Abstract
Ammonium-nitrogen (NH4+-N) recovery from high concentration of NH4+-N-containing wastewater by struvite (MgNH4PO4·6H2O, MAP) precipitation method has been realized, but whether NH4+-N recovery under different reagent adding sequence of NaOH, solid Mg salt and P salt can generate different effects, remains ambiguous. In view of the problem, four modes to add reagents were investigated in detail on the formation of struvite. The results show that the Mode IV (M-IV, i.e. using 50% NH4+-N wastewater to dissolve completely the Mg salt and the P salt, respectively and then simultaneously poured into a beaker to mix the solution evenly and adjust the pH to 9.5.) has the highest NH4+-N recovery efficiency (90.80%) and the maximum mass of precipitates (896 mg) because of the more amount of alkali and initial seed formation. From the morphology of the obtained precipitates, it can be seen that sample M-IV is more loose and porous than the others. XRD patterns show that the four products under the different modes basically agree with the standard MAP.
Similar content being viewed by others
Introduction
Water environment deterioration and eutrophication of natural water bodies such as rivers, lakes and wetlands in China have been caused wide public concern in the last few decades1. High concentration NH4+-N is commonly present in textile, fertilizer, petrochemical, pharmaceutical industrial wastewater2,3,4,5. Meanwhile, nitrogen (N) is one of the indispensable nutrients for crops6,7. Therefore, it is necessary to recover NH4+-N from wastewater containing NH4+-N. Several methods have been applied to pretreat wastewater containing high concentration NH4+-N, such as steam-stripping / air-stripping means8, biological denitrification technology9,10 and MAP method. Struvite precipitation method11,12,13,14 is considered to be an attractive treatment option due to its simple operating, high efficiency, low cost, and can recover NH4+-N as slow-release fertilizer15,16,17, but different reaction conditions directly affect the recovery efficiency of struvite.
Many researchers have been working to improve the reaction conditions of struvite precipitation, include the solution of pH18, the molar ratio of Mg, P, N3 and combined struvite precipitation and microwave irradiation19. To the best of my knowledge, the sequence of adding reagents is an important aspect of the mineral flotation influencing factors studied by Zhang Qidong20 and Wang Jizhen21. But there have been few reports on the effect of the order of reagent addition on NH4+-N recovery and removal. In addition, in practical applications, the reagent addition sequence introduced in this article is mainly applicable to actual wastewater with little or no Mg salt and P salt, such as coking wastewater19 and hydrometallurgy wastewater22.
Based on the aforementioned information, the effect of the reagent addition sequence of solution on the formation of struvite was investigated. The corresponding precipitation products were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD).
Results and discussion
The effect of reagent addition sequence on NH4+-N recovery efficiency
The NH4+-N concentration of solution, pH, and the molar ratio of Mg, P, and N were 500 mg L−1, 9.5, and 1.3:1:1, respectively. The reaction mechanism of struvite formation can be expressed as the following formula:
It can be seen from Fig. 1 that the sequence of reagent addition has a great influence on the NH4+-N recovery efficiency. Among the four modes, the M-IV has the highest NH4+-N recovery efficiency, up to 90.80%. The NH4+-N recovery efficiency in the other three modes is 66.17%, 60.70%, and 84.08%, respectively.
The significant difference in the recovery efficiency of NH4+-N may be related to the sequence of pH adjustment of the solution. As elucidated by Eq. (1), when the Mg salt and the P salt reacted with the NH4+-N wastewater to form struvite crystallization, the pH of solution will decrease. It is reflected in the Fig. 1 that when the pH was adjusted after reagent reaction (M-III and M-IV), the NH4+-N recovery rate were larger than that of pH value adjusted before the reaction (M-I and M-II). When the NaOH solution was used to adjust the pH to 9.5, it was confirmed that the latter two (M-III, 2.4 ml and M-IV, 2.4 ml) used more alkaline solution than the first two (M-I, 1.3 ml and M-II, 1.2 ml). This is a powerful explanation of why the latter two (M-III and M-IV) are significantly better than the former two (M-I and M-II) for NH4+-N recovery rate. Consequently, one of the mechanisms by which different reagent addition sequences lead to different ammonia nitrogen recovery rates can be attributed to the discrepancy in the final NaOH addition amount. Additionally, other possible causes will be explained in the next section on the effect of reagent addition sequence on precipitates mass recovery.
The effect of reagent addition sequence on mass of precipitates
From Fig. 2 can be seen that the sequence of reagent addition has also great influence on the yield of precipitates. Among the four modes, the M-IV has the highest mass of sediment, up to 896 mg. The amount of sediment in the other three modes is 689 mg (M-I), 649 mg (M-II), and 886 mg (M-III), respectively. Compared with Fig. 1, it can also be observed that the higher NH4+-N recovery efficiency, the more precipitates are produced.
Meanwhile, the reason why the M-IV is better than the M-III is probably that the difference in seed amount of crystals formation, which is conducive to the increase of precipitation23. For M-IV, it was ensured that Mg salt and P salt solids were dissolved in NH4+-N wastewater, respectively, before adjusting the pH to 9.5, then the three reagents reacted with each other and formed the initial crystal seed24. By contrast, P salts took longer (30 seconds–1 minute) to dissolve completely than Mg salts when Mg salt and P salt reagents added into NH4+-N wastewater, which affected the formation of crystal seed, leading to a bit lower mass of precipitates in M-III than that of M-IV25.
SEM analyses
Figure 3 shows the SEM images of products obtained under different reagent addition sequences. According to the results shown in Fig. 3, the morphology of products formed in four modes was quite different. In particular, the orthorhombic crystal phases of M-II and M-IV differ greatly, in which M-II is broad and dense and M-IV thin and loose. This is because in order to promote the formation of precipitation, the compaction degree of solids is affected, thus becoming loose and difficult to further precipitate. This result is similar to Song et al.26. This also in accord with the results analyzed in Fig. 1. The amount of sodium hydroxide has an effect on the morphology.
X-ray diffraction
Figure 4 shows the XRD spectra of products obtained under different reagent addition sequences. As can be seen from the XRD diffractogram (Fig. 4), the (020), (111) and (040) reflections of the four spectra are almost identical with the standard struvite spectrum, which can be confirmed that struvite crystal is the mainly component in the obtained precipitates according to JCPDS files (15–0762). For the peak’s intensity of (022) and (211) reflection, M-III and M-IV were stronger than that of M-I and M-II. This is due to the more sodium hydroxide retained by M-III and M-IV, which is consistent with the results obtained in Fig. 1.
Conclusions
The experimental results showed that the sequence of reagent addition has a great influence on NH4+-N recovery and mass of precipitates. The optimal NH4+-N recovery efficiency (90.80%) appeared in M-IV, that is, using 50% NH4+-N wastewater to dissolve completely the Mg salt and the P salt, respectively and then simultaneously poured into a beaker to mix the solution evenly and adjust the pH to 9.5. The mechanism for M-IV mainly resulted from the more alkali than M-I and M-II, and the more amount of initially crystal seed formation than M-III.
Materials and Methods
Materials
All reagents were of analytical grade and purchased in Shantou Xiqiao Science Co., Ltd., Guangdong, China. P salt and Mg salt used in the experiment were disodium hydrogen phosphate dodecahydrate (Na2HPO4·12H2O) and magnesium chloride hexahydrate (MgCl2·6H2O), respectively. Ammonium chloride (NH4Cl) was used to prepare simulated NH4+-N wastewater. The initial pH of solution was adjusted with 1 mol L−1 NaOH and HCl. All solvents were deionized water.
Procedures of experiments
Under room temperature (25 ± 2°C), four modes of reagent addition sequences are as follows: Three 200 ml beakers were filled with 100 ml 500 mg L−1 synthetic NH4+-N wastewater. In the beaker I (M-I), the initial pH of solution was adjusted to 9.5 firstly, then added solid Mg salt and P salt at the same time and stirred to dissolve completely. In the beaker II (M-II), solid P salt was added and stirred to dissolve completely, then adjusted the pH of the mixture to 9.5, following Mg salt was added and stirred to dissolve completely. For the beaker III (M-III), Mg salt and P salt were added at the same time and then stirred to dissolve completely, following adjusted the pH of the solution to 9.5. As for the beaker IV (M-IV), Mg salt and P salt were first added into a 100 ml beaker containing 50 mL of NH4+-N wastewater and then stirred to dissolve completely, respectively. Next simultaneously poured into a 200 ml beaker to mix the solution evenly and adjust the pH to 9.5. Four modes of reagent addition sequences and schematic diagram of struvite formation have shown as Fig. 5.
The mixed solution of the four beakers was stirred by a magnetic stirrer to promote the formation of precipitates and then standing for 30 min to make the precipitation complete. After that, precipitation yield was obtained after filtrating through a 0.45-μm filter membrane, washing by deionized water three times and drying in an oven at 50°C. The content of NH4+-N in the filtrate was determined. All batch experiments were performed in triplicate and the average was taken as the experimental results.
Analytical methods
The morphology of the precipitates was characterized using a scanning electron microscope (SEM, MLA650F, FEI, Hillsboro, USA). The crystal patterns of the synthesized struvite was obtained by X-ray diffractometer with Cu-Kα radiation (40KV, 40 mA), from radiation angle 10–60°(XRD, DX-2700, Shjingmi, Shanghai, China). The content of NH4+-N in solution was measured by visible spectrophotometer (722 N, INESA, Shanghai, China) with a wavelength of 420 nm according to Nessler’s reagent spectrophotometry method.
The calculation Eq. (2) for the recovery of NH4+-N is:
where Y (%) is the recovery efficiency of NH4+-N, C0 refers to the initial NH4+-N concentration (mg L−1) and Ct refers to the equilibrium NH4+-N concentration (mg L−1) of the solution.
References
Liu, W. & Qiu, R. Water eutrophication in China and the combating strategies. J. Chem. Technol. Biotechnol. 82, 781–786 (2007).
Abu Hasan, H. et al. Removal of ibuprofen, ketoprofen, COD and nitrogen compounds from pharmaceutical wastewater using aerobic suspension-sequencing batch reactor (ASSBR). Sep. Pur. Technol. 157, 215–221 (2016).
Chen, Y., Liu, C., Guo, L., Nie, J. & Li, C. Removal and recovery of phosphate anion as struvite from wastewater. Clean Techn Environ Policy 20, 2375–2380 (2018).
Fu, L. Y., Wu, C. Y., Zhou, Y. X., Zuo, J. E. & Ding, Y. Treatment of petrochemical secondary effluent by an up-flow biological aerated filter (BAF). Water Sci. Technol. 73, 2031–2038 (2016).
Zhang, S., Peng, Y., Wang, S., Zheng, S. & Guo, J. Organic matter and concentrated nitrogen removal by shortcut nitrification and denitrification from mature municipal landfill leachate. J. Environ. Sci. 19, 647–651 (2007).
Liu, T., Hu, S., Yuan, Z. & Guo, J. High-level nitrogen removal by simultaneous partial nitritation, anammox and nitrite/nitrate-dependent anaerobic methane oxidation. Water Res. 166, 115057 (2019).
Huang, H., Liu, J. & Jiang, Y. Crystallization and precipitation of phosphate from swine wastewater by magnesium metal corrosion. Sci Rep 5, 16601 (2015).
Xiong, J. et al. Recovery of NH3-N from mature leachate via negative pressure steam-stripping pretreatment and its benefits on MBR systems: A pilot scale study. J. Cle. Pro. 203, 918–925 (2018).
Asadi, A., Zinatizadeh, A. A., Van Loosdrecht, M. & Younesi, H. Nitrogen removal by ANAMMOX and simultaneous nitrification–denitrification (SND) processes in a novel single airlift bioreactor. RSC Adv. 6, 74367–74371 (2016).
Sri Shalini, S. & Joseph, K. Combined SHARON and ANAMMOX processes for ammoniacal nitrogen stabilisation in landfill bioreactors. Bioresour. Technol. 250, 723–732 (2018).
Doyle, J. D. & Parsons, S. A. Struvite formation, control and recovery. Water Res. 36, 3925–3940 (2002).
Yetilmezsoy, K. & Sapci-Zengin, Z. Recovery of ammonium nitrogen from the effluent of UASB treating poultry manure wastewater by MAP precipitation as a slow release fertilizer. J. Hazard. Mater. 166, 260–269 (2009).
Simoes, F., Vale, P., Stephenson, T. & Soares, A. The role of pH on the biological struvite production in digested sludge dewatering liquors. Sci Rep 8, 7225 (2018).
Wang, F. et al. Phosphate Recovery from Swine Wastewater by a Struvite Precipitation Electrolyzer. Sci Rep 9, 8893 (2019).
Lee, S.-H. et al. Enhancement of struvite purity by re-dissolution of calcium ions in synthetic wastewaters. J. Hazard. Mater. 261, 29–37 (2013).
Siciliano, A. Assessment of fertilizer potential of the struvite produced from the treatment of methanogenic landfill leachate using low-cost reagents. Environ Sci Pollut Res. 23, 5949–5959 (2016).
Min, K. J., Kim, D., Lee, J., Lee, K. & Park, K. Y. Characteristics of vegetable crop cultivation and nutrient releasing with struvite as a slow-release fertilizer. Environ Sci Pollut Res. 26, 34332–34344 (2019).
Stratful, I., Scrimshaw, M. D. & Lester, J. N. Conditions influencing the precipitation of magnesium ammonium phosphate. Water Res. 35, 4191–4199 (2001).
Huang, H., Liu, J., Xiao, J., Zhang, P. & Gao, F. Highly Efficient Recovery of Ammonium Nitrogen from Coking Wastewater by Coupling Struvite Precipitation and Microwave Radiation Technology. ACS Sustainable Chem. Eng. 4, 3688–3696 (2016).
Zhang, Q. Fundamental study on regulation and control floatability difference of molybdenite and talc. (Northeastern University, 2016).
Wang, J. Study on flotation and separation intensification of complex refractory scheelite and its reaction mechanism. (Northeastern University, 2015).
Peng, C. et al. Study on the mechanism of copper–ammonia complex decomposition in struvite formation process and enhanced ammonia and copper removal. J. Environ. Sci. 51, 222–233 (2017).
Muhmood, A. et al. Biochar seeding promotes struvite formation, but accelerates heavy metal accumulation. Sci. Tot. Environ. 652, 623–632 (2019).
Kataki, S., West, H., Clarke, M. & Baruah, D. C. Phosphorus recovery as struvite: Recent concerns for use of seed, alternative Mg source, nitrogen conservation and fertilizer potential. Resources, Con. Recycl. 107, 142–156 (2016).
Zhang, T., Ding, L., Ren, H. & Xiong, X. Ammonium nitrogen removal from coking wastewater by chemical precipitation recycle technology. Water Res. 43, 5209–5215 (2009).
Song, Y. et al. Nutrients removal and recovery by crystallization of magnesium ammonium phosphate from synthetic swine wastewater. Chemosphere 69, 319–324 (2007).
Acknowledgements
This work was supported by the National Key Research and Development Program of China (grant number 2018YFC1903401) and the National Natural Science Foundation of China (No. 51568023, 51864021), and the authors are grateful for the helpful suggestions and evaluations given by many anonymous reviewers.
Author information
Authors and Affiliations
Contributions
H.C.Q. and C.Y.N. wrote the main manuscript text. L.C. and J.Y. prepared all figures. All authors discussed the data, interpreted the results and reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
He, C., Chen, Y., Liu, C. et al. The role of reagent adding sequence in the NH4+-N recovery by MAP method. Sci Rep 10, 7672 (2020). https://doi.org/10.1038/s41598-020-64634-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-64634-9
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.