Sustainable oil palm trunk fibre based activated carbon for the adsorption of methylene blue

Activated carbon (AC) is becoming the limelight due to its widespread application as an adsorbent for wastewater treatment, gases, and catalysis. However, its high consumption and price have drawn more attention to the sustainable use of natural resources as precursor for AC production. This study focuses on synthesising AC from two types of oil palm trunk (OPT) fibres, a significant agricultural waste products produced by Malaysia's thriving palm oil industries. The BET surface area of about 2057.9 m2 g−1 was achieved by chemical activation with phosphoric acid (H3PO4). The efficiency of the synthesised AC was critically analysed based on the adsorption experiments with methylene blue (MB) by varying several parameters (dosage of adsorbent, pH, initial dye concentration, and temperature of the solution) to elucidate the adsorption mechanism(s). A maximum adsorption capacity of 320.4 mg g−1 at 50 °C was achieved, and the Temkin (r2 = 0.98, 0.95, 0.95) and Langmuir (r2 = 0.94, 0.93, 0.95) isotherm models fitted the adsorption process better than the Freundlich (r2 = 0.95, 0.90, 0.86) model. Besides, the pseudo-second-order model (r2 > 0.90) best described the adsorption process, favouring chemisorption over physisorption. Thermodynamics showed MB adsorption on AC was spontaneous except at the highest dye concentration. It was exothermic at lower dye concentrations (50 and 100 mg L−1) and endothermic at higher ones (300, 500, and 700 mg L−1). In a nutshell, this study reveals that OPT fibre is a promising precursor for synthesising highly porous AC for the adsorption of MB dye.


Sustainable oil palm trunk fibre based activated carbon for the adsorption of methylene blue
Muniandy Gayathiri 1 , Thiruchelvi Pulingam 1 , K. T. Lee 2 , Azam Taufik Mohd Din 4 , Akihiko Kosugi 3,4 & Kumar Sudesh 1* Activated carbon (AC) is becoming the limelight due to its widespread application as an adsorbent for wastewater treatment, gases, and catalysis.However, its high consumption and price have drawn more attention to the sustainable use of natural resources as precursor for AC production.This study focuses on synthesising AC from two types of oil palm trunk (OPT) fibres, a significant agricultural waste products produced by Malaysia's thriving palm oil industries.The BET surface area of about 2057.9 m 2 g −1 was achieved by chemical activation with phosphoric acid (H 3 PO 4 ).The efficiency of the synthesised AC was critically analysed based on the adsorption experiments with methylene blue (MB) by varying several parameters (dosage of adsorbent, pH, initial dye concentration, and temperature of the solution) to elucidate the adsorption mechanism(s).A maximum adsorption capacity of 320.4 mg g −1 at 50 °C was achieved, and the Temkin (r 2 = 0.98, 0.95, 0.95) and Langmuir (r 2 = 0.94, 0.93, 0.95) isotherm models fitted the adsorption process better than the Freundlich (r 2 = 0.95, 0.90, 0.86) model.Besides, the pseudo-second-order model (r 2 > 0.90) best described the adsorption process, favouring chemisorption over physisorption.Thermodynamics showed MB adsorption on AC was spontaneous except at the highest dye concentration.It was exothermic at lower dye concentrations (50 and 100 mg L −1 ) and endothermic at higher ones (300, 500, and 700 mg L −1 ).In a nutshell, this study reveals that OPT fibre is a promising precursor for synthesising highly porous AC for the adsorption of MB dye.

AC
Activated carbon ACP1. 5  Activated carbon from parenchyma fibre with acid to precursor ratio of 1.5 ACVB1.5 Activated carbon from vascular bundle fibre with acid to precursor ratio of 1.The manufacturing and consumption of dye in various forms in our daily life generate vast amounts of dye wastewater, primarily from industries such as papermaking, textile, food, printing, cosmetics, etc.Approximately 7 × 10 7 tons of synthetic dyes have been produced to date globally, with the textile industry contributing over

Materials
MB dye (λ max = 664 nm) with molecular weight of 373.9 g mol −1 was purchased from Sigma-Aldrich (M) Sdn Bhd, Malaysia and used as the synthetic dye (adsorbate) in this study.The MB standard curve of absorbance versus concentration was plotted and was used to determine the remaining dye concentrations for the adsorption experiment at different time intervals.Phosphoric acid of 85% was purchased from QRec.Permissions to collect the plant specimens (OPT fibre) was granted by the SATREPS Kluang pilot plant, Johor.

