Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Bionanocomposites based on chitosan intercalation in designed swelling high-charged micas


Bionanocomposites based on layered inorganic components, as clays, and polymers of biological origin, as chitosan, have a major impact in medical and environmental fields, being economical and environmentally friendly materials. Na-Mn micas (n = 2 and 4) with controlled surface charge, high cation exchange capacity and swelling behaviour, are attractive inorganic composite components that exhibit improved adsorption properties compared to other inorganic solids which makes them potentially useful for bionanocomposites. The goal of this research was to explore the potential use of those synthetic brittle micas to form eco-friendly bionanocomposites with chitosan biopolymer. Hence, chitosan-mica bionanocomposites were prepared by ion-exchange reaction between chitosan solution and synthetic high charge mica. X-ray diffraction, Fourier transform infrared spectroscopy, thermal analysis, MAS-NMR spectroscopy and zeta-potential have been employed for bionanocomposites characterization. The results showed that the adsorption of chitosan is effective, although a chitosan portion remains in the outer surface being hydrogen-bonded to the tetrahedral sheet of the silicate.


Bionanocomposites are nanocomposites composed of a biopolymer and an inorganic solid1. Polymers of biological origin are the primary constituents for bionanocomposite preparation, among them chitosan, a natural polysaccharide, is being increasingly applied2,3,4,5. Chitosan is the second most abundant organic compound on Earth and is a deacetylate derivative of insects, molluscs, crustaceans, and fungi chitin2. The biopolymer chitosan offers excellent biological and physicochemical characteristics6,7, their derivate composites are easy to prepare8 and have been developed to adsorb heavy metals and dyes from wastewater9,10,11,12, with better behaviour than conventional adsorbents8.

Nanoclays are the most popular inorganic components in the preparation of bionanocomposites due to their low cost, high availability, high cation exchange capacity, strong adsorption ability and high surface area13,14,15,16. Montmorillonite12,17,18,19,20,21,22,23,24,25,26, laponite27,28,29, hectorite30,31, and saponite32,33 have been extensively studied in the literature. The introduction of chitosan in their structures leads to an improvement in their natural adsorption capabilities, forming biodegradable, economical and environmentally friendly materials34. Thus, chitosan-clay nanocomposites as bio-adsorbents have been successfully reported for the removal of water pollutants such dyes and heavy metals (tungsten, As(V) and Cr(VI))9,12.

Controlling the biopolymer/nanoclay interactions can open new route to generate smart nanomaterials with interesting technological properties, such as reliable thermal stability, hydrophobicity surface, and relevant environmental applications. In fact, many authors35,36 have expressed the need to explore parameters such as time, initial chitosan concentration, chitosan/clay ratio and type of the clay to optimize the chitosan loading. Among them, the nature of the clay, 2:1 phyllosilicate, is one of the critical parameter35 since electrostatic attractive forces improve the controlled drug release of those bionanocomposites37,38,39. Therefore, design synthetic nanoclays, that allow controlling their structural composition, can be a priceless help to obtain a deep knowledge of the bioloymer/nanoclay interaction.

Synthetic swelling high-charged fluorophlogopites, Na-Mn (n = 2 and 4 represents the layer charge), are attractive nanoclays adsorbents for their unique combination of high cation exchange capacity (CEC, 247 meq/100 g of clay for Na-M2 and 468 meq/100 g of clay for Na-M4), swelling behaviour and high layer charge. Moreover, their physical and chemical properties can be easily tuneable by an appropriate synthesis method40,41,42,43. These synthetic clay minerals have been successfully applied for the selective removal of heavy metals40, highly radioactive ions44,45 and hydrocarbon molecules after an appropriate surface modification46,47. In fact, they overcome the limited CEC and adsorption capacity of natural nanoclays, and, in particular, organo-functionalized swelling high charged micas have already shown their excellent sorption capacity for the non-ionic organic pollutants benzene, toluene and phenol47. Thus, they could be used as inorganic former of bionanocomposites obtaining better bioadsorbents.

Up to our knowledge, bionanocomposites formed with the combination of swelling brittle micas, Na-Mn, and chitosan biopolymer has never been explored although their joint properties and controlled synthesis will make this new bionanocomposite opens new routes in the field. Thus, the objective of this research was to evaluate the potential use of those synthetic mica, that overcome the limited CEC and adsorption capacity of the natural clay minerals, as inorganic component of an eco-friendly bionanocomposite. Even more, several synthesis recipes have been explored (Table S1) for the optimization of the chitosan loading. The bionanocomposites were characterized by Thermal analysis (TG), X-ray diffraction (XRD), Fourier Transform Infrared spectroscopy (FTIR), Zeta-potential and Solid State Nuclear Magnetic Resonance spectroscopy (MAS-NMR).

Results and Discussion

The stability and adsorbed amount of chitosan was evaluated with thermogravimetrical analysis. The DTG plots (Fig. S2) show mainly two weight loss regions: the first one in the range 25–200 °C, related to the adsorbed water molecules, and the second one, between 200 and 900 °C, due to dehydration, polymer chains depolymerisation and decomposition.

The weight loss between room temperature and 200 °C is 7.6% and 6.8% in the starting silicates, Na-M2 and Na-M4, respectively. The bionanocomposites show higher losses than the starting inorganic mica, up to 10.6% (Table 1) due to the high water-retention capacity of chitosan.

Table 1 Water content, chitosan content and zeta-potential of Ch-NaMn (n=2 and 4).

