Inhibitory properties of Chinese Herbal Formula SanHuang decoction on biofilm formation by antibiotic-resistant Staphylococcal strains

The aim of this study was to explore the effect of Chinese herbal SanHuang decoction (SH) on biofilm formation of antibiotic-resistant Staphylococci on titanium surface, and to explore its mechanism. Biofilm-forming ATCC 35984, ATCC 43300 and MRSE 287 were used in this study. The MICs of SH and vancomycin against Staphylococci were determined by the broth microdilution method. Six groups were designed, namely control group (bacteria cultured with medium), 1/8MIC SH group (1MIC SH was diluted by 1/8 using TSB or saline), 1/4MIC SH group, 1/2MIC SH group, 1MIC SH group and vancomycin group (bacteria cultured with 1MIC vancomycin). The inhibitory effect on bacterial adhesion and biofilm formation were observed by the spread plate method, CV staining, SEM, and CLSM. Real-time PCR was performed to determine the effect of SH on the expression levels of ica AD and ica R gene in ATCC 35984 during the biofilm formation. The strains were found to be susceptible to SH and vancomycin with MIC of 38.75 mg/ml and 2.5 μg/ml, respectively. SH with 1 MIC and 1/2 MIC could inhibit the bacteria adhesion, showing only scattered adhesion from SEM. CLSM showed that SH with 1 MIC and 1/2 MIC inhibited the biofilm formation. The quantitative results of the spread plate method and CV staining showed that there was significant differences between the SH groups (P < 0.05). Further, with an increase in SH concentration, the inhibitory effect became more obvious when compared with control group. Among the groups, vancomycin had the strongest inhibitory effect on bacterial adhesion and biofilm formation (P < 0.01). With an increase in SH concentration, the expression levels of ica AD decreased, and the expression of ica R increased correspondingly (P < 0.05). In conclusions, SH can inhibit the biofilm formation of antibiotic-resistant Staphylococci. Its probable mechanistic activity may be through the inhibition of polysaccharide intercellular adhesin synthesis by down-regulating the expression of ica AD gene.

Hence, how to inhibit biofilm formation on the surface of titanium alloy becomes important in the prevention and treatment of orthopedic infections.
For intractable orthopedic infections, in addition to local debridement, an important option is a long-term application of systemic intravenous antibiotics 7 . In clinical practice, a very large proportion of implant-related infections are caused by Staphylococci, and two Staphylococcal species, Staphylococcus aureus and Staphylococcus epidermidis, together account for two out of three infection isolates 8 . As for biofilm-related infections, however, antibiotic-resistant Staphylococcus, especially MRSE (meticillin-resistant Staphylococcus epidermidis) and MRSA (methicillin-resistant Staphylococcus aureus), makes the treatment of implant-associated infections with antibiotics still one of the challenges for orthopedic surgeons 2,4,7 . Hence, discovering alternative treatment methods for orthopedic infections linked to multi-antibiotic-resistant bacterial biofilm is becoming more and more relevant.
For a long time, traditional Chinese medicine (TCM) has been widely used in the treatment of various infectious diseases in China, and many traditional or empirical prescriptions have been proved to have satisfactory clinical therapeutic effects [9][10][11][12] . The SanHuang decoction (abbreviated as SH) is one of the treatment methods widely used in our hospital for treatment of limb infections with bone and implant exposure. This decoction is composed of Scutellaria baicalensis Georgi, Coptidis rhizoma, Cortex Phellodendri chinsis and other Chinese herbs. According to the theory of traditional Chinese medicine, it has the heat-clearing and detoxing functions. Through external soaking and washing of the locally infected wound with SH, it was found that this decoction can effectively control the infections [10][11][12] . However, there has been no study to date that has explored the antibiofilm formation properties of the SH in vitro.
Therefore, based on previously published clinical studies and the widely used titanium implant material for orthopedic surgery 6,[10][11][12] , the aim of this study was to investigate the effect of SH decoction on adhesion and biofilm formation of MRSE and MRSA on titanium surfaces, and also to explore the probable mechanism behind its effect on biofilm formation.

