Meniscal tears have a poor healing capacity, and damage to the meniscus is associated with significant pain, disability, and progressive degenerative changes in the knee joint that lead to osteoarthritis. Therefore, strategies to promote meniscus repair and improve meniscus function are needed. The objective of this study was to generate porcine meniscus-derived matrix (MDM) scaffolds and test their effectiveness in promoting meniscus repair via migration of endogenous meniscus cells from the surrounding meniscus or exogenously seeded human bone marrow-derived mesenchymal stem cells (MSCs). Both endogenous meniscal cells and MSCs infiltrated the MDM scaffolds. In the absence of exogenous cells, the 8% MDM scaffolds promoted the integrative repair of an in vitro meniscal defect. Dehydrothermal crosslinking and concentration of the MDM influenced the biochemical content and shear strength of repair, demonstrating that the MDM can be tailored to promote tissue repair. These findings indicate that native meniscus cells can enhance meniscus healing if a scaffold is provided that promotes cellular infiltration and tissue growth. The high affinity of cells for the MDM and the ability to remodel the scaffold reveals the potential of MDM to integrate with native meniscal tissue to promote long-term repair without necessarily requiring exogenous cells.
The menisci are C-shaped fibrocartilaginous tissues found between the femoral condyles and tibial plateau in the knee. The menisci serve to distribute loads, provide a low friction surface for joint loading and movement, and are critical for maintaining the normal biomechanical function of the knee1,2,3,4. Meniscal tears, particularly those in the avascular inner zone, have a poor healing capacity. Damage to the meniscus is associated with significant pain and disability, as well as degenerative changes in the knee joint that ultimately lead to osteoarthritis (OA)5,6,7,8,9,10,11. Approximately two-thirds of patients with meniscal tears develop radiographic knee OA within 5–15 years of injury12,13. Current orthopaedic practice aims to preserve meniscal integrity and restore function through a variety of different methods. These techniques include fixation devices, abrasion, trephination, biocompatible meniscus scaffolds (such as the collagen meniscus implant)14,15, and allograft transplantation. In the United States, 850,000 meniscal surgeries are performed annually, and there are nearly twice as many performed worldwide16. Despite favorable short-term results, none of these treatments have yielded long-term regeneration of functional meniscal tissue or prevented OA development17. Therefore, strategies to promote meniscus repair and induce long-term regeneration of functional meniscus tissue are needed.
In this regard, tissue engineering approaches that use biomaterial scaffolds in combination with endogenous or exogenous cells provide a novel approach for biological repair of meniscal injuries17,18. In particular, extracellular matrix (ECM)-derived scaffolds have been shown to promote tissue healing and repair for a variety of orthopaedic applications. For example, demineralized bone matrix has been used to enhance bone regeneration and repair19, and a cartilage-derived matrix has been shown to promote neocartilage formation20. Additionally, these tissue-derived matrices direct stem cell differentiation towards a phenotype similar to the tissue of origin21,22,23,24,25,26. There are several advantages of tissue-derived matrices over other scaffold types for tissue engineering applications. In particular, tissue-derived scaffolds contain native components of the ECM and promote cell infiltration and remodeling27,28. Tissue-derived scaffolds may also contain natural growth factors localized to the ECM27 and thus may minimize the need for exogenous growth factor addition. In addition, these scaffolds may promote cellular infiltration and tissue repair by enabling cells to interact with their native ECM components.
Several prior studies have generated meniscus tissue-derived scaffolds for either tissue repair or replacement. Whole meniscus tissue has been decellularized to generate allograft scaffolds for meniscus tissue replacement29,30,31,32,33,34. However, these scaffolds maintain the dense ECM that limits cellular migration into the meniscus35, which is necessary for biological repair of meniscus tissue. Other studies have used physical disruption36, chemical treatments, enzymatic treatments, or a combination thereof to generate scaffolds6,37,38,39 or hydrogel additives23,24,25,26,40,41 from meniscus tissue that could potentially be utilized for meniscus repair.
The objective of this study was to use only physical disruption of porcine meniscus tissue to generate minimally processed meniscus-derived matrix (MDM) scaffolds and test their effectiveness in promoting integrative meniscus repair. Meniscus repair and integration with meniscus tissue was evaluated using different densities of MDM with and without scaffold crosslinking. The scaffolds were filled by endogenous meniscus cells migrating from the injured meniscus tissue or seeded with exogenous bone marrow-derived mesenchymal stem cells (MSCs). Additionally, exogenous growth factors were not used, in order to evaluate the ability of endogenous cells or MSCs seeded on the MDM scaffolds to promote meniscus repair. In this study, we provide evidence that the MDM scaffold is a promising tool for integrative meniscus repair.
Generation of MDM scaffolds for meniscus tissue repair
Porcine medial menisci were harvested, minced, frozen, lyophilized, and pulverized in a freezer mill (Fig. 1). The powder was run through a 500 μm sieve to remove large particles and rehydrated to 4% or 8% concentration by weight with distilled water. The resulting slurry was homogenized on ice42 and pipetted into a mold with cylindrical holes. Next, the scaffolds were frozen, lyophilized, and removed from the mold. Half of the scaffolds at each concentration were dehydrothermally crosslinked (X) by heating at 120 °C for 24 hr in a dry oven22,43.
Scanning electron microscope (SEM) imaging was performed on MDM scaffolds to visualize the physical structure of the scaffolds (Fig. 2). The pore diameters were as follows (mean ± SEM): 81 ± 4 μm for the 4% MDM, 77 ± 4 μm for the 4% X MDM, 53 ± 3 μm for the 8% MDM, and 53 ± 2 μm for the 8% X MDM scaffolds. On average the 4% MDM scaffolds had significantly larger pore diameters than the 8% scaffolds (p < 0.000001). However, there was no effect of crosslinking on pore diameter. In all scaffolds, pores were larger than cell diameters (10–12 μm)44 and appear to be interconnected to facilitate cellular penetration into the scaffolds.
