Abstract
Bimolecular charge recombination is one of the most important loss processes in organic solar cells. However, the bimolecular recombination rate in solar cells based on novel non-fullerene acceptors is mostly unclear. Moreover, the origin of the reduced-Langevin recombination rate in bulk heterojunction solar cells in general is still poorly understood. Here, we investigate the bimolecular recombination rate and charge transport in a series of high-performance organic solar cells based on non-fullerene acceptors. From steady-state dark injection measurements and drift–diffusion simulations of the current–voltage characteristics under illumination, Langevin reduction factors of up to over two orders of magnitude are observed. The reduced recombination is essential for the high fill factors of these solar cells. The Langevin reduction factors are observed to correlate with the quadrupole moment of the acceptors, which is responsible for band bending at the donor–acceptor interface, forming a barrier for charge recombination. Overall these results therefore show that suppressed bimolecular recombination is essential for the performance of organic solar cells and provide design rules for novel materials.
Similar content being viewed by others
Introduction
The development of non-fullerene acceptors has recently accelerated the improvement in power-conversion efficiency of organic solar cells1,2,3. As a result, the efficiency of single-junction organic solar cells has reached 18%4,5. The recent transition from conventional fullerene to non-fullerene acceptors has offered the advantages of more flexibility in tuning the energy levels, as well as the realization of a complementary absorption spectrum to that of the donor polymers1,6. While great progress has been made in the efficiency of organic solar cells comprising non-fullerene acceptors, it is not fully understood why these acceptors perform so well7,8,9,10,11,12,13,14,15,16,17,18,19. In particular, bimolecular recombination rates have only been sparsely investigated in these solar cells18,20,21,22,23. It is known that non-geminate recombination plays in an important role in the fill factor of solar cells24, as well as the open-circuit voltage25, and therefore the power-conversion efficiency. While bimolecular recombination in low-mobility semiconductors closely follows the Langevin mechanism26,27, being based on the diffusion of oppositely charged carriers toward each other in their mutual Coulomb field, the bimolecular recombination rate in efficient organic bulk-heterojunction solar cells can be orders of magnitude lower than the predicted Langevin rate based on the mobility of charge carriers28. One can describe the reduced Langevin recombination rate according to29
where \(\gamma \) is the Langevin-reduction factor, q is the elementary charge, ε is the permittivity of the material, and \({\mu }_{n}\) and \({\mu }_{p}\) are the mobilities of electrons and holes, respectively. The origin of the Langevin-reduction factor, which can have values even below \({10}^{-3}\)29, is not fully understood, although sub-Langevin recombination is of paramount importance to achieve high-performance organic solar cells. While phase separation in a bulk heterojunction in combination with unbalanced mobilities can lead to minor deviations from classical Langevin recombination, this is insufficient to explain the frequently observed large deviations from the Langevin recombination coefficient30. Reduced Langevin recombination has been linked to enhanced dissociation of charge-transfer excitons at the donor–acceptor interface31,32,33, although the origin of an improved CT-states dissociation rate itself is not straightforward34. Enhanced CT-dissociation has been associated with domains with greater percolation31, with energetic disorder35,36,37, and with an energetic cascade between pure and mixed phases of the donor–acceptor blend38,39. Being a major determinant of device performance, it is crucial to understand the origin of reduced Langevin recombination in organic solar cells.
Here, we investigate bimolecular recombination in a series of organic solar cells, comprising the fluorinated-thienyl benzodithiophene (BDT-2F) based donor PM6 blended with three different acceptors PC61BM40, IT-4F41 and Y66, and PBDB-T blended with IE4F-S42 or O-IDTBR43 (as shown in Fig. S1). By measuring the steady-state electron, hole, and double-carrier currents in dark, the charge-carrier mobilities and Langevin prefactors are obtained. The recombination prefactors are additionally obtained by simulation of the current–voltage characteristics of the solar cells under illumination. For well-performing systems, Langevin reduction factors of around 10–2 or even lower are obtained, which is demonstrated to be of critical importance for the fill factor of the solar cells. Computer simulations demonstrate that the quadrupole moment of the acceptors is responsible for band bending at the donor–acceptor interface, giving rise to an energy barrier for bimolecular recombination. The calculated quadrupole moments correlate with the measured recombination rates, rationalizing the high performance of organic solar cells based on non-fullerene acceptors.
