## Abstract

Magneto-optical effects are among the basic tools for characterization of magnetic materials. Although these effects are routinely calculated by the ab initio codes, there is very little knowledge about their origin in the electronic structure. Here, we analyze the magneto-optical effect in bcc Fe and show that it originates in avoided band-crossings due to the spin-orbit interaction. Therefore, only limited number of bands and *k*-points in the Brillouin zone contribute to the effect. Furthermore, these contributions always come in pairs with opposite sign but they do not cancel out due to different band curvatures providing different number of contributing reciprocal points. The magneto-optical transitions are classified by the dimensionality of the manifold that is formed by the hybridization of the generating bands as one- or two-dimensional, and by the position relative to the magnetization direction as parallel and perpendicular. The strongest magneto-optical signal is provided by two-dimensional parallel transitions.

### Similar content being viewed by others

## Introduction

The magneto-optical (MO) effects are routinely used for characterization of ferro-, ferri-, and antiferromagnetic materials. Magneto-optics can be employed as spectroscopy tool^{1,2,3,4}, microscopy tool^{5,6,7,8}, tool to investigate ultrafast magnetization dynamics^{9,10,11,12}, etc. The MO effects are used in many applications, such as holographic displays^{13,14,15}, optical isolators^{16,17,18} and photonic crystals^{19,20,21}.

In ferromagnets, the MO spectra are the result of simultaneous presence of the exchange and spin-orbit (SO) interactions and several theoretical models have been presented in the past^{22,23}. The first evaluation of magneto-optical spectrum of iron from first principles was performed by Singh et al.^{24} followed by Oppeneer et al.^{25} evaluating the Kerr rotation spectra of bcc Fe. The rise of the ab initio codes in recent decades have enabled to model the MO spectra for real materials^{26,27} and it has quickly become a common practice in research^{28,29,30,31,32,33}. The ab initio codes also opened up new possibilities in the investigations of the microscopic origins of the MO effect that go beyond the semiclassical models^{34,35}. They enable thorough *k*-resolved band-by-band analysis of the MO spectra that can significantly contribute to the understandning of the underlying mechanisms. The importance of a complete band structure analysis is emphasized by recent discoveries of large MO Kerr effect in antiferromagnets potentially connecting MO to Berry curvature effects^{36,37,38}.

In this manuscript, we thoroughly analyze the linear MO effect of bcc Fe and identify the origin of the MO signal in the band structure. We pinpoint the conditions and necessary features of the electronic structure leading to the MO response. Understanding of these features can lead to the enhancement and tuning of the various MO effects (e.g. Kerr effect, Faraday effect, magnetic circular dichroism) with the band structure engineering. The MO transitions are classified by their dimensionality and position in the Brillouin zone with respect to magnetization with each class manifesting differently in the spectra.

## Ab initio description

The electronic structure is calculated by the WIEN2k code^{39,40} with the bcc Fe lattice constant of 2.8665 Å^{41}, 729,000 *k*-points in the full Brillouin zone, and the local spin density approximation^{42}. The calculation is performed with the magnetization in the *z*-direction and with the spin-orbit interaction. The product of the smallest atomic sphere and the largest reciprocal space vector was set to \(R_{\mathrm{MT}}K_{\mathrm{max}}=8\) with the maximum value of the partial waves inside the spheres \(l_{\mathrm{max}}=10\). States up to 3*s* are treated as core states. Bands are labeled by an increasing energy eigenvalue starting with 3*p* states.

The linear MO response is described by the off-diagonal element of the permittivity tensor calculated by^{43,44} (SI units):

The imaginary part of the permittivity tensor is obtained by the Kramers–Kronig relations. The summations run over occupied (labeled *i* as initial states) and unoccupied states (*f* standing for final). \(E_{fi}=E_f-E_i\) is the energy difference between pair of bands. The integration runs over a surface of constant energy difference, \(E_{fi}(\mathbf {k})=E\), with *E* corresponding to the photon energy. The gradient is evaluated on the surface of constant energy difference.