Imaging of MDM scaffolds cultured with or without meniscus tissue
An in vitro model of meniscal injury was created using porcine medial meniscus tissue cut to 8 mm diameter and 2 mm thick explants with a 3 mm diameter core removed from each explant to simulate a full-thickness defect45,46,47,48,49,50 (Fig. 3a). For control samples (Meniscus) the inner core was immediately reinserted into the defect (Fig. 3b), while in the experimental groups (Unseeded Scaffolds) the defect was filled with a 4%, 4% crosslinked (4% X), 8%, or 8% crosslinked (8% X) MDM scaffold (MDM + Meniscus) (Fig. 3c). Scaffolds were cultured without tissue (MDM alone) to allow baseline characterization of the scaffold composition (Fig. 3d). The samples were cultured in meniscus growth media and harvested after 7 or 28 days in culture for fluorescence imaging, and at 28 days for biochemical analyses, mechanical testing, and histological analysis.
Fluorescence imaging at day 7 revealed that meniscus cells migrated from the outer meniscus tissue and infiltrated the periphery of the unseeded scaffolds (Fig. 4a–d). However, very few meniscus cells migrated into the core of the scaffold (Fig. 4f–i). Conversely, there were abundant meniscus cells throughout the outer ring (Fig. 4e) and inner core (Fig. 4j) in the meniscus tissue control. At day 28, the meniscal cells had completely bridged the meniscus-scaffold interface (Fig. 4k–n) and infiltrated throughout the scaffold inner core (Fig. 4p–s). The control meniscus tissue was still filled with meniscus cells at day 28 (Fig. 4t), but fewer cells had bridged the interface between the meniscus inner core and outer ring (Fig. 4o) as compared to the MDM + Meniscus samples.
Biochemical evaluation of MDM scaffolds cultured with or without meniscus tissue
The scaffolds from the MDM + Meniscus groups had significantly higher DNA content relative to the MDM alone, indicating that native meniscal cells infiltrated the scaffold (Fig. 5a, p < 0.000001). There was no significant effect of scaffold composition (4% vs 8%) or crosslinking on the DNA content. Most notably, the DNA content of the MDM + Meniscus scaffolds was similar to the DNA content of the native meniscus tissue after 28 days.
The sulfated glycosaminoglycan (sGAG) content of the scaffolds was greater when cultured with meniscus tissue, as compared to MDM alone (Fig. 5b, p < 0.000001). In addition, the 8% scaffolds had higher sGAG content than the 4% scaffolds (p < 0.01) and crosslinked scaffolds contained more sGAG than the uncrosslinked scaffolds (p < 0.005). The native meniscus tissue contained only 2–3-fold higher sGAG content than the MDM scaffolds.
The collagen content, measured as hydroxyproline (OHP), of the scaffolds was lower in the MDM + Meniscus scaffolds than the MDM alone (Fig. 5c, p < 0.01). There was no significant effect of crosslinking on collagen content. However, the 8% scaffolds had higher collagen content than the 4% scaffolds (p < 0.01). In addition, there was an interactive effect of MDM concentration and tissue revealing the following significant differences in collagen content between groups: 4% MDM + Meniscus group < 4% MDM alone <8% MDM + Meniscus <8% MDM alone (p < 0.01). The native meniscus tissue contained only approximately 3-fold higher collagen content than the MDM scaffolds.
Imaging of MSC seeded MDM scaffolds cultured with meniscus tissue
In order to assess the potential use of MSCs in the MDM scaffolds to promote meniscus repair, MSCs were transduced with lentivirus to constitutively overexpress enhanced green fluorescent protein (eGFP) and then seeded onto 4%, 4% X, 8%, or 8% X MDM scaffolds (Fig. 3e). The expression of eGFP allowed visualization of the MSCs on the MDM scaffolds and in the meniscus tissue. After creating meniscus injuries using our in vitro model (Fig. 3a), the defect was immediately filled with the meniscus tissue inner core for control samples (Meniscus) (Fig. 3b) or a scaffold seeded with MSCs for the experimental groups (Fig. 3e) (MSC seeded MDM + Meniscus). Samples were cultured in meniscus growth media and harvested after 7 or 28 days for fluorescence imaging and at 28 days for biochemical analyses, mechanical testing, and histological analysis.
Fluorescence imaging of seeded scaffolds at day 7 showed eGFP-expressing MSCs throughout the scaffold inner cores (Fig. 6f–i). In addition, some MSCs had migrated from the scaffold into the surrounding meniscus tissue (Fig. 6a–d). At day 28, the MSCs were still evident throughout the MDM scaffold (Fig. 6p–s) and had infiltrated further into the meniscus outer ring tissue (Fig. 6k–n). On the other hand, no GFP expressing cells were visible in the meniscus tissue control at either day 7 (Fig. 6e,j) or day 28 (Fig. 6o,t).
Biochemical evaluation of MSC seeded MDM scaffolds cultured with meniscus tissue
The 8% MSC seeded scaffolds had significantly higher DNA content relative to the 4% MSC seeded scaffolds (Fig. 7a, p < 0.001), indicating that the more concentrated scaffolds could support more cells. However, there was no significant effect of crosslinking on the DNA content. Most notably, the DNA content of the 8% seeded scaffolds after 28 days of culture surrounded by meniscus tissue was similar to the DNA content of the native meniscus tissue.
The 8% MSC seeded scaffolds had higher sGAG (Fig. 7b, p < 0.000001) and collagen content (Fig. 7c, p < 0.000001) than the 4% MSC seeded scaffolds. However, there was no significant effect of crosslinking on the sGAG or collagen content of the seeded scaffolds. The native meniscus tissue control contained 2-fold higher sGAG content and approximately 10-fold higher collagen content than the 8% seeded scaffolds.