Results and discussion
To investigate bimolecular recombination in organic cells, we measure space-charge-limited currents (SCLCs) in the donor–acceptor blends. Measuring SCLCs is a well-known method to obtain the steady-state charge-carrier mobility in semiconductors29. By selectively injecting either electrons or holes into the material or material blend, a space charge of electrons and holes builds up. This is the maximum electrostatically allowed charge in the semiconductor, giving rise to bulk-limited current that depends only on the charge-carrier mobility, as given by the Mott-Gurney law44. When injecting electrons and holes simultaneously, the electrons and holes either recombine or neutralize each other depending on the recombination rate. A low recombination rate leads to effective charge neutralization due to the coexistence of electrons and holes, allowing an increased buildup of net space charge. This increased space charge enhances the injected double-carrier current. Therefore, the magnitude of the double-carrier current can be used to quantify the amount of charge recombination, competing with charge neutralization29.
To extract the recombination rate, or the Langevin-reduction factor γ, one has to know the electron, hole, and double-carrier current, as obtained from the dark current of an electron-only, hole-only, and solar-cell device, respectively. The Langevin prefactor is then analytically obtained as29
where \({J}_{p(n)}\) is the hole (electron) current density and \({J}_{D}\) the double-carrier current density, equivalent to the injected dark current density of a solar cell. This equation demonstrates that low Langevin prefactors are obtained for high injected dark currents (JD), which arise from effective electron and hole neutralization. We note that γanalytical is obtained from experimentally measured currents only, without any data fitting. Alternatively, the Langevin prefactor can also be obtained by fitting the J-V characteristics with numerical drift–diffusion simulations.
Besides the Langevin prefactor, the electron and hole mobility can be obtained from the space-charge-limited electron and hole current densities, \({J}_{n}\) and \({J}_{p}\). These are obtained by fitting the \(J\)-\(V\) characteristics with drift–diffusion simulations45 (Fig. S2). As illustrated in Table 1, the electron and hole mobilities for PM6 based optimal blend films are balanced and quite similar for all three acceptors (PCBM, IT-4F, and Y6) used, all values being close to 3 × 10–8 m2 V−1 s−1. As a result, similar theoretical Langevin recombination strengths are expected for these three blends. The deduced experimental Langevin prefactors from Eq. (2), on the other hand, show a clear difference, with reduction factors in the range of 10–2 for both non-fullerene acceptors and 10–1 for PC61BM and PC71BM (Fig. S4). Alternatively, the prefactors are obtained by fitting the dark current characteristics (JD-V) of double-carrier devices with drift–diffusion simulations, using the obtained experimental mobilities and the Langevin prefactor (γdark) as the only adjustable fit parameter. As expected from the previously established agreement between Eq. (2) and numerical drift–diffusion simulations29, similar results are obtained, as shown in Table 1.
To demonstrate the impact of these Langevin reduction factors on the solar-cell performance, the \(J\)-\(V\) characteristics of the solar cells under illumination are simulated and compared to experiment. Simulating the solar-cell characteristics with classical Langevin recombination, as determined from the experimental electron and hole mobilities, results in a clear underestimation of the fill factor and open-circuit voltage, as shown in Fig. 1a. This demonstrates that the bimolecular recombination rate must be clearly reduced with respect to Langevin recombination. For the fullerene-based blend, the deviation from the experiment is the smallest, indicating that the bimolecular recombination rate is closer to Langevin recombination as compared to the solar cells with non-fullerene acceptors. This is consistent with the Langevin prefactors determined from the dark measurements (Table 1; Fig. 1b).
As a next step, the \(J\)-\(V\) characteristics under illumination are simulated by using the Langevin prefactor (γlight) as a fit parameter, while using the measured charge-carrier mobilities. As observed in Fig. 1a, excellent agreement with experiment is obtained, with the used Langevin prefactors (γlight) listed in Table 1. The prefactors obtained from the drift–diffusion simulations under illumination agree well with those determined by the dark measurements, ascertaining the obtained values. An important conclusion that can be drawn from these results is that in particular the high fill factor is a direct result of the reduced bimolecular recombination rate in the solar cells based on the non-fullerene acceptors. The decent mobilities do not necessarily guarantee good device performance (cf. simulations with Langevin rate in Fig. 1a) stressing the importance of reduced bimolecular recombination in these systems.
