Synthesis, physico-mechanical and microstructural characterization of Al6063/SiC/PKSA hybrid reinforced composites

The utilization of agro-residues ash as complementary reinforcing materials continues to gain prominence for metal matrix composite (MMCs) development. A rarely investigated but largely available ash among these agro-residues is the palm kernel shell ash (PKSA). Thus, the present study investigates the influence of PKSA particulates hybridized with SiC on the physico-mechanical properties and microstructure of Al6063 metal composites. The composites are synthesized using the double stir-casting technique with SiC held constant at 2 wt.%, while the PKSA contents are varied from 0 to 8 wt.%. The phases present and morphology of the composites are investigated using X-ray diffractometer (XRD) and scanning electron microscopy (SEM), respectively. The density, porosity, hardness, tensile and fracture toughness tests are carried out on the hybrid composites. X-ray diffractometer revealed that for Al 6063, only Al cubic crystal system was identifiable within the matrix. However, for the reinforced composites, major phases identified are Al, Fe3Si, SiC, MgO, and SiO2. The SEM images show that the particulates reinforcements (SiC and PKSA) were uniformly dispersed in the matrix. The percentage porosity for the composites ranged from 2.06 to 2.39%. In addition, hardness, yield strength and ultimate tensile strength of the composites are about 10.3%, 18.5% and 10.4%, respectively better than for Al 6063. However, the percent elongation and fracture toughness are lower for the hybrid composites than for Al 6063 and SiC reinforced composite with values decreasing with increase in ash content. Hence, the MMCs produced will be applicable for light-weight engineering applications.

The development of new materials for industrial technology with various applications is growing fast [1][2][3] . The search for new materials has been attributed to the limitations of conventional metals and alloys for the attainment of good strength combination, resistance to wear, toughness, high temperature performance, as well as resistance to corrosion 2,4-6 . Aluminium matrix composites (AMCs) are new materials that has become a major attraction to researchers for some decades. AMCs have been widely utilized in the automobile, aerospace, sport, manufacturing industries and many more 1,[7][8][9][10] . However, there has been continuous efforts to improve the existing AMCs as well as developing novel types for various applications.
The utilization of single or hybrid ceramic reinforcements in AMCS has been the focus of some studies 6,11,12 . For the suitability of usage of AMC produced using Al matrix and SiC as reinforcement, Poornesh et al. 12 studied the mechanical properties of AMCs produced through stir casting technique using Al-18wt%Si as matrix and SiC as reinforcement. The hardness and tensile strength of the AMC produced were better compared to the unreinforced Al-alloy, though it was the opposite for the toughness of the samples. Hybrid ceramic reinforcements (SiC and B 4 C) and AA6082-T6 alloy were used for the development of AMCs by Singh & Goyal 6 . Conventional stir casting method was used with varying weight percentages of reinforcement between 5 and 20 wt.% for the production. It was reported that increase in the reinforcement led to an increase in the hardness and tensile strength with decreasing percentage elongation. The mechanical properties of the hybrid AMCs in the study was better compared with the unreinforced alloy. Rajesh and Kaleemulla 10 also investigated the mechanical behaviour of AMCs produced using Al7075 alloy reinforced with SiC and Al 2 O 3 via stir casting method. The mechanical properties of the reinforced Al7075 were better compared to the unreinforced alloy.
Due to the high cost of synthetic ceramic reinforcements, researchers continue to study alternative materials (agro-residues and industrial wastes) which could serve as partial replacement for ceramic reinforcement in AMCs in recent years 3,[14][15][16] . Hence, attention to low cost reinforcing material is growing rapidly. Dinaharan et al. 16 used rice husk ash (RHA) as the reinforcing materials in AA6061 aluminium matrix for the production of AMC via friction stir processing. The reinforced alloy showed homogenous distribution of RHA particles. The tensile strength of the AMC improved while the fractured surface examined confirmed an excellent interfacial bonding of the RHA particles with the Al matrix. The mechanical and fracture properties as well as microstructure of hybrid AMC reinforced with SiC and groundnut shell ash (GSA) was investigated by Alaneme et al. 14 . The AMCs was produced using two-step stir casting technique. The reinforcement particulates were uniformly distributed in the AMC through the microstructure assessment and the mechanical properties improved.
