Photocatalytic degradation of organic dyes using reduced graphene oxide (rGO)

Photocatalysts have developed into a successful strategy for degrading synthetic and organic toxins, such as chemicals and dyes, in wastewater. In this study, graphene oxide was reduced at different temperatures and used for degrading indigo carmine and neutral red dyes. The wide surface areas, strong adsorption sites, and oxygen functionalities of reduced graphene oxide (rGO) at 250 °C (rGO-250) produced more photocatalytic degradation efficiency and adsorption percentage. The catalyst dosage, initial dye concentration, solution pH and recyclability were all used to optimize the photocatalytic activity of rGO-250. This research presents a capable nano-adsorbent photocatalyst for the efficient degradation of organic dyes. GO and rGOs were also investigated for carbon dioxide (CO2) absorption properties. Results showed that rGO-250 has better CO2 adsorption properties than other rGOs. Overall, it was observed that rGO-250 has better photocatalytic and CO2 adsorption capabilities compared to graphene oxide reduced at different temperatures.

www.nature.com/scientificreports/The technological advantages of photocatalysis are currently manifested through the photocatalytic degradation of dyes.Typically, electrons are stimulated, forming electrons and holes, when the energy of the light absorbed is equal to or less than the band gap of the photocatalyst.The photogenerated electron-hole pairs then use the nearby oxygen and water molecules to make ROS, which destroy the dye molecules 20,21 .Numerous studies have described using rGO in the photocatalytic removal of dye contaminants.The novelty of using reduced graphene oxide (rGO) for dye degradation lies in its remarkable catalytic properties and potential to revolutionize wastewater treatment methods.Unlike traditional approaches, rGO-based catalysts offer several unique advantages: 1. Enhanced catalytic activity: rGO exhibits high surface area and excellent electron transfer properties, enabling it to catalyze the degradation of dyes and other organic pollutants efficiently.2. Improved reaction kinetics: Using rGO can significantly accelerate the degradation kinetics of dyes, reducing the time required for wastewater treatment.3. Sustainability: rGO can be synthesized from abundant and inexpensive graphite sources, making it a sustainable and cost-effective option for environmental remediation.4. Versatility: rGO can be functionalized and tailored to target specific dye molecules, increasing its versatility for various wastewater treatment applications.5. Low environmental impact: Compared to some traditional chemical catalysts, rGO-based systems are often less harmful to the environment, aligning with the growing emphasis on green and sustainable technologies.
In summary, using rGO as a catalyst for dye degradation represents a novel and promising approach that addresses both the efficiency and sustainability challenges associated with wastewater treatment.This innovation has the potential to contribute significantly to cleaner water resources and reduced environmental pollution.
In this study, rGO was produced using a straightforward, eco-friendly solvothermal method without any harmful reducing chemicals, and it demonstrated outstanding adsorption capabilities and photoactivity towards the removal of IC and NR dye.The investigation examined the optimisation of extraneous elements such as catalyst concentration, initial dye concentration, light intensity, and pH.

Experiment Chemicals
All the chemicals used (graphite powder, potassium permanganate (KMnO 4 ), sulphuric acid (H 2 SO 4 , 98%), hydrogen peroxide (H 2 O 2 , 30%) and ethanol (C 2 H 5 OH) were of analytical grade, procured from Sigma Aldrich.Deionized water was used as the solvent for preparing practical solutions.

Synthesis of GO
Graphite powder pretreatment is initially carried out to prepare Graphene oxide (GO).In the beginning, graphite (1 g) was added to H 2 SO 4 (25 ml).It was stirred in an ice bath for uniform suspension for a few minutes.After 20 min, the ice bath was removed.
A modified Hummer method is used to prepare GO from graphene.KMnO 4 (3 g) was added slowly to the solution and stirred for 3 h.50 ml of distilled water was added slowly into the solution after 3 h.50 ml of H 2 O 2 was added to cease the process.When a brown colour is observed, add 100 ml of distilled water.Add 5 ml of H 2 O 2 and centrifuge the mixture.Wash with H 2 O to collect the GO.For drying, it was placed in an oven at 60 °C for 2 h.

Preparation of reduced Graphene oxide (rGO) at different temperatures
To reduce GO to rGO, the solvothermal method was used.The mixture is then heated at different temperatures for the reduction process.Initially, 20 ml of C 2 H 5 OH and 200 mg of GO were mixed with 10 ml of deionized water.After vigorously sonicating the mixture for 30 min, a stable GO dispersion was produced.After that, the mixture was heated for 2 h at 100, 150, 200, and 250 °C in an 80 cc stainless steel autoclave lined with Teflon.The samples were designated rGO-x, with x standing for the investigated reduction temperatures.The rGO samples were subsequently filtered, washed, and dried.

