Abstract
The paper proposes a fully optical method for determination of a cubic crystal grain orientation in a sample inspected by a Raman microscope. The method is based on a universal and strong polarisation anisotropy of the Raman scattering by doubly degenerate optic phonon modes and it only requires a standard Raman microscope equipped with a polarisation analysis. Explicit formulas for the orientation of the crystal grain are derived. The feasibility of the approach is demonstrated by comparing grain orientations in a polycrystalline cubic lacunar spinel GaV_{4}S_{8} determined independently using electron backscatter diffraction and Raman scattering methods.
Similar content being viewed by others
Introduction
Optical microscope is a standard laboratory tool for inspection of the sample geometry and its internal microstructure at μm to mm dimensions. Raman microscope is an instrument that allows, on the top of it, recording Raman spectra from the area selected by the focus of the objective. In this way, Raman microscopy provides a complementary, spatially resolved information about the structure and chemical composition.
Another important characteristic of the investigated material could be the orientation of the crystal structure within the optically inspected area. For example, optically uniaxial domains in crystals exist in several orientation variants that can be easily distinguished by polarisation sensitivity of Raman scattering. Also the crystal grain orientations in optically uniaxial polycrystalline materials can be determined by Raman scattering. In particular, the angle between the local principal optical axis and the sample surface normal can be calculated from the fine spectral shifts caused by dipoledipole interaction among polar Raman modes (oblique phonon mode method)^{1}. Among others, combination of the oblique phonon mode method with the piezoforce scanning microscopy allowed us to assign the ferroelectric domain wall types in BiFeO_{3} ceramics^{2}.
Let us stress that none of the above methods can be applied to cubic crystalline materials, because the optical indicatrix of cubic crystals does not have any special direction and these crystals have no oblique phonon eigenmodes. Fortunately, there is still another possibility, which is applicable to cubic crystals. We are suggesting here a method for detection of a completely arbitrary crystallite orientation by relying only on the universal polarisation dependence of Raman scattering by their doubly degenerate nonpolar phonon modes. The procedure is demonstrated here on a polycrystalline ceramic pellet of a cubic lacunar spinel GaV_{4}S_{8}. We have chosen GaV_{4}S_{8} since it is a cubic substance with wellseparated Raman active doublet modes and at the same time it is known to be one of the very few hosts of magnetoelectric skyrmion phases^{3,4,5}. Currently, this fascinating lacunar spinel family is attracting more and more attention^{6,7,8,9,10,11}. Nevertheless, the same approach is applicable for any other cubic material with a welldefined doubly degenerate Raman active optic phonon mode.
The paper is organised as follows. At first, we introduce GaV_{4}S_{8} and summarise the known polarisation dependence of its Raman active modes. Then we briefly describe the orientation texture of our specimen obtained by the well established electron backscatter diffraction (EBSD) and we explain how the orientation can be obtained by Raman scattering only. Finally, we compare the results and conclude the paper by discussing the advantages of this fully optical method.
Results
Raman scattering spectra of GaV_{4}S_{8}
Our demonstration material GaV_{4}S_{8} crystallizes in a noncentrosymmetric cubic structure with the \(F\bar{4}3m\,({T}_{d}^{2})\) symmetry. Below about ≈40 K it undergoes a phase transition to a rhombohedral \(R3m\,({C}_{3v}^{5})\) phase. This rhombohedral distortion, driven by JahnTeller effect in vanadium tetrahedra, causes ferroelectric polarisation in the lowtemprature phase^{3,4}. On the top of it, magnetic ordering with helicoidal and skyrmion^{12,13} arrangements observed at moderate magnetic fields and at temperatures below about 15 K attracted a great attention to the whole lacunar spinel family^{3,4}.