Several other agro-residues that have been used include bean pod ash 7 (Aigbodion, 2019), corn cob ash 17 , bagasse ash 15 and palm kernel shell 18 . Palm kernel shell (PKS) and palm kernel shell ash (PKSA) is also an agrowaste and their usage as reinforcement particulates in AMCs production are limited in literature. PKS and PKSA have been used extensively in reinforcement in concrete [19][20][21] , biomass briquette and particleboard 22,23 , geopolymer composite 24 , and activated carbon for supercapacitor electrode 25 . PKS is an agro-residue that is abundant in several countries such as Nigeria, Brazil and Malaysia [26][27][28] . PKSA is obtained from the complete burning of PKS into ash 26 . To reduce environmental pollution, PKS and PKSA could be used as partial reinforcement in the production of metal matrix composites. During the synthesis of a novel surface AMC composite, PKSA reinforcement was included in aluminium substrate surface via the friction stir processing route 13 . More so, a new stir casting method (double layer feeding) was employed in the synthesis of AMCs. The AMCs was developed using 1-4 wt.% PKSA nanoparticles (PKSAnp) in A356 alloy matrix. Uniform distribution of the PKSAnp in the matrix was seen from the morphological analysis, while the mechanical properties of the developed AMCs improved compared to the unreinforced alloy 8 . The influence of PKSA on the mechanical properties of recycled Al alloy obtained from automobile engine block cylinder was investigated by Oladele & Okoro 29 . The results revealed that the PKSA is suitable for usage in some automobile parts production. The study of Edoziuno et al. 18 evaluated the physical and chemical properties as well as the microstructural characteristics of AMCs produced using novel PKS particulates. The weight percentage range of the PKS was between 2.5 and 15 wt.%. Stir casting technology was employed in the production of the AMCs. The results showed improved physical properties and homogenous distribution of the PKS in the matrix.
However, little or no work has been done on the influence of hybrid reinforcement particulates of PKSA and SiC on the physical and mechanical properties of AMCs. For any developed material to be useful for engineering purposes, the developed composite material should be subjected to various tests to ascertain its properties for real-life applications. Hence, the rationale behind this study is to investigate the influence of hybrid reinforcements of PKSA and SiC on the properties of Al6063 matrix alloy for engineering purposes. Therefore, this study synthesized the AMC using Al-6063 matrix and hybrid reinforcements of SiC and PKSA. This research examines the influence of PKSA produced at 900 • C as reinforcement in AMCs. More so, the effects of the particulate composition variation by weight fraction of PKSA and SiC on the physico-mechanical properties as well as on the microstructure of the AMCs produced were investigated. The findings from this study would add to the existing database of cost-effective hybrid reinforcement in aluminium matrix composites.

Materials and method
Matrix alloy and reinforcement materials. This study utilized Al6063 as the matrix material. Table 1 displays the elemental compositions of the Al6063 matrix material. To obtain one of the reinforcement materials, PKS was purchased from a local market in Osogbo, Osun State, Nigeria. PKSA and SiC were the reinforcing materials used in the formation of the hybrid AMC. The PKSA was obtained through complete combustion of PKS in a muffle furnace at 900 °C. PKSA obtained from the burning of PKS was sieved to an average size of < 40 µm , while the average size of the SiC particulate was about 30 µm . Table 1 also displays the chemical oxides present in the produced PKSA.
Production of composites. The technology employed in the production of the composites is the liquid metallurgy route using the two-step stir casting method 14 . The flowchart of the processes involved in this study is shown in Fig. 1. The amount of PKSA and SiC required for the preparation of the 2, 4, 6, 8, and 10 wt.% reinforcements in the matrix was determined through charge calculation consisting of PKSA to SiC ratios (0:0, 0:2, 2:2, 4:2, 6:2, 8:2). To remove moisture inherent in the reinforcements' particulates and for improved wettability with the Al6063 matrix, they were firstly preheated at 250 °C. The Al6063 matrix ingots were charged into a gas-fired crucible furnace and heated to 750 ± 30 • C (above the alloy's liquidus temperature) to guarantee the whole matrix alloy melting. The obtained molten matrix alloy was permitted to cool (semi-solid state) in the www.nature.com/scientificreports/ furnace before charging the preheated reinforcement particulates into it. Thereafter, there was manual stirring of the slurry for 5-10 min before the slurry was superheated to 800 ± 50 • C . A mechanical stirrer was utilized for the second stirring of the slurry at a speed of 400 rpm for 10 min. Finally, the melt was poured into sand mould prepared until it solidifies (Fig. 2a,b). The designation of the samples produced is shown in Table 2.