While reduced bimolecular recombination has been observed frequently in organic bulk heterojunction solar cells, its origin is still not well understood. Unbalanced mobilities in combination with phase separation can account for a minor reduction in the bimolecular recombination rate, but is unable to explain Langevin coefficients reduced by several orders of magnitude30. Such reduction coefficients are remarkable, especially since Langevin recombination is well obeyed in pristine organic semiconductors26,27. To investigate the origin of reduced bimolecular recombination in organic solar cells based on non-fullerene acceptors, it is useful to study systems in which the bimolecular recombination rate is markedly different. Therefore, we selected the non-fullerene acceptors IE4F-S and O-IDTBR blended with the non-fluorinated donor PBDB-T, which have been reported to give markedly different fill factors42,46. Since charge transport is even slightly superior in PBDB-T:O-IDTBR (Table 1 and Fig. S5), the low fill factor likely originates from increased bimolecular recombination compared to the PBDB-T:IE4FS system. Indeed, as shown in Table 1 and Fig. S6, the Langevin prefactor obtained for the PBDB-T:O-IDTBR system is close to Langevin recombination, while for PBDB-T:IE4FS bimolecular recombination is reduced by more than two orders of magnitude compared to Langevin recombination. Figure 2 shows that classical Langevin recombination can almost reproduce the solar-cell characteristics under illumination for PBDB-T:O-IDTBR, while the fill factor is severely underestimated for PBDB-T:IE4F-S, indicating strongly reduced bimolecular recombination in the latter case. Even though the Langevin reduction factor is clearly different for these blends, the difference in the fill factor is not as pronounced, which is due to the favorable electron and hole transport in the PBDB-T: O-IDTBR solar cell, in combination with a lower charge-carrier generation rate, reducing the photogenerated electron and hole density and thereby bimolecular recombination. On the other hand, the low Langevin prefactor in the PBDB-T:IE4F-S blend allows for more photogenerated charge carriers while maintaining a high fill factor, and thereby increasing the power-conversion efficiency.
To investigate the origin of the difference in recombination strength among the studied system, we simulated the rough donor–acceptor interface using the lattice model47 (details are given in the Supplementary Information). The concentration gradient gives rise to a gradient in electrostatic potential near the interface, as shown in Fig. 3a. Effectively, this results in the energy level bending at the donor–acceptor interface, of which the magnitude is dictated by the quadrupole moment9,17,48,49 and intermixing50 of the organic semiconductors9,17,48,49, and has range of up to 5–6 nm on either side of the donor–acceptor interface48,51, which is comparable to or larger than the effective Coulomb capture radius52. The role of the bias potential has so far been recognized in the splitting of charge-transfer states, reducing geminate recombination9,18,53,54. We hypothesize that the bias potential may also give rise to a barrier for nongeminate recombination. Energy level bending at the donor–acceptor interface, shown in Fig. 3b, would create a barrier \(B\) for electrons and holes, reduce the electron and hole density in close proximity to the interface, and suppress bimolecular recombination.
To quantify this reduction, we modified a model for bimolecular recombination by Arkhipov, initially proposed for amorphous silicon with a fluctuating potential landscape55. Within the approximations of this model (see Supplementary Information for details), the reduction of non-geminate recombination is exponentially proportional to the barrier B,
where \(\xi =1/\langle {e}^{-\frac{U\left(x\right)}{{k}_{\mathrm{B}}T}}\rangle \sim 1\), and \(R\) is the interface recombination coefficient. Equation (3) suggest that \(\gamma \) is temperature-activated, which indeed has been observed experimentally, see Fig. S3. The bias potential \(B\) is in fact a rather involved quantity that depends on the interfacial roughness, molecular packing, solid-state electrostatic contribution to ionization energy and electron affinity9,48,56. The key dependence in the case of acceptors aligned along the donor acceptor interface is, however, due to the interaction of a charge with quadrupole moments of surrounding NFA molecules56, with a dominant contribution due to the component along the \(\pi \)-staking direction, \({Q}_{\pi }\),
This proportionality is shown in Fig. 3c. For IE4F-S, having a large quadrupole moment, the Langevin prefactor is the lowest. For Y6 and IT-4F, the quadrupole moments are similar, also exhibiting a similar reduction in bimolecular recombination. The smallest quadrupoles of the acceptors investigated in this study are observed for O-IDTBR and PCBM (dimer), which has the highest Langevin prefactor. Figure 3c is augmented with Langevin prefactors obtained from the literature57,58, with the quadrupole moments of the respective acceptors calculated as provided in Table S2. These results corroborate the relation between the Langevin prefactor and the quadrupole moment, suggesting that the bias potential at the donor–acceptor interface indeed suppresses bimolecular recombination. The barrier near the donor–acceptor interface thus reduces the population of electrons at the interface, which reduces the bimolecular recombination rate, being proportional to the product of the electron and hole concentration.