Here we only deal with the ambient temperature \(F\bar{4}3m\) phase. The factor group analysis predicts 3A_{1} + 3E + 3F_{1} + 6F_{2} Brillouin zone centre optic modes there, out of which 3A_{1} + 3E are nonpolar Raman active modes and 6F_{2} are simultaneously Raman and IR active modes. Previous single crystal spectroscopic and theory investigations^{14} allowed us to estimate frequencies of all its Raman active modes. For the purpose of the grain orientation analysis, it is practical to inspect well separated and strongly scattering modes, such as the A_{1} phonon mode near 277 cm^{−1} and the E phonon mode near 330 cm^{−1} (see Fig. 1).
The modes belonging to different irreducible representations are known to be conveniently distinguishable by the polarisation analysis^{15}. In the case of GaV_{4}S_{8}, within its natural crystallographic reference frame, Raman tensor R of the A_{1} modes has a general form of
Raman tensors R_{α} of the Esymmetry mode components read
and the Raman tensor of the F_{2} mode components can be expressed as
In the following it will be important that the polarisation dependence of the firstorder Raman scattering intensity by a phonon mode spanned by one or more orthogonal components α is given by a simple prefactor \({{\rm{\Lambda }}}_{{\rm{in}},{\rm{out}}}\) given by the sum of the squared moduli of the corresponding Raman tensors \({({R}_{\alpha })}_{ij}\), contracted by the incoming and outgoing photon polarisation vectors e_{in}, e_{out}, as follows
In this paper, we have only considered parallelpolarised scattering configuration, where \({{\bf{e}}}_{in}={{\bf{e}}}_{out}={\bf{e}}\), and the equation (4) reduces to
The polar plot of the parallelpolarised Raman intensity prefactor \({\rm{\Lambda }}\) is plot in Fig. 2 for the case of A_{1} and E modes, respectively. The scattering by the E mode is strongly enhanced when the photon polarisation is parallel to one of the fourfold axes. It is this universal strong anisotropy that is exploited in this paper in order to determine the orientation of the crystallographic axes within the scattering volume.
Crystal grain orientations from EBSD
To inspect the GaV_{4}S_{8} ceramics surface we used the EBSD technique. The scanning electron microscope image in Fig. 3a shows the surface morphology of the sample covering 250 × 500 μm^{2}. As can be seen, some smaller grains were removed from the surface by the polishing. Figure 3b shows an EBSD micrograph (inverse pole figure map) of the above area. The average grain size of this material is (6.8 ± 3.8) μm, according to the EBSD data. However, it is necessary to point out that several grains within the map reach the size of ≈25 μm. Some of these grains were thereafter chosen for further analysis. The selected grains, labelled A, B, C, D, are shown in Fig. 3c with their respective orientation. The colour coding of the inverse pole figure map refers to the standard unit triangle shown in Fig. 3d. The positions of grains A, B, C, D in this unit triangle are presented in Fig. 3e. The EBSD imaged area has been marked by focused ion beam (FIB) in order to facilitate its localisation under the optical microscope (not shown in Fig. 3).
In general, the crystal grain orientation relates the laboratory Cartesian reference frame A1 − A2 − A3 (see Fig. 3a) with the local Cartesian reference frame B1 − B2 − B3, attached to the crystal grain axes. The crystallographic orientation of the individual crystal grains identified by EBSD is typically given in the standard texture notation (hkl) [uvw].
The first three indices (hkl) define the crystallographic orientation of the sample surface facet (A3 in Fig. 3a) in the B1 − B2 − B3 frame. This local B1 − B2 − B3 Cartesian frame is attached to the three mutually perpendicular fourfold axes of the grain. Since the EBSD scattering intensity is invariant with respect to symmetry operations of the \(m\bar{3}m\) Laue symmetry class of the \(\bar{4}3m\) point group symmetry of the grain, one can choose the crystal grain axes B1 − B2 − B3 in a way that the Miller indices of the surface comply with
In this case, the local crystal grain coordinates of the surface unit normal n can be expressed as
where the directional cosines are ordered and nonnegative:
Each such vector n is then uniquely associated with one point in the inverse pole figure triangle (Fig. 3d).