Preparation of OPT based ACs by chemical activation
The OPT was chipped, washed in a dipping tank, wet-milled, screw-pressed, and dried before use.The vascular bundle and parenchyma fibres were separated using different sizes of sieve where the vascular bundle was the retentate of the 1 mm mesh whereas parenchyma was the filtrate of the 0.25 mm mesh.The parenchyma and vascular bundle fibres were impregnated in 85% H 3 PO 4 with an impregnation ratio (acid (g)/fibre (g)) of 0.5, 1.5, 2.5, and 3.5 19 .The solid-liquid mixtures were dried in the oven at 105 °C and carbonised in a horizontal tubular furnace at 600 °C for 1.5 h in an inert atmosphere (N 2 gas flow rate at 200 cm 3 min −1 ) with a heating rate of 10 °C min −1 .Then, the dried samples were weighed before and after carbonisation to determine the percentage yield of AC.The carbonised samples were thoroughly washed using Büchner funnel until the pH of the filtrate water was ~ 7 and dried at 105 °C.

Characterisation of the lignocellulosic precursors and activated carbon
The precursors were analysed for main elements such as carbon, hydrogen, nitrogen, sulphur, and oxygen based on combustion whereby the ratio of the elements was later measured by gas chromatography based on the products from combustion.The Brunauer-Emmett-Teller (BET) surface area analyser (Micromeritics ASAP 2020, USA), was used to determine the specific surface area, pore volume and pore size of the ACs.Besides, the energy dispersive X-ray spectroscopy (EDX) with FEI Quanta FEG 650 SEM were used to determine the elemental compositions on the surface of the precursors and ACs with high pore surface area.

Adsorption experiment
MB dye stock solution of 1000 mg L −1 was prepared and diluted as desired.A 0.1 g of ACs were added to 100 mL of MB dye solution (100 mg L −1 ) and the adsorption was carried out in an incubator shaker for 12 h at 30 °C and 200 rpm.The pH was maintained within 6-7.The absorbance of the samples was measured using UV-vis spectrophotometer at wavelength of 664 nm at intervals after removing the AC through centrifugation (8000 rpm, 6 min) 20 .The concentration of the sample was determined using the MB standard curve.The adsorption capacity (equilibrium at different time) and percentage removal of dye were calculated based on the Eqs.(1), (2), and (3).
The adsorption capacity at equilibrium, q e : where C 0 : initial dye concentration (mg L −1 ), C e : equilibrium dye concentration (mg L −1 ), V: volume of solution (L), w: mass of the AC (g).The adsorption capacity, q t , at time, t: where C 0 : liquid phase concentration of the dye at initial (mg L −1 ), C t : liquid phase concentration of the dye at any time (mg L −1 ), V: volume of solution (L), w: mass of the AC (g).
The percentage removal of MB: where C 0 : liquid phase concentration of the dye at initial (mg L −1 ), C t : liquid phase concentration of the dye at any time (mg L −1 ), V: volume of solution (L), w: mass of the AC (g).
The effects of different parameters: adsorbent dosage (12.5-50 mg), pH of the solution (3-11), initial dye concentration (50-700 mg L −1 ), and temperature (30-50 °C) on the adsorption capacity of MB dye were determined in this study.The Fourier transform infrared (FTIR) spectroscopy (Perkin Elmer, spectrum 2000, USA) was then used for characterising the surface functional groups of AC before and after adsorption of MB.All methods were carried out in accordance with relevant guidelines 21 .

