Efficacy of alumina nanoparticles as a controllable tool for mortality and biochemical parameters of Culex pipiens

Mosquitoes still pose a clear risk to human and animal health. Recently, nanomaterials have been considered one of the cost-effective solutions to this problem. Therefore, alumina nanoparticles (Al) were synthesized using an auto-combustion method, followed by calcination at 600 and 800 °C. Glucose (G) and sucrose (Su) were used as fuels and the combustion was performed at pH 2, 7, and 10. The as-synthesized Al2O3 nanoparticles were characterized by XRD, FTIR, SEM, and TEM. Alumina nanoparticles prepared using G and Su fuels at pH 7 and 800 °C (Al-G7-800 and Al-Su7-800) have crystallite sizes of 3.9 and 4.05 nm, respectively. While the samples (Al-G7-600 and Al-Su7-600) synthesized at pH 7 and 600 °C were amorphous. The prepared alumina nanoparticles were applied to the larval and pupal stages of Culex pipiens. The results showed that alumina nanoparticles cause higher mortality in the 1st larval instar than in all other larval instars and pupal stages of Culex pipiens after treatment at a high concentration of 200 ppm. Additionally, the larval duration after treatment with LC50 concentrations of alumina (Al-G7-800 and Al-Su7-800) was 31.7 and 23.6 days, respectively, compared to the control (13.3 days). The recorded data found that the content of glutathione-S-transferase, alkaline/acid phosphatase, β/α-esterase, and total protein were altered upon treatment with the LC50 concentration of alumina (Al-G7-800) nanoparticles. Based on these findings, alumina nanoparticles are a promising candidate as a potential weapon to control pests and mosquitoes.

vector for many fevers in Egypt and the world 5,10 .Consequently, controlling vectors is at the forefront of innovative solutions that have been taken into account.However, synthetic insecticide applications, despite their high effectiveness against these species, these substances are problematic because of their frequent use and misuse, which in turn has led to environmental pollution, especially in agricultural and aquatic ecosystems, as well as developing resistance to almost all insecticide classes 11 .Therefore, insect resistance provokes an imperative need for developing new control tools and formulations.
Nanotechnology opens new horizons for scientific technology that could provide a cost-effective solution to a lot of challenging environmental problems.Remarkably, nanoparticles have been applied in many fields such as industry, biomedicine, and agriculture [12][13][14] , where nanoparticles have been recently used as pesticides against insects, either medically or agriculturally 15 .Metal oxide nanoparticles have received much attention and have been widely produced over the last few years in many fields 16,17 .Many researchers confirm the high efficacy of metal oxide nanoparticles as larvicides to mosquitoes and other insects 18,19 .Aluminum oxide nanoparticles are considered a very active member of the metal oxide nanomaterial family, as they can be readily handled and are easily accessible [20][21][22] .Considerably, alumina nanoparticles are characterized by exceptional properties, i.e., their simple and cost-effective protocols and easy surface functionalization.Therefore, they are widely used in the biological environment, particularly in biomedicine and biotechnology, including biosensing treatment of diseases, drug delivery, destruction of microbes 23 , insecticide formulation, and orthopedic applications 24 .This study sheds light on alumina nanoparticles as an alternative insecticide against mosquitoes and other insects.
The preparation of aluminum oxide nanoparticles will presumably be effective against mosquito larvae as an alternative to the use of synthetic insecticides to avoid environmental harm and insecticidal hazards.Therefore, the objective of this study is to fabricate aluminum oxide nanoparticles via a facile auto-combustion method and investigate the toxicity of the as-prepared alumina nanoparticles against Culex pipiens mosquito larvae and pupae.The alteration of some biological aspects will be estimated following treatment with sub-lethal concentrations of the tested aluminum oxide nanoparticles.