The adsorbed chitosan amount is calculated from the total weight loss in the 200 °C-900 °C temperature range. It is referenced to the dried sample and corrected taken into account that in this temperature range: (i) Na-Mn samples loss 2.5 and 1.5% of weigh (for n = 2 and 4, respectively) due to dehydroxylation, and, (ii) 98.6% of the chitosan sample decomposes (Table 1). The obtained values are comprised between 1 and 10.3 g of chitosan per 100 g of mica. Mica layer charge influences the amount of adsorbed chitosan, being higher in Mica-4 than in Mica-2, in good agreement with the higher cation exchange capacity, CEC, of Mica-4 (468 meq/100 g) vs Mica-2 (247 meq/100 g).

There is no influence of acetic acid concentration (Ch-NaMn-A and Ch-NaMn-B) in the adsorption of chitosan. Chitosan is a weak polyelectrolyte and their amine groups are protonated under acidic conditions, with pKa ~ 6.548, thus, the pH of the solution during the chitosan loading experiment was fixed at 4.9, to ensure that the amine groups are fully protonated.

However, the initial concentration of chitosan does have an influence (Ch-NaMnC vs Ch-NaMn-D). Yu et al.36 observed a linear increasing of loaded chitosan with initial chitosan concentration up to a plateau is reached. In Mica-2, the adsorption notably increases when the initial concentration of chitosan is raised (Ch-NaM2-C and Ch-NaM2-D), as it was previously reported for montmorillonite20. However, this increment is not observed in Mica-4 (Ch-NaM4-C and Ch-NaM4-D) due to the partial compensation of the layer charge by protons in the acid reaction media45,49.

Chitosan adsorption was enhanced for the highest layer charge nanoclay, except for Ch-NaMn-D samples. Na-M2 and Na-M4 differ in the ratio of isomorphous substitution of aluminium by silicon in the tetrahedral sheet, and, hence, in the number of negative charges per unit cell in the aluminosilicate layer. As the layer charge increases from 2 to 4, two opposite forces control the adsorption: the electrostatic interactions between the interlayer cations and the framework difficult the exchange mechanism whereas the high cation exchange capacity allows that more molecules can be hosted in the interlayer space. The adsorption of chitosan was lower in Ch-NaM4-D than in Ch-NaM2-D, as previously observed by Osuna et al.42 for the adsorption of Cs+ at severe conditions due to a higher layer charge compensation by hydronium in Mica-4.

Replacing water by acetic acid in the dissolving process improved Na-M4 chitosan adsorbent ability whereas the opposite occurred in Na-M2 sample (Ch-NaMn-D and Ch-NaMn-E). Günister et al.50 observed that the addition of acetic acid to the aqueous dispersions increases the interlayer space of clay minerals, facilitating chitosan adsorption. As observed in our samples, this effect is more evident when layer charge increases.

The DTG curves in the range between 200 °C to 900 °C (Fig. S2) illustrate the thermal decomposition behaviour of chitosan. Ch-NaMn bionanocomposites exhibit higher thermal decomposition temperature than pure chitosan, shifting ca. 165 °C, due to the intercalation of chitosan into the mica that stabilizes the organic matter51,52. Bionanocomposites exhibit two peaks on the DTG curves, one at lower temperature, similar to pure chitosan and other at higher temperature due to chitosan-mica nanocomposites. This suggest that a certain amount of polymer molecules is outside adhered to other chitosan molecules by Van der Waals forces due to the difficulty to penetrate into the interlayer space in high charged micas53.

Nanoclays surface is affected by chitosan incorporation in the framework, as it can be observed in the zeta-potential values (Table 1) obtained for chitosan-mica nanocomposites. Zeta-potential of mica particles is negative, as expected, −34.5 mV in Na-M2 and −32.2 mV in Na-M4, whereas a positive value, +16.7 mV, is observed for pure chitosan. When bionanocomposites are formed, NaMn zeta-potential is turned positive, indicating that mica particles are covered by ionized chitosan molecules20,53, this effect is quite noticeable for Ch-NaMn-E, where acetic acid is used as solvent for the mica dispersions. In those samples, the high zeta-potential values observed (+23.2 and +24.4 for Ch-NaM2-E and Ch-NaM2-4) are also related to the retained protons, as chitosan contents are similar to those observed for samples D, which show lower values, +1.9 and +1.3 mV for Ch-NaM2-D and Ch-NaM4-D respectively.

However, in Ch-NaM2-A and Ch-NaM4-C samples, the zeta-potential value remains negative, although the absolute vale diminishes The remaining negative value could be interpreted as the main adsorption mechanism in those conditions was thorough cation exchange reaction being the amount of outside adhered chitosan low50,53. Additionally, the low amount of chitosan adsorbed into the nanoclay in Ch-NaM2-A, (1.0 g/100 g, Table 1) justifies this behaviour.

X-ray diffractograms of the Na-Mn (Figs 1a and S3a) show patterns that corresponded to that previously reported for swelling high-charged micas54 with a unique 001 reflection corresponding to a basal space of 1.22 nm due to hydrated Na+55.

Figure 1

XRD in the 5–8° 2θ range of Mica-2 (n = 2), left graph, and, Mica-4 (n = 4), right graph. (a) NaMn, (b) Ch-NaMn-A, (c) Ch-NaMn-B, (d) Ch-NaMn-C, (e) Ch-NaMn-D, and, (f) Ch-NaMn-E.