Mechanical testing to assess the shear strength of repair of the MDM scaffolds with meniscus tissue
Push-out testing was used to assess the integrative shear strength of repair45,46,48,49,50,51 between the various inner cores and the outer ring of meniscus tissue after 28 days of culture. For the unseeded MDM scaffolds, the 8% scaffolds had a 160% higher shear strength of repair than the control meniscus tissue (Fig. 8a, p = 0.05) and also repaired better than the 4% and 4% X scaffolds (p < 0.01). The 4% X scaffolds also had significantly reduced shear strength of repair, as compared to the control meniscus tissue (p < 0.05). On the other hand, the 8% X scaffolds trended towards increased repair strength compared to the control meniscus tissue, but only had improved repair strength compared to the 4% X scaffolds (p < 0.01).
For the MSC seeded MDM scaffolds, both the 8% and 8% X scaffolds had a higher shear strength of repair compared to the 4% X scaffolds (Fig. 8b, p < 0.05). While on average the 8% seeded scaffold groups had a higher shear strength of repair than the control meniscus tissue, no significant difference was detected (p = 0.2).
Histological analysis of MDM scaffolds cultured with meniscus tissue
After 28 days in culture, safranin O, fast green, and hematoxylin staining was performed to visualize the tissue structure at the interface between the meniscus tissue and MDM scaffolds. Histological analysis revealed that the MDM scaffolds had integrated with the surrounding meniscus tissue (Fig. 9). The ECM was composed predominantly of a collagenase matrix; however proteoglycan staining was apparent as well. Overall, more ECM was apparent in the samples containing 8% MDM scaffolds. All MDM scaffolds were more porous than the meniscus tissue control.
The MDM scaffold is a promising tool to enhance meniscus repair. The unseeded 8% MDM scaffolds improved the integrative repair strength of an in vitro meniscal defect as compared to a native meniscal tissue implant. In the absence of exogenous cells, crosslinking and concentration of the MDM influenced the biochemical content and shear strength of repair, revealing that the properties of the scaffolds can be modulated to promote tissue repair. Meniscal cells migrated from the surrounding meniscus tissue into the scaffolds and produced sGAGs, but decreased the collagen content of the scaffolds. Likewise, exogenous MSCs also showed high infiltration into the scaffolds, and higher MDM concentrations promoted the growth and retention of more cells. In the MSC seeded scaffolds, MDM concentration but not crosslinking influenced the biochemical and mechanical properties. The high affinity of cells for this scaffold, combined with their ability to remodel the scaffold is promising for the potential of MDM to integrate seamlessly into the native meniscal tissue to promote repair.
A major barrier to integrative meniscus repair is the dense ECM that prevents endogenous cells from readily migrating through the tissue to the tear site. Previous work has shown that the extracellular matrix of the adult meniscus sterically hinders cell mobility35,52. Therefore, our approach was to generate porous scaffolds that allowed migration of native meniscus cells into the scaffolds to form reparative tissue. The quantity of native meniscus cells on the unseeded scaffolds was not influenced by either the MDM concentration or crosslinking, although there was a trend towards more cells on the higher percentage scaffolds. In addition to being readily populated by native cells, the scaffolds were also able to support the growth and expansion of MSCs. In this case, there were more cells on the more concentrated MDM scaffolds. Remarkably, in only 28 days the number of either native meniscus cells or MSCs was quite similar to the number of cells found in the meniscus tissue control, indicating the high affinity of these cells for the MDM scaffold.
The MDM scaffold processing procedures resulted in retention of only approximately 1% of the DNA content of the meniscus control. On average, the MDM scaffolds contained 25 ng DNA per mg dry weight, which is lower than the recommended criteria for decellularization (<50 ng DNA/mg dry weight)53. Previous work has shown that in vivo there was no significant difference in M2:M1 macrophage ratios in response to implanted collagen scaffolds supplemented with 50 ng DNA or equivalent cellular amounts of mitochondria or cell membranes, as compared to collagen scaffolds alone54. However, in vivo experiments would be necessary to rule out immunoreactivity to our MDM scaffolds. Nonetheless, our reduction in DNA content is equivalent to or better than that seen with chemical and enzymatic decellularization protocols for meniscus, which range from 10 to 100-fold decreases in DNA content24,25,37,38,39,40,41. Furthermore, many of these prior decellularization protocols also reduced proteoglycan content25,40,41,55. Even after 28 days in culture, in this study the 8% scaffolds alone contained approximately 50% of the sGAG content of the meniscus tissue control, highlighting the ability of our scaffold preparation protocol to retain proteoglycans. As expected, there was greater sGAG and collagen content in the 8% scaffolds than the 4% scaffolds. However, the crosslinking of the scaffolds allowed for the retention of even more proteoglycans. This result is consistent with prior experiments using cartilage-derived matrix22 and with prior work demonstrating that dehydrothermal crosslinking results in covalent crosslinks between collagen and chondroitin sulfate56. Interestingly, there was greater sGAG content in the MDM + Meniscus samples than the MDM cultured alone, indicating that the infiltrating meniscus cells produced sGAGs that were retained in the scaffold.
The MDM + Meniscus samples had lower collagen content than the MDM alone, indicating a degradation of the collagen matrix in the presence of the meniscus cells. Dehydrothermal treated collagen matrices are more sensitive to trypsin digestion, which suggests that the crosslinking may partially denature the collagen matrix57. However, the decrease in collagen content in our study was independent of crosslinking, suggesting that the meniscus cells are remodeling the MDM scaffold and have not yet synthesized new collagen matrix. Future studies may explore the addition of physiologic mechanical stimulation to enhance collagen production and alignment58.
The enhanced integrative repair strength using the MDM shows the potential of the scaffold to improve tissue healing. There was increased repair beyond that seen with the meniscus control in the unseeded 8% MDM scaffolds. This work underscores the fact that native meniscus cells can enhance meniscus healing if provided with a favorable scaffold to promote cellular infiltration. Therefore, the use of exogenous cells may not be necessary to improve integrative meniscus tissue repair. However, one advantage of cell-based therapies is that they can be tailored to allow modulation of the injury microenvironment. For example, MSCs expressing inducible IL-1 receptor antagonist (IL-1ra) seeded on 3D woven polycaprolactone or cartilage-derived scaffolds have been used to modulate the pro-inflammatory environment59,60 that is present following joint injury and in OA. Therefore, future work could investigate whether genetically modified cells can further improve meniscus healing beyond that which is possible with native meniscus cells.
In these experiments, exogenous growth factors were not added to the culture media. We relied on the growth factors and matrix proteins that were retained in the MDM scaffolds to stimulate matrix production. However, prior studies have shown that chondrogenic media containing TGF-β3 was necessary for chondrogenic differentiation of MSCs in methacrylated gelatin hydrogels with meniscus matrix extract25 or decellularized meniscus scaffolds37. Connective tissue growth factor or TGF-β3 has also been shown to promote more robust chondrogenesis of infrapatellar fat pad stem cells as compared to control cultures in alginate functionalized with meniscus ECM26. While the combination of TGF-β3 and insulin-like growth factor (IGF)-1 was necessary to induce chondrogenesis of synovial fluid MSCs in a meniscus-derived matrix36. Previously, we found that TGF-β1 enhances meniscus cell accumulation in the interface of an injured meniscus explant and improves integrative shear strength of repair47. Several other studies have utilized chondrogenic media to promote matrix gene expression, ECM production, or both by MSCs in scaffolds containing meniscus-derived matrix23,24,25. Without the use of exogenous growth factors, our MDM scaffold was able to promote cellular migration into the scaffold, sGAG production, and improved integrative repair. The addition of soluble exogenous growth factors, tethering growth factors to the MDM, or introducing viral delivery systems to the MDM scaffold might further enhance tissue production and improve fibrochondrogenesis and integrative repair; however, this would increase the difficulty of translating this native MDM scaffold into the clinic for meniscus repair applications.
Early work on meniscus matrix scaffolds focused on the use of whole menisci for meniscus replacement29,30,31,32,33,34, which is necessary for degenerative joints and complex meniscus tears. However, our MDM scaffold can be used to reintegrate two pieces of meniscus tissue for radial, peripheral, longitudinal, or horizontal flap tears. As evidenced by the porous nature of our MDM scaffolds even after culture, the MDM scaffold is not mechanically robust enough to functionally replace the whole meniscus tissue. However, pre-fabricated MDM scaffolds could be used to bridge small gaps in a meniscus lesion to promote cellular infiltration and integrative repair. Alternatively, the MDM could be injected into lesions as a slurry to function as a biological glue. Further studies in meniscus-injured animal models will be necessary to translate the MDM scaffold to clinical use.
In this study, we provide evidence that the MDM scaffold is a promising tool for integrative meniscus repair. The scaffold provides a favorable environment for cellular infiltration and remodeling, and can enhance integrative repair. Thus, it has the potential to integrate seamlessly into meniscal lesions and promote repair without the need for an exogenous cell source or external growth factors. The high affinity of native meniscal cells to infiltrate the acellular MDM scaffolds, suggests that MDM is a favorable scaffold material to recruit native cells and promote long-term meniscal repair and homeostasis.
Medial menisci were harvested from the knees of skeletally mature 2–3 year old female pigs obtained from a local abattoir (n = 33), minced into ≤5 mm pieces, frozen overnight at −80 °C, and then lyophilized (FreeZone 2.5 L, Labconco, Kansas City, MO) for 24 h (Fig. 1). The lyophilized meniscus pieces were pulverized (5 min pre-cool, 5 cycles of 1 min at 5 Hz and 2 min cool) in a 6770 freezer mill (SPEX SamplePrep, Metuchen, NJ). The powder was sieved (500 µm) and pooled into a superlot that was used for further experiments.
MDM powder was rehydrated to either 4% or 8% weight fraction by mixing 0.4 g or 0.8 g MDM powder with distilled water to achieve 10 g total mass. After resuspension, the MDM slurry was homogenized (PRO260, PRO Scientific Inc., Oxford, CT) at 30,000 rpm for 2 cycles of 2 min run, 2 min cool on ice42. This homogenized slurry was pipetted into a delrin mold to completely fill holes of 1.8 mm-2 mm deep x 3 mm diameter and leave no trapped air bubbles. A silicone lid was placed over the delrin mold containing MDM slurry and was frozen at −80 °C overnight.
The next day the silicon cover was removed from the mold, and the delrin base containing the frozen slurry was returned to −80 °C for 30 min to ensure the scaffolds were completely frozen. The delrin mold with scaffolds was lyophilized for 24 h and the scaffolds were removed. Half of the scaffolds at each concentration were dehydrothermally crosslinked (X) by heating at 120 °C for 24 h in a dry oven22. All scaffolds were ethylene oxide sterilized in scintillation vials.
SEM imaging of scaffolds
The MDM scaffolds were sputter-coated (Desk IV, Denton Vacuum, Moorestown, NJ) with gold at 18 mA for 600 s, resulting in a 20 nm thick deposition. After coating, samples were scanned (FEI XL30 ESEM, Hillsboro, OR) at an accelerating voltage of 30 kV. Images were taken at 250x magnification. To characterize pore size, maximum pore diameters were measured from SEM images using Image J (NIH) (n = 20/group).
Meniscus explant harvest and injury model
Medial menisci were harvested from the knees of skeletally mature female pigs. 8 mm diameter punches were taken along the centerline of the tissue and then cut to a uniform thickness of 2 mm. A 3 mm diameter inner core was removed from the explant to simulate a full-thickness defect45,46,47,48,49,50,51 (Fig. 3a). For control samples (Meniscus), the inner core was immediately returned to the defect (Fig. 3b). Tissue explants were then transferred to 12 well plates (Corning Life Sciences), which had previously been coated with 500 μL of 2% agarose (Bio-Rad, Hercules, CA) to prevent cell attachment. Explants were incubated for 1 hour in wash media containing DMEM high glucose (DMEM-HG; Invitrogen, Carlsbad, CA) supplemented with 10% penicillin/streptomycin/fungizone (Invitrogen). Next the explants were removed from the wash media and the defect was filled with a 4%, 4% X, 8%, or 8% X MDM scaffold for the experimental groups (MDM + Meniscus) (Fig. 3c). These scaffolds were either wetted with DMEM-HG (Invitrogen) immediately prior to placement in the defect (Fig. 3c) or seeded with eGFP-expressing MSCs (Fig. 3e) as described below. The explants with MDM cores were then cultured in 4 mL meniscus growth medium consisting of DMEM-HG supplemented with 10% FBS (AVH79983, HyClone), 1% penicillin-streptomycin (Invitrogen), 1% HEPES buffer (Invitrogen), 1% non-essential amino acids (Invitrogen), and 37.5 μg/mL ascorbic acid 2-phosphate (Sigma-Aldrich, St. Louis, MO) at 37 °C/5% CO2 with media changes every 3 days. Unseeded MDM scaffolds (MDM alone) were also cultured without tissue (Fig. 3d). Samples were harvested after 7 or 28 days for fluorescent imaging and at day 28 for mechanical testing, biochemical analyses, and histology.