The other part of the (hkl) [uvw] symbol defines the three Miller indices [uvw] of the conventionally chosen reference direction in the sample surface (A1 in the case of Fig. 3a). Local crystallographic coordinates of the corresponding unit vector b read
Crystal grain orientations from Raman scattering
We have selected grains with larger top surfaces which have been well observable in the optical microscope (such as those marked in Fig. 3c). The Raman scattering intensity I, detected at the resonant frequency of the selected phonon mode, is mostly given by the first order Raman scattering by that mode. Therefore, its dependence on e is proportional to the corresponding factor \({\rm{\Lambda }}\) of equation (5). The angular dependence of \({\rm{\Lambda }}\), shown in Fig. 2, suggests that for an E symmetry mode the intensity I is maximised when e is close to the direction of one the local fourfold symmetry axes.
By rotation of the sample stage around the axis of the objective of the microscope, we could collect Raman spectra from the selected grain as a function of the oriented precession angle \(\phi \) between the reference direction b and the photon polarisation \({\bf{e}}(\phi )\), where
where t = n × b.
Since the scattering intensity at frequencies corresponding to the A_{1} is isotropic, it is convenient to get rid of overall geometrical factors by inspecting the E to A_{1} intensity ratio instead of the Emode intensity alone. The angular dependence of such ratio I_{330}/I_{277} of Raman scattering intensities at frequencies 330 and 277 cm^{−1}, corresponding to the selected strong A_{1} and E modes, is shown in Fig. 4 for several selected grains. As expected, the angular dependence of the intensity near the frequency of the E mode is rather pronounced, and it allows us to extract the angles \({\phi }_{{\rm{m}}}\) and \({\phi }_{{\rm{m}}}\) at which the \({I}_{330}(\phi )\) has the highest and the second highest maxima.
For the sake of quantitative estimation of the crystal grain orientation, it is convenient to extract not only the angles \({\phi }_{{\rm{M}}}\) and \({\phi }_{{\rm{m}}}\) but also the corresponding values of \({I}_{{\rm{m}}}=I({\phi }_{{\rm{m}}})\) and \({I}_{{\rm{m}}}=I({\phi }_{{\rm{m}}})\). By comparing these values to the Emode intensity I_{0} detected for a special configuration with \({\bf{e}}\parallel \langle 100\rangle \), one can derive directly the desired values of the reduced polarisation factor λ
To achieve a higher precision, the spectra at \({\phi }_{{\rm{M}}}\) and \({\phi }_{{\rm{m}}}\) were fitted to the standard model of a superposition of damped harmonic oscillators response functions and the ratio of damped harmonic oscillator amplitude prefactors associated with the selected E to A_{1} modes was then used as the \(I({\phi }_{{\rm{m}}})\) and \(I({\phi }_{{\rm{m}}})\) values. The normalisation factor I_{0} has been determined here as the global maximum of E to A_{1} mode intensity ratios in the ensemble of all spectra taken in different orientations, but it could have been equally well set up from a spectrum measured on a selected calibration grain or on an oriented single crystal with a precisely known surface orientation.
