Abstract
Polycrystalline Lead Oxide (poly-PbO) was considered one of the most promising photoconductors for the direct conversion X-ray medical imaging detectors due to its previous success in optical imaging, i.e., as an optical target in so-called Plumbicon video pick-up tubes. However, a signal lag which accompanies X-ray excitation, makes poly-PbO inapplicable as an X-ray-to-charge transducer in real-time X-ray imaging. In contrast, the recently synthesized Amorphous Lead Oxide (a-PbO) photoconductor is essentially lag-free. Here, we report on our approach to a PbO detector where a thin layer of a-PbO is combined with a thick layer of poly-PbO for lag-free operation. In the presented a-PbO/poly-PbO bilayer structure, the poly-PbO layer serves as an X-ray-to-charge transducer while the a-PbO acts as a lag prevention layer. The hole mobility in the a-PbO/poly-PbO bilayer structure was measured by photo-Charge Extraction by Linearly Increasing Voltage technique at different temperatures and electric fields to investigate charge transport properties. It was found that the hole mobility is similar to that in a-Se—currently the only commercially viable photoconductor for the direct conversion X-ray detectors. Evaluation of the X-ray temporal performance demonstrated complete suppression of signal lag, allowing operation of the a-PbO/poly-PbO detector in real-time imaging.
Similar content being viewed by others
Introduction
Direct conversion detectors opened a new era in X-ray medical imaging because of the number of advantages intrinsic to the direct conversion scheme, such as spatial resolution that is limited only by the pixel dimensions and high dose efficiency even at low radiation exposure.
In the direct conversion method, incident X-rays are absorbed in a layer of photoconductor that directly generates electron–hole pairs, which are afterwards separated by an electric field to produce an electrical signal. The photogenerated electrons and holes drift towards the opposite electrodes, making it possible to create an image with a thick detector layer while maintaining high spatial resolution. The first commercial mammographic direct conversion detectors based on amorphous selenium (a-Se) photoconductor to directly convert incident X-rays to charge, which is subsequently electronically read out by a two-dimensional array of a-Si:H thin film transistors (TFTs), made a breakthrough in the breast imaging field due to the excellent detectability of small breast lesions1.
Currently, the only commercially feasible photoconductor for X-ray imaging is a-Se, which limits the extensive use of the direct conversion scheme. Indeed, a-Se has a low atomic number Z, and thus, is efficient only when low-energy X-rays are used, e.g., in mammography. To expand the benefits of direct conversion detectors over the diagnostic energy range, i.e., in radiography and fluoroscopy, a-Se must be substituted by a high-Z material, which can efficiently absorb higher energy X-rays.
Since X-ray imaging detectors should normally have a large active area (one cannot converge X-rays), single crystalline photoconductors are ruled out from the application in direct conversion detectors in conjunction with large area a-Si:H flat panel technology (i.e., active matrix flat panel imagers or AMFPIs). Thus, it is imperative to focus on amorphous and polycrystalline phases of high-Z photoconductors, that can be directly deposited on an imaging array of a large area. Potential X-ray photoconductors such as polycrystalline layers of BiI32, PbI23,4, HgI25,6,7, ZnO8, CdTe9, Cd1−xZnxTe10, and PbO11 have been investigated and have shown potential for use in direct conversion detectors. The X- ray-to-charge conversion rate of these materials is 3–8 times larger than that of a-Se and thus, they are capable of X-ray quantum noise limited operation at low exposures, since the X-ray quantum noise can prevail over the electronic noise. The performance of these polycrystalline photoconductors is far from ideal due to either a large dark current, incomplete charge collection, or inadequate temporal response to X-ray irradiation, appearing as a residual current after X-ray exposure is terminated, i.e., signal lag (or from a combination of these problems). In addition, the deposition of poly-CdTe and poly-Cd1−xZnxTe layers requires a high substrate temperature (400–600 °C), which is incompatible with most of the readout electronics, or requires a hybrid deposition method, where the film is firstly deposited on the glass or alumina substrate and then coupled to the readout circuitry. The latter involves very precise alignment of the photoconductor relative to the matrix array to achieve proper pixel-to-pixel bonding that is technologically challenging, especially for high-resolution detectors.