The XRD patterns of mica/chitosan bionanocomposites (Fig. 1b–f) show that the reflection of the basal space of Na-Mn does not disappear, but a new weakened broad reflection at lower angle is observed. This shift indicates the formation of an intercalated nanostructure, while the broadening and low intensity of the reflection indicates a disordered intercalated structure or a partially exfoliated structure56.

The increase in the basal spacing, Δd001 ca. 0.17 nm, is below the d00l value measured from the XRD pattern of a chitosan film (0.38 nm)57 indicating that the treatment of mica with chitosan could not achieve the total intercalated state of the nanocomposite. Probably, due to the coiled structure of chitosan, intercalation only occurs in planar conformation, so that, although polymer molecules were effectively trapped inside the mica interlayer, part of them could remain at the outer surface of the clay particles53. Similar behaviour was observed by Günister et al.50, who concluded that chitosan molecules did not enter sufficiently into the layers of clay structures and the protons in chitosan were hydrogen-bonded to the oxygen species of Si–O and Al–O segments. In any case, there is co-existence between the original and intercalated samples.

The intensity of the low angle reflection increases with the initial chitosan concentration (Ch-NaMn-C vs Ch-NaMn-D, Fig. 1d,e, respectively), being remarkable in micas dispersed in acetic acid instead of water, Ch-NaMn-E (Fig. 1f). The d-spacing for the unmodified clay minerals swells when acetic acid 1% v/v is added to the aqueous dispersions50,58, and thus, the incorporation of chitosan into the interlayer space is facilitated thorough electrostatic interaction, compatible with the quite high positive zeta-potential in those samples.

The 2Ѳ region of the XRD patterns where the chitosan reflections appear is shown in Fig. S3. The XRD pattern of pure chitosan (Fig. S3g) is characterized by two main reflections at 9.92° and 20.19° 2Ѳ due to 002 and 200 planes57. The XRD pattern of the bionanocomposites, Fig. S3b-3f, show only the reflection of the starting Na-Mn, Fig. S3a, whereas the reflections of pure chitosan, Fig. S3g, are not detected. Therefore, in all of the Ch-NaMn bionanocomposites, the chitosan is interacting with the mica structure as part of the bionanocomposite.

A deep insight into the chitosan-mica interaction can be performed thorough the analysis of the 4000–2600 cm−1 and 1800–1400 cm−1 regions of the FTIR spectra (Fig. 2). Chitosan spectrum (Fig. 2g) shows bands at ca. 3450 cm−1 (interlayer O-H stretching), 3370 cm−1 (N-H stretching) and those close to 2900 cm−1 which corresponds to aliphatic C-H stretching vibrations. Additionally, the amide II band, C-O stretching of the acetyl group and N-H deformation vibration appear at 1650 and 1590 cm−1, respectively. Finally, the bands at ca. 1400 cm−1 is attributed to C-H bending58,59. The Na-Mn spectra (Fig. 2a) only show a very weak band at ca. 3622 cm−1 (structural O-H stretching).

Figure 2

4000–2600 cm−1 and 1800–1400 cm−1 regions of the FTIR spectra of Mica-2 (n = 2), left graph, and, Mica-4 (n = 4), right graph. (a) NaMn, (b) Ch-NaMn-A, (c) Ch-NaMn-B, (d) Ch-NaMn-C, (e) Ch-NaMn-D, (f) Ch-NaMn-E, and, (g) chitosan.

The infrared spectra of the chitosan-mica composites (Fig. 2-f) are formed by the combination of the mica and chitosan pure phase bands. On the one hand, in the 4000–2600 cm−1 region of the bionanocomposites (Fig. 2b–f, upper), the weak band at ca. 3622 cm−1 mica structural O-H stretching almost disappears and the N-H stretching band of chitosan emerges. On the other hand, the bands of amides and the N-H bending vibration shift to low frequency in the bionanocomposite FTIR spectra (Fig. 2b–f, bottom). As previously reported, the shifts of ν(NH3+) band confirms the interaction mainly of amino groups with mica58,59. Moreover, the interaction between the mica and the polymer modified the intensity of the band at 1550 cm−1 attributed to NH3+ which is the responsible of the intercalation by cation exchange mechanism56.

Although, the FTIR data are compatible with interaction chitosan/mica, the changes in the coordination sphere of the remaining interlayer sodium can only be analysed by 23Na MAS-NMR spectroscopy (Fig. 3). The spectra of sample Na-Mn are characterized by two set of signals: (i) a main one in the range between 0 to −25 ppm due to hydrated interlayer sodium60; and, (ii) a broad signal at ca. 27 ppm from non-exchangeable sodium61. The 23Na MAS-NMR spectra of bionanocomposites indicate that the initial Na+ content in the mica is strongly reduced after treatment with the chitosan solutions. Even at chitosan-mica ratios < 1, the intensity of 23Na signal decreases. In this way, cation exchange mechanism drives the intercalation of the biopolymer into the mica substrate20.

Figure 3

23Na MAS NMR spectra of Mica-2 (n = 2), left graph, and, Mica-4 (n = 4), right graph. (a) NaMn, (b) Ch-NaMn-A, (c) Ch-NaMn-B, (d) Ch-NaMn-C, (e) Ch-NaMn-D, and, (f) Ch-NaMn-E.

