Introduction

Zeolites are microporous, alumino silicate minerals with open three-dimensional framework structures, made up of SiO4 and AlO4 tetrahedrons linked by sharing oxygen atoms to form regular intra crystalline cavities and channels of atomic dimensions. Zeolites are commonly used as commercial adsorbents and composites, as well as cation exchangers, molecular sieves and antimicrobial agents1,2,3.

Attaching nanoparticles on solid surfaces has been used as a traditional procedure to prepare heterogeneous composites with specific properties. Leaching and aggregation of nanoparticles often lead to composite deactivation4,5. In order to overcome these problems, some methods have been proposed including strengthening the metal-support interaction6,7 and using booster and setting out the morphology of nanoparticles8,9. Based on these advances, nanoparticles can be loaded on zeolites for antimicrobials, anti-fungal and anti-virus applications10,11. These achievements convinced researchers to produce nanoparticles inside zeolite. The new composite (zeolite with nanoparticles) can be tuned through the presence of precise nanopores3,12,13.

The issue of contamination by certain microorganisms in some materials, especially food, enables a significant hazardous pathway for humans. The most important pathogenic bacteria in food for mankind are Salmonella spp, Escherichia coli O157H7, Staphylococcus aureus, and Listeria monocytogenes3,14. Metal oxide nanoparticles (MONP) were tested with an excellent antimicrobial activity in the efficient removal of pathogens. MONP may not show a considerable antimicrobial activity in form of metal oxide and metal salt alone, because of their tendency of aggregation15. However, the stability and slow release of metal ions from MONP are effective properties that can be tuned by appropriate synthesis. For this reason, new methods to immobilize MONP into zeolite membranes have been suggested16. One of the most important factors in antimicrobial activity is light. MONP, particularly ZnO and TiO2, become activated against pathogenic bacteria when exposed to ultraviolet (UV) light17,18. The mechanism of this procedure involves substrate adsorption in the composite surface, depending on pH, temperature, composite stability, area and substrate concentration19,20,21,22. Some of the disadvantages are low adsorption ability (small active area) and photo corrosion23,24. Therefore, with precise preparation of ZnO and TiO2, especially regarding morphologies and sizes, most of these caveats can be overcome25,26,27.

MONP also show significant antimicrobial activity through connection to microbial DNA and proteins, and caused to preventing bacterial duplication, avoiding metabolic enzymes of the bacterial electron transport chain, leading to their inactivation2.

The semiconductor properties of zinc oxide (ZnO) and titanium dioxide (TiO2) can be tuned in nano scale28,29,30,31. Manufacturing nanoparticles involves protocols of different complexities with aggregation of ZnO and TiO2 nanoparticles as an important limitation in the process32,33. These compounds are useful in pharmaceutical utilization34, pigmentation35, antimicrobial activities, anti-fungal and anti-viruses properties36. In addition, ZnO and TiO2 are important components in the novel and active packaging industry.

Tiny ZnO and TiO2 nanoparticles with a wide surface can maintain their photoactivity; however, their recovery at the end of the procedure is very difficult. Accordingly, a useful approach is to support ZnO and TiO2 in a zeolite structure which can enhance adsorption and subsequently, increase the composite efficiency and ease of recovery by ordinary deposition37,38. The use of effective composites made up with ZnO and TiO2 impregnated in zeolites is a new strategy to produces nanoparticles with supporter. Recent research reported some properties of ZnO supported in zeolites including ZSM-5, Y, X and A39,40. In this research, we have focused on the description and development of ZnO and TiO2 nanoparticles supported in the channels of a porous matrix (4A zeolite) for antimicrobial application. First of all, we described a simple synthetic route for preparation of ZnO and TiO2 impregnated into 4A zeolite (4A z). Secondly, the structural properties and antimicrobial effects of the materials were determined. In fact, zinc and titanium in high quantities may have toxic effects41,42,43,44,45; hence, in this work we have tried to use 4A z as a support of metal nanoparticles. These nanoparticles are encapsulated inside zeolite cavities or external channels to decrease the possibility of leaching as low as possible. This process reduces the toxicity of nanoparticles and their release from the matrix and therefore, this complex (nanoparticles and zeolite) can be used in polymer matrix for food packaging. In this work, we aimed to select the lowest effective amount of nanoparticles into 4A z with antimicrobial activity.

