Green synthesis of peptide functionalized reduced graphene oxide (rGO) nano bioconjugate with enhanced antibacterial activity

Bioengineered nanoconjugates have enormous potential as a multifunctional platform for biomedical applications. Conjugation between biotic and abiotic materials enables formulation of nanoconjugates with enhanced physico-chemical properties, increased stability and ability to overcome the inherent shortcomings of individual materials. In this study, we report the preparation and biophysical characterization of an antibacterial system formulated by functionalizing reduced graphene oxide (rGO) with an antimicrobial peptide via covalent as well as non-covalent interaction mechanisms. Environmentally benign synthesis approach was adopted for the formation of rGO, using L-ascorbic acid as a reducing agent. Covalently conjugated peptide-graphitic conjugate displayed improved antibacterial efficacy against Escherichia coli with considerably low cytotoxic activity towards erythrocytes in comparison to self-assembled conjugate and rGO alone. The studies described herein are highly significant in the field of biomaterials and aims to open new avenues of research focusing on a plethora of applications as a prospective non-toxic substitute to conventional antibacterial approaches.

peptides, Chicken cathelicidins have been reported to effectively kill a variety of bacterial species inducing little or no resistance 15,16 . In this study we have selected, the N-terminal fragment of Cathelicidin-2 (CATH-2) as the AMP for conjugation to rGO, because of its reported broad-spectrum activity against various pathogenic microorganisms ( Fig. 1) 17,18 .
Conjugation of AMPs with nanoparticles has been proposed to result in increasing the local concentration of the peptide at the site of delivery, thereby increasing the efficacy 3,19 . The probable mechanism engaged in antibacterial activity exhibited by nano bioconjugates can be accredited to membrane stress leading to cell membrane degradation which further results in loss of membrane integrity causing outflow of cell organelles, leading to cell lysis ( Fig. 2) 20,21 .
Numerous peptide-nanoparticle systems formed by application of harsh and toxic reagents have been explored as antimicrobial agents. Such complexes comprise of residual toxic substances and are usually not appropriate for biomedical based applications 22 . However, antibacterial peptide functionalized nanoparticle systems formulated via green route have not been prominently explored.
Motivated by this, we used different approaches to couple the antimicrobial peptide CATH-2 with rGO by covalent and non-covalent interaction mechanism. Covalent interaction between peptide and rGO was established by use of biocompatible crosslinkers; whereas, non-covalent interaction was facilitated by a facile self-assembly approach. Biophysical characterization techniques provided insight into the interaction behaviour and structural properties of the formed nano bioconjugates. The formed conjugates were evaluated for their efficiency to inhibit the growth of E. coli, a gram-negative bacterium. Further, the hemolytic cytotoxicity of the conjugates was also evaluated.
To the best of our knowledge, no study regarding the application of peptide functionalized rGO nano bioconjugate as an effective antibacterial agent has been reported. With further developments, we aim to expand the application of the reported nano bioconjugate as a prospective substitute to conventional antimicrobial approaches.

Results
Synthesis and characterization of L-ascorbic acid reduced graphene oxide. L-ascorbic acid was used as a reducing agent to produce rGO from graphite. It is a mild and nontoxic alternative for conventional reducing agents. Moreover, it can be used for large scale production of rGO. L-ascorbic acid has a tendency to maintain its reducing functionality in acidic as well as alkaline pH. This property aids in converting the residual Mn(VII) ions to a more soluble Mn(II) ions, thereby reducing the potentially hydrophilic, oxygen functionalities containing GO to rGO during the reduction process 11,23 . The crystallographic structure of graphite nano powder, GO and rGO was analysed by conducting X-ray diffraction (XRD) studies. Figure 3(a-c) illustrates XRD patterns of graphite, GO and rGO, respectively.
Graphite shows a single sharp characteristic peak at 26.7° corresponding to the d-spacing with interlayer distance calculated to be 0.34 nm. Whereas, upon reduction by L-ascorbic acid, the graphite peak shifts and gives a broad band centred at 24° and an increased d-spacing of about 0.37 nm. Occurrence of a single peak in graphite scan represents presence of robust interlayer covalent bonds within the carbon layers and existence of weak Van der Waals interactions amid consecutive carbon sheets. After reduction, broadening and shifting of the characteristic diffraction peak of graphite from 26.7° to 24° is attributed to the short-range order in randomly arranged www.nature.com/scientificreports www.nature.com/scientificreports/ stacks along with removal of some oxygen-containing functional groups 24 . This is an indication of graphitic network restoration in rGO by the elimination of oxygen moieties.
Another less intense peak observed at 42° corresponds to occurrence of turbostratic carbon assembly; along with structural defects in rGO, this peak is frequently observed in materials of graphitic origin 25,26 . A small characteristic diffraction peak of graphite oxide at approximately 2θ = 9° remained in the XRD pattern of rGO depicting incomplete reduction of oxygen-containing functional groups. In rGO, d-spacing changed due to the removal of few oxygen containing functional groups which indicates re-establishment of sp 2 network on reduction, composed of free-standing graphene sheets 27 . The interlayer space of rGO is larger than that of pristine graphite, due to the presence of complicated residual contributions of intercalated water molecules between the layers. In comparison to XRD pattern of graphite, rGO displayed an amorphous structure because of decomposition of oxygen-containing groups which also eliminates carbon atoms from the carbon plane resulting in lattice defects 24 . These X-ray diffractograms demonstrate successful reduction of graphite nanoparticles to yield a randomly arranged reduced graphitic compound possessing an exfoliated structure which can prove to be beneficial during conjugation studies.
Spectroscopic characterization of rGo and peptide functionalized rGo-nano bioconjugates. FT-IR spectroscopy of rGO (blue line), rGO-P C (orange line) and rGO-P S (red line) is shown in Fig. 4.
In FT-IR spectroscopy of rGO, the absorption peaks observed at 1569 and 1077 cm −1 can be attributed to C=C alkenes bending confirming the formation and recovery of sp 2 carbon structure of rGO and presence of C-O group, respectively. The discussed rGO peaks show reduction of oxygen-containing groups by the action of reducing agents. The covalent bonding of peptide with rGO was confirmed by the presence of absorption bands at 3331, 2153, 1958, 1644, 1566, 1073 and 679 cm −1 . The broad peak at 3331 cm −1 represents N-H stretching due to secondary amide groups. The weak intensity peak at 2153 cm −1 corresponds to the characteristic peak of C≡C alkynes. Strong peaks ranging from 1644 to 1580 cm −1 attributes to in-plane NH bending vibration from the peptide corresponding to amide bond 27 . Moreover, the representative peak of C-H binding at 1958 cm −1 is also exhibited in rGO-peptide (rGO-P C ) spectrum, which confirms covalent binding of peptide with rGO 28 . The peak at 679 cm −1 is ascribed to N-H bending vibrations of amine.
Spectra of rGO-P S exhibits peaks at 3363, 2251, 2154, 1959, 1641, 1078, 984.5, 854 cm −1 . The strong band at 3363 cm −1 corresponds to N-H stretch of aliphatic primary amines. The presence of C-O alcohol group was revealed from the peak at 1078 cm −1 . The spectrum around 2154 cm −1 attributes to C≡C alkynes. Similar peaks of amide bond around 3400 cm −1 and 1600 cm −1 in both the conjugates confirm absorption of peptide 28 . In the rGO conjugates, the O-H vibrations diminished whereas the carbonyl C=O peaks appeared, but with weaker intensities. The strong IR peak observed near 2300 cm −1 is due to the -NCO vibration which clearly indicates the www.nature.com/scientificreports www.nature.com/scientificreports/ formation of amides from peptide/reduced graphene oxide COOH group 27 . The FT-IR spectra of the peptide-rGO complex displays modification of rGO by peptides.
The presence of elements carbon (C), oxygen (O), nitrogen (N) and sulphur (S) was identified in the synthesized rGO-peptide nano bioconjugates (rGO-P S and rGO-P C ) by energy-dispersive X-ray (EDX) spectroscopy ( Table 1). Presence of higher percentage of oxygen along with low carbon percentage was observed in rGO as compared to graphite.
Increase in percent oxygen content was observed in both conjugates i.e., rGO-P C and rGO-P S . Figure 5 depicts the mapping results of the conjugates revealing presence of other elements such as nitrogen and sulphur. The increased oxygen content of the conjugates can be attributed to the side chains of the various amino acids of the peptide.   www.nature.com/scientificreports www.nature.com/scientificreports/ Microscopic characterization of rGo and peptide functionalized rGo-nano bioconjugates. Transmission Electron Microscopy (TEM) was used to measure the particle size and investigate the morphology of the samples; Fig. 6 reveals rGO structure before conjugation (a), rGO-P C (b) and rGO-P S (c), respectively at 100 nm magnification. TEM micrograph of rGO reveals a transparent layered rGO with few wrinkles on its surface. The edges of the sheet appeared to be smooth. rGO mostly consists of exfoliated, few-layered sheets, that are wide and flat. Further, TEM images reveal that the oxidation-reduction process leaves disordered carbon inclusions within the sheets depicting successful reduction of graphite to rGO. The exfoliated edges of rGO sheets act as binding sites for peptides 29 . The TEM images of rGO-P C shows the presence of a dense network of peptide on the surface of rGO sheets. This changed the morphology and thickness of rGO sheets confirming the covalent conjugation of peptide on rGO sheets. Abundant peptide fibrils filled the entire field of vision of rGO surface.
Studies show that rGO can be functionalized by covalent attachment of atoms or molecular groups to sp 2 carbons. Such modifications maintain the 2-D lattice of rGO, however, due to the loss of the π-conjugated electron cloud present above and below the rGO plane, there are dramatic changes to its properties. rGO lends itself to covalent functionalization due to the presence of defects in the graphene lattice that act as reaction sites 30 . TEM images of rGO-P S reveal abundant deposition of peptides mainly at the edges of the rGO flakes. A high-resolution scan of the complex tip was analysed and thickness was observed to be significantly larger than the thickness  www.nature.com/scientificreports www.nature.com/scientificreports/ measured for isolated rGO flakes. The anchoring force that enables the binding of peptides on the edges or planar rGO surface can be attributed to electrostatic or π interactions. Molecules that can be tailored to recognize and interact either on the planar surface or edges of rGO can prove to be beneficial in modulating properties of nanoconjugates 31 . The size of rGO and peptide was found to be 16 nm and 7 nm, respectively. Significant changes were observed in the size after formation of the conjugates. The conjugate formed by self-assembly was observed to be 24 nm in size with 18 peptides bound to an individual sheet of rGO. This calculation was done using TEM images by a protocol 32 , already described in the literature.
Water contact angle measurement. Wettability of a nanocomposite is an important parameter to study the interaction between water molecules and material surface. Wettability and adhesion analysis are useful in regulating the nanostructure and chemical configuration of nanomaterials 33 . The water contact angle (WCA) obtained between water droplet and Graphite, rGO, rGO-P C and rGO-P S are 140°, 44°, 20° and 23°, respectively (Fig. 7).
Graphite exhibited highest WCA at 140° amongst the samples being evaluated. A material is said to be hydrophilic when it exhibits a WCA of less than 90° and hydrophobic in case the angle is more than 90°. Therefore, it can be stated that graphite is hydrophobic in nature. The hydrophobicity exhibited by graphite can be attributed to numerous reasons like lack of polarity due to presence of carbon atoms in its structure and adsorption of hydrocarbons from air which causes decrease in the surface energy of the substrate thereby increasing its hydrophobicity. High contact angle value also indicates smoothness in graphite's topology 34,35 . A decrease in hydrophobic behaviour was displayed by rGO (44°) synthesized from graphite nanopowder. It can be associated to high degree of reduction leading to removal of oxygen thereby enhancing the corrugation on its surface. Conjugation of rGO with peptide caused considerable increase in wettability from 44° to 20° in rGO-P C and 23° in rGO-P S . Both the prepared conjugates are observed to be hydrophilic in nature due to addition of negatively charged functional groups present on the rGO-peptide along with presence of Van-der Waals interactions between the conjugate 36 . Numerous factors affect the WCA in graphitic nanocomposites like surface morphology, number of layers present, temperature of thermal treatment, method employed for sample deposition and environmental factors like relative humidity 37,38 . Understanding of the wettability characteristics of graphene-based nanocomposites provides direction to the research towards specific biomedical applications.
Antibacterial activity. Antibacterial activity of rGO, peptide and peptide conjugated rGO complex (rGO-P C , rGO-P S ) was evaluated against Escherichia coli (E. coli) as a model bacterium since it is the most prevalent gram-negative infection-causing agent in humans 39 . The concentration dependent bacterial inhibitory activity of GO and antimicrobial peptide was studied by performing MIC (Minimum Inhibitory Concentration) method. MIC is interpreted as the required minimum inhibitory concentration for bacterial membrane disruption. The samples were incubated with E. coli cells at different concentrations ranging from 500-7.6 µg/ml for 16 hours. The MIC of GO and antimicrobial peptide was found to be 125 and 64 μg/mL, respectively. Further, agar well diffusion method was performed to evaluate the zone of inhibition formed by rGO and the synthesized conjugates. As displayed in Fig. 8, rGO-P C exhibited a higher antibacterial activity followed by rGO-P S . At 125 µg/mL the zone of inhibition diameter for rGO, rGO-P C and rGO-P S was observed to be 11 mm, 15 mm and 13.2 mm. At 250 µg/mL a clear zone surrounding the sample wells was observed to be 13.27 mm, 21.81 mm and 16.50 mm of rGO, rGO-P C and rGO-P S, respectively.
The occurrence of clear zone is an indicator of antibacterial activity of the samples against E. coli. The zone of inhibition is more for rGO-P C , indicating a higher inhibitory efficacy, followed by rGO-P S in comparison to rGO. rGO structure comprises of sharp edges called "nano-knives". Upon interaction, these nano-knives disrupt the bacterial membrane thereby causing DNA leakage and consequently death of the pathogen 20 . It can be inferred that conjugation of peptides with rGO, imparted antibacterial property to the graphitic material. The difference in the antibacterial activity of the two peptide conjugates lies in the peptide conjugation process and the mode of action of antimicobial peptides. AMPs kill bacteria by disrupting the cell membrane through barrel stave model or toroidal model 40 . In this mechanism of action the amino acid side chain plays a very importat role. The cationic side chains aid in the interaction of the peptide with negatively charged phospholipids of the bacterial membrane and hydrophobic and aromatic side chains help in disruption of the membrane, causing increased permeability www.nature.com/scientificreports www.nature.com/scientificreports/ leading to leakage of cell organelles thereby causing death of the bacteria 41 . When we form a conjugate between peptide-rGO through covalent modification method the side chain functionalities are free to carry out their usual role of bacterial membrane disruption.Whereas, in self-assembly conjugation the peptide adheres to the rGO surface through non-covalent interactions with the various side chains, thereby making them unavailable to carry out their function of membrane disruption hence explaining the reported increase in antibacterial activity of the conjugate formed by covalent interaction method. As a matter of fact, surface neutralisation of the bacterial membrane is an important physicochemical parameter governing the antibacterial activity of potential antibacterial conjugates which come directly in contact with the bacterial surface. Previous studies have reported that untreated E. coli exhibits a negative zeta potential usually in the range of −23.0 to −44.0 to mV 42,43 . Whereas, both antimicrobial peptides and rGO, possess a positive zeta potential value, thereby having the capability to neutralize negative charge on E. coli surface and exhibit bactericidal activity 44,45 . In-vitro Hemolytic activity. To evaluate the efficacy as a therapeutic agent the hemolytic activity of rGO, rGO-P C and rGO-P S was determined by measuring their effect on blood samples (Fig. 9). The compromise of RBC membrane by rGO and the formed conjugates was studied in a dose dependent manner.
In-vitro hemolytic assay enabled quantification of hemoglobin release as a result of RBC (Red blood cell) membrane lysis. It was observed that, both the conjugates exhibited a negligible hemolytic activity as compared to rGO alone. rGO-P C displayed a significantly lower hemolysis percentage as compared to rGO-P S . The maximum hemolysis value was observed to be less than 22% at a concentration of 500 µg/mL by rGO-P C conjugate whereas, at same concentration rGO-P S exhibited 28% cell lysis. This may be attributed to the fact that the peptides self-assembled at the edges of rGO leaving its surface exposed to interact and disrupt the RBCs more readily 46 . On the other hand, covalently attached peptides mask the electrostatic moieties present on the surface of rGO. Hence, it was observed that the hemolytic cytotoxicity caused by rGO was higher in comparison to peptide whereas, rGO-P C displayed a lower hemolytic cytotoxicity in comparison to the self-assembled conjugate.

Discussion
A sustainable peptide functionalised rGO conjugate system with a potential to exhibit reduced cytotoxicity and enhanced antibacterial activity was successfully synthesized through application of green chemistry approach. The characterization of the nanoconjugate uses XRD, FT-IR, EDX, TEM and WCA techniques. It was observed that corrugations present on rGO lend themselves to covalent and non-covalent coupling reactions. Thereby, emphasizing on the importance of nanoconjugate structure between rGO and peptides and its remarkable impact on the antimicrobial and hemolytic properties. WCA study revealed a decrease in hydrophobic behaviour of rGO making it hydrophilic upon conjugation with peptide molecules which is an essential characteristic for utilization of conjugate in therapeutic applications.
Enhanced antibacterial activity against E. coli along with decrease in hemolysis was exhibited by covalently conjugated peptide-rGO nano bioconjugate. The reported bioengineered nanoconjugate aims to open new avenues for diverse applications such as prospective substitutes to conventional antibacterial platforms being used in sensing to drug delivery scaffolds. Further, it may find its future as an antibiofouling membrane in biomedical devices. This type of peptide functionalized rGO nanoconjugates can serve as suitable candidate for theranostic based applications with improved activity.

Methods
No experiments were performed on humans or human tissues. Hemolysis analysis was performed using human blood by taking a written informed consent from the volunteer prior to the commencement of the study as per the declaration of Helsinki, 2013, World Medical Association. The experimental protocols were approved by the Research Monitoring Committee, Panjab University and also, Institutional Biosafety Committee, Panjab University, Chandigarh, India (IBSC/PU/2019/158). Apparatus. X-ray Diffraction (XRD) measurements were carried out using X'Pert Pro XRD equipped with x'Celerator solid-state detector. Fourier-Transform Infrared Spectroscopy (FT-IR) studies were performed using Perkin Elmer -Spectrum RX-FT-IR by casting sample on potassium bromide (KBr) pellets within a scan range of 4000-400 cm −1 . KRÜSS-DSA25E was used to evaluate hydrophilic/phobic behaviour of nanoparticle membranes by measuring static contact angle of a water droplet at room temperature (37 °C). Transmission Electron Microscopy (TEM) was used to study the morphology by using TEM, Hitachi (H-7500) 120 kV. The samples were prepared using the drop casting method. Minimum Inhibitory Concentration (MIC) was evaluated by observing readings using ELISA plate reader.
Green synthesis of reduced Graphene oxide. Reduced graphene oxide was prepared using green approach reported previously in the literature 23 . Initially, 1 g of graphite nanopowder was introduced to 50 mL concentrated H 2 SO 4 followed by constant stirring in a bath containing ice cold water. 3 g KMnO 4 was slowly added to the mixture by maintaining the temperature below 10 °C. The obtained suspension was stirred using a magnetic stirrer for 25 minutes at 37 °C followed by 5 minutes sonication treatment in an ultrasonic water bath. The stirring-sonication process was repeated several times. 200 mL distilled water was added to the solution to stop the reaction. The pH of the obtained solution was adjusted to ~6 by addition of 1 M NaOH. Reducing solution was prepared by dissolving 10 g L-ascorbic acid in 100 mL distilled water. The solution was added to the exfoliated graphite oxide suspension slowly. Reduction was performed by heating the solution at 95 °C for 1 hour. After the reduction process was over, black precipitates were obtained by filtering the solution through cellulose filter paper. The precipitates were consecutively washed with 1 M HCl solution and distilled water to obtain a neutral pH 47 . Fine rGO powder was obtained by freeze-drying the filtrate for 2-3 days.

Synthesis of peptide functionalized nano bioconjugate via different interaction mechanisms.
Peptide was covalently conjugated with rGO by a method reported previously 48 . In this study, covalently conjugated rGO-peptide complex is abbreviated as rGO-P C. In a typical protocol, powdered rGO was dissolved in de-ionized water followed by sonication for 30 minutes to obtain a clear solution of rGO. Cross-linkers, 1-ethyl-3 -(3-dimethylaminopropyl) carbodiimide hydrochloride (EDC) and N-Hydroxysuccinimide (NHS) were successively added into the rGO solution and sonicated for 1 hour to generate semi-stable NHS esters linkage with rGO. Then, pH of the mixture was adjusted to 8. The peptides (dissolved in phosphate buffer solution (PBS), 0.145 mM, 0.1 mL) were added to the obtained mixture followed by incubation at 4 °C in dark for 12 hours to enable cross-linking of the NHS esters with peptides. Unbound peptides were removed from the final solution by centrifugation at 11,750 g for 30 minutes. The obtained sediment was then re-dispersed in de-ionized water and centrifuged several times to obtain a homogenous solution.
Whereas, the non-covalent interaction between peptide and rGO complex, abbreviated as rGO-P S was obtained by using a protocol described earlier 49 . Peptide was mixed with rGO suspension in 9:1 ratio (v/v) in PBS followed by incubation at 25 °C for 5 minutes. www.nature.com/scientificreports www.nature.com/scientificreports/ calculation for number of peptides molecules bound with a nanoparticle. The number of peptide molecules binding with one rGO nanoparticle was obtained by the following equation (Eq. 1) 50 .
- pep  3  rGO  3  pep  3 where, R rGO-pep = Radius of conjugated nanoparticle R rGO = Radius of rGO R pep = diameter of peptide Hemolysis assay. The hemolytic assay of rGO and peptide functionalized conjugates (rGO-P C , rGO-P S ) was performed according to the protocol reported previously in literature 46 . Briefly, fresh Ethylenediaminetetraacetic acid (EDTA)-stabilized human whole blood samples were collected from a healthy volunteer. Whole blood was added to PBS followed by centrifugation to isolate Red Blood Cells (RBCs) from serum. Separated RBCs were washed 4 times using PBS at 500 g for 10 minutes at 5 °C. The washed RBCs were resuspended in PBS and stored at low temperature till further use. To test the hemolytic activity of rGO and nano bioconjugates samples, diluted RBC suspension was added to rGO and conjugate suspension solutions in PBS at different concentrations (0-500 μg mL -1 ). DI water (+RBCs) and PBS (+RBCs) were used as the positive control and negative control, respectively. All the samples were placed on a rocking shaker in an incubator at 37 °C for 3 hours. After incubation, the samples were centrifuged at 10,016 g for 3 minutes. Following the literature described protocol 46 , absorbance of hemoglobin in the supernatant was measured at 540 nm using a spectrophotometer.
Minimum inhibitory concentration determination. Microtiter broth dilution method was used to determine the MIC as previously described 32 . MIC is defined as the value of minimal concentration that inhibits visible growth of microorganisms. E. coli was cultured according to the ATCC protocols/specifications. The bacterial culture was inoculated in Luria-Bertani (LB) broth and was left to grow for 12 hours at 37 °C and harvested in the mid-exponential growth phase to obtain a final concentration of 10 5 colony forming units (cfu)/mL followed by centrifugation. The obtained pellet of cells was washed three times and re-suspended in PBS to remove residual macromolecules and other constituents. Then, growth of E. coli was monitored spectrophotometrically by measuring the absorbance at 600 nm. Bacterial cell suspension was diluted up to the desired concentration of 10 5 cfu/ mL to bring the desired initial optical density. For MIC protocol, in each well of 96-well plates containing serially diluted samples of rGO, AMP, rGO-P S and rGO-P C were inoculated with bacterial suspension. To avoid any contamination, all the experimental work was done under laminar hood. Then, the samples were allowed to mix with LB media by using shaker at 37 °C for 3 hours followed by overnight incubation at 37 °C. Absorbance was observed at 600 nm after 16 hours and 24 hours, respectively. Microbial suspension in the absence of rGO-peptide conjugate was used as the negative control, while DI water was treated as a positive control. All experiments were performed in triplicates to avoid errors.
Well diffusion method. Antibacterial activity of the synthesized rGO, rGO-P C and rGO-P S was determined, using the agar well diffusion assay method 51,52 . Approximately 20 ml of molten and cooled media (Nutrient agar) was poured in sterilized petri dishes. The plates were left overnight at room temperature to check for any contamination to appear. The bacterial test organisms were grown in nutrient broth for 24 hours. A 100 ml nutrient broth culture of each bacterial organism (1 × 10 5 cfu/ml) was used to prepare bacterial lawns. Three agar wells of 5 mm diameter were prepared. The wells were loaded with 20 µl of the synthesized nanoparticles. The plates containing the bacterial and nanoparticles were incubated at 37 °C. The plates were examined for evidence of zones of inhibition, which appear as a clear area around the wells. The diameter of such zones of inhibition was measured for each sample and expressed in millimetre.