Direct Measurement of the Radiative Pattern of Bright and Dark Excitons and Exciton Complexes in Encapsulated Tungsten Diselenide

Abstract

The optical properties of particularly the tungsten-based transition-metal dichalcogenides are strongly influenced by the presence of dark excitons. Recently, theoretical predictions as well as indirect experimental insights have shown that two different dark excitons exist within the light cone. While one is completely dark, the other one is only dipole forbidden out-of-plane, hence referred to as grey exciton. Here, we present angle-resolved spectroscopic data of a high-quality hexagonal-BN-encapsulated WSe2 monolayer with which we directly obtain the radiation pattern of this grey exciton that deviates from that of the bright exciton and other exciton complexes obtained at cryogenic temperatures.

Introduction

Transition-metal dichalcogenides (TMDCs) have recently drawn lots of attention due to their extraordinary rich exciton physics1, showing trions2,3, biexcitons4 and other higher-order exciton complexes5,6. Furthermore, caused by their huge binding energy, higher-order states of the Rydberg-like series can be even seen at room temperature7,8. In addition, even polaritons9 and valley polaritons10,11 can be observed in suitable microcavity structures at these temperatures. With recent publications, it has been revealed that several dark excitons12,13 exist that strongly affect the dynamics14,15 and spectral features13,16 of the system. While there have been several experimental studies for the dark exciton17,18,19,20, little has been reported about their emission characteristics.

Recent detailed group-theory analysis of the possible excitons’ branches15 of WSe2 has shown that four different exciton configurations exist within the light cone at the A-exciton peak (cf. Figure 1). Firstly, two bright excitons (Γ6) at K respectively K’ are provided, where hole and electron exhibit the same spin. Secondly, owing to a small but nonnegligible intravalley interaction, two more possible states arise that represent a coherent superposition of intervalley excitons composed of the spin-forbidden transition across K and K’ valley (irreducible representations Γ4 and Γ3). A schematic two-particle picture for these species is shown in Fig. 1a, whereas their radiation pattern is indicated in Fig. 1b. The Γ4 state transforms like a z-component of a vector of D3h group, rendering it a dipole-allowed transition for z-polarization (corresponds to the direction out of plane, as indicated by small arrows attached to the exciton representation in Fig. 1b). In contrast, the Γ3 state is completely dark, i.e. it cannot couple to the electromagnetic field.

Figure 1
figure1

Schematic drawing of the excitonic non-degeneracy and the dark exciton landscape in tungsten diselenide. (a) Possible bright and dark exciton states for neutral WSe2 arising from the crystal symmetry, indicated in the two-particle picture (energy E vs. centre-of-mass momentum Q) around zero momentum (Γ point). The bright exciton (X0 – Γ6) is separated from the grey exciton (XD,g – Γ4) and the dark exciton (XD – Γ3). Arrows indicate the optical excitation of the respective states. In contrast to bright excitons, the grey exciton is only dipole allowed for z-polarization (corresponding to an out-of-plane dipole). A sketch of the expected radiation pattern for the excitons with different symmetries is shown in (b).

This bears huge implications, as the Γ4 can only emit in the plane and not out of the plane. The energetic difference between bright and grey exciton will be here labelled Δ, whereas the one between grey and dark exciton will be represented by δ (cf. Fig. 1a).

This implication has already been investigated using a micro-photoluminescence (µ-PL) setup with separate detection paths for optical x- and z- polarisation17 for encapsulated samples. For a bare substrate-supported monolayer at room temperature, the radiation pattern of emission has also been addressed by Fourier-space spectroscopy21. However, to the best of our knowledge, no direct measurement of the radiation pattern has been performed for the dark exciton. Here, we present an angle-resolved photoluminescence (PL) study with the focus on the distinct radiation patterns of bright and dark states.

Results

The angle-resolved photoluminescence measurement has been carried out on an h-BN encapsulated WSe2 monolayer. An atomic-force microscopy (AFM) image of the assembled stack is shown in Fig. 2a. Experiments were performed under pulsed quasi-resonant excitation with an effective detuning of 54 meV to the bright exciton. A schematic of the detection concept is presented in Fig. 2b.

Figure 2
figure2

Sample image and measurement concept. (a) AFM measurement of the sample and (b) conceptual drawing of the measurement showing a schematic radiation pattern for an in-plane radiation from the exciton and the resulting expected intensity distribution in the back-focal (BF) plane of the microscope objective.

