slip measured by the displacement meters gradually increased, until the steel bar was slowly pulled out.In this test category, the ratio of the thickness of concrete cover to the diameter of steel bar was over 6, which eliminated the possibility of splitting damage 4,21 .After the pull-out test, no crack appeared on SFRC blocks, while that occurred on some of conventional concrete ones.Except for the steel bars of two groups of specimens entered the stress strengthening stage, others did not yield.www.nature.com/scientificreports/As all specimens failed in pull-out pattern without splitting of blocks, a group of pictures is typically exhibited in Fig. 7.It is easily observed the pull-in of steel bar at the free end from Fig. 7a), and the pull-out of steel bar at the tensile end from Fig. 7b).With the continuously increase of tensile force, the steel bar was gradually pulled out accompanied with the sound of steel fibre tearing occurred inside the specimen.From the post-split section of tested specimen along the steel bar as shown in Fig. 7c), it is found that the SFRC was obviously squeezed between the ribs of steel bar, and the crushed SFRC was remained along the bond interface.

Effect of steel bar diameter
As is known, the bond strength comes from the chemical adhesiveness before the slip takes place, and from the surface friction between steel bar and concrete with the occurring of the slip.This makes the same initial ascending bond stress-slip curve with a difference came from the different interfacial roughness that controls the surface friction between steel bar and concrete.Because the bond stress is calculated with Eq. (1), the effect of steel bar diameter can be fully accounted for in this calculation, resulting in a neglection of the influence of steel bar diameter on the bond-stress in theory.This is rational for the plane steel bar in concrete, while the issue becomes complex for the ribbed steel bar in concrete, since different bonding mechanism appeared after the sliding of steel bar 4,5 .The inconsistent results to the theoretical law discussed above are reflected on the bondslip curves of specimens changed with the diameter of steel bar, as shown in Fig. 8.In which the specimens are divided into a group with the same fibre volume fraction and concrete strength.
With the increase of sliding, the interlocking effect of the ribs of steel bar plays a dominant role to impede the slip of concrete in front of the compression side of the ribs 6,10 .This blocking effect will be relied on the physical dimension of steel bar especially on the ribs dimension and spacing, while a deeper rib and a larger number of ribs provide a higher obstruction to concrete to resist the slip of steel bar.It can be seen from Table 2 that the height of rib is 1.17 mm, 1.24 mm and 1.33 mm with a corresponded spacing from 8.54 mm, 10.48 mm and 10.61 mm when the steel bar diameter d = 14 mm, 16 mm, and 20 mm.Therefore, the corresponded number of ribs in bond length (5d) was 8, 7 and 9.The inconsistent numbers of ribs in the test specimens leads a different bond performance of steel bar with different diameter that is presented on the bond stress-slip curve, which results in the disturbing to the bond-stress distribution along the bond length.However, for the specimens with a fibre volume fraction of 0.8%, 1.2%, 1.6% and 2.0%, an error to the average of the bond strength only was −1.75 to 4.27%, −9.48 to 7.07%, −4.32 to 5.90% and −1.75 to 4.42%.Therefore, the influence of steel bar diameter on the bond strength can be neglected, due to the error of test results was within a limit of 15% specified 9 .

Effect of SFRC strength
The bond stress-slip curves of specimens with different SFRC strength are exhibited in Fig. 9, in which the specimens are divided into a group with the same steel bar and fibre volume fraction.With the increase of concrete strength, the elastic stage of ascending portion of the curves became longer, because of the accordingly increased chemical adhesiveness and the interlocking effect.This is identical to the study of Garcia-Taenga et al. 21that a higher concrete compressive strength generates a higher bond strength.Meanwhile, compared with the specimens with C40 SFRC strength grade, the specimens with C50 SFRC strength grade exhibit a steeper descending slope of the bond stress-slip curve.This indicates a fast reduction of the residual bond strength at descending stage of the bond-slip curve, although the absolute values remain at a higher level.

Effect of fibre volume fraction
The bond stress-slip curves of specimens with different fibre volume fraction are shown in Fig. 10, in which the specimens are divided into a group with the same diameter of steel bar in the same strength grade of SFRC.A slight influence of steel fiber on the elastic ascending portion of bond stress-slip curve occurred, due to the bonding stress mainly came from the chemical adhesiveness on the interface of steel bar in SFRC.With the increase of the bond slip, the slope of the ascending portion trends to be smaller until it reached the peak bonding stress.This attributes to the interlocking effect of steel fibres which increases the bond stiffness between ribs of steel bar 24,26 .Once the steel bar presented an obvious slip, the bond-slip curve drops down with a deeper slope, followed by a gradually descending offstage with a slowly decreasing of bond-stress at a larger slip rate.With the increase of fibre volume fraction, the bond strength and peak-slip behave an obvious growth, except for the specimen C5H4/14-16 presents a less slip at the ascending portion of the curve.For the two groups of specimens coded in Fig. 8, the bond strength had an increase of 26.7% and 15.7% for the SFRC with a fibre volume fraction increased from 0.8 to 2.0%, respectively.However, compared with that for referenced conventional concrete, the bond strength creates an increase of 24.4% and 25.2% for the SFRC with a fibre volume fraction of 0.8%.This indicates that the presence of steel fibres inherently improves the bond behavior of steel bar in concrete.
Meanwhile, the residual bond strengths of specimens exhibit an increase with the fibre volume fraction, although a steeper reduction appears at the descending portion of bond stress-slip curve.A larger area under the   www.nature.com/scientificreports/bond-slip curve, representing a significantly increase of the energy dissipation during the bond-slip, created with the increase of fibre volume fraction.This indicates the contribution of steel fibres to the bond-slip toughness due to the increased confinement of steel fibres around the interface of steel bar in SFRC 26 , and the interlocking between steel fibers and steel bar ribs 30 .

Prediction of bond strength and peak-slip
The test results of bond-strength (τ u ) and peak-slip (s u ) are shown in Table 4. Based on above discussion of the bond stress-slip behaviours with influencing factors, the variation of τ u with the diameter of steel bar is first analyzed.Results show that with the increase of the diameter of steel bar from 14 to 20 mm, τ u presented a flat tendency despite of the dispersion of test results.Similarly, the tested specimens were assembled in a group with   the same fibre volume fraction.This once again indicated that in condition of l a = 5d, the changes of diameter and strength of steel bar had a slight effect on τ u .Meanwhile, the bond strength was higher with a higher strength of SFRC.The bond strength of steel bar in C50 concrete increased 13.3% in average than that of C40 concrete.Disregarding the impact of the diameter of steel bar, the bond strength ratio of steel bar in SFRC with and without steel fibres is depicted in Fig. 11 with a correlation to the fibre factor.It can be seen that despite a large scatter of test data, a similar tendency is presented for the bond strength ratio with the fibre factor, which indicates a less coupling effect between SFRC strength and fibre factor on the bond strength.This is consistent to the study of Hou et al. 25 that the steel fibre effect is correlated with the fibre factor and fibre distribution uniformity.Based on the test data, the following formula can be gotten by a linear fitness, Comparing Eq. ( 4) with Eq. (1), the reinforcing of steel fibre on bond strength is weaker than that on tensile strength, as the reinforcing coefficient of 0.60 for bond strength is smaller than that of 0.74 for tensile strength.This attributes the different strengthening effects of steel fibers, the reinforcing contribution to the bond strength relies in certain degree on the increase of tensile strength to provide an effective confinement of steel fibres around the interface of steel bar and the interlocking of SFRC between ribs of steel bar 25,26,42 .
The variation of peak-slip s u0 for steel bar to conventional concrete is shown in Fig. 12.A relationship between s u0 and d can be obtained by a linear fitting analysis, the expression can be written as, The variation of peak-slip ratio s u /s u0 with F is shown in Fig. 13, a linear relationship can be obtained by fitting the s u /s u0 and F, Therefore, combined with Eq. ( 5), the peak-slip of steel bar in SFRC can be predicted with the equation expressed as, (4) τ u = (1 + 0.6F)τ u0 www.nature.com/scientificreports/

Prediction of anchorage length
Based on the equilibrium of the actions on the bond length of steel bar, with a premise of ensuring that the yield of steel bar is prior to the bond-slip reached the peak-slip, the anchorage length can be calculated by the formula as follows 31 : Substitute Eq. ( 4) into it, the equation transforms as: If no steel fibre is used for reinforcing conventional concrete, Eq. ( 8) is degenerated into that used for calculating the anchorage length (l a0 ) of steel bar in conventional concrete, that is, Therefore, when the strength grade of conventional concrete is determined, the anchorage length (l a0 ) of steel bar can be obtained according to relative design codes of concrete structures 23,32,33 .Based on a principle of an equivalent strength grade of SFRC to conventional concrete, the anchorage length of steel bar in SFRC can be obtained using the following equation: According to the specification of Chinese code GB50010 32 , the anchorage length of steel bar in conventional concrete is computed with the Eq.(11a) transferred from Eq. ( 9), In which the coefficient α=f t0 4τ u0 , taken as a constant of 0.14 for ribbed steel bar.With a premise of steel bar in SFRC behaves a similar bond behaviour with the steel bar in conventional concrete, the anchorage length of steel bar in SFRC is computed with Eq. (11b) using the tensile strength of SFRC replacing that of conventional concrete as specified in Chinese code JGJ/T465 28 , that is, Submitted Eq. (11a) into Eq.(11b), the equation can be rewritten as, With the specification of f t =(1 + 0.7F)f t0 in Chinese code JGJ/T465 28 , Eq. (12a) can be rewritten as a similar expression of Eq. ( 10), that is (6) www.nature.com/scientificreports/Therefore, when the fibre volume fraction varies from 0.5% to 2.0%, a 1.9-5.3%shorter anchorage length of steel bar in SFRC is given out from Eq. (12b) than that from Eq. ( 10).This may lead to a lower reliability for the anchorage length of steel bar in SFRC when the tensile strength of SFRC is directly used to replace that of conventional concrete.This difference comes from the lack of test data in developing specification of Chinese code JGJ/T465 to verify the reasonability of Eq. (11b) for the bond of steel bar in SFRC with ingot mill steel fibres.Therefore, it is necessary to revise the specification of anchorage length to meet the actual property.
It can be gotten from this equation that the anchorage length of steel bar in SFRC shortens with the increase of fibre factor, compared to that of steel bar in conventional concrete at an equal strength grade.For instance, using the steel fibre of this study and taken the volume fraction of 0.8-2.0%, the anchorage length of steel bar in SFRC can be shortened by 18-45%.This is convenience for the construction of reinforced concrete structural joints with a shortened anchorage length of steel bar.That is, applied SFRC technology in reinforced concrete structures, the criss-cross issue of many steel bars within the structural joints can be solved, which makes concrete easily cast to rise the concrete quality.

Conclusions
Considered the influencing factors of SFRC strength grade, fibre volume fraction, and steel bar diameter, an experimental study was carried out on twenty-four groups of specimens using the central pull-out test method.The formulae for predicting the bond strength and peak-slip, and the anchorage length are proposed based on the test results analysis.Conclusions can be drawn as follows: With a sufficient concrete cover around steel bar and a higher tensile strength of SFRC, all SFRC bonding specimens failed with pull-out of steel bar.The feature of failure was apparently expressed with the steel bar that was pull-in at free end and pull-out at tension end.No yield of steel bar while no splitting of SFRC block took place in this study.
The strength of SFRC was dominant to the bond of ribbed steel bar in SFRC, resulting in the bond strength with an increase of 13.3% when the strength grade of SFRC changed from C40 to C50.The presence of steel fibres generated a positive effect on the bond behavior of steel bar in SFRC.Compared with the referenced conventional concrete specimens, an increase of 19.2% was presented for the bond strength of steel bar in SFRC with a fibre volume fraction of 0.8%, and an increase of 48.0% when the fibre volume fraction is 2.0%.The bond slip is negative to the steel bar diameter, and positive to the fibre volume fraction.
The equations for predicting the bond strength and peak-slip of steel bar in SFRC are proposed, which are associated with the bond strength and peak-slip of steel bar in conventional concrete by considering the effect of fibre factor.And then, the anchorage length of steel bar in SFRC is predicted considered the reinforcing of steel fibre on the bond strength.It is valuable that using the ingot mill steel fibre of this study with a volume fraction of 0.8-2.0%, the anchorage length can be shortened by 18-45%.
Compared with test results of this study, a little shorter anchorage length of steel bar in SFRC is obtained from the specification of Chinese code JGJ/T465.This indicates that a revision is necessary for the reliable anchorage of steel bar in SFRC with ingot mill steel fibres.

Figure 1 .
Figure 1.Ingot mill steel fibres used in this study.

Figure 4 .
Figure 4. Specimen for bond strength test.(a) schematic of specimens (b) Treated steel bars.

Figure 5 .
Figure 5. Composition of the pull-out testing device.

Figure 6 .
Figure 6.Displacement meters arrangement at free end of steel bar and on the surface of block.

Figure 7 .
Figure 7.Typical failure patterns of tested specimens.(a) pull-in at free end (b) pull-out at tension end (c) failure surface on bond length.

Figure 9 .
Figure 9.Bond stress-slip curves of specimens with different concrete strength.

Figure 10 .
Figure 10.Bond stress-slip curves of specimens with different volume fraction of steel fibre.(a) C40 concrete and d=14 mm (b) C50 concrete and d=14 mm.

Table 2 .
Mechanical properties and physical dimensions of steel bars.

Table 3 .
Details of test specimens.

Table 4 .
Test results of bond strength and pike-slip.
Relationship of s u /s u0 and F.