Introduction

Recently, a rechargeable lithium-ion batteries (LIBs) have been widely used in various portable electronic devices and small mobile information technology (IT) devices. The high-capacity, energy density and power density are required for next-generation energy storage devices1,2,3,4. This is because, the application of LIBs has extended from small mobile IT devices to electric vehicles (EVs), hybrid electric vehicles (HEVs), and plug-in HEVs5.

LiCoO2 (LCO), the most common cathode material for LIBs, has been widely used because of its high coefficient of lithium ion diffusion, easy fabrication processing and high voltage6,7. However, LCO has major limitations such as low capacity, high cost, toxicity, poor rate capability and environmental pollution8,9. Especially, high energy and power density are essential towards in application of large-scaled devices such as EVs and HEVs. Therefore, many researchers have been focused on searching new cathode materials, which can have high power and energy density10,11,12,13. Among various candidates, LiNiO2 (LNO) cathode materials are being studied as an alternative to solve these problems such as high price and low capacitance of LCO. However, LNO, having low structural stability, is deformed from ‘layered structure’ to ‘spinel structure’ as the cycle progresses, finally resulting in slow lithium ion kinetics14,15.

To address these concerns, the LiNi1−y−zCoyAlzO2 (NCA) has been developed as a breakthrough16. It has also been reported that increasing the Al content provides higher capacity with stable performances7,17,18,19,20. The structural stability and the electrochemical performance of LNO can be improved by Co and Al substitutions for Ni site. Owing to smaller size of Co3+ (0.685 Å) and Al3+ (0.530 Å) than Ni3+ (0.740 Å), the substitution of Co and Al ions can lead to shrinkage of the a-axis, resulting in better stabilization of the layered structures which presents both high specific energy and power density.

Therefore, in this study, we synthesized NCA cathode material with various sintering temperatures (660–810 °C) to optimize the electrochemical performances. This is because crystallinity and structural stability, affected by sintering temperature, play an important role in the electrochemical performances of NCA12,21,22,23. Therefore, we investigated the effect of sintering temperature on structural stability and electrochemical performance of NCA.

Experiment

For synthesis of NCA cathode material, Ni0.93Co0.04(OH)2 precursor (Fig. S1) was fabricated via a co-precipitation process. Ni0.93Co0.04(OH)2 precursor was mixed with, LiOH·H2O (Sigma-Aldrich) and Al(OH)3 (Sigma-Aldrich) as followed molar ratio (Li:Me:Al = 1.05:0.97:0.03). The mixture was calcined at 450 °C for 5 h and then calcined at different sintering temperature (660 °C/690 °C/720 °C/750 °C/780 °C/810 °C) for 15 h under an oxygen atmosphere.

For fabrication of cathode electrodes, NCA active materials, carbon black (Super P) and Polyvinylidene difluoride (PVDF) were mixed in the weight ratio of 96:2:2. N-methyl-2-pyrrolidone (NMP) solvent was then added to form slurry. The obtained slurry was casted on Al foil via bar coating process and then dried at 100 ℃ in vacuum oven for 10 h to remove the residual N-methyl-2-pyrrolidone solvent.

The 2032 coin cells were assembled with Li metal disc as anode in a glove box filled with argon gas, 1 M LiPF6 in ethylene carbonate, dimethyl carbonate and ethyl methyl carbonate (EC:DMC:EMC 1:1:1 v/v/v) as electrolyte and polyethylene was used as separator11.

Surface morphologies of the NCA particles were observed by FESEM (Field Emission Scanning Electron Microscopy, Hitachi S-4800, resolution limit 1 nm) at 1 K, 5 K and 15 K magnifications. The Ni, Co and Al element ratios were determined by using an EDS (Energy dispersive X-ray). Crystalline structure of the NCA powders was examined by XRD (X-ray diffraction, Philips, X-pert PRO MPD) analysis. The electrochemical performances were characterized via an electrochemical device (TOSCAT-3100, Toyo system).

Results and discussion

Figure 1 shows the (a) XRD patterns and magnified views of the (b) (003) peaks, (c) (104) peaks, (d) (006)/(102) peaks and (e) (108)/(110) peaks. All peaks correspond to the NCA with the α-NaFeO2 layered structure, belonging to hexagonal system (space group R-3 m). In addition, it was confirmed that there are no additional peaks, indicating a secondary phase, are not observed24,25. Rietveld refinement is measured to confirm the lattice parameters and I(003)/I(104) ratio, as shown in Fig. 2. All samples with an I(003)I(104) ratio greater than 1.2, has low cation disordering. In addition, the obvious splitting of I(006)/I(102) and I(108)/I(110) demonstrates that all samples except 660 °C are well-formed orderly layered structure. As shown in Table 1, the intensity ratio of I(003)/I(104) increased as the temperature increasing from 660 to 720 °C. However, it can be confirmed that the intensity ratio of the I(003)/I(104) is adversely decreased at the higher sintering temperature above 720 °C. It can be concluded that excessive sintering temperature deteriorates the structural stability of NCA.

Figure 1
figure 1

(a) XRD patterns and magnified views of the (b) (003) peaks, (c) (104) peaks, (d) (006)/(102) peaks and (e) (108)/(110) peaks.

Figure 2
figure 2

Reitveld refinement results of NCA sintered at (a) 660 °C, (b) 690 °C, (c) 720 °C, (d) 750 °C, (e) 780 °C and (f) 810 °C.

Table 1 Structural parameters of NCA with various sintering temperatures.

FE-SEM images of NCA sintered at different sintering temperatures [(a) 660 °C, (b) 690 °C, (c) 720 °C, (d) 750 °C, (e) 780 °C and (f) 810 °C] are shown in Fig. 3. From SEM images, all the samples show a spherical morphology with an average particle size of 10 ~ 20 um, which is composed of numerous primary particles (400 ~ 800 nm). Notably, the average size of primary particles increases as the sintering temperature increased from 660 to 810 °C. The average size of primary particle sintered at 660 °C is about 450 nm, much smaller than that of NCA (800 nm) sintered at 810 °C. Also, the clear Ni, Co, and Al peaks were observed in EDS mapping without any impurity peaks, as shown in Fig. 3g. It indicates that desired composition of NCA has been successfully synthesized.

Figure 3
figure 3

FE-SEM images of NCA sintered at (a) 660 °C, (b) 690 °C, (c) 720 °C, (d) 750 °C, (e) 780 °C and (f) 810 °C (g) EDS mapping of NCA sintered at 720 °C.

Figure 4a shows the initial charge–discharge curves of NCA with different sintering temperatures at current density of 0.5 A/g in the voltage range of 3.0–4.3 V. The voltage plateau around 4.2 V is due to the high Ni ion concentration in the NCA26. We can confirm that the capacity of all samples except 660 ℃ and 810 °C is not significantly different. Therefore, the sintering temperature does not significantly affect the initial charge–discharge capacities in the range from 690 to 780 °C. The sample sintered at 720 °C shows the highest discharge capacity of 217.48 mAh g−1 with excellent Coulombic efficiency of 87.84%. This is due to the low cation mixing and well-crystallized layered structure, as mentioned earlier (Fig. 1). Figure 4b presents the rate performance of NCA with different C-rates (0.1, 0.5, 1.0 and 2.0 C) in voltage range of 3.0–4.3 V. All the rate performances were measured at a fixed charge current density of 0.5 C while the discharge current density was measured at different current densities. The cell was cycled at each rate and then back to 0.5 C. The rate capabilities of all samples are decreased with increasing C-rate. However, it can be seen that the difference between the capacity values of samples increases, as the C-rate increases. Compared to the other cases, the NCA sintered at 720 °C maintains the highest capacities regardless of C-rates. More importantly, the NCA sintered at 720 °C still has the highest capacity of 195.3 mA h g−1 when the C-rate is decreased back to 0.5 C, indicating superior reversibility. This is because well-defined layered structure via optimized sintering temperature allows electrochemically active {010} planes of lithium ions and electron conduction despite the fast charge/discharge rate, resulting from high cation ordering and highly crystallized layered structure.

Figure 4
figure 4

(a) Initial charge–discharge curves and (b) rate performances of NCA.

Figure 5 shows the cycle performances of NCA samples at 0.5 C in the voltage range 3.0–4.3 V. No obvious capacity fading is observed for all samples before 45 cycles. However, there is a difference in the rate of decrease for each sample after 45 cycles. Among the samples at different sintering temperatures, the NCA sintered at 720 °C possesses the highest capacity with capacity retention of 95.4% after 80 cycles. It can be explained by not only the rapid/durable electrochemical kinetics but also interfacial stability between electrode/electrolyte. On the other hand, the NCA sintered at 660 °C and 810 °C shows inferior cyclabilities compared to others. The samples sintered at 660 °C and 810 °C show a sharp decrease in capacity upon cycling. This is due to inferior crystallization (660 °C), disordered layered structure (660 °C and 810 °C), and longer Li ion-transfer channels (810 °C). Such drawbacks cause sudden drop in capacity during cycling since they could destroy the structural integrity of NCA, resulting in reduced reactivity of active material. It was reported that the hydrogen fluoride (HF), originated from reaction of water and LiPF6, is one of the most important factor for performance degradation. This is because HF elutes the transition metal ions in NCA, leading to deformation of layered structure. The optimum sintering temperature can suppress the negative effects on the NCA via boosting structural stability.

Figure 5
figure 5

Cycling performances of NCA.

To better understand the electrochemical performances, EIS tests of NCA sintered at 660 °C and 720 °C are performed. Nyquist plots for the both samples after 1st and 80th cycles are shown in Fig. 6a and b. It is well known that Nyquist plots is composed of three components: electrolyte resistance (Rs) in the high frequency, the charge transfer resistance (Rct) in medium frequency and the Warburg impedance in the low frequency26,27,28. Among three components, the Rct can be regarded as a key parameter for the cathode impedance, affecting the electrochemical behavior. The Rs values of both samples are almost same since they use the same electrolyte. However, there is significantly difference in Rct values between 1 and 80 cycles for both samples. Among them, the increase in Rct value of NCA sintered at 660 °C (174.4 Ω to 295.9 Ω) is much larger compared to that of NCA sintered at 720 °C, as shown in Table 2. It can be inferred that highly crystallized layered NCA offers enlarged exposed active planes for Li ions. The Rct value of NCA sintered at 720 °C shows about two-thirds than NCA sintered at 660 °C, resulting from enhanced charge-carrier transport at the NCA surface. Therefore, it can be concluded that optimized sintering temperature is beneficial to suppress the capacity fading during cycling based on structural stability of NCA.

Figure 6
figure 6

Nyquist plots of NCA sintered at (a) 660 °C and (b) 720 °C.

Table 2 Rsf and Rct values of NCA sintered at 660 °C and 720 °C.

Figure 7 shows the HCl titration curves of NCA with different sintered samples. The residual lithium compounds (Li2CO3 and LiOH) is derived from (i) moisture absorption and (ii) spontaneous reduction of Ni3+ into Ni2+, accompanied by oxygen release. The amount of HCl used in the HCl titration up to pH 4 of NCA sintered at 660 °C is higher compared to that of 720 °C, as shown in Table 3. The amount of Li2CO3 and LiOH can be calculated via following equations29,30:

$${\text{LiOH }} + {\text{ HCl }} \to {\text{ LiCl }} + {\text{ H}}_{{2}} {\text{O}}$$
(1)
$${\text{Li}}_{{2}} {\text{CO}}_{{3}} + {\text{ HCl }} \to {\text{ 2LiCl }} + {\text{ H}}_{{2}} {\text{O }} + {\text{ CO}}_{{2}}$$
(2)
Figure 7
figure 7

HCI-titration curves NCA with various sintering temperatures.

Table 3 Titration results of residual LiOH and Li2CO3 of NCA with various sintering temperatures.

The Li2CO3 is produced on the surface of LiOH by reaction with CO2, and then moisture remains, as follows:

$${\text{2LiOH }} + {\text{ CO}}_{{2}} \to {\text{ Li}}_{{2}} {\text{CO}}_{{3}} + {\text{ H}}_{{2}} {\text{O}}$$
(3)

Also, the CO2 and POF3 gases are generated by reaction with Li2CO3 and LiPF6. It can be represented by the following equation:

$${\text{LiPF}}_{{6}} + {\text{ Li}}_{{2}} {\text{CO}}_{{3}} \to {\text{ POF}}_{{3}} + {\text{ CO}}_{{2}} + {\text{ 3LiF}}$$
(4)

A portion of lithium is originated from the interior of NCA with the enhanced cation disordering. Therefore, the amount of residual lithium on the surface for sample sintered at 720 °C is small due to optimum sintering temperature31. It indicates that appropriate sintering temperature can effectively suppress the gassing and performance decay due to smooth surface chemistry without unwanted materials.

Conclusion

In this study, we successfully synthesized the Ni-rich LiNi0.93Co0.04Al0.03O2 cathode materials with low Li+/Ni2+ disorder and high crystallinity under various sintering temperature conditions (660–810 °C). The effect of sintering temperature on the structural properties and electrochemical performances of NCA were investigated. The results indicate that the electrochemical performances of NCA are effected by sintering temperature. Among various sintering temperatures, NCA sintered at 720 °C shows the highest electrochemical performances based on excellent structural stability. It can be elucidated that NCA sintered at 720 °C has a good layered structure with high cation ordering thereby allowing fast and smooth Li ion and electron diffusion. Therefore, we can conclude that NCA sintered at 720 °C could be used as a promising cathode material for next-generation high-energy LIBs.