Materials
Aluminum nitrate, glucose, sucrose, ammonia, TetraMin, and nitric acid (98%, density of 1.5 g/cm 3 ) were supplied by El-Nasr Pharmaceutical Chemicals Company, Egypt.The bovine albumin standard was purchased from the Stanbio laboratory (Texas, USA).The Coomassie brilliant blue G-250 was from Sigma (Sigma Chemical Co.).P-nitro anisole (purity 97%) was obtained from Ubichem Ltd. (Hampshire), while nicotinamide adenine dinucleotide phosphate (the reduced form, NADPH), was obtained from BDH Chemicals Ltd. (Poole, England).The rest of the chemicals were of high quality and purchased from commercially established local companies.Culex pipiens mosquitoes were obtained from the Medical Entomology Section, Entomology Department, Faculty of Science, Benha University.

Culex pipiens colony
Culex pipiens larvae were reared and kept as a continuous series of laboratory mosquito colonies at 27 ± 2 °C, 75 ± 5% RH, and a photoperiod of 14:10 h (light/dark) in the Medical Entomology Section, Entomology Department, Faculty of Science, Benha University.Larvae of Culex pipiens were fed on TetraMin food fish.TetraMin was added to ground bread with a ratio of 3:1 to prevent any fungal infection.As for pupae, they were periodically transferred from white enamel plates to white plastic cups containing de-chlorinated tap water that were put in screened wooden cages of dimensions (35 × 35 × 35 cm), where adults were allowed to emerge.Periodically, adults were provided with a 10% sucrose solution after a meal of blood through an anesthetized hamster mouse.Larvae and pupae were maintained under the same laboratory conditions 18 .

Synthesis of aluminum oxide nanoparticles
Aluminum oxide nanoparticles were prepared by adding an aqueous solution of aluminum nitrate (10 mL, 10.25 mmol, 4.05 g) to an aqueous solution of glucose (G) as fuel (80 mL, 28 mmol, 9.2 g).The reaction solution was magnetically stirred for 5 min, then divided into four portions: the pH value of the first portion was left unadjusted, and the pH values of the other portions were adjusted into 2, 7, and 10, separately, using 0.2 M NaOH or HNO 3 solutions.Afterward, each solution portion was subjected to auto-combustion at 300 °C on a hot plate for 10 min.Each produced burnt residue after auto-combustion was divided into two parts.One part was calcined at 600 °C for 3 h, and the other part at 800 °C for 3 h.Alumina nanoparticles were prepared at unadjusted and adjusted pH (2, 7, and 10, respectively) and calcined at 600 °C as well.These products are denoted by the symbols (Al-G-600, Al-G2-600, Al-G7-600, and Al-G10-600, respectively).Similar experiments were conducted using sucrose fuel (Su).In the case of sucrose fuel, the products calcined at 600 °C were denoted by the symbols (Al-Su-600, Al-Su2-600, Al-Su7-600, and Al-Su10-600, respectively).While the products calcined at 800 °C by glucose and sucrose fuels were denoted as Al-G-800, Al-G2-800, Al-G7-800, Al-G10-800, Al-Su-800, Al-Su2-800, Al-Su7-800, and Al-Su10-800, respectively.

Characterization of aluminum oxide nanoparticles
Characterization is a crucial procedure to elucidate the crystallinity, phase purity, chemical structure, and morphology of the prepared aluminum oxide nanoparticles.Therefore, X-ray diffraction (XRD), Fourier transmission infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) were employed for this research to investigate the aforementioned characteristics, respectively.

Preparation of Culex pipiens larvae for biochemical analyses
The laboratory strain of the 4th larval instar of Culex pipiens was treated with the LC 50 concentration of the tested alumina nanoparticles.Afterward, 0.5 to 1 g of treated larvae were frozen at − 25 °C for a week.Untreated larvae were maintained in the same conditions.Treated and untreated samples were transferred to the laboratory in iceboxes (− 20 °C) for biochemical analyses.Larval bodies were homogenized using buffer (1 g of insect body/1 mL) in a chilled glass-teflon tissue grinder (ST-2 Mechanic-Preczyina, Poland) for 3 min 25 .Afterward, homogenates were centrifuged at 14,000 rpm in a refrigerated centrifuge for 15 min at a temperature of − 2 °C.Then the supernatant was kept for 2 weeks at − 5 °C to conduct different biochemical analyses.