In fact, each of the six lobes of the \({\rm{\Lambda }}\) function for an Esymmetry mode has an almost perfect rotational symmetry so that in the vicinity of the given fourfold axis it can be well approximated by an expression depending only on the deviation angle δ between e and that axis. After inserting the equation (2) into equation (5), it is convenient to express the unit polarisation vector e in spherical coordinates \({\bf{e}}=(\cos \,\delta \,\sin \,\varepsilon ,\,\sin \,\delta \,\sin \,\varepsilon ,\,\cos \,\varepsilon )\) of the local Cartesian reference frame B1 − B2 − B3 and by keeping only the leadingorder terms in δ up to o(δ^{2}), the dependence on the azimuthal angle \(\varepsilon \) drops out and the reduced prefactor \(\lambda ={\rm{\Lambda }}\)/\(4b{}^{2}\) can be expressed as
Therefore, when the photon polarisation e is close to the direction of a fourfold axis, the corresponding angle δ can be determined from the reduced scattering intensity λ using the inverse of the equation (12),
Since δ(λ) is also a monotonous function, it is clear that \(\delta (\phi )\) has a minimum where \(I(\phi )\) has a maximum, and, therefore, \({\delta }_{{\rm{m}}}=\delta ({\lambda }_{{\rm{m}}})\) and \({\delta }_{{\rm{m}}}=\delta ({\lambda }_{{\rm{m}}})\) correspond to the deviation of the closest and second closest local fourfold axes from the surface of the sample. In other terms, \({n}_{1}=\,\sin \,{\delta }_{{\rm{m}}}\) and \({n}_{2}=\,\sin \,{\delta }_{{\rm{M}}}\) and both angles in the arguments are taken positive due to the inequalities assumed in equation (8). The normalisation condition \(n=1\) then allows us to determine the missing component n_{3}. The surface normal in the local crystallographic basis of the B1 − B2 − B3 Cartesian frame can be thus expressed as
Similarly, first two directional cosines of the unit vector b can be determined from the set of equations
yielding finally
where the unknown signs \({s}_{i}=\pm \,1\) should be chosen in a way that B1 and B2 axes are mutually orthogonal, which means that
what together with \({n}_{1} > 0\) and \({n}_{2} > 0\) implies that one should select \({s}_{i}=\pm \,1\) in agreement with
Finally, b_{3} can be determined from the orthonormality condition \({{\bf{b}}}_{{\rm{Raman}}}\cdot {{\bf{n}}}_{{\rm{Raman}}}=0\).
The obtained values of λ_{M} and λ_{m} for several selected grains from Fig. 3, together with the resulting local coordinates of vectors n, determined from equation (14), are given in Table 1. Additional information about the vectors b, obtained from \({\phi }_{{\rm{M}}}\) and \({\phi }_{{\rm{m}}}\) with the help of equation (16), are given in Table 2.
Discussion
The grain orientations obtained from Raman scattering are in a quite good agreement with the results obtained from EBSD technique. It is worth noting that GaV_{4}S_{8} is a semiconductor with a sizeable absorption at the wavelength of the laser used for the present Raman scattering experiment. Consequently, the Raman scattering is collected from the top submicron layer of the investigated surface. In more transparent materials, optic method may show more deviations from the EBSD technique simply because the Raman scattering would be averaging a deeper volume. To some extent, if needed, the penetration depth could be tuned by selection of the laser wavelength. The vertical resolution would be more coarse but, in principle, one can possibly seek information about the depth profile by using confocal Raman microscopy.
On the practical side, application of this Raman spectroscopy method generally requires an optically polished or a naturally flat incident surface and, in absorbing materials like GaV_{4}S_{8}, one have to limit the laser power in the focused area in a way to avoid local heating or even laserinduced surface degradation. Since cubic materials are optically isotropic, one might also expect that when using a uniformly polished surface of the pellet and when paying an attention to maintain the same focus, power and similar geometrical conditions, one could perhaps directly use the recorded Emode intensities, without their normalisation to the intensity of A_{1}mode. However, in the case of our GaV_{4}S_{8} ceramics, this strategy was not successful, and in spite of our utmost care, the overall scattering intensity considerably varied from grain to grain, and we had to use the relative mode intensities.
It should be noted that the protocol described above fails for grains accidentally oriented with domain normal very close to the \(\langle 111\rangle \) directions, because then the \(I(\phi )\) is constant and therefore the positions of the maxima cannot be well determined. However, the expression for the surface normal n is still reasonably estimated by this method. For determination of the inplane orientation of such grain, that is for the bvector coordinates, this protocol is not suitable, but one can still use the angular dependence of Fsymmetry modes instead. In either case, if a high precision in crystal grain orientation is needed, one can always abandon equation (12) and resort to a direct numerical fitting of the measured \(I(\phi )\) profiles to the exact expressions given by equations (5).
Finally, we would like to stress that the form of the Raman tensor given in equation (2) is common to a doubly degenerate Raman mode in any of the five cubic point groups. Therefore, the present method and the equations (7–16) are valid for all cubic crystals having a firstorder Raman active mode transforming as a twodimensional irreducible representation (as a mode of E or E_{g} symmetry). In particular, it applies to both centrosymmetric and noncentrosymmetric cubic crystal structures. Obviously, the simplest cubic structures like rocksalt or cubic perovskite have no Raman active modes at all. On the other hand, a similar approach can be adopted even for certain noncubic crystals, for example the angular dependence of the pure transverse optic mode of rhombohedral BiFeO_{3}, located at 520 cm^{−1}, seems to have almost identical polarization dependence with respect to the pseudocubic axes as the cubic doublet modes investigated here^{16}. Nevertheless, as mentioned in the introduction, there are other, more straightforward optic and Raman scattering methods available for noncubic crystals, too.
In conclusion, we have realised that the strong polarisation dependence of Raman scattering by E or E_{g} symmetry modes in cubic materials could be used to determine crystallographic orientation of an arbitrarily oriented crystal facet. We have derived and tested approximate analytic expressions that allow of determining both the crystallographic orientation of the surface normal as well as the crystallographic orientation of a selected direction in the crystal surface. The method can be applied to any cubic material with E or E_{g} symmetry Raman modes. Comparison of Raman scattering and EBSD techniques applied to the same grains on a selected surface of GVS ceramics indicates that the method is functional and reasonably precise. The method can be very useful when a polycrystalline sample is used to determine anisotropic properties. In particular, we believe that this fully optical method can have advantage as a relatively cheap alternative to EBSD or in a limited experimental environment, for example when insitu EBSD is not available but optical microscopy can be arranged.
Methods
GaV_{4}S_{8} was synthesised by direct singlestep synthesis from elements. Sulphur and vanadium powders were mixed with lumps of gallium. The mixture was heated slightly by infrared lamp to melt gallium and thereafter ground and mixed in an agate mortar. The reaction mixture was put into the silica glass ampoule previously filled with argon. The ampoule was evacuated by a rotary pump, filled with argon, again evacuated, filled with argon, finally evacuated to residual argon pressure of about 2 mbar and sealed. The ampoule with reaction mixture was slowly heated at a rate of 40 K/h to 1270 K in a chamber furnace, annealed for 7 days and cooled at 10 K/min. The slow heating is necessary to allow the reaction of sulphur, since at quick heating the high pressure of sulphur can burst the ampoule. Unlike the experience of other authors this singlestep synthesis resulted in pure singlephase GaV_{4}S_{8} powders as was proved by Xray diffraction. The powder was axially pressed at a pressure of 380 MPa. The sintering was done again in a sealed silica glass ampoule by the same annealing procedure as for the synthesis of powders. The resulting ceramic GaV_{4}S_{8} pellet has 99% purity according to Xray diffraction. Samples were cut from the sintered pellet with a diamond cutoff wheel and then mechanically polished using diamond suspensions with particle sizes of 9 and 3 μm. Final mechanicalchemical polishing was performed using a solution of colloidal silica (Struers OPS).
The electron microscopy imaging and EBSD measurements were performed at 15 kV using an FEI Quanta 3D FEG scanning electron microscope equipped with TSL/EDAX Hikari camera. The EBSD analysis was done using the GaV_{4}S_{8} room temperature crystal structure data^{17}.
Raman scattering measurements were carried out using a Renishaw Raman microscope with 514 nm Argon laser in backscattering geometry and a very similar setup as the one used in our previous systematic polarised Raman scattering investigations^{18,19}.
Data Availability
The datasets generated and/or analysed during the current study are available from the corresponding author on reasonable request.
References
Hlinka, J., Pokorny, J., Karimi, S. & Reaney, I. M. Angular dispersion of oblique phonon modes in BiFeO_{3} from microRaman scattering. Phys. Rev. B 83, 020101 (2011).
Borodavka, F., Pokorny, J. & Hlinka, J. Combined piezoresponse force microscopy and Raman scattering investigation of domain boundaries in BiFeO_{3} ceramics. Phase Transitions 89, 746–751 (2016).
Kézsmárki, I. et al. Néeltype skyrmion lattice with confined orientation in the polar magnetic semiconductor GaV_{4}S_{8}. Nat. Mater. 14, 1116–1122 (2015).
Bordács, S. et al. Equilibrium Skyrmion Lattice Ground State in a Polar Easyplane Magnet. Sci. Reports 7, 7584 (2017).
Butykai, A. et al. Characteristics of ferroelectricferroelastic domains in Néeltype skyrmion host GaV_{4}S_{8}. Sci. Reports 7, 44663 (2017).
Wang, Y., Puggioni, D. & Rondinelli, J. M. Assessing exchangecorrelation functional performance in the chalcogenide lacunar spinels GaM_{4}Q_{8} (M = Mo, V, Nb, Ta; Q = S, Se). arXiv:1905.09170 [condmat.mtrlsci] (2019).
Nikolaev, S. A. & Solovyev, I. V. Microscopic theory of electric polarization induced by skyrmionic order in GaV_{4}S_{8}. Phys. Rev. B 99, 100401(R) (2019).
Kim, H.S., Haule, K. & Vanderbilt, D. Molecular Mott state in the deficient spinel GaV_{4}S_{8}. arXiv:1810.09495 [condmat.strel] (2018).
Lee, H. et al. Charge density functional plus U calculation of lacunar spinel GaM_{4}Se_{8} (M = Nb, Mo, Ta, and W). EPL 125, 47005 (2019).
Padmanabhan, P. et al. Optically Driven Collective Spin Excitations and Magnetization Dynamics in the Néeltype Skyrmion Host GaV_{4}S_{8}. Phys. Rev. Lett. 122, 107203 (2019).
Okamura, Y. et al. Microwave Directional Dichroism Resonant with Spin Excitations in the Polar Ferromagnet GaV_{4}S_{8}. Phys. Rev. Lett. 122, 057202 (2019).
Bogdanov, A. & Hubert, A. Thermodynamically stable magnetic vortex states in magnetic crystals. J. Magn. Magn. Mater. 138, 255–269 (1994).
Leonov, A. O. et al. The properties of isolated chiral skyrmions in thin magnetic films. New J. Phys. 18, 065003 (2016).
Hlinka, J. et al. Lattice modes and the JahnTeller ferroelectric transition of GaV_{4}S_{8}. Phys. Rev. B 94, 060104 (2016).
Gregora, I. Raman scattering, Part of the International tables for crystallography. Vol. D, Physical properties of crystals. (ed. Authier, A.) 314–328 (Springer Netherlands, Dordrecht, 2003).
Himcinschi, C. et al. Ferroelastic domain identification in BiFeO_{3} crystals using Raman spectroscopy. Scientific Reports 9, 379 (2019).
Pocha, R., Johrendt, D. & Pöttgen, R. Electronic and Structural Instabilities in GaV4S8 and GaMo4S8. Chem. Mater. 12, 2882–2887 (2000).
Rafalovskyi, I., Guennou, M., Gregora, I. & Hlinka, J. Macroscopic lamellar heterophase pattern in Pb(Mg_{1/3}Nb_{2/3})O_{3} − PbTiO_{3} single crystals. Phys. Rev. B 93, 064110 (2016).
Pokorný, J. et al. Polarized Raman scattering study of PSN single crystals and epitaxial thin films. J. Adv. Dielectr. 5, 1550013 (2015).
Acknowledgements
This work has been supported by the Czech Science Foundation (project no. 1711494J).
Author information
Authors and Affiliations
Contributions
P.V. synthesised and sintered the sample, K.T. performed EBSD analysis and contributed to Raman scattering experiments, P.B. and I.G. performed and analysed the most of the Raman scattering experiments, P.O. verified the mathematical expressions and helped with improving the manuscript, J.H. conceived the principal idea and wrote the main text of the manuscript. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Tesar, K., Gregora, I., Beresova, P. et al. Raman scattering yields cubic crystal grain orientation. Sci Rep 9, 9385 (2019). https://doi.org/10.1038/s4159801945782z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s4159801945782z
This article is cited by

Optical phonons of SnSe(1−x)Sx layered semiconductor alloys
Scientific Reports (2020)