Nucleobase morpholino β amino acids as molecular chimeras for the preparation of photoluminescent materials from ribonucleosides

Bioinspired smart materials represent a tremendously growing research field and the obtainment of new building blocks is at the molecular basis of this technology progress. In this work, colloidal materials have been prepared in few steps starting from ribonucleosides. Nucleobase morpholino β-amino acids are the chimera key intermediates allowing Phe–Phe dipeptides’ functionalization with adenine and thymine. The obtained compounds self-aggregate showing enhanced photoluminescent features, such as deep blue fluorescence and phosphorescence emissions.


Scientific Reports
| (2020) 10:19331 | https://doi.org/10.1038/s41598-020-76297-7 www.nature.com/scientificreports/ side chain. During the years, several linear α 21,22 and β 11,12 nucleo amino acids 23 have been developed and used for the preparation of tubular or sheet-like aggregates. In this work, we present a new class of β amino acids 1 containing a morpholino ring and a nucleobase. These nucleo amino acids were prepared in enantiopure form from ribonucleosides 2, through nucleo morpholino alcohols 3, as the key intermediates (Scheme 1). Nucleo amino acids 1 were then used for the preparation of ultra-short peptides containing the dipeptide Phe-Phe that showed self-aggregation propensity in water and polar solvents, leading to the obtainment of sub-micrometric spherical morphologies. Finally, given the formally deep-UV active features of the Phe-Phe residue 24,25 , steady state and time resolved photoluminescence (PL) studies have been performed on the synthesized ultra-short peptides revealing their deep blue fluorescence and an unprecedent phosphorescence.
The synthesis of alcohol intermediates 3 was reported in 1993 by Summerton in a patent 26 and consisted in a "one-pot" oxidative ring-opening and reductive amination of the ribose sugar leading to the obtainment of the morpholino ring (Scheme 2). Several modifications of this procedure have been reported in the last years [27][28][29][30] . Here, we started from unprotected ribonucleosides, using the Summerton's procedure with different work up conditions. Briefly, the sugar ring is converted into the corresponding morpholino through a "one-pot" oxidation/amination reaction using NaIO 4 (1.1 eq) and (NH 4 ) 2 B 4 O 7 (1.15 eq) in MeOH. The crude intermediates A were directly treated with NaCNBH 3 (1.7 eq) in MeOH affording compounds 3. The reaction was quenched with HCl and the products 3a and 3b were isolated as hydrochloride salts by crystallization from polar solvents (3a: MeOH, 60%; 3b: ACN, 70%).
We then investigated the oxidation reaction of the hydroxyl group affording to the β-amino acid function. Firstly, the protection of the endocyclic nitrogen was required to avoid side reactions on the free amine. The Fmoc protecting group was selected, in view of using N-protected compounds 1 for the preparation of nucleopeptide materials. Fmoc group is indeed known to favor self-assembly through π-π stacking 31 . The reaction was carried out directly on the crude 3a,b obtained in the previous reaction (Scheme 2) simply adding FmocOSu (1 eq) and DIEA (1-3 eq) in DMF. The target compounds 4a and 4b were thus obtained in 85% and 55% yield, respectively. Several oxidants were then tested on the compounds 4a and 4b ( www.nature.com/scientificreports/ 4b scarcely reacted and the Fmoc deprotection occurred by prolonging reaction times. Acid 1b (70%) was thus obtained by Jones oxidation with CrO 3 (Scheme 3). N-Fmoc protected thymine and adenine nucleo amino acids 1a-b were then used for the preparation of ultra-short nucelopeptides containing diphenylalanine. The coupling with the dipeptide H 2 N-Phe-Phe-OMe 5 was performed using HOBt/HBTU (1.1 eq each), as condensing agents, and DIEA (4 eq), as the base, leading to compounds 6a,b in 80% yield (Scheme 4).
The self-assembly behavior of both compounds 6a,b was studied using the solvent displacement method. A solution of compound 6a,b in hexafluoroisopropanol (HFIP, 100 mg/mL) was diluted with different solvents (distilled water, EtOH, 50% EtOH, MeOH, isopropanol, chloroform) to a final concentration of 2 mg/mL. The formation of sub-micrometric aggregates was observed by drop-casting on silicon wafers for recording SEM after 30 min and after 24 h (see Supplementary information). In water, both compounds 6a and 6b exhibited spherical aggregates (Fig. 1) whose size ranged from a few tens of nanometers to less than a micron. In chloroform, isopropanol and HFIP no aggregates were observed.
In EtOH and MeOH, 6a and 6b had a different behavior. Compound 6a exhibited indeed spherical macroaggregates in 50% EtOH (Fig. S1 in Supplementary information), while 6b self-aggregates in ordered spherical structures both in EtOH and MeOH (Fig. 2).
Considering the promising results obtained in HFIP/ H 2 O, we performed DLS analysis on 6a and 6b at different HFIP/H 2 O ratios (see Supplementary information). Our results suggested that the quantity of water is fundamental for determining the formation of aggregates, their size and and their distribution. At the lowest water content (HFIP/H 2 O, 70:30) the formation of nanocolloidal clusters of 5-6 nm was observed together with larger agglomerates. An enhancement in the size of the aggregates was obtained increasing the water amount, although the distribution was not optimal. When the HFIP content was only the 2% the 6a and 6b suspensions showed only one sharp peak centered at ca. 200 nm, indicating the formation of a monodispersed colloidal suspension (see Table 1 and Supplementary information). In the case of 6a, an increase of the size of the agglomerates was observed by measurements repeated after 24 h and 48 h. A negative ζ-potential was detected for both 6a and 6b, suggesting a protonated state of the nucleobases with a consequent formation of a tight ion pair due to the presence of acidic HFIP.
The stability of 6a and 6b water aggregates was examined at different pH and upon heating at 120 °C. Both aggregates were not stable at high temperature and at acidic pH. At basic pH (pH = 10), a change of the morphology was observed (Fig. 3).   www.nature.com/scientificreports/ To understand the molecular conformation of the self-assembled structure of 6a and 6b, FT-IR experiments were performed (Fig. 4). In both cases, the minima at 1688 cm −1 in the amide-I region and 1540 cm −1 in the amide-II region suggested the presence of β-sheet conformations 33 . We thus hypothesized that the closer of sheets along the two axes results in the formation of the spherical structure 34 . The other minima in the spectrum (1652 cm −1 for 6a and 1660 cm −1 for 6b) are ascribable to adenine (A) and thymine (T) residues, respectively (see Fig. S2 in Supplementary Information).
Photophysical characterizations were performed on diluted solutions (1-2 × 10 -5 M) of the tripeptides 6a and 6b (see Supplementary Information for details) and on self-assembled materials in water, obtained from HFIPwater (98:2 v/v) at the concentration of 5 × 10 −5 M (Fig. 5). Photophysical characterization in the same conditions were performed on 1a and 1b (see Figs. S7, S8, Table S2 in Supplementary Information). The normalized absorption spectra of the tripeptides 6a and 6b acetonitrile (ACN) solutions (Fig. S3) looked very similar and are characterized by a strong deep UV absorption below 230 nm, a broad band between 240-280 nm and two slightly resolved vibrionic transitions between 280-300 nm (more evident in the excitation spectra, see Figs. S3 and S4 in Supplementary Information). In addition, both compounds 6a,b showed deep blue room temperature photoluminescence in solution (PL, normalized data reported in Fig. 5 gray lines with square drawings and Fig. S4) with a maximum at 303 nm and a barely resolved shoulder at lower energy. The corresponding fluorescence quantum yield (QY) was 0.12 for 6a and 0.13 for 6b; the lifetimes were 5.0 and 5.5 ns respectively. The emissions and the photophysical parameters are similar to the ones measured on the Fmoc protected 1a and 1b (see Fig. S8 and Table S2). In Fig. 5, the PL emissions of the colloids obtained from HFIP-water mixture at 50 µM concentration are superimposed. Compound 6a showed an overall QY of 0.018 and biexponential decay of 1.41(63%) and 6.06 (37%) ns at 330 nm. Its emission was composed by a dominant high energy band around 308 nm (similar to the emission in ACN solution and only slightly red-shifted) followed by a week visible emission tailing up to 500 nm. 6b, with an overall QY of 0.03, displayed a high energy emission at 306 nm characterized by a biexponential decay of 1.08(57%) and 7.07(43%) ns at 330 nm, and a broad unstructured band between 400-600 nm with maximum at 440 nm and lifetime of 2.82(27%) and 13.1(73%) ns. Whereas the former is similar to the molecular emission in Table 1. Hydrodynamic diameter by DLS and ζ-potential of 6a and 6b aggregates.   www.nature.com/scientificreports/ diluted solution, the latter could be ascribed to the fluorescence emission linked to the restricted intramolecular rotation of the backbone as previously reported in the literature for the Phe-Phe system 25 . Upon cooling the colloidal suspensions of compounds 6a,b at 77 K (pink curve in Fig. 5 insets) a new, previously undescribed, emission appeared in the visible range between 420 and 550 nm and characterized by structurally resolved features. These emissions had a long radiative lifetime of 4.2 and 4.1 s for 6a and 6b, respectively, thus indicating a process originated from a triplet state. To understand the origin of the phosphorescence emission, PL studies were performed on the isolated building blocks to generate compounds 6 (i.e. H 2 N-Phe-Phe -OMe 5 and the Fmoc protected 1). As evident from Fig. S5 (SI) a structured emission above 400 nm is only observed from the nucleobase thus allowing the attribution of the phosphorescence observed in the tripeptide systems to the adenine or thymine unit 35 .
In conclusion, a new class of β amino acids containing a morpholino ring and a nucleobase has been developed starting from ribonucleosides. Their synthesis takes advantage from a "one-pot" oxidative ribose ringopening and reductive amination, followed by the oxidation of the primary alcohol of the sugar. The so obtained β amino acids have been used for the functionalization of Phe-Phe dipeptide leading to sub-micrometric aggregates possessing photoluminescent features of both fluorescence and phosphorescence type. Thus, it was proved that the here presented tripeptides possess the photoluminescent properties given by the β-AA and the self-assembly behaviour due to the presence of Phe-Phe. They hence represent promising tools for the development of bioinspired functional materials with applications not only in the biotechnology field but also in non-biological optoelectronic ones. www.nature.com/scientificreports/ Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creat iveco mmons .org/licen ses/by/4.0/.