Exploring the half-metallic ferromagnetism, dynamical and mechanical stability, optoelectronic and thermoelectric properties of K2NaMI6 (M = Mn, Co, Ni) for spintronic applications

The structural stability, optoelectronic and magnetic characteristics of K2NaMI6 (M = Mn, Co, and Ni) halide double perovskites have been demonstrated to be explained using density functional theory computations. The prominent generalized gradient approximation and integration of the mBJ potential are implemented to estimate the exchange–correlation potential, which is the only unidentified parameter in the state-of-the-art formulism. The structural optimization, mechanical stability criteria, and tolerance factor demonstrate the reliability of the double perovskites in a cubic structure with Fm3m symmetry. The elastic constants facilitated mechanical stability and revealed the brittle nature of these double perovskites. The spin-polarized electronic band profile and the behaviour of the dielectric constant and absorption coefficient in the spin-up and down channels show the presence of half-metallic nature in these materials. Additionally, we examined magnetism and the genesis of the half-metallic gap in this article. The half-metallic and magnetic properties are attributed to the unpaired electrons in the split d-orbitals of the M-sited elements in the crystal field. The Mn-, Co-, and Ni-based double perovskites were found to possess total magnetic moments of 4 μB, 4 μB, and 1 μB, respectively, with the transition metal atoms comprising up the majority of this magnetic moment. The Fermi level’s perfect spin polarisation promotes the potential application of double perovskites in spintronic technology.

the visible-UV region, as well as an appearance of a half-metallic nature.Similarly, Cs 2 NaMCl 6 (M = Ti, V) 12 has a good thermoelectric response and has a figure of merit zT that is almost identical to one and is a half-metallic ferromagnet.The halide double perovskite Cs 2 KXCl 6 (X = Co, Ni) and Rb 2 NaCoF 6 13,14 are also half-metallic ferromagnets with a good response to optical characteristics.BaMO 3 (M = Mg, Ca), KMgO 3 , and REMnO 3 (RE = Ce, Pr) [15][16][17] are new half-metal ferromagnetic materials for spintronic applications.
This study examines the structural, optoelectronic, magnetic, and elastic properties of a cubic K 2 NaMI 6 (M = Mn, Co, Ni) compound employing realistic density functional theory and the PBE-GGA and mBJ approximation.These compounds exhibit half-metallic ferromagnetism in their cubic phase.This research aims to examine structural stability, photovoltaic and thermoelectric applications, and the genesis of half-metallicity in these materials.Inspire by the above similar discussed materials we explored the cubic phase of the K 2 NaMI 6 combination because, as far as we were aware, there are no data on its electrical, elastic, optical, magnetic, and transport properties.The high value of the absorption coefficient makes its use for optical implementations and the sophisticated value of the thermoelectric figure of merit zT makes it viable for thermoelectric efficiency which is a necessary component for an eco-friendly environment.These survey results might pave the path for the use of these materials in spintronics.
Computational.The ground-state energy, electronic, and magnetic properties of the K 2 NaMI 6 (M = Mn, Co, Ni) perovskites were assessed through spin-polarized calculations employing the Wien2k simulation package.Optimizing the crystal energy concerning volume can be used to numerically predict the stability and ground-state structure.To improve the structure, the Birch-Murnaghan equation 18,19 of state was utilized E 0 , B 0 , V 0 , and B ′ 0 indicate the relaxed state's energy, bulk modulus, volume, and pressure derivatives of B 0 , accordingly.For the Kohn-Sham equation to be solved, both the potential from the core and valence electrons were considered.The exchange-correlation impact was approximated by employing the well-known generalized gradient approach (GGA) 20 .Further, the magneto-electronic property of perovskites was analyzed using the Tran-Blaha-modified Becke-Johnson potential (mBJ) 21 .The unit cell volume is partitioned by muffin-tin spheres (with R MT radii) about the atomic sites and interstitial space.The response of electrons inside the muffin-tin sphere and in interstitial space was addressed by employing a linearized augmented plane wave basis set.The plane wave cut-off in interstitial space was altered to R MT K Max = 7, whereas the atomic-like wave functions within spheres have been extended to l Max = 10.The interval between the core and valence states was chosen to be -6.0Ry (cut-off energy), and the irreducible Brillouin zone was incorporated using a k-mesh of 1000 points.While the charge converged up to 0.0001e and the energy convergence has been 0.0001 Ry.

Structural stabilities.
The double perovskite materials K 2 NaMI 6 (M = Mn, Co, Ni) with the stoichiometric formula A 2 BB′X 6 crystallize in a cubic shape with the space group Fm3m (225).The components (atoms) retain their respective position.The bulkier cation possesses 12-fold coordination and dwells in the body-centered cubic system with a Wyckoff position at (0.25, 0.25, 0.25).The enduring B(Na) and B′(M) atoms have fractional coordinates (0.5, 0.5, 0.5), and (0, 0, 0) are positioned in the middle.Furthermore, the B and B′ atoms are settled within the enclosures and are encompassed by the X atoms, which have a geometrical position at the corner locations (0.25, 0, 0), producing varying BX 6 and B′ X 6 octahedrons, as depicted in Fig. 2. It is apparent that the Na/M-atoms are surrounded by octahedra of I-atoms, whereas K is coordinated by 12 I-atoms.Moreover, Birch Murnaghan's equation of state demonstrates the accuracy of the relaxed lattice constants 22,23 .According to the literature survey and visual representation presented in Fig. 1, the minimum ground state energy for the given materials is explicit in the ferromagnetic phase.However, as displayed in Table 1, the stabilization curves for the specified compounds exhibit significant properties like the lattice constant a 0 (nm), volume in (a.u 3 ), bulk modulus (B), a derivative of the bulk modulus (B′), and crystal-free minimum energy (Ry).Moreover, taking into account the formation enthalpy and tolerance factor mentioned in Table 1 is vital when assessing the structural stability of these perovskites 24 .If the estimated result is between 0.9 and 1.0, it means that every atom is precisely aligned at its individual places, leading to an ideal cubic structure.The tolerance factor (τ) is highly dependent on the crystal structure.Because the 12-folded cation is too tiny to occupy its position (τ = 0.71-0.9),an orthorhombic or rhombohedral structure results.If τ is greater than one, the A-site cations become larger to accommodate their sites, leading to hexagonal formations.Different structures are generated for τ = 0.71.The current work demonstrates that K 2 NaMI 6 (M = Mn, Co, Ni) defines structural stability in the Fm-3 m space group with tolerance factor values in the cubic range (0.9-1).In Mn > Co > Ni-based double perovskites, it is apparent by contrasting the unit cell volume that the lattice constant decreases.This is due to the fact that atomic size decreases.Figure 2 depicts the structure of the unit cell.It is obvious the Na/M atoms are contained within the octahedron of I atoms, with I being coordinated by 12 atoms.
The enthalpy of formation is negative on being calculated, which affirms the energetically and thermodynamically stability of the given compound.Therefore, the given compound is stable as revealed in the Table 1.
The energy required to separate a solid into its constituent atoms or significant structural units is known as cohesive energy (Echo).When it comes to compound stability, this energy is vital.The stronger a compound's stability, the higher its cohesive energy.This energy represents how tightly atoms in a material are bound together.