XRD and microstructural characterization. The X-ray diffractometer utilized to obtain the phases present in the produced composites was PANalytical Empyrean diffractometer, with Cu K α radiation = 1.5406 Å , acceleration voltage of 45 kV, and 40 mA current. The scan range (2θ) was between 5 and 90° with 0.026°/min scan speed. The mineral phases were picked using X'Pert Highscore Plus software attached with the diffractometer. A Vega 3 Tescan model SEM with EDS attachment was employed for the microstructural examination of the produced composites. The test specimens were obtained from the cylindrical rods through machine-cut from rods. The samples were metallographically grinded and polished with emery paper of different grits and polishing clothes, then etched with Keller's reagent. The polished and etched samples were loaded into the SEM machine. The magnification was set (majorly 500 micron) and beam intensity of 14 was used. The Vega software was then used to capture the image from the SEM. The image was scanned unto EDS using Aztec software. The fractured surface morphology of the composites was visualized using the SEM-EDS equipment.   www.nature.com/scientificreports/ Physical properties tests. Density determination. The principle of Archimedes was used to measure the density of the base metal and the reinforced samples as described by Prasad et al 30 . Each sample was weighed in air (m) and distilled water (m 1 ). The mass and other parameters were then used to obtain the density ( ρ c ) of the composite based on Eq. (1).
where ρ c , m , m 1 , and ρ w is composite density (kg/m 3 ), mass of sample (in air), mass of sample composite in distilled water (kg), and distilled water density (1000 kg/m 3 ), respectively.
Porosity determination. The method presented by Prasad et al. 30 was adopted to estimate the porosity of the composite using Eqs.
where ρ th and ρ m are the theoretical and measured densities (in kg/m 3 ), respectively. Equation (3) is the mathematical relationship of the theoretical density for the hybrid composites. The volume fractions for both reinforcements as well as the matrix were included and calculated using Eq. (3): where ρ Al , ρ PKSA , ρ SiC are densities of aluminum matrix, PKSA and SiC, respectively while V Al , V PKSA , V SiC are volume fractions of aluminum matrix, PKSA and SiC, respectively.

Mechanical Tests. Hardness test.
The hardness test was carried on the samples out based on the ASTM E10-18 standard 31 . Brinell hardness machine was used in the determination of the hardness value. On each specimen, four indents were done and readings were obtained for reliability of the data. The average hardness value was computed for each of the specimen.
Tensile test. Prior to performing the tensile test, the as-cast composite cylindrical samples were prepared to dimension, 5 mm diameter and 30 mm gauge length using the lathe machine (Fig. 2c). The tensile experiment was done on a Universal testing machine (Model no: Instron 3369). A strain rate of 10 -3 /s was utilized to monotonically pull each clamped specimen until failure/fracture based on ASTM E8/E8M-16ae1 standard 32 . For data reliability, the test was carried out in triplicates for each composite designation. Yield strength (YS), ultimate tensile strength (UTS), and percentage elongation were the properties obtained through the test.
Fracture toughness. For the evaluation of the fracture toughness of the produced AMCs, circumferential notch tensile (CNT) samples were prepared in tandem with the method of Alaneme et al 33 . The samples were machined to dimension: 30 mm gauge length, 4 mm gauge diameter, 3.1 mm notch diameter, and 60° notch angle. Each specimen was subjected to a tensile loading strain rate of 10 -3 /s until fracture with the aid of an Instron 3369 universal testing machine. The fracture toughness was evaluated using Eq. (4) by Dieter 34 . Equation 5 was then used to validate the fracture toughness values 35 .
where P f is the fracture load (kN), D is the gauge diameter (mm), and d is the notch diameter (mm). The condition of 1.2 ≤ D d ≤ 2.1 was reported to be valid. The test was done in triplicates to ensure repeatability and reproducibility of the generated results.

