Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Gate-tunable graphene-based Hall sensors on flexible substrates with increased sensitivity


We demonstrate a novel concept for operating graphene-based Hall sensors using an alternating current (AC) modulated gate voltage, which provides three important advantages compared to Hall sensors under static operation: (1) The sensor sensitivity can be doubled by utilizing both n- and p-type conductance. (2) A static magnetic field can be read out at frequencies in the kHz range, where the 1/f noise is lower compared to the static case. (3) The off-set voltage in the Hall signal can be reduced. This significantly increases the signal-to-noise ratio compared to Hall sensors without a gate electrode. A minimal detectable magnetic field Bmin down to \(290\,{\rm{nT}}/\surd {\rm{Hz}}\) and sensitivity up to 0.55 V/VT was found for Hall sensors working on flexible polyimide (PI) substrates. This clearly outperforms state-of-the-art flexible Hall sensors and is comparable to the values obtained by the best rigid III/V semiconductor Hall sensors.


Magnetic field sensors are widely used in several key industries such as consumer electronics, automotive, healthcare and robotics1,2, where they provide position and speed detection, switching applications or current monitoring3. Hall effect sensors currently dominate the market in terms of these operations4,5,6,7,8 and the key figures of merit for these sensors are their magnetic field resolution (Bmin) and current (Si) and voltage related (Sv) sensitivities9. Today’s technology utilizes mainly silicon based Hall sensors because of the advanced silicon CMOS technology that enables reliable and cost efficient production10. However, applications of silicon based Hall sensors are limited by their relatively low sensitivity when compared to Hall sensors based on III/V semiconductors such as InAs and GaAs11,12,13, and by their mechanical stiffness. Graphene, because of its very high mobility µ and low charge carrier density n (Sv ~ µ and Si ~ 1/n) as well as its mechanical flexibility, appears to be ideally suited as the sensing material in Hall effect sensors14,15,16,17,18,19,20,21. Previously, graphene based Hall sensors were demonstrated, that outperformed silicon and other III/V semiconductors based rigid sensors8,9,15,22,23,24. In addition, graphene-based Hall sensors already significantly outperform all other technologies on flexible substrates22. However, the sensitivity of flexible graphene Hall sensors is not yet comparable to rigid Hall sensors based on conventional semiconductors, at least if the graphene Hall sensors are fabricated with a scalable approach.

In this work, we introduce a novel concept for increasing the signal-to-noise ratio in graphene-based Hall sensors with an AC modulated gate electrode, on flexible substrates with local top-gate. Such dynamic gating provides three advantages compared to graphene Hall sensors under static operation: First, the AC modulated gate voltage allows reaching sensitivity maxima for n- and p-type conductance, which doubles the effective sensitivity. This advantage is unique for graphene based Hall sensors due to their ambipolar operation. Second, a static magnetic field can be read out at higher frequencies, where 1/f noise is significantly lower. And third, offsets in the Hall voltage can be reduced by adjusting a static voltage superimposed on the AC voltage. The basic operation mechanism of such a top-gated Hall sensor is illustrated in Fig. 1a. While the second and third advantage can be achieved by other methods, e.g. AC modulation of the supply voltage for the former or spinning current readout for the latter25, there exists no approach offering all three advantages. In the following, we describe the fabrication and detailed characterization of top-gated graphene Hall sensors on flexible substrates and demonstrate an increased signal-to-noise ratio. These Hall sensors do not only set a new benchmark for flexible Hall-sensors, but are also on a par with the best III-V based rigid Hall sensors.

Figure 1
figure 1

Device schematic and the I-V characteristics of the top gated graphene based flexible Hall sensor. (a) Comparison of measured ∆VH and basic operating principles using a DC gate voltage and an AC modulated gate voltage across the charge neutrality point. In the latter, both sensitivity maxima for n- and p-type conductance can be utilized and the effective sensitivity is doubled by AC gate modulation. (b) Isometric device schematic of the top gated graphene Hall sensor with corresponding biasing scheme (top). Schematic illustration of the cross section along the red dashed line in the device schematic (bottom). Graphene and Al2O3 encapsulation are indicated in grey and green colors respectively. (c) Optical microscope image of a device after fabrication with four probing metal pads and top gate. A constant bias voltage VC is applied between the contacts S and D and ∆VH is measured between the contact V1 and V2. Gate voltage VG is applied to the contact G. d) Room temperature two terminal top gate characteristic of the fabricated device at VC of 300 mV.

Results and Discussion

Schematics and the optical microscope image of the fabricated Hall sensors on PI substrate are shown in Fig. 1b,c. The transfer characteristic of one representative device is shown in Fig. 1d for both sweeping directions from −4 V to 4 V and back. These field effect transistor measurements have been conducted to check the integrity and quality of the devices. The transfer characteristic shows little hysteresis, which demonstrates successful passivation by the Al2O326, and also a low residual doping level of the graphene of 3.5 · 1011 cm-2. The two-probe field effect mobility of the device is 2830 cm2/Vs, including the contact and access resistance. Detailed device statistics of 51 out of total 54 devices fabricated on the same chip are shown in the Supplementary Information and demonstrate good reproducibility. Three devices which did not function are excluded from the statistics.

First, conventional Hall effect measurements have been performed with constant gate voltage in order to extract the basic parameters of the device. The measurement configuration is shown in Fig. 1b. A constant bias voltage (VC) and a magnetic field perpendicular to the graphene channel, ranging from 7.2 to 28.8 mT, has been applied and the current (IC) and the Hall voltage (VH) have been measured. In addition, the charge carrier concentration of the graphene, and thus the sensitivity of the device, has been controlled by applying a gate voltage (VG). The offset removed Hall voltage ∆VH, which represents the measured Hall voltage minus the offset voltage at zero magnetic field (∆VH = VHVH, B=0) is plotted as a function of gate voltage in Fig. 2a with a constant VC = 300 mV. The voltage (Sv) and current related (Si) sensitivities can be derived from this measurement using Eqs. (1) and (2) 15:

$${S}_{v}=\frac{1}{{V}_{c}}|\frac{\partial {V}_{H}}{\partial B}|$$


$${S}_{i}=\frac{1}{{I}_{c}}|\frac{\partial {V}_{H}}{\partial B}|$$
Figure 2
figure 2

Hall measurements of the sensor. (a) Magnitude of the ∆VH as a function of the gate voltage at VC = 300 mV. The inset shows ∆VH as a function of the magnetic field at VG = −1.2 V. (b) ∆VH and voltage sensitivity Sv as a function of channel voltage VC. (c,d) Absolute values of current sensitivity Si and Sv plotted against VG at VC = 300 mV.

Figures 2c,d show Sv and Si as a function of top gate voltage at a bias voltage of VC = 300 mV. The sensitivities crucially depend on the doping level of the graphene with a slight asymmetry between hole and electron transport regime. The maximum values for the sensitivities Si and Sv are found to be 800 V/AT and 0.278 V/VT, respectively, for this device. We further observe a linear dependence of ∆VH regarding VC (Fig. 2b), which indicates that the sensitivities are independent of the applied bias and the sensors can be operated with low power. The corresponding charge carrier mobility (µ) can be calculated according to Eq. (3) 9:

$$\mu ={S}_{v}\frac{L}{W}$$

where L and W are the length and width of the graphene channel in the fabricated Hall sensor device. This results in a charge carrier mobility of 4400 cm2/Vs at the Sv maxima, which turned out to be an average value across the chip. Detailed performance analyses of all devices on the chip are shown in Figs. S1 and S2 in the Supplementary Information. The device with the highest values on this chip showed Sv = 0.35 V/VT, corresponding to a mobility of 5600 cm²/Vs.

The characteristics of the Hall sensors under AC gate modulation have been measured in a different setup, illustrated in Fig. 3a. Here, we report data measured on the same device as discussed in Fig. 2. In this setup, a signal generator is used to modulate the gate voltage, which consists of a static offset voltage plus an AC voltage. An SRS 380 lock-in amplifier is used to demodulate the read-out signal (VH). The modulation frequency is fixed at 2 kHz for all measurements, which is well below the calculated RC bandwidth of the Hall sensor of 1.7 MHz. Figure 3b shows the ∆VH as a function of the peak-to-peak AC gate modulation amplitude. In this measurement a constant VC of 300 mV was applied. As expected from the gate voltage dependent sensitivity, the Hall signal increases first with increasing AC amplitude and decreases again after reaching a maximum at ~1.5 V. To directly compare the Hall voltage under DC and AC operation, 45 s long measurements have been performed while the magnetic field was alternated between zero and values up to 28.8 mT (Fig. 3c). In both measurements, VC = 300 mV. The gate voltages have been set to achieve maximum sensitivity, i.e. VG = −1.2 V for the DC measurement and VG = 1.5 V AC voltage in amplitude for the AC case. The effective Hall signal and thus the sensitivity is approximately a factor 2 higher for the AC case, confirming the advantage of the AC gate modulation. The extracted sensitivity Sv is 0.55 V/VT and 0.278 V/VT for the AC and DC case, respectively (Supplementary Information Fig. S3). In addition, the noise in the AC measurements is significantly lower compared to the DC case. However, we note that this noise reduction is mainly due to the sensor read-out using a lock-in amplifier for the AC case, which is not possible under static operation.

