Fabrication of composite transparent conductive electrodes based on silver nanowires

Composite transparent conductive electrodes (C-TCEs) have recently been produced using low-cost techniques to keep up with the boom in the fabrication and development of optoelectronic devices. In this article, silver nanowires (AgNWs) were successfully synthesized by a simple hydrothermal method using different molecular weights MWs of poly (N-vinylpyrrolidone) (PVP). Graphene oxide (GO) was prepared using the modified Hummers’ method and a reduction step was held on GO films to produce reduced GO (rGO). C-TCEs were fabricated by over-coating the AgNWs electrodes with rGO, or poly(3,4-ethylenedioxythiophene) polystyrene sulfonate to improve the roughness, surface energy, and sheet resistance. The influence of using lower and higher MWs of PVP on the yield, shape, and size of AgNWs was investigated. The results showed that using lower MW of PVP had a great effect on the yield, morphology, and aspect ratio of AgNWs with diameter of 46 nm and average length 12 µm. The optical, morphological, topographical, and electrical properties of TCEs were studied. AgNWs/rGO composite electrode provided the lowest surface roughness and surface energy of 250 nm and 47.95 mN/m, respectively, with a relatively high transparency of 78.2% at 550 nm light wavelength, and a low sheet resistance of 27 Ω/□.


Synthesis of AgNWs
Long AgNWs were synthesized by a hydrothermal route.A summary of the AgNWs synthesis procedure is shown in Fig. 1.First, separate solutions of silver nitrate (102 mg, 30 mL), D + glucose (240 mg, 10 mL), sodium chloride (70 mg, 30 mL) and PVP (2 g, 10 mL) were dissolved in deionized water at room temperature except PVP solution was stirred at 65 ℃.In each synthesis, PVP solutions with different M W s, PVP 1 of 40,000 and PVP 2 of 1300,000, were prepared systemically.After 10 min (mins) of continuous stirring, glucose solution was added to silver nitrate solution to assist in the reduction process.Then, PVP solution was added to the above mixture and stirred for 20 min to obtain a blurred mixture.Grey solution was grown by adding NaCl dropwise to the blurred mixture with continuous stirring for 1 h (h) as a nucleating agent of pentagonal structure seeds of Ag.The obtained turbid mixture was poured into a 100 mL Teflon-lined stainless-steel autoclave and heated in an

Synthesis of GO
The modified Hummers' method was utilized to synthesize GO from natural graphite (2 g) and (8 g) of sodium nitrate by adding 50 mL of 98% sulfuric acid 17 .This mixture was stirred for 20 min in an ice-water bath and then, potassium permanganate (12 g) was gradually added over a period of 50 min with a continuous stirring for another 2 h.Afterwards, the above solution was left to reach room temperature to produce a thick slurry.Then, DI water (160 mL) was added slowly, and the solution temperature was raised to 98 °C.Hydrogen peroxide 50% (30 mL) was added to the above suspension after cooling to room temperature to form GO. Finally, the GO solution was washed twice with 300 ml of 5% HCl and DI water three times.After that, GO powder was obtained by filtration and drying in an oven at 60 °C.GO solution in deionized water with concentration (1:1 mg/mL) is obtained to form GO films for further treatment.
Chemical and thermal treatment of GO films by hydrazine vapor was carried out to reduce GO films to rGO.First, GO film inside a glass petri dish containing 1 mL of hydrazine monohydrate 60% was heated at 150 °C for 1 h in a muffle furnace under the flow of nitrogen gas.The color of the films changed from matte brown to metallic gray, indicating a reduction process and formation of rGO layer which can be easily scratched and characterized.

Fabrication of TCEs
Glass substrates were sequentially cleaned with hellmanex III, DI water, acetone, and isopropanol.Additionally, Clean glass substrates were treated using nitrogen plasma by (Edwards E3064) at high vacuum (2 × 10 -4 mbar).The glow discharge valve was opened, and pure nitrogen gas was allowed to fill the chamber until the pressure reached 10 -2 mbar.By applying high tension at 20 mA, a purple color of nitrogen ionization appeared, and the glass samples were left under plasma treatment for 10 min.Transparent conductive films of AgNWs were deposited on glass by a spin coater at 2000 rpm for 30 s.To protect and improve morphological and electrical properties of AgNWs mesh, composite electrodes of AgNWs/rGO or AgNWs/PEDOT:PSS were fabricated.GO and PEDOT:PSS were spin coated on AgNWs films at 2000 and 4000 rpm for 30 s, respectively.Furthermore, AgNWs/PEDOT:PSS electrodes were dried at 50 °C for 1 min and a reduction step for GO is needed to enhance the conductivity and get AgNWs/rGO composite electrodes.

Characterization techniques and measurements
The absorption and transmittance spectra of AgNWs, GO, rGO and the fabricated electrodes were investigated using an UV-Vis spectrophotometer (Evolution 300 double beam scanning spectrophotometer, Thermo Scientific, USA).FTIR spectra of the prepared materials were obtained using (a spectrum BX 11 spectrometer FTIR LX 18-5255 Perkin Elmer).Raman spectra confirm the formation and reduction of GO (Senterra Raman, Bruker Corporation, USA, λ (532 nm)).X-ray diffraction patterns were obtained for the prepared films using (XRD, D2 PHASER, Bruker) and the X-ray source was a Cu target generated at 30 kV and 40 mA.The contact angles of a drop of water and diiodomethane on AgNWs, AgNWs/rGO, and AgNWs/PEDOT:PSS electrodes were measured before and after treatment using a contact angle goniometer (Ramé-hart CA instrument, model 190-F2).High-resolution transmission electron microscopy (JEOL JEM -2100F, Japan) was used to confirm the morphology and dimensions of AgNWs and GO films.The topography, morphology and 2D and 3D images for the AgNWs and composite films were investigated by scanning electron microscope (JEOL-IT200, Japan) at an acceleration voltage of 25 kV and atomic force microscopy.SIGNATONE four point-probe was used to measure and calculate the sheet resistance (R S ) and resistivity of thin films and materials.By moving the lever, allowing the 4 probes to touch the substrate, and applying a current of 4.5 mA, the measured voltage is recorded using a Keithley meter.R S values were estimated using the following equation.
where ΔV is the voltage measured by Keithley (mV) and I is the current applied to the probes (mA).

Results and discussion
Characterization of prepared AgNWs, GO, and rGO.

Optical properties of prepared materials
Figure 2 describes the optical properties of prepared AgNWs, GO, and rGO.The effect of PVP M W on absorbance spectra of AgNWs is illustrated in Fig. 2a.For AgNWs prepared with PVP 1 , the peak located at ~ 348 nm is ascribed to the quadrupole resonance excitation (π-π*) and the narrow peak at ~ 385 nm is corresponded to transverse plasmonic resonance mode (n-π*).This confirms the formation of high yield and pure AgNWs in the sample.However, the red shift in the peak assigned to ≈ 400 nm in AgNWs prepared by PVP 2 indicates the formation of Ag nanoparticles (AgNPs) [18][19][20] .At the same time, the broad peak at 400 nm indicates more diverse morphologies of the Ag nanostructures [19][20][21][22] .
As shown in Fig. 2b the absorption spectrum of GO solution has two peaks and the main absorption peak at 230 nm is attributed to π-π* transitions of C=C in amorphous carbon system and a broad shoulder with center at ∼ 300 nm that is commonly assigned to n-π* transitions in C=O 23,24 .On the other hand, the peak of the π-π* (1) transition is significantly shifted to 265 nm for rGO, indicating that some groups on the GO surface are reduced and the conjugated structure is restored 24,25 .Figure 2c represents infrared spectrum of pure PVPs and AgNWs synthesized by PVP 1 and PVP 2 .The FTIR spectra of pure PVPs show that the peaks concentrated around 1660 cm −1 and 2950 cm −1 correspond to the vibration of the functional groups -C=O and -C-H, respectively.The absorption peak at 1290 cm −1 is also due to the vibration of the functional group -C-N-.Also, the vibration peak associated with the O-H functional group is located at 3445 cm −1 .The strength of the coordination interaction between Ag + ions and PVP can be estimated in terms of the magnitude of band shifts.It is noticed that the sequence of the strength of the coordination interaction between Ag + ions and PVPs occurs as follows: PVP 2 M W of 1300,000 > PVP 1 M W of 40,000, and this confirms that with higher M W of PVP, the production of limited growth of AgNWs occurs and different morphologies of silver nanocrystals are formed 20 .
Figure 2d displays FTIR spectra of GO and rGO powders, there is a broad peak at 3413 cm −1 assigned to O-H stretching in hydroxyl, carboxyl groups, and water molecules.The peak around 1620 cm −1 is attributed to C=C stretches from unoxidized graphitic domain and transmittance band at 1725 cm −1 of C=O stretch of carboxyl group and ketones which are adjacent to benzene rings is observed.In addition, the transmittance band at 1070 cm −1 corresponds to the edge phenols and the high-intensity sharp peak at 1380 cm −1 of C-OH stretch of alcohol group is noted.The presence of 1210 and 1100 cm −1 bands is ascribed to vibration of the epoxy groups and peroxides or five-membered ring lactols, receptively [26][27][28][29] .All of these oxidation groups alter the van der Waals interactions among GO layer 30 .Although rGO spectrum has the same features of GO, the intensities of these peaks are declined indicating the success of decomposition of these groups during reduction process of GO by hydrazine and heat treatment 31,32 .
Raman spectroscopy is a simple and powerful characterization tool to determine structure, type of graphitic structures and number of graphene layers.Here in Fig. 3, Raman spectrum of GO exhibits two characteristic peaks at 1352 and 1594 cm −1 .The sharp order G-band at 1594 cm −1 results in the first order scattering of E 2g phonon characteristic of sp 2 hybridization of C-C bonds (i.e., in-plane vibrational mode of C-C bonds).On the  www.nature.com/scientificreports/and rGO, respectively, and this indicates a low degree of defects of GO and the successful thermal and chemical reduction to rGO 33 .

Structural and morphological properties of GO, rGO and AgNWs
The crystalline structure of the AgNWs, GO, and rGO are identified through XRD analysis as shown in Fig. 4. The AgNWs samples with different M W s of PVP exhibit typical XRD patterns of center cubic structure of silver metal as depicted in Fig. 4b.The four characteristic Bragg's reflection peaks of AgNWs-PVP 1 sample are indexed as (111), ( 200), ( 220) and (311) with the highest intensity peak at 2θ of 37.9° ascribed to the (111) plane as illustrated in Fig. 4a (JCPDS, Card No. 04-0783) 34 .AgNWs-PVP 2 pattern suffers from disappearance of the ( 220) and (311) reflection peaks and all the collected data from them are ambiguous.
The standard intensity ratio between (111)/(200) reflection planes and the (111)/(220) reflection planes are 2.5 and 4, respectively, which demonstrate a preferential growth of the AgNWs in (111) plane (i.e. both ends of silver nanowires).However, by using higher M W s of PVP, the intensity ratio decreases, since PVP is coated on the (111) reflection plane and limits their natural growth (i.e.(111) reflection plane is not the preferred orientation of growth) as listed in Table 1 11,35 .Also, the sharpness of Bragg's reflection planes indicates the crystalline nature of the AgNWs samples.To quantify the crystalline nature of AgNWs samples, the degree of crystallinity was evaluated via the percent relative crystallinity (X c ) by using Eq. ( 2) 36 : where A c and A a are the areas of crystalline and amorphous peaks, respectively.
The percentage of crystallinity is calculated to be 92.7%, and 47.3% for the AgNWs samples with PVP of Mw 40,000, and 1300,000, respectively.It is observed that the higher M W PVP affects badly (limitation of preferred growth in (111) reflection plane) on the crystallinity of the AgNWs samples.For a deeper analysis of the AgNWs samples versus the Mw of PVP by using XRD pattern, the main crystallite size (D) and average crystallite size (D Average ) is estimated via Debye-Scherrer's equation (Eq. 3) 37 : where β hkl (2θ) is full width at half maximum (FWHM), hkl are the miller indices of the crystal lattice, k is a constant known as a shape factor = 0.9, λ is the wavelength of X-ray radiation, and 2θ is Bragg's diffraction angle.
As listed in Table 1, the mean crystallite size of the AgNWs samples of the characteristic peak (111) increases as the Mw of the PVP increases.To qualify the crystal structure and the unit cell formation of the AgNWs samples, the interlayer spacings (d-spacings, d hkl ) between AgNWs planes were detected by applying Bragg's Law (Eq.4) and listed in Table 1.
where n is an integer number and d hkl is the interlayer spacing between atoms.
The d-spacing of the characteristic peak (111) were found to be a bit higher than the standard values, as listed in Table 1 34 .Also, the lattice constant (a) of the AgNWs cubic unit cell was also calculated via Eq.( 5) 38 .
where a is the lattice constant for the cubic unit cell.
The lattice constant (a) of (111) plane for the AgNWs samples is found to be slightly higher than the standard database (a = 0.4086 nm) 34 , as listed in Table 1.Notably, both the d-spacing and the lattice constant of the AgNWs samples increased by increasing the Mw of the PVP.Hence, it implies an increase in the distortion of the unit cell formation by increasing the Mw of the PVP, which is previously confirmed by the reduction in the percentage of crystallinity.Consequently, microstrain fluctuations and dislocations are formed in the crystal structure of the AgNWs samples.
The microstrain fluctuations (ɛ) in crystal structure are extracted from the lattice constants equation to be: where a is the measured lattice constant for the AgNWs sample and a o is the standard lattice constant for silver metal.
As shown in Fig. 4b and listed in Table 1, AgNWs samples exhibit tensile macrostrain fluctuations, and their values increase as the Mw of the PVP and crystallite size increases.The tensile microstarin is attributed to the lattice mismatch of the AgNWs due to the increase in the Mw of PVP.Hence, it explains the previously noticed % of expansion in d hkl and lattice constant values as compared with the standard database JCPDs.Also, it elucidates the shift of diffraction angles toward lower values as compared with standard.Subsequently, dislocations between the AgNWs atomic planes were induced as a reflection of the lattice mismatch and macrostrain fluctuations.The dislocations density (δ) in were calculated from 1/D 2 (D is the main crystallite size) 39 , as shown in Fig. 4b and listed in Table 1.It is obvious that by increasing the Mw of the PVP in the AgNWs samples, the particle size increases, and the dislocation density decreases.Interestingly, the average crystallite size (D) and the microstrain fluctuations (ε) can be also calculated by applying Williamson-Hall (W-H) expression (Eq.6) 40 : As shown in Fig. 4c, the average crystallite size and the microstrain fluctuations were extracted from intercept and the slope of the W-H plot, respectively and listed in Table 1.Notably, the average crystallite size and microstrain fluctuations that were calculated from the W-H differ than those from Debye-Scherrer's method.The discrepancy in the values from both methods is attributed to existence of diverse geometries along with microstrain in d hkl .
Figure 4d illustrates the XRD patterns of GO and rGO.XRD patten of GO exhibits sharp and characteristic reflection plane (100) at 2θ of 9.91° with a corresponding d-spacing of 0.8916 nm, which is a good consistency with literature 41 .The high value of the d-spacing confirmed the intercalation of the oxygen atoms, water molecules, and other structural defects between graphitic layers in the GO, which bound to the graphite planar surface 42,43 .Also, two shoulder peaks at 2θ of 20.05° and 26.42° are appeared in the XRD pattern of the GO, which are attributed to a fraction of oxygen atoms was not fully intercalated into GO 10,11 .On the other hand, rGO pattern is displayed with broad characteristic reflection peak (220) at 2θ of 24.27° and d-spacing of 0.3664 nm, which is a good consistency with literature 41 .
Morphological property of GO and AgNWs is illustrated and confirmed by HRTEM micrographs as displayed in Fig. 5.It can be seen from Fig. 5a,b that GO exhibits a typical translucent sheet structure with curls and wrinkles in the middle portion inside yellow circle.GO HRTEM micrographs present diverse layers and lateral dimensions with folded structure due to a deformation during peeling and the presence of attraction forces of functional groups (-OH, -COOH, C=O and C-O-C) 44,45 .
The detailed morphology of a long and thin AgNWs prepared by PVP 1 is shown in Fig. 5c, AgNWs/PVP 1 exhibits homogeneity and sharp end face that comprised (111) planes 35,46 .Furthermore, a thin and lighter contrast coating layer of PVP is clearly wrapped onto the surface of AgNWs so post-treatment step is crucial to remove excess PVP and improve the junction among wires 47 .Obviously, Fig. 5d illustrates high aspect ratio with an average uniform diameter ≈ 46 nm and length ≈ 1.2 µm, and the lattice spacing of 0.23 nm which is in agreement with the d-spacing value of the (111) plane of face centered cubic (FCC) in XRD patterns of AgNWs/PVP 1 .
Figure 5e describes the lattice spacing of 0.23 nm and FCC structure which are characteristic to formation of AgNWs prepared by PVP 2 solution.However, there are more diverse morphologies of Ag NPs, Ag nanorods and lower yield of thick AgNWs in sample prepared by PVP 2 as shown in Fig. 5f.In conclude, the lower the M W of PVP the more uniform formation of AgNWs 48 .In addition, to fabricate high transparent conductive electrodes based on pure AgNWs, samples of AgNWs synthesized by PVP 1 are recommended to be used.