The cohesive energy for double perovskites can be computed as The evaluated value of the given double perovskite K 2 NaMI 6 is displayed in a Table 1.The results show that the atoms are firmly bound together to form the crystal.www.nature.com/scientificreports/Phonon stability.We executed self-consistent computations on the optimized unit cells to obtain ground state wave functions with a more confined convergence threshold of 10 -18 for potential residual.The adequate effect of density functional perturbation theory (DFPT) as encoded in Quantum espresso 25 has been determined in the present scenario to evaluate the dynamical stability within the primitive unit cells of K 2 NaMnI 6 , K 2 NaCoI 6 , and K 2 NaNiI 6 perovskites and evaluated using mBJ potential and carried out self-consistent perturbation computations with the convergence threshold of 10 -18 for the potential residual to obtain the dynamic matrix.For the phase stability of K 2 NaMI 6 scenarios, the quantified phonon dispersion curves along the highsymmetry directions in the Brillouin zone appear in Fig. 3.The stability of the compound K 2 NaMI 6 (M = Mn, Co, Ni) has been evaluated using a phonon spectrum computation.In addition, a proper understanding of the lattice-dynamical characteristics of solid materials-where phonons play an intriguing role-is necessary to comprehend many aspects of materials.The phonon dispersions curves were obtained for that purpose once lattice dynamics computations were completed.In theory, a crystal lattice with n atoms per unit cell will have 3 n branches, 3 of which will be acoustic, while the remaining n will be optical.According to the criterion for a structure's dynamical stability, all frequent vibration modes must exhibit actual and finite frequency.Our findings are displayed in Fig. 3. Imaginary frequencies are absent in K 2 NaMnI 6 and K 2 NaCoI 6 based perovskites, indicating their dynamical stability.Additionally, it is evident that the K 2 NaNiI 6 structure has imaginary frequencies 26 , which are below zero in the ordinate scale of Fig. 3.As a result, based on the current computations, K 2 NaNiI 6 is dynamically unstable in this structure because it shows a small negative frequency.
Elastic properties.The computed elastic constants are vital for comprehending the material's structural reliability and certain other mechanical properties.It expresses the material's behavior when pressure is applied to the material.The cubic structure has 3 (three) elastic constants C 11 , C 12 , and C 14 that can depict the material's mechanical properties.Table 2 shows the simulated elastic constants of lead-free double perovskites K 2 NaMI 6 (M = Mn, Co, Ni).To ensure the validity and reliability of our computation, we incorporate Born-Huang stability rules 27 for cubic crystals: C 11 > 0; C 44 > 0; C 11 + 2C 12 > 0; C 11 − C 12 > 0. The observation of our calculations suggests that these titled double perovskites K 2 NaMI 6 (M = Mn, Co, Ni) meet the Born-Huang stability criteria, confirming these perovskite materials are stable.The shear modulus (G) 28 of a material, which offers information about its rigidity, is used to evaluate its resistance to reversible deformation under shear stress.As a result, G is computed using two models: Voigt (G V ) 29,30 and Reuss (G R ) And, Hill 31 (G H ) computed the arithmetic mean of G V and G R : The measured G H values depicts that K 2 NaMnI 6 has the maximum shear modulus (18.26 GPa), implying that it is harder than the other materials.Young's modulus (Y) can be used to evaluate a material's reaction to linear deformation 32 , which implies that a material's toughness is inversely correlated with the value of Y. Owing to the connection, the tougher the material is, the higher the value of Y.
The greater Y value (45.96GPa) for K 2 NaMnI 6 signifies that it is the toughest of these compounds.A material's ductile or brittle character can be distinguished using Pugh's ratio (B/G) 33 ; a specimen is ductile if the ratio is more than 1.75; otherwise, it is brittle.Our analysis of the data shows that these materials are brittle because their B/G values are below the critical value of 1.75.Cauchy pressure can be used to define a material's capacity for bonding as well as its brittle or ductile nature.
The following equation explores the value of Cauchy pressure.