## Off-diagonal permittivity spectra

Figure 1 shows the calculated MO spectra (off-diagonal permittivity) of bcc Fe compared to experiments^{1,2,25,32}. The dash-dotted black line is the direct result of evaluating Eq. (1) and the solid black line is obtained by Lorentzian broadening with \(\gamma =0.5\) eV which accounts for finite lifetimes of the excited states and finite temperature and allows for comparison with experiment. The permittivity is multiplied by energy and acquires the units of eV. Therefore, it resembles the conductivity spectrum due to the relation \(\varepsilon _{xy}=\frac{i\hbar }{\varepsilon _0 E}\sigma _{xy}\) in SI units. The agreement of the model with all experiments is solid in the entire energy interval.

In order to study the microscopic origin of the MO transitions, we define individual contributions \(\varepsilon ^{if}_{xy}\):

depicted in Fig. 2. Note that there are only several significant contributions.

In Fig. 3a the conventional band structure of bcc Fe is shown. Next, we define the joint band structure (Fig. 3b) that shows the energy difference of all pairs of bands over the same *k*-path with the condition that the upper band lies above the Fermi level and the lower band below it. The colors correspond to \({\text {Im}}[\langle i|p_x|f\rangle \langle f|p_y|i\rangle ]\) in Rydberg units for the respective pair of bands. Green color represents zero, thus no MO signal from the respective pair of bands in the respective *k*-point. Red (blue) color corresponds to the positive (negative) product of the momentum matrix elements and contributes negatively (positively) to the MO spectra due to the minus sign in Eq. (1). Strong transitions are labeled in the joint band structure and located in the conventional band structure.

Particular transition can be visualised directly in the Brillouin zone. The contribution to the permittivity is governed by \({\text {Im}}[\langle i|p_x|f\rangle \langle f|p_y|i\rangle ]\) which is integrated over a surface that is unique for a given pair of bands and a given energy (see Eq. (1)). As an example, we present this surface for transition 14 \(\rightarrow \) 17 at 2.23 eV in Fig. 4a, which corresponds to the maximal contribution to the permittivity tensor provided by this pair as shown in Fig. 2. This transition originates in a single point in the Brillouin zone denoted as C\(_\Sigma =(0, 0.319, 0.319)\) in the \(\Gamma \)-N direction and is repeated eight times due to symmetry. This transition is labeled j in Fig. 3.

## Magnetic quantum number

Electric dipole transitions are allowed only when certain conditions are met. Apart from the energy and momentum conservation (indirect transitions are not considered), the selection rules dictate the change of the angular momentum, \(\Delta j=\pm 1\). This can be observed in Fig. 3a as for every transition either initial or final band loses its almost pure *d*-character (the color gets lighter). The change in the magnetic quantum number, \(\Delta m=\pm 1\), then corresponds to the absorption of right or left circularly polarized light, their difference is the MO signal.

In Fig. 5, the band structure is shown with colors corresponding to the expectation value of the magnetic quantum number of the *d*-states. The magnetic quantum number gets polarized when bands approach each other and hybridize. An isolated band will always have its expectation magnetic number equal to zero. This comes from the perfect balance of substates with quantum numbers \(+m\) and \(-m\) for every real orbital. This balance is broken when two or more orbitals are mixed by the SO interaction^{46}.

All strong transitions originate in *k*-points where two *d*-bands energetically approach each other and hybridize by the SO interaction while simultaneously there is a suitable third band with partial *p*-character to enable the transition. Therefore, the strong MO transitions come from several isolated *k*-points in the Brillouin zone. These transitions also come in pairs with opposite signs and slight energy shift and thus tend to cancel each other out as observed in Fig. 2.

## Why the transitions do not cancel?

Transitions come in pairs with similar MO strength and opposite sign, but the spectrum is dominated by negative contributions. This is caused by the joint density of states (JDOS) that in the case of bcc Fe is generally larger for negative contributions. The JDOS can not be shown directly as it by definition also includes states that are optically forbidden.

Therefore, we define the MO-JDOS:

which corresponds to the number of *k*-points contributing to the MO transitions. In Fig. 6 only pairs of bands with large MO activity are shown. Note that negatively contributing transitions 13 \(\rightarrow \) 17 and 14 \(\rightarrow \) 17 have larger MO-JDOS than their positively contributing counterparts 13 \(\rightarrow \) 18 and 14 \(\rightarrow \) 18. Thus, transitions that contribute negatively to the MO spectrum have larger MO-JDOS most of the time resulting in overall negative spectrum of bcc Fe.

## Classification of magneto-optical transitions

### Dimensionality of the generating manifold

When two bands approach each other energetically, they hybridize due to the SO interaction. This hybridization polarizes magnetic quantum number and generates MO transitions. The hybridization of the generating bands can be tracked and used to localize *k*-points where maximal hybridization occurs. The set of such *k*-points forms locally a manifold which can be one-dimensional (1D) or two-dimensional (2D). The dimension of this manifold defines the dimensionality of the MO transitions involving these generating bands.

*1D transitions* When touching of two bands is split by the SO interaction, a suitable third band can induce 1D MO transitions into the split touching. An example would be transitions 11 \(\rightarrow \) 17 and 12 \(\rightarrow \) 17 labelled g in Fig. 3 that originate in hybridization of bands 11 and 12. In this case, both bands hybridize along \(\Gamma \)-H and diverge in all other directions. The line segment \(\Gamma \)-H is the 1D manifold generating this transition.

In Fig. 7a we present local MO spectra in the vicinity of C\(_{\Delta \parallel }=(0, 0, 0.7)\). It is a result of integration of the Kubo formula (Eq. (1)) in a cubic part of the Brillouin zone centered at C\(_{\Delta \parallel }\) with side length of 0.2 (sketched in the inset). The MO response is dominated by 1D transitions that originate from splitting of bands 11/12 and 14/15. Such transitions are typically weak in intensity and spread out in energy. In pairs, they tend to cancel out almost identically, therefore their contribution to the MO spectra is negligible. These transitions are marked by solid arrows in Fig. 3.

*2D transitions* When crossing of two bands is split by the SO interaction, a suitable third band can induce 2D MO transitions into the split crossing. An example would be transitions 14 \(\rightarrow \) 17 and 14 \(\rightarrow \) 18 labeled j in Fig. 3 that originate in the avoided crossing of bands 17 and 18 at C\(_\Sigma \). The surface generating this transition is shown in Fig. 4b and it is a collection of *k*-points where bands 17 and 18 maximally hybridize.

In Fig. 7b local MO spectrum in a cube centered at C\(_\Sigma \) is shown. In this part of the Brillouin zone, the MO response is dominated by 2D transitions originating in the splitting of bands 17/18 (and also of bands 16/17 which is also located in this cube as shown in Fig. 3; the vertical lines around point C\(_\Sigma \) indicate the edges of the cube). This cube is repeated eight times in the full Brillouin zone, therefore the contribution to the total spectrum coming from this part of the Brillouin zone will be eight times larger which practically covers all the strong peaks around 2–3 eV of the total spectrum. A typical 2D transition consists of two peaks in the MO spectra that are approximately equal in magnitude, have opposite signs and are shifted in energy preventing them from canceling each other. Such transitions exhibit large contributions to the MO spectra and are localized in energy. These transitions are marked by dashed arrows in Fig. 3.

### Position relative to the magnetization

The magnetization vector assumed in the *z*-direction lowers the symmetry of the cubic crystal by breaking the time-reversal symmetry. The band structure therefore slightly differs in directions parallel and perpendicular to the magnetization. Even such minor change can alter the MO contributions significantly.