Materials and Methods

Materials

Here, 4A z (Si/Al ≅ 2) was synthesized according to the formula below. Zinc acetate dehydrate, orthotitanate and ethanol were purchased from Merck. All the applied reagents were of analytical grade. It should be noted that in order to test antimicrobial activity, bacterial strains were obtained from Biological and Genetic Resource Center, Tehran, Iran. Nutrient broth and Nutrient agar were all purchased from Micromedia, Canada.

Measurements

X-ray diffraction patterns (XRD) were performed using a Siemens D5000 diffractometer with Cu kα radiation (λ = 1.5418 A and 2θ = 4–70°) at room temperature, 40 kV and 30 mA.

The degree of crystallinity is measured by peak height method46 based on Eq. (1):

$${\rm{Crystallinity}}\,{\rm{Index}}({\rm{CrI}})=(\frac{{\rm{I}}-{{\rm{I}}}_{0}}{I})100$$
(1)

where CrI is crystallinity degree (%), I, is peak height at the angle of diffraction (2θ) related to crystalline section and I0 is peak height at the angle of diffraction (2θ) related to non-crystalline section.

Scanning electron microscope (SEM) (Philips XL30) was evaluated to catch SEM images and to carry out elemental analysis. The SEM sample was gold coated prior to examination and SEM was operated at 5 kV. MAP was obtained by wavelength-dispersive X-Ray spectroscopy (WDS) system to show the spatial distribution of elements in a sample and be extremely useful for displaying element distributions in polymer matrix, particularly for showing compositional zonation. Transmission electron microscopy (TEM) was determined by electrons microscope systems and was also used to indicate the interactions between the electrons and the atoms in order to observe crystal structure and features in the structure like dislocations and grain boundaries. The minimum inhibitory concentration (MIC90), minimum bactericidal concentration (MBC) and fractional inhibitory concentration (FIC) of MONP dropped into 4A z were also determined.

Methods

Preparation of 4A zeolite

4A z (alumina silicates) with a silica to alumina ratio (Si/Al ≅ 2) was synthesized by hydrothermal method. In this process, clinoptilolite and alumina were used as sources of silicon and aluminum, respectively, and then mixed with NaOH. In the final stage, the solution was conveyed to teflon reactor at 90 °C, in order to produce 4A z nanocomposite37.

Preparation of ZnO doped into 4A zeolite

In this research, ZnO clusters were synthesized by the following stage response: in the first step, a solution of 0.17 g Zn(CH3CHOO)2·2H2O was prepared, mixed with a ratio of 5:95% w/w (nanoparticles:4A z) and was shaken for 30 min. In the second step, integration of zinc acetate to 4A z using an ion exchange process was done (24 h at 60 °C). Next, by the use of distilled water, the solution was washed and dried at 80 °C. The final powder was calcined at 500 °C for 2 h to produce ZnO/4A z nanocomposite.

Preparation of TiO2 doped into the 4A zeolite

In this research TiO2 salt was created by the following stage response: in the first step, 0.2 g ortho titanate was dissolved in ethanol. Then, this solution was mixed with a ratio of 5:95% w/w (nanoparticles:4A z) and was shaken for 30 min. In the second step, integration of ortho titanate to 4A z using an ion exchange process was done (6 h at 90 °C). Next, by the use of distilled water, the solution was washed and dried at 80 °C. The final powder was calcined at 500 °C for 2 h in order to produce TiO2/4A z nanocomposite.

Preparation of ZnO and TiO2 doped into 4A zeolite

In order to prepare ZnO/TiO2doped into 4A z, ZnO nanoparticle was prepared and mixed with a ratio of 2.5:95% w/w (nanoparticles:4A z). Then, 2.5% w/w titanium dioxide ethanol dried powder was added to the mixture of 4A z and ZnO and dried at 80 °C. The final powder was calcined at 500 °C for 2 h in order to produce TiO2 and ZnO/4A z nanocomposite.

Determination of minimum inhibitory concentration (MIC), minimum bactericidal concentration(MBC) and fractional inhibitory concentration (FIC)

The antimicrobial activity of 4A z, TiO2/4A z, and ZnO/4A z was defined by micro dilution method on 96-well microplates according to previously reported methods (Tajik et al., 2015). Four bacterial suspensions including Escherichia coli O157:H7 (IBRC-M 10698), Listeria monocytogenes (IBRC-M 10671), Pseudomonas fluorescens (IBRC-M 10752), and Staphylococcus aureus (IBRC-M 10690) were collected after 24 h cultures on Nutrient broth and regulated to 0.5 McFarland standard turbidity (1.5 × 10−8 CFU/mL). In order to evaluating antimicrobial activity of nanoparticles, we used bacterial suspensions (20 μL), different concentrations of 4A z, TiO2/4A z, ZnO/4A z and TiO2, ZnO/4A z suspension (0.5, 1, 2, 3, 4, 5, 6 and 7 mg/mL), 20 μL for each nanoparticles or 4A z and 10 μL in combination; and 160 μL of Nutrient broth in tested wells. The last wells of micro-plates were considered as positive controls containing uninoculated broth with antimicrobials materials (nanoparticles), and as negative controls containing inoculated broth without antimicrobials materials. The microplates were incubated at 37 °C for 24 h under constant shaking (50–100 rpm) by a microplate shaker (Boeco, Hamburg, Germany). It should be noted that for Pseudomonas fluorescens, we needed 25 °C for 24 h. MIC90 values were determined as the lowest concentration with no visible bacterial growth. The best concentration of each antimicrobial agent was determined by MIC method.

The MBC is the lowest concentration of an antibacterial agent required to kill a particular bacterium47,48. It can be determined from broth dilution MIC tests by sub culturing to agar plates that do not contain the test agent. The minimum bactericidal concentration is identified by determining the lowest concentration of antibacterial agent that reduces the viability of the initial bacterial inoculum by ≥99.9%. The MBC is complementary to MIC; whereas, MIC test demonstrates the lowest level of antimicrobial agent that inhibits growth, MBC test demonstrates the lowest level of antimicrobial agent that results in microbial death49,50. The fractional inhibitory concentration was used for combination of materials based on the following equation:

$${{\rm{FIC}}}_{{\rm{A}}\& B}=\frac{{\rm{MIC}}({\rm{A}}\& B)}{{\rm{MIC}}({\rm{A}})+{\rm{MIC}}(B)}$$

where A refers to TiO2 nanoparticles and B refers to ZnO nanoparticles.

Determination of antibacterial activity of nanoparticles doped in 4Azeolite

The disc diffusion test was performed to determine the antibacterial activity of nanoparticles doped in 4A z51. Pseudomonas fluorescens, Staphylococcus aureus, Listeria monocytogenes, and Escherichia coli O157:H7 suspensions were collected from 18 h nutrient broth cultures then adjusted to 0.5 McFarland standard turbidity (1.5 × 10−8 CFU/mL) and diluted (1:10) to the desired bacterial density (1.5 × 10−6 CFU/mL). The Mueller-Hinton agar medium was then inoculated with 0.1 mL of the bacterial suspensions (1.5 × 10−6 CFU/mL). Next, the suspensions of nanoparticles doped in 4A z and also 4A z individually, were prepared under sterile conditions and then situated on the surface of Mueller-Hinton agar plates (100 λ). The plates were incubated at 37 °C (for L. monocytogenes, E. coli O157:H7, and S. aureus) or 25 °C (for P. fluorescens) for 24 h, after which the inhibition zone around the discs were measured by a digital micrometer. Indeed, inhibition zone have shown the antibacterial effect of nanoparticles. The greater the diameter of the inhibitory zone, the greater antimicrobial activities of nanoparticles.

Inductively coupled plasma mass spectroscopy (ICP-MS)

Migration tests were performed according to EU regulation for plastic materials and articles intended to be in contact with food (Regulation 10/2011/ EU)52. Migration of TiO2 and ZnO nanoparticles was assessed using a simulant (deionized water with pH = 6–7) over 12 days at 25–30 °C. Prior to the migration tests, the concentration of ZnO and TiO2 nanoparticles in 4A z was determined. In ICP-MASS assay, we first produced a nano bio-composite film with selected polymer and nanoparticles zeolite. Then, this nano bio-composite film was converted to food packaging by thermal processing. Next, to measure the migration of nanoparticles zeolite from food packaging to food product, we have used food simulant. Food simulant was filled in food packaging, packed and stored for 12 days. Next, the simulants were filtered through a 220 nm Millipore filter and then migrated nanoparticles were analyzed using ICP-MS (Agilent 7800 Quadrupole ICP-MS, Perkin Elmer, California, United States). In the final stage, the migration results were normalized to nanoparticles migrated/cm2 after 12 days. It should be noted that, on the first day, the measurement of nanoparticles zeolite in food packaging was conducted regardless of food simulant. This was to discover the exact amount of nanoparticles embedded in 4A z and polymer matrix.

Ethical approval

This article does not contain any studies with human participants or animals performed by any of the authors.

Results and Discussion

Evaluation of XRD patterns

XRD showed the impact of homogenization on crystalline structure of the combination53,54. XRD patterns of ZnO, TiO2, and ZnO/TiO2 supported into 4A z are shown in Fig. 1. Based on the obtained template, TiO2 nanoparticles in the form of anatase, had significant peaks at 2θ = 7.36, 10.31, 12.66, 21.90, 24.21,27.32,30.14, 30.19 and 34.41°. According to Scherrer equation (τ = κ λ/β cosθ), the average crystallite size of nanoparticle was approximated to be 50 nm. In this equation, τ is the average crystalline size, κ is the shape factor (about 0.9), λ is the wavelength of X-ray radiation, β is the full wide at half the maximum intensity and θ is the Bragg diffraction angle55. As shown in Fig. 1, the peaks of 4A z are visible at certain 2θ with high intensity. The diffraction peaks for ZnO and TiO2 were in good agreement with those given in the standard data (PCPDF, 79–0207 and JCPDS, 21–1272, respectively) with acceptable crystallinity. According to XRD patterns, it was found that ZnO and TiO2 was crystallized with hexagonal wortzite and anatase phase, respectively. On the other hand, it is clear to see that the width of the reflections is considerably broadened, which indicates a small crystalline domain size. In the spectra of oxide nanoparticles doped into 4A z, the presence of nanoparticles can be confirmed based on the observed peaks, in particular 2θ = 4–70. Regarding the significant peaks with miller indices of TiO2(642), (664) and ZnO (842), (664), they have considerable overlap with the peaks of 4A z (Fig. 1), and therefore, the oxide nanoparticle peaks are not clearly visible.

Figure 1
figure 1

XRD spectra of nanocomposite TiO2/4A z, TiO2, ZnO/4Az and ZnO/4A z. Pink color is 4A z individually, blue color is TiO2 nanoparticle individually and orange color is ZnO nanoparticle individually.

Full size image

But according to MAP pattern, the presence of elements (titanium and zinc) has been confirmed which affects the intensity of 4A z peaks (Fig. 2). Also, it should be noted that in ZnO/TiO2 spectrum, the intensity of crystalline plates with Miller indices (200, 220 and 222) are lower than when there is only one type of metal oxide.

Figure 2
figure 2

(A) Evaluation of SEM pattern; a: ZnO/4A z, b: TiO2, ZnO/4A z and c: TiO2/4A z. (B) Evaluation of TEM image; a: TiO2 and ZnO/4A z. (C) Evaluation of MAP images; a: ZnO/4A z, b: TiO2, ZnO/4A z and c: TiO2/4A z.

Full size image

Evaluation of SEM, TEM and MAP patterns

The size and morphology of the samples are illustrated in Fig. 2(A–C). According to Figs. 2A, 3A z particles with cubic structure are completely visible and ZnO and TiO2 nanoparticles are dispersed in the form of almost spherical particles into 4A z. Based on Fig. 2A, cube-shaped particles are completely apart from one another and the deformed structures are not visible. The image (Fig. 2A) showed that the matrix of ZnO and TiO2 nanoparticles had homogeneous and smooth surfaces without any roughness and cracks, which indicated proper synthesis of the materials. The size of 4A z particles, based on Fig. 2A,B, is 400 to 600 nm; besides the oxide nanoparticles are very thin and smaller than 50 nm. According to the obtained images (Fig. 2B,C), the dispersion of ZnO and TiO2 nanoparticles into 4A z structure is uniform and no accumulation has been observed. Also, cubic particles with square layers are present. Figure 2B shows a typical TEM micrograph of ZnO/TiO2 nanoparticles powder. This powder is formed by 10–50 nm size particles having equiaxed morphology. The particles are well separated from each other. Dark field imaging displayed that each particle was a single crystal. The nanoparticle sizes from TEM examination were in good agreement with both XRD and MAP.

Figure 3
figure 3

Disc diffusion test of nanoparticles doped in 4A z. In each figure: number 1 is ZnO/4A z, number 2 is TiO2/4A z, number 3 is ZnO and TiO2/4A z and number 4 is 4A z.

Full size image

MIC, MBC and FIC values of nanoparticles

MIC90, MBC and FIC values of 4A z, TiO2/4A z, ZnO/4A z, and TiO2, ZnO/4A z nanocomposite are shown in Tables 1–3. And 4A z do not have antimicrobial activity against bacteria’s56 (Table 1). TiO2/4A z, ZnO/4A z, and TiO2/ZnO/4A z nanocomposite were activated in the concentrations of 1–4 mg/mL against E. coliO157:H7, S. aureus, P. fluorescens, and L. Monocytogenes, separately. These results were in agreement with the outcome of prior studies57,58. The best concentrations of MIC were selected for TiO2/4A z, ZnO/4A z, and TiO2, ZnO/4A z nanocomposite as 2, 1 and 1 mg/mL, respectively; against microorganisms (Table 1). This concentration in MBC corresponded to 2, 2 and 2 mg/mL, respectively; and 0.25 mg/ml concentration of TiO2, ZnO/4A z nanocomposite against E. coli O157:H7, had an excellent FIC value (Table 3). Based on the results, gram negative bacteria were more sensitive compared to antimicrobial agents. Gram positive bacteria have a thick layer of peptidoglycan in their cell walls which have caused more resistance compared to gram negative bacteria against antimicrobial agent. Gram negative bacteria contains a thin peptidoglycan layer which facilitates the mobility of metal ion nanoparticles to the cell, and it also assists the interaction between nanoparticle and bacterial cell walls due to lack of thick peptidoglycan layer. Another aspect of gram negative bacteria is the negative charge of lipopolysaccharide layer. This charge has a role as a significant incorporation factor for positive ions, which consequently leads to nanoparticle emission, intracellular damages and destruction of DNA and proteins (Fig. 4).

Table 1 MIC of TiO2, ZnO, and TiO2 and ZnO doped in 4A z against bacteria.
Full size table
Table 2 MBC of TiO2, ZnO, and TiO2 and ZnO doped in 4A z against bacteria.
Full size table
Table 3 FIC of TiO2/ZnO doped in 4A z against bacteria.
Full size table
Figure 4
figure 4

Antimicrobial mechanism of nanocomposites (TiO2/4A z, ZnO/4A z and TiO2 and ZnO/4A z).

Full size image

Antibacterial activity of nanoparticles doped in 4A zeolite

The disc diffusion procedure was conducted to assess the antimicrobial activity of nanoparticles doped in 4A z (Table 4). Inhibition zone diameter indicated that TiO2, ZnO/4A z had a greater antimicrobial effect against bacteria compared to the combination of individual nanoparticles with 4A z (Fig. 3). Also it should be noted that, 4A z individually do not have an antimicrobial activity against bacteria56. Based on the results, Gram-negative bacteria (particularly E. coli O157H7) were more sensitive to the antimicrobial agents. The main purpose of using 4A z, as a carrier with nanoparticles, is to control the release of them and increase the antimicrobial activity. The highest zone of inhibition was seen against E. coli O157H7 including; 6.86 ± 0.03 mm, 9.13 ± 0.03 mm, and 10.73 ± 0.04 mm for ZnO/4A z, TiO2/4A z and ZnO and TiO2/4A z, respectively; while S. aureus had the lowest inhibitory zone in all treatments (P < 0.05). Indeed, nanoparticles disturb the permeability of both the cell wall and cell membrane, thereby affect biomolecules such as DNA and protein, and prevent processes such as DNA replication and protein synthesis59.

Table 4 Disc diffusion analysis of nanoparticles doped in 4A z.
Full size table

Titanium dioxide (TiO2), is also called titania, is one of the most widely used semiconductor nanoparticles with specific hydrophilic and photocatalytic properties, which caused to antimicrobial and ultraviolet (UV) protecting characteristics51,60. These nanoparticles are extensively used in producing polymer nanocomposites in food packaging. TiO2 nanoparticle works in two phases: first, the ability to degrade bio polymeric compound (such as polysaccharides and proteins)61 on its surface and second, to alter the surface properties of the objects to hydrophilic state when TiO2 is placed on that surface. In Europe, TiO2 (E171) is confirmed and categorized as a color additive in confectionaries, dairy products, and soft drinks under Directive of 1994/36/EC62. TiO2 is more prone to oxidization when exposed to ultraviolet (UV) in a wavelength lower than 385 nm. As a result, TiO2 can produce active oxygen species when exposed to sunlight63. Furthermore, the antimicrobial activity of TiO2 is related to its crystal structure, the kind of artificial light, UVA light intensity, shape and size64 as well as production of ROS, active radical species, hydrogen peroxide, superoxide radical, and hydroxyl radical64,65,66. These active species destroy the outer membrane of the bacteria, namely phospholipids, proteins and lipopolysaccharides and finally damage the bacteria.

ZnO is recognized as a colorless, wide band gap semiconductor with an optical band gap in UV region which makes it applicable as an impressive absorbent of UV radiation. Currently, ZnO is listed as generally recognized as safe (GRAS) by the US Food and Drug Administration (FDA) and is consumed as a food additive, considering the fact that zinc is an important trace element in nutrition67. The antimicrobial activities and potential applications of ZnO nanoparticles in food preservation have been approved68. In this regard, ZnO nanoparticles were combined in polymeric matrix in order to supply the packaging material with antimicrobial activity and to improve some packaging properties69,70. Furthermore, the antimicrobial properties of ZnO is related to photocatalytic activity of H2O2. Both Zn+2 and ZnO particles hold antibacterial activities. The antimicrobial activities of ZnO at nanoscale would yield affordable and safe innovative strategies69,71. Moreover, ZnO has been blended into the linings of food cans used for meat, fish, corn, and peas to preserve colors and hinder spoilage because of its antimicrobial action.

Indeed nanoparticles have the ability to decline or remove the microorganism resistance by two mechanisms: (a) free metal ion toxicity arising from dissolution of metals from the surface of nanoparticles and (b) oxidative stress via generation of reactive oxygen species (ROS) using hydrogen peroxide (H2O2) and organic hydro peroxides (OHP) on the surface of nanoparticles72. Actually, nanoparticle can effect on the survival of microorganisms by agglomeration on the surface of bacteria and alter the structure of lipids, peptidoglycan, proteins and their DNA73. But there may be differences in the impact of nanoparticles on types of specific microorganisms; for instance, Sierra et al.74 showed a higher antimicrobial effect against Streptococcus mutans of Cu nanoparticles at lower concentrations than zinc. In another study, Ruparelia et al.75 showed that copper nanoparticle has great impact as an antimicrobial agent against E. coli, Bacillus subtilis, and Staphylococcus aureus in comparison with TiO2. Our results are in agreement with those of Lou et al.59 and Yael N et al.76.

Inductively coupled plasma mass spectroscopy

Migration is a mass transfer process where low molecular mass particles are released into the surroundings. To assess migration, the system must be simplified and particles must be analyzed separately. The package is assumed to be homogeneous, the food is substituted by food simulants and the substance is introduced at the recognized concentration. In this research, nanoparticles ion releasing capacity in food simulants of the composites was quantified by ICPMASS.

Zinc and Titania ions are doped into 4A z through ionic exchange, preferably with Na+ ions77. Next, ions are released from composites through ionic exchange with cations/protons present in food simulants, and their concentration determines the amount of released nanoparticles. Therefore, for applications where a long-term antibacterial activity is expected, nanoparticles zeolites should be placed in solutions with low ionic strength78.The immersion of matrix (nanoparticles doped in 4A z) in distilled water (as a food simulant) demonstrated that nanoparticles were sensitive to water. When the matrix was immersed in water for a long period of time, the water molecules interacted with polar groups in nanoparticles were doped in 4A z, which led to the swelling and deformation of the matrix. According to ICP-MS results (Table 5), the amount of ZnO in ZnO/4A z was initially 1031 ppb, and decreased to 943.3 ppb (ZnO/4A z) after 12 days of immersion in food simulant. These values were 655 and 3.1 ppb for TiO2/4A z, respectively; while they were recorded to be 1259 and 344.1 ppb for ZnO and TiO2/4A z. Based on the results, the migration values for ZnO, TiO2, and ZnO and TiO2 were approximately 47%, 0.47% and 21%, respectively. It is worth mentioning that ZnO and TiO2 have been approved by the US Food and Drug Administration (FDA) as safe compounds to be used in food and food contact materials at restricted quantities below 2 and 1% of the food weight for ZnO and TiO2 nanoparticles, respectively79,80. Moreover, low amounts of ZnO and TiO2 nanoparticles are beneficial for the human body because of their antimicrobial and anticancer properties. ICP-MS was used to detect the metal ions with high sensitivity, and it could detect very low signals of ZnO and TiO2 nanoparticles from the digested solutions. These results revealed that the slight migration of nanoparticles occurs in food simulant; however,this amount is in accordance with the standard rate by FDA81. Our results regarding TiO2 nanoparticles are in accordance with those of Lian et al.82.

Table 5 Migration assay of nanoparticles zeolite with ICP-MASS test.
Full size table

Conclusions

TiO2, ZnO and TiO2/ZnO nanoparticles supported into 4A z were successfully synthesized through hydrothermal method, and were evaluated for antimicrobial activity for the first time. The size of 4A z particles were around 400 to 600 nm and the average crystallite size of nanoparticles was approximately 50 nm. The XRD, SEM, MAP and TEM analysis demonstrated that crystallographic plate, size, shape and morphology of nanocomposite (nanoparticles with 4A z) are very close to 4A z itself. Moreover, the results of antimicrobial test confirmed a considerable antimicrobial activity against gram positive and negative bacteria of the nanoparticles supported in 4A z. Indeed, the antimicrobial activity of nanoparticles embedded into 4A z was dependent on the type of nanoparticles and on the species of microorganism (gram positive or gram negative). The most sensitive bacteria were P. fluorescens and then E. coli O157:H7. Embedding of nanoparticles in 4A z caused to control the release of them, and enhance their antimicrobial properties. Hence, using these composites can be a promising approach to create new active packaging in food industry.