. www.nature.com/scientificreports/Higher Cauchy pressure affects ionic bonding, while lower values reveal directional bonding (covalent bonding).These compounds are brittle by nature, as shown by the C P values in Table 2. Compressibility is assessed using Poisson's ratio v, which gauges the contribution of neighbouring longitudinal strain to non-axial tensile stress: Exploring Poisson's ratio can also acknowledge the elastic properties of a composite material.The difference between ductile and brittle characters is denoted by the index value of 0.26.Double perovskites exhibit a brittle character below their index value while being ductile above it.Electronic band structure.A material's electronic and magnetic properties can be analyzed to determine its feasibility for technological applications.The electronic band structure (BS) operates a vital role in describing the nature of a material whether a material is a conductor, semiconductor, or insulator.If the electronic states between the valence band (VB) and conduction band (CB) overlap at the fermi level this results in metallic behavior or if there exists a forbidden gap between VB and CB this results in a semiconductor or insulator.The forbidden gap between VB and CB can be reduced by applying the temperature that is band gap and temperature are inversely proportional to each other.For the mentioned double perovskites, we address the electronic band structure, total density of states, and partial density of states (TDOS and PDOS).Spin-polarized calculations are used to interpret the electrical behavior of up and down spin channels.Figure 4 depicts the band structure as evaluated using the spin-polarized GGA and mBJ techniques.From the BS, it is apparent that the spin-up states of Mn and Ni compounds and the spin-down of Co detect metallic properties since the energy states in each channel surpass the Fermi level, which is set at 0 eV.There are no energy states at the fermi level when in the spin-down channel except in the case of Cobalt which manifests the metallic aspect in the spin-down channel.Furthermore, for Mn (Ni) based materials, the prohibited band gap between the conduction band minima and the valance band maxima is 4.41 (4.87 eV) indicating that the spin-down channel is semiconducting in nature, and for cobalt-based material semiconducting gap (5.3 eV) exists in the up channel.The occurrence of transition element d-valance electrons in K 2 NaMI 6 may render the GGA inefficient for the compounds which in turn makes the energy band gap underrated.As a result, modified Becke Johnson potentials are combined in GGA to more precisely describe band structure.
The electronic properties of the K 2 NaMI 6 (M = Mn, Co, Ni) double perovskites are modified by both GGA and GGA + mBJ approximations and are illustrated by the total density of states (TDOS) as shown in Fig. 5.The band gap in the spin-down semiconducting channel (Mn, Ni) and spin-up channel of Co has broadened as a response to the electronic states of K 2 NaMI 6 drifting farther from the Fermi level.
Furthermore, we assessed the partial density of states (PDOS) to exclusively examine the band structure and framed the energy states affiliated with the valence and conduction bands.As demonstrated in Fig. 6, the I-atom promotes the greatest layout of the valance band.The d-states of the transition atom are vital and have a profound impact on electronic performance.Assessing the PDOS of the three double perovskites discloses that the transition atoms' d-states are orientated diversely across the Fermi level, which contributed to their half-metallic nature.In the spin-up channel's valance band of Mn, p-d hybridization emerges between the dt 2g states of Mn and I.The Mn-deg states at the Fermi level are accountable for the metallic nature of the Mn-based double perovskite.In addition, all of the d-states of Mn in the spin-down channel are shifted from the Fermi level form the conduction band minima.In the Co-based double perovskite Both the dt 2g and de g states of the   www.nature.com/scientificreports/metallic character in the spin-up channel at the Fermi level, whereas in the spin-down state, they support the conduction band minima.The total magnetic moment for the Mn-, Co-, and Ni-based double perovskites is 4μB, 4μB, and 1μB, respectively.The prevalence of half-metallicity is also revealed by the integral magnetic moment.) sets, is diminished by the crystal field caused by M-I Coulomb interactions.According to Hund's rules, the d eg state can only hold an aggregate of 4 electrons (2↑ + 2↓), whereas the dt 2g state has an intake ability to hold 6 electrons (3↑ + 3↓).The electrons have a choice of concerning forming a low-spin state, in which d eg states are filled only after the dt 2g states are completely occupied, or a high-spin state, in which higher energy de g levels are filled before pairing appears in the dt 2g orbitals.The crystal field splitting energy (CFS) and pairing energies