Another promising class of materials to be used in radiation detection are perovskite semiconductors12; however, they are at a very early stage of the development (suffering from material instability, signal lag and, comparatively high dark current, technological difficulties in manufacturing a thick and uniform layer over a large area) and are not mature enough to be considered as a practical solution to improve radiation medical imaging.
It should be mentioned that among the potential X-ray-to-charge transducers listed above, polycrystalline Lead Oxide (poly-PbO) is especially promising because, similarly to a-Se, it has a long history of commercial utilization in optical imaging. Previously, thin layers of poly-PbO were used in “Plumbicon” video pick-up tubes that were widely used for broadcast, fluoroscopy and digital subtraction angiography in conjunction with image intensifiers. However, the first prototype of poly-PbO based X-ray detector with the radiography-thick photoconductor film was unsuccessful. The photoconductor exhibited signal lag13 that did not permit the use of PbO detectors in real time fluoroscopic imaging, which is the most clinically demanding application14.
Recently, we reported on the development of a new polymorphic form of the PbO material, namely amorphous Lead Oxide (a-PbO), which had not been previously synthesized15. In contrast to its polycrystalline counterpart, a-PbO is dense, capable of withstanding higher electric fields with lower dark current and exhibits no signal lag16. In this work, we use a-PbO in a bilayer PbO structure, where a thick layer of poly-PbO serves as a recording and charge transport layer while a thin layer of a-PbO acts as a lag-preventing layer.
The use of multilayer photoconductive structures is a standard solution in direct conversion detectors. Indeed, practical a-Se direct conversion detectors utilize a multilayered structure, consisting of a thick photoconducting layer of stabilized a-Se, sandwiched between one or two adjacent blocking layers needed to maintain an acceptable level of dark current.
In the majority of those detectors, two blocking layers are identified as n-like (hole blocking) and p-like (electron blocking). Examples of n-like layers are a-Se alloyed with a small percent of As and doped with alkali metal (usually Na or LiF)17,18,19,20,21,22,23, cold-deposited a-Se19,20, Sb2S324 and CeO223,25. Among p-like layers are As2Se317,18,19,20,24, a-Se doped with Cl22, and Sb2S324,25,26. Additional layers may be used, such as Arsenic-rich a-Se layers to retard crystallite formation at the interface24,26,27; and protective overcoating layer such as nigrosine28, Parylene29, epoxy resin26. As it is seen, the manufacturing of an a-Se based detector requires multistage doping and alloying with different elements, normally performed in one deposition cycle without breaking the vacuum. This process is technically challenging and requires precise control to avoid cross-contamination, leading to high deposition cost30.
Our approach to combine two allotropic forms of the same material, namely, PbO, in a blocking structure reduces technical complexity, in comparison with a-Se technology. At the same time, it will allow to combine excellent (low) ionization energy inherent to PbO, adequate hole mobilities and low dark current at practical electric fields. This holds a potential to make the direct conversion system simpler and hence, more economical to manufacture. Although we do not claim that the developed technology can be immediately used in commercial products, we show that it allows for lag-free real-time imaging in the diagnostic energy range. We also report on the direct measurements of hole mobilities and demonstrate, for the first time, the application of the bilayer PbO structure as a direct conversion X-ray detector.
Results
Experimental sample
A schematic presentation of a bilayer Lead Oxide structure is shown in Fig. 1a. The bottom 2 μm lag-preventing a-PbO layer was deposited on an ITO-coated glass substrate (bottom biased electrode) by an ion-assisted thermal evaporation technique31. Subsequently, the a-PbO layer was covered by a 12 μm layer of poly-PbO (recording and charge transport layer) using conventional thermal evaporation31. Although this sequential deposition of amorphous and polycrystalline layers was performed in a single deposition cycle (without breaking the vacuum), it should be noted that it can be done in separate evaporators, giving essentially identical results. Finally, a 200 nm thick Au contact was sputtered atop a-PbO/poly-PbO structure by magnetron sputtering to serve as the top readout electrode.
The SEM image of the cross-section of the sample is shown in Fig. 1b. As can be seen, the thin and dense layer of amorphous material in the lower part of the structure transforms into a less dense, inhomogeneous disordered layer of polycrystalline material. It should be noted that the structure of the poly-PbO layer in the presented bilayer structure is slightly different from the previously reported single poly-PbO layer structure. Indeed, a single poly-PbO film is essentially a porous network of individual platelets oriented mainly in the growth direction31, whereas the layer in the current sample consists of overlapping flakes.
Mobility measurements
Hole mobility was measured by the photo-Charge Extraction by Linearly Increasing Voltage (CELIV) technique in a range of electric fields (0.03–0.22 V/μm) and temperatures (260–350 K). The choice of CELIV was determined by its proven efficacy in the evaluation of field and temperature dependencies of mobilities in single poly-PbO layers, characterized by dispersive carrier transport with mobilities which decrease in the course of time. This feature makes a conventional Time-of-Flight (TOF) technique ineffective for transport characterization. In contrast, the theory of CELIV was recently extended to dispersive transport regime32 making it a technique of choice as an alternative to TOF for disordered materials with dispersive transport.
In photo-CELIV, a light pulse is used to generate charge carriers in the volume of an unbiased sample. The wavelength of optical excitation (595 nm) was chosen to provide a uniform bulk absorption so that electron–hole pairs are generated in the volume of the layer. Subsequently, a linearly increasing voltage is applied to the sample to extract the photo-generated carriers. As the applied voltage increases, so does the photocurrent since charge carriers are extracted faster. At the end of the extraction, when most carriers have been collected, the photocurrent decays (Fig. 2).
The carrier mobility is derived from the measured time needed to reach the peak of the photocurrent. For disordered materials with dispersive transport, the mobility is calculated using an equation
where d—detector’s thickness, tpeak—time to the peak of the photocurrent, A—slope of the voltage ramp, α—dispersion parameter derived from the relationship 32
A typical CELIV response at given experimental conditions is shown in Fig. 3, where T—temperature, Rosc—input resistance of the oscilloscope, tpulse—duration of a light pulse, and tdelay—time delay between the light and voltage pulses. The dark-response, which is a capacitive component of the current, was subtracted from the photo-response, and the peak time was measured from the differential photocurrent transient.
To satisfy the requirements of the CELIV model and to prevent the accumulation of space charge33, the magnitude and duration of the light pulse were adjusted to make the amplitude of the photocurrent (differential signal) smaller than the capacitive (dark) signal; and the input resistance of the oscilloscope was adjusted to minimize the RC-component of the signal. Also, since it has been previously shown that holes are much faster carriers in poly-PbO32,34, the experimental conditions were tuned (i.e., a voltage pulse of low amplitude and short duration was used throughout the experiments) to make the photocurrent caused by the drift of holes only, so that slower electrons do not contribute to the recorded photocurrent.
Figure 4 shows experimentally measured time to peak dependence on the voltage ramp at different temperatures. A slope of a log–log fit curve yields a value of the dispersion parameter α = 0.42, from Eq. (2). The dispersion parameter is temperature independent, similarly to what has been found in single poly-PbO layers32; however, its value is twice larger than that in single poly-PbO.
The mobility of holes μ(F) was calculated using Eq. (1) for electric field at the time of maximum extraction \(\left(F=\frac{A\cdot {t}_{peak}}{d}\right)\) at different voltage ramps A and temperatures (Fig. 5). Hole mobility is strongly dependent on the electric field and reaches a value of 0.35 cm2/Vs at 0.22 V/μm. To compare, the mobility of holes in a-Se is 0.15 cm2/Vs at 1 V/μm at room temperature35. The weak dependence of mobility on temperature and the strong dependence on applied field indicates a dispersive transport regime mainly governed by spatial inhomogeneity32.
