Spin dynamics investigations of multifunctional ambient scalable Fe3O4 surface decorated ZnO magnetic nanocomposite using FMR

Microwave spin resonance behavior of the Fe3O4 surface decorated ZnO nanocomposites (FZNC) has been investigated by ferromagnetic resonance (FMR). Modified hydrothermal method has been adopted to fabricate FZNC samples with Fe3O4 nanoparticles chains were used as seeds in the uniform magnetic field to decorate them on the surface of the ZnO nanoparticles in a unique configuration. Spin dynamics investigation confirms the transition of ZnO from diamagnetic to ferromagnetic as the sharp FMR spectra converts to the broad spectra with Fe3O4 nanoparticles incorporation. A single broad FMR spectra confirms that no isolated Fe3+ or Zn2+ ions exist which is also in agreement with XRD confirming suitable composite formation. Further, the increase in Fe3O4 concentration leads to decrease in g-value which is resulting from the internal field enhancement due to magnetic ordering. Also, various spin resonance parameters were calculated for the FZNC which provides a detail information about the magnetic ordering, exchange coupling and anisotropy. Elemental analysis confirms the presence of Fe and Zn simultaneously and transmission electron microscopy (TEM) image show the presence of Fe3O4 on the grain boundaries of ZnO which has been confirmed by taking high-resolution TEM and electron diffraction patterns on both sides of the interface. These unique structural configuration of the FZNC has tremendous potential in various magneto-optoelectronic, spintronics and electro-chemical applications.


Microwave spin resonance behavior of the Fe 3 O 4 surface decorated ZnO nanocomposites (FZNC) has been investigated by ferromagnetic resonance (FMR). Modified hydrothermal method has been adopted to fabricate FZNC samples with Fe 3 O 4 nanoparticles chains were used as seeds in the uniform magnetic field to decorate them on the surface of the ZnO nanoparticles in a unique configuration. Spin dynamics investigation confirms the transition of ZnO from diamagnetic to ferromagnetic as the sharp FMR spectra converts to the broad spectra with Fe 3 O 4 nanoparticles incorporation. A single broad FMR spectra confirms that no isolated Fe 3+ or Zn
ions exist which is also in agreement with XRD confirming suitable composite formation. Further, the increase in Fe 3 O 4 concentration leads to decrease in g-value which is resulting from the internal field enhancement due to magnetic ordering. Also, various spin resonance parameters were calculated for the FZNC which provides a detail information about the magnetic ordering, exchange coupling and anisotropy. Elemental analysis confirms the presence of Fe and Zn simultaneously and transmission electron microscopy (TEM) image show the presence of Fe 3 O 4 on the grain boundaries of ZnO which has been confirmed by taking highresolution TEM and electron diffraction patterns on both sides of the interface. These unique structural configuration of the FZNC has tremendous potential in various magneto-optoelectronic, spintronics and electro-chemical applications.
Magnetic manipulation in materials achieved through hybrid materials are of great interest owing to their unique physical, chemical and optical properties which can be tuned by external magnetic field 1 . Magnetic control on the materials properties has been an exciting area of research as they exhibit immense potentials for the device development with enhanced performance 2 . One of the most vital part of both basic research and applications of these composites lies in rational understanding the spin dynamics of these materials to achieve the desired properties 3 . Metal oxide materials are widely used in engineering as well as biomedical applications. In particular, zinc oxide (ZnO) of wurtzite hexagonal structure (space group-C 6v 4 -P6 3 mc, direct band gap 3.37 eV) is one of the most prominent materials with wide interdisciplinary applications in optoelectronic, photo-catalysis, sensing, and drug delivery 4,5 . However, nanotechnology has opened a whole new horizon of several biomedical application such as bio-imaging/sensing, anti-microbial/cancer and drug/gene delivery etc. as nanostructures behaves in contradicting manner from their bulk counterparts due to enhanced surface dependent properties and large defect sites 6 .