Characterization of reduced graphene oxide
The X-ray diffractometer, a Malvern Panalytical Xpert (45 kV, 40 mA), was utilised to collect the XRD pattern from a Cu target.The materials were dispersed in ethanol before being put onto the copper grid for transmission electron microscopy (TEM) with an FEI Tecnai G2 S-Twin FEG 200 kV TEM.The sample was prepared for transmission electron microscopy (TEM) by dissolving the powder in isopropanol using a bath sonicator for 10-20 min.After being drop cast onto 200-grit carbon film, the sample was examined.An FTIR spectrometer called the Thermo Nicolet Nexus 670 was used to assess the purity of nanopowder.A Biochrom UV-Vis Spectrophotometer with a 190-1100 nm scanning range was used for the characterisation.A 300-750 nm scanning range and a medium scan speed were used in this case.The surface areas, pore diameters, and pore volumes of GO and rGOs were examined using Brunauer-Emmett-Teller (BET) analysis using the Micromeritics ASAP 2020 Surface Area and Porosity Analyzer (Georgia, USA).Before measurement, the samples were degassed at 150 °C for 24 h to eliminate moisture.

www.nature.com/scientificreports/
Dye degradation analysis To 20 ml of distilled water, 15 mg of the photocatalyst (GO&rGO' s) were measured and added.The fluid was sonicated for around 30 min to produce a consistent suspension.Approximately 5 ml of this solution is added to the 40 ml of NR and IC aqueous solutions.The sample solution was left in the dark for roughly 30 min, allowing the reaction to reach adsorption equilibrium.After being maintained in the dark for 30 min, three millilitres of the sample are removed and subjected to UV-vis spectroscopy examination.Magnetic stirring was used to keep the solution stable while it was in the sun.A sample of the supernatant solution was taken every 20 min until three hours into the procedure.At this point, it was examined with UV-vis technology.The absorbance and wavelength were plotted.It was also investigated how varied catalyst loadings (1, 2, 3, 4, and 5 mg) of GO and rGOs, pH effect (3, 7, 10), recyclability, and initial dye concentrations (25, 40, 50, and 75 ppm) of two dyes would affect the process 22 .
The following equations were used to calculate the photodegradation efficiency (% Cdeg) and adsorption percentage (% Cads): The dye concentrations at the start, after attaining adsorption-desorption equilibrium, and at time t are designated as C initial , C 0 , and C t , respectively.The pseudo-first-order kinetic equation shown below was then used to simulate the photocatalytic degradation reaction: where k (time −1 ) is the rate constant for pseudo-first-order.

Evaluation of CO 2 adsorption properties
To evaluate the CO 2 adsorption properties, we dissolved 50 mg of GO and rGOs in 10 ml water.After passing CO 2 for 15 s in all the samples, it is titrated against 0.1 N NaOH, adding 10 drops of indicator.Noted the colour change and volume of NaOH for calculating the amount of CO 2 absorbed using the following equations.
where V 1 -Volume of the sample used; N 1 -Normality of the sample; V 2 -Volume of NaOH; N 2 -Normality of NaOH The amount of CO 2 adsorbed was calculated using the following equation,