Results and discussion
X-ray diffraction of the hybrid composites. The various phases present in Al6063 and as formed composites were obtained and the XRD spectrum are presented in Figs. 3 and 4, respectively. In Fig. 3, only aluminium with a cubic crystal system can be identified with a = b = c = 4.0500A and ∝= β = γ = 90 • with calculated density of 2.70 g/cm 3 . However, in the composite as displayed in Fig. 3, peaks depicting various phases present are identified as Al, Fe 3 Si (an intermetallic cubic crystal system), MgO, SiO 2 , and SiC. The presence of SiC, SiO 2 , and Fe 3 Si in the composites is strongly related to the presence of silica and Fe 2 O 3 in the PKSA ( Table 1). The formation of Fe 3 Si intermetallic phase emanated from the interaction and reaction of silica and Fe 2 O 3 . These same oxides were earlier identified in the characterized PKSA and described as hard particulates, which strengthen metallic materials 26 . In the same light, the diffractograms of AMCs produced with breadfruit seed hull particulates showed the presence of Fe 3 Si, Al 6 Fe, and ∝-Al indicating the presence of the reinforcement particulates in the composites 36 . The interaction of silica and MgO resulted in the formation of Mg 2 SiO 4 as described in the study of Aigbodion & Ezema 8 . However, further report by Aigbodion & Ezema 8 , indicated that Al 4 C 3 (a brittle reaction product) was not formed. This was not also seen in the composites produced in this Microstructural characterization of the composites. The microstructure of the unreinforced alloy reveals structures without voids as shown in Fig. 5(a). Figures 6(a) and 7(a) show the representative microstructure of the monolithic reinforced and hybrid reinforced composites, respectively. The reinforcements (SiC and PKSA) present were uniformly dispersed in the matrix. There was no indication of crack formation and enlarged pores in the castings. This may be due to the appropriate process parameters utilized for synthesizing of the composite. This indicates better wetting condition between the matrix and the reinforcements. This assertion is corroborated by the use of Al/Zn matrix alloy with hybrid reinforcement of fly ash and SiC 37 ; Al-Mg-Si matrix alloy with hybrid reinforcements of alumina, RHA, and graphite 38 ; and Al-Cu-Mg matrix alloy with bean pod ash as reinforcement 7 and many others; maintained no crack formation due to proper process parameters employed. Figures 6(a) and 7(a) further buttress the observations made in the low values of porosity in the as-formed composites. The evenly dispersed particulates observed in the SEM images further confirm that the double stir casting was reliable route in breaking the surface tension between the matrix alloy and the reinforcement particulates 39,40 . The double stir casting process also helped in reducing porosity by allowing air bubbles trapped in the slurry to escape during processing. The elemental mappings from the EDS profile for both the unreinforced (Fig. 5b) Table 3. Figure 8 shows the density and percentage porosity of the produced AMCs. The Al-matrix had a density of 2.6443 g/cm 3 , which was 5.4% higher than the composite in sample A5 with PKSA and SiC ratio (8:2) having a density of 2.5014 g/cm 3 . It was observed that as the PKSA particulates increased in the AMCs, the density of the AMCs reduced. However, sample A1 showed an increment in the density when compared to the unreinforced alloy and the reinforced alloy with the inclusion of PKSA and SiC. This could be attributed to the density of SiC that is higher than for the base alloy. The lower and reducing densities of other reinforced samples (A2-A5) may be attributed to the inclusion of the PKSA particulates. Thus, PKSA particulates lower the density of the composites. In a similar study by Prasad et al 30 , there was decrease in density when RHA and SiC were used as hybrid reinforcements. The drop in density was attributed to the inclusion of low density RHA particulates. Edoziuno et al. 18 also reported similar observation when novel PKS reinforcement was solely used in the production of AMCs. The low density of the PKS resulted in low density AMCs. However, the usage of higher density reinforcement particulates in matrix alloy is said to improve the density of composite alloy 39,41 . Kumar et al. 41 utilized Si 3 N 4 as reinforcement in Al6063 alloy in the production of metal composites and observed that the higher the contents of the reinforcement, the higher the density, which ultimately enhanced the hardness of the produced composites. The percentage porosities of the produced AMCs were observed to be less than 2.5%, which were within the acceptable limits for cast MMCs. Alaneme & Sanusi 38 reported the maximum permissible percentage porosity to be less than 4% in cast MMCs. Hence, this further affirmed that double stir casting technique is reliable and efficient in breaking the surface tension between the Al matrix and the reinforcement particles. In addition, the double stir casting process helped in reducing porosity by allowing air bubbles entrapped in the slurry to escape during processing 39,40 . Based on the physical properties obtained, light-weight composites can be produced from the use of PKSA particles as reinforcement in MMCs.
Influence of PKSA on the mechanical properties of the composite. Hardness. The material strength, toughness, and resistance to wear could be influenced by the hardness value of the material. Figure 9 showed the hardness values of the produced AMCs. From Fig. 9, it can be observed that the hardness value of Al6063 alloy was enhanced as the percentage weight of the PKSA increased with a constant SiC value of 2 wt.%. The presence of the hard phases of silica and other strengtheners in the PKSA could be said to be the reason for the increase in hardness. According to Reddy et al 42 , the improvement of hardness of MMCs have been attributed to the incorporation of reinforcement particulates into the base alloy. Same observation was accredited   Table 1). The presence of the Fe 3 Si intermetallic could also improve the hardness of the composites. This could also be attributed to the increment in reinforcements surface area and matrix grain size reduction as a result of reinforcement particulate addition 43 . The increase in hardness could be attributed to the increase in the volume of precipitated phases or a high dislocation density. More plastic deformation resistances are obtained by the inclusion of these particulates leading to rise in hardness value. From this study, a 10.31% increment in hardness value was obtained for sample A5. This implied that the introduction of PKSA as substitute to SiC does not adversely affect the resistance to indentation of the composite. This is in agreement with the study of Alaneme et al 44 . The hardness value obtained in this study was better compared with that obtained in the study of Aigbodion & Ezema 8 . This is because of the presence of SiC particulate incorporated as the second reinforcement in this study. The hardness increased with decrease in the average size of aluminium composites when bamboo leaf ash was incorporated into Al-4.5Cu matrix in the study of Kumar and Birru 45 . This observation was seen in the study of Bannaravuri and Birru 46 , where the hardness increased as the reinforcement contents increased. The findings in this present study makes the MMCs produced suitable to be used in light-weight applications where mild hardness is required such as in architectural works, and window and door frames.
Yield and ultimate tensile strengths. The YS and UTS of the hybrid-reinforced composites derived from the stress-strain curves generated by the universal testing machine, are shown in Fig. 10. It can be observed that the YS and UTS of sample A1 are higher than that of the un-reinforced sample (Sample A0). Sample A1 is a sample with 2 wt.% SiC inclusion into the base alloy. Improvement in the values of the YS and UTS may be ascribed to the hard nature and strength of the SiC particulates present. The influence of the PKSA particulates addition between 2 and 8 wt.% with the constant 2 wt.% SiC showed increment in the YS and UTS for the samples A2 -A5. The more the PKSA content, the better the strengths of the synthesized composites. These may be assigned to the presence of the hard nature of the brittle PKSA particulates as well as the presence of the SiC particulates, which were agglomerated into the Al6063 alloy. The hard nature of PKSA particulates could be as a result of the existence of hardening and strengthening oxides such as SiO 2 , Al 2 O 3 , Fe 2 O 3 , MgO, and so on 26 . Hence, the rise in tensile strength is proportional to the rise in hardness value. This observation is in accordance with the study of several researchers 37,39,41,42 . Based on this study, the rise in the yield strength and ultimate tensile strength of the composites could be linked to three mechanisms. These include the grain boundary strengthening known as the Hall-Petch effect, the coefficient of thermal expansion (CTE) as well as the Orowan strengthening mechanisms 47 . According to Atuanya et al 36 , various factors significantly affect the mechanical properties of metallic materials. These factors include grain boundaries, solid solutions, sub-structures, second phases, and many more. However, the information from the morphology of the composites developed reveal that the grain refinement of the reinforcement and the matrix are the core contributors to the tensile strength improvement. The grain boundaries serve as obstacles to the dislocation movement. Around the dislocation density, there is rise in grain boundaries which could result in increasing the strength of the composite 47 . The particulates of the PKSA reinforcement play significant function on the load transfer in the strengthening of the composites developed. There is an atomical bonding interface between the matrix and the PKSA reinforcement to produce grain-boundaries. The increase in the tensile strength of the developed composites as PKSA content increases www.nature.com/scientificreports/ may be attributed to the grain refinement of the aluminium matrix alloy. More loads are transferred when the volume fractions of the reinforcements are increased in the matrix alloy; resulting in higher strength. This is in agreement with the study of Atuanya et al. 36 . The more the PKSA particulates in the matrix, the smaller is the grain of the Al matrix 8,36 . More so, when there is a thermal matrix-reinforcement interface mismatch owing to the disparity between the thermal expansion coefficients of the matrix and the reinforcement, the composite material is strengthened. The particulates are hard and brittle, while the matrix is soft and ductile; however, the thermal mismatch of the CTE could result into elastic and plastic incompatibility between the matrix and the reinforcement 36 . The mismatch occurs during the cooling or solidification process of the composite production; hence, producing plastic deformation in the interface of the matrix 8,15 . In addition, the grain size of the matrix is bigger with a low volume fraction of particulates, which may lead to the Orowan bypass mechanism in operation within the large grains of the matrix. The higher reinforcing particulate fraction in the matrix, the grains get reduced to induce grain refinement 36 . This could also lead to higher yield and tensile strength values through load bearing transferred directly to the interface. With the addition of bamboo leaf ash and breadfruit seed hull ash into Al matrix, increase in YS and UTS were observed, respectively 36,46 .
Percentage elongation. The percentage elongation (strain to fracture) of the produced composites is presented in Fig. 11. The % elongation of the samples produced were observed to be between 5.8 and 7.6%. In addition, reduction in % elongation can be observed as the PKSA particulates in the hybrid reinforcement increased. The reduction in %elongation may be attributed to the reduction in the plastic strain sustenance ability of the composites due to the presence of hard constituents in the PKSA (Table 1) and SiC particulates. This could cause a reduction in the ductile phase of the matrix leading to decline in percentage of elongation. It can also be www.nature.com/scientificreports/ observed that there is a consistent reduction in the strain to fracture value, which may be ascribed to the flowability resistance of the matrix alloy with the inclusion of reinforcement particles as well as the reduction of the ductile nature of the aluminium matrix content 6 . The PKSA inclusion has slight detrimental effect on the ductility of the AMCs produced. Good ductility was observed when 1 wt.% corn cob ash (CCA) was utilized along with SiC in the development of AMCs when compared with unreinforced matrix 17 . However, as the CCA content increased, the ductility of the composites declined. Furthermore, there was decrease in ductility as the reinforcement (Si 3 N 4 ) particulates increased in the study of Kumar et al. 41 . The inclusion of PKSA as reinforcement in the development of AMCs caused an inverse response in the hardness value and the percentage elongation. As the PKSA content increased, the hardness value increased while the % elongation reduced. The elastic property and the ability of the drawn of the matrix alloy reduces with the reinforcement content (PKSA and SiC) increase because PKSA and SiC particulates are brittle in nature. The results in this study is similar to the work of Atuanya et al. 36 , in which the increment in breadfruit seed hull ash slightly lower the percentage elongation. This is a consistent trend in the study. However, an inconsistent trend of %elongation was seen when hybrid reinforcements of groundnut shell ash and SiC was used to develop MMCs. Some of the samples show slightly improved ductility, while others revealed otherwise 14 . Similar pattern of reduction in the %elongation was reported for alumina and quarry dust 44 , bamboo leaf ash 46 and breadfruit seed hull ash 36 when used as hybrid reinforcements in Al matrix. The reduction in the percentage elongation may be due to the increase in hardness and strength of the composite. The results obtained in this study is in tandem with these studies and are thus recommended for light weighted application.
Fracture toughness. Fracture toughness is the ability of composite material to resist crack propagation.
The fracture toughness values of the samples produced are shown in Fig. 12. The range of the fracture toughness values can be observed to be between 8.55 and 12.49 MPa m 1/2 , which declined as the PKSA content in the hybrid reinforcement increased. Alaneme et al. 39 reported similar observation, where fracture toughness reduced with increase in alumina particulate inclusion. In this study, the unreinforced matrix gave the highest fracture toughness of 12.49 MPa m 1/2 . The lower fracture toughness of the composites may be due to the presence of brittle PKSA particulates in the composites. Brittle materials such as PKSA have low resistance to crack propagation. Thus, low fracture toughness corresponds to low ductility in brittle materials unlike ductile materials that show better opposition to crack propagation. Ductile materials have the ability of redistributing applied stresses and strains by plastic deformation. In ceramic reinforced MMCs, the basic micro-mechanism was reported to be due to particle cracking, interfacial cracking, and particle bonding. The increased crack nucleation due to the increase in the brittle PKSA reinforcement particulates may be responsible for the trend observed in this study. This assertion has been reported by Alaneme & Bodunrin 48 and Alaneme et al 39 . The fracture toughness of sample A1, which is higher than for other samples (A2-A5) is indicative of the ductile nature of SiC particulates, which may result in a mixed fracture modes 39 .
SEM characterization of the fractured surface. For the tensile fracture, the surface morphologies of the representative samples are displayed in Fig. 13(a-c). Figure 13(a) shows the SEM micrograph of the fractured surface for Al 6063 alloy, while Fig. 13(b,c) show the SEM micrographs of fracture surfaces of the composites. Cup and cap surfaces can be observed on the fractured surfaces of the composites. The fractured surface of the Al matrix shows large population of well-developed dimples. A mixed fracture mechanism was seen on the fractured surface of the composite samples. This is as a result of the ductile tearing of the matrix alloy and the brittle fracture of the reinforcement particles. There is no noticeable necking formation for the composites pro- www.nature.com/scientificreports/ duced. This could be attributed to the rapid occurrence of pore nucleation, growth and coalescence. According to Yigezu et al 3 , pores nucleation, growth, and coalescence majorly contribute to the final fracture of the matrix. More so, the presence of weak and detrimental phases from the PKSA and intermetallic phases activate a different fracture mechanism, which cause the composite to fail via the nucleation, growth, and coalescence of the pores. The growth of the pores is by plastic straining through the local necking of the intervoid matrix, leading to final fracture. There is strong interfacial bonding among the PKSA, SiC and the Al6063 matrix alloy as particlematrix interfacial bonding was not observed 36 . Although, the samples showed good hardness and strength as the PKSA particulates increased; the PKSA particulates lowered the ductility of the hybrid reinforced composites.

Conclusion
The study was on the physico-mechanical properties and morphological examination of aluminium hybrid composites produced using Al 6063 as the matrix alloy with SiC and PKSA as reinforcements of different proportions. The occurrence of some compounds such as SiO 2 , MgO, SiC, and intermetallic (Fe 3 Si) were seen in the composites based on the XRD analysis. These compounds serve as strengtheners and hardeners for the composites. There was homogenous dispersion of both reinforcements in the alloy. It can be concluded that the density of the AMCs produced reduced as the PKSA particulates contents increased in the matrix. The level of the porosity of composites produced through double stir casting route was found to be within the permissible limit (4%) for MMC castings. The increased addition of PKSA when the SiC was constant at 2% into the matrix improved the hardness value, yield strength, ultimate tensile strength, and reduced the percentage elongation and fracture toughness of the synthesized composites. A fracture mechanism was activated due to the presence of weak phases from the PKSA and intermetallic phases, which resulted in composite failure through nucleation, growth, and coalescence of pores. The AMCs produced will be very useful in light-weight engineering applications such as aluminium frames and roofing sheets production.