Single-Walled Carbon Nanotube Supported PtNi Nanoparticles (PtNi@SWCNT) Catalyzed Oxidation of Benzyl Alcohols to the Benzaldehyde Derivatives in Oxygen Atmosphere

This study reports a developed process which is a general and facile method for the oxidation of benzyl alcohol (BnOH) compounds to the benzaldehyde (BA) derivatives, under mild conditions. The oxidation of BnOH species catalyzed by PtNi@SWCNT in toluene (3 ml) at 80 °C under a continuous stream of O2. Single wall carbon nanotube supported PtNi (PtNi@SWCNT) nanoparticles were synthesized using a single-step modified reduction process. The characterization of PtNi@SWCNT nanocatalyst was performed by transmission electron microscope (TEM), X-ray diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), and elemental analysis by ICP-OES. A variety of BnOH compounds were oxidized by the PtNi@SWCNT catalyst and all the expected oxidation products were obtained in high efficiency in 2 hours of reaction time. TLC was used to monitoring the reaction progress, and the products were identified by 1H/13C-NMR analysis.


Single-Walled carbon nanotube Supported ptni nanoparticles (ptni@SWcnt) catalyzed oxidation of Benzyl Alcohols to the Benzaldehyde Derivatives in oxygen Atmosphere
Haydar Göksu 1 ✉ , Kemal cellat 2 & fatih Şen 2 ✉ this study reports a developed process which is a general and facile method for the oxidation of benzyl alcohol (BnoH) compounds to the benzaldehyde (BA) derivatives, under mild conditions. the oxidation of BnOH species catalyzed by PtNi@SWCNT in toluene (3 ml) at 80 °C under a continuous stream of o 2 . Single wall carbon nanotube supported ptni (ptni@SWcnt) nanoparticles were synthesized using a single-step modified reduction process. The characterization of PtNi@SWCNT nanocatalyst was performed by transmission electron microscope (TEM), X-ray diffraction (XRD), X-ray Photoelectron Spectroscopy (XpS), and elemental analysis by icp-oeS. A variety of BnoH compounds were oxidized by the PtNi@SWCNT catalyst and all the expected oxidation products were obtained in high efficiency in 2 hours of reaction time. TLC was used to monitoring the reaction progress, and the products were identified by 1 H/ 13 c-nMR analysis.
The bimetallic nanoparticles have been recently extensively studied in many applications such as fuel cells, electrochemical sensors, biosensors, solar cells, drug materials, hydrogen storage, etc. [1][2][3][4][5][6] . As a catalyst, bimetallic nanoparticles have many unique properties such as increased efficiency, activity, selectivity, durability, reusability, stability, etc. Those properties are explained by the synergistic effect of two different metal atoms. The catalytic activity is related to the size and shape of the nanoparticles, the interactions between the metal atoms, and the support material. Bimetallic catalysts, basically simplify a complex synthesis and are used to synthesize valuable molecules with higher efficiency, has been used for alcohol oxidation, including fuel cells in recent years 7,8 . On the other hand, the oxidation of primary alcohols is one of the most important tools in organic chemistry for the synthesis of carboxylic acids, aldehydes, and ketones. Even numerous oxidation methods have been developed such as chromium and manganese oxides, hypervalent iodine reagents, pyridine·SO 3 , and NaOCl/TEMPO (TE MPO = 2,2,6,6-tetramethyl-1-piperidinyloxyl); the oxidation by O 2 gas is still common method in research laboratories and industry. Numerous studies for the oxidation of primary alcohols can be found in the literature. Most of these studies are based on the conversion of primary alcohols to carboxylic acids and esters. However, keeping the aldehydes of primary alcohols is quite difficult and requires special systems. Especially in the