Materials and methods
Preparation of SH decoction. SH decoction contains Scutellaria baicalensis Georgi (25 g), Coptidis rhizoma (25 g), Cortex Phellodendri chinsis (25 g), Sophora flavescens (20 g), Lonicera Japonica (20 g), Forsythia suspensa (20 g) and Taraxacum mongolicum Hand.-Mazz. (20 g) (Table 1). All the herbs were provided by the TCM pharmacy of Henan Luoyang Orthopedic-Traumatological Hospital following the requirement standards of the section one of Pharmacopoeia of the People's Republic of China (2015 edition). The procedure of preparing the SH aqueous extract is as follows: firstly, all herbs were tipped into a ceramic pot with 1000 ml pure water and soaked for 30 min. Secondly, the concoction was boiled at high heat for 30 min, and was maintained at a low flame until the aqueous extract reduced to 250 ml. Finally, aqueous extract was filtered with filter paper, and water extraction of the liquid was performed through Ø 22 μm filter. Based on the original herb dose, the initial liquid concentration of the extract solution was about 0.62 g/ml, which was stored in the refrigerator at − 20 °C for the subsequent experiments. Only one batch of SH were used in this study.
Preparation of bacterial strains. Two standard strains, the positive biofilm-forming S. epidermidis ATCC 35984 (American Type Culture Collection [ATCC], MRSE) and S. aureus ATCC 43300 (MRSA), and one clinical isolate, methicillin-resistant S. epidermidis (MRSE 287) which was isolated from one patient with an orthopaedic implant-related infection, were used in this study 13,14 . The strains frozen in a − 80 °C refrigerator were rapidly thawed and inoculated on a Tryptone Soy Agar (TSA) plate and cultured in an incubator at 37 °C for 24 h. A single colony was selected from the TSA and inoculated in a 50 ml centrifuge tube containing 10 ml Tryptone Soy Broth (TSB), the tube was incubated for 10 h at 37 °C with agitation at 100 rpm. Then, 25 µl of bacterial suspension was transferred to another sterile centrifuge tube containing 10 ml TSB and incubated at 37 °C for 14 h, after which 1 ml suspension was transferred into a 1.5 ml centrifuge tube and the bacteria in the suspension was harvested by centrifugation for 5 min at 4 °C and 1000 rpm (Sorvall TC6 centrifuge, Du Pont, Bad Nauheim, Germany). The precipitate was then washed three times with 0.15 M PBS (phosphate buffered saline) to remove the remaining TSB, and resuspended in sterile PBS to an optical density of 0.490 at 600 nm using Synergy HT multi-detection microplate spectrophotometer (Bio-tek, Winooski, VT), which corresponded to 10 9 CFUs (Colony forming units)/ml.  15 . An overnight culture of the strains were diluted tenfold in TSB and incubated at 37 °C until they reached exponential growth phase. Serial twofold dilutions of SH (155 mg/ ml to 4.84 mg/ml), gentamicin (1024 μg/ml to 0.5 μg/ml), penicillin (1024 μg/ml to 0.5 μg/ml) and vancomycin (8 μg/ml to 0.0625 μg/ml) in Mueller Hinton (MH) broth were prepared in a 96-wells plate with 190 μl per well. Ten microlitres of bacterial inocula of each strain containing 5 × 10 6 CFUs/ml was added in all wells. A number of wells with only MH broth (without inoculum and drugs) in each plate were designed as blank control, and a number of wells with MH broth and inoculum (without drugs) were designed as negative control. The plates were incubated for 24 h at 37 °C. The MIC was detected following addition of 50 μl of INT (2-4-Iodophenyl-3-4-nitrophenyl-5-phenyl-2H-tetrazolium chloride) at a final concentration 0.2 mg/ml in all the wells and incubated for 30 min at 37 °C. Bacterial growth was determined by observing the color change of INT in the wells. Biologically active bacterial cells will reduce the colourless tetrazolium salt which act as an electron acceptor to a red-coloured formazan product 16 . Inhibition of bacterial growth is observed when the solution in the well remained clear after incubation with INT. MIC was defined as the lowest extract concentration that completely inhibits the growth of microorganisms. Each experiment was performed three times in duplicate.

Effect of different SH concentration on bacterial adhesion and biofilm formation.
Titanium discs of 10 mm in diameter and 1 mm in thickness were placed into a 48-well plate (Costar 3548, Corning, NY, USA), and six replicates were used for each group. All disks were autoclaved at 121 °C for 20 min before used. S. epidermidis ATCC 35984, S. aureus ATCC 43300 and MRSE 287 were diluted to a density of 10 6 CFUs/ml with 0.9% saline, saline-vancomycin, or different sub-MICs of SH (dilution with saline), and 1 ml of the cell suspension was added to the well containing the discs. The plates were incubated in aerobic conditions for 4 h. Then, the bacterial adhesion on the titanium surface were analyzed with the following methods.