Magnetic nanocomposites (MNC) or magneto-hybrid materials are multiphase materials with one or more magnetic phases and one of the phases present in the nanoscale range 7  www.nature.com/scientificreports/ properties that are inherently different from the present phases or encompasses a combination of the property of all the present phases in the system. The MNCs are solid solutions of two or more components in which the matrix of one material is mixed with the other material to obtain the desired properties. Superparamagnetic (SP) Fe 3 O 4 particles of inverse spinel AB 2 O 4 structure with A (octahedral) site occupied by Fe 2+ ions and B (tetrahedral) sites occupied by Fe 3+ ions has high magnetic saturation (M s = 40 emu/g with average particle diameter = 10 nm) which makes them effective as a hybrid material 2,8 . SP Fe 3 O 4 nanoparticles are ideal for their use in combination with ZnO as it has a narrow bandgap, biocompatible, non-toxic, high chemical stability, mechanical hardness, and high saturation magnetization (M s ) material 9 . The embodiment of the magnetic nanoparticles in ZnO provides a unique blend of properties as ZnO provides excellent optoelectronic properties and incorporation of magnetic nanoparticles provides an opportunity to tune these properties through an external magnetic field. The unique magneto-optoelectronic properties of these materials have engrossed the research focus on the synthesis of Fe 3 O 4 -ZnO nanomaterials (FZNM) in various morphologies and structures. Also, FZNM fabrication has been reported in wide domain and interdisciplinary field such as biomedical, optoelectronics, electrochemical, and photocatalytic due to its enhanced magnetic field induced magneto-optoelectronic, spintronic, and electrochemical performance. Altogether, heterostructure FZNM has tremendous potential to be efficiently used in spintronic devices. The ferromagnetic alignment in ZnO by incorporating magnetically active material provides new landscapes in the field of magneto-optoelectronic, spintronics, and electrochemical devices 10 .
The existence of the strong correlation between the structure of the composite to its physical and chemical properties requires exploration of different nanocomposite structures and its optimization. Major attention in the fabrication of the FZNM is required to attain isotropic properties by uniformly distributing the nanoparticles in the matrix. Matrix dispersed structures are useful when uniformity of the properties is required throughout the material. The molten salt method is one pot novel technique for the synthesis of matrix dispersed magnetite-zinc oxide nanocomposites. Reddy et al. 5 prepared Fe 3 O 4 -ZnO hybrid nanocomposite for application in anode material in Li-Ion batteries. They have prepared the composite by the molten salt method in the average size range above 100 nm. ZnO acts as a good matrix element for Fe 3 O 4 imparting it exceptional Li-ion recycling properties. The two-step approach adopted by S. Singh et al 11 for the fabrication of Fe 3 O 4 embedded ZnO magnetic semiconductor nanocomposites has shown great potential and has achieved good isotropic properties. In the first step, glycine functionalized magnetic nanoparticles were prepared which are mixed with the Zn precursors and refluxed to in-situ fabricate ZnO. The prepared composite displays remarkable detoxification properties which were used for the removal of bacterial pathogens.
Further, core-shell structures are highly efficient as they provide excellent stability, dispersibility, and functionality to the composite materials. Constituents of the core-shell and their ratio can be manipulated to achieve the desired properties required by the application. Seed mediated growth process and sequential nanoemulsion techniques have been successfully employed for the synthesis of core-shell nanostructures 4,12,13 . Jian Wang et al 14 prepared Fe 3 O 4 -ZnO core-shell nanocomposites by a simple two-step chemical method of size range 60 nm for their use in wastewater treatment. They have not observed any degradation of photocatalytic properties after several cycles of water treatment suggesting a high performance of the material. Magnetic properties imparted by Fe 3 O 4 core ensured the re-usability of the composite. These core/shell nanocomposites were employed in the fabrication of inverted solar cells for their enhanced performance. The incorporation of magnetite nanoparticles leads to an increase in short circuit current density due to the presence of local magnetic field and ZnO nanoparticles suppressed parasitic absorption of radiation by magnetic nanoparticle 15 . Further, multicore-shell structures are sculptured when a magnetic layer is needed to be sandwiched between two non-magnetic layers. Interfacial interactions at the two surfaces of the core nanoparticles impart unique properties to the material. Multifunctionality of the structure facilitates their use as a probe for target-specific imaging and drug delivery agents 16 . Uniform spatial distribution of properties necessitates the fabrication of Janus structures Fe 3 O 4 -TiO 2 nanocomposites prepared by Zeng et al 17 shows good imaging properties and can be employed in photodynamic therapies.
