Antiferromagnetism in perfectly ordered L10-MnAl with stoichiometric composition and its mechanism

Manganese (Mn)-based strong magnets have long been a challenge because their 3d half-filled nature, owing to the close proximity of Mn atoms, results in antiferromagnetic ordering. Among various Mn magnetic materials, L10-MnAl (τ-phase) has received much attention since it shows ferromagnetism at a high Curie temperature despite the very short Mn–Mn distance. However, because of the difficult synthesis of the stoichiometric and perfectly ordered τ-phase, its intrinsic magnetic properties and mechanism are unclear. Here, we show the first observation of antiferromagnetism, having sixfold magnetic superstructure along the c-axis, in stoichiometric and chemically ordered τ-phase. Moreover, we found that super-exchange interaction between Mn atoms via p-electrons of Al atoms causes antiferromagnetism in τ-phase. The ferromagnetism in the conventional Mn-rich τ-phase results from the suppression of the super-exchange interaction due to the substitution the excess Mn atoms for the Al atoms. The current study of Mn-based magnetic materials mainly focuses on the lattice constant engineering based on the simple Beth-Slater picture of direct exchange. These findings present effective ways to obtain high magnetization without antiferromagnetic ordering.

Scientific RepoRtS | (2020) 10:12489 | https://doi.org/10.1038/s41598-020-69538-2 www.nature.com/scientificreports/ Recently we have reported that a τ-phase with nearly stoichiometric composition with higher-ordering parameter was obtained by post-annealing of electrodeposited MnAl powder, but it unexpectedly showed metamagnetism 17 . However, the mechanism of metamagnetism is unclear, and it may reflect exhibiting antiferromagnetic ground state. Actually, it has been pointed out by Edström et al. 18 that the stoichiometric and perfectly ordered τ-phase shows antiferromagnetism, and the excess Mn atoms essentially contribute to the stability of the ferromagnetic ordering. In other words, the Mn dilemma has been resolved by the excess Mn in τ-phase.
In this paper, we examine the magnetic structure of τ-phase using neutron diffraction experiments and investigate the mechanism of metamagnetism in τ-phase by means of first principle calculation.

Magnetizations and crystal structures
The magnetization curves of as-deposited and typical annealing conditions such as 500, 550 °C for 16 h and 600 °C for 0.5 h are shown in Fig. 1a. An as-deposited sample shows ferromagnetic behaviour with a large coercivity of 7.4 kOe. The MnAl powders annealed at 500 and 550 °C shows a sudden increase in magnetization under a magnetic field of approximately 50 and 20 kOe, respectively. This field-induced first-order nonmagnetic to ferromagnetic transition is the so-called metamagnetism. However, the 600 °C-annealed sample shows ferromagnetic behaviour with smaller coercivity than that of the as-deposited one. The magnetism of electrodeposited MnAl powder drastically changes by annealing, which has already been reported in previous article 17 .
For further investigation of the metamagnetic transition, the temperature-dependent magnetizations of the 550 °C-annealed sample were shown in Fig. 1b. In the low-temperature range 100-300 K, the magnetic-field of 10 kOe was applied after zero-field cool. In the high-temperature range 300-700 K, the magnetic-field of 5 kOe was applied. As for the low temperature range, the magnetization gradually increases with decreasing temperature. The magnetization shows a characteristic of the second-order ferromagnetic transition in contrast to a sharp first-order ferromagnetic transition, for example, observed in MnAs 19 . On the other hands, in the range of high temperature range, the magnetization increases as elevating temperature and has a broad peak. This behaviour indicates antiferromagnetic to paramagnetic transition. To clarify this point, the temperature dependence of reciprocal susceptibility in high-temperature range was shown in inset of Fig. 1b. The dotted line, which is a single straight line fit to the data above 600 K, shows the data obeys the Curie-Weiss law and the Neel temperature T N was estimated to be about 570 K. These results indicate the mechanism of metamagnetism involved antiferromagnetic to ferromagnetic transition.
The annealing temperature dependence of synchrotron radiation X-ray diffraction (SR-XRD) in electrodeposited MnAl powders is shown in Fig. 2. In the as-deposited sample, single-phase τ was observed. As for 400-500 °C for 16 h, only Al-rich Mn 11 Al 15 (γ 2 -phase) 20 appeared as the decomposition phase, although the τ-phase is still the main phase. For 550 °C for 16 h and 600 °C for 0.5 h, Mn-rich Mn 3 Al 2 (β-phase) 21 was simultaneously observed.

Magnetic-structure determination by neutron diffraction
In order to determine the magnetic structure of the τ-phase, neutron diffraction measurement was performed. The neutron diffraction pattern of the 500 °C-annealed sample in the range from 1.8 to 3.8 Å of lattice spacing d is shown in Fig. 3a. Although it is well known that the τ-phase shows ferromagnetism, ferromagnetic peaks (d = 1.9, 2.2 Å) were not observed. However, we found several peaks undetected by XRD, which corresponded to the magnetic scattering indicated by the dashed line in Fig. 3b. These peaks were indexed as rational "l" miller indexes of 1/6, where the unit cell is regarded as a BCT structure. It indicates that there exists a sixfold magnetic       www.nature.com/scientificreports/ the τ-phase was A-type antiferromagnetic, namely, magnetic moments are anti-ferromagnetically ordered along the c-axis but ferromagnetically ordered in the ab plane. In the ab plane, the existence of strong ferromagnetic exchange interaction has already pointed out by previous theoretical study 2,15 but the origin of antiferromagnetic ordering along the c-axis is unclear. Below we discuss the validity of the magnetic moment deduced by our Rietveld fitting. Although the maximal value of the magnetic moment of 3.86 μ B is significantly larger than the theoretical estimation of 2.4 μ B [13][14][15][16] , if all the magnetic moments are forcedly aligned ferromagnetically, that is, 3.86, 0.86, 0.86, 3.86, 0.86 and 0.86 μ B , the average magnetic moment is 1.86 µ B /cell, which corresponds to the saturated magnetization of 120 emu/g. Considering the coexistence of non-magnetic decomposition phase, the value is in agreement with the saturated magnetization of 110 emu/g evaluated by using the VSM measurement.

Rietveld analysis of synchrotron radiation X-ray diffraction patterns
In order to investigate the reason for antiferromagnetism in τ-phase, crystal structural analysis was performed using the SR-XRD. In general, the magnetism of Mn magnetic materials was strongly affected by the Mn-Mn distance. Therefore, the annealing temperature dependence of lattice constants a and c, which are related to the Mn-Mn distance, was estimated using the Rietveld analysis. In the as-deposited sample, the lattice constants were 3.608 and 2.773, respectively. The c value was larger than the value of conventional τ-phase Mn 1.11 Al 0.90 of 3.57, whereas the a value was equivalent to the conventional value of 2.77 10 . The lattice constant c monotonically decreases above 450 °C, as shown in Fig. 4a. The annealing temperature dependence of the lattice constant a is rather complex, as shown in Fig. 4b. By annealing, the lattice constant a abruptly decreases at 400 °C and gradually increases with the increase in temperature, but it decreases again at 600 °C. Please note that the changes in lattice constants a and c, 0.04 and 0.16%, respectively, were not significantly large.
We also examined the axial ratio c/a and cell volume a 2 c as shown in Fig. 4c,d. The c/a has a peak value at 400 °C and decreases with increase in annealing temperature. As for a 2 c, it monotonically decreases with increase in annealing temperature. It indicates that the Mn composition of τ-phase increases by annealing since the atomic radius of Mn atom is smaller than that of the Al atom. The change in Mn composition might result from decomposition into Al-rich γ 2 -phase, which is expressed as τ → τ + γ 2 . This preferential decomposition into Al-rich γ 2 -phase is different from conventional MnAl 23 .
In order to confirm this point, scanning transmission electron microscopy high-angle annular dark-field (STEM-HAADF) imaging and energy-dispersive spectroscopy (EDS) mapping images of as-deposited, annealed sample at 500 °C and 600 °C are shown in Fig. 5a  www.nature.com/scientificreports/ phase and Al-rich phase. By performing selected-area electron diffraction, the Mn-rich and Al-rich phases were identified as τ and γ 2 phases, respectively. It is noted that the compositional contrast of 600 °C seem to be stronger than one of 500 °C. This point supports the Mn composition change by the decomposition into Al-rich γ 2 -phase indicated by our Rietveld analysis. However, the slight Mn composition change of τ-phase by annealing conditions was not quantitatively demonstrated by our EDS analysis. In order to investigate quantitatively composition change of τ-phase due to decomposition, the Mn composition x was estimated from the following equation.
here m τ , m γ2 , and m β are the molar ratio of each phase, estimated by using the Rietveld quantitative phase analysis. x 0 is 49.3%, which is the Mn composition of as-deposited sample determined by inductively coupled plasmaatomic emission spectrometer (ICP/AES). The annealing temperature dependence of the Mn composition is shown in Fig. 6. The Mn composition gradually increases with increase in annealing temperature. Note that the stoichiometric composition was realized at 500 °C, where the metamagnetic behaviour is clearly observed.
Although we have already reported 17 , the order parameters S of the τ-phase in the as-deposited samples, the 500 °C annealed sample, and 600 °C annealed sample were 0.76, 0.90 and 0.86, respectively. Here, the ordering parameter S is defined as follows: where g is the Mn (or Al) occupancy at the Al (or Mn) site of τ-phase. As expected, the ordering parameter of the as-deposited sample increased by annealing. However, the order parameter S of the 500 °C-annealed sample was larger than that of the 600 °C-annealed one. This difference is associated with the increase in Mn composition of the τ-phase accompanied by decomposition. From these results, we conclude nearly stoichiometric and chemically ordered τ-phase having S = 0.90 with Mn = 50.0 at% is obtained by the post-annealing of electrodeposited MnAl powder. www.nature.com/scientificreports/

First principles electronic-structure calculations of L1 0 -MnAl
In order to elucidate the mechanism of antiferromagnetism in τ-phase, we investigated the stable magnetic structure by using the first principles calculations. First, we consider the stoichiometric and perfectly ordered L1 0 -Mn 50 Al 50 . We calculated the total energies of the collinear ferromagnetic and antiferromagnetic ordering of the Mn atoms. Possible magnetic structures for L1 0 -MnAl are the collinear ferromagnetic, A-, C-and G-type antiferromagnetic ordering, as shown in Fig. 7a. Comparing the total energies we find that the A-type antiferromagnetic ordering of Mn spins has the lowest energy among the various collinear structures considered as shown in Fig. 7b. These results are consistent with our experimental results as well as with the calculations by A. Edström 18 , although our calculated model was not assumed as a sixfold superstructure along the c-axis. The total energy of the A-and C-type antiferromagnetic ordering was determined to be 42.8 and 19.7 meV/atom lower than that of the ferromagnetic structure. Whereas for the G-type antiferromagnetic ordering, the corresponding value was 111.6 meV/atom higher. The stability trend in antiferromagnetic structures is in agreement with previous studies 16 , except for the result concerning the ferromagnetic state. The magnetic moment of Mn in the A-type antiferromagnetic ordering was 3.21 µ B . Although the value is considerably larger than estimations of previous theoretical studies 13,14,18 , it is smaller than the maximal magnetic moment of 3.86 µ B observed by neutron diffraction measurement. If the antiferromagnetism in τ-phase originates from the direct exchange coupling between Mn atoms, the Mn-Mn distance should affect its magnetic structure. Therefore, the dependence of the stable magnetic structure  www.nature.com/scientificreports/ on the lattice constant was examined by first principles calculations without lattice constant relaxation. The dependence of the lattice constant on the stability of ferromagnetism, that is, the total energy difference E FM -E AFM between ferromagnetic and A-type antiferromagnetic structure, is shown in Fig. 8a,b. As for the two lattice constants a and c, the antiferromagnetic structure was stable within the lattice constant change of ± 1.0%. Although it seems that the origin of the antiferromagnetism is associated with the Mn dilemma since the lattice constant a, which corresponds to the nearest-neighbour Mn-Mn distance in τ-phase, is smaller than the critical value of 2.9 Å, the ferromagnetic state tended to stabilize as the lattice constant decreased. This implies the existence of an antiferromagnetic mechanism other than direct exchange coupling. Extrapolating these results, the stabilization of the ferromagnetic structure requires a reduction of the lattice constant of more than 10.0%. Therefore, since the lattice constant change by annealing is less than 0.20%, we conclude that the Mn-Mn distance is not the cause of antiferromagnetism in τ-phase. Our crystal structural analysis revealed the change in Mn composition and the ordering parameter S of τ-phase by annealing. Therefore, we investigate the effect of Mn composition and the ordering parameter S on the stable magnetic structure. The dependence of the Mn composition on the stable magnetic structure was calculated by substituting Mn atoms for Al atoms. On the other hand, the dependence of the order parameter S was calculated by exchanging Mn atoms and Al atoms where the Mn composition is set to 50 at%. In these calculations, there are several non-equivalent configurations due to the arbitrariness of substitution or exchange site. Therefore, the minimum total energy was evaluated by calculating these conceivable non-equivalent configurations. Our calculations find that the antiferromagnetic state is stable for the Mn concentration of 50.0-52.5 at%, but the ferromagnetic state is stable when the Mn concentration over 52.5 at%, as shown in Fig. 8c. This result is consistent with the fact that the conventional Mn-rich τ-phase shows ferromagnetism. This stabilization of ferromagnetism has already been pointed out by previous studies 16,18 . According to S, the antiferromagnetic state is stable as for S > 0.88, as shown in Fig. 8d. These results are quantitatively consistent with showing antiferromagnetism in the 500 °C-annealed sample having S = 0.90 and Mn = 50.0 at% as well as showing ferromagnetism in the as-deposited sample and the 600 °C-annealed sample having S = 0.76, 0.86, respectively. In particular, for the 600 °C-annealed sample, slight Mn-rich composition of 51.7 at% also has contributed to the stabilization of ferromagnetism. www.nature.com/scientificreports/ Finally, we discuss the mechanism of antiferromagnetism in τ-phase. Our calculation clearly showed that the stable magnetic structure in τ-phase is A-type antiferromagnetic and the stable magnetic structure was not strongly affected by the Mn-Mn distance but by Mn occupancy ratio of the Al site, which related to the Mn composition and order parameter S of τ-phase. From these results, it is considered that the origin of antiferromagnetism in τ-phase is super-exchange interaction, which is the magnetic coupling between the magnetic atoms through hybridization with the p-orbital electrons of the non-magnetic ligand. In order to confirm the existence of the super-exchange interaction via p-electrons of Al atoms, the total energy of hypothetical system Mn 50 Mg 50 using the same lattice constants of τ-phase was calculated without the lattice and atom position relaxation. As a result, the ferromagnetic structure is preferred over the antiferromagnetic structure in that system. The total energy difference E AFM -E FM , between A-type antiferromagnetic and ferromagnetic structure, was 55.5 meV/atom. In addition, the results of local partial density of state (LPDOS) of Mn and Al in A-type antiferromagnetic ordering τ-phase MnAl is shown in Fig. 9. The 3d orbit of Mn and 3p orbit of Al is hybrid above the Fermi energy, as previous reports have suggested 24 . Therefore, we conclude that the mechanism of antiferromagnetism in τ-phase is the super-exchange interaction between Mn atoms via p-electrons of Al atoms.

conclusions
We conclude nearly stoichiometric and chemically ordered L1 0 -MnAl having S = 0.90 and Mn = 50.0 at% was obtained by the subsequent annealing of the electrodeposited sample, which improves the order parameter S and increases the Mn composition accompanying preferential decomposition into Al-rich γ 2 -phase. Using neutron diffraction, the magnetic structure of the τ-phase was determined to be A-type antiferromagnetic having a sixfold magnetic superstructure along the c-axis. Our calculation clearly showed that the A-type antiferromagnetic state is stabilized when S > 0.88 or Mn < 52.5 at%. In addition, we conclude that the mechanism of antiferromagnetism in τ-phase is the super-exchange interaction between Mn atoms via p-electrons of Al atoms, and therefore, the stable magnetic structure was not strongly affected by the Mn-Mn distance but by Mn occupancy of the Al site.
Conventionally, in Mn-based magnetic materials, the Mn-Mn distance has been focused based on the simple Beth-Slater picture of direct-exchange 4 . The Mn dilemma represents the difficulty caused by direct exchange coupling between the Mn atoms. However, this study pointed out the super-exchange interaction of Al electrons via p electrons is dominated in τ-phase. Therefore, the Mn-Mn distance does not strongly affect the magnetism in this system. The mechanism of ferromagnetism in the conventional Mn-rich τ-phase is the suppression of the super-exchange interaction due to the substitution the excess Mn atoms for the Al atoms, which reduces the magnetization simultaneously.
For further improvement of magnetization in τ-phase, it may be necessary to add to elements having no valence p-electrons for obtaining high magnetization with ferromagnetic ordering. Furthermore, these findings are considered to be effective for alloys of Mn with elements having p electrons, such as Mn-Ga and Mn-Bi, which also have large potential as a rare-earth free magnets 1,8 .

Methods
Sample preparation 17 . The alloy powders consist of τ-MnAl electrodeposited onto planar copper substrates using an aluminium chloride electrolyte composed of a 51:49 mol ratio of AlCl 3 :NaCl containing MnCl 2 of 1.0 wt%. The electrochemical cell was made of Al 2 O 3 . The cell was heated using a muffle furnace and the temperature was maintained at 300 °C. The counter electrode was an aluminium plate placed parallel to the copper substrate. The alloy powders were electrodeposited galvanostatically at a current density of 40 cm/cm 2 in an Ar atmosphere. After deposition, the powders were collected by decanting an aluminium chloride molten salt and washing the residual salt in water. The powders were subsequently annealed in an Ar atmosphere. www.nature.com/scientificreports/ Magnetization measurements. Magnetization measurements were carried out using a 9 T physical property measurement system with a VSM manufactured by Quantum Design. Specimens for the VSM measurement were prepared by inserting the powder in a 2 mm × 2 mm columnar-shaped measurement capsule. The temperature-dependent magnetization in the low-temperature range of 100-300 K were measured using superconducting quantum interference device magnetometer (Quantum Design, MPMS-Evercool). For the measurement, the specimen with paraffin was placed inside a capsule (Eli Lilly, No.4). The specimen was cooled in zero-field down to 100 K. To magnetize the sample, 50 kOe was applied. Then, the field down to 10 kOe field, and the data were recorded up to 300 K. The temperature-dependent magnetization in the high-temperature range of 300-700 K were measured using VSM (Toei Industry, VSM-5). For the measurement, the specimen with quart glass was placed in a copper capsule. Magnetic-field of 5 kOe was applied, and the data were recorded up to 700 K under an Ar flow.
X-ray diffraction. The XRD measurement for the phase analysis was performed with synchrotron radiation.
The measurement was carried out on beam line BL02B2 at SPring-8 in Hyogo, Japan. A specimen was ground to the size of 0.24 × 0.24 × 15 mm and then sealed in a quartz tube capillary filled with an inert gas. The analysis was performed using the Z-Rietveld software 25,26 . Microstructural analysis. HAADF and EDS images were obtained using the STEM, Titan-G2 manufactured by FEI. Specimens for the STEM were fabricated by a focused ion beam using Versa 3D manufactured by FEI. STEM-EDS maps were obtained using Super-X EDS detector manufactured by FEI and the Bruker Esprit version 1.9 software (https ://www.bruke r.com/produ cts/x-ray-diffr actio n-and-eleme ntal-analy sis/eds-wdsebsd-sem-micro -xrf-and-sem-micro -ct/espri t-2.html).
Neutron diffraction. Neutron diffraction measurements were performed using the time-of-flight neutron diffractometer iMATERIA (beamline BL20, MLF/J-PARC, Japan). A vanadium cylinder was used as the sample holder. The neutron data were collected at 293 K. The analysis was performed using the Z-Rietveld software 25,26 . first principle calculation. The calculations are performed using the frozen-core full-potential projected augmented wave (PAW) method 16 , as implemented in the Vienna ab-initio simulation package (VASP) [27][28][29] . On-site Coulomb interaction of the d orbitals was corrected using the + U method, where U was determined to reproduce the experimental lattice parameters of MnAl (a = 2.77 Å and c = 3.57 Å). The electronic exchange and correlation effect are described within the generalized-gradient approximation (GGA-PBE sol ) 30 to reduce the difference in lattice constant between experimental and calculated one. The energy cutoff of the plane wave basis set is taken as 500 eV. The energy convergence is set at 10 −5 . The supercell was used in the calculations, which consists of 32 atoms (16 Mn atoms and 16 Al atoms). The integrations in the Brillouin zone are performed with k-point grids of 5 × 5 × 5. Unless otherwise noted, the lattice constants, atom position and magnetic moment are relaxed in this study.