EGFP was previously cloned into a lentiviral vector with the constitutive human EF-1α promoter (Addgene plasmid 12250)59,61. Lentivirus was produced in HEK293T/17 (ATCC CRL-11268, Manassas, VA), concentrated ∼75-fold using Amicon Ultra 100 kDa MWCO filters (Millipore, Cork, Ireland), and titered as described previously59.
MSC transduction and scaffold seeding
Excess bone marrow aspirate was obtained from three de-identified adult bone marrow transplant donors at Duke University School of Medicine, in an IRB-exempt waste tissue protocol. Human MSCs were isolated, expanded, and pooled into a superlot as described previously42,60. MSCs at passage 3 were plated at 1 × 106 cells/T-225 flask (Corning). The next day, cells were transduced with lentivirus vectors (2.48 × 107 infectious particles/mL) supplemented with 4 μg/mL polybrene. After 20 hr, MSC expansion media containing 2 ng/mL bFGF was added to the cells. Media was refreshed every 2 days. On day 6, cells were trypsinized, counted, and frozen in liquid nitrogen to ensure they would be at the same passage during all subsequent experiments.
GFP-expressing MSCs were thawed and expanded. Passage 4 cells were trypsinized and resuspended in MSC expansion medium at a density of 7.8 × 106 cells/mL. MDM scaffolds (4%, 4% X, 8%, and 8% X) were placed in a silicone seeding mold with holes 3 mm in diameter x 2 mm deep. Then 8 μL of cell suspension was pipetted onto the top of each scaffold. The seeding mold was placed into a vacuum chamber for 45 seconds to improve cell infiltration62. Scaffolds were flipped and 8 μL of cell suspension was pipetted onto the other side of the scaffolds and a vacuum was pulled for another 45 seconds to encourage cellular infiltration throughout the entire volume of the scaffold. The scaffolds were placed in individual wells of 24 well low attachment plates (Corning) for 30 min to allow cellular attachment. Then 1 mL of supplemented MSC expansion media was added to each well. The cells were expanded on the MDM scaffolds for 6 days, with media replaced every 48 hr. After 6 days of cell expansion, the seeded scaffolds were placed into the outer ring of the meniscal explant injury model described above (Fig. 3e).
Fluorescent imaging of constructs
For the unseeded MDM scaffold experiments, confocal microscopy (LSM 510, Zeiss, Thornwood, NY, USA) was used to visualize the interface between the inner core and outer ring of meniscus tissue, and the central portion of the various inner cores during culture. Meniscal repair model explants were harvested after 7 and 28 days in culture for imaging to visualize live cells (calcein AM, Invitrogen) and matrix (Alexa fluor 633 NHS ester, Invitrogen). For MSC seeded experiments, widefield fluorescent images (IX83, Olympus) were taken of eGFP-labeled MSCs and Alexa fluor 633 NHS ester stained matrix at days 7 and 28.
Mechanical testing for the shear strength of repair
After 28 days of culture, explants were harvested for mechanical testing using a push-out test (n ≥ 9/group)45,46,48,49,50,51. Each sample was loaded onto a dish, which contained a 4 mm hole in the center, and placed in the loading frame (ELF 3200, EnduraTec, Minnetonka, MN). A 2 mm piston was connected to a load cell (Honeywell, Morris Plains, NJ) and centered directly above the inner core. A 0.5 g tare load was applied for 10 seconds, and then the piston was lowered to a final displacement of 4 mm at a rate of −0.083 mm/sec. Images taken of each construct were imported into Image J software to measure sample thickness and diameter. MATLAB (Mathworks, Natick, MA) was used to create force-displacement curves and shear strength was calculated as the peak force divided by the area of the repair interface.
Biochemical analyses of MDM constructs
After mechanical testing, each MDM inner core was digested in 500 μL of papain (125 μg/mL papain (Sigma), 100 mM phosphate buffer, 10 mM cysteine, and 10 mM EDTA, pH 6.3) at 65 °C overnight22,63,64 for biochemical analyses (n ≥ 9/group). MDM scaffolds that were cultured alone were subjected to the same digest conditions (n = 6/group). The picogreen assay (Invitrogen) was used to measure DNA content. The sGAG content was measured using the dimethylmethylene blue assay65, and a bovine chondroitin sulfate standard (Sigma-Aldrich). Collagen content was assessed through the hydroxyproline assay66, which utilizes alkaline hydrolysis to cleave collagen into hydroxyproline, followed by reaction with chloramine-T and 4-(Dimethyl-amino)benzaldehyde63,64. Biochemical data was corrected for the volume of the scaffold.
Histological analysis of constructs
After 28 days in culture, samples were fixed in formalin overnight at 4 °C, dehydrated, and paraffin embedded. Samples were cut into 8 μm sections and then stained with Harris’ hematoxylin (Poly Scientific), 0.02% aqueous fast green (Electron Microscopy Sciences), and 0.1% aqueous Safranin-O (Sigma-Aldrich) in order to visualize cell nuclei, collagen, and proteoglycans respectively.
Statistical analyses were performed using Statistica (Tibco). All data were normally distributed. For the biochemical outcomes, factorial ANOVA and Fisher LSD post hoc tests were performed to determine significant group differences (α = 0.05), as well as the interactive effects of concentration, crosslinking, and tissue. In order to allow statistical comparison to the meniscus control group, one-way ANOVA and Fisher LSD post hoc tests were performed for the shear strength data.
All data generated or analyzed during this study are included in this published article.
Ahmed, A. M. & Burke, D. L. In-vitro measurement of static pressure distribution in synovial joints–Part I: Tibial surface of the knee. J Biomech Eng 105, 216–225 (1983).
Markolf, K. L., Bargar, W. L., Shoemaker, S. C. & Amstutz, H. C. The role of joint load in knee stability. J Bone Joint Surg Am 63, 570–585 (1981).
Wojtys, E. M. & Chan, D. B. Meniscus Structure and Function. AAOS Instructional Course Lectures 54, 323–330 (2005).
Carter, T. E. et al. In vivo cartilage strain increases following medial meniscal tear and correlates with synovial fluid matrix metalloproteinase activity. J Biomech 48, 1461–1468, https://doi.org/10.1016/j.jbiomech.2015.02.030 (2015).
Badlani, J. T., Borrero, C., Golla, S., Harner, C. D. & Irrgang, J. J. The effects of meniscus injury on the development of knee osteoarthritis: data from the osteoarthritis initiative. The American journal of sports medicine 41, 1238–1244, https://doi.org/10.1177/0363546513490276 (2013).
Berthiaume, M. J. et al. Meniscal tear and extrusion are strongly associated with progression of symptomatic knee osteoarthritis as assessed by quantitative magnetic resonance imaging. Ann Rheum Dis 64, 556–563, https://doi.org/10.1136/ard.2004.023796 (2005).
Christoforakis, J., Pradhan, R., Sanchez-Ballester, J., Hunt, N. & Strachan, R. K. Is there an association between articular cartilage changes and degenerative meniscus tears? Arthroscopy-the Journal of Arthroscopic and Related Surgery 21, 1366–1369 (2005).
Hunter, D. J. et al. The association of meniscal pathologic changes with cartilage loss in symptomatic knee osteoarthritis. Arthritis Rheum 54, 795–801, https://doi.org/10.1002/art.21724 (2006).
Roos, H. et al. Knee osteoarthritis after meniscectomy: prevalence of radiographic changes after twenty-one years, compared with matched controls. Arthritis Rheum 41, 687–693, https://doi.org/10.1002/1529-0131(199804)41:4<687::AID-ART16>3.0.CO;2-2 (1998).
Sharma, L. et al. Relationship of meniscal damage, meniscal extrusion, malalignment, and joint laxity to subsequent cartilage loss in osteoarthritic knees. Arthritis Rheum 58, 1716–1726, https://doi.org/10.1002/art.23462 (2008).
Wyland, D. J., Guilak, F., Elliott, D. M., Setton, L. A. & Vail, T. P. Chondropathy after meniscal tear or partial meniscectomy in a canine model. J Orthop Res 20, 996–1002 (2002).
Lohmander, L. S., Englund, P. M., Dahl, L. L. & Roos, E. M. The long-term consequence of anterior cruciate ligament and meniscus injuries: osteoarthritis. The American journal of sports medicine 35, 1756–1769, https://doi.org/10.1177/0363546507307396 (2007).
Lohmander, L. S., Roos, H., Dahlberg, L., Hoerrner, L. A. & Lark, M. W. Temporal patterns of stromelysin-1, tissue inhibitor, and proteoglycan fragments in human knee joint fluid after injury to the cruciate ligament or meniscus. J Orthop Res 12, 21–28, https://doi.org/10.1002/jor.1100120104 (1994).
Lin, D. D., Picardo, N. E., Adesida, A. & Khan, W. S. Clinical Studies Using Biological and Synthetic Materials for Meniscus Replacement. Curr Stem Cell Res Ther 12, 348–353, https://doi.org/10.2174/1574888X11666160429123110 (2017).
Guo, W. et al. Advances and Prospects in Tissue-Engineered Meniscal Scaffolds for Meniscus Regeneration. Stem Cells Int 2015, 517520, https://doi.org/10.1155/2015/517520 (2015).
Baker, B. S., Lubowitz, J. H. & Wolf, B. T. Meniscus Injuries, http://www.emedicine.com/sports/TOPIC160.HTM (2015).
Scotti, C., Hirschmann, M. T., Antinolfi, P., Martin, I. & Peretti, G. M. Meniscus repair and regeneration: review on current methods and research potential. European cells & materials 26, 150–170 (2013).
Mauck, R. L. & Burdick, J. A. From repair to regeneration: biomaterials to reprogram the meniscus wound microenvironment. Ann Biomed Eng 43, 529–542, https://doi.org/10.1007/s10439-015-1249-z (2015).
Urist, M. R. Bone: formation by autoinduction. Science 150, (893–899 (1965).
Cheng, N. C., Estes, B. T., Young, T. H. & Guilak, F. Engineered cartilage using primary chondrocytes cultured in a porous cartilage-derived matrix. Regen Med 6, 81–93, https://doi.org/10.2217/rme.10.87 (2011).
Little, D., Guilak, F. & Ruch, D. S. Ligament-derived matrix stimulates a ligamentous phenotype in human adipose-derived stem cells. Tissue Eng Part A 16, 2307–2319, https://doi.org/10.1089/ten.tea.2009.0720 (2010).
Rowland, C. R., Lennon, D. P., Caplan, A. I. & Guilak, F. The effects of crosslinking of scaffolds engineered from cartilage ECM on the chondrogenic differentiation of MSCs. Biomaterials 34, 5802–5812, https://doi.org/10.1016/j.biomaterials.2013.04.027 (2013).
Yuan, X. et al. Stem cell delivery in tissue-specific hydrogel enabled meniscal repair in an orthotopic rat model. Biomaterials 132, 59–71, https://doi.org/10.1016/j.biomaterials.2017.04.004 (2017).
Shimomura, K., Rothrauff, B. B. & Tuan, R. S. Region-Specific Effect of the Decellularized Meniscus Extracellular Matrix on Mesenchymal Stem Cell-Based Meniscus Tissue Engineering. The American journal of sports medicine 45, 604–611, https://doi.org/10.1177/0363546516674184 (2017).