investigate whether a high-spin state or a low-spin state will occur.The high-spin state can emerge only when the splitting energy is less than the pairing energy.The CFS is impacted by the size of the central atom and the number of electrons.The splitting is impacted by the ligand type; strong field ligands may cause extensive splitting.The creation of the high-spin state relies on the oxidation number, electron number, and size of the transition anion when weak field ligands like Cl/Br/I appear because the CFS is small.The expected oxidation states in these double perovskites are K 2 1+ Na 1+ M 3+ I 6 1-.Mn 3+ , Co 3+ , and Ni 3+ have 4, 6, and 7 valance electrons, respectively, in their d states.The Mn 3+ d state has an electron occupancy of 3t 2g (↑), 1eg (↑), 0t 2g (↓), and 0e g (↓), leading to a high-spin state with S = 2.The conduction band minima are generated by the vacant d states in the spin-down state.As shown in Fig. 6 the deg state in the spinup channel is partially filled and resides at the Fermi level.The Co-based double perovskite's DOS plots make it remarkably clear that all of the d states in the spin-up channel are inhabited.The Fermi level is attained by the dt 2g states in the spin-down channel.As a result, the electrons inhabiting the valance states of the Co 3+ states are 3t 2g (↑), 2e g (↑), 1t 2g (↓), and 0e g (↓), resulting in four electrons unpaired with S = 2.The occupancy suggests that the d-orbitals in the spin-up channel are filled, producing the valance band.While partially filled dt 2g states in the anti-parallel spin channel contribute the associated spin channel a metallic aspect.The number of electrons at the center atom grows as one moves from Mn to Ni, while the size diminishes.Ni3 + has the electrical configuration 3t 2g (↑), 3t 2g (↓), 1e g (↑), and 0e g (↓), which left one unpaired electron and so S = 1/2.When Ni is the most central atom, the spin state turns from high to low.Each unpaired electron possesses a magnetic moment approaching 1 μB, therefore the total magnetic moment for the Mn-, Co-, and Ni-based double perovskites is 4 μB, 4 μB, and 1 μB respectively.

Thermodynamics.
We have integrated a quasi-harmonic approximation of the Debye model (QHM) 34 to examine the thermodynamic reliability of these perovskites K 2 NaMI 6 (M = Mn, Co, Ni).The QHM massively represents the stability of these different quantities, encompassing the specific heat at a constant volume (C v ), Debye temperature, and Gruneisen parameter (γ), in the temperature and pressure range of 0-550 K and 0-5 GPa, this type of model is desirable and acknowledged as being efficient in predicting the findings in a certain temperature and pressure ranges.
We proceeded by demonstrating the specific heat of each material at constant volume (C V ), which belongs to the critical aspects that affect the material's behavior.The current materials have a flatter trajectory for heat transmission at room temperature due to the T 3 relation.At elevated temperatures, the graphical deviation of the specific performance of the entitled compound has a drift toward the Dulong petit limit, as depicted in Fig. 7.The high-temperature constraint indicates that the change follows Delong-law Pettit's 35 .
Among solids' most essential thermodynamic qualities is the Debye temperature (θ D ) 36 .It is the maximum temperature at which the particles (constituents) produce correlated vibrations and the vibrations attain their highest achievable frequencies.It is an effective indicator of material hardness; materials with a significant θ D have high stiffness and are relatively very robust than materials with a low θ D . Figure 7 depicts θ D as a function of temperature, it is recognizable that θ D diminishes as temperature increases.Thermal expansion and anharmonicity are modest at low temperatures, resulting in a virtually constant Debye temperature.At low temperatures, the high-frequency modes can be thought of as locked; only the sound waves are activated.As a result of the θ D decreasing with temperature, the atoms' vibrational frequencies change as a function of temperature.K 2 NaMNI 6 , K 2 NaCoI 6 , and K 2 NaNiI 6 have Debye temperatures of 157.87 (206.11)K and 427.09 (444.34)K and 153.44 (209.90)K at 300 K and 0 (5) GPa respectively, at ambient temperature.The perovskites can be operating for applications at higher temperatures, depending on the high value of the Debye temperature.www.nature.com/scientificreports/Moreover, as depicted in Fig. 7, we have simulated the Gruneisen parameter (γ), which describes the anharmonicity and presents a clear explanation of the phonon frequency modes.At lower temperatures, the Gruneisen parameter (γ) has a gradual ascending exponential pattern; but, at higher temperatures, remains almost constant.However, pressure's consequence on (γ) has a limited impact on it.The Gruneisen parameter has been assessed to have values of 2.39, 1.94, and 2.93 at 300 K and 0 GPa, respectively.