Temporal performance evaluation
The temporal performance was examined by the X-ray induced Photocurrent Method (XPM) in a pulsed mode. The photocurrent in a bilayer PbO structure was measured at an electric field of 10 V/μm (negative bias on ITO) under 1 s long X-ray exposure, modulated using a rotating chopper at various frequencies in the range of 10–60 Hz and 50% duty cycle (Fig. 6). In this test, image lag would reveal itself as an increase in the signal in each frame36.
To demonstrate this, Fig. 7 compares outputs of a bilayer PbO structure and a single poly-PbO layer biased at 5 V/μm and irradiated with X-rays pulsed at a frequency of 10 frames per second (fps). The exposure was 2 s long, during which both samples were exposed to 20 X-ray pulses (100 ms alternating intervals with open and closed chopper). When irradiated with pulsed X-rays, a rise of the photocurrent level with each subsequent frame is evident in the single poly-PbO layer. In addition, there is a well-pronounced residual signal, that decays to zero in approximately 2 s after the termination of X-ray exposure. In contrast, a bilayer a-PbO/poly-PbO structure shows a stable photocurrent value and no signal lag.
The temporal performance of the bilayer detector shows a nearly constant amplitude of the signal in each frame even at a high readout rate (Fig. 8). A uniform amplitude during the X-ray exposure indicates no build-up of the injection current, allowing maintenance of constant dark current. After the termination of the X-ray pulse, the photocurrent drops rapidly to zero level with no residual signal, proving lag-free operation.
Frequency of 30 fps used in this experiment corresponds to readout rate conventionally used in a real-time fluoroscopy imaging. A reduced frame rate can be used to increase the signal-to-noise ratio (SNR) of the detector and to moderate patient dose. A higher readout rate might be necessary when one must image a rapidly changing process, such as heart beating (cardiac imaging and coronary catheterization)37.
Discussion
The performance of a-PbO/poly-PbO bilayer structure has been investigated in terms of whether combining these PbO polymorphs into a multilayer structure allows to consolidate the adequate hole mobility inherent in poly-PbO with the excellent X-ray temporal response inherent in a-PbO layers. CELIV measurements confirmed that hole transport in the bilayer structure is dispersive and qualitatively similar to that in single layers of poly-PbO32. Weak temperature dependency of mobility μ and dispersion parameter α, and strong field dependence of μ indicates that dispersion is governed by spatial disorder rather than energy disorder. Mobility of holes reaches value of 0.35 cm2/Vs at relatively low field 0.22 V/μm (the upper value of the applied electric field was limited by the bandwidth of the function generator). The fact that mobility increases rapidly with an increase in electric field is very desirable since it provides a tool to improve the carrier schubweg i.e. the average distance drifted before a carrier is lost to traps (schubweg is a product of the carrier drift mobility µ, the lifetime τ and field F, i.e. µτF) and to avoid depth dependent charge collection. Both the dispersion parameter and hole mobility obtained for a bilayer a-PbO/poly-PbO structure are somewhat higher than those for poly-PbO. This can be attributed to the differences in structural heterogeneity between a single poly-PbO and that grown on a-PbO: depositing a poly-PbO layer on a-PbO sublayer makes hole transport less dispersive and increases hole mobility.
Evaluation of the temporal response of the bilayer structure with the pulsed X-ray radiation did not reveal signal lag—a major obstacle for application of poly-PbO layers in the direct conversion X-ray detectors. Indeed, the presence of signal lag and subsequently, image lag, does not permit to use poly-PbO detectors in the most demanding clinical application that is real time fluoroscopic imaging. Dynamic readout, as that used in real time applications, requires very little to no lag at the end of each frame, otherwise previous images will be superimposed with the subsequent ones, thus resulting in a misleading view. The elimination of signal lag can be explained by decreasing charge trapping at a-PbO/poly-PbO interface and suppressing X-ray triggered injection caused by local enhancement of the electric field at the interface between the electrode and photoconductor13. In a bilayer configuration, a lag-preventing layer of a-PbO separates poly-PbO from the electrode, preventing charge injection and eliminating image lag.
Despite this, the dark current of a bilayer structure is still higher than the recommended value for digital flat panel detectors (~ 10 pA/mm2)38. Further decrease in the dark current may be achieved by using a thin blocking layer between the electrodes and PbO bilayer. One of the most suitable candidates is polyimide (PI). It is a well-developed material that was already successfully used with a-Se photoconductors36. Careful optimization of the film’s thickness allows the tuning of its resistivity to prevent significant voltage drop across the blocking layer as well as redistribution of the electric field inside the structure39. It should be noted that polyimide film can be easily applied by a conventional spin coating technique, in contrast to complicated process of growing of the doped layers mentioned earlier. The development of the PI blocking layer to be used in a-PbO/poly-PbO-based X-ray detectors is left for future work.
Overall, our results demonstrate that combining an a-PbO lag-preventing layer with a poly-PbO X-ray-receiving layer in a bilayer structure allows to obtain lag-free operation while preserving adequate hole mobilities (relative to other disordered photoconductors) needed for adequate schubweg and high efficiency in collecting X-ray generated charge.
Methods
Sample preparation
The bilayer PbO sample was thermally evaporated on Indium Tin Oxide (ITO) coated glass substrate. To form a-PbO layer, a high purity (5 N) yellow PbO powder was evaporated at the temperature ~ 1000 °C in atmosphere of ionized oxygen at the pressure ~ 0.1 Pa. The growing layer was continuously bombarded by Oxygen ions with energy ~ 70 eV. The poly-PbO layer was formed from the same powder and at the similar temperatures, but in contrast to a-PbO, evaporation took place in atmosphere of molecular oxygen at the pressure ~ 0.3 Pa. The substrate temperature was kept below 150 °C in both processes. A top gold contact was sputtered ex situ in a dedicated chamber. Since poly-PbO is known to degrade under ambient conditions by forming a hydro-cerussite compound14, all measurements were performed in the protective atmosphere of dry Nitrogen.
CELIV apparatus
A sample was placed in a heating–cooling stage Linkam LTS350 that enables a precise temperature control in a wide range of temperatures. A 2-channel function generator Tektronix AFG 3022C was used to apply a linearly increasing voltage pulse on ITO and trigger a light pulse from the ITO side. The current transients were readout from Au electrode on the oscilloscope Tektronix TDS 2024C with adjustable input resistance. For an excitation LED light pulse with a radiant power ~ 100 μW and a wavelength of 595 nm, the attenuation depts in Lead Oxide is 90 μm40, which is much larger than the detector’s thickness of 14 μm. This provides a homogeneous generation of charge carriers through the bulk of the film. The range of electric fields used in these measurements was limited by the bandwidth of the function generator.
XPM apparatus
The sample was placed in the shielded Aluminum box with a 2-mm thick lead collimator. A negative DC bias was applied to the ITO from a high voltage power supply (Stanford Research Systems PS350), and the photocurrent was readout from the Au electrode on oscilloscope Tektronix TDS 2024C with input resistance of 1 MΩ. The X-ray tube (Dunlee PX1412CS, insert DU-304) with a Tungsten target and a 2-mm Al filter was used to generate 60 kVp X-ray pulse (tube current was 200 mA). A chopper controller (Stanford Research Systems SR540) drives a 2-mm thick Copper chopper to modulate an X-ray pulse at different frequencies and 50/50 duty cycle that was used to simulate a pulsed irradiation mode.
Data availability
The datasets generated and analysed during the current study are available from the corresponding author on reasonable request.
References
Kasap, S. et al. Amorphous selenium and its alloys from early xeroradiography to high resolution X-ray image detectors and ultrasensitive imaging tubes. Phys. Stat. Sol. (B) 246, 1794–1805 (2009).
Liu, Y. et al. Electrical properties of X-ray detector based on bismuth tri-iodide single crystal with electrode configuration considering. Mater. Res. Express 6, 055902 (2019).
Sun, H. et al. Laser-induced surface recrystallization of polycrystalline PbI2 thick films for X-ray detector application. Appl. Surf. Sci. 427, 1146–1151 (2018).
Condeles, J. F. & Mulato, M. Polycrystalline lead iodide films produced by solution evaporation and tested in the mammography X-ray energy range. J. Phys. Chem. Solids 89, 39–44 (2016).
Lee, D., Lee, K. & Seo, J. High signal-to-noise ratio HgI2 X-ray detector assisted with ultraviolet radiation. Nucl. Inst. Methods Phys. Res. A 941, 162364 (2019).
Antonuk, L. E., El-Mohri, Y., Zhao, Q. & Jiang, H. Exploration of strategies for implementation of screen-printed mercuric iodide converters in direct detection AMFPIs for digital breast tomosynthesis. In: Medical Imaging 2017: Physics of Medical Imaging, vol. 101320A (2017).
Street, R. A. et al. Comparison of PbI2 and HgI2 for direct detection active matrix X-ray image sensors. J. Appl. Phys. 91(5), 3345–3355 (2002).
Zhou, L. et al. A high-resistivity ZnO film-based photoconductive X-ray detector. IEEE Photon. Technol. Lett. 31(5), 365–368 (2019).
Lee, S. et al. Direct thermal growth of large scale Cl-doped CdTe film for low voltage high resolution X-ray image sensor. Sci. Rep. 8, 14810 (2018).
Znamenshchykov, Y. V. et al. Electrical, structural and optical properties of Cd1−xZnxTe thick polycrystalline films. Vacuum 149, 270–278 (2018).
Simon, M. et al. Analysis of lead oxide (PbO) layers for direct conversion X-ray detection. IEEE Trans. Nucl. Sci. 52(5), 2035–2040 (2005).
Rowlands, J. A. Medical Imaging. Material change for X-ray detectors. Nature 550, 47–48 (2017).
Semeniuk, O. et al. Characterization of polycrystalline lead oxide for application in direct conversion X-ray detectors. Sci. Rep. 7, 8659 (2017).
Simon, M. et al. PbO as direct conversion X-ray detector material. Med. Imaging 2004 Phys. Med. Imaging 5368, 188–199 (2004).
Semeniuk, O., Sukhovatkin, V. & Reznik, A. Amorphous lead oxide based energy detection devices and methods of manufacture thereof. U.S. Patent 10,163,9701 B2 (2018).
Semeniuk, O., Grynko, O., Juska, G. & Reznik, A. Amorphous lead oxide (a-PbO): suppression of signal lag via engineering of the layer structure. Sci. Rep. 7, 13272 (2017).
Polischuk, B. T. & Jean, A. Multilayer plate for X-ray imaging and method of producing same. U.S. Patent 5,880,472 (1999).
Rougeot, H. M., Jean, A., Mani, H. & Shukri, Z. A. Indirect X-ray image detector for radiology. U.S. Patent 7,692,157 B2 (2010).
Frey, J. B., Belev, G., Tousignant, O., Mani, H. & Kasap, S. O. Dark current in multilayer stabilized amorphous selenium X-ray photoconductors. Phys. Stat. Sol. (C) 6(S1), S251–S254 (2009).
Frey, J. B. et al. Dark current in multilayer stabilized amorphous selenium based photoconductive X-ray detectors. J. Appl. Phys. 112, 014502 (2012).
Manouchehri, F., Kabir, M. Z., Tousignant, O., Mani, H. & Devabhaktuni, V. K. Time and exposure dependent X-ray sensitivity in multilayer amorphous selenium detectors. J. Phys. D Appl. Phys. 41, 235106 (2008).
Brauers, A. et al. Charge collection in a Se photoconductor on a thin film transistor array during X-ray imaging. Mater. Res. Soc. Symp. Proc. 467, 919–924 (1997).
Huang, H. & Abbaszadeh, S. Recent developments of amorphous selenium-based X-ray detectors: a review. IEEE Sens. J. 20, 1694–1704 (2020).
Imai, S. Radiation image detector. U.S. Patent 7,834,324 B2 (2010).
Tanioka, K. et al. An avalanche-mode amorphous Selenium photoconductive layer for use as a camera tube target. IEEE Electr. Device Lett. 8, 392–394 (1987).
Irisawa, K., Noda, K., Hayashi, K., Yamane, K. & Miyake, K. Radiation detector. U.S. Patent 7,947,970 B2 (2011).
Fender, W. D., Zanrosso, E. M., Leiga, A. G. & Manchego, R. Process for manufacturing an improved selenium alloy X-ray imaging member on transparent substrate. U.S. Patent 5,320,927 (1994).
Fender, W. D., Speiser, R. C., Kramer, G. K. & Ceelen, H. P. Selenium alloy imaging member. U.S. Patent 4,770,965 (1988).
Cheung, L., Bogdanovich, S., Ingal, E. & Williams, C. L. Amorphous selenium flat panel X-ray imager for tomosynthesis and static imaging. U.S. Patent 7,304,308 B2 (2007).
Belev, G. S. Electrical properties of amorphous selenium based photoconductive devices for application in X-ray image detectors. Ph.D. dissertation, University of Saskatchewan, Saskatoon, SK, Canada (2007).
Semeniuk, O., Csik, A., Kökényesi, S. & Reznik, A. Ion-assisted deposition of amorphous PbO layers. J. Mater. Sci. 52, 7937–7946 (2017).
Semeniuk, O. et al. Charge transport mechanism in lead oxide revealed by CELIV technique. Sci. Rep. 6, 33359 (2016).
Juška, G., Arlauskas, K. & Genevičius, K. Charge carrier transport and recombination in disordered materials. Lith. J. Phys. 56, 182–189 (2016).
Semeniuk, O. et al. Transport of electrons in lead oxide studied by CELIV technique. J. Phys. D Appl. Phys. 50, 035103 (2017).
Kasap, S., Koughia, C., Berashevich, J., Johanson, R. & Reznik, A. Charge transport in pure and stabilized amorphous selenium: re-examination of the density of states distribution in the mobility gap and the role of defects. J. Mater. Sci. Mater. Electron. 26, 4644–4658 (2015).
Abbaszadeh, S., Scott, C. C., Bubon, O., Reznik, A. & Karim, K. S. Enhanced detection efficiency of direct conversion X-ray detector using polyimide as hole-blocking layer. Sci. Rep. 3, 3360 (2013).
Kruger, R. A. et al. Computerized fluoroscopy in real time for noninvasive visualization of the cardiovascular system. Radiology 130(1), 49–57 (1979).
Kasap, S. et al. Amorphous and polycrystalline photoconductors for direct conversion flat panel X-ray image sensors. Sensors 11, 5112–5157 (2011).
Camlica, A. et al. Use of pulse-height spectroscopy to characterize the hole conduction mechanism of a polyimide blocking layer used in amorphous-selenium radiation detectors. IEEE Trans. Electron Devices 67, 633–639 (2020).
Biberman, L. M. & Nudelman, S. The Plumbicon. In Photoelectronic Imaging Devices, Vol. 2. Devices and Their Evaluation (eds Stupp, E. H. & Levitt, R. S.) 275–300 (Plenum, New York, 1971).
Acknowledgements
Financial support from Teledyne DALSA, the Natural Sciences and Engineering Research Council of Canada (NSERC) and Mitacs funding agencies is gratefully acknowledged.
Author information
Authors and Affiliations
Contributions
O.G. deposited experimental bilayer PbO sample, performed CELIV experiment and drafted the manuscript text. T.T. and E.P. performed XPM experiment. G.J. and A.R. examined and analyzed the obtained results. A.R. edited the manuscript text. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Grynko, O., Thibault, T., Pineau, E. et al. Bilayer lead oxide X-ray photoconductor for lag-free operation. Sci Rep 10, 20117 (2020). https://doi.org/10.1038/s41598-020-77050-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-77050-w