Probing the spin dynamics of the nanocomposite can provide us with new insight enabling the improvements in the functionality of the composite. Understanding the dipolar and superexchange interactions existing among the particles is essential to comprehend the dynamics of the composite 18 . Spin resonance studies of pure ZnO and Fe 3 O 4 nanoparticles using the FMR technique have been carried out extensively in the past 19,20 . ZnO nanoparticles are diamagnetic but reveal their paramagnetic comportment in the FMR spectrum. The peak observed in the FMR spectra for ZnO stipulates the existence of paramagnetism 21 . Further, the presence of oxygen vacancies and interstitial zinc ions are responsible for the manifestation of paramagnetic behavior in the resonance spectra. The random orientation of electron spins in ZnO realigns itself altogether into the direction of the applied magnetic field absorbing energy in a narrow band of frequencies. Due to the simultaneous realignment of all the spins, a narrow linewidth is observed in the ZnO FMR spectra. On the other hand, Fe 3 O 4 nanoparticles are SP in nature and exhibit high spin polarization at room temperature 22 . Anisotropy energy enforces the magnetization direction of individual spins to freeze in a specified direction. Exchange interactions existing among the spins preserves the parallel alignment of the magnetic moments. The cumulative effect of the two interactions results in a parallel alignment of spins in different directions. Due to different directions of spins in neighboring crystallites, absorption of radiation occurs over a wider range of frequencies leading to linewidth broadening. FZNM provide opportunities of resonance enabling widespread applications and components concentration or amount of the constituents in the composite can be optimized to get the resonance properties in accordance with the application implementation 18 .
Numerous reports are available in the literature investigating the structural, magnetic, and electronic properties of FZNC. However, no significant attempts have been made to explore the spin dynamics of FZNC to the best of our knowledge. All the previous FZNC reported in the literature has Fe 3 O 4 nanoparticles in the core and ZnO in the shell, whereas in the present work we have capitalized the chain structure formation of the Fe 3 O 4 nanoparticles to occupy the shell of the ZnO core. This configuration has not been reported yet and has several advantages. An intensive literature search has been made and we have not observed any investigation targeting the spin dynamics of FZNC in detail. The understanding of the spin dynamics of the magneto-nanocomposite can open new avenues in the field of magnetic field tunable semiconductor oxides 23 .
Herein we have performed a detailed investigation of the dynamic magnetic properties of multifunctional FZNC. We have adopted a simple facile chemical synthesis technique for the fabrication of the nanocomposite in which Fe 3 O 4 nanoparticles prepared by co-precipitation technique were used as seeds followed by in-situ hydrothermal growth of the ZnO. The ZnO precursors were mixed with the Fe 3 O 4 seeds in the presence of the constant magnetic applied radially to assist in chain formation over the in-situ seeding ZnO nanoparticles. This allows Fe 3 O 4 nanoparticles to coat the ZnO nanoparticles rather than taking the core position. Further, the structural behavior of the prepared nanocomposite has been obtained by the X-ray diffraction (XRD) technique. The obtained XRD pattern for each sample was fitted by Williamson-Hall (W-H) method to calculate the crystallite size and strain. The morphology and size distribution was confirmed by scanning electron microscope (SEM) and transmission electron microscope (TEM). Further, an energy dispersive X-ray spectrum (EDS) was used to obtain the elemental mapping to confirm the structure of the FZNC. The static magnetic properties of the pure ZnO, Fe 3 O 4, and FZNC were obtained by vibrating sample magnetometer (VSM) to observe the effect of magnetic nanoparticles incorporation. The spin dynamics of the FZNC was investigated by the microwave spin resonance technique by fitting the FMR spectra of the samples. The FMR spectra obtained for the samples were fitted with various theoretical models presented to establish a relationship among different spin resonance properties. Various spin resonance properties were calculated for each sample and optimized concentrations were obtained, which is the key for efficient material performance.