A deep understanding of the effect of chitosan on the mica framework is analysed by 29Si MAS-NMR spectroscopy. The 29Si MAS-NMR spectra of Na-Mn (Fig. 4a) consist on a set of signals on the −70 to −95 ppm region due to Q3(mAl) (3 ≤ m ≤ 0) mica environments40 and in Na-M2, Q4(4Al) from sodalite62. Due to the different number of isomorphous substitutions in the mica tetrahedral sheet, a shift is observed in all the Q3(mAl) signals in NaM2 sample, accompanied by a different relative intensity ratios between them. The relative intensity of each 29Si Q3(mAl) signals are the same as previously reported for Na-Mn40.

Figure 4

29Si MAS NMR spectra of Mica-2 (n = 2), left graph, and, Mica-4 (n = 4), right graph. (a) NaMn, (b) Ch-NaMn-A, (c) Ch-NaMn-B, (d) Ch-NaMn-C, (e) Ch-NaMn-D, and, (f) Ch-NaMn-E.

The 29Si MAS-NMR signals of Ch-NaM2 remain at the same chemical shifts but those of the Ch-NaM4 (Fig. 4b–f) shift to lower frequency, being more evident as the amount of chitosan in the bionanocomposite increases (Table 1). Alba et al.46 observed the same effect in the 29Si MAS-NMR signals signals of O-Mica-n (O is alkylammonium cation), justifying it with the incorporation of the NH3+ group into the hexagonal hole formed by the Si/Al tetrahedra, the optimal tilt angle being 50–51° 63.

However, XRD results showed that chitosan molecules are intercalated in a planar conformation, with part of them outer attracted to the mica particles53. Chitosan protons are, hence, hydrogen-bond to the Si-O and Al-O bonds in the tetrahedral sheet, provoking a weakness in those bonds and a distortion in the tetrahedral symmetry of these moieties, and, consequently, a shift in the 29Si signals50.

Additionally, the relative intensity of the Q3(mAl) signals of the Ch-NaM4 change respect to the pure Na-M4. An increasing enrichment of Q3(mAl), m ≤ 2, environments is observed that can be caused by a decrease of the total layer charge and could also contribute to the lower frequency shift of the signals40. Alba et al.64 found that in acid media the tetrahedral aluminium can leach generating an increase in the Si/Al ratio and, consequently, an intensity decreases in the Q3(mAl) sites rich in aluminium increases and Q3 rich in aluminium decreases.

In the case of Ch-NaM2, the relative intensity of the signals remains almost constant except for Ch-NaM2-E, mica dispersion with acetic acid, (Fig. 4) where the Q3(3Al) environment almost disappears. That shows that the intercalation of chitosan in the low charge nanoclay does not perturb the mica framework.

Summary and Conclusions

For the first time, bionanocomposites based on the combination of chitosan with designed swelling high-charged micas have been prepared.

In general, the bionanocomposite prepared from NaM4 contains more chitosan than those from NaM2.Those bionanocomposites exhibits higher thermal stability than the pure chitosan.

The XRD, FTIR, 29Si and 23Na MAS-NMR spectroscopy results indicate that chitosan is incorporated into the mica but part of them remains at the outer surface being hydrogen-bonded to the Si-O and Al-O of the basal plane. The surface coverage is quite high and the zeta-potentials change from a negative value of Na-Mn to a positive value for the bionanocomposites.

The most favourable chitosan loading condition was attained with a chitosan/mica ratio of 5 wt. and a 5 mg/ml solution of chitosan in acetic acid at 1%. The dispersion medium of mica has a minor influence, although optimum conditions is obtained in acetic medium.


Synthesis of Mica

The synthesis method employed was that described by Alba et al.40. Powder mixtures with molar composition: (8 - n) SiO2, (n/2) Al2O3, 6 MgF2, and (2n) NaCl (n is the layer charge per unit cell, n = 2 and 4) were used. The starting materials were SiO2 from Sigma (CAS no. 112945-52-5, 99.8% purity), Al(OH)3 from Sigma Aldrich (CAS no. 21645-51-2, 99% purity), MgF2 from Aldrich (CAS no. 20831-0, 98% purity), and NaCl from Panreac (CAS no. 131659, 99.5% purity). All reagents were mixed and ground in an agate mortar and, then, they were heated in air up to 900 °C for 15 h, in a Pt crucible. Finally, the solids were washed with deionized water and dried at room temperature. The as-synthesized samples were named as Na-Mn (n = 2 and 4).

Synthesis of bionanocomposites

Chitosan (Ch) with 310000-375000 Da of molecular weight and a viscosity of 1210 CPS was supplied by Aldrich (Product number 419419). A molecular structure of the chitosan has been included in Fig. S1.

Chitosan solutions were prepared by the addition of the corresponding amounts of polysaccharide to 10% (v/v) or 1% (v/v) acetic acid (see Table 2) proportion chitosan: acetic solution). The solution was stirred for 4 h and the pH adjusted to 4.9 with NaOH solution before mixing with the clay dispersion. Chitosan solutions containing variable weight of biopolymer were slowly added to a 2% mica dispersion (0.5 g of Na-Mn in 25 mL of bidistilled water or 1% (v/v) acetic acid) and stirred for 2 h, at 323 K, to obtain the bionanocomposites, Ch-NaMn-X (n = 2 or 4, and X = A, B, C, D or E, see Table 2).

Table 2 Synthesis parameters and sample name of Ch-NaMn (n=2 and 4).

The resulting mixture was stirred for 48 h and washed with purified water. The nanocomposites were air-dried and ground to powder.


Thermogravimetric analysis, TG, were carried out using a TA (model STD-Q600) instrument, in the Characterization Service (CITIUS, University of Seville, Spain), with alumina as reference. The samples were placed into a Pt crucible and maintained in air throughout the heating period. The temperature was increased at a constant rate of 10 °C/min. The temperature of each loss weight on the TG was determined thorough the derivative TG curve as a function of temperature (DTG).

Electrokinetic potentials were determined in a Malvern Zetasizer nano-zs90 in the Colloidal Materials Laboratory of ICMS. For each determination, 2.5 mg of samples were dispersed in 5 mL of a 10−3 M KCl solution, the slurry was stirred and pH was measured, the natural pH value for all the bionanocomposites was ca. 6 and for Na-M2 and Na-M4 that was ca. 9 and, thus, it was adjusted to 6 by adding 0.1 M HCl solution.

X-ray diffraction (XRD) patterns were obtained at the X-ray laboratory (CITIUS, University of Seville, Spain) on a Bruker D8 Advance instrument equipped with a Cu Kα radiation source operating at 40 kV and 40 mA. Diffractograms were obtained in the 2θ range of 1.5–70° with a step size of 0.015° and a step time of 0.1 s.

FTIR spectra were recorded in the range 4000–300 cm–1 in the Spectroscopy Service of the ICMS (CSIC-US, Seville, Spain), as KBr pellets dried at 120 °C, using JASCO FT/IR-6200 IRT-5000 instrument.

Single-pulse (SP) MAS-NMR experiments were recorded on a Bruker AVANCE WB400 spectrometer equipped with a multinuclear probe, in the Nuclear Magnetic Resonance Service of University of Córdoba (Córdoba, Spain). Powdered samples were packed in 3.2 mm zirconia rotors and spun at 10 kHz. 29Si MAS-NMR spectra were acquired at a frequency of 79.49 MHz, pulse width of 2.7 µs (π/6) each 3 s. 23Na MAS-NMR spectra were recorded at 105.84 MHz with a pulse of 0.75 µs (π/12) and a delay time of 0.1 s. The chemical shift values were reported in ppm from tetramethylsilane for 29Si and from a 0.1 M NaCl solution for 23Na.


  1. 1.

    Ruiz-Hitzky, E. R., Darder, M. & Aranda, P. Functional biopolymer nanocomposites based on layered solids. J. Mater. Chem. 15, 3650–3662, (2005).

    CAS  Article  Google Scholar 

  2. 2.

    Kurita, K. Chitin and chitosan: Functional biopolymers from marine crustaceans. Mar. Biotechnol. 8, 203–226, (2006).

    CAS  Article  PubMed  Google Scholar 

  3. 3.

    Rinaudo, M. Chitin and chitosan: Properties and applications. Prog. Polym. Sci. 31, 603–632, (2006).

    CAS  Article  Google Scholar 

  4. 4.

    Kumar, M., Muzzarelli, R. A. A., Muzzarelli, C., Sashiwa, H. & Domb, A. J. Chitosan chemistry and pharmaceutical perspectives. Chem. Rev. 104, 6017–6084, (2004).

    Article  PubMed  Google Scholar 

  5. 5.

    Aguzzi, C. et al. Chitosan-silicate biocomposites to be used in modified drug release of 5-aminosalicylic acid (5-ASA). Appl. Clay Sci. 50, 106–111, (2010).

    CAS  Article  Google Scholar 

  6. 6.

    Krajewska, B. Application of chitin- and chitosan-based materials for enzyme immobilizations: a review. Enzyme Microb. Technol. 35, 126–139, (2004).

    CAS  Article  Google Scholar 

  7. 7.

    Krajewska, B. & Ciurli, S. Jack bean (Canavalia ensiformis) urease. Probing acid-base groups of the active site by pH variation. Plant Physiol. Biochem. 43, 651–658, (2005).

    CAS  Article  PubMed  Google Scholar 

  8. 8.

    Ngah, W. S. W., Teong, L. C. & Hanafiah, M. Adsorption of dyes and heavy metal ions by chitosan composites: A review. Carbohydr. Polym. 83, 1446–1456, (2011).

    CAS  Article  Google Scholar 

  9. 9.

    Budnyak, T. M., Tertykh, V. A., Yanovska, E. S., Kolodynska, D. & Bartyzel, A. Adsorption of V(V), Mo(VI) and Cr(VI) Oxoanions by Chitosan-Silica Composite Synthesized by Mannich Reaction. Adsorpt. Sci. Technol. 33, 645–657, (2015).

    CAS  Article  Google Scholar 

  10. 10.

    Budnyak, T. M., Pylypchuk, I. V., Tertykh, V. A., Yanovska, E. S. & Kolodynska, D. Synthesis and adsorption properties of chitosan-silica nanocomposite prepared by sol-gel method. Nanoscale Res. Lett. 10, 10, (2015).

    CAS  Article  Google Scholar 

  11. 11.

    Budnyak, T., Tertykh, V. & Yanovska, E. Chitosan Immobilized on Silica Surface for Wastewater Treatment. Mater. Sci.-Medzg. 20, 177–182, (2014).

    Article  Google Scholar 

  12. 12.

    Hu, C., Zhu, P. F., Cai, M., Hu, H. Q. & Fu, Q. L. Comparative adsorption of Pb(II), Cu(II) and Cd(II) on chitosan saturated montmorillonite: Kinetic, thermodynamic and equilibrium studies. Appl. Clay Sci. 143, 320–326, (2017).

    CAS  Article  Google Scholar 

  13. 13.

    Chang, M.-Y. & Juang, R.-S. Use of chitosan-clay composite as immobilization support for improved activity and stability of beta-glucosidase. Biochemical Engineering Journal 35, 93–98, (2007).

    CAS  Article  Google Scholar 

  14. 14.

    An, N., Zhou, C. H., Zhuang, X. Y., Tong, D. S. & Yu, W. H. Immobilization of enzymes on clay minerals for biocatalysts and biosensors. Appl. Clay Sci. 114, 283–296, (2015).

    CAS  Article  Google Scholar 

  15. 15.

    Bertolino, V. et al. Effect of the Biopolymer Charge and the Nanoclay Morphology on Nanocomposite Materials. Industrial & Engineering Chemistry Research 55, 7373–7380, (2016).

    CAS  Article  Google Scholar 

  16. 16.

    Daraei, P. et al. Novel thin film composite membrane fabricated by mixed matrix nanoclay/chitosan on PVDF microfiltration support: Preparation, characterization and performance in dye removal. J. Membr. Sci. 436, 97–108, (2013).

    CAS  Article  Google Scholar 

  17. 17.

    Darder, M., Aranda, P., Ruiz, A. I., Fernandes, F. M. & Ruiz-Hitzky, E. Design and preparation of bionanocomposites based on layered solids with functional and structural properties. Mater. Sci. Technol. 24, 1100–1110, (2008).

    CAS  Article  Google Scholar 

  18. 18.

    Zheng, J. P., Li, P., Ma, Y. L. & De Yao, K. Gelatin/montmorillonite hybrid nanocomposite. I. Preparation and properties. J. Appl. Polym. Sci. 86, 1189–1194, (2002).

    CAS  Article  Google Scholar 

  19. 19.

    Zheng, J. P., Li, P. & Yao, K. D. Preparation and characterization of gelatin/montmorillonite nanocomposite. J. Mater. Sci. Lett. 21, 779–781, (2002).

    CAS  Article  Google Scholar 

  20. 20.

    Darder, M., Colilla, M. & Ruiz-Hitzky, E. Biopolymer-clay nanocomposites based on chitosan intercalated in montmorillonite. Chem. Mat. 15, 3774–3780, (2003).

    CAS  Article  Google Scholar 

  21. 21.

    Rhim, J. W. The effect of clay concentration on mechanical and water barrier properties of chitosan-based nanocomposite films. Food Sci. Biotechnol. 15, 925–930 (2006).

    CAS  Google Scholar 

  22. 22.

    Rhim, J. W., Hong, S. I., Park, H. M. & Ng, P. K. W. Preparation and characterization of chitosan-based nanocomposite films with antimicrobial activity. J. Agric. Food Chem. 54, 5814–5822, (2006).

    CAS  Article  PubMed  Google Scholar 

  23. 23.

    Kampeerapappun, P., Aht-Ong, D., Pentrakoon, D. & Srikulkit, K. Preparation of cassava starch/montmorillonite composite film. Carbohydr. Polym. 67, 155–163, (2007).

    CAS  Article  Google Scholar 

  24. 24.

    Wang, L. & Wang, A. Q. Adsorption characteristics of Congo Red onto the chitelsan/montmorillonite nanocomposite. J. Hazard. Mater. 147, 979–985, (2007).

    CAS  Article  PubMed  Google Scholar 

  25. 25.

    Zheng, J. P. et al. Preparation of biornimetic three-dimensional gelatin/montmorillonite-chitosan scaffold for tissue engineering. React. Funct. Polym. 67, 780–788, (2007).

    CAS  Article  Google Scholar 

  26. 26.

    Depan, D., Kumar, A. P. & Singh, R. P. Cell proliferation and controlled drug release studies of nanohybrids based on chitosan-g-lactic acid and montmorillonite. Acta Biomater. 5, 93–100, (2009).

    CAS  Article  PubMed  Google Scholar 

  27. 27.

    Fan, Q., Shan, D., Xue, H. G., He, Y. Y. & Cosnier, S. Amperometric phenol biosensor based on laponite clay-chitosan nanocomposite matrix. Biosens. Bioelectron. 22, 816–821, (2007).

    CAS  Article  PubMed  Google Scholar 

  28. 28.

    Shi, Q. F., Li, Q. B., Shan, D., Fan, Q. & Xue, H. G. Biopolymer-clay nanoparticles composite system (Chitosan-laponite) for electrochemical sensing based on glucose oxidase. Mater. Sci. Eng. C-Biomimetic Supramol. Syst. 28, 1372–1375, (2008).

    CAS  Article  Google Scholar 

  29. 29.

    Ramya, E., Rajashree, C., Nayak, P. L. & Rao, D. N. New hybrid organic polymer montmorillonite/chitosan/polyphenylenediamine composites for nonlinear optical studies. Appl. Clay Sci. 150, 323–332, (2017).

    CAS  Article  Google Scholar 

  30. 30.

    Ray, S. S. & Bousmina, M. Biodegradable polymers and their layered silicate nano composites: In greening the 21st century materials world. Prog. Mater. Sci. 50, 962–1079, (2005).

    CAS  Article  Google Scholar 

  31. 31.

    Salcedo, I. et al. In vitro biocompatibility and mucoadhesion of montmorillonite chitosan nanocomposite: A new drug delivery. Appl. Clay Sci. 55, 131–137, (2012).