Determination of biochemical parameters
Determination of nonspecific esterases for the 4th larval instar of Culex pipiens Beta esterases (β-esterases) and alpha esterases (α-esterases) were evaluated using β-naphthyl acetate or α-naphthyl acetate as substrates, respectively.The reaction mixture was composed of 5 mL substrate solution (3 × 10-4 M β-or α-naphthyl acetate, 1% acetone, and 0.1 M phosphate buffer, pH 7) and 20 µL of larval homogenate.Then this mixture was subjected to incubation for 15 min at 27 °C, and then 1 mL of diazo blue color reagent (prepared by mixing 2 parts of 1% diazo blue B with 5 parts of 5% sodium lauryl sulfate).The developed color was read at 600 or 555 nm for β-and α-naphthol produced from the hydrolysis of the substrate, respectively.β-and α-naphthol standard curves were prepared by dissolving 20 mg β-or α-naphthol in 100 mL of phosphate buffer at pH 7 (stock solution).Afterward, ten milliliters of stock solution were diluted up to 100 mL by the buffer.Aliquots of 0.1, 0.2, 0.4, 0.8, and 1.6 mL of the diluted solution (equal to 2, 4, 8, 16, and 32 µg naphthol) were pipetted into test tubes and filled to 5 mL with phosphate buffer.One milliliter of diazo blue reagent was added, and the developed color was measured as mentioned before 26 .

Determination of glutathione S-transferase for the 4th larval instar of Culex pipiens
The reaction mixture was made up of 1 mL of the potassium salt of phosphate buffer (pH 6.5), 100 µL of Glutathione (GSH), and 200 µL of larval homogenate.The reaction started with the addition of 25 µL of the substrate 1-chloro-2, 4-dinitrobenzene (CDNB) solution.The concentration of both GSH and CDNB was adjusted to be 5 mM and 1 mM, respectively.Enzyme and reagents were incubated at 30 °C for 5 min.The increment in absorbance at 340 nm was recorded against a blank containing everything except the enzyme to determine the nanomole substrate conjugated (min/larva) using a molar extinction coefficient of 9.6/mM/cm 27 .

Determination of phosphatases for the 4th larval instar of Culex pipiens
In this method, the phenol released by the enzymatic hydrolysis of disodium phenyl phosphate reacts with 4-amino antipyrine, and by the addition of potassium ferricyanide, the characteristic brown color is produced.The reaction mixture consisted of 1 mL carbonate buffer (pH 10.4) for alkaline phosphatase or 1 mL citric buffer (pH 4.9) for acid phosphatase, 1 mL of 0.01 M disodium phenyl phosphate (substrate), and 0.1 mL sample, which were mixed and incubated for exactly 30 min at 37 °C.At the end of the incubation period, 0.8 ml of 0.5 N NaOH was added to stop the reaction.Afterwards, 1.2 mL of 0.5 N NaHCO 3 were added, followed by the addition of 1 mL of 4-amino antipyrine solution (1%) and 1 mL of potassium ferricyanide (0.5%).The produced color was measured immediately at 510 nm.The enzyme activity is expressed in units (U), where 1 unit will hydrolyze 1.0 µM of p-nitrophenyl phosphate per minute at 37 °C, and pH 10.4 and 4.8 for alkaline and acid phosphatases, respectively.All experiments involved 3-4 replicates (insects' homogenates), and the results of biochemical determinations were pooled from triplicate determinations 28 .

Determination of total protein for the 4th larval instar of Culex pipiens
The protein reagent was prepared by dissolving 100 mg of Coomassie Brilliant Blue G-250 in 50 mL of 95% ethanol.Moreover, 100 mL of 85% (w/v) phosphoric acid was added to the previous solution.The resulting solution was diluted to a final volume of 1 L. Sample solution (50 µL) or for preparation of the standard curve, 50 µL of serial concentrations containing 10 to 100 µg bovine serum albumin were pipetted into test tubes.The volume in the test tube was adjusted to 1 mL with phosphate buffer (0.1 M, pH 6.6).Five millimeters of protein reagent were added to the test tube, and the contents were mixed either by inversion or vortexing.The absorbance at 595 nm was measured after 2 min against a blank prepared from 1 mL of phosphate buffer and 5 mL of protein reagent 29 .

Statistical analysis
The statistical analysis was conducted using a one-way ANOVA test with five factors with a significance level of 0.05 for the whole set of results using SPSS (ver.22).Data were treated as complete randomization designs 30 .Multiple comparisons were subjected to Fisher's least significant difference (LSD).As for Lethal Concentration www.nature.com/scientificreports/(LC 50 ), it was calculated using Probit analysis software 31 .Mean percentages of larval mortality were calculated and corrected for natural mortalities; corrected mortality = (observed mortality % − control mortality %)/100 (control mortality × 100) 32 .The enzymes' results were analyzed by one-way analysis of variance (ANOVA) using COSTA statistical software.When the ANOVA statistics were significant (P < 0.01), the means were compared by Duncan's multiple range test.

Institutional review board
The study was conducted according to the guidelines of the Declaration of Benha University and approved by the Ethics Committee of the Faculty of Science, Benha University under the Code: BUFS 2023-44Ent.

Results and discussion
Nanotechnology is a new scientific technology that could provide a cost-effective solution to some of the most challenging environmental problems, as it is applied in numerous fields such as industry, biomedicine, and even agriculture 12 .Metal oxide nanoparticles have received much attention and have been widely produced in recent years 33 .Investigators have shed light on the general advantages of nanomaterials, recommending their safe application in pesticide production as an application of nanotechnology that will be useful to meet targeted delivery of pesticides.Unlike bulk materials, nanoparticles have unique physical and chemical properties such as tunable size that make them more effective in drug delivery systems 34 , lithium-ion batteries 35 and insecticides 36 .
At the nanoscale, size-dependent effects are more controlled.Therefore, alumina nanoparticles were employed to conduct this study.The X-ray diffraction analysis (XRD) technique was used to investigate the phase composition, purity, and crystallinity of the as-synthesized Al  www.nature.com/scientificreports/nanoparticles prepared by adding glucose and sucrose fuels at pH 7 and calcined at 600 and 800 °C are of cubic phase and well-indexed [No.01-010-0425; space group: Fd3m] 37 .However, alumina nanoparticles (Al-G7-800 and Al-Su7-800) were more crystalline and had crystallite sizes of 3.90 and 4.05 nm, respectively.While the other products, Al-G7-600 and Al-Su7-600, are amorphous.This may be due to the important role of temperature in crystallization, as higher calcination temperatures facilitate the growth of crystals 38,39 .The crystallite size was calculated using the Debye-Scherrer equation 40 : where λ (nm) is the X-ray radiation wavelength, β is the full width of the diffraction peak at half maximum (FWHM), and θ B is the Bragg diffraction angle.The results showed that calcining alumina at 600 and 800 °C was sufficient for obtaining pure nano alumina products, while calcining the samples at lower temperatures produced less crystalline or amorphous alumina contaminated with carbon residues 41 .Conversely, it was reported that well-crystallized α-Al 2 O 3 nanoparticles were prepared after calcination at 1100 °C42 .Therefore, this study implied that pure and crystalline alumina nanoparticles were obtained at a lower temperature.Glucose and sucrose fuels were employed in the production of alumina nanoparticles.The results indicated that the usage of glucose and sucrose fuels at pH 7 produced smaller crystallites, finer agglomeration, and a higher specific surface area than those synthesized by utilizing different pH values.Using glucose as a fuel was better than sucrose.This may be because the nature of agglomeration is primarily governed by the enthalpy or flame temperature generated and the amount of gases that escape during combustion, and subsequently, they affect different characteristics such as particle size, surface area, and crystallinity 42,43 .So, fuel type and pH value are important parameters to the combustion process 44 .It was detected that the fuel affected the properties of alumina nanopowders, which were prepared by an auto-combustion synthesis using aluminum nitrate as an oxidizer and urea ammonium acetate and ammonium nitrate as fuels 38 .
Fuel's impact on the properties of alumina nanoparticles may be attributed to the reduction of the exothermicity of the combustion reaction and the nature of the reaction between both the oxidizing agent and the fuel.This finding was in agreement with data published earlier which used two different fuels, ovalbumin and urea, along with aluminum format to prepare alpha-alumina nanoparticles of different sizes ranging 20-40 nm.On the other hand, the chemical composition of the calcined samples was identified using FT-IR spectroscopy, and the results are shown in Figs. 5, 6, 7 and 8.The FT-IR spectra indicated the composition of alumina nanoparticles (Al-G7-600, Al-Su7-600, Al-G7-800, and Al-Su7-800) by exhibiting the corresponding characteristic frequencies in the region of 400-850 cm −1 .On the contrary, the other samples prepared using other pH values revealed additional vibrational bands due to the carbon residues.The band that appeared at ca. 800-1000 cm −1   may be due to the Al-O-C bond between Al 3+ and glucose and sucrose fuels.The band that appeared at ca. 1339-1645 cm −1 indicated alumina formation.While the band at ca. 2855-2945 cm -1 is probably due to stretching C-H bond of the remaining carbon residue.Finally, the band that appeared at ca. 3444-3454 cm −1 may be due to (-OH) stretching vibrations that indicate the presence of a hydroxyl group 38,45 .
The surface morphology of the as-prepared Al 2 O 3 (Al-G7-600, Al-G7-800, and Al-Su7-600 and Al-Su7-800) was investigated by scanning electron microscope (SEM), and the images are exhibited in Fig. 9.The investigation of the SEM images of the products revealed that they are composed of agglomerates of spherical and irregular morphological shapes.Besides, they are also porous.The products calcined at 800 °C have more spherical shapes than the products calcined at 600 °C.Additionally, the products obtained using sucrose fuel have more symmetrical spherical particles than those obtained using glucose fuel.In addition, the microstructure of the prepared nanomaterials was further characterized by transmission electron microscopy (TEM), as shown in Fig. 10.The TEM images of the products exhibited that the particles have spherical, cubic, and irregular shapes with an average particle size of 15 nm which is consistent with the XRD results.Moreover, the TEM images revealed that alumina (Al-G7-800 and Al-G7-600) synthesized using glucose fuel was more porous than alumina (Al-Su7-800 and Al-Su7-600) synthesized using sucrose fuel.This is probably because the combustion reaction is more exothermic and gives off more CO 2 , N 2 , and H 2 O gases, resulting in more porous products 41 .
The mortality of Culex pipiens larval and pupal stages treated with alumina nanoparticles was investigated.The results showed that alumina nanoparticles induced mortality in all Culex pipiens larval and pupal stages (Tables 1, 2, 3, 4).These results might be explained as nanoparticles being small enough to penetrate nearly all the body whatever the path they took, either by inhalation or feeding.Moreover, insect mortality could be interpreted in terms of protein expression and its relation to RNA and DNA synthesis.It is worth noting that nanoparticles may attenuate the expression of proteins, causing inhibition of RNA and DNA synthesis, which were considered the first signs of cell death 46 .In addition, alumina nanoparticles (Al-G7-800, Al-Su7-800) calcined at 800 °C using glucose and sucrose fuels at pH 7 were more effective on Culex pipiens larval and pupal stages than alumina (Al-G7-600, Al-Su7-600) calcined at 600 °C at the same conditions.This may be because alumina (Al-G7-800, Al-Su7-800) nanoparticles have a smaller particle size and higher surface area than alumina particles (Al-G7-600, Al-Su7-600) coated with carbon residue layers 47 .Distinctly, the present study exhibited that the highest mortality was observed in the 1st larval instar when compared to other larval instars and pupal stages treated with alumina (Al-Su7-600), where the mortalities were 85% and 95%, and with alumina (Al-G7-600), the mortalities were 93.33% and 100% at 200 ppm concentration after 24 h and 48 h, respectively.Meanwhile, in the 1st larval instars treated with Al-Su7-800, the mortality was 95% and 100% after 24 h and 48 h, respectively, and in the 1st larval instars treated with Al-G7-800, they were 100% after both 24 h and 48 h.
Similarly, in another study, it was reported that the mortality of the Aedes aegypti mosquito was positively correlated with the concentration of silver nanoparticles 48 .Furthermore, larvicidal activity against Anopheles stephensi (80 ± 13.69%), Culex quinquefasciatus (72 ± 13.04%), and Aedes aegypti (65 ± 8.66%) mosquito larvae was reported after the previously mentioned species were treated with copper oxide nanoparticles 49 .This high mortality in the first larval instar may be due to their susceptibility caused by the declining rate of detoxification enzymes 50 .
Biochemical studies were also conducted and were presented in Table 5.This investigation was performed through the assessment of some biochemical parameters such as total protein, α-/β-esterases, glutathione transferases (GSTs), and alkaline and acid phosphatases after treating with the LC 50 of alumina nanoparticles (Al-G7-800 and Al-Su7-800) that induce more mortality to investigate the reasons for mortality as indicated in Table 5.In the current results, total protein content is remarkably higher in two alumina nanostructures.This obtained result agreed with a study conducted earlier that indicated histological sections displaying that negatively charged gold nanoparticles were encapsulated inside the discoid cockroach nervous system, which indicated the depletion of proteins for forming a protein corona around the negatively charged gold nanoparticles as a type of defense mechanism 51 .This may be attributed to the active interaction between gold nanoparticles and proteins found www.nature.com/scientificreports/within the biological system, including the nervous system 19 .These findings might point out that developing resistance to metal oxide nanoparticles is possible where the nanoparticles (below 50 nm in diameter) are small enough to be encapsulated 52 .
The tabulated data showed that α-esterase and glutathione transferase (GST) enzymes increased significantly in treated samples compared to untreated samples, indicating that these enzymes increased in Culex pipiens larvae as a defense mechanism against the effectiveness of Al 2 O 3 nanoparticles 53 .Similar results reported that α-/βesterases and glutathione transferase (GST) have been comprehensively scouted in different mosquito species 54 .The aforementioned enzymes may have developed resistance through direct detoxification and urge endogenous and exogenous compounds to be eliminated through different metabolic pathways and/or transformed into useless substances that an insect's body could easily get rid of 55 .Meanwhile, β-esterase activity took a reverse route on treatment with the LC 50 of alumina nanoparticles, as it remarkably decreased.It is noteworthy that β-esterase activity often contradicts the activity of α-esterase 56 .This may be attributed to esterase proteins that are not completely similar in their primary DNA sequences and consequently differ in substrate specificities.Therefore, the catalytic site and binding site that comprise the enzyme's active site are different in both α-/βesterases 57,58 .Acid phosphatase is a lysosomal enzyme that is highly abundant in Malpighian tubules, guts, and disintegrating organs and tissues that have undergone cytolysis 59 .This enzyme is responsible for the hydrolysis of orthophosphate esters and transphosphorylation reactions to provide a phosphate pool for the synthesis of compounds of higher energy such as adenosine triphosphate (ATP), ATPase, and genetic materials (DNA or RNA) 60 .Significantly, in this study, alkaline and acid phosphatases were reduced in samples treated with the LC 50 of alumina nanoparticles compared to the control samples.This highly significant decline may be due to a reduction in the lysosomal enzyme acid phosphatase caused by the ingestion of xenobiotics or toxic substances, which can passively affect the lysosome's activity or cause a lack of energy required for different vital functions and genetic malformations 61 .
Alkaline phosphatase is found primarily in intestinal epithelial tissues, and its core function is to supply phosphate ions from mononucleotides and ribonucleoproteins for different kinds of metabolic processes.However, alkaline phosphatase is active primarily in tissues with active membrane transport, such as intestinal epithelial Table 1.Toxicity of alumina nanoparticles (Al-Su7-600) against larvae and pupae of Culex pipiens, 24 and 48 h post-treatment.Where, a, b, and c symbols mean that there is no significant difference (P > 0.05) between any two means, within the same column that has the same superscript letter.Besides, A, B, and C symbols mean that there is no significant difference (P > 0.05) between any two means for the same attribute, within the same row have the same superscript letter.www.nature.com/scientificreports/cells, Malpighian tubules, and hemolymph 62 .Therefore, the remarkable reduction of alkaline phosphatase may be due to the binding of Al 2 O 3 nanoparticles to the active sites of the enzyme.In addition, alkaline phosphatase may act as a hydrolase during the final stages of digestion, gonad maturation, and metamorphic molts 63 .Consequently, the prolonged larval-adult duration after treatment with the LC 50 of alumina nanoparticles (Al-G7-800 and Al-S7-800) compared with the control shown in Table 6 may be owing to the remarkable reduction in alkaline phosphatases, which play a prominent role in molting, metabolism, cell signaling, and other physiological processes 61 .