Synthesis of MNC samples
A detailed experimental investigation has been performed to investigate the spin dynamics of FZNC to understand their microwave absorption behavior. The schematic of the synthesis of the Fe 3 O 4 surface decorated ZnO magnetic nanocomposite is depicted in Fig. 1. Multifunctional MNC was prepared in a two-steps process; in the first step, seeds of Fe 3 O 4 nanocrystals have been prepared by the standard co-precipitation method. Synthesis and surface functionalization of Fe 3 O 4 nanocrystals were performed by adopting a procedure described before 24 . Further, in the second step, these prepared Fe 3 O 4 nanocrystals were utilized as seeds for the synthesis of MNC using the hydrothermal method. In the typical procedure, 2 g polyethylene glycol was added in 10 ml of deionized (DI) water at a uniform stirring rate of 400 rpm for 15 min. Dried Fe 3 O 4 nanocrystals were then added in three different concentrations (25,50, and 100 mg) under controlled sonication during the mixing process. These three samples were named FZA, FZB, and FZC respectively with increasing Fe 3 O 4 concentration in the composite system. Afterward, 0.5 M 10 ml zinc acetate solution was added to the above solution dropwise under a constant stirring rate (400 rpm) for 30 min. 10 mL 1 M urea and 0.5 g polyvinylpyrrolidone (PVP), were mixed separately and added to the resultant solution dropwise while maintaining a constant temperature of the solution. The resultant solution was kept in a uniform radial magnetic field with mechanical stirring for 15 min to allow chain formation of the Fe 3 O 4 nanoparticles providing the shell to grow the ZnO nanoparticles in the core as shown in Fig. 1. The complete solution was transferred into the 100 mL hydrothermal autoclave reactor and kept inside a hot air oven at temperature 200 °C for 14 h. The resultant product was then washed several times with ethanol and DI water and dried in a vacuum oven overnight. The obtained powder was calcined at 600 °C for 2 h in a muffle furnace (CARBOLITE GERO-temperature stability + 2.3 °C) 9,25 . Further uncapped ZnO was prepared by adopting the same procedure and experimental conditions except for the addition of Fe 3 O 4 nanocrystal. Also, a small amount of Fe 3 O 4 nanocrystal was taken out for different characterizations in the first step and it has also been probed for all the characterizations to provide an intensive comparison of bare ZnO, Fe 3 O 4 nanocrystals, and MNC. The details of the samples and nomenclature are shown in Table 1.

Results and discussions
The XRD plots of FZNC, ZN, and FN samples are shown in Fig. 2(a-e). The XRD pattern of FN is shown in Fig. 2 27 . From the XRD patterns, we have observed that the optimized concentration of FN in nanocomposite does not affect the structural properties significantly and appears as a separate phase. It is not mixed with the ZnO matrix which signifies that the composite will show properties of both of the constituents' particles. Figure 3 shows the SEM micrographs of the FZNCs at low and high magnification to observe the morphology of the samples. Figure 3(a1-c1) depicts the SEM images at low magnification and (a2-c2) at high magnification for the MNC samples. From the SEM micrographs, we can clearly distinguish two differentiable sizes of the particles in all the FZNCs samples. The XRD results confirm that the crystallite size of the FZNCs lies in the range 40-50 nm and Fe 3 O 4 nanoparticles taken as seeds are in the range around 10 nm. So, we can conclude from the micrographs that the large particle size depicted in the SEM micrographs are ZnO nanoparticles and smaller Fe 3 O 4 nanoparticles are decorated on the surface of the ZnO. Figure 3(a1) and (a2) shows the SEM micrographs of the FZA samples at low and high magnification from which we can clearly observe that the small Fe 3 O 4 particles are randomly dispersed in the samples. The ZnO and Fe 3 O 4 particles are oriented erratically and thus the system will demonstrate isotropic behavior. This is well in agreement with the XRD results in which no separate peak is observed for the Fe 3 O 4 nanoparticles which implies that the ZnO peaks suppress the Fe 3 O 4 peak due to their much lower concentration. Whereas, for sample FZB, Fe 3 O 4 nanoparticles were very well decorated at the surface of the ZnO particles as shown in Fig. 3(b1) and (b2). This makes the MNC sample highly uniform and isotropic as particles are uniformly distributed in the sample. The XRD results also confirm the same as the slight bump at the major peak of Fe 3 O 4 is observed compared to the pure ZnO nanoparticles. Finally, Fig. 3(c1) and (c2) show the SEM micrograph for the sample FZC which contains the largest concentration of FN nanoparticles. Figure 3(c1 and c2) clearly illustrates that FN nanoparticles are agglomerated at the surface of the ZnO www.nature.com/scientificreports/ nanoparticles and they are appearing as a separate phase which can be corroborated from the XRD results where the Fe 3 O 4 major peak is appearing abruptly. Figure 4(a) depicts the bright field image of FZB sample that clearly shows the presence of lower contrast small particles surrounding the dark core. The high-resolution transmission electron microscope (HRTEM) images and selected area electron diffraction (SAED) micrograph were taken at the interface to observe the present structures. The HRTEM image and SAED patterns shown in Fig. 4(b) confirm that the lower contrast small particles are Fe 3 O 4 and dark big particles are ZnO. The existence of lattice fringes in both regions confirms the crystalline nature of the structures. SAED pattern present in the inset of Fig. 4(b) shows the polycrystalline nature of the nanocomposites. The uniform and well-organized lattice fringes of 0.281 nm corresponding to the (100) plane confirms the presence of hexagonal ZnO in the core. However, the lattice fringes of 0.253 and 0.296 nm corresponds to (311) and (220) planes, respectively, that affirms the presence of cubic crystalline phase Fe 3 O 4 2,28,29 . The particle size of Fe 3 O 4 is calculated to be range 2-10 nm. EDS analysis in Fig. 4(c) demonstrates various elements; Zn, Cu, Fe, and O present in the structure. Figure 4(e-i) shows the elemental mapping of C, Fe, O, Cu, and Zn elements, respectively obtained using TEMCON software. Figure 4 confirms the Fe 3 O 4 surface decorated ZnO structure as shown schematically in Fig. 1.