Note that the quadrupole moment of the acceptor is not the only parameter contributing to the bias potential and, by extension, the reduced bimolecular recombination rate. For instance, the intermixing at the donor–acceptor interface is another important factor that affects the bias potential50, rationalizing the different Langevin prefactors observed for donor–acceptor blends processed under different conditions33,38,59. However, in optimized cells, we expect the quadrupole moment of the acceptor to play an important role. In a similar fashion, the quadrupole moment of the donor also contributes to the bias potential, such that comparisons between different acceptors based on their quadrupole moments is only justified when the same or very similar donors are considered. Quadrupole moments for several donor polymers are listed in Table S3 for comparison. While the quadrupole moment may not always provide a full explanation of the observed reduced bimolecular recombination rate in all systems, it is likely an important factor, in the same fashion as it is important for charge generation9,18,53,54, as bimolecular recombination also occurs via the CT state.
Conclusions
The bimolecular recombination rate and charge transport in a series of high-performance organic solar cells based on non-fullerene acceptors was investigated. From steady-state dark injection measurements and drift–diffusion simulations of the current–voltage characteristics under illumination, Langevin reduction factors of up to over two orders of magnitude are observed. It was demonstrated that reduced bimolecular recombination can explain the high fill factors of these solar cells based on non-fullerene acceptors. To rationalize the reduced recombination rates, we conduct electrostatic-potential simulations, which demonstrate band bending near the donor–acceptor interfaces, forming a barrier for charge recombination. The formed barrier is related to the quadrupole moment of the non-fullerene acceptors, correlating with the experimentally observed Langevin reduction factors. These results demonstrate that reduced bimolecular recombination is an essential element for the observed high fill factors of organic solar cells based on non-fullerene acceptors and further contribute to understanding the large deviations from Langevin recombination, providing design rules to suppress recombination losses in organic solar cells.
Methods
Active-layer processing
All active layers were deposited by spin coating in a nitrogen-filled glovebox. For PM6:IT-4F films, the blend in its optimal donor/acceptor (D/A) ratio (1:1, w/w) was dissolved in chlorobenzene and 1% (v/v) 1,8-diiodooctane (DIO) as solvent additive. Spin coated films were annealed at 100 ℃ for 10 min. For PM6:Y6, a chloroform solution was prepared with a 1:1.2 D/A ratio. Afterwards, 0.5% (v/v) chloronaphthalene (CN) was added and the spin coated films were thermally annealed at 110℃ for 10 min. For PM6:PC61BM, a chloroform solution with a 1:1 D/A ratio with 0.5% (v/v) DIO as an additive was prepared. For PBDB-T based blends, PBDB-T:O-IDTBR was dissolved in chlorobenzene with a D/A ratio of 1:1.5 (w/w) and 0.5% (v/v) CN as additive and spin coated films were annealed at 120 ℃ for 10 min. PBDB-T:IE4F-S was dissolved in a 1:1 ratio (w/w) ratio in chlorobenzene, and the resulting film was annealed at 160 ℃ for 10 min.
Device fabrication
Hole-only, electron-only and double-carrier devices were fabricated on glass substrates with the respective device structures of Cr(1 nm)/Au(30 nm)/PEDOT:PSS(40 nm)/active layer/MoO3(10 nm)/Al(100 nm), Al(30 nm)/active layer/Ba(5 nm)/Al(100 nm) and Cr(1 nm)/Au(30 nm)/PEDOT:PSS(40 nm)/active layer/Ba(5 nm)/Al(100 nm). The glass substrates were first cleaned by detergent solution and deionized water, followed by sonication in acetone and isopropyl alcohol. For hole-only and double-carrier devices, Cr and Au were thermally evaporated as the bottom electrode. These metallic electrode were used instead of indium-tin oxide (ITO) electrodes to reduce the effect of the electrode series resistance at high current densities. A hole-injection layer of PEDOT:PSS (VP Al4083, H.C. Starck) was applied by spin coating. For electron-only devices, 30 nm of Al was thermally evaporated as a bottom electrode. In all devices top electrodes were applied by thermal evaporation. For solar cells measured under illumination, the device structure was ITO/PEDOT:PSS/active layer/PDINO/Al (100 nm).
Measurements
All electrical measurements were carried out in a nitrogen-filled glovebox. Current–voltage measurements were performed with a Keithley 2400 source meter. Layer thicknesses were measured with a Bruker Dektak XT profilometer.
Data availability
The datasets used and/or analysed during the current study available from the corresponding author on reasonable request. Log files for Gaussian simulations are available as Supporting Information.
References
Lin, Y. et al. An electron acceptor challenging fullerenes for efficient polymer solar cells. Adv. Mater. 27, 1170–1174 (2015).
Armin, A. et al. A history and perspective of non-fullerene electron acceptors for organic solar cells. Adv. Energy Mater. n/a, 2003570 (2021).
Meredith, P., Li, W. & Armin, A. Nonfullerene acceptors: A renaissance in organic photovoltaics?. Adv. Energy Mater. 10, 2001788 (2020).
Zou, Y. et al. Tuning the electron-deficient-core of non-fullerene acceptor to achieve over 17 % efficiency in single-junction organic solar cell. Energy Environ. Sci. https://doi.org/10.1039/d0ee00862a (2020).
Yao, J. et al. Cathode engineering with perylene-diimide interlayer enabling over 17% efficiency single-junction organic solar cells. Nat. Commun. 11, 1–10 (2020).
Yuan, J. et al. Single-junction organic solar cell with over 15% efficiency using fused-ring acceptor with electron-deficient core. Joule 3, 1140–1151 (2019).
Dimitrov, S. D. et al. On the energetic dependence of charge separation in low-band-gap polymer/fullerene blends. J. Am. Chem. Soc. 134, 18189–18192 (2012).
Hendriks, K. H., Wijpkema, A. S. G., van Franeker, J. J., Wienk, M. M. & Janssen, R. A. J. Dichotomous role of exciting the donor or the acceptor on charge generation in organic solar cells. J. Am. Chem. Soc. 138, 10026–10031 (2016).
Karuthedath, S. et al. Intrinsic efficiency limits in low-bandgap non-fullerene acceptor organic solar cells. Nat. Mater. 20, 378–384 (2021).
Shen, X., Han, G., Fan, D., Xie, Y. & Yi, Y. Hot charge-transfer states determine exciton dissociation in the DTDCTB/C60 complex for organic solar cells: A theoretical insight. J. Phys. Chem. C 119, 11320–11326 (2015).
Shoaee, S. et al. Charge photogeneration for a series of thiazolo-thiazole donor polymers blended with the fullerene electron acceptors PCBM and ICBA. Adv. Funct. Mater. 23, 3286–3298 (2013).
Burke, T. M., Sweetnam, S., Vandewal, K. & McGehee, M. D. Beyond Langevin recombination: How equilibrium between free carriers and charge transfer states determines the open-circuit voltage of organic solar cells. Adv. Energy Mater. 5, 1500123 (2015).
Albrecht, S. et al. On the efficiency of charge transfer state splitting in polymer: Fullerene solar cells. Adv. Mater. 26, 2533–2539 (2014).
Benduhn, J. et al. Intrinsic non-radiative voltage losses in fullerene-based organic solar cells. Nat. Energy 2, 1–6 (2017).
Vandewal, K. et al. Efficient charge generation by relaxed charge-transfer states at organic interfaces. Nat. Mater. 13, 63–68 (2014).
Nakano, K. et al. Anatomy of the energetic driving force for charge generation in organic solar cells. Nat. Commun. 10, 2520 (2019).
Schwarze, M. et al. Impact of molecular quadrupole moments on the energy levels at organic heterojunctions. Nat. Commun. 10, 1–9 (2019).
Perdigón-Toro, L. et al. Barrierless free charge generation in the high-performance PM6:Y6 bulk heterojunction non-fullerene solar cell. Adv. Mater. n/a, 1906763 (2020).
