Hierarchical Eutectoid Nano-lamellar Decomposition in an Al0.3CoFeNi Complex Concentrated Alloy

This paper reports a novel eutectoid nano-lamellar (FCC + L12)/(BCC + B2) microstructure that has been discovered in a relatively simple Al0.3CoFeNi high entropy alloy (HEA) or complex concentrated alloy (CCA). This novel eutectoid nano-lamellar microstructure presumably results from the complex interplay between Al-mediated lattice distortion (due to its larger atomic radius) in a face-centered cubic (FCC) CoFeNi solid solution, and a chemical ordering tendency leading to precipitation of ordered phases such as L12 and B2. This eutectoid microstructure is a result of solid-state decomposition of the FCC matrix and therefore distinct from the commonly reported eutectic microstructure in HEAs which results from solidification. This novel nano-lamellar microstructure exhibits a tensile yield strength of 1074 MPa with a reasonable ductility of 8%. The same alloy can be tuned to form a more damage-tolerant FCC + B2 microstructure, retaining high tensile yield stress (~900 MPa) with appreciable tensile ductility (>20%), via annealing at 700 °C. Such tunability of microstructures with dramatically different mechanical properties can be effectively engineered in the same CCA, by exploiting the complex interplay between ordering tendencies and lattice distortion.

with both Al and Ti, tends to further stabilize the L1 2 phase and increase its phase fraction. This approach has been exploited to develop a range of FCC + L1 2 or γ + γ′ based HEAs, mimicking Ni and Co base superalloys, potentially for high temperature applications 7,[16][17][18][19][20] . The most recent alloy developed under this category was reported by Yang et al. 7 . The composition of this alloy being Al 0. 25 Ti 0. 25 CoFeNi, was based on the medium entropy CoFeNi system to maximize the L1 2 volume fraction. Al and Ti were added to produce a wide FCC + L1 2 dual phase region and the obtained precipitation strengthened HEA had excellent mechanical properties. In another study by Gwalani et al. 6 , FCC solid solution of Al 0. 3 CoCrFeNi was tailored to produce triplex microstructure containing FCC, B2 and sigma via thermomechanical processing which resulted in a 400% increase in yield strength. Fu et al. 21 studied the effect of Ti addition on Al 0.6 CoNiFe and they reported a high compressive yield stress of 2200 MPa and 6.2% ductility for spark plasma sintered Al 0. 6 CoFeNi. The microstructure consisted of a mixture of ultra-fine FCC and BCC grains along with L1 2 precipitates in FCC phase.
Addition of even higher amounts of Al in 3d transition element-based high entropy alloys (HEAs) can result in a eutectic FCC/B2 + BCC lamellar microstructure, which can also be rationalized based on the inability of a single FCC phase accommodating a high Al content. Such eutectic transformations have been previously reported in many HEAs, including AlCoCrFeNi 2.1 22 , Al 0.7 CoCrFeNi 23 , CoCrFeNiMnPd x 24 and CoCrFeNiZr x 25 .The interlamellar spacing observed in these eutectic systems is usually of the order of microns, since the decomposition initiates directly from the liquid phase during solidification. Lu et al. 22 , proposed the eutectic concept in HEAs and designed the alloy AlCoCrFeNi 2.1 that exhibited an FCC/B2 lamellar microstructure. Gao et al. reported for the same alloy, a tensile yield strength (YS) of ~500 MPa, ultimate tensile strength (UTS) of 1100 MPa with 18% ductility. Gwalani et al. 23 used thermomechanical processing on Al 0.7 CoCrFeNi to produce a tensile YS ~1000 MPa and UTS of ~1400 MPa with 13% plastic strain. The microstructure consisted of FCC and B2 lamellae, which on further annealing led to the precipitation of ordered L1 2 precipitates within the eutectic FCC lamellae. Liao et al. 26,27 have also reported a eutectic microstructure in the as cast condition of the Fe 30 Ni 20 Mn 35 Al 15 HEA with a tensile yield strength of ~740 MPa and 8% ductility. Guo et al. 28 investigated a near-eutectic high entropy alloy, Al 2 CrCuFeNi 2 where a sunflower-like microstructure involving complex hierarchical phase decomposition was observed in the as solidified form. This study, however, focuses on the effect of Al addition on the phase stability and phase transformation pathways in a simple equiatomic CoFeNi system. Based on CALPHAD modeling, the competition among disordered and ordered phases introduced by Al addition, has been investigated in a simple quaternary Al 0.3 CoFeNi alloy with the motivation of designing hierarchical multi-phase microstructures.

Results
An isopleth for the Al x CoFeNi system with varying Al content in CoFeNi was calculated using TCHEA3 database in Thermocalc and is shown in Fig. 1(a). Based on this isopleth that can be treated as a pseudo-binary section of the complex phase diagram, the composition of Al 0.3 CoFeNi was chosen since this composition traverses a large range of different complex multi-phase fields. Additionally, two different annealing temperatures were identified, 600 °C and 700 °C. While both these temperatures are quite close and separated by only 100 °C, the isopleth shown in Fig. 1 clearly indicates a rather substantial change in the predicted phase stability from a three-phase FCC + L1 2 + B2 at 600 °C to a two-phase FCC + B2 region at 700 °C, for the composition Al 0.3 CoFeNi.
The single-phase FCC solid solution condition of the Al 0.3 CoFeNi HEA/CCA was initially investigated via cold-rolling to 85% followed by isothermal solution/recrystallization annealing at 1250 °C/5 mins in the single FCC phase field. This condition has been referred to as the CRSA condition. Subsequent precipitation annealing at 600 °C for 50 hrs, starting from the solutionized condition has been referred to as CRSA600. A backscatter SEM image recorded from the CRSA condition is shown in Fig. 2(a). Large recrystallized grains (~150 um) of a single FCC phase are visible in this image. There is no evidence of any intragranular or grain boundary precipitation in this condition, as revealed by the higher magnification image of a sample grain boundary, shown in the inset in Fig. 2(a).
A backscatter SEM image from the CRSA600 condition is shown in Fig. 2(b). The predicted phase stability at this temperature of 600 °C, is a three-phase FCC + L1 2 + B2 field. The image in Fig. 2(b) clearly reveals a high refined lamellar microstructure, resembling the pearlite-type microstructure observed in steel 29 , in all the grains. The inset in Fig. 2(b) exhibits possible further decomposition within these lamellae, but the resolution is not sufficiently high to discern the details. Figure 2(c) shows an EBSD inverse pole figure (IPF) map of this nano-lamellar microstructure with the different lamellar colonies clearly delineated with different colors. The EBSD phase map shown in Fig. 2(d) shows that alternate lamellae within the same colony can be indexed as alternate FCC and BCC phases. An image quality map is also shown in the inset of Fig. 2(d) for reference. The colony size was found to be ~10 μm and the interlamellar spacing appears to be ~150 nm. The volume fractions of BCC and FCC phases determined from the same map were ~75% and ~25% respectively which may not be strictly representative due to the indexing issues associated with such a fine scale lamellar microstructure. Discrete plots from the FCC and BCC phases shown in Fig. 2(e,f) respectively, reveal that {011} BCC // {111} FCC and <001> BCC // <011> FCC, indicating a Nishiyama-Wasserman orientation relationship between the lamellae 30 .
More details of this nano-lamellar microstructure in the CRSA600 sample were revealed by transmission electron microscopy (TEM) investigations, the results of which have been summarized in Fig. 3. Figure 3(a) shows a bright field TEM image highlighting the periodic nature of this lamellar structure with the lamellar thickness being ~150 nm. The microdiffraction pattern in the inset of Fig. 3 Fig. 3(b), highlights these L1 2 ordered regions within the FCC lamellae. Similarly, the selected area electron diffraction pattern shown in inset of Fig. 3(c) can be indexed as the [011] zone axis of BCC and this diffraction pattern also exhibits {100} type superlattice reflections indicating B2 type ordering within the BCC lamellae. The corresponding superlattice dark-field, also shown in Fig. 3(c), clearly highlights the ordered B2 regions within the BCC lamellae. Therefore, the CRSA600 condition, exhibits a complex nano-lamellar eutectoid-like microstructure consisting of alternate FCC + L1 2 and BCC + B2 lamellae. It must be noted that strain free microstructure prior to 600 °C annealing for CRSA600 did not prevent B2 from nucleating, indicating that concurrent growth of FCC/L1 2 and BCC/B2 lamellae in the form of eutectoid-like colonies, overcomes the relatively high nucleation barrier for B2 precipitates within the FCC matrix. Dark-field images shown in both Fig. 3(b,c) indicate that within each lamella, the FCC and L1 2 phases and the BCC and B2 phases are co-continuous in nature, suggesting that a spinodal decomposition process occurred within both FCC and BCC lamellae. The compositional partitioning between these phases was investigated using STEM-EDS mapping, and the maps are presented in Fig. S1(a-d). Al and Ni maps also confirm the B2 morphology within the BCC lamellae. Co and Fe appear to be lean in the intermetallic phases and rich in the FCC and BCC solid solution regions of these lamellae.
Atom Probe Tomography (APT) was performed to delineate and determine the constitution of phases in the complex four-phase microstructure of the CRSA600 condition. Figure 4 shows the APT reconstruction with several interphase interfaces. Al, Ni, Co and Fe maps were also provided to understand the partitioning of elements amongst the four phases. Composition of each phase was determined by averaging the uniform volume of the phase within a sphere of 10 nm diameter, placed such that it is completely encompassed within that specific phase. The BCC phase, as expected, was lean in Al and Ni and rich in Fe and Co with an approximate composition of 4Al-45Co-47Fe-4Ni. The B2 precipitates were rich in Ni and Al with an approximate composition of 30Al-11Co-10Fe-49Ni. In the other FCC based lamella, the continuous matrix appears to be rich in Ni and Al and has thus been assigned as the L1 2 phase, with a composition of 23Al-5Co-5.5Fe-66.5Ni. While it was rather difficult to discern in the STEM-EDS maps, the APT reconstructions and analysis clearly reveal Ni and Al lean regions within the L1 2 lamellae, and these regions are expected to be FCC with the composition 6Al-30Co-30Fe-34Ni. The compositions of each phase are tabulated in Fig. 4(c). Based on these compositions obtained from APT, the possible site occupancies in the L1 2 ordered regions could be represented as (Ni,Fe,Co) 3 (Al,Fe) 31 and that in the B2 ordered regions as (Ni,Co)(Al,Fe,Co) 31,32 .
The second part of this investigation focuses on the microstructure and properties of Al 0.3 CoFeNi HEA/CCA in a different region of phase stability (FCC + B2) by annealing at 700 °C. The first set of samples were rolled, recrystallized at 1250 °C/5 mins in the single FCC phase field, and subsequently annealed at 700 °C/50 hrs, with these samples being referred to as CRSA700, the same type of designation as that used previously for the 600 °C www.nature.com/scientificreports www.nature.com/scientificreports/ annealed samples. A backscattered SEM image from the CRSA700 condition is shown in Fig. 5(a). While the fully recrystallized FCC grains are clearly visible in this image, there appears to be no significant intra-granular precipitation or decomposition of the FCC grains visible in this case. However, the higher magnification inset in the same figure shows the presence of grain boundary precipitates. An EBSD IPF map and phase map from the same condition are shown in Fig. 5(b,c) respectively. These EBSD maps clearly reveal that there is a BCC based phase at the grain boundaries of the CRSA700 condition. Based on previous reports of such grain boundary precipitates in the Al 0.3 CoCrFeNi HEA 33 , these are likely to be grain boundary B2 precipitates in the CRSA700 condition. CALPHAD calculations shown in Fig. 1(b) predicts a substantially higher B2 phase fraction as compared to the experimentally observed grain boundary B2 phase fraction in the CRSA700 sample. Therefore, as discussed in previous reports on the Al 0.3 CoCrFeNi HEA 6,33 , there appears to be difficulty in intra-granular B2 precipitation resulting from the high thermodynamic nucleation barrier of B2 within the FCC matrix. Consequently, the B2 precipitates nucleate only on the FCC grain boundaries. www.nature.com/scientificreports www.nature.com/scientificreports/ Therefore, in order to promote B2 precipitation in the current Al 0.3 CoFeNi HEA/CCA, an attempt was made to increase the number density of heterogeneous nucleation sites for the B2 phase via cold-rolling the sample to 85% reduction in thickness, followed by directly annealing at 700 °C for 50 hrs. This condition has been referred to as the CR700 condition. Figure 6(a) shows a backscatter SEM image from the CR700 condition. Corresponding EBSD IPF and phase maps from the CR700 sample are shown in Fig. 6(b,c). These EBSD maps clearly establish that the darker second phase precipitates in the CR700 condition belong to the BCC phase, and www.nature.com/scientificreports www.nature.com/scientificreports/ likely to be ordered B2 precipitates. Based on Fig. 6, it is evident that a substantially higher number density as well as phase fraction of B2 precipitates form in the CR700 condition, as compared to the CRSA700 condition (Fig. 5). As CR700 condition involved recrystallization of the FCC matrix grains at a lower temperature of 700 °C, as compared to 1250 °C in case of CRSA700, the matrix grains are substantially refined in the CR700 condition. Additionally, size of the B2 precipitates in CR700 was found to be on the scale of refined recrystallized FCC grains.
The tensile engineering stress-strain curves for the four conditions are presented in Fig. 7. The CRSA condition exhibits a yield stress (YS) ~457 MPa, an ultimate tensile stress (UTS) ~852 MPa and a net tensile strain ~76%. The samples did not fail during the test as they reached the maximum elongation. High strain hardenability could be observed in this single-phase condition. The high volume fraction of intermetallic L1 2 and B2 phases in the CRSA600 condition, coupled with the homogeneous nano-lamellar microstructure, resulted in this condition exhibiting a high yield stress of ~1074 MPa, UTS of ~1302 MPa and a net plastic strain of ~8%. The dislocation movement in this condition was expected to be extremely difficult owing to the presence of interphase boundaries every ~100 nm and intermetallic precipitates. However, the stress-strain plot indicates a high strain hardenability and a reasonable ductility in this nano-lamellar condition of the CRSA600 samples. www.nature.com/scientificreports www.nature.com/scientificreports/ The tensile stress-strain plots for the CRSA700 and CR700 conditions are also shown in Fig. 7. Interestingly, the CRSA700 condition exhibits a marginally lower yield stress as compared with the CRSA condition, despite the low phase fraction of B2 precipitates at the grain boundaries in case of the former. This can be potentially attributed to the reduction in the solid solution strengthening in the FCC matrix of the CRSA700 sample, due to Al and Ni depletion for formation of the grain boundary B2 precipitates, as compared to the CRSA sample. The B2 phase fraction is still very small to lead to any significant strength enhancement in this condition. However, with increasing B2 phase fraction, as observed in case of the CR700 condition, an excellent balance of tensile properties can be achieved, with a yield stress www.nature.com/scientificreports www.nature.com/scientificreports/ 893 MPa, ultimate tensile strength ~1187 MPa and a tensile ductility ~26%. The tensile properties of all conditions discussed in this paper are tabulated in Fig. 7(b). In order to determine if the high strength in case of the CR700 condition was solely a result of B2 precipitates, or due to a combination of both B2 and fine scale L1 2 precipitates, further characterization was done using TEM. The bright field TEM image in Fig. S2(a,b) shows the microstructure and [011] FCC zone diffraction pattern from the CR700 condition. This [011] FCC diffraction pattern has been recorded solely from a matric FCC grain. There are no L1 2 reflections visible in the diffraction pattern. A [001] BCC zone diffraction pattern is shown in Fig. S2(c), together with {100} type ordered B2 superlattice reflections. The corresponding dark field www.nature.com/scientificreports www.nature.com/scientificreports/ image shown in Fig. S2(d), has been recorded from such a {100} type superlattice reflection, and confirms the identity of these precipitates to be B2.

Discussion
The Al 0.3 CoFeNi HEA/CCA contains ~ 9at% Al added to an equi-atomic CoFeNi solid solution. While Co, Fe, and Ni have nearly identical atomic radii of 0.125 nm, 0.126 nm, and 0.124 nm respectively, the atomic radius of Al (0.143 nm) is substantially larger. Therefore, introducing Al atoms into CoFeNi distorts the FCC lattice of the parent solid solution. Additionally, Al also introduces a strong tendency for chemical ordering in the solid solution, since while Co-Fe, Fe-Ni, and Co-Ni have enthalpies of mixing close to zero, Al-Ni (−22 kJ/mol) and Al-Co (−19 kJ/mol) have large negative mixing enthalpies 40 which manifest in the strong ordering tendency. Furthermore, depending on the thermo-mechanical treatments and decomposition temperature (700 °C versus 600 °C), these two tendencies (lattice distortion and chemical ordering) manifest in different ways, resulting in different phase transformation pathways. A total of four conditions i.e. CRSA, CRSA600, CRSA700 and CR700 have been investigated in the present paper. The solutionized condition, CRSA of the Al 0.3 CoFeNi alloy, which had a single-phase microstructure exhibited relatively high yield strength and excellent strain hardenability. This result is comparable to other FCC based HEAs supporting the lattice distortion theory and/or complex interaction of multiple principal elements with dislocations 18,34,41 . Thermomechanical processing was employed to engineer this single-phase FCC microstructure by using the phase fields at 600 °C and 700 °C. A novel nano-lamellar eutectoid-like microstructure, with a hierarchical decomposition at multiple length scales, develops in this alloy on annealing at 600 °C. Detailed high-resolution microstructural characterization revealed partitioning between and within each nano-lamella providing an opportunity to understand the role of complex chemistry in HEA/CCAs. The CRSA600 condition of the Al 0.3 CoFeNi alloy is the first reported evidence of a nano-lamellar structure formed by a solid-state eutectoid reaction in a HEA, leading to a hierarchically decomposed FCC + L1 2 /BCC + B2 lamellae. The interlamellar spacing in this condition is ~100 nm, substantially refined as compared to coarser (~micron) lamellae observed in case of eutectic HEAs. Each 100 nm nano-lamella in case of the CRSA600 condition is further decomposed into either an FCC + L1 2 or BCC + B2, containing high volume fractions of intermetallic L12 and B2 precipitates. This hierarchical microstructure leads to a high yield stress of ~1074 MPa, UTS of ~1302 MPa, while still retaining a tensile ductility of 8%. The average work hardenability (∆σ/∆ε) is measured to be ~3000 MPa for this condition. The lamellar eutectic microstructure, previously reported in HEAs, such as AlCoCrFeNi 2. Based on the formation of this novel lamellar eutectoid-like microstructure, it can be conjectured that hypoeutectoid and hypereutectoid microstructures may be possible for other HEA compositions. Similar to the case of pearlitic steels, such hypo-and hyper-eutectoid microstructures in HEAs could potentially widen the range of mechanical properties of these HEAs. The widely known eutectoid pearlitic structure in carbon steels offers high strength, toughness, ductility and wear resistance enabling its use in a wide variety of applications 43 . Pearlite is essentially a nano-scale composite of ferrite and cementite that could produce strengths as high as 5.7 GPa 44 . While the ferrite lamella contributes to the plastic flow, cementite strengthens the material by regulating plastic flow. Interlamellar spacing and prior austenite grain size are known to be some of the important factors governing mechanical properties of these pearlitic steels 45 . Strength and ductility of these alloys can be further tuned by using the hypo-eutectoid space where a higher phase fraction of ferrite results in ductility enhancement or the hypereutectoid region where a higher phase fraction of cementite results in enhanced strength but with compromised ductility. Such microstructural tuning can result in tensile properties ranging from 200 MPa with 50% ductility to 5.7 GPa with reasonable ductility [46][47][48] . Apart from steels, Ti base, Zr base, and Ni base alloys also exhibit nano-lamellar microstructures resulting from either eutectoid or cellular (discontinuous) solid-state transformations [49][50][51][52] . However, the novel nano-lamellar eutectoid-like microstructure observed in the present case in the Al 0.3 CoFeNi HEA/CCA annealed at 600 °C is a rather interesting case where the individual FCC and BCC based lamellae clearly exhibit further decomposition resulting in a multi-scale hierarchical microstructure. Thus, both the FCC based and BCC based lamellae appear to undergo a spinodal decomposition to form FCC + L1 2 and BCC + B2 regions, respectively. At 600 °C, the initially single-phase FCC solid solution decomposes via two possible decomposition pathways as outlined below: In the first pathway, the transformation proceeds by a eutectoid reaction resulting in the nucleation of non-equilibrium compositions of L1 2 and BCC lamellae at the grain boundaries of a single-phase FCC solid solution. The L1 2 and BCC lamellae then undergo a second order phase transformation resulting in the formation of co-continuous FCC/L1 2 and BCC/B2 phases. While, in the second pathway, the FCC solid solution undergoes discontinuous/cellular decomposition to form a lamellar FCC 1 + BCC 1 microstructure with the composition of the FCC 1 product phase lamellae being different as compared to the parent FCC single-phase solid solution. Subsequently, there is a secondary decomposition within each of the FCC 1 and BCC 1 lamellae, resulting in the formation of FCC 2 + L1 2 within the FCC 1 lamellae, and BCC 2 + B2 within the BCC 2 lamellae. Therefore, it can Scientific RepoRtS | (2020) 10:4836 | https://doi.org/10.1038/s41598-020-61538-6 www.nature.com/scientificreports www.nature.com/scientificreports/ be postulated that the ordered L1 2 and B2 phases form during the second step of the decomposition process. As often observed in the case of discontinuous precipitation or eutectoid reactions in alloys 53 , the nucleation of the lamellar colonies is expected to initiate at the prior FCC grain boundaries. In either of the processes, based on the co-continuous like nature of the mixed BCC + B2 and FCC + L1 2 phases within the individual lamellae, as revealed by the dark-field TEM results ( Fig. 3(b,c)) and APT reconstructions (Fig. 4), it is possible that the ordering reactions within the lamellae are a result of a concurrent phase separation and ordering process, as previously discussed in the literature 53,54 . Detailed investigation of the mechanism of this complex decomposition is the subject of future study. A schematic illustration of the four different microstructures investigated in this paper is shown in Fig. 9.
CALPHAD calculations using ThermoCalc and the TCHEA3 database predict the existence of a four-phase field FCC + L1 2 + B2#1 + B2#2 as shown on the 2D isothermal sections at Al = 0.3 and 600 °C, shown in Fig. 10(a). While the experimental results reported in this paper are generally consistent with the predicted phase equilibria, there are two main discrepancies regarding the predicted four-phase field: (i) it is found shifted to higher Co composition than experimentally observed at 600 °C, and (ii) a second ordered B2 phase replaces the experimentally observed BCC phase. The difference in the predicted four-phase field of FCC + L1 2 + B2#1 + B2#2 at Al 0.3 CoFeNi and the experimentally observed four-phase mixture of FCC + L1 2 + BCC + B2 at around Al 0.3 Co 1.34 Fe 0.78 Ni 0.91 , can be potentially attributed to inaccuracies in the solution thermodynamic models used for modeling these multiple phases involving complex compositions.
Comparing the transformation pathways in case of 700 °C versus 600 °C annealing, there are some noteworthy differences. The onset driving force for the precipitation of B2 and L1 2 phases as a function of temperature, starting from a homogeneous FCC solid solution, has been estimated using ThermoCalc and has been plotted in Fig. 10(b). At both 600 °C and 700 °C, there is a substantial driving force for B2 precipitation in the FCC matrix (marked on Fig. 10(b)). While there is a driving force for L1 2 precipitation at both these temperatures, it is much smaller as compared to the B2 phase. However, the ThermoCalc predictions indicate that while L1 2 is an equilibrium phase at 600 °C (refer to isopleth shown in Fig. 1(a,b)), this phase is in metastable equilibrium at 700 °C, in agreement with a study on similar HEA/CCA composition by Gwalani et al. 33 Furthermore, as discussed in previous reports 6,33 , B2 precipitation within an FCC matrix has a high nucleation barrier that is likely due to the high B2/FCC interfacial energy. However, the mechanism of B2 precipitation is substantially different at the two temperatures. While heterogeneous nucleation sites such as grain boundaries, deformation bands, and deformation twins are required for B2 precipitation at 700 °C, at 600 °C the B2 precipitation occurs by concurrent precipitation and growth of FCC + L1 2 /BCC + B2 nano-lamellar colonies from the FCC matrix grain boundaries. Therefore, the cooperative growth of both FCC + L1 2 lamellae and BCC + B2 lamellae appears to reduce the nucleation barrier for B2 precipitation at 600 °C. As noted earlier the possible transformation pathways indicates that the single-phase FCC solid solution initially decomposes into grain boundary colonies of nanoscale lamellae of L1 2 /FCC and BCC (related by the Nishiyama-Wasserman orientation relationship), and subsequently there is a second-order decomposition of L1 2 or FCC lamellae to FCC + L1 2 , and BCC lamellae to BCC + B2 within the BCC lamellae. Therefore, the ordered B2 phase forms within a parent BCC-based phase in case of the decomposition pathway at 600 °C, resulting in a substantially lower nucleation barrier, unlike at 700 °C, where the B2 phase has to nucleate directly within the FCC parent matrix. The details of these mechanisms need further investigation. www.nature.com/scientificreports www.nature.com/scientificreports/ Two different thermomechanical processing routes were employed to study the effect of B2 on tensile properties. In CRSA700 condition, coarse single-phase grains with grain boundary B2 was observed. Due to a high thermodynamic nucleation barrier for B2, it was able to nucleate only at grain boundaries since these are the available heterogenous nucleation sites. When compared to CRSA, the relatively lower yield stress of CRSA700 could be explained by two possible reasons. First, the diminished grain boundary area due to the coarse grain structure resulted in only a small phase fraction of B2 precipitation and consequently B2 did not contribute substantially to the tensile yield stress. Secondly, solid solution strengthening in the matrix was reduced due to solute depletion (Al and Ni), caused by grain boundary B2 precipitation. Therefore, the semi-continuous grain boundary B2 layer could not have overcome the weakening of the matrix. In the case of direct annealed condition or CR700, large number of heterogenous nucleation sites, such as deformation bands comprising a high dislocation density as well as deformation twins, were introduced by cold-rolling and this aided in the formation of a high phase fraction of B2 precipitates. This large B2 phase fraction coupled with Hall-Petch strengthening arising from a more refined FCC matrix grain, can rationalize the high yield stress of ~893 MPa observed for this condition.  www.nature.com/scientificreports www.nature.com/scientificreports/ 3. Optimization of the balance of mechanical properties in the same Al 0.3 CoFeNi alloy has been successfully demonstrated by tuning the microstructure in the FCC + B2 two-phase field via higher temperature annealing at 700 °C. Depending on the thermo-mechanical processing steps adopted, the resulting microstructure could either be coarse-grained FCC with a small fraction of B2 precipitates along the grain boundaries, or a much finer grain sized FCC matrix, with a substantial phase fraction of B2 precipitates, largely located at the grain boundaries. These two different heat-treatment conditions lead to substantially different mechanical properties with the former annealing treatment resulting in a low YS ~380 MPa, UTS ~750 MPa, together with an elongation to failure ~57%. In contrast, the latter heat-treatment, involving direct annealing of the sample at 700 °C after cold-rolling, resulted in YS ~ 900 MPa, UTS ~ 1190 MPa, and tensile elongation at failure ~26%.

Methods
Al 0.3 CoFeNi, with the nominal chemical composition 9.1Al 30.3 Co 30.3 Fe 30.3 Ni (at. %) was produced using conventional arc melting. The composition of the cast ingot was measured with Energy dispersive spectroscopy in Scanning electron microscope (SEM-EDS) and was found to be 9.4Al −30.1 Co −31.9 Fe −28.6 Ni (at. %). The cast alloy was homogenized at 1250 °C for 30 min before rolling and annealing treatments. All samples were cold rolled to 85% and encapsulated in quartz tubes backfilled with argon and solutionized at 1250 °C for 5 min, solutionized and annealed at 600 °C or 700 °C for 50 hrs or directly annealed at 700 °C for 50 hrs and water quenched. The heat treatment schedule and nomenclature for different conditions was given in Table S1. Microstructural characterization was performed with FEI Nova-NanoSEM 230 ™ Scanning electron microscope coupled with energy dispersive spectroscopy (EDS) and Hikari Super Electron Backscattered Diffraction (EBSD) detectors, FEI Tecnai G2 TF20 ™ Transmission electron microscope operated at 200 kV and Cameca LEAP 5000XS 3D Atom Probe Microscope operated at 30 K with a pulse fraction of 20% and detection rate of 0.5 in Laser mode. Samples for EBSD were prepared by conventional polishing method, coarse polishing with SiC papers and final polishing with 0.04 μm colloidal silica solution. EBSD maps were taken using a beam voltage of 20 kV and a current of 6.1 nA with step size ranging from 0.05-2.0 μm. TEM and APT lift-outs were prepared using an FEI Nova 200 dual beam focused ion beam (FIB) microscope. Mechanical properties were characterized with customized mini-tensile testing machine at a strain rate of 0.001/sec. Tensile specimens with approximate gauge dimensions 3 × 1 × 1 mm were sectioned in an Electric Discharge Machine according to ASTM standards. Three specimens were tested for each condition for statistical purposes.

Data availability
All the background data and information is available with the corresponding author and can be presented on a reasonable request.