Ultraviolet protection of Bacillus thuringiensis through microencapsulation with Pickering emulsion method

An encapsulated formulation of Bacillus thuringiensis (Bt) was produced by the Pickering emulsion technique to improve its activity and stability under UV-A radiation. In this technique latex particles, GO nanosheets, olive oil, ethanol, and water were used to encapsulate Bt in colloidosomes. The protective efficacy of this formulation in protecting Bt subsp. Kurstaki against deactivation by UV-A irradiation was measured, so that spore viability and mortality on Ephestia kuehniella (E. kuehniella) Zeller larvae under UV-A radiation are investigated. According to the results of both tests, encapsulated formulation at a concentration of 0.045% has the highest protection of viability. Hence, colloidosome microcapsule formulations successfully provide good protection against UV radiation.


Scientific Reports
| (2020) 10:20633 | https://doi.org/10.1038/s41598-020-77721-8 www.nature.com/scientificreports/ materials. Herein, among various materials and techniques that have been developed to fabricate colloidosomes, we report pH-responsive colloidosomes containing Bt crystals that were formed by Pickering emulsions and stabilized by GO nanosheets. The four advantages of these microcapsules include, the release of Bt crystals in the midgut of lepidopteran larvae, especially when pH > 8; formation of aqueous formulation which could be dispersed in water; prevention of light-induced damage of the Bt spore; and maintaining the bioactivity of Bt. The present work is aimed to evaluate the toxicity of the Bt on Ephestia kuehienlla (E. kuehniella) Zeller larvae through bioassay. The main objective was the development of biological agents to improve the protective effect of the GO nanosheets on the stability of formulations exposed to UV radiation. Therefore, the spore viability and the crystal activity of encapsulated formulations were measured.

Results
Structure and properties of GO. The XRD pattern of GO presented in Fig. 1 illustrates a sharp diffraction peak located at 2θ = 12.02°. The interlayer spacing of GO is 0.73 nm, which is more than the interlayer spacing of graphite (0.33 nm). Graphite has a sharp diffraction peak at 26.34°. The evidence confirms that oxygen-containing functional groups had been introduced to layers and successful oxidation of graphite into GO. An increased interlayer distance might be due to the formation of oxygen-containing functional groups, such as carboxyl, hydroxyl, and epoxy. The results of XRD proved the successful synthesis of the GO sheets by oxidizing graphite. The FESEM image of surface GO nanosheets is shown in Fig. 2. It was found that GO nanosheets consist of crumpled thin sheets and a wrinkled structure with an irregular surface. This result confirms the two-dimensional nanosheets of GO.
The chemical structure of GO nanosheets was investigated by FT-IR and the characteristic FTIR spectrum of GO nanosheets is depicted in Fig. 3. The characteristic peaks of 1054, 1393, 1634, 1706 and 3445 cm −1 corresponding to C-O, C-OH, C=C, C=O and O-H stretching vibrations, respectively confirm the formation of GO.
Preparation of the microcapsule. An emulsion polymerization process was applied for the preparation of colloidosomal microcapsules by a pH-sensitive latex of poly(methyl methacrylate-co-methacrylic acid). According to the DLS measurements, the average diameter of the polymer latex particles was 54.5 nm (Fig. 4). As shown in Fig. 4, the graph shows a narrow distribution range. Also, polymer latex particles before the formation of colloidosomal microcapsules and after their formation were characterized by optical microscopy (Fig. 5a,b). The water-core emulsions were found to have a hollow structure. Figure 6a shows the FESEM images of a mixture of Bt and polymer latex particles. Figure 6b reveals the FESEM images of colloidosomal microcapsules containing the encapsulated Bt. These results indicate the hollow structure of latex particles and that the aggregation of the latex particles causes the stabilization of the water-core colloidosomes. The water-core emulsions are stabilized by interfacial nanosheets. These nanosheets could stabilize the emulsion in the colloidal sense. They eventually lead to phase separation with the prevention of water droplets fusion. Figure 7 shows the AFM image of colloidosomal microcapsules containing the encapsulated Bt. R ms and R a values were obtained as 135.7 and 96.91 nm, respectively. As shown in Fig. 8, TEM image shows two different nanostructures that confirm the presence of GO nanosheets and polymer latex in the microcapsule.   Fig. 9, increasing GO nanosheets concentration in microencapsulated formulations from 0.009 to 0.045% w/v resulted in increased spore viability, while increasing the GO concentration up to 0.09% reduced it. However, this value generally fell for all formulations after 120 h UV-A exposure. During each exposure time, the Bt encapsulated formulations of 0.045% GO nanosheets were significantly higher than non-protected Bt formulation after UV-A exposure. So, this formulation provided the most photostable formulations.
The effect of UV-A on the Bt encapsulated formulation of GO nanosheets with different concentrations for 96 h was compared and the results are shown in Table 1. There were significant differences between all of irradiated Bt encapsulated and irradiated non-protected formulations, while there was no significant difference between 0.009% w/v GO formulation with 0.018% w/v GO formulation (p = 0.001). According to the obtained results of spore viability, among the four formulations of protected Bt, encapsulated formulation at a concentration of 0.045% has the highest protection of viability.  www.nature.com/scientificreports/ Assessment of bioassay. Figure 10 shows the trend of mortality obtained in the laboratory for encapsulated Bt formulations with different concentrations of GO nanosheets during evaluated exposure times. Mortality evaluation against E. kuehniella larvae after 96 h of exposure to UV-A radiation showed that this factor declined to 58.12, 60.66, 70.68, 56.38, and 38.20% for the encapsulated formulations of Bt at different concentration of 0.009, 0.018, 0.045, 0.090% w/v of GO, and free spore, respectively. This is proportional to encapsulation efficacy of 51.68%, 54.61%, 66.17%, 49.67%, and 28.70%, respectively. According to the results of Table 1, there are significant differences between the four Bt formulations at p = 0.05. GO nanosheets at 0.045% w/v in Bt encapsulated formulation as a UV-protectants offered the highest UV protection.

Discussion
The microencapsulated formulations of Bt were prepared by the Pickering emulsion technique using poly(methyl methacrylate-co-methacrylic acid) as latex particles. The reasons for choosing this polymer as the main constituent of colloidosomal microcapsules include:    NaCl was added to the aqueous phase to stabilize the emulsion against Ostwald ripening. GO nanosheets were added to the oil phase as a protective agent against UV. The UV absorption of GO has been shown by our previous researches 20 . Although the antibacterial activity of GO has been confirmed in some studies, the size of the nanosheets has been identified as an influencing factor on their antibacterial property. Therefore, larger GO nanosheets can display stronger antibacterial activity as compared to small GO nanosheets 21 . Olive oil was used in making the oil phase. A water/oil emulsion was obtained by mixing two phases. The mixing order was known as one of the main factors. Adding ethanol directly to the aqueous phase leads to aggregation of the latex before forming the shell. These results showed that the role of ethanol was to irreversibly fix the shell of the water-core emulsions and to stabilize the water-core emulsions. Therefore, using ethanol in the oil phase allowed the correct staging of events and successful colloidosome formation at low temperatures. This method does not involve high temperatures which is a necessary factor to maintain Bt bioactivity. Therefore, it is compatible with Table 1. The spore viability%, larval mortality%, and spore count for the microencapsulated formulation of at different concentrations of GO against UV-A. The bioassay carried out on E. kuehniella. Note The data are mean ± SE. Means within the same column, followed by a different letter are significant at p < 0.05, Duncan test. Spore count for treatments was carried out using three replicates. F = 153.214, df = 9, p = 0.0001. Mean is the average of three replicates 45 larvae per in treatment, F = 3069.403, df = 10, p = 0.0001.

Treatment
Spore viability % Larval Mortality % cfu (10 8 spores/mL)   8 . In our previous study, we showed the highest mortality of irradiated combination formulation of GO/olive oil on second-instar larvae E. Kuehniella was 68.89% 20 . In this study, the same parameter for 96 h Irradiation of 0.045% GO encapsulated is 70.68%. Based on our previous study which showed that GO was a UV absorbent, during this study we checked their ability as a photo protectant after exposure to UV-A by the spore viability and mortality. Also, both experiments illustrated that the microencapsulation process confers extended bioactivity of Bt and that the microencapsulated Bt formulations are significantly more efficient than the free spore of Bt. Furthermore, the analysis of the results shows that the colloidosomal encapsulated formulations could be a promising and effective strategy for the extension of eco-friendly Bt insecticide.

Synthesis of poly(methyl methacrylate-co-methacrylic acid) as latex particles. 50 mL deion-
ized water (DI), 10.65 g of methyl methacrylate, 4.24 g methacrylic acid, 0.20 g of sodium dodecyl sulfate as a stabilizer, and 0.12 g of ammonium persulfate as initiator were transferred to a 250 mL balloon flask and mixed and stirred at 350 rpm and degassed by bubbling nitrogen for 30 min. Then, the mixture was heated to 80 °C under a nitrogen blanket to avoid O 2 introduction. After 10 h a latex was obtained. The particles were easily soluble in an alkaline environment (pH = 8).
Synthesis of GO nanosheets. GO was synthesized according to a modified Hummer's method. Briefly, 5.0 g of graphite powder, 115 mL of H 2 SO 4 , and 2.5 g of NaNO 3 were added to a flask in an ice bath under vigorous stirring condition for 30 min. Then, it was followed by the slow addition of 15.0 g of KMnO 4 for 2 h while maintaining the temperature at 35 °C. The reaction mixture was cooled to room temperature and 230 mL of DI water was added slowly to the solution. Eventually, the reaction was terminated by slowly adding 700 mL DI water and 30 mL H 2 O 2 . The final suspension turned bright yellow and was washed several times with HCl (3%, 80 mL) to remove the unreacted materials and then with DI water until neutrality. A homogenizer (Hielscher, UP400St, 20 kHz, 400 W, Germany) was used to the suspension in water laminated into GO nanosheets. Finally, the GO nanosheets were obtained in the form of a grey powder after freeze-drying 25 for 72 h. loidosomes was as follows (Fig. 11). In a glass vial, 2 mL of ethanol was vortexed with 20 mL of commercial olive oil and 0.01 g of GO nanosheets for 1 min. In a separate glass vial, 1 g of dry powder of Bt kurstaki strain was added to 5 mL of the synthesized latex. Then, 5 mL of DI water containing 146 mg of NaCl was added and then vigorously vortexed for 1 min. After air bubbles disappeared from the mixture, the contents of both vials were added together. To form a stable emulsion, immediately the homogenization process of the mixture was performed with a vortex mixer for 1 min. The resulting colloidosomes were collected by repeated centrifugation at 4000 rpm, which separates colloidosomal microcapsules from the oil phase. Centrifugation was continued until no oil remained above the surface of the microcapsules.
Characterization. X-ray diffraction (XRD) patterns were recorded on a Phillips X'Pert PRO (Panalytical, Netherlands) using filtered Cu Kα radiation (λ = 1.5417 Å) in the range of 2θ = 10°-80°. The morphology was investigated by scanning electron microscopy (FE-SEM, Sigma, Zeiss). For AFM analysis, dilution of different samples of each material was performed with water. A drop of the diluted suspension containing the microcapsules and some samples were placed on a lam and was allowed to dry in air. The plate was analyzed on a Veeco (Bruker/Veeco, Icon, USA). Tapping mode AFM was used for all images at 25 °C and analyzed with the Proscan software. The topography of materials was evaluated with AFM. Average roughness (R a ) and root-meansquare (Rms) values were obtained for different samples. Transmission electron microscope (TEM) images were obtained by a LEO 912 AB transmission electron microscope (Zeiss, Germany).
Ultraviolet resistance of encapsulated Bt formulations. The diluted encapsulated Bt formulation and nonprotected formulation of Bt with 10 8 CFU mL −1 as a control, were exposed to UV-A radiation in an open Petri dish at the same height and at 15 cm distance from the lamp (Philips, 15 W, white light 385 nm peak emission). To replace the water lost by evaporation; the volume of each sample was adjusted with sterile DI water before the determination of spore count. These formulations at different concentrations of GO (0.009, 0.018, 0.045, and 0.090%w/v) were subjected to UV-A treatment up to 120 h. The microcapsules were dissolved in a sodium hydroxide (pH = 8.5). Next, the released microcapsules were assessed for spore viability. The spore count of the samples was carried out by serial dilution with a nutrient agar medium (CFU). The percentage of spore viability was calculated by Eq. (1): where cfu rad is the count of the irradiated spores (protected or nonprotected formulation), and cfu 0 is the count of the initial non-irradiated spores (protected or nonprotected formulation. All the experiments were performed in triplicate and repeated on three different days. Bioassay procedures. Bioassays were carried out using second instars larvae of E. kuehniella Zeller. The larvae were reared using a mixture consisting of 1 kg flour and 0.5 kg of wheat bran as the nutrition source at 28 °C with 65% relative humidity. Fifteen larvae were selected and placed in a Petri dish, then 5 peanuts were immersed in various formulations as larval food, and dried for 5 min then added to Petri dishes. All procedures were performed under sterile conditions. These were incubated at 28 °C and 60% humidity. The percentage of mortality of larvae was recorded for all encapsulated formulations and compared to the control for 10 days. Each treatment was carried out in triplicate. The percentage of encapsulation efficacy was calculated by the Schneider Orelli equation (Eq. 2) where X is larval mortality percentage obtained in the treatment and Y is the mortality percentage in the negative control treatment (without Bt treatment).
(1) Spore viability (%) = cfu rad cfu 0 × 100 www.nature.com/scientificreports/ Statistical analysis. All results related to the determination of CFU counts, spore viability, and bioassays were the average of three replicates of three separate experiments. They were statistically analyzed by Statistical Package for the Social Sciences (SPSS) using the Duncan test performed after analysis of variance (ANOVA).
Scientific Reports | (2020) 10:20633 | https://doi.org/10.1038/s41598-020-77721-8 www.nature.com/scientificreports/ Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creat iveco mmons .org/licen ses/by/4.0/.