Deep eutectic solvents for solid pesticide dosage forms

Deep eutectic solvents aid the formulation of solid pesticide dosage forms for water-insoluble actives. This was demonstrated by encapsulating Amitraz powder in a low-melting matrix based on the eutectic mixture of urea (32 wt%) and 1,3-dimethylurea. Dissolution in water of melt-cast discs, containing 20 wt% active, led to the rapid release of Amitraz in a finely dispersed form. The order of magnitude reduction in particle size, after dissolution, is ascribed to the solubilization of Amitraz in the hot deep eutectic solvent and its subsequent precipitation as a separate phase on crystallization of the matrix.


Scientific Reports
| (2020) 10:20729 | https://doi.org/10.1038/s41598-020-77559-0 www.nature.com/scientificreports/ the diffractogram obtained for the eutectic composition. In addition, the latter features three new low-intensity reflections at 2θ = 22.5°, 25° and 30°. This may indicate that a minor amount of co-crystallization of urea and 1,3-dimethylurea occurred, most likely at the grain boundaries where the growing pure component crystals impinged on one another. Figure 4 shows the dissolution results for both small and large discs of the neat eutectic as well as of the formulation that contained 20 wt% Amitraz. The data trends were consistent with the Hixson-Crowell cube root law 9 where M o is the initial mass; M(t) is the mass remaining after time t, and τ is a characteristic time constant indicative of the time required for complete dissolution. Surprisingly, the dissolution time τ was unaffected by the disc diameter but it was shorter when Amitraz was present (τ = 6.56 min; 95% confidence interval (6.38, 6.78)) compared to the neat eutectic system (τ = 4.65 min; 95% confidence interval (4.55, 4.75)). The disc thickness was the  www.nature.com/scientificreports/ same in both cases and the aspect ratios were relatively large (11 and 20). Therefore, the diameter-independent dissolution time probably indicates that the large exposed circular surface controlled the dissolution rate with the much smaller surface area of the disc edges playing a minor role.

Dissolution in water.
Particle size distributions. Figure 5 compares the particle size distributions of the aqueous Amitraz dispersions with that of the original neat powder. The D 10 , D 50 and D 90 particle sizes are listed in Table 1. The key finding is an almost order-of-magnitude reduction in the Amitraz particle size as released from the solid dosage system. The D 50 particle size of the neat Amitraz powder was 240 ± 10 µm. After dissolution of the solid dosage form, the D 50 particle size of the Amitraz dispersion was less than 30 µm.

Discussion
There are two possible explanations for the observed results. The large particles indicated by the particle size distribution results could in fact have been agglomerates of much smaller constituent particles. It could then be, that the processing that happened during the preparation of the Amitraz-filled eutectic effected their dispersion as free individual particles. Solubilization of the Amitraz by the molten deep eutectic solvent presents a second alternative explanation. In this scenario, phase separation occurred during cooling of the homogeneous solution on or before solidification. This resulted in the formation of small Amitraz domains that solidified as separate, much smaller particles trapped inside the eutectic matrix. These were subsequently released during the dissolution process.
Both SEM results and DSC information favor the second interpretation. Figure 1b shows that the eutectic, filled with 20 wt% Amitraz, featured only one major endotherm. It is located at a slightly lower temperature range than the one observed for the urea-1,3-dimethylurea eutectic. This, and the absence of a second endotherm closer to the melting point of the Amitraz indicates that the active did indeed dissolve in the deep eutectic solvent. This led to a further lowering of the melting point of the eutectic. Finally, the SEM micrograph, shown as an insert in Fig. 5, shows that the neat Amitraz powder consisted of monolithic particles exceeding 100 μm in size. This means that, although the neat Amitraz particles might have been partially agglomerated and difficult to disperse, the actual particles released on dissolution must have derived from a recrystallization from the deep eutectic solvent.

Conclusions
Nonionic deep eutectic solvents show potential as matrix materials useful for formulating rapid release dosage forms for water-insoluble pesticides. Advantages include low temperature (< 100 °C) processing and mixing of the ingredients; the possibility of direct casting of the required tablet shapes by pouring the molten mixture into the plastic packaging containers used for storage and transport; rapid release in water media via dissolution of the matrix; the automatic generation of a finely dispersed forms of the active through the process of melting the deep eutectic solvent, the dissolution of the active and its phase separation on cooling and solidification of the eutectic. This implies that fine grinding of the actives might not be necessary. The above features were exemplified using the acaricide Amitraz incorporated into the urea-1,3-dimethylurea eutectic.