Characterization
In Fig. 1a, at 2 = 26.570°and 2 = 54.700°,respectively, graphite showed an intense (002) peak and a very modest (101) peak.Both peaks were associated with JCPDS card 41-148713 and supported graphite structure.After oxidation, the (002) peak moved to 2 = 11.030°,caused by incorporating oxygenated functionalities and water molecules into the graphene layers.Despite this, the (002) peak of GO was still discernible during reduction at 100 and 150 °C, maybe due to the low reduction temperatures that only slightly converted GO to rGO.The (002) peak of GO started to fade as the reduction temperature rose, but a new, broader (002) peak of rGO started to appear at 2 = 24.890°for rGO-200 and 2 = 23.850°for rGO-250.The shifting of the (002) peak indicated that the sp 2 carbon structure had recovered partially 23 .Also, the (100) GO peak at 2θ = 42.630° was detected in all rGOs, resembling the turbostratic band of disordered carbon materials.Figure 1b displays the FTIR spectra of rGO samples produced at various reaction temperatures.The GO surface contains a large number of functional groups.Figure 1b shows the peaks of C-O (alkoxy) stretch, O-H (hydroxyl) vibration, C=C aromatic stretch vibration, and C=O stretch on rGO surfaces at 1122, 1632, and 3451 cm −1 .As the temperature rose, so did the peak intensity corresponding to the C=O vibration band at 1632 cm −1 .From 100 to 250 °C, there was a decrease in the hydroxyl group's (3451 cm −1 ) permeability intensity 15 .As the temperature rises, the absorbed water molecules intercalate and vaporise.Furthermore, the hydrophilic characteristics of GO are lost, as well as the presence of functional groups containing oxygen 24 .
Figure 1c shows the pore size distribution curves for GO and rGOs.According to Fig. 1c, the total pore volume decreased from 0.11 to 0.037 cm 3 g −1 when the GO was lowered from 100 to 150 °C, decreasing the surface area (Table 1).This resulted most likely from the GO's aggregation action following the decrease.The considerable loss of oxygen functional groups led to the production of greater pore volume, which in turn resulted in a pronounced increase in surface area for rGO-250 at higher reduction temperatures 25 .
The UV-vis absorption spectra of GO and rGOs are shown in Fig. 2a.The aromatic C=C bond π-π* transition of GO results in an absorption peak at 284 nm.The temperature ranged from 100 to 250 °C, and as a result, the peak location gradually shifted to lower wavelengths 13 .Peak shifting partially restored the sp 2 conjugation, leading to a narrower band gap 17 .The optical band gaps of GO and rGOs were subsequently determined using the linear fits of the Tauc plots, as seen in Fig. 2b.Table 2 shows the band gap of the samples.The band gap of GO was 2.80 eV, which was in line with results from earlier literature 26 .The TEM micrographs in Fig. 3a and b show the sheet-like morphology of GO and wrinkled rGO caused by functional group evaporation and thermal instability of GO during annealing 19 .The GO displayed a pristine surface and a closely packed lamellar and plate structure consistent with previously made GO.The distinctive sheet-like silky waves, wrinkled appearance, and clumped structure of rGO, in contrast to GO, were between 20 and 100 nm in size 27 .

Photocatalytic activity of rGOs
Structural conjugation, hydrophobic association, electrostatic interaction, and -interaction is how rGO interacts with dyes.These interactions allow a variety of dyes to adsorb on rGO.To maximise the dye adsorption capacity, it is essential to have rGO with a large surface area and high porosity.This is achievable by carefully controlling the GO precursor's quality and the reduction process.The mechanism of dye degradation involves the excitation of dye from its ground state (Dye) to its triplet excited state (Dye*) under visible light photon (λ > 400 nm).An electron injection into the conduction band transforms this excited state dye species into a semi-oxidized radical cation (Dye +• ).Superoxide radical anions (O 2 -• ) are produced as a result of an interaction between these  www.nature.com/scientificreports/trapped electrons and the dissolved oxygen in the system, which in turn causes the creation of hydroxyl radicals (OH • ) (Fig. 4). Figure 5 illustrates the photocatalytic activity of different rGOs in IC and NR, respectively.The solution is collected after the dyes have been exposed to the sun for a predetermined time.It is measured how much UV-vis is absorbed (Figure S1, S2, S3 and S4).Table 3 shows the concentration-time profile (C t /C 0 ) and degradation efficiency (%), which were derived using the absorbance values obtained for the initial dye concentration (C 0 ) and the absorbance values acquired at certain time intervals (C t ).The photodegradation of dyes was found to be much more effective with rGO-250.It may be attributed to the fact that the rGO-250 may have the large and optimum surface area for the highest adsorption of dyes 28,29 .Figure 6a and c depict GO and rGO photoactivity, respectively, while Fig. 6b and d depict the pseudo-first-order fitting of photocatalytic dye degradation.Table 3 shows the values for % C ads , % C deg , k, and R 2 .rGO-100, rGO-150, and rGO-200 behaved similarly to GO in the dye adsorption process to other rGOs because low reduction temperatures were insufficient for GO reduction.Because of its large surface area, rGO-250 had the highest dye adsorption 30 , with an adsorption percentage of 29.26 for IC and 25.23 for NR, respectively.The photocatalytic degradation efficiency of rGO-250 was 36.28 and 25.73 for IC and NR, respectively.The statistical analysis of linear curve fit was performed using origin software.This statistical analysis aimed to regulate factors affecting dye photodegradation performance.The statistical analysis results of fitted curves for indigo carmine and neutral dye are represented in Table 4. Statistical evidence, such as Fisher variation ratio (F-value) and probability value (P value), was used to assess the linear fit for estimating photodegradation performance.Additionally, degrees of freedom (DF), mean squares (MS), and sum of squares (SS) were calculated.The  www.nature.com/scientificreports/F-value of 14.55 indicates the model is significant.Noise has a 0.01% probability of causing a ''Model F-value".Significant model terms are indicated by "'Probability > F" values < 0.0500.