The spread plate method. The discs were gently washed three times with saline to remove loosely adherent bacteria, and then transferred into a 10 ml glass tube containing 0.5 ml saline. The tubes were then placed in an ultrasonic bath (B3500S-MT, Branson Ultrasonics Co., Shanghai, China) and the bacteria attached on the disc were dislodged by ultrasonication (5 min) at a frequency of 50 Hz. Ultrasonication was followed by rapid vortex mixing (Vortex Genie 2, Scientifific Industries, Bohemia, NY, USA) at maximum power for 1 min to remove bacteria that had adhered to the material. This method is known to be effective for removing biomaterial-adherent bacteria 17 . The vortexed solutions were serially diluted tenfold and the final three dilutions were plated in triplicate onto TSA and then incubated at 37 °C for 24 h. Finally, the number of CFUs on the TSA were counted, and the number of bacteria adhering to titanium surface was calculated and is expressed relative to the surface area (CFUs/mm 2 ).
SEM assay. A sterile pipette was used to carefully remove the saline from each well. The discs were transferred with forceps into another fresh 48-well plate and gently washed with saline three times to remove loosely adherent bacteria. The discs were fixed in 2.5% glutaraldehyde for 2 h at 4 °C, then washed with PBS and dehydrated through a series of graded ethanol solutions (25, 50, 75, 95 and 100%). The samples were subsequently freezedried, sputter coated with gold, and observed using SEM (Joel JSM-6310LV, JEOL Ltd., Tokyo, Japan). After incubation for 24 h with TSB, TSB-vancomycin, or different sub-MICs of SH (dilution with TSB). Biofilm formation on the titanium surface were analyzed by the following methods. Crystal violet (CV) staining assay: A sterile pipette was used to carefully remove the TSB from each well. The discs were transferred into another 48-well plate and gently washed three times with PBS. Then, 1 ml of 2.5% glutaraldehyde solution was added into each well for 10 min to allow fixation. The glutaraldehyde solution was removed and the wells were washed with PBS. Subsequently, PBS was removed and 2 ml of 0.1% (w/v) aqueous CV solution was added to each well followed by incubation for 20 min at room temperature. CV solution was discarded, and the wells were washed with PBS again and air-dried for 12 h in the dark. Next, the quantity of biofilm was analyzed by adding 30% acetic acid in a volume of 1 ml to each well to dissolve dye for 30 min, after which 200 μl of the dye solution were transferred into a 96-well microtiter plate, one group equaling one vertical row of the plate. The optical density was read at a wavelength of 492 nm using a plate reader (Synergy HT, BioTEK) 18 .
CLSM assay. After 24 h incubation, the TSB medium were removed carefully from each well, and the discs were transferred into another 48-well plate and gently washed with PBS three times. Then the wells containing the titanium discs were added with 500 μl combination dye (LIVE/DEAD Baclight bacteria viability kits, L13152; Molecular Probes, Eugene, OR, USA) in a dark environment at room temperature for 15 min and were subsequently analyzed with a CLSM (Leica TCS SP2; Leica Microsystems, Heidelberg, Germany). The live/dead kit containing two kinds of fluorescence dyes were used to distinguish the viable and non-viable cells under the fluorescence microscope, because dye SYTO 9 can make the viable bacteria with intact cell membranes display green fluorescence, whereas dye PI (Propidium Iodide) can make non-viable bacteria with damaged membranes display red fluorescence. The Leica confocal software was used to analyze the biofilm images. Statistical analysis. All the experiments were performed in triplicate and repeated three times. Data are expressed as mean ± standard deviation. The total number of bacteria was normalized by the number obtained from the control group. This method for presenting the data was chosen because the number of colony forming units was not exactly the same for each condition. The results were tested using a one-way analysis of variance. The Tukey's multiple comparison test was applied for multiple comparisons between individual treatments once significant difference was observed by ANOVA. The differences observed between groups were considered to be significant at P < 0.05 using SPSS 19.0 software.

Effect of SH decoction on bacterial adhesion.