presence of water, the aldehyde phase of the alcohols in the oxidation stage is not achieved. Since the aldehydes obtained by one stage oxidation of primary alcohols are highly reactive molecules and continue to oxidize, forming carboxylic acids or esters. Therefore, aldehyde compounds formed in the reaction medium should be either rapidly removed from the reaction medium or reactions should be maintained in a non-aqueous medium 9-13 . In the oxidation reactions, organic (nitrogen-containing) and inorganic (K 2 CO 3 , Na 2 CO 3 , NaCH 3 COO, KCH 3 COO, CoCl 2 ) bases are generally utilized 14,15 . However, these oxidation reactions can be conducted for characterization methods. The characterization of PtNi@SWCNT nanoparticles was achieved using, XRD, XPS, and TEM analyses. The X-ray diffraction patterns (θ-2θ scans) were taken on a Panalytical Empyrean diffractometer with Ultima+ theta-theta high-resolution goniometer system using Cu Kα (λ = 1.54056 Å) as the X-ray source. Scans were recorded at 40 kV and 40 mA, in step scan mode between 2θ range of 20 and 90° (scan rate 0.02° 2θs −1 ). X-ray Photoelectron Spectroscopy (XPS) measurements were carried out in a Specs spectrometer instrument. The X-ray source was Mg Kα (1253.6 eV, 10 mA) radiation. Cu double-sided tape (3 M Inc.) was used for the sample preparation. The reference point was C 1 s line at 284.6 eV. TEM images of PtNi@SWCNT nanoparticles have been obtained by a JEOL 200 kV TEM instrument. 1 H and 13 C NMR spectra were recorded on a Jeol ECS 400 MHz spectrometer. All the individual NMR spectra were analyzed using JEOL Delta NMR control and process software.
Inductively coupled plasma optical emission spectrometry (ICP-OES, Perkin Elmer Avio 500 coupled with Ultrasonic Nebulizer) analyses were performed to concentration determination of Pt and Ni after consecutive using of PtNi@SWCNT nanoparticles. The operating parameters of the ICP-OES were as follows: nebulizer flow of 10 mL min −1 ; an auxiliary gas flow of 0.2 L min −1 ; sample introduction of 1 mL min −1 ; in radial mode. www.nature.com/scientificreports www.nature.com/scientificreports/ Thin-layer chromatography (TLC) was performed on 20 × 20 cm plates pre-coated with silica gel, and the mobile phase was ethyl acetate/hexane (v:v = 1:5).
Organic compounds were determined by gas chromatography-mass spectrometry (GC/MS, Agilent) equipped with a mass selective detector and HP-5MS column (30 m, 250 μm, 0.25 μm). The operation conditions of GC/ MS: an ion source, the mass spectrum of the cations produced by 70 eV electron impact ionization; 280 °C of transfer line temperature; carrier gas was He (purity ≥99.99%) with a flow rate of 1 mL/min. Splitless injection mode with 1 µL sample solution was used. The oven temperature program was as follows: hold initial temperature at 100 °C for 0 min, 10 °C/min to 250 °C 31 min, 4 °C/min to 280 °C, hold at 280 °C for 31 min. The compounds were identified according to the mass spectra and their retention time. Results were compared to internal reference library data.

Synthesis of SWcnt.
For the SWCNT synthesis, ferrocene was used as a catalyst precursor, thiophene was growth promoter, and ethanol was carbon source. Ferrocene (0.3 wt%) and thiophene (molar ratio of S/Fe = 0.2) were dissolved in ethanol (99.9%) and placed in an ultrasonic bath for 2 minutes to obtain a homogenous solution. The synthesis was conducted by injection of the solution using a syringe pump at a feed rate of 4-10 µL/ min. The resulting solution was evaporated in a heating line at a constant temperature of 140 °C. It was carried via a mixture of H 2 and N 2 gases with a volume of 800 sccm. The SWCNTs particles were collected at the downstream of the reactor and filtered using a membrane filter 27 .

Synthesis of ptni@SWcnt nanoparticles.
A facile, single-step modified reduction procedure was employed for the synthesis of PtNi@SWNT nanoparticles. Initially, 60 mg of as-synthesized SWCNT, 30 mg of Ni(CO 2 CH 3 ) 2 4H 2 O, and 30 mg of PtCl 4 were dissolved in absolute ethanol. The mixture was kept in a sonicator for 30 min to achieve a homogeneous solution. The mixture was poured into a Schlenk tube and mixed under N 2 gas flow for 1 h, it was mixed for 45 min after the addition of DMAB (148 mg). Subsequent to the mixing procedure, it was refluxed, and the resulting nanoparticles were isolated by centrifugation. The obtained black PtNi@ SWCNT nanoparticles were washed with purified water, and dried in a vacuum oven at a temperature of 150 °C, and used as a catalyst for the redox reactions in this study. www.nature.com/scientificreports www.nature.com/scientificreports/ ptni@SWcnt catalyzed reduction of BA compounds. NaBH 4 (3.0 mmol) was added to a mixture of BA (1 mmol) and PtNi@SWCNT nanoparticles (2 mg) in 3 mL of water/methanol (v/v = 1/2) and the reaction mixture was stirred at room temperature. The reaction progress was checked by TLC. The products were identified by 1 H/ 13 C-NMR analysis. The yields stated in the article are not isolation yields. ptni@SWcnt catalyzed oxidation of BnoH compounds. To a mixture of BnOH (1 mmol) and PtNi@SWCNT nanoparticles (2 mg) in toluene (3 ml) was added KOH (1.5 mmol) and the reaction mixture was stirred at 80 °C under a continuous stream of O 2 for the required time. The reaction progress was observed by TLC. The products were identified by 1 H/ 13 C-NMR analysis. The yields stated in the article are not isolation yields.

Results and Discussion
The crystalline structure of the PtNi@SWCNT was investigated by XRD analysis (Fig. 1). The XRD data exhibited clear diffraction peaks of PtNi@SWCNT. The diffraction peak observed at around 25.1° corresponds with the carbon (0 0 2) reflection of the graphitic planes of the SWCNT (JCPDS card no. 75-1621). The peaks appearing at diffraction angles of 39.8°, 46.2°, 67.7°, 81.5°, and 83.8° (JCPDS-ICDD, Card No. 04-802) are corresponding to the face-centered cubic crystal (fcc) planes of (1 1 1), (2 0 0), (2 2 0), (3 1 1), (222) respectively. There are no noticeable characteristic peaks for Ni and its oxides; however, their existence cannot be discarded due to the fact www.nature.com/scientificreports www.nature.com/scientificreports/ that they may be present as very small crystallites, and alloy formation between Pt and Ni. In addition, a right shift to higher 2θ values was detected on PtNi@SWCNT peaks, compared to Pt@SWCNT, in agreement with Vegard's law 28 , and this is a result of the substitution of smaller Ni atoms.
In electrocatalyst studies, X-ray photoelectron spectroscopy (XPS) is an analytical technique for the determination of changes in the electronic structure based on shifts of the binding energies of core-level electrons. The XPS spectrum of the PtNi@SWCNT was shown in Fig. 2. The XPS peaks were fitted using the Gaussian-Lorentzian method, and the Shirley-shaped background correction procedure was applied. The peaks of Pt 4f 7/2 and Pt 4f 5/2 spectrum appearing at a binding energy of 71.5 eV and 75.0 eV correspond to metallic Pt°. (Fig. 2a). The peaks for Pt 2+ species, such as PtO and Pt(OH) 2 , were observed at 72.7 eV and 76.2 eV, and Pt 4+ species were detected at 74.6 eV and 77.2 eV. According to relative intensities of the peaks, Pt is predominately present in the metallic state (Pt°). The peaks for Ni 2p 3/2 and Ni 2p 1/2 with the binding energies of 856.3 eV and 874.0 eV are characteristic of metallic Ni° (Fig. 2b). The other peaks on Ni 2p spectrum at 861.8, 880.1 eV correspond to Ni 2+ . The characteristic peaks observed in XPS spectra prove the existence of Pt and Ni in the samples. With reference to pure Pt, the Pt 4 f XPS spectrum of PtNi nanospheres experienced peak shifts negatively, which indicates an electronic stage change of Pt when it was alloyed with Ni.
TEM analysis was carried out to determine the morphological structure and particle size of PtNi@SWCNT (Fig. 3). The particles were largely spherical, homogeneously distributed on the SWCNT support, and no agglomeration was observed. As shown in Fig. 3(a), the diameter of SWCNTs was found to be 1.3-2.8 nm. The representative atomic lattice fringes of PtNi@SWCNT was measured as 0.22 nm (Fig. 3(b)), which is quite close to the nominal Pt(111) spacing of 0.23 nm. Furthermore, particle size histogram obtained from counting approximately 300 particles was given in Fig. 3(c) and the mean particle size was calculated as 2.10 ± 0.70 nm. The particle size analysis is compatible with the previous studies in literature 29 .
The selective oxidation performance of PtNi@SWCNT nanocatalyst on BnOH to BA was examined. The performance tests were conducted in the 5 wt% of oxidant catalyst loading; in the presence and absence of a base, K 2 CO 3 , NaHCO 3 , KOH; at room temperature, and 80 °C ( Table 1). Despite of the fact that the reaction time was 5 hours, no products were detected without a base. After 4 hours of reaction time, when 1 mmol of K 2 CO 3 and NaHCO 3 was used, the yield of BA was 12% and 10%, respectively. Adding 1 mmol of KOH and 4 mg of catalyst into reaction medium significantly increased the conversion yield of the reaction (Table 1, entry 4). 2 mg of catalyst was used, the BA was obtained by high conversion yields within 2 hours using 1.5 mmol of the base (Table 1, entry 7). When there was no catalyst in the reaction medium at room temperature, BA formation was not observed (Table 1, entry 8,9).
The presence of molecular oxygen is important in terms of the continuity and efficiency of oxidation reactions. In this study, the absence of molecular oxygen causes a significant decrease in reaction efficiency. Because the catalyst is regaining its activity with molecular oxygen. It is not sufficient to maintain the reaction in air environment when BA from BnOH is present in the medium. In particular, there is a need to provide a continuous flow of oxygen gas to increase the concentration of molecular oxygen in the reaction medium. After optimization experiments, the BA synthesis procedure was carried out from BnOH. It was then determined which BnOH derivatives to work on. The selected BnOH derivatives were molecules that contained electron donor and electron acceptor groups such as 4-hydroxy benzyl alcohol and 4-nitro benzyl alcohol, respectively, as well as steric effects such as anthracene. The results of PtNi@SWCNT nanoparticles catalyzed NaBH 4 dehydrogenation and hydrogenation reactions over a variety of BA derivatives were summarized in temperature. These experimental results suggest that the PtNi@SWCNT nanoparticles are sensitive to the reduction of aldehyde functional groups. In the first stage, some BA derivatives were reduced to the BnOH compounds by transfer hydrogenation, and PtNi@SWCNT nanoparticles were used in this procedure for the first time in the literature. Finally, 1.0 mmol of BA derivatives, 2.0 mg of PtNi@SWCNT, and 3.0 mmol of NaBH 4 exhibited satisfactory performance on the reduction of BA derivatives at room temperature with high conversion yields in water/methanol mixture (1:2, 3 mL) ( Table 2, entry 1-6). Figure 4 indicates the catalytic performance of PtNi@SWCNT nanoparticles on BnOH oxidation. Herein, individual BA derivatives were successfully achieved with high efficiencies by oxidation of various BnOH compounds in 2 hours at 80 °C. For example, the oxidation of BnOH (1) into BA (2) was obtained with 99% efficiency.