Differential scanning calorimetry (DSC).
The melting endotherms of the raw materials and the urea-1,3-dimethylurea eutectic, in neat form as well as filled with the acaricide, were determined by differential scanning calorimetry using a PerkinElmer Pyris 6 DSC. Samples weighing 12 ± 3 mg were sealed in aluminum pans with pinhole lids. The temperature was twice cycled from 20 °C to 140 °C and back. The heating rate was 10 K min −1 with nitrogen flowing at 20 mL min −1 . Only the melting events recorded in the second heating cycle are reported here. The temperature calibration of the DSC instrument was checked using an indium standard.
Cooling curves. Cooling curves were generated in order to identify the eutectic composition. The procedure was as follows: Predetermined quantities of urea and 1,3-dimethylurea were weighed into a test tube. The test tube was partially submerged in silicon oil contained in a beaker placed on a heater-stirrer. The contents were heated until the test tube contents were fully molten. The molten mixture was agitated with a glass rod to ensure complete homogenization of the contents. After the heater-stirrer was switched off, the change in temperature with time was tracked with a Hairuis Model SSN-61 temperature data logger. Care was taken that the thermocouple inserted into the test tube did not touch the glass walls. In most cases, sub-cooling occurred as indicated by a sudden rise in the temperature when freezing commenced. The peak temperature measured, following this event, was taken to correspond to the equilibrium crystallization temperature for the corresponding composition. Duplicate runs were conducted for each composition considered.
X-ray diffraction. Samples of urea and 1,3-dimethylurea as well as the eutectic mixture were pulverized with a mortar and pestle. The powder samples were stored over silica gel absorbent in a desiccator for at least 12 h before analyses. Near randomly oriented samples were prepared by means of the PANalytical backloading system. X-ray powder diffraction data was obtained on a PANalytical X'Pert Pro diffractometer in the θ-θ configuration using an X'Celerator detector with variable divergence-and fixed receiving slits. Fe-filtered Co Kα radiation (λ = 1.789 Å) was used.
Preparation of solid dosage forms. The deep eutectic solvent was prepared by heating powder mixtures of urea and 1,3-dimethyl urea, corresponding to the eutectic composition, for approximately 1 h in an oven set at a temperature of 70 °C. The Amitraz solid dosage form was obtained by dissolving the acaricide in the hot solvent. Test discs for the dissolution experiments were cast by pouring the prepared solutions into two differentsized polypropylene cups. These served as the molds that facilitated the casting of discs with different diameters (55 mm ϕ and 100 mm ϕ) but with identical thicknesses (5.0 mm). Predetermined quantities of the homogeneous liquids were poured into the molds and allowed to cool and solidify over a period of 1 h in a refrigerator set at a temperature of 2 °C. The castings were removed from the molds and stored in an airtight container. Casts were made using the neat eutectic composition as is, and also with the Amitraz pesticide powder mixed-in at a ratio of 1:4 by mass.
Dissolution trials. The dissolution of the discs was tracked gravimetrically. Duplicate determinations were made according to the following procedure. Prior to each experiment, the discs were weighed using a Radwag PS 360/C/2 laboratory scale. They were then placed in a 2 L beaker filled with 1 L of deionized water, which was agitated with an overhead WiseStir HS-120A stirrer set to 200 rpm. The discs were temporarily removed and weighed at regular intervals.
Particle size analysis. Particle size analysis was conducted on a Malvern Mastersizer 3000. The wet dispersion of the solid powders for particle size analysis was controlled with a Malvern LV Hydro. The ultrasound setting was 20% and the shear mixer was set at 3500 rpm. The reported values represent averages of five measurements. The particle size distributions of the neat Amitraz powder and the dispersions obtained after the completion of the dissolution experiments were determined.
Scanning electron microscopy (SEM). Amitraz powder was sputter coated with chromium and viewed using a Zeiss Supra 55 FEGSEM at 5 kV. The purpose was to determine the fundamental size of the individual particles.
Consent for publication. All authors have given their consent for the submission of the manuscript.

Data availability
The authors are willing to share the data in Excel format with interested parties.