From the results of the spread plate method (Fig. 1 www.nature.com/scientificreports/ statistically significant difference of bacterial adhesion between SH groups under 1/4, 1/2 and 1MIC concentrations, which was more obvious with the increase of SH concentration (P < 0.01). On the other hand, vancomycin at 1MIC had the strongest inhibitory effect on the bacterial adhesion among the groups (P < 0.01). Further, we performed SEM (Fig. 2) after 4 h incubation with bacteria and found that scattered bacterial colonies were observed on the titanium surface in the 1/2MIC SH (Fig. d1, d2, and d3), 1MIC SH (Fig. c1, c2, and c3) and vancomycin group (Fig. f1, f2, and f3). However, the bacteria in the control (Fig. a1, a2, and a3), 1/8MIC SH (Fig. b1, b2, and b3) and 1/4MIC SH group (Fig. c1, c2, and c3) obviously clumped together. For SH groups with 1/4, 1/2 and 1MIC concentrations, the inhibition of the bacterial adhesion on the surface of titanium disc became more obvious with the increase of SH concentration. Meanwhile, the number of adherent bacterial colony on the titanium surface in vancomycin group (Fig. f1, f2, and f3) was the least in all groups. Fig. 3, compared with the control and 1/8MIC SH groups of S. epidermidis ATCC 35984 (Fig. 3a) and MRSE 287 (Fig. 3c), the OD values of 1/4MIC SH, 1/2MIC SH, 1MIC SH and vancomycin groups were significantly decreased (P < 0.01), while there was no significant difference between the control and 1/8MIC SH groups (P > 0.05). For the SH groups in the two strains, the OD values decreased with the increase of SH concentration, and the difference among the 1/8MIC, 1/4MIC, 1/2MIC and 1MIC SH groups was statistically significant (P < 0.05). For S. aureus ATCC 43300 (Fig. 3b), compared with the control group, the other groups had lower OD values with significant difference among 1/4MIC SH, 1/2MIC SH, 1MIC SH and vancomycin groups (P < 0.01), and on difference between 1/8MIC SH and 1/4MIC SH groups (P > 0.05). The OD value of vancomycin group was lower than that of 1MIC SH group (P < 0.01).

Antibiofilm activity of SH decoction. As shown in
CLSM of bacterial biofilms on the titanium surface is shown in Fig. 4. After culture for 24 h, a large number of bacterial colonies were clustered to form a dense biofilm structure on the titanium surface in the control (Fig. a1, a2, and a3) and 1/8MIC SH (Fig. b1, b2, and b3) groups, displaying high-intensity green fluorescence. However, with the increase of the SH concentration, the intensity of green fluorescence gradually decreased, suggesting that the bacterial biofilm formation was also gradually inhibited. For S. epidermidis ATCC 35984 and S. aureus ATCC 43300, high-intensity green fluorescence was still visible in 1/4MIC SH group ( Fig. c1 and c2), indicating the existence of severe biofilm formation; While in 1/4MIC SH group of MRSE 287 (Fig. c3) and in 1/2MIC SH groups of three bacterial strains (Fig. d1, d2, and d3), low-intensity green fluorescence was shown, indicating that there was still mild biofilm formation on the titanium surface. In the 1MIC SH (Fig. e1, e2, and e3) and vancomycin (Fig. f1, f2, and f3) groups, only scattered green fluorescence of the bacterial colonies were seen, showing no biofilm formation. (Fig. 5) showed that the OD value of biofilm had an increasing trend in the control and 1/8MIC SH groups with the increase of incubation time, suggesting the strains adhered to the titanium surface and gradually formed biofilm; from 6 to 24 h, we observed significant differences of the OD values between any two time-points (P < 0.01), while no statistical difference of OD value was found for S. epidermidis ATCC 35984 (Fig. 5a) or MRSE 287 (Fig. 5c) (P > 0.05) and statistical difference was found for S. aureus ATCC 43300 (Fig. 5b) (P < 0.01) between 24 and 48 h. For the 1/4MIC SH group of S. epidermidis ATCC 35984 (Fig. 5a) and MRSE 287 (Fig. 5c), the OD values increased and difference between any two time-point were found from 6 to 18 h (P < 0.01), then no difference from 18 to 48 h (P > 0.05); for S. aureus ATCC 43300 (Fig. 5b), the OD values of 1/4MIC SH group increased and difference between any two time-point were statistically significant from 6 to 48 h (P < 0.05). For the 1/2MIC SH group of S. epidermidis ATCC 35984 (Fig. 5a) and S. aureus ATCC 43300 (Fig. 5b), the OD values increased and difference between any two time-point were found from 6 to 48 h (P < 0.05); for MRSE 287 (Fig. 5c), the OD values of 1/2MIC SH group increased and difference between any two time-point were statistically significant from 6 to 24 h (P < 0.01), then no difference from 24 to 48 h (P > 0.05). On the contrary, the OD values from 6 to 48 h in the 1MIC SH and vancomycin groups were stable, and no obvious difference was found between any two time-points (P > 0.05). At different time point, the OD values of S. epidermidis ATCC 35984 (Fig. 5a) and S. aureus ATCC 43300 (Fig. 5b) in the control, 1/8MIC SH and 1/4MIC SH groups were higher than that in www.nature.com/scientificreports/ 1/2MIC SH, 1MIC SH and vancomycin groups (P < 0.01). The OD values of MRSE 287 (Fig. 5c) in the control, 1/8MIC SH, 1/4MIC SH and 1/2MIC SH groups were higher than that in 1MIC SH and vancomycin groups (P < 0.01). The vancomycin group had the lowest OD value of all the groups (P < 0.01).

Effect of SH decoction on biofilm formation at different incubation time-point. CV staining
SH effects on the expression of ica AD and ica R. As shown in Fig. 6, the expression level of ica AD was not significantly different between the TSB and 1/8MIC SH groups (P > 0.05). The expression level of ica AD in the 1/4 MIC, 1/2MIC, 1MIC SH and vancomycin groups decreased compared with that of the TSB and 1/8MIC groups (P < 0.05). In the SH groups, the ica A expression level showed a gradual decrease with the increase of SH concentration, showing statistically significant differences (P < 0.01). Further, no differences of ica AD expression were found between the 1MIC SH and vancomycin groups (P > 0.05). For ica R expression level, there existed a gradual increase with the increase of SH concentration; Compared with the TSB and 1/8MIC SH groups, the 1/4MIC, 1/2MIC, 1MIC SH and vancomycin groups showed high expression level of ica R (P < 0.01). However, there were no statistically significant differences between the TSB and 1/8MIC SH groups or among the 1/2MIC SH, 1MIC SH and vancomycin groups (P > 0.05).

Discussion
Inhibition of biofilm formation and the killing of antibiotic-resistant bacteria are the key methods for effective treatment of the refractory infections related to the orthopedic implants. Intravenous use of sensitive antibiotics is necessary for the clinical treatment of infections. However, unfortunately, multidrug-resistant bacteria are often found in the bacterial culture of orthopedic infection wounds, and based on the antibiotic sensitivity tests, vancomycin has often become the first choice for clinicians 19 . Studies have shown that only a small portion of intravenous vancomycin can reach bone and joint tissues, and even less penetrates into bone tissues at the site of osteomyelitis; thus, vancomycin may not eliminate multidrug-resistant pathogens in biofilms 20 . In addition, the application of vancomycin has led to the emergence of vancomycin resistant Staphylococcus strains 21 . External application of the TCM, which has been used in the Chinese population to prevent and treat orthopedic infectious for long time, and many prescriptions have been proved to be therapeutically effective [10][11][12] .  www.nature.com/scientificreports/ chronic orthopedic infections. For local infections of extremities caused by multi-antibiotic-resistant bacteria with exposure of bone and implants, based on the TCM theory of "simmer pus promoting the regeneration", we have successfully controlled the local infected wounds by the external use of SH decoction. Specifically, the infected wound was soaked and washed for 30 min in SH extract twice a day, and after treatment for mean 3 weeks, local infections of the limbs are clearly controlled, secretions and necrotic tissue are reduced, and the granulation tissue grows well, which provided better tissue conditions for reoperation and wound healing. This decoction contains Scutellaria baicalensis Georgi, Coptidis rhizoma, Cortex Phellodendri chinsis and so on, which are heat-clearing and detoxifying drugs. Modern medical research have shown that these Chinese herbs had a broad-spectrum antibacterial and bacteriostatic effects, and no bacterial resistance was found in the combined application. The clinical application of SH prescription can play the role of anti-bacterial and anti-inflammatory in the wound, thus achieving the purpose of eliminating the infections [10][11][12] . This study investigated the in vitro effect of SH decoction on adhesion and biofilm formation of bacteria on the titanium surface, and explored the potential value of this prescription as an effective method to treat orthopedic infections. Since the majority of orthopedic implant-related infections are caused by S. epidermidis and S. aureus 22 . Therefore, we selected the S. epidermidis ATCC 35984, S. aureus ATCC 43300 and MRSE 287 to understand biofilm formation in this study. Previous research have demonstrated that biofilm formation proceeds www.nature.com/scientificreports/ in two phases: primary attachment of Staphylococcal cells on a biomaterial, which is followed by bacterial accumulation in multiple layers and glycocalyx formation leading to a mature biofilm, the attachment of Staphylococcus to titanium surfaces is strongly seen as an essential step in the formation of biofilm 3,7 . If the primary bacterial adhesion is interfered, then the biofilm formation could be prohibited consequently 3,16 . The results in this study showed that SH decoction could inhibit the bacterial adhesion on the titanium surface, and there was a trend that the inhibition effect was more obvious with the increase of dilution concentration of SH decoction. The results also showed that SH decoction could inhibit the formation of dense structural biofilms of the antibiotic-resistant Staphylococcus on the titanium surface by either quantitative or qualitative analysis. Specifically, the bacterial strains cannot form biofilms when incubated with the 1MIC of SH decoction, only showing loose adhesion of the bacterial colonies. Although biofilm was formed at 1/4 MIC and 1/2MIC, its OD values were obviously less than that of TSB group. At 1/8MIC of SH decoction, biofilm formation was not inhibited compared to the TSB control group. It can be seen from above analysis that SH decoction could inhibit the biofilm formation on the titanium surface, which is dependent on the dilution concentration of the SH decoction.
Many studies have shown that polysaccharide intercellular adhesin (PIA) is the primary determinant of the accumulation phase of staphylococcal biofilm formation [22][23][24] . It has been reported that the ica A and ica D partially overlaps in sequence and they together mediate the synthesis of N-acetylglucosamine using UDP-N-acetylglucosamine as a substrate, which composes β-1,6-linked homoglycan to synthesize PIA 25 . Co-expression of the functional ica A and ica D gene can catalyze the synthesis of PIA, and the down-regulation of ica AD expression leads to the reduced activity of N-acetylglucosaminyl transferase, which also leads to reduced amount of PIA [25][26][27] . In addition, studies have shown that the complex gene regulation system of Staphylococcus may ultimately influence the biofilm formation by regulating the expression of ica operon 24,27 . Therefore, in order to verify the role of ica operon in the inhibition of bacterial biofilm formation on the titanium surface by SH decoction, S. epidermidis ATCC 35984 with property of positive biofilm formation and ica AD gene expression was selected in this study 13 . The expressions of ica AD were detected by real-time fluorescence quantitative PCR, and the results showed that during the process of biofilm formation, the expression level of ica A and ica D genes in the biofilm and culture medium was inhibited by the SH decoction at different dilution concentrations, and the inhibition became more obvious with the increase of SH concentration. In addition, the expression of ica operon is negatively regulated by its upstream inhibitory gene ica R 27 . In our study, we found that SH decoction could not only down-regulate the expression of ica AD, but also up-regulate the expression level of ica R in a concentration dependent manner. Therefore, it could be inferred that the SH decoction activates ica R to inhibit the transcription of ica AD, thus leading to the reduced synthesis of PIA and formation of biofilm on the titanium surface.
Several limitations of the present study deserve to be mentioned. Firstly, although our results demonstrated a beneficial effect of SH decoction against bacterial biofilm formation, the synergistic effect of SH combined with conventional antibiotics on the bacterial biofifilm remains unclear. Future studies are warranted to clarify this issue. Secondly, the biofilm formed by Staphylococcus is a complex process, in which PIA encoded by the ica ADBC operon plays a major role [22][23][24]28 . The complex regulatory system of Staphylococcus may ultimately influence the biofilm formation by regulating the expression of ica operon. For example, sarA, SigmaB and RsbU genes can promote the transcription level of ica ADBC, while ica R and lux S can inhibit the transcription of ica ADBC 29,30 . Although our study has suggested that SH decoction can inhibit the biofilm formation by down-regulating the expression level of ica AD, its effect on the expression of upstream regulatory genes is still unclear. Therefore, additional studies are necessary to better understand these mechanisms.

Conclusions
SH decoction can inhibit biofilm formation of antibiotic-resistant Staphylococcus on the titanium surface based on in vitro results. There appears to be a concentration dependent relationship between SH decoction and biofilm formation. The mechanism may be that the SH decoction inhibit the transcription of ica AD, thus, leading to reduced synthesis of PIA and inhibilation of biofilm formation.