Effect of pH
15 mg of rGO-250 in 20 ml distilled water kept for sonication of about 30 min.Two sets of dye solutions (IC&NR) were made of pH 3, 7 and 10. 5 ml from the catalyst solution was added to 40 ml of aqueous solutions of dyes of    www.nature.com/scientificreports/ 25 ppm of concentrations (Fig. 7).The degradation (91.85% for IC and 90.17% for NR) is much more pronounced in the basic medium (pH 10) for both dyes than in the acidic (pH 3, 85.15% for IC and 84.58%for NR) and neutral medium (87.92% for IC and 86.47% for NR) (Table 5).This may be because the solution contained more hydrogen ions under acidic conditions.Many hydrogen ions competed with the dye molecules for unoccupied adsorption sites on the catalyst surface.In this case, IC is an anionic dye, and NR is a neutral dye 28 .

Effect of initial dye concentrations
The photocatalytic degradation of dyes was studied using various initial concentrations such as 25, 40, 50 and 75 ppm.15mg of catalyst in 20 ml of DI water was added to 40 ml of each dye (IC, NR) of varied initial concentration (Table 6).An initial concentration of 25 ppm was observed to have greater dye degradation efficiency than other initial dye concentrations for both dyes (91.85% for IC and 90.17% for NR).As the initial concentration increases, degradation efficiency decreases.This may be because the number of dye molecules contacting the catalyst surface and the number of dye molecules in the solution rises.This leads to the active sites on the catalyst surface being covered by dye molecules, which interferes with photon arrival and reduces catalytic efficiency.As a result, less OH radical generation occurs on the catalyst surface 23,31 .As a result, increased dye concentration can reduce removal efficiency and reaction rate (Fig. 8).

effect of catalyst loading
An essential practical factor affecting the photocatalytic reaction's effectiveness is catalyst loading.The number of active sites in the reaction system rises due to increased catalyst loading since it increases the concentration of the active material overall.When it comes to the photodegradation removal process, increasing the dose often results in higher removal efficiencies up until a point at which adding more catalyst results in lower light transmittance of the suspension and lower removal efficiencies.rGO-250 is dissolved in 50 ml of distilled water in a variety of ratios, including 15, 25, 35, 45, and 55 mg. 10 ml of dye solutions with an IC and NR of 25 ppm each and a pH of 10 were combined with 5 ml of this solution.For 30 min, the sample solutions were left in the dark.3 ml are withheld after 30 min, and UV-vis recordings are made.For roughly 3 h, the remaining sample solution was exposed to sunshine.After every hour, the aliquots were removed, and UV-vis measurements were taken.
As the catalyst loading increased, it was found that the deterioration grew (Table 7).For 15 mg of catalyst, degradation efficiency was ~ 92 for both dyes.The degradation efficiency was determined to be 98.74% for IC and 97.56% for NR, respectively, with a catalyst dosage of 55 mg.Herein, The overall surface area of the photocatalyst grew along with the catalyst concentration.Thus, there were more accessible adsorption sites, which improved the dye adsorption procedure (Fig. 9).Additionally, when the total amount of catalyst particles rose, photon absorption for generating electrons and holes and the rate of the synthesis of reactive oxygen species (ROS) for degrading dye molecules both improved 32,33 .
Table 8 compares the present work with the existing literature values.The proposed work has the highest degradation efficiency with lower catalyst dosage compared to existing literature for the degradation of IC.In the case of NR dye, it was observed that the rGO catalyst only exhibits a degradation efficiency higher than 90%, whereas the other literature exhibits a degradation efficiency less than 85%.In conclusion, using rGO as a catalyst www.nature.com/scientificreports/for both IC and NR degradation demonstrates significant promise in enhancing the efficiency and kinetics of dye removal compared to the existing literature.This innovative approach not only offers an eco-friendly and cost-effective solution for wastewater treatment but also opens up avenues for further research and development in the field of advanced materials and catalysis.