Figure 3
figure 3

Hall measurements of the sensor with gate voltage modulation. (a) Illustration of AC gate modulation setup. A signal generator is used to modulate the gate voltage and an SRS 380 lock-in amplifier is used to demodulate the read-out signal (VH). (b) Hall voltage response of the device to the varying magnetic field at a peak to peak gate modulation amplitude at 28.8 mT. (c) Offset removed Hall voltage under DC (black) and AC (red) operation over time, while the magnetic field was stepped between 7.2 mT up to 28.8 mT. For both measurements, VC was 300 mV and the gate voltage was tuned to maximum sensitivity, i.e. VG = −1.2 V for the DC measurement and VG = 1.5 V for the AC case.

The magnetic resolution Bmin represents another key parameter for Hall sensors in addition to the current and voltage related sensitivities. It can be calculated using the noise spectral density and the sensitivity of the sensor using Eq. (4) 15:

$${B}_{min}=\frac{\sqrt{{P}_{v}}}{({S}_{v}\cdot {V}_{c})}$$

The noise power spectral density (PV) of the Hall voltage is measured in ambient with SR770 FFT Spectrum analyzer directly connected to the contacts V1 and V2 in Fig. 1c, while a constant bias voltage VC between the contacts S and D and zero magnetic field B are applied9. Zero VG is applied during the noise measurements since the harmonic contributions of the AC modulated gate restrains determining of the noise floor. However, contribution of the gate voltage to the noise is studied and analyzed in detail previously by Mavredakis et al.27 and the effect of the noise originated from the gate bias on the Bmin of the Hall sensor will not be significant. The results are shown in Fig. 4a, confirming that the major source of noise has a 1/f dependency for the measured frequency range up to 12 kHz. Hence, higher read-out frequencies lead to lower noise levels. The magnetic resolution is derived from PV (Fig. 4b). At 2 kHz, Bmin is found to be 500 \({\rm{nT}}/\sqrt{{\rm{Hz}}}\). The lowest value measured on the chip was 290 \({\rm{nT}}/\sqrt{{\rm{Hz}}}\). Comparison of our findings with literature values for the state-of-the-art Hall sensor elements made from silicon, graphene and other III/V based semiconductors on rigid and flexible substrates are shown in Table 1. The table clearly shows that our CVD graphene based Hall sensors on flexible substrates remarkably outperforms all the other Hall sensor elements on flexible substrates and are highly competitive with respect to all existing technologies on rigid substrate. The measured minimum magnetic resolution of our Hall sensors also outperform the state-of-the-art Hall elements based on Si and is close to the very best values achieved by AlInSb4,6 and exfoliated graphene9 based Hall sensors. It should be noted that the highest9,22 values shown in the Table 1, have been achieved by non-scalable micro-mechanical exfoliated graphene and hBN and/or in vacuum conditions.

Figure 4
figure 4

Noise and Bmin measurements. (a) Noise power spectral density (PV) as a function of frequency. The dashed line indicates 1/f behavior of the noise. (b) Derived magnetic resolution Bmin of the Hall sensor as a function of frequency.

Table 1 Metrics comparison of different high-performance Hall elements working at room temperature. (‘Gr’ stands for graphene).

Finally, the stability of the devices for flexible applications has been investigated. Bending tests have been performed where the device was exposed to varying strain values. Figure 5a shows a photograph of a flexible chip after it has been peeled off mechanically from the silicon carrier substrate. For electrical measurements, the PI substrate has been bent under different bending radii of 25.4 mm, 12.7 mm, and 6.4 mm, respectively (Fig. 5b inset). Bending has been performed one time for each radius, with the sensor on the outer side of the bending curvature (tensile strain). Hall measurements have been performed afterwards in flat status in constant voltage mode. In addition to the measurements with different bending radii, the sensors have undergone up to 1000 bending cycles with a bending radius of 6.4 mm (Fig. 5b). No major degradation of the device performance is observed up to 1000 bending cycles. These results expand the application space of Hall sensors to flexible electronics, e.g., wearable sensors for personal fitness or healthcare systems.

Figure 5
figure 5

Bending tests for flexible Hall sensor. (a) Optical photograph of the flexible chip after it has been peeled off from Si substrate. (b) Bending cycle dependent measurement of the Hall sensor sensitivity. The PI substrate has been bent under bending radii of 6.4 mm up to 1000 times. The inset shows the measured Sv before and after bending tests with different bending radii of 25.4 mm, 12.7 mm, and 6.4 mm. The measurements have been carried out in flat status before and after bending at constant VC of 300 mV and VG of −1.2 V.