Conclusions
In this study, mosquito larvae (Culex pipiens) were used to test how well alumina nanoparticles kill insects and how they affect biochemical parameters in the lab.This study sheds light on the mechanism of action of alumina nanoparticles and their impact on mosquito larvae.Alumina nanoparticles caused some developmental and enzymatic alterations in Culex pipiens larvae, demonstrating their insecticidal activity.Also, this kind of formulation could help cut down on the use of chemical pesticides, which are a major source of pollution and are making insects of medical importance such as Culex pipiens and Anopheles spp.resistant to them.In anticipation of the need for effective integration into pest management strategies, nano-based insecticides may be used in the Table 3. Toxicity of alumina nanoparticles (Al-Su7-800) against larvae and pupae of Culex pipiens 24 and 48 h post-treatment.Where, a, b, and c symbols mean that there is no significant difference (P > 0.05) between any two means, within the same column having the same superscript letter.Besides, A, B, and C symbols mean that there is no significant difference (P > 0.05) between any two means for the same attribute, within the same row having the same superscript letter..00± 0.00aA 100.00 ± 0.00aA 100.00 ± 0.00aA 100.00 ± 0.00aA 70.00 ± 2.89aB 94.00 ± 3.24a Table 5. Determination of total protein, alkaline phosphatase, acid phosphatase, β-esterases, GST, and α-esterases of 4th larval instar of Culex pipiens treated with LC 50 of alumina nanoparticles (Al-G7-800 and Al-Su7-800) after 24 h post-treatment.Where, a, b, and c symbols mean that there is no significant difference (P > 0.05) between any two means, within the same column having the same superscript letter.Besides, A, B, and C symbols mean that there is no significant difference (P > 0.05) between any two means for the same attribute, within the same row having the same superscript letter.Table 6.Means of larval and pupal duration (days) of Culex pipiens at LC 50 of alumina (Al-G7-800 & Al-Su7-800) nanoparticles after 24 h.Where, a, b, and c symbols mean that there is no significant difference (P > 0.05) between any two means, within the same column that has the same superscript letter.Besides, A, B, and C symbols mean that there is no significant difference (P > 0.05) between any two means for the same attribute, within the same row have the same superscript letter.

Table 2 .
Toxicity of alumina nanoparticles (Al-G7-600) against larvae and pupae of Culex pipiens 24 and 48 h post-treatment.Where, a, b, and c symbols mean that there is no significant difference (P > 0.05) between any two means, within the same column that has the same superscript letter.Besides, A, B, and C symbols mean that there is no significant difference (P > 0.05) between any two means for the same attribute, within the same row have the same superscript letter.

Table 4 .
Toxicity of alumina nanoparticles (Al-G7-800) against larvae and pupae of Culex pipiens 24 and 48 h post-treatment.Where, a, b, and c symbols mean that there is no significant difference (P > 0.05) between any two means, within the same column having the same superscript letter.Besides, A, B, and C symbols mean that there is no significant difference (P > 0.05) between any two means for the same attribute, within the same row having the same superscript letter.