Thermoelectric.Due to the expansion of the global economy in recent years, there have been severe energy crises and significant environmental degradation as a result of the massive increase in the utilization of fossil fuels.To determine how effectively thermal energy can be converted into electrical power, the thermoelectric (TE) characteristics of K 2 NaMI 6 double perovskites are examined.Utilizing TE compounds, excess heat can be www.nature.com/scientificreports/turned into electricity to solve the energy shortage and minimize harmful emissions [36][37][38][39][40] .In the 0-1000 K temperature range, we assessed TE parameters such as electrical conductivity (σ), Seebeck (S), thermal conductivity (κ), and figure of merit zT using the BoltzTraP2 code.The number of electrons applicable for conduction dictates electrical conductivity (σ).In the Spin-up channel of K 2 NaMnI 6 , K 2 NaNiI 6, and the spin-down channel of K 2 NaCoI 6 the electrical conductivity diminishes with a rise in temperature revealing the metallic behavior in the respective channels as indicated in Fig. 8.At 50 K (1000 K) the simulated electrical conductivity values for Mn, Co, and Ni are 6.62 (6.15) Ω −1 m −1 s -1 , 1.72 www.nature.com/scientificreports/ (1.26) Ω −1 m −1 s −1 , and 1.12 (0.98) Ω −1 m −1 s −1 .Moreover, in the spin-down of K 2 NaMnI 6 , K 2 NaNiI 6 , and the spin-up of K 2 NaCoI 6 the electrical conductivity increases with an increase in temperature determining the semiconducting behavior in their respective channels.The calculated values for Mn, Co, and Ni at 50 K (1000 K) are 0.0012 (1.23) Ω −1 m −1 s -1 , 0.0017 (9.95) Ω −1 m −1 s −1 , and 0.0102 (6.54) Ω −1 m −1 s −1 .At 0 K the semiconductor behaves almost like an insulator, however, with rising temperature, the amount of charge carriers increases as they acquire sufficient energy to move from the VB to CB.These compounds have maximum electrical conductivity owing to their exceptionally low resistance, implying that they could be employed to fabricate thermoelectric devices.
The Seebeck coefficient (S) explains a material's capability of producing electrical potential.It is a crucial factor for determining the thermoelectric efficiency of a material.The Seebeck coefficient indicates the quantity of voltage generated by a material as a result of a temperature variation across it.Figure 9 shows the Seebeck coefficients (S) of the given halides K 2 NaMI 6 (M = Mn, Co, Ni).The halide perovskite (Mn, Ni) performs metallically in the case of spin-up, which implies that the Seebeck coefficient rises with an increase in temperature, and for Co, it shows metallic behavior in the down channel thus for the metallic case, the Seebeck coefficient in K 2 NaMnI 6 , K 2 NaNiI 6 , and K 2 NaCoI 6 grows abruptly from a lowest value of 0.86 (57 μV/K), 3.91 (39.28 μV/K) and 3.20 (37.79 μV/K) along the specified 50 (1000 K) temperature.The exact diminishing nature is experienced in the spin-down scenarios for the two specific perovskites K 2 NaMnI 6 and K 2 NaNiI 6 from the lowest temperature of 50 K with a value of 2698.27μV/K and 2334.19 μV/K towards the known value of 244.19 μV/K and 274.28 μV/K at 1000 K and in case of Cobalt, it shows the decreasing trend in spin up channel depicts semiconducting nature in the respective channel.The calculated Seebeck coefficient value of K 2 NaCoI 6 at 50 K (1000 K) is 2270 μV/K (265 μV/K).As a result, the interpretation retrieved from the proper Seebeck coefficient ratio values desires to broaden the approach toward thermoelectric applications.
Thermal conductivity (к) is a flow of energy (heat) in response to a temperature difference.The significance of к is comprised of two components.The prime is induced by electronic transport, which is addressed as the electronic part of thermal conductivity (к e ), and the second is impacted by lattice vibrations (phonons), which is examined as the lattice component of thermal conductivity (к l ).