The difference of the parallel and perpendicular contributions to the total MO spectrum is demonstrated in Figs. 7 and 8 with the parallel ones dominating in the entire spectral range. Bands that generate the transitions are split by SO and hybridize in the parallel direction while they remain degenerate in the perpendicular direction and are magneto-optically inactive.

## Conclusion

The origin of the magneto-optical effect in bcc Fe was thoroughly studied. The MO response originates in avoided band-crossings due to the SO interaction, therefore MO transitions come in pairs with opposite signs and tend to cancel each other. The extent of the cancellation is predominantly determined by the JDOS of the opposite transitions. In the case of Fe, JDOS is larger for negatively contributing transitions, resulting in overall negative spectrum.

The MO transitions have been classified by the dimensionality of the manifold that is formed by the hybridization of the generating bands as one- or two-dimensional, and by the position relative to the magnetization direction as parallel and perpendicular. The strongest signal to the MO spectra is provided by two-dimensional parallel transitions. We also present several possibilities of enhancing the MO signal (Fig. 9) by an appropriate band structure engineering.

## References

Krinchik, G. S. & Artemjev, V. A. Magneto-optic properties of nickel, iron, and cobalt.

*J. Appl. Phys.***39**, 1276–1278 (1968).Ferguson, P. E. & Romagnoli, R. J. Transverse Kerr magneto-optic effect and optical properties of transition-rare-earth alloys.

*J. Appl. Phys.***40**, 1236–1238 (1969).Silber, R.

*et al.*Scaling of quadratic and linear magneto-optic Kerr effect spectra with L2\(_1\) ordering of Co\(_2\)MnSi Heusler compound.*Appl. Phys. Lett.***116**, 262401 (2020).Ješko, R.

*et al.*Spectral permittivity tensor and density functional theory calculations on the Heusler compound Co\(_2\)FeAl\(_{0.5}\)Si\(_{0.5}\).*Phys. Rev. B***103**, 075146 (2021).McCord, J. Progress in magnetic domain observation by advanced magneto-optical microscopy.

*J. Phys. D Appl. Phys.***48**, 333001 (2015).Urs, N. O.

*et al.*Advanced magneto-optical microscopy: Imaging from picoseconds to centimeters - imaging spin waves and temperature distributions (invited).*AIP Adv.***6**, 055605 (2016).Liu, C., Zhang, X. & Zhou, Y.-H. A novel design for magneto-optical microscopy and its calibration.

*Meas. Sci. Technol.***30**, 115904 (2019).Kim, D.

*et al.*Extreme anti-reflection enhanced magneto-optic Kerr effect microscopy.*Nat. Commun.***11**, 5937 (2020).Huisman, T. J., Mikhaylovskiy, R. V., Tsukamoto, A., Rasing, T. & Kimel, A. V. Simultaneous measurements of terahertz emission and magneto-optical Kerr effect for resolving ultrafast laser-induced demagnetization dynamics.

*Phys. Rev. B***92**, 104419 (2015).Wieczorek, J.

*et al.*Separation of ultrafast spin currents and spin-flip scattering in Co/Cu(001) driven by femtosecond laser excitation employing the complex magneto-optical Kerr effect.*Phys. Rev. B***92**, 174410 (2015).Razdolski, I.

*et al.*Analysis of the time-resolved magneto-optical Kerr effect for ultrafast magnetization dynamics in ferromagnetic thin films.*J. Phys. Condens. Matter***29**, 174002 (2017).Wang, C. & Liu, Y. Ultrafast optical manipulation of magnetic order in ferromagnetic materials.

*Nano Converg.***7**, 35 (2020).Takagi, H., Nakamura, K., Goto, T., Lim, P. B. & Inoue, M. Magneto-optic spatial light modulator with submicron-size magnetic pixels for wide-viewing-angle holographic displays.

*Opt. Lett.***39**, 3344–3347 (2014).Aoshima, K.

*et al.*A magneto-optical spatial light modulator driven by spin transfer switching for 3D holography applications.*J. Display Technol.***11**, 129–135 (2015).Shirakashi, Z.