Deibel, C. & Dyakonov, V. Polymer–fullerene bulk heterojunction solar cells. Rep. Prog. Phys. 73, 096401 (2010).
Zhang, X. et al. Understanding charge transport and recombination losses in high performance polymer solar cells with non-fullerene acceptors. J. Mater. Chem. A 5, 17230–17239 (2017).
Karki, A. et al. Understanding the high performance of over 15% efficiency in single-junction bulk heterojunction organic solar cells. Adv. Mater. 31, 1903868 (2019).
Vollbrecht, J. et al. Design of narrow bandgap non-fullerene acceptors for photovoltaic applications and investigation of non-geminate recombination dynamics. J. Mater. Chem. C 8, 15175–15182 (2020).
Khan, J. I. et al. Impact of acceptor quadrupole moment on charge generation and recombination in blends of IDT-based non-fullerene acceptors with PCE10 as donor polymer. Adv. Energy Mater. n/a, 2100839 (2021).
Bartesaghi, D. et al. Competition between recombination and extraction of free charges determines the fill factor of organic solar cells. Nat. Commun. 6, 2–11 (2015).
Koster, L. J. A., Mihailetchi, V. D., Ramaker, R. & Blom, P. W. M. Light intensity dependence of open-circuit voltage of polymer:fullerene solar cells. Appl. Phys. Lett. 86, 123509 (2005).
Albrecht, U. & Bässler, H. Efficiency of charge recombination in organic light emitting diodes. Chem. Phys. 199, 207–214 (1995).
Kuik, M., Koster, L. J. A., Wetzelaer, G. A. H. & Blom, P. W. M. Trap-assisted recombination in disordered organic semiconductors. Phys. Rev. Lett. 107, 256805 (2011).
Lakhwani, G., Rao, A. & Friend, R. H. Bimolecular recombination in organic photovoltaics. Annu. Rev. Phys. Chem. 65, 557–581 (2014).
Wetzelaer, G.-J.A.H., der Kaap, N. J. V., Koster, L. J. A. & Blom, P. W. M. Quantifying bimolecular recombination in organic solar cells in steady state. Adv. Energy Mater. 3, 1130–1134 (2013).
Heiber, M. C., Baumbach, C., Dyakonov, V. & Deibel, C. Encounter-limited charge-carrier recombination in phase-separated organic semiconductor blends. Phys. Rev. Lett. 114, 136602 (2015).
Zarrabi, N. et al. Experimental evidence relating charge-transfer-state kinetics and strongly reduced bimolecular recombination in organic solar cells. J. Phys. Chem. Lett. 11, 10519–10525 (2020).
Armin, A. et al. Reduced recombination in high efficiency molecular nematic liquid crystalline: Fullerene solar cells. Adv. Energy Mater. 6, 1600939 (2016).
Shoaee, S. et al. Decoding charge recombination through charge generation in organic solar cells. Sol. RRL 3, 1900184 (2019).
Gillett, A. J. et al. The role of charge recombination to triplet excitons in organic solar cells. Nature 597, 666–671 (2021).
Hood, S. N. & Kassal, I. Entropy and disorder enable charge separation in organic solar cells. J. Phys. Chem. Lett. 7, 4495–4500 (2016).
Hosseini, S. M. et al. Putting order into PM6:Y6 solar cells to reduce the Langevin recombination in 400 nm thick junction. Sol. RRL 4, 2000498 (2020).
Zuo, G., Shoaee, S., Kemerink, M. & Neher, D. General rules for the impact of energetic disorder and mobility on nongeminate recombination in phase-separated organic solar cells. Phys. Rev. Appl. 16, 034027 (2021).
Schwarz, K. N. et al. Reduced recombination and capacitor-like charge buildup in an organic heterojunction. J. Am. Chem. Soc. 142, 2562–2571 (2020).
Cha, H. et al. Suppression of recombination losses in polymer: Nonfullerene acceptor organic solar cells due to aggregation dependence of acceptor electron affinity. Adv. Energy Mater. 9, 1901254 (2019).
Pan, M. A. et al. 16.7%-efficiency ternary blended organic photovoltaic cells with PCBM as the acceptor additive to increase the open-circuit voltage and phase purity. J. Mater. Chem. A 7, 20713–20722 (2019).