Finally, anthracene-9-ylmethanol (33) was converted to anthracene-9-carbaldehyde (34) with 92% efficiency. Synergistic bonds are σ and π component bonds. The Sigma component is frequently encountered, and the electron density of the ligand is given to the metal. π component is a part of the electron density of metal that is given to the ligand that is called back bonding (Fig. 6). The metal must have empty trajectories to obtain the electron density of the ligand and must have the appropriate energy and symmetry-filled orbits to restore (back binding) some of the electron density. In addition, the ligand must have electron density and empty π * orbits in the appropriate energy and symmetry to recover some of the electron density of the metal. In the bond establishment, the empty orbitals of metal overlap with the atom or hybrid orbitals containing the electron pair of the    www.nature.com/scientificreports www.nature.com/scientificreports/ ligand. Moreover, the full orbitals of metal match with the π * orbitals of the ligand. The s, p, and d orbitals can be used here.
The binding event, i.e. the σ component, is generally essential between ligand and metal, in catalytic reactions. But, the back bonding is highly related with the existence of ligand's d orbitals. Accordingly, the molecules are connected to the catalyst surface stronger. If back bonding is not close to the reaction center, reduction in the reaction efficiency is occurred.
Due to the fact that binding event increases the interaction process on the surface of the catalyst and around it of the BnOH derivatives, the increase in the reaction efficiency has occurred. However, due to the limited mobility on the catalyst surface, the reaction efficiency of (4-(methylthio)phenyl)methanol (29) is reduced (Fig. 4, entry  15).
As shown in Fig. 4, the presence of atoms such as halogen, nitrogen, and oxygen in the alkyl groups in the BnOH derivatives increases the conversion yield of the reaction. However, the size of the alkyl groups bound to these heteroatoms ((4-(dimethylamino)phenyl)methanol (3)) or the size of the molecule (anthracene-9-ylmethanol (33)) causes a decrease in the conversion yield of the reaction (Fig. 4, entry 17).
In addition to high catalytic performance, PtNi@SWCNT is also reusable and stable, after 3 rd repeated using ≤95% conversion efficiency was obtained as shown in Fig. 7. Reusability was also proved by the ICP-OES analyses, and no significant loss of Pt and Ni (0.8 and 1.0 ppm leaching to a solution respectively) was observed after three cycles. Figure 8 shows the schematic diagram for the proposed mechanism of oxidation reaction. Initially, the activation of BnOH occurs. Herein, initiating step occurs via coordination of the aromatic ring on the surface of the catalyst and the coupling of the alcohol oxygen to the metal. Then, aldehyde formation is occurred by linking the hydrogen atoms of the hydroxy group and the benzylic position to the catalyst surface. both the coordination and aldehyde formation stages, zero-valent metal is oxidized to +2 state. The oxidized metal ion is re-reduced to zero-valent metal atom in the coexistence of O 2 . As a result of this, catalytic activity is renewed and the oxidation reactions are sustained.
Herein, the coexistence of O 2 , allows the balance between oxidation and reduction to move in the direction of oxidation (Fig. 8). As mentioned in the previous sections, the reaction efficiency decreases in the absence of oxygen. In fact, the final step is inevitable for the hydrogenation reaction, and the resulting BA is converted to BnOH by hydrogenation.
The 3-nitrophenol added to the reaction medium for the test, and it was observed that it converted to 3-aminophenol with a 65% yield in the absence of molecular oxygen (Fig. 9). This result proves the correctness of the idea we suggest.
Eventually, a comparison of the performance of PtNi@SWCNT nanoparticles with previous studies in the literature was given in Table 3 14,23,25,42,43 . It was found that the catalytic performance f PtNi@SWCNT nanoparticles are comparable.

conclusions
In this paper, PtNi@SWCNT nanoparticles have been successfully synthesized using a simple single-step reduction method. PtNi@SWCNT nanoparticles are a promising material for utilization as a catalyst for alcohol oxidation, which is easy to synthesize, have a large surface area, and excellent catalyst properties. The results showed that the synthesized PtNi@SWCNT nanocomposites shown good catalytic performance for the conversion of  Table 3. Comparison with the recent studies in the literature. a GC yield.