Rothrauff, B. B., Shimomura, K., Gottardi, R., Alexander, P. G. & Tuan, R. S. Anatomical region-dependent enhancement of 3-dimensional chondrogenic differentiation of human mesenchymal stem cells by soluble meniscus extracellular matrix. Acta Biomater 49, 140–151, https://doi.org/10.1016/j.actbio.2016.11.046 (2017).
Romanazzo, S., Vedicherla, S., Moran, C. & Kelly, D. J. Meniscus ECM-functionalised hydrogels containing infrapatellar fat pad-derived stem cells for bioprinting of regionally defined meniscal tissue. J Tissue Eng Regen Med 12, e1826–e1835, https://doi.org/10.1002/term.2602 (2018).
Badylak, S. F. The extracellular matrix as a biologic scaffold material. Biomaterials 28, 3587–3593, https://doi.org/10.1016/j.biomaterials.2007.04.043 (2007).
Cheng, N. C., Estes, B. T., Awad, H. A. & Guilak, F. Chondrogenic differentiation of adipose-derived adult stem cells by a porous scaffold derived from native articular cartilage extracellular matrix. Tissue Eng Part A 15, 231–241, https://doi.org/10.1089/ten.tea.2008.0253 (2009).
Abdelgaied, A. et al. Comparison of the biomechanical tensile and compressive properties of decellularised and natural porcine meniscus. J Biomech 48, 1389–1396, https://doi.org/10.1016/j.jbiomech.2015.02.044 (2015).
Maier, D. et al. In vitro analysis of an allogenic scaffold for tissue-engineered meniscus replacement. J Orthop Res 25, 1598–1608, https://doi.org/10.1002/jor.20405 (2007).
Stabile, K. J. et al. An acellular, allograft-derived meniscus scaffold in an ovine model. Arthroscopy 26, 936–948, https://doi.org/10.1016/j.arthro.2009.11.024 (2010).
Stapleton, T. W., Ingram, J., Fisher, J. & Ingham, E. Investigation of the regenerative capacity of an acellular porcine medial meniscus for tissue engineering applications. Tissue Eng Part A 17, 231–242, https://doi.org/10.1089/ten.TEA.2009.0807 (2011).
Stapleton, T. W. et al. Development and characterization of an acellular porcine medial meniscus for use in tissue engineering. Tissue Eng Pt A 14, 505–518, https://doi.org/10.1089/tea.2007.0233 (2008).
Yamasaki, T. et al. Transplantation of meniscus regenerated by tissue engineering with a scaffold derived from a rat meniscus and mesenchymal stromal cells derived from rat bone marrow. Artif Organs 32, 519–524, https://doi.org/10.1111/j.1525-1594.2008.00580.x (2008).
Qu, F., Guilak, F. & Mauck, R. L. Cell migration: implications for repair and regeneration in joint disease. Nat Rev Rheumatol 15, 167–179, https://doi.org/10.1038/s41584-018-0151-0 (2019).
Liang, Y. et al. Chondrogenic differentiation of synovial fluid mesenchymal stem cells on human meniscus-derived decellularized matrix requires exogenous growth factors. Acta Biomater 80, 131–143, https://doi.org/10.1016/j.actbio.2018.09.038 (2018).
Chen, Y. C. et al. Development and Characterization of Acellular Extracellular Matrix Scaffolds from Porcine Menisci for Use in Cartilage Tissue Engineering. Tissue Eng Part C Methods 21, 971–986, https://doi.org/10.1089/ten.TEC.2015.0036 (2015).
Lee, K. I., Olmer, M., Baek, J., D’Lima, D. D. & Lotz, M. K. Platelet-derived growth factor-coated decellularized meniscus scaffold for integrative healing of meniscus tears. Acta Biomater 76, 126–134, https://doi.org/10.1016/j.actbio.2018.06.021 (2018).
Monibi, F. A. et al. Development of a Micronized Meniscus Extracellular Matrix Scaffold for Potential Augmentation of Meniscal Repair and Regeneration. Tissue Eng Part C Methods 22, 1059–1070, https://doi.org/10.1089/ten.TEC.2016.0276 (2016).
Visser, J. et al. Crosslinkable hydrogels derived from cartilage, meniscus, and tendon tissue. Tissue Eng Part A 21, 1195–1206, https://doi.org/10.1089/ten.TEA.2014.0362 (2015).
Wu, J. et al. An injectable extracellular matrix derived hydrogel for meniscus repair and regeneration. Acta Biomater 16, 49–59, https://doi.org/10.1016/j.actbio.2015.01.027 (2015).
Rowland, C. R., Colucci, L. A. & Guilak, F. Fabrication of anatomically-shaped cartilage constructs using decellularized cartilage-derived matrix scaffolds. Biomaterials 91, 57–72, https://doi.org/10.1016/j.biomaterials.2016.03.012 (2016).
Lee, C. R., Grodzinsky, A. J. & Spector, M. The effects of cross-linking of collagen-glycosaminoglycan scaffolds on compressive stiffness, chondrocyte-mediated contraction, proliferation and biosynthesis. Biomaterials 22, 3145–3154 (2001).
Upton, M. L., Guilak, F., Laursen, T. A. & Setton, L. A. Finite element modeling predictions of region-specific cell-matrix mechanics in the meniscus. Biomech Model Mechanobiol 5, 140–149, https://doi.org/10.1007/s10237-006-0031-4 (2006).
Hennerbichler, A., Moutos, F. T., Hennerbichler, D., Weinberg, J. B. & Guilak, F. Interleukin-1 and tumor necrosis factor alpha inhibit repair of the porcine meniscus in vitro. Osteoarthritis Cartilage 15, 1053–1060, https://doi.org/10.1016/j.joca.2007.03.003 (2007).
McNulty, A. L., Estes, B. T., Wilusz, R. E., Weinberg, J. B. & Guilak, F. Dynamic loading enhances integrative meniscal repair in the presence of interleukin-1. Osteoarthritis Cartilage 18, 830–838, https://doi.org/10.1016/j.joca.2010.02.009 (2010).