Fan, Q. et al. Synergistic effect of fluorination on both donor and acceptor materials for high performance non-fullerene polymer solar cells with 13.5% efficiency. Sci. China Chem. 61, 531–537 (2018).
Zou, Y. et al. High-performance polymer solar cells with minimal energy loss enabled by a main-chain-twisted nonfullerene acceptor. Chem. Mater. 31, 4222–4227 (2019).
Holliday, S. et al. High-efficiency and air-stable P3HT-based polymer solar cells with a new non-fullerene acceptor. Nat. Commun. 7, 1–11 (2016).
Pauling, L. Electronic processes in ionic crystals. By N. F. Mott and R. W. Gurney. J. Phys. Chem. 45, 1142–1142 (1941).
Koster, L. J. A., Smits, E. C. P., Mihailetchi, V. D. & Blom, P. W. M. Device model for the operation of polymer/fullerene bulk heterojunction solar cells. Phys. Rev. B 72, 085205 (2005).
Chen, Z.-H. et al. Quantitatively characterized crystallization effect on recombination energy loss in non-fullerene organic solar cells. J. Phys. Chem. C 123, 12676–12683 (2019).
Poelking, C. & Andrienko, D. Long-range embedding of molecular ions and excitations in a polarizable molecular environment. J. Chem. Theory Comput. 12, 4516–4523 (2016).
Poelking, C. & Andrienko, D. Design rules for organic donor-acceptor heterojunctions: Pathway for charge splitting and detrapping. J. Am. Chem. Soc. 137, 6320–6326 (2015).
Poelking, C. et al. Impact of mesoscale order on open-circuit voltage in organic solar cells. Nat. Mater. 14, 434–439 (2015).
Poelking, C. et al. Open-circuit voltage of organic solar cells: Interfacial roughness makes the difference. Commun. Phys. 5, 1–7 (2022).
Markina, A. et al. Chemical design rules for non-fullerene acceptors in organic solar cells. Adv. Energy Mater. 11, 2102363 (2021).
Clarke, T. M. & Durrant, J. R. Charge photogeneration in organic solar cells. Chem. Rev. 110, 6736–6767 (2010).
Sini, G. et al. On the molecular origin of charge separation at the donor–acceptor interface. Adv. Energy Mater. 8, 1702232 (2018).
de Sousa, L. E., Coropceanu, V., Filho, D. A. D. S. & Sini, G. On the physical origins of charge separation at donor–acceptor interfaces in organic solar cells: Energy bending versus energy disorder. Adv. Theory Simul. 3, 1900230 (2020).
Adriaenssens, G. J. & Arkhipov, V. I. Non-Langevin recombination in disordered materials with random potential distributions. Solid State Commun. 103, 541–543 (1997).
Markina, A. et al. Chemical design rules for non-fullerene acceptors in organic solar cells. Adv. Energy Mater. https://doi.org/10.1002/aenm.202102363 (2021).
Song, X. et al. Highly Crystalline Fused-Ring n-Type Small Molecule for Non-Fullerene Acceptor Based Organic Solar Cells and Field-Effect Transistors. Adv. Funct. Mater. 28, 1802895 (2018).
Khan, J. I. et al. Impact of Acceptor Quadrupole Moment on Charge Generation and Recombination in Blends of IDT-Based Non-Fullerene Acceptors with PCE10 as Donor Polymer. Adv. Energy Mater. 11, 2100839 (2021).
Wilken, S. et al. How to Reduce Charge Recombination in Organic Solar Cells: There are Still Lessons to Learn from P3HT:PCBM. Adv. Electron. Mater. 7, 2001056 (2021).
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
Y.W. and H.F. performed the measurements and contributed to the data analysis. Y.L. and B.v.d.Z. contirbuted to the data analysis. W.L. and A.M. performed computer simulations of the molecular quadrupole moments and associated potentials. H.Y. performed the synthesis of the materials. C.C., Y.L., P.W.M.B., D.A., and G.A.H.W. supervised the project. G.A.H.W. and D.A. designed the experiments, wrote the manuscript, and contributed to the data analysis. All authors reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wu, Y., Li, Y., van der Zee, B. et al. Reduced bimolecular charge recombination in efficient organic solar cells comprising non-fullerene acceptors. Sci Rep 13, 4717 (2023). https://doi.org/10.1038/s41598-023-31929-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-31929-6
This article is cited by
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.