Recyclability
Recyclability studies in photocatalysis are essential for assessing the practicality and sustainability of photocatalytic processes for various applications, such as water purification, air pollution control, and organic pollutant    www.nature.com/scientificreports/ The rGO-250 recovered from each cycle is thoroughly cleaned with deionized water before being added to the catalytic process.Interestingly, its stability is maintained during the five degradation cycles with barely perceptible alterations.Figure 10 shows the stability of rGO-250 in the photocatalytic dye degradation reaction as a function of cycle number.The percentage degradation was still greater than 90% after five consecutive runs.It attests to the catalyst's structural stability even after five cycles of degradation tests.Under exposure to direct sunshine, it can be employed as a possible catalyst for the degradation of IC and NR dyes 25,28 .

CO 2 adsorption performance of rGOs
Table 9 summarizes the comparison of CO 2 uptakes by GOs and rGOs.The rGO-250 was the best compared to other adsorbents (Fig. 11).This excellent adsorption performance is attributed to increased surface area at   www.nature.com/scientificreports/higher reduction temperatures, owing to the significant removal of oxygen functional groups and increased pore volume.After removing surcial oxygen functionalities, graphene's sp 2 -hybridized structure was partially restored at 250 °C41,42 .

Conclusion
A simple one-pot solvothermal approach was used to fabricate reduced graphene oxide at different annealing temperatures.These rGOs were tested for dye adsorption and CO 2 adsorption properties.rGO-250 then achieved the best adsorptive removal (29.26% for IC and 25.23% for NR) and photocatalytic degradation (36.28% for IC and 25.73% for NR) of dyes, revealing that the main reasons were increased surface area and narrowing of the band gap.The optimal adsorption (91.74% for IC and 94.81% for NR) and photocatalytic activity (98.74% for IC and 98.56% for NR) of rGO-250 were improved by increasing the amount of catalyst to 55 mg, the initial dye concentration to 25 ppm, and the solution pH to 10. rGO-250 was able to degrade more than 90% of dyes after repeating the reaction up to five times, indicating that it was highly stable and reusable.It was also observed that rGO-250 possesses better CO 2 adsorption properties than other rGOs.

Figure 5 .
Figure 5. Dye degradation analysis of (a,b) rGO-100 in IC and NR respectively (c,d) rGO-150 in IC and NR respectively (e,f) rGO-200 in IC and NR respectively (a,b) rGO-250 in IC and NR respectively.

Figure 7 .
Figure 7. (a) Effect of pH on photocatalytic degradation of NR normalized under adsorption.(b) The plot of the log of concentration with time.

Figure 8 .
Figure 8. (a,c) Effect of initial dye concentration of IC, NR on photocatalytic degradation of dyes normalized against adsorption.(c,d) The plot of the log of concentration with time.

Figure 9 .
Figure 9. (a,c) Effect of catalyst loading on photocatalytic degradation of dyes normalized against adsorption.(c,d) The plot of the log of concentration with time.

Table 3 .
Effect of reaction temperature on adsorption percentage, photocatalytic degradation efficiency, and photocatalytic degradation rate of IC and NR dye.

Table 4 .
Statistical parameters of indigo carmine and neutral red dyes.

Table 5 .
Effect of pH on adsorption percentage, photocatalytic degradation efficiency, and photocatalytic degradation rate of IC and NR dye.

Table 6 .
Effect of initial dye concentration on adsorption percentage, photocatalytic degradation efficiency, and photocatalytic degradation rate of IC and NR dye.

Table 7 .
Effect of catalyst loading on adsorption percentage, photocatalytic degradation efficiency, and photocatalytic degradation rate of IC and NR dye.
Vol.:(0123456789) Scientific Reports | (2024) 14:3608 | https://doi.org/10.1038/s41598-024-53626-8www.nature.com/scientificreports/degradation.Recyclability studies aim to determine the ability to reuse the photocatalyst multiple times without significantly losing its catalytic activity.According to the set of photocatalytic tests, rGO-250 is a useful material for the breakdown of both dye molecules.As a result, the ability of this decreased graphene oxide material to degrade dye molecules across consecutive cycles of degradation is tested.The catalyst is removed from each photocatalytic experiment and used for the subsequent cycle of the degradation investigation for this reason.

Table 8 .
Comparison of present work with existing literature value.Significant values are in bold and italics.

Table 9 .
CO 2 adsorption by GO and rGOs.