Further, Fig. 5(a) reveals an HRTEM image of sample FZA which shows the presence of ZnO as well as Fe 3 O 4 nanoparticles. Some nanocrystallites of hexagonal ZnO are distributed randomly with different interplanar spacings of 0.246 and 0.261 nm corresponding to (101) and (002) planes. Fe 3 O 4 nanoparticles with an interplanar spacing of 0.253 nm correspond to (311) planes of cubic crystal structure were also noticed at some places 30,31 . Only a few numbers of Fe 3 O 4 nanoparticles are observed due to less concentration taken while synthesizing these samples. Also, the dislocation in (002) planes of the ZnO is evident from Fig. 5(a) which is caused by the www.nature.com/scientificreports/ incorporation of the Fe 3 O 4 (311) planes. The particle size of the Fe 3 O 4 nanoparticles was found to be 11.2 nm ( Fig. 5(b)). It is clear from Fig. 5 Fig. 5(c-d). Fe 3 O 4 and ZnO nanoparticles were observed to be scattered, no uniform structure is present as depicted in Fig. 5(c). The excess amount of Fe 3 O 4 is present as agglomerates around the ZnO nanoparticles which suggests that the formation of the composite is not suitable. An interface between these nanoparticles can be noticed in Fig. 5(d). Thus, the results are found in agreement with the proposed geometry that The dependence on externally applied magnetic field of the static (dc) magnetization, m(H) for all the samples as recorded at room temperature in applied magnetic field up to 2 T is shown in Fig. 6(a-e) Table 1 shows that FZA and FZB samples have low M s = 0.2816 and 0.5565 emu/g, respectively, which can be well understood from the fact that these nanocomposite samples are of low FN concentration. Whereas, sample FZC shows higher Ms = 5.6976 emu/g as it has a higher concentration of FN loading. All the Furthermore, experimental and fitted FMR spectra of the samples have been shown in Fig. 7. All the FMR spectra were fitted using suitable distribution functions and spin resonance parameters were obtained from the best-fit curves. Figure 7 shows a single broad-spectrum for FZNC samples, implying that isolated Fe 3+ and Zn 2+ ions do not exist. The resonance line observed is the contribution from both Fe 3+ and Zn 2+ in a single phase 33 . FMR spectra of all the samples are symmetrical, but their resonance magnetic field ( H R ) and peak-to-peak linewidth ( H PP ) exhibit systematic variations. The resonance parameters such as H R , H PP , g-factor, spin concentration (Ns) and relaxation time (T S ) are calculated for all the samples and listed in Table 1 34 . From Table 1 we can conclude that microwave resonance parameters strongly depend upon Fe 3 O 4 concentration in the composite.
FMR spectra of both bare ZnO and Fe 3 O 4 are in accordance with the earlier reported results in the literature 34,35 and resonance in ZN and FN is observed at 3526 G and 3338 G, respectively 36 . Adding different amounts of Fe 3 O 4 nanoparticles in the ZnO host matrix shifts the resonance spectra of ZnO in a systematic manner. Resonance is achieved at a lower value of the applied magnetic field with an increase in FN content in the composite. This results due to the increase in ferromagnetic interactions among Fe 3 O 4 nanoparticles as the distance between them decreases on increasing of their proportion in the nanocomposite 37 . Another important parameter of the FMR spectrum is the g-value which provides the orbital contribution to the magnetic moment and is calculated using Eq. 1.
Here, h is Planck's constant, ν is microwave frequency, μ B is Bohr's magneton and H R is the resonance magnetic field 37 . ZN and FN show signals at g = 1.969 and g = 2.0809, respectively, which is in accordance with the literature. The g value for Fe 3 O 4 nanoparticles is greater than of bare ZnO nanoparticles, which is in line with the spin-orbit coupling. It can be elucidated from Eq. 2.
Here, λ is the spin-orbit coupling constant and ∆ is the energy level separation. λ takes negative values when the 3d shell is more than half full and is positive for half-filled 3d shells 38 . The g-value increased monotonically from 2.0005 to 2.17008 as the amount of Fe 3 O 4 was stepped up in FZNC because of an increase in the composite, the increase in magnetic anisotropy possibly results in linewidth in the spin-orbital interactions. The large spin-orbit coupling can make FZNC a key material in future spintronic computing 23 . Furthermore, FMR spectra Due to different directions of internal anisotropy fields of differently oriented facets of crystallites, the resonance curve is broadened since individual crystallites achieve resonance at their own magnetizing field. Another factor attributing to the broadening is the interference of crystalline fields of different crystallites in the region at the interface. As a result, both the zero-energy level splitting and the g-value of ferromagnetic ion located at or near the interface will get changed. There will be a random variation in the magnetic field required for resonance and the lines will get broadened 39 . Deepty et al. 40 reported that enhancement in magneto-dipolar interactions partially leads to linewidth broadening. At higher concentrations, the phenomenon of exchange narrowing curtails the effectiveness of magneto dipolar interactions existing among the fine Fe 3 O 4 clusters which result in the narrowing of linewidth 41,42 . This can be elucidated using the Eq. (3) 35,36 .
where H A and H ex are anisotropy and exchange fields, respectively 43 . The small value of linewidth at higher concentrations indicates that incorporation of Fe 3 O 4 in ZnO reduces the energy loss and makes it suitable for highfrequency applications 44 . From the literature, it has been found that two-time effects or relaxation phenomena are involved in the resonance process i.e. spin-spin and spin-lattice relaxation 45 . The applied field H changes the direction of the field that each dipole experiences. As a result, the dipoles undergo a slight re-orientation and hereby relaxation occurs by small changes in the energy levels of the dipoles. Spin-spin relaxation time is a measure of the time required to establish thermal equilibrium in the spin system. It occurs when the applied field H is smaller than fluctuating internal fields H i produced by the dipoles. The spin-spin relaxation time has been calculated from �H 1/2 and g-value, listed in Table 1 using Eq. (4) 40 : Sharp decrease in T S value is observed with increasing Fe 3 O 4 content after which it gets saturated showing no or little dependence on ferromagnetic particle concentration. This can be explained using the Heisenberg uncertainty principle 45 : www.nature.com/scientificreports/ At low Fe 3 O 4 concentrations, due to spreading in the energy levels of dipole because of large dipole-dipole interactions, the dipoles own a wide range of frequencies. Consequently, a dipole will require a shorter time to reorient itself about a different precession axis 39 . At higher concentrations, competitive dipole-dipole and exchange interactions lead to the saturation in relaxation time values. Further, Ns has been calculated using Eq. (6): Here ΔH 1/2 is the full width at half maximum of the absorption peak. It is seen from Table 1 that initially the spin number increases with increasing ferromagnetic particle concentration. After reaching an optimum concentration, it shows a very small incongruous decrease. The aberrant decrease in the value of N S can be ascribed to a decrease in crystallization degree of the composite as the amount of Fe 3 O 4 nanoparticles exceeds a critical concentration resulting in the decrease of the spin number of Fe 3+46 . Another effect of increasing the ferromagnetic particle concentration in the composite is that the line shape changes from Lorentzian to pseudo-Voigt, which is intermediate between Gaussian and Lorentzian and then to a Gaussian line shape. One of the parameters that is indicative of the line shape is the ratio of the full width at half-height, ΔH 1/2 of the integrated spectrum to ΔH PP , ΔH 1/2 /ΔH PP, is 1.657 for a Lorentzian, 1.135 for pseudo-Voigt and 1.191 for a Gaussian line shape. Broader wings of the Lorentzian peak shape as compared to Gaussian peak shape pinpoint to a large number of magnetic spins in sample FZA as compared to sample FZC. This is in conformity with our results for Ns as shown in Table 1. Pseudo-Voigt line shape for sample FZC indicates an optimum balance between magneto-dipolar and exchange forces existing between magnetic moments. The spin resonance parameters suggest that the relationship of the concentration of the Fe 3 O 4 and magnetic and spin dynamic properties are very complex 35,36 . Although, the magnetic saturation is quite straightforward which increases sharply with an increase in Fe 3 O 4 concentration whereas the spin resonance parameters depend on the interaction among the constituents. FZB sample has a lower magnetic saturation value but has higher spin concentration resulting from the uniform distribution of the Fe 3 O 4 nanoparticles which does not affect the magnetic ions distributions, while sample FZC which has high saturation, has low spin concentration due to spin canting effect. The present investigation allows FZNC to be used more effectively in various spintronic and optoelectronic devices.

Conclusion
In conclusion, the room temperature spin dynamics in FZNC have been investigated in detail experimentally and the effect of Fe 3 O 4 concentration on the properties of FZNC has been established. SP Fe 3 O 4 nanoparticles were used as the seed to synthesize FZNC which are incorporated in the ZnO matrix occupying the grain boundaries. Fe 3 O 4 and ZnO are present in the composite as a separate phase which converges that the composite will show properties of both FN and ZnO. The grain boundary incorporation of magnetic nanoparticles is achieved by producing the uniform radial magnetic field which allows the formation of chain structure while in-situ growth of the ZnO nanoparticles. The incorporation of FN particles on the grain boundaries has been confirmed through TEM and SEM. Further, HRTEM and SAED have been taken on both sides of the interface in the FZNC to confirm the constituents of the composite.
The static magnetization curve of FZNC shows an SP behavior which further complements the electron microscopy results that both FN and ZP are present as a separate phase and FN is not incorporated in the matrix of ZnO. Further, single broad FMR spectra of the composite show that no Fe and Zn ions are present in the samples, and large spin-orbit coupling is observed at higher FN loading. T s of the samples also increases with an increase in FN loading and FMR spectra shape changes from Lorentzian to pseudo-Voigt. This is corroborated by the N s results, which show large values of N s for sample FZB rather than sample FZC due to balancing between magneto dipolar and exchange forces between magnetic moment. Large spin-orbit coupling in FZB samples can be achieved which is evident from the spin resonance parameters obtained for the samples. The present investigation depicts some unique and novel results as magnetic incorporation provides unique opportunity for the development of high-performance materials with the external control which unlocks the door for highly efficient devices.

Experimental
To investigate the crystalline phase purity, X-ray diffraction (XRD) measurement of as prepared FZNC, Fe 3 O 4 nanocrystals (FN), and ZnO particles (ZN) was performed using Rigaku Ultima -IV with Cu-Kα radiation (P = 3 kW, λ = 1.5406 Å). All the samples were scanned in the range 5° to 90° at 40 mV-40 mA at a step size 0.01 with a slow scan rate. Crystallite size and strain in the samples were calculated using the Williamson-Hall (W-H) method 47 . The morphology of the MNC samples was observed using SEM (Zeiss EVO MA-10 SEM) operating at 10 keV. Further, to analyze the nanocomposite formation and microstructural features, the TEM images at low and high resolution were obtained by JEOL JEM2100F operating at 200 kV. Also, the EDS spectrum and elemental mapping of the as-prepared nanocomposite samples were depicted using Jeol-JEM2100F standard attachment. The room temperature static dc magnetic measurement of the samples was performed using a vibrating sample magnetometer (VSM, Lake Shore 7304).
The microwave spin resonance investigation has been performed using Bruker EMX-10 spectrometer at room temperature using 100 kHz field modulation. The measurements were performed using X-band (9.85 GHz) microwave frequency, and a TM011 mode cavity. The distortion of the FMR spectra has been avoided by keeping the modulation amplitude less than or equal to one-third of the peak-to-peak linewidth. The FMR spectra were recorded at room temperature and various spin resonance parameters such as resonance field, Landé g-tensor, spin-spin relaxation time, and spin concentration were calculated. Further, these line spectra were fitted to the (6) N S = 9 4π 2 �H 1/2 gµ B