In summary, we have introduced the concept of tunable graphene Hall sensors through AC modulated gate voltages and performed an in-depth characterization of the devices. The AC top gate modulation increased the Hall signal, and thus the voltage and current normalized sensitivities, by a factor of ~2 compared to Hall sensors under DC operation. In addition, AC gate modulation enables read out of the sensors at kHz frequencies, where the noise level is significantly (by a factor of ~105) lower compared to the DC case and thus allows detecting much smaller magnetic fields (~102 higher magnetic resolution). In addition, the device concept and the fabrication process are compatible with large-scale flexible substrates. The performance does not degrade under bending and strain, which enables highly sensitive flexible Hall sensors. These results set a new benchmark for flexible Hall-sensors.


Graphene-based Hall sensors are fabricated on spin-coated PI substrate with conventional photolithography technology. First, the flexible substrates are prepared by spin-coating PI in liquid form on a silicon handling substrate. After curing, the resulting thickness of the solidified PI film is about 8 µm. During the entire fabrication process, Si is used as a supportive layer for the PI. After the PI substrate preparation, commercially available, large area, chemical vapor deposited graphene is transferred by a PMMA assisted method28. Graphene is patterned by oxygen plasma, and contacts to graphene are fabricated by sputtering 50 nm Ni, followed by a lift-off process. The top gate dielectric consists of 40 nm Al2O3 deposited by atomic layer deposition and the top-gate electrode is fabricated by sputter deposition of 20/500 nm Ti/Al and lift-off. Wet buffered oxide etchant is used to open vias in the Al2O3 to access the contacts. All measurements have been performed under ambient condition at room temperature. The devices have been measured in flat status with the PI still on silicon, but the entire flexible stack has been peeled off mechanically from the silicon carrier substrate for electric characterization under bending.


  1. R S Popovic. Hall Effect Devices. (IOP Publishing, 2004).

  2. Magnetic Field Sensors Market by Type, Technology, Applications and Geography - Forecasts & Analysis to 2015–2021. Mark. Mark. Rep (2015).

  3. Heremans, J. Solid state magnetic field sensors and applications. J. Phys. D. Appl. Phys. 26, 1149–1168 (1993).

    ADS  CAS  Article  Google Scholar 

  4. Kunets, V. P. et al. Highly sensitive micro-Hall devices based on Al0.12In0.88SbInSb heterostructures. J. Appl. Phys. 98 (2005).

    ADS  Article  Google Scholar 

  5. Boero, G., Demierre, M., Besse, P.-A. & Popovic, R. S. Micro-Hall devices: performance, technologies and applications. Sensors Actuators A Phys. 106, 314–320 (2003).

    CAS  Article  Google Scholar 

  6. Bando, M. et al. High sensitivity and multifunctional micro-Hall sensors fabricated using InAlSb/InAsSb/InAlSb heterostructures. J. Appl. Phys. 105 (2009).

    Article  Google Scholar 

  7. Shibasaki, I. Mass production of InAs Hall elements by MBE. J. Cryst. Growth 175–176, 13–21 (1997).

    ADS  Article  Google Scholar 

  8. Wang, Z., Shaygan, M., Otto, M., Schall, D. & Neumaier, D. Flexible Hall sensors based on graphene. Nanoscale 8, 7683–7687 (2016).

    ADS  CAS  Article  Google Scholar 

  9. Dauber, J. et al. Ultra-sensitive Hall sensors based on graphene encapsulated in hexagonal boron nitride. Appl. Phys. Lett. 106 (2015).

    ADS  Article  Google Scholar 

  10. Huang, L. et al. Graphene/Si CMOS Hybrid hall integrated circuits. Sci. Rep. 4 (2014).

  11. Berus, T., Oszwaldowski, M. & Grabowski, J. High quality Hall sensors made of heavily doped n-InSb epitaxial films. Sensors Actuators, A Phys. 116, 75–78 (2004).

    CAS  Article  Google Scholar 

  12. Koseva, R., Mönch, I., Schumann, J., Arndt, K. F. & Schmidt, O. G. Bismuth Hall probes: Preparation, properties and application. Thin Solid Films 518, 4847–4851 (2010).

    ADS  CAS  Article  Google Scholar 

  13. Hara, T., Mihara, M., Toyoda, N. & Zama, M. Highly Linear Gaas Hall Devices Fabricated By Ion Implantation. IEEE Trans. Electron Devices 29, 78–82 (1982).

    ADS  Article  Google Scholar 

  14. Banszerus, L. et al. Ultrahigh-mobility graphene devices from chemical vapor deposition on reusable copper. Sci. Adv. 1 (2015).

    ADS  Article  Google Scholar 

  15. Huang, L. et al. Ultra-sensitive graphene Hall elements. Appl. Phys. Lett. 104 (2014).

  16. Liang, Y. et al. High mobility flexible graphene field-effect transistors and ambipolar radio-frequency circuits. Nanoscale 7, 10954–10962 (2015).

    ADS  CAS  Article  Google Scholar 

  17. Polat, E. O. et al. Synthesis of Large Area Graphene for High Performance in Flexible Optoelectronic Devices. Sci. Rep. 5 (2015).

  18. Polat, E. O. et al. Graphene-Enabled Optoelectronics on Paper. ACS Photonics 3, 964–971 (2016).

    CAS  Article  Google Scholar 

  19. Salihoglu, O. et al. Graphene-Based Adaptive Thermal Camouflage. Nano Lett. 18, 4541–4548 (2018).

    ADS  CAS  Article  Google Scholar 

  20. Schmitz, M. et al. High mobility dry-transferred CVD bilayer graphene. Appl. Phys. Lett. 110 (2017).

    ADS  Article  Google Scholar 

  21. Wang, Z. et al. Flexible One-Dimensional Metal–Insulator–Graphene Diode. ACS Appl. Electron. Mater. acsaelm.9b00122, (2019).

    CAS  Article  Google Scholar 

  22. Wang, Z. et al. Encapsulated graphene-based Hall sensors on foil with increased sensitivity. Phys. Status Solidi Basic Res. 253, 2316–2320 (2016).

    ADS  CAS  Article  Google Scholar 

  23. Monch, I. J. et al. Flexible hall sensorics for flux-based control of magnetic levitation. IEEE Trans. Magn. 51 (2015).

    Article  Google Scholar 

  24. Bolshakova, I. et al. Graphene and prospects of radiation-hard hall sensors. Proc. 2017 IEEE 7th Int. Conf. Nanomater. Appl. Prop. N. 2017, 2017-Janua, 3–7 (2017).

    Google Scholar 

  25. Mosser, V., Matringe, N. & Haddab, Y. A Spinning Current Circuit for Hall Measurements Down to the Nanotesla Range. IEEE Trans. Instrum. Meas. 66, 637–650 (2017).

    CAS  Article  Google Scholar 

  26. Kang, C. G. et al. Mechanism of the effects of low temperature Al2O3 passivation on graphene field effect transistors. Carbon N. Y. 53, 182–187 (2013).

    CAS  Article  Google Scholar 

  27. Mavredakis, N., Garcia Cortadella, R., Bonaccini Calia, A., Garrido, J. A. & Jiménez, D. Understanding the bias dependence of low frequency noise in single layer graphene FETs. Nanoscale 10, 14947–14956 (2018).

    CAS  Article  Google Scholar 

  28. Suk, J. W. et al. Transfer of CVD-grown monolayer graphene onto arbitrary substrates. ACS Nano 5, 6916–6924 (2011).

    CAS  Article  Google Scholar 

  29. Vervaeke, K., Simoen, E., Borghs, G. & Moshchalkov, V. V. Size dependence of microscopic Hall sensor detection limits. Rev. Sci. Instrum. 80 (2009).

  30. Xu, H. et al. Flicker noise and magnetic resolution of graphene hall sensors at low frequency. Appl. Phys. Lett. 103 (2013).

    ADS  Article  Google Scholar 

  31. Melzer, M. et al. Wearable magnetic field sensors for flexible electronics. Adv. Mater. 27, 1274–1280 (2015).

    CAS  Article  Google Scholar 

Download references


This work was financially supported by the European Commission under the project Graphene Flagship (contract no. 785219) and by the German Science Foundation (DFG) within the priority program FFlexCom Project “GLECS” (contract no. NE1633/3).

Author information

Authors and Affiliations



B.U. and D.N. proposed the idea and planned the experiments. M.O. helped for sample preparation. B.U. fabricated the devices and performed all the experiments. Z.W. and S.L. helped for the measurements. B.U. analyzed the data and wrote the manuscript. The manuscript was critically reviewed by M.C.L. and D.N. All authors reviewed the manuscript and approved the final version of the manuscript.

Corresponding author

Correspondence to Burkay Uzlu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Uzlu, B., Wang, Z., Lukas, S. et al. Gate-tunable graphene-based Hall sensors on flexible substrates with increased sensitivity. Sci Rep 9, 18059 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing