Impregnation of poly(L-lactide-ran-δ-valerolactone) with essential bark oil using supercritical carbon dioxide

This work studied the incorporation of essential bark oil from Thujopsis dolabrata var. hondae, which is known to repel various insects, in poly(L-lactide-ran-δ-valerolactone) [poly(L-LA-ran-VL)] using supercritical carbon dioxide (scCO2). The poly(L-LA-ran-VL) was synthesized by first purifying the monomers by azeotropic distillation with benzene, followed by polymerization with Sn(oct)2 using the same equipment, representing an efficient one-pot process. The copolymerization of L-LA with VL using this technique at a feed ratio of 90/10 mol/mol gave poly(L-LA-ran-VL) (91/9) with a molecular weight of 6.48 × 104 g/mol and a high yield of 74.9%. Products with molecular weights over 5.0 × 104 g/mol were obtained at L-LA feed proportions of 70 to 90%. Impregnation trials were conducted between 40 and 120 °C at 14 MPa for 3 h. The oil content of a 73/27 specimen was found to increase significantly during processing at 100 or 120 °C. During enzymatic degradation with proteinase K, the 91/9 specimen showed the fastest degradation rate. Although the 71/29 sample was slowly hydrolyzed in a phosphate buffer at pH 7.0, the release of oil vapor from this material was slightly higher than that from the 91/9 specimen, and the vapor release rate continuously increased throughout the hydrolysis process.


Results and Discussion
Synthesis of poly(L-lactide-ran-δ-valerolactone). In a previous study, CL, TEMC and DXO, representing seven-membered cyclic esters and a carbonate, were copolymerized with L-LA, and the incorporation of essential bark oil into the resulting materials was evaluated 24 . The incorporation of CL, TEMC or DXO introduced long methylene chains into the main polymer chain, thus lowering T m and T g relative to those of pure poly(L-LA). Because the crystallinity was also reduced considerably, partial melting of the surface during processing with scCO 2 was observed even at low temperatures.
In the present work, the copolymer was synthesized using VL ( Fig. 1), which is a six-membered cyclic ester with a shorter methylene chain, and the impregnation of the copolymer with the oil using scCO 2 was evaluated. In order to obtain a high molecular weight polymer in conjunction with a high yield, it is typically necessary to first purify the monomers and to perform the polymerization under an inert gas, such as argon or nitrogen. In this work, an efficient synthetic method was developed so as to simplify the process. Therefore, azeotropic distillation, which is often applied to the refining of monomers [28][29][30][31] and manufacture of alcohol, was used. The monomer was purified by removing trace amounts of water and polymerization was carried out using a single standard distillation apparatus.
While developing the copolymerization method, the effect of the polymerization time was initially studied. These trials were performed using a 70/30 mol/mol of L-LA/VL feed ratio at 150 °C, and the resulting yields, molecular weights and L-LA/VL proportions in the product were evaluated after 6, 12, 18 and 24 h. The results are shown in Fig. 2. A copolymer synthesis performed for 6 h was found to produce a 47% yield and a molecular weight of 1.68 × 10 4 g/mol, together with an L-LA/VL ratio in the polymer of 66/34. The yield, molecular weight and L-LA proportion all increased as the polymerization time was extended. Table 1 summarizes the results of copolymerization at 150 °C for 24 h. A 1 H nuclear magnetic resonance (NMR) spectrum of the poly(L-LA-ran-VL) specimen having a 73/27 composition is shown in Fig. 3, while differential scanning calorimetry (DSC) thermograms and gel permeation chromatography (GPC) data obtained from the synthesized poly(L-LA-ran-VL) specimens are presented in Figs 4 and 5, respectively. Copolymerization of L-LA with VL resulted in poly(L-LA-ran-VL) having a molecular weight of 6.48 × 10 4 g/mol at a high yield of 74.9% in the case of the specimen with a monomer ratio of 91/9. Thus, the composition of the copolymer was almost the same as the feed ratio. It has been reported that the copolymerization of L-LA with CL at a 90/10 feed ratio gives a similar molecular weight of 7.06 × 10 4 g/mol and a composition of 92/8 24 . The T m , ΔH m and T g values for the poly(L-LA-ran-CL) were found to be 154.2 °C, 30.9 J/g and 49.8 °C, respectively. Although the T g of the poly(L-LA-ran-VL) (91/9) specimen in the current work was almost equal to that of the poly(L-LA-ran-CL) (with a value of 50.3 °C), its T m and ΔH m were considerably higher, at 173 °C and 39.2 J/g, respectively, indicating    a highly crystalline polymer. As a result of the shorter methylene lengths compared to those obtained with CL, the flexibility of the polymer chain was suppressed and thus the material crystallized more readily. The poly(L-LA-ran-VL) (73/27) also had a relatively high molecular weight, despite the lower L-LA content, and its T m and ΔH m were decreased only slightly compared to that of the poly(L-LA). These results suggest that the incorporation of VL units promotes crystallization of the polymer chain, and the copolymer with an L-LA content over 70% was used for the impregnation experiments. As demonstrated by the 1 H NMR and DSC data, random copolymerization of the VL and L-LA units thus modified the thermal characteristics of the poly(L-LA), such as the T m and T g , while reducing the crystallinity of the product. The random copolymer is therefore likely to hold an increased quantity of essential oil. The copolymerization process was also found to generate a material in which the proportions of L-LA and VL were almost equal to those in the raw material mixture. Furthermore, a high degree of polymerization was obtained from this efficient one-pot process, which also served to purify the monomer.
impregnation of poly(L-LA-ran-δ-valerolactone) with essential bark oil using supercritical carbon dioxide. In prior work, poly(L-LA) random copolymers were impregnated with essential bark oil using scCO 2 , while varying processing conditions such as the pressure, temperature and time 24 . The oil could be most efficiently impregnated into the copolymer at a processing pressure of 14 MPa, and a time span of 3 h was most suitable. Thus, the present impregnation experiments were also conducted at 14 MPa and 3 h, over the temperature range from 40 to 120 °C. The physical properties of the copolymer films used for the impregnation experiments are shown in Table 2. To allow comparisons, pure poly(L-LA) and poly(VL) were also assessed, and the resulting physical properties are provided in Table 3. The thermal properties (T m , T g , ΔH m ), degree of crystallinity (X c XRD ) and haze were all determined using 100 μm thick films produced by the solvent-casting method. The haze of a film is a measure of the degree to which it appears cloudy or translucent. If a polymeric film has a high degree of crystallinity, it will tend to be more cloudy. In this work, the cloudiness of each film (as determined by a haze meter) was considered to equal its haze value. The poly(L-LA-ran-VL) (91/9) had the highest ΔH m (39.2 J/g), along with X c XRD and haze values of 25.3% and 58.0%, respectively. The haze values were found to increase as the L-LA content was reduced, while X c XRD was decreased. The parameters T p and T d , both determined using the haze meter, indicate the degrees of parallel and diffuse light transmittance, respectively, and are correlated with the arrangement and state of the polymer molecules in the specimen. T d is determined by subtracting T p from the total light transmittance (T t ), which is equal to the incoming light. These values can be converted into haze readings, which are typically used to assess the crystallinity of a polymer. Specifically, a high haze value indicates a cloudy sample in which light undergoes diffusion, and is a measure of the transparency of the material. The T p values also decreased as the L-LA proportion was lowered, likely due to increases in the relative amounts of amorphous regions that did not transmit parallel light. The relationship between the X c XRD and the haze value was www.nature.com/scientificreports www.nature.com/scientificreports/ examined by plotting these data (Fig. 6). In the case of the copolymers having composition ratios of 91/9 to 73/27, the X c XRD and the haze value exhibit a very high degree of correlation with an almost linear relationship. Thus, if the films are prepared while keeping the solution concentration, temperature and drying conditions constant, a linear relationship is obtained. At high L-LA proportions, the degree of crystallinity was high but the haze value was reduced, while the opposite was true at lower L-LA levels. In addition, the highly crystalline films exhibited   www.nature.com/scientificreports www.nature.com/scientificreports/ low T d values. Reducing the L-LA content of the copolymer evidently decreased the degree of crystallinity, which in turn increased the haze value. This change in crystallinity was expected to increase the incorporation of essential oil into the copolymer.
To compare the level of incorporation of the essential bark oil in the various poly(L-LA) random copolymers using scCO 2 , impregnation experiments were conducted at temperatures from 40 to 120 °C and at 14 MPa for 3 h. During these trials, the temperature was reduced to approximately 40 °C after processing for 3 h, the pressure was gradually released, and the sample was taken out from the reaction vessel. Because some CO 2 was retained in the copolymer films after processing, the oil content was determined by 1 H NMR (Fig. 7), and the results are shown in Fig. 8. The oil content in each specimen was calculated using a calibration curve prepared based on the solution which precisely weighing the polymer and the essential oil and dissolved them. The calibration curve was generated by plotting the ratio of the integrated area of the peak derived from the CH group in L-LA unit to that of the peak due to the oil in the 1 H NMR spectra against the known oil content. The lowest level of oil (7.4%) was obtained at 40 °C and 14 MPa and this value increased along with the temperature, giving oil concentrations of 18.5% at both 100 and 120 °C. Because poly(L-LA) dissolves in scCO 2 above 120 °C, this temperature should allow the maximum incorporation of the essential oil into the polymer. In a previous study, we determined that synthetic copolymers of L-LA with CL or TEMC could hold more oil than poly(L-LA) 24 . However, these materials had a tendency to dissolve above 80 °C, and so were not suitable for practical applications. In this work, copolymers of L-LA with VL were used and the poly(L-LA-ran-VL) samples (91/9-73/27) did not dissolve up to 120 °C.  www.nature.com/scientificreports www.nature.com/scientificreports/ In fact, this material was found to have a T m as high as 160 °C, as shown in Table 1. In addition, since the ΔH m was greater than 25 J/g, it was predicted that this polymer would not dissolve during scCO 2 processing.
In the case of the poly(L-LA-ran-VL), the copolymer having the composition ratio 91/9 showed almost the same oil content as the pure poly(L-LA), and had a slightly higher oil content at 100 °C. The 83/17 specimen held more oil than the 91/9 sample over the entire temperature range. The T m and ΔH m values for the 83/17 sample were almost equal to those for the 91/9 sample and the poly(L-LA). However, because the T g for this material was lower, the oil content of the copolymer was only slightly increased at all temperatures. Furthermore, the impregnation of the 73/27 material was significantly improved, especially at 100 and 120 °C. The oil concentration in all the poly(L-LA-ran-VL) samples at 120 °C was lower than at 100 °C, and the data for the copolymers also differed from that for the poly(L-LA) at this temperature. These results are attributed to the T g values for the copolymers (which were 50 °C or less) in contrast to the T g for poly(L-LA), which is over 60 °C.
The incorporation of essential oil into the poly(L-LA-ran-VL) and into the other L-LA copolymers made previously was also compared. In previous work, L-LA was copolymerized with CL, TEMC or DXO, to give poly(L-LA-ran-CL), poly(L-LA-ran-TEMC) or poly(L-LA-ran-DXO). The poly(L-LA-ran-CL) and poly(L-LA-ran-DXO) had very similar thermal properties, although their T m and ΔH m were lower than those for poly(L-LA-ran-VL) at the same composition ratios, while the values for the poly(L-LA-ran-TEMC) were even lower. The poly(L-LA-ran-VL) appears to have had a greater degree of crystallinity, based on its higher T m . Because the poly(L-LA-ran-VL) was more difficult to dissolve in scCO 2 compared to the other copolymers, it would be expected to hold less essential oil. The result of impregnation trials using the four types of copolymers at a 9/1 composition ratio were compared. All these results, except those for the poly(L-LA-ran-VL) (91/9), have been previously reported 24 . The oil content of the poly(L-LA) was 7.4% at 14 MPa and 40 °C and the oil concentration increased along with the processing temperature, to 18.3% at 100 °C. Although the poly(L-LA-ran-CL) (88/12) and poly(L-LA-ran-DXO) (92/8) had almost the same T m values, because the ΔH m for the poly(L-LA-ran-DXO) was higher than that for the poly(L-LA-ran-CL), the difference in the oil content of these two materials increased as the temperature was increased, to a maximum ratio of 1.7 at 100 °C. Because the T m and ΔH m values for the poly(L-LA-ran-TEMC) (89/11) were lower than those for the poly(L-LA-ran-CL) (88/12), the oil content was greater even at a low processing temperature (for example, 29% at 80 °C), although the film dissolved at 100 °C. The poly(L-LA-ran-VL) had a very similar ΔH m value to the poly(L-LA-ran-DXO) because the T m for the former (171.3 °C) was 16 °C higher than that for the latter. Thus, the essential oil was not readily incorporated from the film surface and there was little increase in the oil concentration at high temperatures. The data for the poly(L-LA) and poly(L-LA-ran-DXO) (92/8), which had higher T m and ΔH m values, show that increasing the temperature slowly raised the oil levels in the polymers, to 20% at 100 °C, although this value was lower than that obtained for the poly(L-LA-ran-DXO) (92/8).
Next, the results obtained from the impregnation of various copolymers having an 8/2 composition ratio were compared. It has been previously reported that the oil content of poly(L-LA-ran-TEMC) (79/21) and poly(L-LA-ran-CL) (83/17) was somewhat higher at any given temperature compared with copolymers having a 9/1 composition ratio, and that the impregnation of poly(L-LA-ran-DXO) (82/18) was increased remarkably at 100 °C and 14 MPa. Because the poly(L-LA-ran-TEMC) (79/21) had a low T m of 107.4 °C and ΔH m of 8.2 J/g, the surface of the film was already dissolved in the scCO 2 at 40 °C and 14 MPa. Since the poly(L-LA-ran-VL) (91/9) had similar T m and ΔH m values to the poly(L-LA-ran-VL) (83/17), the oil concentrations were also similar at each temperature.
In the case of the copolymers having 7/3 composition ratios, since the T m and ΔH m of the poly(L-LA-ran-CL) (72/28), poly(L-LA-ran-TEMC) (76/24) and poly(L-LA-ran-DXO) (75/25) were significantly lower than those of the poly(L-LA), these copolymers melted at 80 and 100 °C. It has been previously reported that ran-VL) were higher than those of the other copolymers, this material was not plasticized as well during scCO 2 processing, and so showed a lower oil uptake. Overall, the poly(L-LA-ran-VL) appears most suitable for this purpose because it has a higher L-LA proportion and exhibits minimal dissolution.
The impregnation trials described above involved lowering the temperature to 40 °C after processing for 3 h, following by decompression to atmospheric pressure and removal of the sample [termed method (1)]. Impregnation of the essential oil followed by the release of pressure at a constant temperature is referred to herein as method (2), while the simultaneous release of pressure and cooling is method (3). These trials were performed at 14 MPa and 100 °C for 3 h, and the results from all three methods compared. The results of the different scCO 2 impregnation approaches are summarized in Fig. 9, where methods (1), (2) and (3) are indicated by black, mesh and gray bars, respectively. Method (2) evidently lowered the oil content by 1.3 to 4.0% relative to method (1). The release of the essential oil from the film was evidently increased by melting of the sample during decompression at constant temperature, thus decreasing the oil content. However, the oil content of the poly(L-LA-ran-VL) (91/9) was almost equivalent when using methods (1) and (2). This copolymer had the highest T m and ΔH m among the films used for the experiments, and it can be presumed that the degree of softening was minimal in the supercritical state at 100 °C. Although the oil content obtained using method (3) was 0.3 to 4.4% higher than for method (2) in each case, there were only minimal differences compared to method (1). Reducing the pressure and temperature simultaneously [method (3)] avoids softening of the film in response to lowering the temperature, and so the resulting oil content was equivalent to that obtained from method (1). Overall, these results show that method (1), consisting of decompressing after reducing the temperature to 40 °C, gave the highest oil concentration. enzymatic degradation and controlled vapor release during hydrolysis of poly(L-LA-ran-δvalerolactone). In order to use the synthetic poly(L-LA-ran-VL) as a base material for the controlled release of a repellent, the degradability of the polymer needs to be evaluated. For this reason, enzymatic degradability tests were performed with proteinase K (PTK), using 100 μm thick films prepared by the solvent-casting method. The results are presented in Fig. 10. The degradation of LACEA H-100 was also assessed for comparison purposes. The degradation of the poly(L-LA) was slow, with only 85% degraded after 120 h. The sample with 9 mol% VL showed the most rapid degradation rate among the polymers used, with 72% degradation at 120 h. Higher VL proportions reduced the degradation rate, suggesting that the VL units are not easily degraded with PTK. However, the 83/17 copolymer showed slower degradation than the 71/29 specimen, and this result is attributed to the higher crystallinity of the copolymer, which had 17 mol% VL.
To further examine changes in the degradability of poly(L-LA-ran-VL) specimens with PTK, scanning electron microscopy (SEM) images were obtained of samples that had been degraded by approximately 80% (Fig. 11). The samples before degradation were found to have a very smooth surface (data not shown). In contrast, the SEM www.nature.com/scientificreports www.nature.com/scientificreports/ image of poly(L-LA-ran-VL) (71/29) shows changes following enzymatic degradation by PTK at 120 h, with an accompanying 76% mass loss [ Fig. 11(A)]. Small cavities less than 10 mm in diameter appeared in the copolymer, and these cavities became smaller with increasing L-LA content. In the case of the copolymer with an L-LA content greater than 80%, cavities less than 5 mm in diameter were observed.
The release of the oil from the copolymers in the form of vapor during degradation was monitored using a volatile organic compound analyzer. During these trials, the hydrolysis of poly(L-LA-ran-VL) samples impregnated with oil was conducted in a phosphate buffer (pH 7.0) at 37 °C, with the results shown in Fig. 12 The poly(L-LA) was hydrolyzed very slowly, with only 8% mass loss after 112 days. However, the vapor release from this material showed a maximum value of 69 ppm C at only 28 days, and decreased in proportion to the amount of time elapsed after that point. The T m and ΔH m values for the poly(L-LA) were both relatively high, and so high levels of the essential oil could not be incorporated. As a result, it is believed that only the areas near the film surface contained the oil.
The poly(L-LA-ran-VL) with a higher L-LA content was hydrolyzed sooner than the other copolymers, such that the poly(L-LA-ran-VL) with a 91/9 composition ratio was 21% hydrolyzed after 112 days. However, the vapor release from this specimen was the lowest, with a maximum of 58 ppm C at 84 days. Since the oil content of the poly(L-LA-ran-VL) (91/9) was the lowest, even rapid hydrolysis led to a minimal vapor release. Although hydrolysis of the 81/19 specimen occurred sooner than that of the 91/9 material, the vapor release was highest during the early stages of hydrolysis, with a maximum of 80 ppm C at 84 days. This early release of the vapor even in the case of a high oil concentration is ascribed to the rapid hydrolysis of the sample. Although hydrolysis of the 71/29 sample was the slowest, with 63% remaining at 112 days, the vapor release continually increased up to 112 days because of the high oil content, giving a maximum of 78 ppm C at 112 days.
These vapor release data show that the poly(L-LA-ran-VL) (91/9), having the lowest oil content, underwent early hydrolysis of the base material and its release of vapor changed very little during the hydrolysis. On the contrary, the poly(L-LA-ran-VL) (71/29) had a high oil content but exhibited slow hydrolysis and generated more vapor in conjunction with a continuous increase during the hydrolysis experiment. Because the oil levels in the highly crystalline polymers were low, even rapid hydrolysis did not result in a large release of vapor. Furthermore, if both the T m and the crystallinity are low, the oil content is increased but the slower hydrolysis of the base material enables vapor release over a long period of time.

experimental Section
Materials. L-LA [(3S)-cis-3,6-dimethyl-1,4-dioxane-2,5-dione] (Aldrich) was purified by recrystallization from tetrahydrofuran. VL (Wako Pure Chemicals Ind., Ltd.) was employed as a monomer for copolymerization with L-LA and was used as-received without purification. Sn(oct) 2 (Sigma) was used as a catalyst, also without purification. Methanol and chloroform were purchased from the Japan Alcohol Trading Co., Ltd. and the Tokuyama Corporation, respectively. Benzene and ethylbenzene were purchased from Wako Pure Chemicals Ind., Ltd., dried over CaH 2 , and then filtered before use. Poly(L-lactide) (LACEA H-100) was donated by Mitsui Chemicals, Inc. Films of the synthetic copolymers were prepared by the solvent-casting method. In this process, a solution prepared by dissolving 1000 mg of the copolymer in 15 ml chloroform was poured into a Teflon dish www.nature.com/scientificreports www.nature.com/scientificreports/ with a diameter of 100 mm and placed in a fume hood, after which the solvent was allowed to slowly evaporate at approximately 25 °C. The thickness of the resulting film was measured using a micrometer (MDC-25MJ, Mitutoyo Corporation). Essential bark oil from Thujopsis dolabrata var. hondae (herein referred to simply as essential oil) was purchased from Sugiyama Mokuzai K.K. (Aomori, Japan) and used without purification. This www.nature.com/scientificreports www.nature.com/scientificreports/ material contained both neutral and acid oil. The majority of the former comprised the sesquiterpene Thujopsis dolabrata var. hondae (also known as thujopsene), which the latter contained substances such as hinokitiol and β-dolabrin (which have significant antibacterial properties) at a level of 2%. Proteinase K from Tritirachium album and N-[tris(hydroxymethyl)methyl]-glycine (Tricine) (for use as a pH 8.0 buffer) were purchased from Nacalai Tesque, Inc. and used at 37 °C. Ion-exchanged water was employed during all degradation tests. The sodium hydroxide used for pH adjustment was purchased from Wako Pure Chem. Ind., Ltd. characterization of polymers. The number-and weight-average molecular weights of the synthetic copolymers were determined by gel permeation chromatography (GPC) using a Hitachi D-2520 chromatograph equipped with a Shodex GPC K-804 column, employing chloroform as the mobile phase at 40 °C and a flow rate of 1.0 mL/min in conjunction with a refractive index detector. The molecular weights were calculated by comparison with a polystyrene standard.
Thermal characteristics [melting point (T m ), glass transition point (T g ) and enthalpy of melting (ΔH m )] were obtained using differential scanning calorimetry (DSC) using a Rigaku Thermo Plus 2/DSC8230 instrument. In these trials, samples (5 mg) were heated at a rate of 10 °C/min from -20 to 200 °C in a nitrogen stream. The T m and ΔH m values were determined during the initial heating step, while the T g value was determined during the second heating step.
The proportion of L-LA in each specimen was determined by 1 H nuclear magnetic resonance ( 1 H NMR) spectroscopy using a BRUKER AVANCE III HD 400 spectrometer. The amount of essential oil incorporated into the copolymer was also found using 1 H NMR spectroscopy. Chemical shifts are reported herein relative to the residual chloroform signal at 7.27 ppm.
During the oil incorporation experiments, the percent crystallinity (Χ c XRD ) and the haze values for the synthetic copolymer films were assessed to examine the effect of crystallinity on the oil content of the films. Crystal structures were investigated with a Rigaku Rint 2100X-ray diffractometer equipped with a scintillation counter, Each film sample was scanned at 8° (2θ 1 ) and 35° (2θ 2 ), and I c (2θ) and I(2θ) are the diffraction intensities obtained from both scans, representing crystalline and noncrystalline domains, respectively.
The haze values for the films were determined using an NDH 4000 haze meter (Nippon Denshoku Industries Co., Ltd.), measuring the total light transmittance (T t = T p + T d ), parallel light transmittance (T p ) and diffuse transmittance (T d ) simultaneously. The haze value was determined using the equation The haze, T t , T p and T d values reported herein represent the averages of triplicate analyses.

Synthesis of poly(L-lactide-ran-δ-valerolactone).
Poly(L-LA-ran-VL) was produced using an efficient one-pot synthesis reported previously 33 . This process consists of continuous dehydration of the monomers and www.nature.com/scientificreports www.nature.com/scientificreports/ solvent with subsequent polymerization. The copolymer was synthesized using Sn(oct) 2 (0.1 mol% relative to the amount of monomer) as the catalyst at 150 °C over a time span of 24 h, employing an oil bath for heating. Benzene was added at a ratio of 10 ml per g monomer as the azeotropic distillation solvent and ethyl benzene was added at a ratio of 4 ml per g monomer as the polymerization solvent. Azeotropic distillation was initially conducted for 30 min at approximately 110 °C to remove trace amounts of moisture from the reaction mixture, after which the temperature was raised to 150 °C and the polymerization was performed for 24 h. This innovative polymerization method is characterized by its ability to perform purification of both monomers and polymerization using the same distillation equipment, representing an efficient one-pot process. In this process, an azeotropic mixture is necessary to remove water in the monomers in order to successfully perform the subsequent polymerization. The system can easily and effectively utilize general distillation equipment or a distillation tower. The resulting mixture was dissolved in chloroform and then added to an excess of methanol to precipitate the polymer. The product was subsequently dried under reduced pressure at 60 °C and the molecular weights, compositions and thermal properties of the various copolymers were determined by GPC, 1 H NMR and DSC, respectively. incorporation of essential bark oil from Thujopsis dolabrata var. hondae into poly(L-LAran-δ-valerolactone) using supercritical carbon dioxide. Incorporation of essential bark oil into the poly(L-LA-ran-VL) using supercritical carbon dioxide was conducted according to a previously reported method 24,33,34 . Poly(L-LA-ran-VL) was used in the form of 100 μm thick films prepared by the solvent-casting method. Impregnation into the L-LA random copolymer film (ca. 100 mg) was carried out using essential bark oil of 2 g inside a pressure-resistant container made from stainless steel (volume: 0.5 L). The processing was performed with stirring at 100 rpm under scCO 2 at 14 MPa for 3 h, using a high-pressure reaction apparatus (MMJ-500, OM Lab-Tech Co., Ltd.) equipped with a non-pulsating flow pump (NP-KX-500, Nihon Seimitsu Kagaku Co., Ltd.). Five films could be simultaneously processed in this apparatus. The temperature was varied over the range of 40 to 120 °C at a constant pressure of 14 MPa and using a constant reaction time of 3 h. The scCO 2 was prepared by first heating the container to a temperature higher than the critical temperature of 31.1 °C, after which the atmosphere inside the container was replaced with CO 2 gas three times. The container was then filled with CO 2 using a pump intended for use with liquid. To accomplish this, a coolant flow was used to lower the pump head temperature to approximately 0 °C, after which the system pressure was increased to the desired value simply by compressing the liquid CO 2 . The liquid CO 2 that exited the pump changed to either a gas or supercritical fluid depending on the temperature and pressure of the stainless steel tube connecting the pump to the container. The liquefied CO 2 passing through the pump was turned into gas or supercritical fluid within the stainless steel tube heated to about 40 °C. Because the CO 2 temperature increased upon compression by the pumping apparatus, the temperature of the container was kept somewhat lower than the actual desired temperature during filling of the chamber with CO 2 . After filling, the temperature and pressure were adjusted to the desired values. After processing, the polymer was cooled to 40 °C and the pressure in the vessel was lowered gradually over a period of 2 h, after which the sample was removed from the container and weighed. In other trials, supercritical fluid impregnation of the oil was carried out at 14 MPa and 100 °C for 3 h followed by either decompression at a constant temperature or reduction of the pressure and temperature simultaneously. Because the samples contained high concentrations of CO 2 following impregnation, the essential oil levels were determined by 1 H NMR spectroscopy.

Degradation and controlled release of poly(L-LA-ran-δ-valerolactone). Proteinase K from
Tritirachium album (activity: 40.1 IU/mg) was used as the enzyme for the degradation of poly(L-LA-ran-VL) samples. In these trials, the enzyme was dissolved in a 50 mM pH 8.0 Tricine buffer at a level of 1 IU/mg polymer in a 50 mL sample bottle. The bottle was then placed in a shaking water bath for 15 min until it reached the degradation temperature of 37 °C. A polymer film with a mass of approximately 30 mg was prepared by the solvent-casting method and sealed in a mesh bag made from polyethylene sheets (1 mm × 1 mm mesh), then placed in the bottle containing the enzyme and buffer. The enzymatic degradation tests were conducted at 37 °C with shaking at 100 rpm. The enzyme and buffer solutions were replaced every 40 h to maintain enzymatic activity at the desired level throughout the experiments. After incubation, the samples were washed thoroughly with deionized water and dried under vacuum for 3 h. Degradability was evaluated based on the remaining sample mass.
Hydrolysis trials were performed in a 50 mM pH 7.0 phosphate buffer to evaluate the release rates of the essential bark oil vapor, using poly(L-LA-ran-VL) films impregnated with essential oil. Poly(L-LA) and poly(L-LA-ran-VL) specimens having monomer ratios of 91/9, 81/19 and 71/29 were impregnated with the oil via scCO 2 processing in preparation for these trials, and the oil concentrations in these samples were determined to be 15.8, 19.7, 24.9 and 30.3%, respectively. In each trial, a polymer sample with a mass of approximately 1200 mg and the buffer solution were transferred into a 1 L polyvinyl fluoride (PVF) bag equipped with a two-way valve, after which the bag was filled with synthetic air and hydrolysis was performed at 37 °C in an incubator. A 200 mL aliquot of the air in the bag was sampled at 28 day intervals and the amount of essential oil vapor released from each copolymer sample was determined using a volatile organic compound analyzer (VMS-1000F, Shimadzu Corp.). Following each sampling, all the air was discharged from the bag and it was refilled with fresh synthetic air to the original volume of 1 L. Degradation and controlled release tests were conducted three times and the average values are reported. conclusions scCO 2 processing at 14 MPa and 60 °C or above requires the preparation of an L-LA copolymer having a film surface that does not dissolve, thus allowing it to hold the essential oil. In this work, a copolymer made of L-LA and VL and having high T m and T g values was synthesized as the base polymer for a controlled release material, then impregnated with essential bark oil from Thujopsis dolabrata var. hondae. A copolymer with a high degree of polymerization was obtained using an efficient one-pot process. This technique produced poly(L-LA-ran-VL) www.nature.com/scientificreports www.nature.com/scientificreports/ with a high molecular weight at high yield. The T m and ΔH m of the poly(L-LA-ran-VL) were higher than those of poly(L-LA-ran-CL), and the copolymer film did not dissolve during scCO 2 processing even at 14 MPa and 120 °C. Thus, poly(L-LA-ran-VL) is superior to other copolymers, such as poly(L-LA-ran-CL), during scCO 2 processing. Impregnation experiments with the essential oil using scCO 2 showed that films of poly(L-LA-ran-VL) (91/9 to 73/27) did not dissolve up to 120 °C. Poly(L-LA-ran-VL) (91/9) absorbed oil to almost the same level as poly(L-LA), and actually had a slightly higher oil content at 100 °C. Poly(L-LA-ran-VL) (83/17) also held somewhat more oil than poly(L-LA-ran-VL) (91/9) at all temperatures. The oil content of the poly(L-LA-ran-VL) (73/27) was much higher than those of the other specimens, with especially high oil concentrations at 100 and 120 °C.
The optimal method of adding the oil was determined using three methods: decompression after reducing the temperature [method (1)], decompression at constant temperature [method (2)], and simultaneous reduction of pressure and temperature [method (3)]. The highest essential oil content was obtained using method (1), while methods (2) and (3) gave increasingly lower levels of oil impregnation.
During hydrolysis using a phosphate buffer solution at pH 7.0, the oil vapor released upon degradation of the copolymer was measured. Although the poly(L-LA-ran-VL) (91/9) had the lowest oil concentration and underwent early degradation of the base copolymer, it exhibited the least change in vapor release during hydrolysis. Conversely, because the poly(L-LA-ran-VL) (71/29) degraded slowly and held more oil, the vapor release was slightly greater, with a continual increase throughout the hydrolysis.