At high temperatures, the merit of к l can be discarded since it exhibits an inverse relationship with absolute temperature 41,42 .As a response, we computed the thermal conductivity (electronic component) per unit relaxation time (к e /τ) for K 2 NaMI 6 (M = Mn, Co, Ni) as depicted in Fig. 10a.The variation of к e /τ concerning temperature reveals the same increasing pattern as that of σ/τ.The Wiedemann-Franz law 43 explains the linear relationship between electrical and thermal conductivity, which compensates for this behavior.The highest values of к e /τ were 1.53 × 10 15 W m −1 k −1 , 3.40 × 10 15 W m −1 k −1 , and 2.58 × 10 15 W m −1 k −1 for K 2 NaMnI 6 , K 2 NaCoI 6 , and K 2 NaNi 6 respectively.
The figure of merit (zT) is of great importance in scrutinizing the effectiveness of thermoelectric (TE) characteristics.The zT is a thermal efficiency parameter that could be computed utilizing the mentioned calculation [44][45][46] .
The improved value of S with σ and the low value of κ strengthened the value of zT.At 1000 K, the zT values of K 2 NaMnI 6 , K 2 NaCoI 6 , and K 2 NaNiI 6 are 0.15, 0.12, and 0.11 respectively (see Fig. 10b).These findings indicate the feasibility of these materials for thermoelectrical applications.

Optical properties.
To ascertain whether material is adequate for an optoelectronic application, it is essential to scrutinize a variety of optical characteristics, including the real (ε 1 (ω)) and imaginary (ε 2 (ω)) portions of the dielectric function, the absorption coefficient α(ω), the optical conductivity σ(ω), and several others.
The dielectric functions used to scrutinize polarization and absorption of electromagnetic radiation within the specific material are numerically conveyed by the relationship ε 1 (ω) = ε 1 ω + iε 2 (ω) 47,48 .In this relationship, the first term stands for the real part ε1ω, which illustrates the polarisation of light while the second term (ε 2 (ω)) performs the imaginary portion of the dielectric function, or term ε 2 (ω), which measures the degree of light absorption.For optoelectronic devices, the strength of the transitions between and within bands determines the absorption and emission of light strengths.
The fluctuation of ε 1 (ω) and ε 2 (ω) with reference to photon energy is illustrated in Fig. 11a,b where it is practicable that in the spin channels of Mn-up, Co-down, and Ni-up, the high value shifts negative between 0-1.3 eV for the Mn-and Co-based double perovskites.Incoming electromagnetic energy (photon) is effectively dampened by the double perovskites in the negative range of ε 1 (ω), confirming their flawless metallic character.As shown in Fig. 11a the ε 1 (ω) affects the linear behavior of polarisation and photon energy distribution while traveling across materials in spin channels of Mn-down, Co-Up, and Ni-down, its values rise with increasing photon energy and peak at the resonance frequency.The largest peaks for Mn (Co) and Ni were detected at 9 eV (8.5 eV) and 7.8 eV.As a result, at the resonance frequency, the light is entirely polarised or dispersed.When the frequency of an incoming photon fluctuates significantly from resonance values, the polarisation abruptly lowers and light energy begins to absorb, as represented by the imaginary ε 2 (ω) in the following section.
A key indicator of the functionality of optoelectronic devices is the imaginary part of the dielectric constant, ε 2 (ω), which depicts the photons that perovskites can retain.The optical edge noticed at 0 (zero) eV for Mn-up, Co-down, and Ni-up denotes the metallic character in the admissible spin channel.The Mn-down, Co-up, and Ni-down spin channels could be semiconducting because there aren't any energy levels at the Fermi level, contrary to the existence of peaks other than zero energy.Moreover, Fig. 11b illustrates the factor ε 2 (ω) that controls how much photon energy changes as it passes through a material medium.Interestingly, the critical ε 2 (ω) value Figure 12a shows the calculated α(ω) spectrum as a function of energy, indicating how abundant light energy is absorbed by a substance 49 .The energy peaks in the spin-up of Mn and Ni and the spin-down channel of cobalt www.nature.com/scientificreports/support metallic character, and the absence of absorption in the energy range below 2.5 eV, suggests these materials are transparent, supporting the semiconducting nature.The absorption coefficient steadily increases in visible and ultraviolet energy ranges, which is greatly affected by inter-band transitions from the VB to CB.These materials are more convenient for solar cell applications due to their immense optical absorption coefficient α(ω) in visible and ultraviolet ranges.However, we saw significant peaks develop in an energy range of 9-11 eV; following the energy value, absorption gradually diminishes, as shown in the absorption plot (Fig. 12a).The expansion of electrical transmission 50 to high spectral frequencies is defined as optical conductivity σ(ω).The computed conductivities are shown in Fig. 12b, this material feature is important for optoelectronic devices.Mn-up, Ni-up, and Co-down materials exhibit optical conductivity at lower photon energies, indicating that light absorption in low-energy regions sustains the metallic character in their respective channels.Furthermore, the optical conductivity grows quickly with the increase in photon energy at around 4 eV and reaches the maximal value for the given material at around 10 eV for the down channels of Mn and Ni and in the spin-up of Co.The www.nature.com/scientificreports/investigated halides are a viable candidate for implementation in solar cells and other low-energy optoelectronic devices owing to their optical conductivity at this energy level.

Conclusion
In summary, the simulated structure demonstrates that the cubic phase of the halide perovskite K 2 NaMI 6 (M = Mn, Co, Ni) is stable.The negative value of the formation energy E F and the positive value of the cohesive energy (E c ) revealed that the present compound is thermodynamically and energetically stable.The band structure has been specifically acquired using mBJ approximation.From spin-polarized band structure and DOS estimations, it is obvious that all of these compounds are ferromagnetic half metals due to the reasonable band gap in the spin-down channels (Mn and Ni) and up channels of Co, as well as 100% spin polarisation at Fermi level.For K 2 NaMI 6 (M = Mn, Co, Ni) the absolute spin magnetic moment value is 4 μB, 4 μB, and 1 μB and these magnetic moment values are merely due to the M atoms via strong p-d hybrid.The brittle nature of these compositions is revealed in the computation of Poisson's ratio (< 0.26) and Pugh's ratio (1.75) ratio.Diverse optical properties reveal that these materials can be widely used for optical devices/applications owing to their strong absorption and solar cell applications due to their outstanding optical conductivity.By examining the transport properties, advanced thermal efficiency values for K 2 NaMI 6 are achieved.These findings demonstrate that K 2 NaMI 6 can be employed effectively for thermoelectric devices as well as spintronics applications.
spin-up channel lie below the Fermi level and are involved in p-d hybridization.While the dt 2g states are at the Fermi level in the spin-down channel reflects metallic character whereas the de g states are unoccupied lie above the Fermi level reveals the semiconducting nature, leading to the half metallicity of the given compound.The dt 2g states, on the other hand, are totally filled for both spin channels in the Ni-based double perovskite and dwell in the valance band.The de g states in the spin-up channel at the Fermi level contribute to the metallic character, while the conduction band minima appear in the spin-down state.However, the dt 2g states are entirely filled for both spin channels and are positioned in the valance band in Ni-based double perovskite.The deg states produce

κ
= κ e + κ l zT = S 2 σT/κ Vol:.(1234567890)Scientific Reports | (2023) 13:12795 | https://doi.org/10.1038/s41598-023-39230-2www.nature.com/scientificreports/plays a crucial role in revealing the threshold energy that characterizes the difference between transmission and absorption.For K 2 NaMI 6 (M = Mn, Co, Ni), the expected optical and electronic band gaps are in remarkable conformity.The absorption bands' energy values fall within the visible and ultraviolet energy ranges.The existence of an absorption area in the visible range has tremendous potential for the development of solar cells and optoelectronics.

NaMnI 6 K 2 NaCoI 6 K 2 NaNiI 6
The M-site atoms appear in the I-atoms' octahedral environment, as specified in the structural details.The degeneracy of the Mn/Co/Ni d(d xy , d yz , d zx , d x