    CAS  Article  Google Scholar 

  32. 32.

    Szabo, T. S. et al. Layer-by-layer construction of ultrathin hybrid films with proteins and clay minerals. J. Phys. Chem. C 111, 12730–12740, (2007).

    CAS  Article  Google Scholar 

  33. 33.

    Shchipunov, Y., Ivanova, N. & Silant’ev, V. Bionanocomposites formed by in situ charged chitosan with clay. Green Chem. 11, 1758–1761, (2009).

    CAS  Article  Google Scholar 

  34. 34.

    Budnyak, T. M., Yanovska, E. S., Kichkiruk, O. Y., Sternik, D. & Tertykh, V. A. Natural Minerals Coated by Biopolymer Chitosan: Synthesis, Physicochemical, and Adsorption Properties. Nanoscale Res. Lett. 11, 12, (2016).

    CAS  Article  Google Scholar 

  35. 35.

    dos Santos, B. F. F. et al. Synthesis and Preparation of Chitosan/Clay Microspheres: Effect of Process Parameters and Clay Type. Materials 11, 13, (2018).

    Article  Google Scholar 

  36. 36.

    Yu, T., Qu, C., Fan, D. & Xu, R. Effects of Bentonite Activation Methods on Chitosan Loading Capacity. Bulletin of Chemical Reaction Engineering and Catalysis 13, 14–23, (2018).

    CAS  Article  Google Scholar 

  37. 37.

    Liu, K. H., Liu, T. Y., Chen, S. Y. & Liu, D. M. Drug release behavior of chitosan-montmorillonite nanocomposite hydrogels following electro stimulation. Acta Biomater. 4, 1038–1045, (2008).

    CAS  Article  PubMed  Google Scholar 

  38. 38.

    Liu, W. G., Li, F., Zhao, X. D., De Yao, K. & Liu, Q. G. Atom force microscopic characterisation of the interaction forces between bovine serum albumin and cross-linked alkylated chitosan membranes in media of different pH. Polym. Int. 51, 1459–1463, (2002).

    CAS  Article  Google Scholar 

  39. 39.

    Perugini, P., Genta, I., Conti, B., Modena, T. & Pavanetto, F. Periodontal delivery of ipriflavone: new chitosan/PLGA film delivery system for a lipophilic drug. Int. J. Pharm. 252, 1–9, (2003).

    CAS  Article  PubMed  Google Scholar 

  40. 40.

    Alba, M. D., Castro, M. A., Naranjo, M. & Pavon, E. Hydrothermal reactivity of Na-n-micas (n = 2, 3, 4). Chem. Mat. 18, 2867–2872, (2006).

    CAS  Article  Google Scholar 

  41. 41.

    Gregorkiewitz, M. & Rausell-Colom, J. A. Characterization and properties of a new synthetic silicate with highly charged mica-type layers Am. Miner. 72, 515–527 (1987).

    CAS  Google Scholar 

  42. 42.

    Morikawa, Y., Goto, T., Morooka, Y. & Ikawa, T. Conversion of methanol over metal-ion exchanged forms of fluor tetra silisic mica Chem. Lett., 1667–1670, (1982).

    Article  Google Scholar 

  43. 43.

    Paulus, W. J., Komarneni, S. & Roy, R. Bulk synthesis and selective exchange of strontium ions in Na4Mg6Al4Si4O20F4 mica. Nature 357, 571–573, (1992).

    ADS  CAS  Article  Google Scholar 

  44. 44.

    Garcia-Jimenez, M. J., Cota, A., Osuna, F. J., Pavon, E. & Alba, M. D. Influence of temperature and time on the Eu3+ reaction with synthetic Na-Mica-n (n = 2 and 4). Chem. Eng. J. 284, 1174–1183, (2016).

    CAS  Article  Google Scholar 

  45. 45.

    Osuna, F. J., Cota, A., Pavon, E., Pazos, M. C. & Alba, M. D. Cs+ immobilization by designed micaceous adsorbent under subcritical conditions. Appl. Clay Sci. 143, 293–299, (2017).

    CAS  Article  Google Scholar 

  46. 46.

    Alba, M. D. et al. Formation of Organo-Highly Charged Mica. Langmuir 27, 9711–9718, (2011).

    CAS  Article  PubMed  Google Scholar 

  47. 47.

    Pazos, M. C. et al. New insights into surface-functionalized swelling high charged micas: Their adsorption performance for non-ionic organic pollutants. J. Ind. Eng. Chem. 52, 179–186, (2017).

    CAS  Article  Google Scholar 

  48. 48.

    Manni, L., Ghorbel-Bellaaj, O., Jellouli, K., Younes, I. & Nasri, M. Extraction and Characterization of Chitin, Chitosan, and Protein Hydrolysates Prepared from Shrimp Waste by Treatment with Crude Protease from Bacillus cereus SV1. Appl. Biochem. Biotechnol. 162, 345–357, (2010).

    CAS  Article  PubMed  Google Scholar 

  49. 49.

    Park, M., Kim, H. J., Kim, K. S., Duckworth, O. W. & Komarneni, S. Hydronium-Promoted Equilibrium Mechanism for the Alkali Metal Cation Exchange Reaction in Na-4-Mica. J. Phys. Chem. C 116, 18678–18683, (2012).

    CAS  Article  Google Scholar 

  50. 50.

    Gunister, E., Pestreli, D., Unlu, C. H., Atici, O. & Gungor, N. Synthesis and characterization of chitosan-MMT biocomposite systems. Carbohydr. Polym. 67, 358–365, (2007).

    CAS  Article  Google Scholar 

  51. 51.

    Chang, J. H., An, Y. U. & Sur, G. S. Poly(lactic acid) nanocomposites with various organoclays. I. Thermomechanical properties, morphology, and gas permeability. J. Polym. Sci. Pt. B-Polym. Phys. 41, 94–103, (2003).

    ADS  CAS  Article  Google Scholar 

  52. 52.

    Strawhecker, K. E. & Manias, E. Structure and properties of poly(vinyl alcohol)/Na+ montmorillonite nanocomposites. Chem. Mat. 12, 2943–2949, (2000).

    CAS  Article  Google Scholar 

  53. 53.

    Salcedo, I. et al. Intestinal permeability of oxytetracycline from chitosan-montmorillonite nanocomposites. Colloid Surf. B-Biointerfaces 117, 441–448, (2014).

    CAS  Article  Google Scholar 

  54. 54.

    Pavon, E. et al. Hydration properties of synthetic high-charge micas saturated with different cations: An experimental approach. Am. Miner. 98, 394–400, (2013).

    ADS  CAS  Article  Google Scholar 

  55. 55.

    Alba, M. D. et al. Evolution of Phases and Al-Si Distribution during Na-4-Mica Synthesis. J. Phys. Chem. C 115, 20084–20090, (2011).

    CAS  Article  Google Scholar 

  56. 56.

    Cheikh, D., Garcia-Villen, F., Majdoub, H., Viseras, C. & Zayani, M. B. Chitosan/beidellite nanocomposite as diclofenac carrier. Int. J. Biol. Macromol. 126, 44–53, (2019).

    CAS  Article  PubMed  Google Scholar 

  57. 57.

    Clark, G. L. & Smith, A. F. X-ray diffraction studies of chitin, chitosan, and derivatives. J. Phys. Chem. 40, 863–879, (1936).

    CAS  Article  Google Scholar 

  58. 58.

    Celis, R., Adelino, M. A., Hermosin, M. C. & Cornejo, J. Montmorillonite-chitosan bionanocomposites as adsorbents of the herbicide clopyralid in aqueous solution and soil/water suspensions. J. Hazard. Mater. 209, 67–76, (2012).

    CAS  Article  PubMed  Google Scholar 

  59. 59.

    Hu, C., Deng, Y. J., Hu, H. Q., Duan, Y. H. & Zhai, K. Adsorption and intercalation of low and medium molar mass chitosans on/in the sodium montmorillonite. Int. J. Biol. Macromol. 92, 1191–1196, (2016).

    CAS  Article  PubMed  Google Scholar 

  60. 60.

    Laperche, V., Lambert, J. F., Prost, R. & Fripiat, J. J. High-resolution solid-state NMR of exchangeable cations in the interlayer surface of a swelling mica - Na-23, Cd-111, and Cs-133 vermiculites. J. Phys. Chem. 94, 8821–8831, (1990).

    CAS  Article  Google Scholar 

  61. 61.

    Zeng, Z. et al. Synthesis and characterization of inorganic-organic hybrid materials based on the intercalation of stable organic radicals into a fluoromica clay. Dalton Trans. 42, 8585–8596, (2013).

    CAS  Article  PubMed  Google Scholar 

  62. 62.

    Johnson, G. M., Mead, P. J., Dann, S. E., Weller, M. T. & Multinuclear, M. A. S. NMR studies of sodalitic framework materials. J. Phys. Chem. B 104, 1454–1463, (2000).

    CAS  Article  Google Scholar 

  63. 63.

    Johns, W. D. & Sengupta, P. K. Vermiculite-alkyl ammonium complexes. Am. Miner 52, 1706–& (1967).

    CAS  Google Scholar 

  64. 64.

    Alba, M. D. et al. Hydrothermal stability of layered silicates in neutral and acidic media: effect on engineered-barrier safety. Clay Clay Min. 58, 501–514, (2010).

    ADS  CAS  Article  Google Scholar 

Download references


The authors would like to thank the Junta de Andalucía (Spain) and FEDER (Proyecto de Excelencia de la Junta de Andalucía, project P12-FQM-567), to the Spanish State Program R + D + I oriented societal challenges and FEDER (Project MAT2015-63929-R) for financial support. F.J. Osuna thanks his grant to the training researcher program associated to the excellence project of Junta de Andalucía (P12-FQM-567). Finally, we thanks to the Colloidal Materials Group of the Instituto Ciencia de los Materiales de Sevilla (ICMS) for their help in the Zeta-potential measurements.

Author information




Dr. A.C. Perdigón has synthesized the micas and F. Raffin and Dr. M.D. Alba have prepared the bionanocomposites. The characterization of the samples has been carried out by F.J. Osuna (zeta potential, IR spectroscopy and thermal analysis), A. Cota (X-ray diffraction) and Dr. E. Pavón (Nuclear Magnetic Resonance). The data have been interpreted by Dr. M.D. Alba with the help of F.J. Osuna and Dr. E. Pavón. And, the experiments supervision and the manuscript writing have been carried out by Dr. M.D. Alba.

Corresponding author

Correspondence to María D. Alba.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Alba, M.D., Cota, A., Osuna, F.J. et al. Bionanocomposites based on chitosan intercalation in designed swelling high-charged micas. Sci Rep 9, 10265 (2019).

Download citation


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links