Characterization of fabricated TCEs
Morphological and topographical properties of TCEs SEM micrographs are obtained for AgNWs, AgNWs/ PEDOT:PSS, and AgNWs/rGO electrodes from top view in the right side and 30° tilting angle view in the left side, as shown in Fig. 6.SEM micrographs of annealed AgNWs electrode at 150 °C for 10 min.in air are illustrated in Fig. 6a.Apparently, long and one-dimensional shapes with uniform diameter of 81 nm and average length of 12 µm are observed indicating the high aspect ratios of synthesized AgNWs.However, some pentagonal and spherical structures of AgNWs are noticed and distributed in the sea of AgNWs network indicating that AgNWs grew with a pentagonal cross-section as shown in Fig. 6b.Additionally, it is noted that there are bright spots as shown in yellow color circle among AgNWs crosslinks indicating good connectivity and conductivity of AgNWs 49 .
Furthermore, AgNWs/PEDOT:PSS composite electrodes with a thin and transparent coated layer above AgNWs are observed in Fig. 6c,d.On the other hand, there are some areas with dark shadows indicating non fully coverage of AgNWs.In contrast, AgNWs/rGO composite electrodes display high coverage, homogeneity with low roughness in Fig. 6e,f.In high magnification, rGO layer improves the connection among AgNWs network because the GO film wrapped around the AgNWs, which improved the inter-nanowire junction and achieves the composite goal 50 .
The surface topography, roughness and 3D images of AgNWs, AgNWs/PEDOT:PSS, and AgNWs/rGO electrodes are studied and illustrated using AFM as shown in Fig. 7.The topographic image of AgNWs electrode has a rough surface with a max height of 1510 nm as shown in Fig. 7a.This high roughness value indicates the abnormal thickness of multilayered AgNWs electrode and there are imperfections among the nanowires.The presence of dark areas is associated with network discontinuities due to an incomplete surface coverage 16 .However, the high coverage is achieved by fabricating AgNWs/PEDOT:PSS composite electrode on glass substrate as displayed in Fig. 7b.It is observed that the roughness value of AgNWs/PEDOT:PSS composite electrode declines to 635.8 nm.AFM images of AgNWs/rGO composite film illustrated in Fig. 7c have been smoothened to 258.7 nm attributed to embed of AgNWs in rGO matrix.The composites roughness is considerably reduced relative to the surface roughness of the bare AgNWs mesh [51][52][53] .

Surface energy of TCEs
In order to form a transparent conductive film with composite materials, AgNWs surface has to have high wettability.As shown in Fig. 8a the contact angle between the tangent of water and AgNWs surface is found to be 24.7°.The hydrophilic behavior of AgNWs film is due to the high surface roughness and consequently liquid penetrates the grooves of AgNWs as observed in AFM images.On the other hand, 41° and 65° contact angles are obtained (7) when a drop of water is placed on composite electrodes of AgNWs/PEDOT:PSS, and AgNWs/rGO, respectively as presented in Fig. 8b,c.Composite electrodes with smoother surfaces produce higher water contact angles.Contact angles of diiodomethane are measured to evaluate the surface energy values of TCEs.Surface energy is calculated from a set of liquid/solid contact angles.There are several theories for converting contact angle data into solid surface energy values 54 .Fowkes theory is based on primary equations which describe interactions between solid surfaces and liquids.These Eqs.(8-10)  energy of the solid, and θ is the contact angle between solid and liquid.σ L is overall surface tension of the wetting liquid, and σ S is overall surface energy of the solid.Fowkes theory is applied using contact angle data from only two liquids and the recommended liquids are diiodomethane and water.To determine solid surface energy, the contact angle between solid surface and a drop of diiodomethane which has only dispersive component is measured ( σ P L = 0, and σ D L = σ L ).In this case, the Eq. ( 8 electrodes are decreased with covering AgNWs with smother layer 55,56 .In addition, AgNWs/rGO composite electrode with the lowest value of surface energy confirms the formation of large nano islands and thus lower surface diffusion process.

Electro-optical properties of fabricated TCEs
The electro-optical properties are measured and discussed on AgNWs, AgNWs/rGO, and AgNWs/PEDOT:PSS electrodes after a thermal annealing step as it significantly decrease the resistance without having an impact on their transmittance 57 .The effect of number of layers deposited by AgNWs, and composite electrodes on sheet resistance and transmittance values has been recorded in Table 2.It is noted that there is an inverse relationship between number of layers and both sheet resistance and transmittance of AgNWs electrodes as plotted in Fig. 9a, since increasing number of deposited layers means higher yields of AgNWs that formed and crosslinked together which obviously increase the electrons mobility and consequently reduce the sheet resistance.However, the transmittance values have significantly decreased due to higher diffusion caused by grouping of Ag nanostructures on the glass substrates 10 .On the other hand, the composite electrodes AgNWs/rGO and AgNWs/PEDOT:PSS have significant effect on the reduction of sheet resistance, while a small change in transmittance values is observed in Fig. 9b.Embedding AgNWs in PEDOT:PSS or rGO upper layers to form large hybrid areas assists in enhancing the conductivity and lowering the transparency of C-TCEs 58 .Notably, AgNWs/rGO composite electrode has won the trade-off between optical and electrical properties confirming its ability to perform well in optoelectronic applications.
As listed in Table 3.The presented study is compared with the latest in literature.However, slight changes in values are observed in favor of literature, which is attributed to the differences in the preparation method.It is worth being mentioning that the presented study offers simple, fast, and cost-effective synthesis technique for the synthesis of AgNWs with a comparable result as compared with literature.All these minor changes will be greatly considered in our future work.

Conclusions
AgNWs were synthesized by a simple hydrothermal method using two M W s of PVP.A high aspect ratio and high yield with uniform diameter of AgNWs were obtained using PVP of 40,000.Additionally, the higher M W of PVP of 1300,000 led to a larger and non-uniform morphologies of Ag nanostructures, and lower percentage of crystallinity with diversity of Ag nanostructures which consequently reduced the connection between wires and the sheet resistance of the AgNWs film.The optical, structural, morphological, and topographical properties of prepared materials and C-TCEs are investigated in this article.Covering the AgNWs surface with protective layer from rGO obviously enhanced the AgNWs junction and sheet resistance and showed a little effect on the transmittance.The optimum transparent conductive electrodes possessed high transparency of (78.2%) and low sheet resistance of 27 Ω/□.The electrical properties of C-TCEs exhibited high stability when sheet resistance and transmittance were measured after one month of fabrication process without applying any mechanical forces.

Figure 1 .
Figure 1.(a) A schematic representation demonstrates the step-by-step AgNWs synthesis via the hydrothermal technique, and (b) a schematic diagram depicts the reduction process of AgNO 3 by glucose during the AgNWs synthesis.

Figure 4 .
Figure 4. (a) XRD patterns and indexing of AgNWs samples with PVP 1 and PVP 2 , (b) crystallite size of AgNWs versus microstrain and dislocation density, (c) W-H plot extracted from XRD patterns of AgNWs with PVP 1 and PVP 2 samples, and (d) XRD patterns and indexing GO and rGO.

Figure 5 .
Figure 5. TEM and HRTEM micrographs of: (a, b) GO with two different magnifications, (c) AgNWs/PVP 1 solution without treatment with orange circle demonstrate excess of PVP, (d) width and length measurements on AgNWs/PVP 1 sample to calculate its aspect ratio and the inset depicts d-spacing, (e) AgNWs sample/PVP 2 with face centered cubic (FCC) structure and the inset depicts d-spacing, and (f) AgNWs/PVP 2 sample shows nonuniformity and different Ag nanostructures.

4 Figure 6 .
Figure 6.SEM micrographs of: (a) Annealed AgNWs electrode show sea of AgNWs network with a uniform diameter of 81 nm (b) Pentagonal, spherical particles and bright spots of welded nanowires junctions circled by the red and orange circles appeared from top view of AgNWs electrode, (c, d) 30° tilting angle and top view of of AgNWs/ PEDOT:PSS composite electrode at different magnifications, and (e, f) AgNWs/rGO electrode at different magnifications with fully covered layer of rGO above AgNWs electrode.

Figure 8 .
Figure 8. Contact angle measurements for the surface of (a) AgNWs, (b) AgNWs/PEDOT:PSS composite, and (c) AgNWs/rGO composite electrodes using a drop of water in the left side and a drop of diiodomethane in the right side.

Figure 9 .
Figure 9. (a) Relation between transmittance percentage and sheet resistance of AgNWs electrode as a function of number of deposited layers (b) transmittance spectra in the visible region for pure AgNWs, AgNWs/rGO composite, and AgNWs/PEDOT:PSS composite electrodes.

Table 1 .
Crystallographic parameters were extracted from XRD pattern of the AgNWs, GO, and rGO35,42.

Table 2 .
Transmittance and sheet resistance measurements as a function of number of layers of TCEs.

Table 3 .
Comparison between latest literature and our work.