Characterisation of precursors and activated carbon
Table 1 shows that the parenchyma fibre which is in a soft powdery form whereas the vascular bundle fibre has a hard needle-like structure.The precursors were analysed for elements such as carbon, hydrogen, nitrogen, sulphur, and oxygen.There was no significant difference in the elemental compositions between the parenchyma (1)  1.The carbon and oxygen content were approximately 43% and 50%, respectively for both fibres which shows that the OPT biomass may be a suitable precursor to synthesise AC.
The results for the BET analysis are as shown in Table 2 where the precursor had a very low BET surface area of 2.5 m 2 g −1 and 1.7 m 2 g −1 for parenchyma and vascular bundle fibre respectively.However, after chemical treatment of H 3 PO 4 /fibre (0.5), there was a drastic increment in the BET surface area up to 593.0 m 2 g −1 (parenchyma) and 941.3 m 2 g −1 (vascular bundle).This may be due to the role of H 3 PO 4 where it penetrated deeply into the carbon structure of the fibre, forming new pores (mesopores and micropores) that resulted in an increase in the surface area 22 .Similar results were obtained by Zakaria et al. 23 where the mangrove precursor with surface area of 0.0045 m 2 g −1 increased to 789.2 m 2 g −1 after H 3 PO 4 chemical activation at 300 °C.The highest surface area was achieved by ACP1.5 and ACVB1.5 with 1599.8 and 2057.9 m 2 g −1 respectively and were further analysed by SEM and adsorption experiments.
However, the surface area of the synthesised ACs decreased when the IR was further increased to 2.5 and 3.5.This may be due to the dehydration of H 3 PO 4 which formed an insulating layer and prevented the activation by H 3 PO 4 on the OPT fibre which then resulted in the inhibition of internal pore formation 24 .Table 3 shows the surface area obtained for different precursors when H 3 PO 4 was used as the chemical reagent.The surface area of the AC synthesised depends on the type of precursor and the conditions set during carbonisation (concentration of chemical reagent, activation temperature, and the holding time).Besides, when the carbonisation condition and concentration of the H 3 PO 4 were similar, the type of precursor affects the BET surface area, 1545.44 m 2 g −1 (eucalyptus branches) whereas 2375 m 2 g −1 (humins) as shown in Table 3 25,26 .Therefore, the type of precursor also contributes to the pore characteristics of the AC.
The prepared ACs were denoted as ACXY, where AC: activated carbon, X: type of fibre (P: parenchyma and VB: vascular bundle) and Y: IR (0.5/1.5/2.5/3.5).The untreated fibres were denoted as UX (where U: untreated whereas X: type of fibre) and the commercial AC which is of laboratory grade purchased from R&M Chemicals was denoted as CAC.
The relationship between the yield and the BET surface area of the prepared AC at different IR is as shown in Fig. 1A,B.The increase in the IR from 0.5 to 2.5 increased the yield of AC slightly just as reported by Yorgun et al. 29 where the yield of AC produced from paulownia wood treated with H 3 PO 4 increased when IR was increased from 1 to 4. This may be due to the effect of H 3 PO 4 during chemical impregnation causing the cellulose, hemicellulose, and lignin biopolymers to be redistributed while the aliphatic compounds may have converted to aromatic compounds 30 .On the other hand, the BET surface area increased drastically when the IR was increased from 0.5 to 1.5 and then decreased gradually for the ACs prepared from both types of fibre (Fig. 1A, B).The presence of acid derivatives on the fibre may have increased the rate of pore formation, however, excess acid has the potential to break the lignocellulose bonds extensively and shrink the structure, which subsequently suppresses the surface area of the AC 31 .
The untreated parenchyma fibre presented in Fig. 1C has a variety of randomly distributed circular pores of different sizes whereas the AC from parenchyma fibre with highest surface area was able to form large pores as shown in Fig. 1D.The untreated vascular bundle fibre in Fig. 1E has uniformly distributed silica on the external surface.Similar findings were observed by Davamani et al. 32 where the surface of empty fruit bunch of oil palm had accretion of silica with a perforated bottom.The white compounds were still found on the surface of vascular bundle-based AC with highest BET surface area (Fig. 1F).
There is an increase in carbon from 53.5 to 79.2% (parenchyma) and from 29.1 to 86.4% (vascular bundle) and a decrease in the oxygen content after chemical activation.This could be due to gasification and release of volatile matter during the activation process 33 .The phosphorus content on the ACs could be due to H 3 PO 4 impregnation, which formed polyphosphates that retained on the surface of fibres as insoluble metal phosphates or entrapped in the ACs' pores 34 .The nature of the precursor and the chemical activation method play a pivotal role in the synthesis of AC.

Adsorption experiment
Effect of dosage of AC It can be seen that ACP1.5 showed a better dye removal of 78.5% compared to ACVB1.5 with only 59.8% when the least dosage of AC (12.5 mg) was used for the adsorption of MB dye with concentration of 50 mg L −1 (preliminary adsorption) in Fig. 2A).The percentage dye removal increased initially and remained almost similar for both fibres.The adsorption between the MB dye and the AC may have reached saturation at the highest dosage of the adsorbent 35 .The optimum dosage of 50 mg with dye removal of 97% was achieved for both types of ACs in this study.However, in terms of future application of AC for industrial scale, it can be deduced that ACP1.5 would be a better choice than ACVB1.5 for great adsorption of MB with a lesser dosage of AC.The adsorption of ACP1.5 with different parameters was further studied to understand the adsorption process.

Effect of pH of the solution
The increase in the pH from 3 to 11 showed an increment in the adsorption capacity from 92.7 to 99.4 mg g −1 in Fig. 2B).However, no significant increment was observed, therefore, the synthesised AC is robust to different ranges of pH.The slightly higher adsorption capacity at pH of 11 could be due to the dominance of negative charge on the surface of the AC, which created an electrostatic attraction between the positively charged MB and negatively charged OH − ions from the buffer 36 .
The neutral pH was chosen as the optimum pH for further adsorption experiments and not pH 11 as using great amount of buffer to adjust the basicity of the solution is not economically feasible and environmentally benign.

Effect of initial dye concentration and contact time
There is an increasing trend in the maximum adsorption capacity as the initial dye concentration increased as shown in Fig. 2C.The large number of molecules at high initial dye concentration can cause the diffusion rate of the dye molecules through the layer of the surface boundary towards the internal pores on the surface of the AC 37 .The samples with lower initial dye concentrations (50 and 100 mg L −1 ) rapidly attained equilibrium (< 100 min).However, higher initial dye concentrations (300, 500 and 700 mg L −1 ) achieved equilibrium much later (> 360 min).Fewer dye molecules occupy the vacant binding sites rapidly until saturation point compared to when there are more dye molecules with the dosage of adsorbent being the limiting factor.
Figure 2D shows that an increase in the dye concentration induced an increase in the adsorption capacity at equilibrium, q e , 50 mg L −1 (50.0 mg g −1 ), 100 mg L −1 (100.0 mg g −1 ), 300 mg L −1 (246.3 mg g −1 ), 500 mg L −1 (261.5 mg g −1 ), and 700 mg L −1 (310.2 mg g −1 ).Previous literatures obtained a similar trend and this could be due to the availability of large driving force for the MB dye to migrate to the adsorption site on the AC [38][39][40][41] .In contrary, the percentage of dye removal (%R) decreases as the initial dye concentration increases, 50 mg L −1 (100%), 100 mg L −1 (100%), 300 mg L −1 (82.1%), 500 mg L −1 (52.3%), and 700 mg L −1 (44.3%).Al-Ghouti and Al-Absi 42 reported that increasing the initial MB dye concentration caused the adsorption sites on the AC prepared from olive stones to become saturated which subsequently suppressed the dye removal efficiency which can be a reason for the decrease in percentage dye removal in this study as well.
Biomass from different plants is always used to produce AC for dye adsorption studies due to abundant availability and lignocellulosic properties to aid adsorption.Table 4 shows different types of biomasses used and their adsorption capacity for MB dye adsorption at various initial dye concentrations.
The initial dye concentration and the adsorption capacity for different precursors (Table 4) is random.Therefore, in the adsorption process, other factors may have affected the adsorption capacity in addition to the initial www.nature.com/scientificreports/dye concentration.For instance, in a previous literature, it was shown that the atmosphere at which the precursor is activated highly affects the synthesised AC where an atmosphere with oxidant resulted in AC with more oxygen content, higher surface area, and great surface negative charge 43 .

Effect of temperature and initial dye concentration
The effect of temperature on the adsorption capacity (Fig. 2E) shows that the adsorption capacity was unaffected by the temperature for lower initial dye concentrations (50 and 100 mg L −1 ) but it increased with temperature for higher initial dye concentrations (300, 500, and 700 mg L −1 ).
During the adsorption reaction, the increasing amount of adsorbate molecules at higher initial dye concentrations consume energy 42 .Conversely, at lower initial dye concentrations, the small number of dye molecules may have adequate binding sites and may not require energy for the adsorption process.
The adsorption isotherm fitting plotted for each isotherm is as shown in Fig. 3A and the evaluated parameters are as shown in Table 5.Based on the results obtained, the experimental data fitted all three isotherm models studied.However, the Langmuir and Temkin isotherm models have r 2 values more than 0.9 for all three temperatures.This showed that monolayer adsorption was favourable at all temperatures, however, r 2 values of > 0.9 for Freundlich isotherm obtained at 30 and 40 °C showed that multilayer adsorption may have occurred as well.The value of 1/n for Freundlich isotherm lies from 0 to 1, which shows multilayer adsorption taking place on the heterogeneous surface of AC 51 .However, multilayer adsorption of dye on the AC was not favoured at 50 °C (r 2 = 0.86).The decrease in the r 2 value from 0.98 to 0.95 for Temkin model as the temperature increases explains that the heat for adsorption decreases linearly as the adsorbent surface is saturated with adsorbates.