McNulty, A. L. & Guilak, F. Integrative repair of the meniscus: lessons from in vitro studies. Biorheology 45, 487–500 (2008).
McNulty, A. L., Moutos, F. T., Weinberg, J. B. & Guilak, F. Enhanced integrative repair of the porcine meniscus in vitro by inhibition of interleukin-1 or tumor necrosis factor alpha. Arthritis Rheum 56, 3033–3042, https://doi.org/10.1002/art.22839 (2007).
McNulty, A. L., Weinberg, J. B. & Guilak, F. Inhibition of matrix metalloproteinases enhances in vitro repair of the meniscus. Clin Orthop Relat Res 467, 1557–1567, https://doi.org/10.1007/s11999-008-0596-6 (2009).
Wilusz, R. E., Weinberg, J. B., Guilak, F. & McNulty, A. L. Inhibition of integrative repair of the meniscus following acute exposure to interleukin-1 in vitro. J Orthop Res 26, 504–512, https://doi.org/10.1002/jor.20538 (2008).
Riera, K. M. et al. Interleukin-1, tumor necrosis factor-alpha, and transforming growth factor-beta 1 and integrative meniscal repair: influences on meniscal cell proliferation and migration. Arthritis research & therapy 13, R187, https://doi.org/10.1186/ar3515 (2011).
Qu, F. et al. Maturation State and Matrix Microstructure Regulate Interstitial Cell Migration in Dense Connective Tissues. Sci Rep 8, 3295, https://doi.org/10.1038/s41598-018-21212-4 (2018).
Crapo, P. M., Gilbert, T. W. & Badylak, S. F. An overview of tissue and whole organ decellularization processes. Biomaterials 32, 3233–3243, https://doi.org/10.1016/j.biomaterials.2011.01.057 (2011).
Londono, R. et al. The effect of cell debris within biologic scaffolds upon the macrophage response. J Biomed Mater Res A 105, 2109–2118, https://doi.org/10.1002/jbm.a.36055 (2017).
Monibi, F. A. & Cook, J. L. Tissue-Derived Extracellular Matrix Bioscaffolds: Emerging Applications in Cartilage and Meniscus Repair. Tissue Eng Part B Rev 23, 386–398, https://doi.org/10.1089/ten.TEB.2016.0431 (2017).
Mullen, L. M. et al. Binding and release characteristics of insulin-like growth factor-1 from a collagen-glycosaminoglycan scaffold. Tissue Eng Part C Methods 16, 1439–1448, https://doi.org/10.1089/ten.TEC.2009.0806 (2010).
Pieper, J. S., Oosterhof, A., Dijkstra, P. J., Veerkamp, J. H. & van Kuppevelt, T. H. Preparation and characterization of porous crosslinked collagenous matrices containing bioavailable chondroitin sulphate. Biomaterials 20, 847–858 (1999).
Puetzer, J. L. & Bonassar, L. J. Physiologically Distributed Loading Patterns Drive the Formation of Zonally Organized Collagen Structures in Tissue-Engineered Meniscus. Tissue Eng Part A 22, 907–916, https://doi.org/10.1089/ten.TEA.2015.0519 (2016).
Glass, K. A. et al. Tissue-engineered cartilage with inducible and tunable immunomodulatory properties. Biomaterials 35, 5921–5931, https://doi.org/10.1016/j.biomaterials.2014.03.073 (2014).
Rowland, C. R. et al. Regulation of decellularized tissue remodeling via scaffold-mediated lentiviral delivery in anatomically-shaped osteochondral constructs. Biomaterials 177, 161–175, https://doi.org/10.1016/j.biomaterials.2018.04.049 (2018).
Wiznerowicz, M. & Trono, D. Conditional suppression of cellular genes: lentivirus vector-mediated drug-inducible RNA interference. J Virol 77, 8957–8961 (2003).
Solchaga, L. A. et al. A rapid seeding technique for the assembly of large cell/scaffold composite constructs. Tissue Eng 12, 1851–1863, https://doi.org/10.1089/ten.2006.12.1851 (2006).
Collins, A. T. et al. Selective Enzymatic Digestion of Proteoglycans and Collagens Alters Cartilage T1rho and T2 Relaxation Times. Ann Biomed Eng, https://doi.org/10.1007/s10439-018-02143-7 (2018).
Hatcher, C. C. et al. Relationship between T1rho magnetic resonance imaging, synovial fluid biomarkers, and the biochemical and biomechanical properties of cartilage. J Biomech 55, 18–26, https://doi.org/10.1016/j.jbiomech.2017.02.001 (2017).
Farndale, R. W., Buttle, D. J. & Barrett, A. J. Improved quantitation and discrimination of sulphated glycosaminoglycans by use of dimethylmethylene blue. Biochim Biophys Acta 883, 173–177 (1986).
Reddy, G. K. & Enwemeka, C. S. A simplified method for the analysis of hydroxyproline in biological tissues. Clin Biochem 29, 225–229 (1996).
We thank Dawn Chasse for technical support. This work was supported in part by NIH grants AG028716, AR048852, AG015768, AR073752, AG046927, AR073221, AR074800, and AR065527, the Arthritis Foundation, a VA Rehabilitation Research Service Merit Review Award, the Lord Foundation in support of the Shared Materials Instrumentation Facility (SMIF) Undergraduate User Program, and an Orthopaedic Research and Education Foundation grant with funding provided by the Musculoskeletal Transplant Foundation.
F.G. is a founder and shareholder of Cytex Therapeutics, Inc. The other authors declare no competing interests.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Ruprecht, J.C., Waanders, T.D., Rowland, C.R. et al. Meniscus-Derived Matrix Scaffolds Promote the Integrative Repair of Meniscal Defects. Sci Rep 9, 8719 (2019). https://doi.org/10.1038/s41598-019-44855-3
Stem Cell Research & Therapy (2022)
Journal of Experimental Orthopaedics (2020)