The corresponding two-dimensionally plotted (2D) PL spectrum (energy as a function of emission angle) can be seen in Fig. 3a, which is displayed in false-colour linear intensity scale (white: minimum, dark blue: maximum). Several PL peaks can be identified, which are attributed to a variety of excitonic species, ranging from neutral exciton (X°), charged species (X), biexciton (XX) to grey (X°D,g) and dark (XD) excitons. Some peaks feature a fine structure, which is taken into account, whereas some peaks arise from acoustic (ac) or optical (op) phonon sidebands (SB), as labeled in the line spectrum in Fig. 3b. For clarity and linewidth analysis, the angle-integrated spectrum has been fitted with a sum of Lorentzian curves (see Fig. 3b), which can be used to describe nearly-homogeneously broadened excitonic lines. For the sake of comparison, all species have been fitted with the same line profile. The obtained line parameters are summarized in Table 1. The peak positions above 1.67 eV are in agreement with Barbone et al.5 (X°, XX°1, XX°2, Xinter, Xintra, XD,g, XX) and Chen et al.6 (X°, XX°, Xinter, Xintra, XD,g, XX), while the low energy feature can be explained by the predicted phonon-assisted sideband13 emission from the dark excitons (K-K’ and K-Λ transitions). As encapsulation is known to change the band structures as well as the exciton binding energies, above comparison are only done with similarly encapsulated samples. The bright–grey splitting is extracted from the spectrum with Δ = 43 meV. Taking the phonon-band structure from Terrones et al.22 (with phonon wavenumbers LO 260 cm−1, TO 2 cm−1, LA 125 cm−1 TA 100 cm−1) into consideration, the energetic position of the dark exciton arising from the K-K’ transition can be calculated as 1.681 eV and the one from the K-L transition as 1.690 eV, which are in good agreement with predicted values from Brem et al.13. To further confirm the identification as phonon sidebands, a temperature series has been performed (see Fig. SI.4), the experimental data of which well resembles the prediction of Brem et al.13.

Figure 3
figure3

Angle-resolved PL spectrum and emission pattern. (a) 2D false-colour contour plot of an angle-resolved PL spectrum of the encapsulated WSe2 monolayer under pulsed excitation at 1.789 eV with an excitation density of 78 µJ/cm2 at 10 K. (b) Corresponding angle-integrated line spectrum (from red-boxed region in a) showing several excitonic features as well as excitonic phonon sidebands. A fit with multiple Lorentzian curves is shown on top of the measured spectrum (dotted curve) with underlying individual peaks labeled (solid curves). (c) Comparison of the experimentally obtained radiation patterns for both the bright and the grey exciton to the simulated results. For the in-plane dipole (IPD), the contribution of dipoles perpendicular to the excitation arising from valley dephasing were considered in the simulation, too. Therefore, a degree of linear polarization of 5% was determined from measurements (Fig. SI.3). All intensity scales are linear.

Table 1 Extracted parameters of the PL peaks obtained under quasi-resonant pulsed excitation. A multi-peak fit with Lorentzian line profiles yields the following central energies of different excitonic (X) species and their full width at half maxima (FWHM). The corresponding spectrum with labeled features is shown in Fig. 3b.

The grey exciton can be easily identified in the angle-dependent spectrum, as it shows a clearly deviating radiation pattern (for a schematic see Fig. 2b). Its position agrees with aforementioned studies5,6,13,17. In such 2D spectrum, bright excitons feature an almost constant intensity for all collected angles, while the rather flat profile shows slightly reduced intensities at higher angles. In contrast, the grey exciton is hardly present at 0° emission angle (normal to the sample surface) but exhibits a drastic increase in intensity towards the detection limit of emission angles due to the finite numerical aperture of the objective used in the experiment. A minor tilt in the sample plane with respect to the objective normal even allows us to detect an angle span of approximately +41 to −31°.

To highlight the clear differences in the radiation pattern, the corresponding PL intensity as a function of the emission angle is shown as a polar plot for both the grey and bright neutral exciton in Fig. 3c. The intensity levels are in relation to Fig. 3a and due to a varying background signal level in the range of different densely-packed species, the two species can show different intensity levels at 0°. Astonishingly, one can unambiguously identify the grey exciton due to its expected behavior of radiating in the WSe2 plane instead of perpendicular to the monolayer. This does not only provide experimental evidence of such a Γ4 species or give a tool at hand to distinguish them from different excitonic modes, but it also verifies the prediction made by group-theory analysis (cf. Robert et al.15). In fact, all other excitonic modes such as trions, biexcitons and phonon sidebands show a similar pattern as the representative neutral bright exciton.

From first sight it is clear that the measured patterns do not resemble the well-known dipole radiation pattern. The modification can be a consequence of the surrounding dielectrics and occurring interferences in a multilayer structure. However, in order to verify that the distinct patterns really arise from an in- and out-of-plane dipole, an electromagnetic simulation was done to calculate the farfield pattern. Hereby, the anisotropy of h-BN and WSe2 was explicitly taken into account (for further details we refer to the Methods section). Indeed, as can be seen by Fig. 3c, the simulated pattern and the measured pattern are in good agreement with each other. Generally, it can be stated that, for both resonances, the main lobe is surprisingly not mostly directed to the substrate. While being modified by the encapsulation, the difference between the two radiation patterns is still striking. The detailed analysis of the polarization from the simulation can be found in the Supporting Information together with a co- and contra-polarized PL measurement. While the general radiation patterns are not changing, the grey exciton can experimentally only be seen in a cross-polarized measurement, similar to the simulation (cf. Figs. SI.1, SI.2 and SI.3).

Conclusion

The photoluminescence of h-BN-encapsulated WSe2 was analyzed by means of angle-resolved PL spectroscopy. A rich spectrum with numerous excitonic features was obtained that agrees well with previous predictions and measurements on high-quality samples. Strikingly, angle-resolved measurements allow one to clearly distinguish in-plane emitting from out-of-plane emitting excitons, as the analysis of the radiation patterns from excitons shows agreement with electrodynamic simulation. While most of the features show almost no angle dependence, the grey exciton’s signal rises markedly towards higher angles, as predicted for this species. This provides a unique tool for both monolayer samples as well as multilayer stacks, in which various intra- and interlayer excitonic features can form particularly at cryogenic temperatures. This motivates further studies involving charge transfer excitons or hybridized states with partial charge transfer, where a change of dipole moment direction is expected as well.

Methods

Sample fabrication

Tungsten diselenide (WSe2) bulk single crystals were grown in an excess selenium flux (defect density: 5 × 1010/cm2). For encapsulated samples, monolayer WSe2 and h-BN were first exfoliated from bulk single crystals onto SiO2. For WSe2, the SiO2 substrate was first exposed to an O2 plasma step before exfoliation. Monolayers and thin h-BN were both identified by optical contrast using a microscope. Afterwards, a dry stacking technique using polypropylene carbonate (PPC) on PDMS was used to pickup and stack h-BN/WSe2 layers. First a top layer of h-BN is picked up at 48 degrees C, then WSe2, and finally the bottom layer of h-BN. After each h-BN pickup step the PPC is briefly heated to 90 C to re-smooth the PPC and ensure a clean wave front. For transferring the stack onto a clean substrate (~290-nm SiO2 on Si), the substrate is first heated to 75 degrees C, the stack is then put into contact, and gradually heated to 120 degrees C. Afterwards, the PPC/PDMS is lifted and the substrate is immersed in chloroform and rinsed with IPA to remove polymer residue. Atomic-force microscopy confirmed a total stack thickness of ~40 nm (~10 nm + ~30 nm for the encapsulating top and bottom h-BN, respectively).

PL measurement

The measurements were performed using a conventional 4f µ-PL setup with confocal selection. The sample was mounted in a continuous-flow cryostat at high vacuum and was cooled down to 10 K. A 40x (NA 0.6) microscope objective was used to focus a pulsed Titan-Sapphire laser at 1.789 eV onto the sample. A short-pass filter for 700 nm was used to shape the pulse in front of the sample. A long-pass filter 700 nm and a polarizer after the sample were used to suppress the laser in the collection path of the PL signal, which was detected by a monochromator with nitrogen-cooled camera.

Simulations

The farfield pattern of the given structure was simulated using CST microwave studio. The thicknesses for the simulation were taken from the AFM measurement of the structure. Furthermore, the anisotropic refractive index of h-BN was taken from Segura et al.23 and for WSe2 a hybrid approach was taken. The out-of-plane refractive index was taken from Laturia et al.24, \({{\epsilon }}_{\infty ,z}={{\epsilon }}_{s,z}=7.5\). For the in-plane permittivity, a Lorentz model was employed to account for the resonance of the bright A-1s transition. Here, the following values were used: \({{\epsilon }}_{\infty ,x,y}=15,\,{{\epsilon }}_{s,xy}=15.22\) and a damping frequency of 4.77 THz. The contribution of the excitons, especially the grey exciton, to the permittivity in the out-of-plane direction is about 1000 times weaker than for the in-plane component17,25, giving no significant contribution to the permittivity. Therefore, this contribution was neglected for the simulation. For silicon oxide and silicon, they were taken from the programs database. The resulting farfield patterns were analyzed in terms of polarization by projecting them on the unit vector of the radiation sphere using the Ludwig 3 convention.

Visualization

The schematic depiction of the WSe2 monolayer in Fig. 1b is based on crystallographic data provided by the Materials Project26 and drawn by the tool Mercury27.

References

  1. 1.

    Wang, G. et al. Colloquium: Excitons in atomically thin transition metal dichalcogenides. Rev. Mod. Phys. 90, 21001 (2018).

    MathSciNet  Article  CAS  Google Scholar 

  2. 2.

    Plechinger, G. et al. Trion fine structure and coupled spin-valley dynamics in monolayer tungsten disulfide. Nat. Commun. 7, 1–9 (2016).

    Article  CAS  Google Scholar 

  3. 3.

    Jadczak, J. et al. Observation of three-particle complexes in WS2 monolayers. arXiv 1612, 04122v1 (2016).

    Google Scholar 

  4. 4.

    You, Y. et al. Observation of biexcitons in monolayer WSe2. Nat. Phys 11, 477–481 (2015).

    Article  CAS  Google Scholar 

  5. 5.

    Barbone, M. et al. Charge-tuneable biexciton complexes in monolayer WSe2. Nat. Commun. 9, (2018).

  6. 6.

    Chen, S. Y., Goldstein, T., Taniguchi, T., Watanabe, K. & Yan, J. Coulomb-bound four- and five-particle intervalley states in an atomically-thin semiconductor. Nat. Commun. 9, 1–8 (2018).

    Article  CAS  Google Scholar 

  7. 7.

    Chernikov, A. et al. Exciton binding energy and nonhydrogenic Rydberg series in monolayer WS2. Phys. Rev. Lett. 113, 1–5 (2014).

  8. 8.

    Li, Y. et al. Measurement of the optical dielectric function of monolayer transition-metal dichalcogenides: MoS2, Mo S e2, WS2, and WS e2. Phys. Rev. B 90, 1–6 (2014).

  9. 9.

    Liu, X. et al. Strong light-matter coupling in two-dimensional atomic crystals. Nat. Photonics 9, 30–34 (2014).

    ADS  Article  CAS  Google Scholar 

  10. 10.

    Sun, Z. et al. Optical control of roomerature valley polaritons. Nat. Photonics 11, 491–496 (2017).

    Article  CAS  Google Scholar 

  11. 11.

    Lundt, N. et al. Observation of macroscopic valley-polarized monolayer exciton-polaritons at room temperature. Phys. Rev. B 96, 1–7 (2017).

    Article  Google Scholar 

  12. 12.

    Wu, F., Qu, F. & MacDonald, A. H. Exciton band structure of monolayer MoS2. Phys. Rev. B 91, 075310 (2015).

    ADS  Article  CAS  Google Scholar 

  13. 13.

    Brem, S. et al. Phonon-assisted Photoluminescence from Dark Excitons in Monolayers of Transition Metal Dichalcogenides. arXiv 1904, 04711 (2019).

    Google Scholar 

  14. 14.

    Brem, S., Selig, M., Berghaeuser, G. & Malic, E. Exciton Relaxation Cascade in two-dimensional Transition Metal Dichalcogenides. Sci. Rep 8, 1–8 (2018).

    Article  CAS  Google Scholar 

  15. 15.

    Robert, C. et al. Fine structure and lifetime of dark excitons in transition metal dichalcogenide monolayers. Phys. Rev. B 96, 1–8 (2017).

    Article  Google Scholar 

  16. 16.

    Danovich, M., Zólyomi, V., Fal’ko, V. I. & Aleiner, I. L. Auger recombination of dark excitons in WS2 and WSe2 monolayers. 2D Mater 3, 1–5 (2016).