Adsorption kinetics
The adsorption for MB dye by AC in terms of surface adsorption and diffusion into the internal pores was studied by two kinetic studies, pseudo first and pseudo second order.The non-linearised version of the pseudo first and pseudo second order models are stated below in Eqs. ( 7) and ( 8), respectively.( 4) (5) q e = K F C 1/n e (6) q e = Bln(K T C e ) (7) q t = q e 1−e k1 t where k 1 : Equilibrium rate constant for pseudo first order (L min −1 ), k 2 : Equilibrium rate constant for pseudo second order (L min −1 ).The graphs plotted by fitting the experimental data with the kinetic model are as shown in Fig. 3B,C for pseudo first order and pseudo second order, respectively.Table 6 shows the calculated parameters for the two kinetic models.It can be seen that pseudo second order model fits the experimental data better than pseudo first order (8) www.nature.com/scientificreports/model with higher r 2 and lower χ 2 values for all the adsorption experiments regardless of the concentrations and the temperatures.This explains that the adsorption between MB dye and parenchyma fibre based AC favours chemisorption over physisorption 52 .A previous study showed that pseudo second order kinetic model was favoured for the adsorption of methylene blue dye by fly ash as the adsorbent surface is primarily occupied by the dye molecules, leading to a competitive adsorption scenario with water due to the surface being covered by water 53 .The value of rate constant, k 2, decreased with increasing initial dye concentration for all temperatures.This could be due to the competition between the dye molecules at higher initial dye concentrations compared to lower concentrations 54 .The ability to adsorb dye molecules appears to be dependent on the availability of active sites.
Figure 4 shows the Van't Hoff plot and Table 7 shows the thermodynamic parameters for this study.The negative values for ∆G 0 at all temperatures for the initial dye concentrations from 50 to 500 mg L −1 show that the adsorption is spontaneous thermodynamically except for 700 mg L −1 .When the dye concentration reaches a high level, it's likely that the available adsorption sites on the adsorbent surface become fully occupied by dye molecules.Once the surface is saturated in this manner, any additional adsorption becomes less favourable, resulting in a positive ∆G 0 .
The ∆H 0 value for initial dye concentration of 50 and 100 mg L −1 favours physisorption whereas for 300, 500 and 700 mg L −1 chemisorption might have occurred.It was reported previously that enthalpy values of lower than 40 kJ mol −1 indicates physisorption whereas values more than 40 kJ mol −1 indicates chemisorption [55][56][57] .The positive ∆S 0 values for all the initial dye concentrations indicate randomness and stability in the adsorption process.

FTIR spectra analysis
The FTIR analysis was carried out for ACP1.5 before and after adsorption of MB as shown in Fig. 5.The FTIR spectrum for the AC before adsorption shows strong peak at wavelength of 1660 cm −1 .This peak could be due to the stretching of amide I which belongs to protein 58 .It is undeniable that the major source for nitrogen in biomass wood is from proteins and this justifies the availability of nitrogen in parenchyma-based AC.A very slight peak at 1088 cm −1 could be due to two different groups such as the PO 4 which ionised from H 3 PO 4 ester and the P-O-P group from polyphosphate 59 .These phosphate derivatives originated from this study's chemical treatment conducted with H 3 PO 4 .There is a distinction in FTIR spectra between the surface of the AC before and after adsorption.For instance, the two peaks with wavenumber of 1682 and 1584 cm −1 on the AC surface after adsorption may be due to the carboxylic acid (-COOH) and nitromethane group (CH 3 NO 2 ), respectively, which were not present for AC before adsorption 60,61 .This shows the presence of MB on the surface of the AC after adsorption.The slight peak for both AC with wavelength of 1337 cm −1 is due to the hydroxyl group (-C-OH) in-plane stretching which can be due to the hydrogen bond 62 .The small peak at 558 cm −1 may be due to both hydroxyl group out-of-plane bending and alkane group (-C-C) from aromatic hydrogen 63 .The FTIR spectra shows that there is a distinction between the surface of AC before and adsorption of MB dye.

Elucidation of adsorption mechanism
A graphical approach to elucidate the adsorption mechanisms between the dye molecules and the AC is shown in Fig. 6.The four possible interactions involved in this study were hydrogen bonding, van der Waals, electrostatic, and π-π interactions.The existence of electrostatic interactions can be explained due to the increase in the adsorption capacity as the pH of the adsorption medium increased from 3 to 11. Electrostatic interactions may occur between the negatively charged carboxylate group from the AC made from lignocellulosic parenchyma fibre and the positively charged N + group in the MB.Another possible interaction is the H-bonding which might have contributed by the OH − ions added during the adjustment of pH.Besides, the π-π interactions is possible between the aromatic ring that exist in the lignin of the parenchyma fibre and the MB.Although H 3 PO 4 was used to treat the parenchyma fibres initially, it was reported by several literatures that, it is not possible to remove lignin from the lignocellulosic compound efficiently with only H 3 PO 4 64,65 .Van der Waals' forces may have also occurred for the adsorption in this study.The weak attraction force between partial electric charges arising from polar molecules and repulsive force will hold molecules in place and form a stable structure 66 .At lower concentration of dye, the dye molecules diffuse to the internal pores of the adsorbent and adsorb.Adsorption increases the concentration of dye molecules on the surface of the adsorbent, which may have created a stable complex and promote the removal of dye from the solution.

Conclusion
In conclusion, an AC with a large surface area (1599.8m 2 g −1 ), pore volume (1.0), and high adsorption capacity (320.4 mg g −1 ) was synthesised from parenchyma fibre from OPT.The adsorption experiments with different parameters show that ACP1.5 has excellent potential in the adsorption of MB dye, one of the abundantly used textile dyes.It was able to remove 78.5% of dye with least amount of AC (12.5 mg).The AC was robust to different ranges of pH, however neutral pH was optimum for the adsorption process.The adsorption kinetic and isotherm models were used to study the effect of initial dye concentration, temperature, time, and stirring speed on the adsorption capacity.The experimental data well fitted the isotherm models in the following order: Temkin (r 2 = 0.98, 0.95, 0.95) > Langmuir (r 2 = 0.94, 0.93, 0.95) > Freundlich (r 2 = 0.95, 0.90, 0.86), and favours chemisorption (pseudo-second order).In addition, the adsorption is endothermic for lower initial dye concentrations (50 and 100 mg L −1 ) and exothermic for higher initial dye concentrations (300, 500, and 700 mg L −1 ).Elucidation of the adsorption mechanism explains the possible mechanisms (hydrogen bonding, van der Waals, electrostatic, and π-π interactions) involved and can be helpful in forecasting a desired application for future applications.This study shows that AC synthesised from OPT fibre can be a potential adsorbent in dye wastewater treatment.However, further improvements can be made by investigating the effect of carbonisation conditions on the adsorption experiments with wastewater, and reusability studies of the synthesised AC.

Figure 1 .
Figure 1.Effect of impregnation ratio (mass of acid/mass of fibre) on the percentage yield and BET surface area of the AC prepared from (A) Parenchyma and (B) vascular bundle fibre (chemical activation done with phosphoric acid and carbonisation at 600 °C for 1.5 h) and SEM and EDX spectra of parenchyma (C) untreated, (D) activated carbon and vascular bundle (E) untreated, and (F) activated carbon [magnification: ×1000; scale bar 70 µm].

Figure 2 .
Figure 2. (A) Effect of dosage of adsorbent on the percentage of dye removal for activated carbon synthesised from parenchyma (ACP1.5)and vascular bundle (ACVB1.5)fibre, (B) Effect of pH on the adsorption capacity of MB dye on the adsorbent, (C) Adsorption capacity at different time (qt), (D) Relationship between adsorption capacity at equilibrium (q e ) and percentage dye removal, (E) effect of initial dye concentration and temperature on the adsorption capacity of activated carbon.

Figure 4 .Table 7 .Figure 5 .
Figure 4. Van't Hoff plot to determine thermodynamic parameters for different initial dye concentrations and temperatures.

Table 1 .
Elemental analysis of parenchyma and vascular bundle fibres.

Table 2 .
Pore characteristics of untreated fibre, commercial and phosphoric acid treated activated carbon with different impregnation ratios.

Table 3 .
Activated carbon production from various biomass precursor via chemical activation with phosphoric acid.

Table 4 .
Adsorption capacity of various biomass derived adsorbents for MB dye of different initial dye concentrations.

Table 5 .
Parameters for Langmuir, Freundlich and Temkin isotherm models at different temperatures.

Table 6 .
Parameters for pseudo first and pseudo second order kinetics at different temperatures.