*et al.*Reconstruction of non-error magnetic hologram data by magnetic assist recording.*Sci. Rep.***7**, 12835 (2017).Shoji, Y., Mizumoto, T., Yokoi, H., Hsieh, I.-W. & Osgood, R. M. Magneto-optical isolator with silicon waveguides fabricated by direct bonding.

*Appl. Phys. Lett.***92**, 071117 (2008).Stadler, B. J. H. & Mizumoto, T. Integrated magneto-optical materials and isolators: A review.

*IEEE Photonics J.***6**, 1–15 (2014).Yan, W.

*et al.*Waveguide-integrated high-performance magneto-optical isolators and circulators on silicon nitride platforms.*Optica***7**, 1555–1562 (2020).Otmani, H.

*et al.*Magneto-optical properties of magnetic photonic crystal fiber of terbium gallium garnet filled with magnetic fluid.*Photonics Nanostruct. Fundam. Appl.***22**, 24–28 (2016).Pourali, N. & Bahador, H. Tunable magneto-optical responses in a photonic crystal containing two plasma defect layers.

*Phys. Plasmas***26**, 013515 (2019).Grishin, A. M. & Khartsev, S. I. Waveguiding in all-garnet heteroepitaxial magneto-optical photonic crystals.

*JETP Lett.***109**, 83–86 (2019).Wittekoek, S., Popma, T. J. A., Robertson, J. M. & Bongers, P. F. Magneto-optic spectra and the dielectric tensor elements of bismuth-substituted iron garnets at photon energies between 2.2–5.2 eV.

*Phys. Rev. B***12**, 2777–2788 (1975).Bruno, P., Suzuki, Y. & Chappert, C. Magneto-optical Kerr effect in a paramagnetic overlayer on a ferromagnetic substrate: A spin-polarized quantum size effect.

*Phys. Rev. B***53**, 9214–9220 (1996).Singh, M., Wang, C. S. & Callaway, J. Spin-orbit coupling, Fermi surface, and optical conductivity of ferromagnetic iron.

*Phys. Rev. B***11**, 287–294 (1975).Oppeneer, P. M., Maurer, T., Sticht, J. & Kübler, J. Ab initio calculated magneto-optical Kerr effect of ferromagnetic metals: Fe and Ni.

*Phys. Rev. B***45**, 10924–10933 (1992).Uspenskii, Y., Kulatov, E. & Halilov, S. Ab initio studies of optical and magneto-optical spectra in 3d- and 4f-atom-based compounds.

*Phys. A Stat. Mech. Appl.***241**, 89–93 (1997) (**Proceedings of the Fourth International Conference on Electrical Transport and Optical Properties of Inhomogeneoous Media**).Kunes, J. & Oppeneer, P. Ab Initio calculations of magneto-optical effects.

*Trans. Magn. Soc. Japan***2**, 141–146 (2002).Rosa, P., Sangalli, D., Onida, G. & Debernardi, A. Ab initio electronic structure, optical, and magneto-optical properties of MnGaAs digital ferromagnetic heterostructures.

*Phys. Rev. B***91**, 075207 (2015).Merikhi, R., Bennecer, B. & Hamidani, A. Magneto-optical Kerr effect in ZnTMO\(_2\) (TM=Cr, Mn, Fe, Co and Ni).

*J. Magn. Magn. Mater.***424**, 327–338 (2017).Thiering, G. & Gali, A. Ab Initio magneto-optical spectrum of group-IV vacancy color centers in diamond.

*Phys. Rev. X***8**, 021063 (2018).Wimmer, S., Mankovsky, S., Minár, J., Yaresko, A. N. & Ebert, H. Magneto-optic and transverse-transport properties of noncollinear antiferromagnets.

*Phys. Rev. B***100**, 214429 (2019).Silber, R.

*et al.*Quadratic magneto-optic Kerr effect spectroscopy of Fe epitaxial films on MgO(001) substrates.*Phys. Rev. B***100**, 064403 (2019).Graulich, D.

*et al.*Quantitative comparison of the magnetic proximity effect in Pt detected by XRMR and XMCD.*Appl. Phys. Lett.***118**, 012407 (2021).Uba, L., Uba, S., Germash, L. P., Bekenov, L. V. & Antonov, V. N. Electronic structure and magneto-optical spectra of La\(_x\)Sr\(_{1-x}\)MnO\(_{3}\) perovskites: Theory and experiment.

*Phys. Rev. B***85**, 125124 (2012).Uba, S.

*et al.*Electronic structure and magneto-optical Kerr effect spectra of ferromagnetic shape-memory Ni–Mn–Ga alloys: Experiment and density functional theory calculations.*Phys. Rev. B***94**, 054427 (2016).Kargarian, M., Randeria, M. & Trivedi, N. Theory of Kerr and Faraday rotations and linear dichroism in topological Weyl semimetals.

*Sci. Rep.***5**, 12683 (2015).Liu, J. & Balents, L. Anomalous Hall effect and topological defects in antiferromagnetic Weyl semimetals: Mn\(_3\)Sn/Ge.

*Phys. Rev. Lett.***119**, 087202 (2017).Yang, H.

*et al.*Topological Weyl semimetals in the chiral antiferromagnetic materials Mn\(_3\)Ge and Mn\(_3\)Sn.*New J. Phys.***19**, 015008 (2017).Blaha, P., Schwarz, K., Madsen, G. K. H., Kvasnicka, D. & Luitz, J.

*WIEN2K, An Augmented Plane Wave + Local Orbitals Program for Calculating Crystal Properties (Karlheinz Schwarz)*(Techn. Universität, Wien, 2001).Ambrosch-Draxl, C. & Sofo, J. O. Linear optical properties of solids within the full-potential linearized augmented planewave method.

*Comput. Phys. Commun.***175**, 1–14 (2006).Wang, H., Ma, P.-W. & Woo, C. H. Exchange interaction function for spin-lattice coupling in bcc iron.

*Phys. Rev. B***82**, 144304 (2010).Perdew, J. P. & Wang, Y. Accurate and simple analytic representation of the electron-gas correlation energy.

*Phys. Rev. B***45**, 13244–13249 (1992).Kubo, R. Statistical-mechanical theory of irreversible processes. I. General theory and simple applications to magnetic and conduction problems.

*J. Phys. Soc. Japan***12**, 570–586 (1957).Callaway, J.

*Quantum Theory of the Solid State*2nd edn. (Academic Press, San Diego, 1991).Yao, Y.

*et al.*First principles calculation of anomalous Hall conductivity in ferromagnetic bcc Fe.*Phys. Rev. Lett.***92**, 037204 (2004).Stöhr, J. & Siegmann, H.

*Magnetism: From Fundamentals to Nanoscale Dynamics (Springer Series in Solid-State Sciences)*(Springer, Heidelberg, 2006).

## Acknowledgements

This work was supported by the Czech Science Foundation (GACR), Grant No. GA19-13310S and by the European Union project Matfun, Project No. CZ.02.1.01/0.0/0.0/15_003/0000487.

## Author information

### Authors and Affiliations

### Contributions

O.S. performed the calculations; M.V. and J.H. contributed to the interpretation of the results and to the underlying theory. All authors read and commented the manuscript.

### Corresponding author

## Ethics declarations

### Competing interests

The authors declare no competing interests.

## Additional information

### Publisher's note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## Rights and permissions

**Open Access** This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

## About this article

### Cite this article

Stejskal, O., Veis, M. & Hamrle, J. Band structure analysis of the magneto-optical effect in bcc Fe.
*Sci Rep* **11**, 21026 (2021). https://doi.org/10.1038/s41598-021-00478-1

Received:

Accepted:

Published:

DOI: https://doi.org/10.1038/s41598-021-00478-1

## Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.