Preparation of high-crystalline and non-metal modified g-C3N4 for improving ultrasound-accelerated white-LED-light-driven photocatalytic performances

As a non-metallic organic semiconductor, graphitic carbon nitride (g-C3N4) has received much attention due to its unique physicochemical properties. However, the photocatalytic activity of this semiconductor faces challenges due to factors such as low electronic conductivity and limited active sites provided on its surface. The morphology and structure of g-C3N4, including macro/micro morphology, crystal structure and electronic structure can affect its catalytic activity. Non-metallic heteroatom doping is considered as an effective method to tune the optical, electronic and other physicochemical properties of g-C3N4. Here, we synthesized non-metal-doped highly crystalline g-C3N4 by one-pot calcination method, which enhanced the photocatalytic activity of g-C3N4 such as mesoporous nature, reduced band gap, wide-range photousability, improved charge carrier recombination, and the electrical conductivity was improved. Hence, the use of low-power white-LED-light illumination (λ ≥ 420 nm) and ultrasound (US) irradiation synergistically engendered the Methylene Blue (MB) mineralization efficiency elevated to 100% within 120 min by following the pseudo-first-order mechanism under the following condition (i.e., pH 11, 0.75 g L−1 of O-doped g-C3N4 and S-doped g-C3N4, 20 mg L−1 MB, 0.25 ml s−1 O2, and spontaneous raising temperature). In addition, the rapid removal of MB by sonophotocatalysis was 4 times higher than that of primary photocatalysis. And radical scavenging experiments showed that the maximum distribution of active species corresponds to superoxide radical \documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \setlength{\oddsidemargin}{-69pt} \begin{document}$${\mathrm{O}}_{2}^{\cdot-}$$\end{document}O2·-. More importantly, the sonophotocatalytic degradation ability of O-doped g-C3N4 and S-doped g-C3N4 was remarkably sustained even after the sixth consecutive run.

As above mentioned, it is not cost-effective to use high power light or US sources.In this paper, we have developed two different novel photocatalysis by preparing the high-crystalline and non-metal-doped g-C 3 N 4 .The physicochemical features of the catalysts were investigated by various characterization tools e.g., FE-SEM, FT-IR, EDS, PL, HR-TEM, XRD, SAED pattern, BET-BJH, UV-vis DRS, Zeta-potential DLS, and EIS.On this basis, the sonophotocatalytic performances were assessed under the low-power white-LED-light illumination and US irradiation.

Synthesis of photocatalysts.
Graphitic carbon nitride was prepared according to the method presented in our previous report 36 .In detail proper amount of melamine was heated at 520 °C in a crucible with a cover for 2 h.The as prepared yellow powder then washed by ethanol for three times and denoted as CN.
In order to prepare O doped g-C 3 N 4 , 10 g melamine and 6 g Oxalic acid were dissolved in 50 ml solution mixing of distilled water and ethanol; under continuous stirring magnetically at 80 °C.The heating process continued until the complete removal of the solvent.The obtained sample was calcined in a ceramic crucible with a lid from room temperature to 520 °C at a heating rate of 5 °C/min for 2 h.after that the product cooled to room temperature and were ground to a fine powder.The resulting sample was labeled as (OCN) 37 .
To produce g-C 3 N 4 , 10 g of thiourea and 10 g of melamine were calcined in a crucible with a lid at 520°C with a heating rate of 5°C for 2 h and then cooled to room temperature.The prepared sample then washed with water and ethanol and denoted as (SCN) 38 .

Characterization and instrumentation.
The X-ray Diffraction (XRD; Bruker D8 with Cu 40 Kα and 30 mA, USA) was used to study the crystallinity of the samples.Field Emission Scanning Electron Microscopy (FE-SEM; TESCAN, MIRA3, France) was applied to discern the surface topology, the Energy-Dispersive X-ray Spectroscopy (EDS) was executed to detect the elemental components in the samples.Brunauer-Emmett-Teller (BET) and Barrett-Joyner-Halenda (BJH) were utilized to measure the specific surface area (S BET ), pore size, and pore volume via the N 2 -gas adsorption-desorption method (BEL, Belsorp-mini-II analyzer, Japan), which degassing and operating temperature were + 200 and −196 °C, respectively.Dynamic Light Scattering ((DLS), Malvern, DLS zeta-sizer ZS90 model, United Kingdom) was executed to determine the Zeta (ζ) potential and the average particle size, respectively.UV-Vis Differential Reflectance Spectroscopy (UV-Vis DRS; Analytikjena, Specord 210 plus, Germany) and Photoluminescence Spectroscopy (PL; Avantes-Avaspec-2048, Netherlands) determined Eg value and e -h + recombination rate, respectively.Electrochemical Impedance Spectroscopy (EIS) was utilized to survey the electrical conductivity, and the potential of CB (E CB ) (OrigaFlex, France).UV-vis spectrophotometer (RayLeigh UV-2601, Beijing Beifen-Ruili Co.; China) was employed to measure the removal efficiency of MB.

The assessment of catalytic performances. The MB decolorization efficiency and catalytic degradation
mechanism.The experiments were carried out at the specified dosage of catalyst (0.25, 0.5, 0.75, and 1 g L −1 ), the adjusted pH value (3, 5, 7, 9, and 11), and the desired initial MB concentration (10, 15, 20, and 25 mg L −1 ).Then, the suspension was agitated for 0.5 h in the non-illuminated (dark) condition; then, it turned irradiation sources on [white-LED lamp (30 W, 2800 Lumen) and or Ultrasonic bath (28 kHz, 100 W)] with or without opening Oxygen inlet and controlling temperature (Fig. 1).At specified time intervals (30, 45, 60, 75, 90, 105 and 120 min), 4 ml of the reactive suspension was removed.The suspension was then centrifuged at 4000 rpm.The decolorization efficiency of MB (DEM) was calculated using Eq. ( 1) where A0 and At are assigned to initial and final absorption of MB, respectively.According to Eq. ( 2), the degree of the MB mineralization [i.e., Total Organic Carbon (TOC) decay efficiency] was checked by a TOC analyzer (Shimadzu UV-160, German), where TOC t=0 and TOC t=x is ascribed to the TOC value in the MB degradation process before running and after the specific time, respectively.
To detect the reactive species that generate in the catalytic reactions, 4 m.mol of three typical scavengers (i.e., BQ, BA, and AO preferred as the scavengers of O •− 2 , HO • , and hole (h + ), respectively) separately used in the sonocatalytic degradation of MB under the optimum condition.According to Eq. ( 1), the effectiveness of each active species on the MB degradation process was studied.

Electrochemical measurements.
All electrochemical measurements were accomplished in a three-electrode cell.FTO electrodes deposited with the samples as the working electrode, a platinum wire as the counter electrode, and Ag/AgCl [saturated KCl (3 M)] as a reference electrode respectively.All tests were conducted in a Na 2 SO 4 (0.1 M) aqueous solution as the supporting electrolyte using electrochemical workstation (Origaflex/ France OG 01A).For the preparation of the working electrodes, 200 mg of the obtained photocatalysts were mixed with a small amount of polyethylene glycol and distilled water.The mixture then blended in a mortar until the homogenous slurry obtained and spread onto the Fluorine-doped Tin Oxide (FTO) glass (1 × 1 cm 2 ).The prepared films then were heated at 400° C for one hour in a muffle furnace.
The Electrochemical Impedance Spectroscopy (EIS) was carried out at a frequency range from 10 kHz to 100 mHz with a 10 mV AC voltage, which the Mott-Schottky plots obtained under AC potential frequency 1 kHz, and DC potential range from −1 to + 1 eV vs. Ag/AgCl under dark environment.

Results and discussion
As depicted in Fig. 2, the diffraction peaks located at around 13.1° (100) and 26.8° (002) attributed to the in-plane structural packing of tri-s-triazine units and the typical graphene-like stacking of the conjugated aromatic motif, respectively.Following JCPDS No. 87-1526, these plates are attributed to hexagonal graphitic materials, confirming the lamellar nature of g-C 3 N 4 39 .The (100) peak positions of the modified samples had a negligible shift than CN, indicating that the Oxygen or Sulfur atoms were successfully replaced with Nitrogen and Carbon atoms in the tri-s-triazine units of g-C 3 N 4 .Besides this, the intensity of (100) peak weakened than CN, indicating that the in-plane repeating motifs enlarged.Meanwhile, the position of the (002) peaks was constant, illustrating the retention of the crystalline motif of g-C 3 N 4 .More importantly, the (002) diffraction peaks of the modified samples become sharper and narrower in comparison with CN, implying that the increased degree of polymerization of the precursors led to the higher crystalline structure of g-C 3 N 4 in SCN and OCN than CN [23][24][25] .Scherer equation ( D = K βCosθ , where D, K, λ, β, and θ represent the crystal size, the shape constant value of 0.9, the X-ray radiation wavelength of 1.5418 Å, the full line width at half-maximum height, and the half of the scanning angle range, respectively) uses to calculate the crystalline size of particles.Hence, the index of (002) in CN, SCN, and OCN (1)  40 .Furthermore, no obvious signal of impurities was detected, which is related to the high purity of the prepared catalysts.In summary, the findings suggest that non-metallic doped g-C 3 N 4 samples were successfully produced and their higher crystalline nature was effectively enhanced by introducing different dopant atoms into the g-C 3 N 4 lattice structure 41 .
The obtained FT-IR spectra of the synthesized samples are demonstrated in Fig. S1.The presented characteristic peaks at around 887 and 1200-1700 cm −1 originated from the deformation mode of N-H and the stretching vibration of heptazine heterocyclic ring units, respectively 19,41,42 .In particular, two peaks located around 800-890 cm −1 refer to the out-of-plane breathing mode of tri-s-triazine units.The intensity of these peaks was more vigorous in SCN and OCN than in CN, indicating that the crystalline network of g-C 3 N 4 had become widespread via the successful insertion of Oxygen or Sulfur atoms in the g-C 3 N 4 framework, agreeing well with the results of the acquired XRD patterns 41,43 .In addition, the broader peak at 3100-3500 cm −1 corresponds to -OH stretching states and uncondensed amine groups, while the decrease in the intensity of this peak is attributed to the greater degree of polymerization of the precursors in SCN or OCN than in CN 36 .Moreover, the stretching vibration of the C-O-C peak extremely overlapped at around 1240 cm −141 .More importantly, decreasing the intensity of the -NH x band is due to a more crystalline nature in SCN and OCN than CN, revealing that the most active sites probably do not exist in the lateral edges of SCN or SCN, effectively can lead to diminishing the long-term adsorption of organic pollutant molecules to dominate the catalytic activity [21][22][23] .
The microscopic structural and surface morphology of CN, OCN, and SCN were investigated by FE-SEM.The FE-SEM images in Fig. 3a, c, e show that the structure of the prepared samples includes large grains and two-dimensional bulky sheets with irregular blocks and non-uniform morphology.Unlike CN, which has nearly smooth sheets with sizes of about a few micrometers, SCN and OCN show semi-bulky fractions with smaller sheet size, which is probably the result of the polymerization process.In fact, the thermal conditions of the precursors for the preparation of SCN and OCN have led to changes in the size and shape of the sheets.Smaller particle size and higher porosity network of modified samples compared to CN can lead to an increase in the light-based performance of these samples.In addition, according to the information in Fig. 3a, c, e and Fig. S2, the particle sizes of SCN and OCN are in the range of one micrometer, which shows that a significant reduction in the length and thickness of the modified samples has occurred compared to CN.In fact, when melamine and oxalic acid or thiourea were used as precursors, volatile H 2 O or H 2 S gases created inorganic nanocrystals with a microporous structure in the g-C 3 N 4 framework.In addition, the release of these gases can exfoliate carbon nitride sheets with more wrinkles and irregular shapes.Therefore, these smaller sizes of carbon nitride can lead to increased mass transfer phenomenon in SCN or OCN compared to CN.And the catalytic responses of photocatalysts can be improved 19,30,[44][45][46][47][48][49] .
Figure 3b, d, f revealed that Oxygen or Sulfur elements successfully doped in g-C 3 N 4 structure as OCN or SCN, respectively.Besides this, the prepared samples had high purity without disturbing elements, helping the prepared samples can display the truth of catalytic activities without disruptive impurities 44 .Moreover, a comparison between SCN and OCN evinced that the Oxygen content was more than Sulfur, originating from the truth that AO exerted a potent force for inserting Oxygen atoms into the g-C 3 N 4 structure.Then, it changed the elemental composition of the g-C 3 N 4 motif during the polymerization step, interpreting the stronger electronegativity of Oxygen than Sulfur for doping into the g-C 3 N 4 structure 19,41 .
As shown in the HR-TEM images in Fig. 4a, c, e, the as-prepared samples showed a graphite-like shape with a layered configuration.In addition, the planar structure of CN was transformed into a porous structure in SCN or OCN due to the extraction of off-gases during the intense polymerization of melamine or AO 20 .It is worth noting that the porous structure improves the contact between the surfaces of the catalyst and reactant molecules and leads to the improvement of the catalytic activities of SCN or OCN compared to CN 43 .Significantly, the dark area in the images of SCN and OCN shows the higher crystallinity framework of g-C 3 N 4 , which indicates that more tris-s-triazine units are uniformly arranged in these samples than in CN 38,50 .According to Fig. 4b, d, f, the absence of bright spots in the SAED patterns indicates that these samples have a crystalline nature.In addition, the identified rings match well with the double peaks obtained in the XRD patterns of Fig. 2.
Based on IUPAC classification methods, SBET and pore size distribution in the synthesized catalysts were determined by BET-BJH techniques.The adsorption-desorption isotherms of N 2 gas are shown in (Fig. S3).Information is well presented on the type IV isotherm and H3 residual loops (P/P0 < 0.98), which are associated with slit-like pores resulting from the stacking state of the nanosheets 22,51 .In addition, the obtained isotherms of the non-metal-doped samples shifted toward higher volume compared with CN, proposing that using AO in polycondensation of Melamine presumably led to producing more exhaust gases that concluded to enhancing S BET and the mesopore nature.With a more detailed observation of the statistics summarized in Table 1, the SBET is gradually enlarged and the presence of mesoporous structures (pore size less than 50 nm) sufficiently increases the number of active sites and diffusion channels, resulting in active centers for Provides quick access to reactants 41,43 .In addition, mesoporous structures increase the scattering and multiple reflection of received light and improve the light-dependent responses of catalysts 51 .According to the SBET obtained from SCN and OCN samples, it was concluded that the g-C3N4 non-metallic doping process shows that the catalytic activity is improved, which leads to high sonophotocatalytic performance.More significantly, the relatively low SBET and small pore volume increase the long-term stability of the prepared catalysts 52 .
It is worth noting that the white-LED light source used in this experiment had the ability to emit in the visible light region (λ ≥ 420 nm) (Fig. 5a), the light collection spectrum of the prepared catalysts effectively matches this spectrum.Diffuse reflectance spectra of the as prepared samples are plotted in Fig. 5b.A strong increase in light absorption between 350 and 420 nm was detected for the prepared OCN and SCN samples compared to CN, which implied that increasing mesoporous nature could affect the photo-responses in the high-energy levels of the received light 53 .Besides this, the absorption edge of these modified samples presented a little blue-shift compared to CN, which may be ascribed to the modified van der Waals interactions between tri-s-triazine units due to progressing layer-by-layer exfoliation and decreasing particle size under harsh calcination 53 .Remarkably, the light absorption spectrum of OCN and SCN samples severely red-shifted at the entire visible-light spectrum, originating from the larger atomic radius of Sulfur or Oxygen atoms, and loosely bonding electrons of the dopant atoms in the π-π conjugated system.All of these benefits can lead to facilitating the n → π* transition in the sp 2 hybridization, increasing the generation of the photo-excited of e -h + pairs, and further charge distribution in the g-C 3 N 4 domain 16,38,54 .In addition, the visual investigation reveals that the color change from pale yellow  www.nature.com/scientificreports/ to dark brown in CN to OCN, respectively; signifying that the non-metal doped samples can absorb a broader range of the received light 38,55 .
The band gaps obtained from the Tauc plot, using the Kubelka-Munk function are shown in Fig. 5c, the liner area extrapolated to determine Eg, which obtained 2.17, 2.79, and 2.86 eV for OCN, SCN, and CN, respectively.Therefore, the narrower Eg of OCN and SCN compared to CN, shows that OCN and SCN samples can absorb www.nature.com/scientificreports/more solar energy to produce more electrons and photon-hole pairs, which leads to the improvement of the optical activity of the samples 52 .PL spectra display the photo-generated luminescent intensity of the catalysts, introducing the charge carrier of separation, excitation, recombination, or even migration phenomenon.As known, the defect sites could act as the recombination center of the photo-induced charges.According to the PL quenching theory, if a photocatalyst demonstrates the low-intensity peak of PL, signifying it has a low recombination probability of photo-excited charges, and a high crystallinity nature.As depicted in Fig. 5d, under the wavelength illumination of λ excitation = 355 nm and the expansive emission peak of the λ emission ~ 470 nm, the CN had higher intensity than SCN or OCN. the high crystalline frameworks of the modified samples could have special features, such as the efficient separation ability, and significantly prevent the direct reuniting of charge carriers.Compared with CN, the low peak intensity of PL in SCN or OCN samples denoted that the non-metal atoms were successfully inserted in the g-C 3 N 4 network, which could probably facilitate the charge transport across the photocatalyst interface.In conclusion, the superior suppressed charge carriers' recombination could donate the enhanced photocatalytic performance in the modified samples [18][19][20][21][22][23]56 .
Mott-Schottky plots use to determine the flat band (FB) potential of photocatalysts, thereby meticulously calculating their CB and VB positions.According to Fig. 5e, the FB of CN, SCN, and OCN obtained −0.29, −0.34, and −0.38 V vs. the Ag/AgCl electrode, respectively.In addition, the positive slope approves the n-type conductivity of the prepared samples.As known, the CB potential of the n-type semiconductors has the vicinity to FB (exactly from −0.1 to −0.4 eV); and, the gap between the CB and the FB is usually selected −0.2 eV 41 .Therefore, the CB of CN, SCN, and OCN were estimated at around −0.49, −0.54, and −0.58 eV vs. the Normal Hydrogen Electrode (NHE), respectively.As the displayed Tauc plots in Fig. 5(c), the Eg of CN, SCN, and OCN were 2.86, 2.79, and 2.17 eV, respectively, resulting in the VB potential being calculated as + 2.37, + 2.25, and + 1.59 eV vs. NHE for the samples of CN, SCN, and OCN, respectively.The characteristics of the Eg revealed that SCN and OCN probably represent better photo-dependent performances than CN.
Figure 5f, shows the EIS analyzes to evaluate the resistance and charge transfer in CN, OCN, and SCN.The diameter of the arc radius in the Nyquist diagrams indicates the efficiency of charge transfer.As seen in Fig. 5f the smallest diameter of the arc radius belongs to the OCN, which shows that it has a low resistance to charge transfer and a high ability to separate and transfer e/h + pairs.Therefore, OCN and SCN are expected to have better photocatalytic performance compared to CN 30,43,44 .
Based on the aforementioned analysis, a plausible photocatalytic-based mechanism for the MB degradation using SCN or OCN was exhibited in Fig. 6.According to Fig. 5c, e, the E CB of SCN and OCN were obtained at −0.54 and −0.58 eV, respectively; and, the E VB of SCN and OCN were calculated + 2.25 and + 1.59 eV, respectively.Furthermore, E o (H 2 O/HO • ) and E o ( HO − /HO • ) are equal to + 2.72 eV and + 2.38 eV, respectively; which were more positive than the E VB of the catalysts.It could cause generating h + in the VB of catalysts to be unable to oxidize water molecules for producing HO • .Moreover, the CB of catalysts was more negative than E o (O 2 /O •− 2 ) = −0.33 eV, which could progress the transformation of O 2 into O •− 2 on the CB of catalysts 18,52 .
Assessing the effectiveness of the operational variables on MB decolorization.Screening the effect of catalyst's type and the utilized process.As known, the uncondensed-amine groups of g-C 3 N 4 are strong active sites for pollutant absorption ability; therefore, it should be minimal for accelerating mass transportation over active centers' catalyst without long-term binding to the catalyst surface.As displayed in Fig. S4 and Fig. S1, CN had the most absorption of MB, arising from more amine groups that could create strong Hydrogenbonding between MB molecules and g-C 3 N 4 particles.On the contrary, the high-crystalline samples (i.e., SCN, and OCN) revealed better photocatalytic performances that could originate from the fewer uncondensed-amine groups, and the higher π-π electrostatic interactions between aromatic sections of MB and g-C 3 N 4 .Then, a hybrid process of US and photocatalysis exhibited the accelerated degradation of MB due to the US cavitation causing turbulence near the photocatalytic particles [57][58][59][60] .Therefore, this hybrid could have some benefits for photocatalysis, such as improving the photo-dependent capabilities of catalysts via the deaggregation of particles, continuously cleaning the catalyst's surface to avoid the accumulation of pollutants, accelerating the generation of ROS through the sonoluminescence phenomenon, and promoting mass transfer from the solution to the extremely impede the sonophotocatalytic performances.The DEM experienced a decreasing trend by increasing the initial concentration of MB, which could be referred to (I) As the Beer-Lambert law, increasing the turbidity of the solution prevents light penetration into the dye solution.(II) The generated ROS is approximately similar when the primary dosage of the catalyst is constant; whereas, the efficiency of the catalytic-oriented processes for producing new ROS diminished by occupying active sites in the higher concentration of MB and its by-products.Therefore, the argumentative MB concentration is considered as 20 mg L −15, 9 .
The catalyst dosage.As it is known, the efficiency of photocatalysis and sonocatalysis is strongly dependent on the catalyst dosage.Increasing the catalyst dosage can increase active sites, improve light utilization, and enhance ROS production.As shown in Fig. 7c,d, DEM increased drastically with increasing SCN or OCN dosage from 0.25 to 0.75 g L −1 .A higher catalyst dose (i.e. 1 g L −1 ) was not able to enhance the sonophotocatalytic performance, indicating that the complementary role of US leads to the acceleration of the photocatalytic process.
From a photocatalytic point of view, the turbidity reached its maximum at 0.75 g L −1 SCN or OCN, the excessive amount of catalyst may shield the light, thus decreasing the photon absorption of the photocatalysts.Therefore, US did not have much ability to maintain the upward trend of DEM, and it seems that US can only help to stimulate the catalyst charge during sonophotocatalysis 9 .
The initial pH.The vital variable that could determine the rate of catalytic-based reactions is the initial pH, which is affecting on the surface charge of the catalyst, the aggregation rate of particles, the rate of mass transfer rate into the diffusion layer across the catalyst surfaces, the type of catalytic reactions, and the electrochemical interactions between reactants and catalyst.As known, all as-prepared samples have the many -NH x groups and the wide-spread aromatic network that could form the Hydrogen-bonds and π-π interactions between the MB molecules and the catalyst surface, respectively 9,56 .Furthermore, the obtained ζ potential of CN, SCN, and OCN were −20.5, −12.6, and −6.71 mV, respectively, which correlates with the electronegativity of Oxygen, Nitrogen, Sulfur, and Carbon elements are 3.44, 3.04, 2.58, and 2.55, respectively; implying that the dopant with the higher electronegativity could easily insert into the g-C 3 N 4 network, and increase the positive charge density [61][62][63] .Hence, the low negative charge of OCN and SCN could cause low pH sensitivity and weak electrostatic interactions between the cationic molecules of MB and the catalysts; thereby, the high basic pH could effectively ionize functional groups and increase the amount of negative surface charge.Thus, when the initial pH was adjusted to 11, the DEM improved due to the well-absorbed MB molecules that can effectually react on the highly negativecharged surface of catalysts (Fig. 7e, f) 9 .
The kinetic investigation of the operational variables in the MB decolorization.The kinetic mechanism of the pollution degradation has complexities that can be assessed by calculating the pseudo-firstorder (−Ln (A t /A 0 ) = kt) and the pseudo-second-order ((1/A t ) − (1/A 0 ) = kt) equations, which "k", "t", "A 0 ", and "A t " are the apparent rate constant, the reaction time, the initial absorption of the MB-polluted solution, and the instantaneous absorption of the MB solution, respectively.The regression coefficient (R 2 ) and k could calculate by evaluating the time-based plot of "−Ln (A t /A 0 )" or "(1/A t ) − (1/A 0 )" towards the pseudo-first-order or pseudo-second-order reaction, respectively.Based on the obtained results in Fig. 7, the kinetic studies were accomplished.In the presence of the OCN sample (Table S1, and Fig. S5), the acquired results displayed that all variables had the highest number of R 2 > 0.98 in pseudo-first-order.Meanwhile, for the SCN sample (Table S2, and Fig. S6), the parameter of the initial MB concentration only had the highest R 2 > 0.98 in the pseudo-secondorder, and the other variables followed the pseudo-first-order mechanism.Overall, all drawn of "−Ln (A t /A 0 )" had a nearly linear trend from beginning to end rather than "(1/A t ) − (1/A 0 )", confirming that the sonophotocatalytic reactions of the MB degradation followed the pseudo-first-order kinetic mechanism at presence OCN or SCN.Apart from the desired amount of MB concentration (i.e., 20 mg L −1 ), the other ideal variables (i.e., the catalyst dosage = 0.75 g L −1 and pH 11) had a remarkable agreement with the largest k, offering that the maximum mass transportation could successfully occur by sonophotocatalysis at the optimized values of the operational conditions 8,64 .
The sonophotochemical mechanism and the stability of SCN and OCN to degrade MB.The DEM results obtained for SCN and OCN show that the combination of photocatalyst and sonocatalyst improves the catalytic process, (Fig. S4 and Fig. 7).Absorbed energies (Eqs.( 3)-( 14)) 4,8,9,[64][65][66] .To ensure sufficient mineralization of the organic content, the use of boosters i.e., sufficient oxygen injection and spontaneous temperature increase during sonication can synergistically accompany each other to improve DEM and TOC decomposition (Fig. 8a).In the optimized sonophotocatalytic process, the observations can be justified by the following factors.5)-( 12)) 67,68 .Thus, these synergistic parameters can accelerate the excitation of charges from VB and prevent the accumulation of excited electrons in CB by promoting the activation of O 2 .
(3) The reusability of catalysts is one of the essential criteria for the decontamination process of an aqueous environment, when long-term industrial application is considered.To investigate the superiority of SCN and OCN over each other, we evaluated their recycling performance and reusability in the sonophotocatalytic degradation of MB over six consecutive trials.After each cycle, the catalysts were collected, washed and dried at 90 °C for 5 h 69 .Separation of these catalysts was performed by centrifugation due to their particle size of about one micrometer, which is in good agreement with the results of Fig. 3 and Fig. S2 70 .In addition to sufficient recyclability, the efficiency of sonophotocatalytic degradation of MB was compared in them and the findings are shown in Fig. 8b.When the temperature was kept at about 21 °C and no oxygen was injected into the suspension in each run, the obtained DEM showed a significant decrease of about 22%.Meanwhile, the injection of 0.25 mL s −1 of oxygen gas together with a spontaneous increase in temperature (from about 21 to 33 °C due to US irradiation) caused the DEM efficiency to be maintained for several consecutive periods without losing the profound efficiency.This observation confirmed that oxygen injection can prevent catalyst aggregation and effectively drive Eqs. ( 5) and ( 6).The enhancement temperature could accelerate the heat-dependent reaction (Eqs.( 3), ( 4) and ( 12)) [71][72][73] .
From the first to the fifth run, a slight decrease in the photocatalytic performance of SCN and OCN was observed, which could be due to the adsorption of a small amount of MB molecules and their side products, including mineral ions or photosensitive hydroxides, on the catalyst surfaces.When these disturbing agents accumulate on the surface of the photocatalyst, they block the active sites of the catalyst, and as a result, less excited electrons and less amounts of O •− 2 and HO • are produced.Sometimes these accumulated byproducts may scavenge HO • or form bonds that reduce the catalytic activities of SCN and OCN.Therefore, the catalysts were calcined at 400 °C for 45 min to remove the unwanted side products from the active sites, which can lead to the restoration of the catalyst's performance.In fact, the heat treatment process is suitable for the decomposition of organic compounds, which can greatly clean the catalyst surfaces to reactivate the catalysts.Fortunately, in the sixth run, the sonophotocatalytic abilities were restored to close to the initial run.More importantly, the diffraction peaks in Fig. S7 show that both SCN and OCN maintain their intensity and state without the appearance of new peaks, and in fact, the high crystallinity of SCN and OCN can prevent the loss of sonophotocatalytic efficiency.Thus, it is worth mentioning here that the repeatability and recyclability of these catalysts can attributable to their excellent physicochemical features and optimizing conditions for promoting sonophotocatalytic reactions [74][75][76] .
As known, the photocatalyst can continuously produce reactive species over the surface of itself.Besides this, it believes that radicals discontinuously formed by the transient implosion of cavitation bubbles near the photocatalysts could reinforce the degradation efficiency of MB and its derivative molecules.As a result, the MB can decompose by h + , O •− 2 , and HO • in an ultrasound-accelerated photocatalysis; thereby, the scavenging trials were carried out to identify the dominant reactive species in the presence of AO, BQ, and BA, respectively 9,73 .As depicted in Fig. 8c, d, the addition of BQ effectually led to inhibiting the MB decolorization, indicating that O •− 2 played the determining role in the optimized sonophotocatalytic process.On the contrary, the DME did not significantly reduce after introducing AO, representing that h + was not the primary active substance.In addition, at presence enhancers in the optimized condition, the effect of O •− 2 and OH • was much higher than that of the h + .In addition, the majority of OH • generation can result from the indirect conversion of O •− 2 and the cavitation effect (Eqs. ( 3) and (7-12)).In summary, the obtained results show the prominent role of O •− 2 and then OH • in the removal of MB 77 .

Conclusion
In summary, some simple modification methods for the fabrication of SCN and OCN were carried out through a one-pot non-metallic doping process under special polymerization conditions, which ultimately led to the enhancement of the optical and photocatalytic properties of SCN and OCN, such as reducing Eg and improving light utilization ability, and reduced recombination of charge carriers.So far, the applied synthesis modifications resulted in a safe, inexpensive and simple approach to fabricate highly crystalline nonmetallic g-C 3 N 4 with good structural and surface properties.Then, DRS analysis showed that white-LED light has good harmonics for carrier excitation.Cold-white-low-power LED light showed suitable photocatalytic responses for MB reduction.According to Figure S8, with the synergy between US and photocatalyst, the use of US successfully promoted the photodegradation of MB under optimized conditions.Apart from the role of US in accelerating the excitation of charge carriers by the emission of long-wavelength radiation, the spontaneous increase in temperature (as the first enhancer) showed that the crossing of the activation energy barrier could be improved to facilitate the catalytic reactions.The second booster (i.e., O 2 gas injection) synergistically with sonophotocatalysis, ultimately leads to an increase in MB mineralization efficiency by trapping the most excited electrons to produce OH • Therefore, the introduction of these enhancers into the sonophotocatalytic systems finally revealed the maximum capabilities of the designed heterogeneous AOPs.In conclusion, these practical implementations optimistically extended our insight into the preparation of long-lived g-C 3 N 4 -based catalysts and enhanced sonophotocatalytic performance for rapid decontamination of organic dyes under low-power radiation sources.

Figure 1 .
Figure 1.The schematic of the used sonophotocatalytic reactor.

Figure 5 .
Figure 5. (a) The irradiated spectrum of the used white-LED lamp along with the visual color of the as-prepared samples, (b) UV-Vis DRS spectra, (c) the obtained Tauc plots from the DRS spectra, (d) PL spectra, (e) Mott-Schottky plots, and (f) Nyquist plots.

Figure 6 .
Figure 6.The position of CB and VB in SCN and OCN for performing visible-light-driven reactions in sonophotocatalysis.
(I) According to the Arrhenius theory, increasing the temperature during catalyst-based reactions can improve the reaction rate (Eqs.(3), (4) and (13)).(II) Apart from the catalyst surfaces that sites provide an activity to carry out the cavitation phenomenon, there are sites for the sonophotocatalytic process.Therefore, sufficient O 2 dissolution can absorb the excited electrons and H • and affect the catalytic formation of O •− 2 (Eqs.(5 and (6))67 .(III) As hot spot theory, the irradiated energies could induce to excite the semiconductors for further producing eh + pairs (Eq.(4)) 17 .(IV) As known, the lifetime and stability of ROSs generally isH 2 O 2 > O •− 2 > OH • .Therefore, the additional consumption of O 2 by photocatalysts could produce more O •− 2 and H 2 O 2 , which consequently results in the photo-generated e -h + pairs having enough opportunity for attacking H 2 O 2 for the additional production of O •− 2 and OH • (Eqs.(

Figure 8 .
Figure 8.(a) Screening the portion of the processes along with showing the effect of injecting O 2 gas along with spontaneous raising temperature in sonophotocatalytic degradation of MB, (b) the reusability tests for SCN and OCN, (c) the scavenging experiments over SCN, and (d) the scavenging experiments over OCN.(AC: without enhancers (without O 2 injection + holding temperature about 21 °C); and, BC: with enhancers (injecting 0.25 mL s −1 O 2 + spontaneous raising temperature without control)).

Table 1 .
The attained data from adsorption-desorption isotherms.