    Article  CAS  Google Scholar 

  17. 17.

    Wang, G. et al. In-Plane Propagation of Light in Transition Metal Dichalcogenide Monolayers: Optical Selection Rules. Phys. Rev. Lett. 119, 1–7 (2017).

    Google Scholar 

  18. 18.

    Zhou, Y. et al. Probing dark excitons in atomically thin semiconductors via near-field coupling to surface plasmon polaritons. Nat. Nanotechnol 12, 856–860 (2017).

    ADS  Article  CAS  Google Scholar 

  19. 19.

    Park, K. D., Jiang, T., Clark, G., Xu, X. & Raschke, M. B. Radiative control of dark excitons at room temperature by nano-optical antenna-tip Purcell effect. Nat. Nanotechnol 13, 59–64 (2018).

    ADS  Article  CAS  Google Scholar 

  20. 20.

    Berghäuser, G. et al. Mapping of the dark exciton landscape in transition metal dichalcogenides. Phys. Rev. B 98, 1–6 (2018).

    Article  Google Scholar 

  21. 21.

    Schuller, J. A. et al. Orientation of luminescent excitons in layered nanomaterials. Nat. Nanotechnol 8, 271–276 (2013).

    ADS  Article  CAS  Google Scholar 

  22. 22.

    Terrones, H. et al. New First Order Raman-active Modes in Few Layered Transition Metal Dichalcogenides. Sci. Rep 4, 1–9 (2014).

    Google Scholar 

  23. 23.

    Segura, A. et al. Natural optical anisotropy of h-BN: Highest giant birefringence in a bulk crystal through the mid-infrared to ultraviolet range. Phys. Rev. Mater 2, 024001 (2018).

    Article  CAS  Google Scholar 

  24. 24.

    Laturia, A., Van de Put, M. L. & Vandenberghe, W. G. Dielectric properties of hexagonal boron nitride and transition metal dichalcogenides: from monolayer to bulk. npj 2D Mater. Appl. 2, 1–7 (2018).

    Article  CAS  Google Scholar 

  25. 25.

    Echeverry, J. P., Urbaszek, B., Amand, T., Marie, X. & Gerber, I. C. Splitting between bright and dark excitons in transition metal dichalcogenide monolayers. Phys. Rev. B 93, 121107 (2016).

    ADS  Article  CAS  Google Scholar 

  26. 26.

    Persson, K. Materials Data on WSe2 (SG:194) by Materials Project, https://doi.org/10.17188/1192989 (2014).

  27. 27.

    Macrae, C. F. et al. 2.0 - new features for the visualization and investigation of crystal structures. J. Appl. Cryst. 41, 466–470 (2008).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

The authors acknowledge financial support by the German Research Foundation (DFG: SFB1083, RA2841/5-1), by the Philipps-Universität Marburg, and the German Academic Exchange Service (DAAD). Synthesis of WSe2 and heterostructure assembly are supported by the NSF MRSEC program through Columbia in the Center for Precision Assembly of Superstratic and Superatomic Solids (DMR-1420634). The authors thank G. Witte and D. Günder for assistance with the AFM measurement. For further reading, group-theory analysis related to Ref. 15 can be found in Phys. Rev. Lett. 111, 026601 (2013) and Phys. Rev. B 92, 125431 (2015).

Author information

Affiliations

Authors

Contributions

A.R.-I. conceived the experiment and initiated the study on angle-dependent measurements in 2015. The joint work was guided by J.C.H. and A.R.-I. High-quality WSe2 synthesis and heterostructure assembly were achieved by S.S.E., D.A.R., K.B. and J.C.H. The setup was established by L.M.S. and A.R.-I., and the structures measured by L.M.S. The results were interpreted, discussed and summarized in a manuscript by L.M.S. and A.R.-I. with the support of all coauthors.

Corresponding authors

Correspondence to Lorenz Maximilian Schneider or Arash Rahimi-Iman.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Schneider, L.M., Esdaille, S.S., Rhodes, D.A. et al. Direct Measurement of the Radiative Pattern of Bright and Dark Excitons and Exciton Complexes in Encapsulated Tungsten Diselenide. Sci Rep 10, 8091 (2020). https://doi.org/10.1038/s41598-020-64838-z

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing