Abstract
Damage of enteric neurons and partial or total loss of selective neuronal populations are reported in intestinal disorders including inflammatory bowel diseases and necrotizing enterocolitis. To develop three-dimensional scaffolds for enteric neurons we propose the decoration of ionic-complementary self-assembling peptide (SAP) hydrogels, namely EAK or EAbuK, with bioactive motives. Our results showed the ability of EAK in supporting neuronal cell attachment and neurite development. Therefore, EAK was covalently conjugated to: RGD, (GRGDSP)4K (fibronectin), FRHRNRKGY (h-vitronectin, named HVP), IKVAV (laminin), and type 1 Insulin-like Growth Factor (IGF-1). Chemoselective ligation was applied for the SAP conjugation with IGF-1 and the other longer sequences. Freshly isolated murine enteric neurons attached and grew on all functionalized EAK but IGF-1. Cell-cell contact was evident on hydrogels enriched with (GRGDSP)4K and HVP. Moreover (GRGDSP)4K significantly increased mRNA expression of neurotrophin-3 and nerve growth factor, two trophic factors supporting neuronal survival and differentiation, whereas IKVAV decoration specifically increased mRNA expression of acetylcholinesterase and choline acetyltransferase, genes involved in synaptic communication between cholinergic neurons. Thus, decorated hydrogels are proposed as injectable scaffolds to support in loco survival of enteric neurons, foster synaptic communication, or drive the differentiation of neuronal subtypes.
Similar content being viewed by others
Introduction
The extracellular matrix (ECM), the network of glycoproteins providing mechanical support and biochemical signals for tissue homeostasis, plays a key role in the economy of biological tissues. The ECM determines polarization and motility of cells and tunes the local concentration of adhesive proteins, growth factors, and glycosaminoglycans. Therefore, a big challenge in regenerative medicine is to design artificial ECM mimicking the in vivo 3-dimensional (3D) architecture of fibrous proteins, the nano- and micro-scale structural complexity, the tensional cues, and the interaction with the cytoskeletal network of the cells to eventually support a more dynamic environment for cell motility, wound healing and tissue reconstruction1. By now, traditional two-dimensional cell culture systems have been overcome by 3D scaffolds that more closely reproduce the in vivo architecture of the tissue2,3. In this scenario, nanofibrous structure and self-assembling materials gained considerable interest as scaffolds able to properly control cell-ECM interactions and in loco activity of bioactive factors. Scaffolds of self-assembling peptides (SAPs) were described at first by Zhang in 1992 who reported Zoutin protein fragments assuming highly stable β-sheet conformation in solution. However, SAPs are naturally occurring structures usually generated by simple molecules organized in nano- or micro-metric structures by means of weak interactions such as hydrogen or Van der Waals bonds4,5. In SAP scaffolds, hydrophilic (positively or negatively charged) and hydrophobic residues alternate resulting in amphiphilic β-sheet layers that in turn stack one with the other (Fig. 1).
The resulting scaffolds are hydrogels made of water (99% of the composition) and woven nanofibers with mean length ranging from hundreds of nanometers to few micrometers6. The network of SAP fibers supports the exchange of bioactive factors, oxygen, nutrients, and waste products among cells and the environment, but most of all SAP hydrogel provides a framework resistant to high temperature (90 °C for 4 hours) and digestion mediated by proteolytic enzymes4,5,6,7. Therefore, SAP scaffolds have been proposed as suitable cell supports in tissue engineering. Moreover, features of SAPs are easily scalable since the self-assembling process can be controlled by temperature, pH, concentration and nature of positive monovalent ions. Thanks to their compatibility and versatility, SAP hydrogels have been extensively proposed for application in regenerative medicine and the most promising application concerns the engineering of nervous tissue8,9,10,11,12. Indeed, electrospun cylinders filled with SAPs were successfully used to repair chronic injuries in the spinal cord13 and to restore the optic tract in hamsters14.
SAP hydrogels have the potential to be excellent supports in regenerative medicine of the nervous system due to the nanofibrous structure, the biomechanical properties and the ability to accelerate serum protein adsorption. However, the application of SAPs is strongly jeopardized by the lack of adhesive motives able to properly drive attachment, growth, and differentiation of specific neuronal cells on hydrogels. To fill this gap, in this study we proposed the enrichment of plain SAPs with self-assembling sequences joining bioactive factors. The simple and key idea of our study was to create ECM scaffolds by blending SAP-conjugated bioactive molecules with plain SAPs. Since de-absorption of biological factors is usually involved in inhibition of adhesion15, we decided to covalently bind the bioactive motives to the hydrogels. However, to keep the SAP side chains available for cell receptor interaction, two strategies were adopted in covalent binding: (i) extension in the protocol of solid phase peptide synthesis to condense short bioactive fragments (≤5 amino acids) to the self-assembling sequence; (ii) chemoselective ligation for the conjugation of SAPs with longer bioactive peptides. Indeed, chemoselective ligation ensures a bio-orthogonal reaction under mild conditions and without perturbing protein tertiary structure (Fig. 2, 3 + 4 → 5) whereas transamination using pirydoxal-5-phosphate (PLP) converts the first amino acid of the peptide/protein sequence in ketone or aldehyde (Fig. 2, 1 → 3) under non-denaturing conditions, thus introducing a functional group for chemoselective ligation16,17.
As compared with superficial addition, conjugation of bioactive motifs with SAPs provides, through self-assembling, the decoration of the whole hydrogel volume rather than only its surface and offers the possibility to build precise microenvironments for selected cellular systems.
Hydrogels enriched with conjugates (i.e. EAK-(GRGDSP)4, EAK-HVP, and EAK-IGF-1) have been successfully used in our previous studies as scaffolds to induce adhesion and growth of mesenchymal stem cells18. Moreover, we demonstrated the advantage in adding a spacer among the bioactive sequences and the aldehyde group to optimize the chemoselective ligation protocol19. In the present work, we proposed the decoration of 3D self-assembling matrices with new adhesive motives and previously reported conjugates18 in different combinations to provide scaffolds for the engineering of the enteric nervous system (ENS). The ENS is a complex network of glial cells and motor and sensory neurons embedded in the gastrointestinal wall that controls motility, secretion, digestion, and even pain perception and inflammatory process of the gut20. Enteric neuropathies are commonly associated with loss of enteric neurons and functional gut disorders ranging from inflammatory bowel diseases to chronic constipation and necrotizing enterocolitis21.
To support the in vitro growth of enteric neurons, in this study ionic self-assembling peptides of module II (EAK or EAbuK)2 were conjugated with (i) RGD motif; (ii) linear peptide of 4 GRGDSP motives previously reported to support adhesion in osteoblasts, cardiomyocytes and endothelial cells15,22,23; (iii) (351–359) fragment of the human vitronectin involved in proteoglycan-mediated osteoblast adhesion22,24,25; (iv) laminin sequence IKVAV26; (v) insulin-like growth factor-1 (IGF-1) promoting survival of cortical neurons27. Freshly isolated murine enteric neurons populated SAP hydrogels and modulated gene expression in response to specific scaffold enrichment. Up today, peptide nanofiber hydrogels have been used for regeneration of the central nervous system10. Our work demonstrated that hydrogels can be successfully applied also in recovery of injured enteric nerves. Moreover, since phenotype of enteric neurons is strictly connected to ECM composition28, data reported in the present study further confirmed that designing scaffolds for the engineering of the enteric nervous system is feasible and crucial in tissue regeneration during severe clinical conditions such as megacolon, short bowel syndrome, or inflammatory bowel disease21. Knowledge about the influence of the ECM composition in neuronal stem cell differentiation proved that enteric cell transplantation in aganglionic gut areas has therapeutic effects29,30,31. However, our data demonstrated that application of injectable hydrogel matrices decorated with different motives could support gut neuronal plasticity possibly fostering in loco migration and differentiation of definite intestinal neuronal subtypes but avoiding inoculation of foreign biological materials.
Results and Discussion
CD analysis of peptides in PBS solution
As reported in Fig. 3, the typical β-sheet spectra were observed for all EAK-based peptides in PBS solution, indicating the integrity of principal secondary structure was not perturbed by the addition of adhesion cues. In fact, the positive band remains around 194 nm (the spectrum of EAK is reported for comparison32), whereas the negative band is around 217 nm. Considering the EAK-HVP spectrum, the red shift of positive band and the reduction of its intensity with respect to EAK one, might result from the contribution of HVP conformation (type II β-turn) that is characterized by a negative band at 190 nm (Supplementary Information, Fig. S1). The spectrum of EAbuK, published in Gambaretto R. et al. confirmed a predominant β-sheet structure32.
Structure of EAK, EAbuK and EAK enriched with bioactive sequences
Figure 4 reports the atomic force microscopy images of a) EAK, b) EAbuK, c) EAK-RGD (EAK: EAK-RGD, 1:1) and d) EAK-RGD + IKVAV (EAK: EAK-RGD + IKVAV, 1:1) peptides (0.15% w/v) on freshly cleaved mica surfaces, after 1 hour of incubation in buffer solution. It can be seen that EAK sequences yield a remarkable self-organization process already after an hour of incubation, i.e. at very short time with respect to the employed cell incubation time, producing a relatively dense network of mostly parallel aligned nanofibrils.
The characteristic dimensions of the self-assembled fibrils have been determined by applying the Canet-Ferrer method that takes into account the tip-fibrils convolution effects arising from the finite dimensions of the AFM tip33. This model yields the effective corrected Weff width based on the measured fibrils width. In the present case, the average fibril width for EAK peptide, is 5.3 ± 0.5 nm and height is 1.2 ± 0.4 nm, while the average length is variable in a range of 140.0–630.0 nm. These data are in agreement with the previous results, i.e., Weff = 5.9 ± 1.1 nm for the corrected width (assuming a flat configuration of the sequences) and h = 1.1 ± 0.1 nm for the height value34. Therefore, in this case, with respect to previous results obtained at very low concentration (∼10−6 M) and with LiCl in the buffer, a much higher density and related higher bifurcation events of the assembled fibrils are found, due to the striking difference in EAK concentration and the nature of the buffer solution employed (containing no Li salt).
Contrarily, EAbuK sequences, differing only for the presence of an ethyl group as side chain of Abu instead of a methyl group as side chain of Ala, don’t form a significant amount of fibrils, giving mostly very short fibers peptide aggregates, with a typical height of 1.7 ± 0.2 nm and the effective width of 7.6 ± 1.1 nm. In particular, Fig. 4b shows small nanometric holes suggesting the presence of a peptide monolayer formed on mica substrate. The peptide carpet formation is likely due to the strong electrostatic interactions between peptide and surface. The peptide monolayer thickness measured by AFM section analysis is 1.2 ± 0.01 nm and it suggests a side-on molecules arrangement.
The enrichment of EAK sequence with EAK-RGD (Fig. 4c) produces the formation of a two-level system, an underlayer consisting of a compact network with fibrils 1.5 ± 1.1 nm thick and high cross-linking density, and an overlayer of sparse and short fibers aggregates (average hight = 2.1 ± 1.4 nm). The fibrils and the fibrous aggregates of the two layers have roughly the same width, about 12.1 ± 1.1 nm.
The presence of IKVAV decoration on the EAK-RGD + IKVAV hydrogel (Fig. 4d) causes the formation of a first layer with a less dense network, with narrower fibrils (width = 9.8 ± 0.7) and larger meshes and an increase of the fibrillar aggregation of the second layer characterized by a bigger width (17.9 ± 1.4 nm).
The AFM analysis highlights the formation of the fibrils only in the presence of EAK that should be attributed to the ß-sheet secondary peptide folding where the hydrophobic alanine units are thought to promote the coupling of the hydrophobic sides of the two adjacent molecules, coupled with the electrostatically-driven peptide-peptide interaction involving the oppositely charged lysine and glutamic acid residues on the two adjacent sequences, yielding the ordered growth of the fibrils in a checkerboard-like manner.
On the other hand, the unstructured nature of the EAbuK aggregates could not be explained at this stage of the study, because EAbuK has the same length of EAK peptide. This may suggest that the presence of the side chain of amino butyric acid, hinders efficiently the self-organization process.
The fibrillary self-organization process of EAK has been shown previously to boost the cell adhesion and proliferation, in agreement with the present results, while EAbuK unstructured aggregates appear to be significantly less effective in promoting cell adhesion processes. Accordingly, we attribute to the ordered arrangement of the peptides the capability of efficiently interacting with the cell adhesion “mechanism”.
Biological characterization
In order to evaluate the biological properties of SAPs, EAK and EAbuK were deposited on sterile glass coverslips (0.15% w/v on 1 cm2) and incubated for 1 hour. Freshly isolated murine enteric neurons were seeded on glass coverslips coated with SAPs and cultured for 6 days. As reported in Fig. 5a, cells were seeded on EAK and stained with anti-peripherin antibody, a marker of neuronal cells, developed a frank neuronal phenotype characterized by organization in ganglia and several neurites extending from the soma to neighbouring neurons35. On the contrary, EAbuK did not support adhesion of neurons neither extension of neurites. Indeed, cells cultured on EAbuK were barely positive for neuronal peripherin marker and showed rounded shape with small or absent projections (Fig. 5b).
Indeed, quantitative analysis of confocal images reported lower number of peripherin positive cells and shorter axonal networks in EAbuK with respect to cells cultured in EAK (p < 0.001; Fig. 5b,c). Overall, EAbuK did not report a strong ability in adhesion of neurons (Fig. 5a) but all attached cells were peripherin positive (Fig. 5d). By matching the biological results with AFM structural characterization of SAPs (Fig. 4) we infer that the self-assembling process of EAK resulting in a dense organized network of parallel fibrils supports adhesion and proliferation of neuronal cells. On the contrary, unstructured aggregates described in EAbuK (Fig. 4a) significantly impairs cell adhesion and phenotype development. Indeed, during morphogenesis organization of extracellular fibrils in precise geometric structures is mandatory for cell dynamic interaction36. At the same, organization of tenascin in parallel fibrils is required for integrin-mediated neuronal migration and development of the cerebellum37.
Taking into consideration the above described results, subsequent biological analysis were performed on EAK hydrogels enriched with bioactive motives (namely RGD, (GRGDSP)4, HVP, IGF-1, or RGD + IKVAV) deemed to foster neuronal adhesion and differentiation22,23,24,25,26,27. As reported in Fig. 6, enrichment of EAK differentially supported neuronal attachment and growth as well as the outgrowth of neuronal projections.
When compared with non enriched EAK, functional motives did not improve adhesion and axonal outgrowth of neuronal cells (Fig. 6b,c). Indeed, the number of peripherin positive cells was comparable in EAK-RGD, EAK-(GRGDSP)4, and EAK-HVP and even decreased when cells were cultured on EAK-RGD + IKVAV and EAK-IGF-1 where peripherin negative cells were costantly observed in 5 different experiments. As compared to non functionalized EAK, EAK-HVP and EAK-RGD + IKVAV increased the selectivity for attachment and growth of peripherin positive neuronal cells (Fig. 6d, p < 0.05). Indeed, 95.0 ± 4,9% of cells cultured on EAK-HVP and 97.4 ± 2.5% of cells grown on EAK-RGD + IKVAV positively stained for peripherin as compared to 76.4 ± 6.2% of cells on EAK. Only 59.4 ± 4.8% of cells cultured on EAK-(GRGDSP)4 stained with anti-peripherin antibody (Fig. 5a,d). Nevertheless, HVP functionalization preserved the ability observed in non functionalized EAK in inducing neurite outgrowth (Fig. 6c).
We previously detailed the hydrogel morphology at the nanoscale18. AFM analysis demonstrated that addition of active motives to SAP backbone did not affect nanofiber structures that preserved features similar to those described in pure SAP. On the contrary, the main effect of conjugates addition was the inhibition of long fiber formation, observed in plain SAP. In addition, rheological analysis (small amplitude oscillatory shear tests) was carried out on EAK and IGF-1-conjugate-enriched EAK hydrogels and reported that IGF-1 conjugates did not alter the viscoelastic properties of the hydrogels18. Thus, the lack of bioactivity in EAK-IGF-1 conjugates described in the present study cannot be explained by the alteration in the biomechanical properties of the hydrogel but rather by the binding with the SAP and the consequent poor accessibility of the IGF-1 N-terminus to the cellular receptors. Indeed, several published data underlying the importance of IGF-1 N-terminal residues for the biological activity, partially explain our results. Indeed, peptides lacking five or six residues at the N-terminal part of IGF-1 weakly interact with cell receptors and fail in reporting biological effects38,39.
While enrichment of EAK with functional motives did not improve neuronal attachment and differentiation, RGD, (GRGDSP)4, HVP, and RGD + IKVAV reported different ability in modulating mRNA transcript levels (Fig. 7). Indeed, all the tested bioactive factors increased expression of mRNA specific for nerve growth factor (Ngf), a soluble factor involved in survival and differentiation of motor and sensory neurons40. Even if RGD + IKVAV decoration did not sustain the overall growth and differentiation of peripherin positive cells (Fig. 6), it increased neurotrophin 3 (Ntf3) mRNA transcript levels at the same extent of (GRGDSP)4 (Fig. 7). Moreover, among the different functional motives tested in this study, RGD + IKVAV decoration was the only one able to increase mRNA transcript levels specific for acetylcholinesterase (Ache) and choline acetyltransferase (Chat), genes involved in synaptic communications between cholinergic motor neurons (Fig. 7).
In conclusion, in this study we showed that SAP conjugated with different bioactive molecules are promising options for enteric nerve regeneration. Indeed, self-assembling hydrogels offer the opportunity to be injected or dabbed onto intestinal areas affected by loss of neurons, a histological hallmark usually associated with gastrointestinal dysfunctions41. Moreover, as we demonstrated in this study, specific decoration of SAP promotes different gene expression in neuronal cells thus sustaining specific functional recovery. The use of self-aggregating peptides provides an easy strategy to design and realize 3D matrices decorated with controlled concentrations of adhesion and growth factors. These molecular architectures have demonstrated great potential in the promotion of enteric nerve regeneration. In our study, different decorations of SAPs, except for IGF-1 conjugate, induced unique gene expression and neuronal cell phenotype. These preliminary results pave the way to targeted research supporting survival of neurons, fostering synaptic communication and driving neuronal subtypes differentiations. The selection and stimulation of certain type of neurons using injectable SAP scaffolds are of promising benefit for the treatment of gastrointestinal disorders caused by the lack of specific neuronal subpopulations.
Materials and Methods
Materials
The solid support, Rink Amide MBHA resin, was purchased from Novabiochem (Merck KGaA, Darmstadt, Germany). The Fmoc protected amino acids were provided by Novabiochem. The coupling reagents 2-(1H-Benzotriazole-1-yl)-1,1,3,3-tetramethyluronium hexafluorophosphate (HBTU), 1-[Bis(dimethylamino)methylene]-1H-1,2,3-triazolo[4,5-b]pyridinium 3-oxid hexafluorophosphate (HATU), 1-Hydroxybenzotriazole (HOBt) and 3H-[1,2,3]-Triazolo[4,5-b]pyridin-3-ol (HOAt) were supplied by Advanced Biotech (Seveso, MI, Italy). N,N-diisopropylethylamine (DIEA) and piperidine were purchased from Biosolve (Leenderweg, Valkenswaard, The Netherlands). 2,4,6-Collidine was from Janssen Chimica NV (Beerse, Belgium). Triethoxysilane (TES) and pyridoxal-5-phosphate (PLP) were from Sigma-Aldrich (Steinheim, Germany). Solvents such as N,N-dimethylformamide (DMF), trifluoroacetic acid (TFA), N-methyl-2-pyrrolidone (NMP) and dichloromethane (DCM) were from Biosolve. Increlex (10 mg/mL IGF-1 solution) was from Ipsen Pharma (Boulogne-Billancourt, France).
Peptide Synthesis
EAK
The detailed solid phase peptide synthesis, purification and characterization of EAK (H-Ala-Glu-Ala-Glu-Ala-Lys-Ala-Lys-Ala-Glu-Ala-Glu-Ala-Lys-Ala-Lys-NH2) are reported in Zamuner et al.18. Final purity grade 99.2%. The analytical HPLC chromatogram of purified peptide is reported in Supplementary Information (Fig. S2).
Aoa-EAK
The Aoa-EAK peptide, sequence: NH2-O-CH2-CO-Ala-Glu-Ala-Glu-Ala-Lys-Ala-Lys-Ala-Glu-Ala-Glu-Ala-Lys-Ala-Lys-NH2, was synthesized as reported elsewhere18.
G7(GRGDSP)4K
The peptide G7(GRGDSP)4K (sequence: H-Gly-7-aminoheptanoic acid-(Gly-Arg-Gly-Asp-Ser-Pro)4-Lys-NH2) was synthesized, purified and characterized as reported in Zamuner et al.18.
α-Ketoaldehyde-7-Aminoheptanoicacid-(GRGDSP)4K
The conversion of G7(GRGDSP)4K in α-ketoaldehyde-7-aminoheptanoic acid-(GRGDSP)4K (sequence: H-CO-CO-NH-(CH2)6-CO-(Gly-Arg-Gly-Asp-Ser-Pro)4Lys-NH2) was obtained by addition of 23.63 mg of G7(GRGDSP)4K (9.061 × 10−6 moles) to 18.12 mL of 10 mM pyridoxal-5-phosphate (PLP) in 25 mM sodium phosphate buffer pH 6.5 (181.23 × 10−6 moles PLP; G7(GRGDSP)4K:PLP = 1:20) for 18 h at 37 °C. The α-ketoaldehyde-peptide was isolated and characterized as reported in Zamuner et al.18.
EAK-(GRGDSP)4
The chemoselective ligation between α-ketoaldehyde-7-aminoheptanoic acid-(GRGDSP)4K and Aoa-EAK produced the conjugate named EAK-(GRGDSP)4. Briefly, 25.894 × 10−6 moles of Aoa-EAK was added to 2.589 × 10−6 moles of α-ketoaldehyde-7-aminoheptanoic acid-(GRGDSP)4K (ratio: 10:1) in 25.89 mL of H2O MilliQ for 24 hrs at room temperature. The product was isolated using RP-HPLC. The identity of the product was confirmed by MALDI mass analysis18. The analytical HPLC chromatogram and 1H NMR spectrum of purified conjugate EAK-(GRGDSP)4 are reported in Supplementary Information (Figs S3 and S9).
G7HVP
The peptide G7HVP (sequence: H-Gly-7-aminoheptanoic acid-Phe-Arg-His-Arg-Asn-Arg-Lys-Gly-Lys-NH2) was synthesized by standard Fmoc chemistry and a fully automated peptide synthesizer. The detailed synthesis, purification and characterization are reported elsewhere18.
α-Ketoaldehyde-7-Aminoheptanoic Acid-HVP
The conversion of G7HVP in α-ketoaldehyde-7-aminoheptanoic acid-HVP (sequence: H-CO-CO-NH-(CH2)6-CO-(Phe-Arg-His-Arg-Asn-Arg-Lys-Gly-Tyr-NH2) was obtained as above reported (4.2.4)18.
EAK-HVP
The chemoselective ligation between α-ketoaldehyde-7-aminoheptanoic acid-HVP and Aoa-EAK produced the conjugate named EAK-HVP. Details are reported elsewhere (paragraph 3.2.5 and in Zamuner et al.18). The analytical HPLC of purified EAK-HVP is reported in Supplementary Information (Fig. S4).
α-Ketoaldehyde-IGF-1
The conversion of IGF-1 in α-ketoaldehyde-IGF-1 was obtained by addition of 10 mg of IGF-1 (1.307 × 10−6 moles) to 26.3 mL of 100 mM pyridoxal-5-phosphate (PLP) in 25 mM sodium phosphate buffer pH 6.5 (2.615 × 10−3 moles PLP; IGF-1:PLP = 1:2000) for 3 hrs at 37 °C and 1 hr at room temperature. The characterization of the product is reported elsewhere18.
EAK-IGF-1
The chemoselective ligation between α-ketoaldehyde-IGF-1 and Aoa-EAK produced the conjugate reported as EAK-IGF-118. The analytical HPLC chromatogram of purified conjugate is reported in Supplementary Information (Fig. S5). Purified EAK-IGF-1 was used for AFM and biological characterization but CD evaluation was not possible due to the exiguity of the material.
EAK-RGD
The peptide EAK-RGD (sequence: H-Arg-Gly-Asp-Ala-Glu-Ala-Glu-Ala-Lys-Ala-Lys-Ala-Glu-Ala-Glu-Ala-Lys-Ala-Lys-NH2) was synthesized through solid phare peptide synthesis using Rink Amide MBHA resin (0.7 mmol/g; scale 0.125 mmoles) and a fully automated peptide synthesizer (Syro I, Multisynthec, Witten, Germany). The side chain protection employed were: Arg, Pbf; Asp and Glu, OBut; and Lys, Boc. All the couplings were double. After the Fmoc deprotection the resin was washed with DCM and vacuum dried for 1 hr. The peptide was cleaved from the solid support with contemporary side-chain deprotection using the following mixture: 0.125 mL H2O MilliQ, 0.125 mL TES, and 4.750 mL TFA (90 min, under magnetic stirring). After cleavage, the resin was filtered, the reaction mixture was concentrated, and the crude peptide precipitated with cold ethyl ether. The identity of crude peptide was ascertained by mass (exp. mass = 1943.06 Da; theor. mass = 1943.16 Da, ESI-TOF). The chromatogram of purified peptide was carried out in the following conditions: column, Symmetry Shield C8 (5 µm, 100 Å, 4.6 × 250 mm, Waters); injection volume, 30 µL of 1 mg/mL peptide solution; flow rate, 1 mL/min; eluent A, 0.05% TFA in water; eluent B, 0.05% TFA in CH3CN; gradient, from 10%B to 25%B in 30 min, detection at 214 nm. Purity grade 99.9%. The retention time was 15.8 min (Supplementary Information, Fig. S6). The 1H NMR spectrum is reported in Fig. S10 of Supplementary Information.
EAK-RGD + IKVAV
The peptide EAK-RGD + IKVAV (sequence: H-Arg-Gly-Asp-Ala-Glu-Ala-Glu-Ala-Lys-Ala-Lys-Ala-Glu-Ala-Glu-Ala-Lys-Ala-Lys-Ile-Lys-Val-Ala-Val-NH2) was synthesized by standard Fmoc chemistry using Rink Amide MBHA resin (0.7 mmol/g; scale 0.125 mmoles) and a fully automated peptide synthesizer (Syro I, Multisynthec, Witten, Germany). The side chain protection employed were: Arg, Pmc; Asp and Glu, OBut; and Lys, Boc. All the couplings were double. After the Fmoc deprotection the resin was washed with DCM and vacuum dried for 1 hr. The peptide was cleaved from the solid support with contemporary side-chain deprotection using the following mixture: 0.125 mL H2O MilliQ, 0.125 mL TES, and 4.750 mL TFA (90 min, under magnetic stirring). After cleavage, the resin was filtered, the reaction mixture was concentrated, and the crude peptide precipitated with cold ethyl ether. After RP-HPLC purification, the identity of crude peptide was ascertained by mass (exp. mass = 2453.40 Da; theor. mass = 2453.81 Da, ESI-TOF). The chromatogram of purified peptide was carried out in the following conditions: column, Symmetry Shield C8 (5 µm, 100 Å, 4.6 × 250 mm, Waters); injection volume, 30 µL of 1 mg/mL peptide solution; flow rate, 1 mL/min; eluent A, 0.05% TFA in water; eluent B, 0.05% TFA in CH3CN; gradient, from 15%B to 25%B in 20 min, detection at 214 nm. Purity grade 96%. The retention time was 12.5 min (Supplementary Information, Fig. S7). 1H NMR analysis of purified EAK-RGD + IKVAV is reported in Supplementary Information, Fig. S11.
EAbuK
The peptide EAbuK (sequence: H-Abu-Glu-Abu-Glu-Abu-Lys-Abu-Lys-Abu-Glu-Abu-Glu-Abu-Lys-Abu-Lys-NH2; Abu stands for α-aminobutyric acid) was synthesized by standard Fmoc chemistry using Rink Amide MBHA resin (0.72 mmol/g; scale 0.125 mmoles) and a fully automated peptide synthesizer (Syro I, Multisynthec, Witten, Germany). The side chain protection employed were: Glu, OBut and Lys, Boc. The loading of the resin with the first amino acid was carried out with a double coupling, the following four couplings were performed once and all the remaining were double. After the Fmoc deprotection the resin was washed with DCM and vacuum dried for 1 hr. The peptide was cleaved from the solid support with contemporary side-chain deprotection using the following mixture: 0.125 mL H2O MilliQ, 0.125 mL TES, and 4.750 mL TFA (90 min, under magnetic stirring). After cleavage, the resin was filtered, the reaction mixture concentrated, and the crude peptide precipitated with cold ethyl ether. The identity of crude peptide was ascertained by mass (exp. mass = 1726.99 Da; theor. mass = 1727.05 Da, ESI-TOF). The chromatogram of purified peptide was carried out in the following conditions: column, Symmetry Shield C8 (5 µm, 100 Å, 4.6 × 250 mm, Waters); injection volume, 100 µL of 1 mg/mL peptide solution; flow rate, 1 mL/min; eluent A, 0.05% TFA in water; eluent B, 0.05% TFA in CH3CN; gradient, from 12%B to 22%B in 20 min, detection at 214 nm. Purity grade 95%. The retention time was 15.0 min (Supplementary Information, Fig. S8). The 1H NMR spectrum is reported in Fig. S12 of Supplementary Information.
Circular Dicroism analysis
CD spectra were performed at room temperature (25 °C) using a Jasco model J-1500 automatic recording circular dichrograph equipped with Spectra ManagerTM software. Cylindrical fused quartz cells of 0.5 mm path length were used. The CD instrument was standardized with D-10 camphorsulphonic acid ammonium salt. Samples were prepared by dissolving weighed quantities of each peptide in a minimum amount of MilliQ water then by adding 10 mM phosphate buffer pH 7 up to a final content of 98% (v/v). Peptide concentration used for CD analysis was 5 × 10−5 M.
Nuclear magnetic resonance spectroscopy (NMR)
NMR characterizations of EAbuK, EAK-RGD, EAK-RGD + IKVAV, and EAK-(GRGDSP)4 were performed by using samples about 1 mM in H2O/D2O (90:10, v-v) at pH values in the range 4–5. NMR experiments were recorded at 298 K on a Varian INOVA 600 MHz spectrometer equipped with a cold probe and Z-gradients. 1H mono-dimensional spectra are referred to internal sodium 3-(trimethylsilyl) propionate 2,2,3,3-d4 (TSP). The water resonance was suppressed by using gradients.
Atomic force Microscopy (AFM)
Sample preparation
A solution 0.15% (w/v) of self-assembling peptide in buffer solution was prepared and 3μl was deposited on a freshly cleaned mica surface. After one hour of incubation the samples were gently washed with buffer solution and dried in air.
Samples of EAK-RGD and EAK-RGD + IKVAV correspond to EAK hydrogel enriched with EAK-RGD or EAK-RGD + IKVAV in a ratio EAK: EAK-bioactive molecule of 1: 1, keeping a final hydrogel concentration of 0.15% w/v. For an easier representation scaffolds of EAK/EAK-RGD and EAK/EAK-RGD + IKVAV were named simply EAK-RGD and EAK-RGD + IKVAV.
AFM measurements
AFM measurements were carried out with the “J scanner” in tapping mode by using a Nanoscope IIIA-MultiMode AFM (Digital Instruments, Santa Barbara, CA, USA) under room conditions. The force was maintained at the lowest value as possible by continuous adjusting the set point during imaging. Images were recorded using 0.5–2 Ω·cm phosphorous (n) doped silicon tips mounted on cantilevers with a nominal force constant of 40 N/m, a resonance frequency of 300 kHz and a tip curvature radius of 10 nm.
Biological assays
Scaffold preparation
Concentrated SAP solutions (1% w/v) were prepared in deionized water. The final concentration of SAP (0.15% w/v) was obtained adding PBS. The biological evaluation was carried out on EAK hydrogel enriched with EAK-RGD or EAK-RGD + IKVAV in a ratio EAK: EAK-bioactive molecule of 1: 1. For an easier representation scaffolds of EAK/EAK-RGD and EAK/EAK-RGD + IKVAV were named simply EAK-RGD and EAK-RGD + IKVAV. Samples of EAK enriched with conjugates obtained through chemoselective ligation (Fig. 2): EAK-(GRGDSP)4, EAK-HVP and EAK-IGF-1, were prepared at the following concentrations: 3.9 × 10−5 M of EAK-(GRGDSP)4, 5.4 × 10−5 M of EAK-HVP and 1.7 × 10−5 M of EAK-IGF-1. In a parallel way, EAK/EAK-(GRGDSP)4, EAK/EAK-HVP and EAK/EAK-IGF-1 were conveniently named EAK-(GRGDSP)4, EAK-HVP and EAK-IGF-1 respectively. All EAK scaffolds enriched with EAK bonded to bioactive sequences were prepared keeping a final hydrogel concentration of 0.15% w/v.
Culture of myenteric neurons
Intestinal neurons were isolated from the gut of adult mice42. The small intestine was aseptically removed, washed in Hanks balanced salt solution (HBSS; Gibco, Monza, Italy) and cut into pieces of 1 cm length. Intestinal segments were streatched on a sterile glass rod and layers of longitudinal muscle containing the myenteric plexus (LMMP) were obtained. LMMP strips were rinsed twice in HBSS, minced with scissors and dissociated by incubation for 10 min at 37 °C with collagenase type II (1.4 mg/mL, WorthingtonBiochemical Corp, Lakewood, NJ) and DNase (6.25 μg/mL, Calbiochem, Milan, Italy). Following enzymatic inactivation, tissues were further triturated using a pipette and collected by centrifugation (350 x g for 8 min). Cells were then plated on coverslips coated with different SAP scaffolds and incubated in Euromed-N medium (Euroclone, Milan, Italy) supplemented with heat inactivated fetal bovine serum (1% vol/vol), penicillin (100 U mL−1), streptomycin (50 μg mL−1), and nerve growth factor (10 ng mL−1), all purchased from Gibco. Medium was changed 18 hrs after isolation and then replaced every 2 days. Cells were used at the 6th day in culture.
Immunocytochemistry
Cultured neurons were washed and fixed in PFA (4% w/vol) for 20 min at room temperature. Cells were then permeabilized with 0.5% Triton X-100 in PBS for 15 min and incubated at room temperature for 1 h with rabbit polyclonal anti-peripherin antibody (Millipore, Milan, Italy). Following extensive washes in PBS, cells were incubated for 1 h at room temperature with TRITC labeled secondary antibodies (Molecular Probe, Milan, Italy). Nuclei were stained with TOTO-3 iodide (Molecular Probe). Samples were then analysed using Leica TCSNT/SP2 confocal microscope. All microscope parameters were set to collect images below saturation and were kept constant during acquisition.
Number of peripherin positive cells was recorded within a minimum of 3 randomly selected fields covering 1.254 mm2 from five independent experiments. The percentage of peripherin positive cells was calculated on the number of total nuclei stained with TOTO-3 iodide. Axonal length was measured in stained neuronal cells by using ImageJ 1.40 g (National Institutes of Health; Bethesda, MD, USA). For each experimental condition, 10 cells in 8 images obtained from at least three separate staining sessions were considered. Quantitative analysis was performed manually by using a counting grid, as previously reported43.
RNA isolation and quantitative PCR
Total RNA was isolated from neurons cultured on different hydrogels using SV Total RNA Isolation System kit (Promega, Milan, Italy) as previously described44. Contaminating DNA was removed by DNase I treatment (Promega). cDNA synthesis and subsequent amplification was performed in a one-step using the iTaq Universal SYBR Green One-Step Kit (Bio-Rad). The reaction mixture contained 200 nM forward primer, 200 nM reverse primer, iTaq universal SyBR Green reaction mix, iScript reverse transcriptase, and 200 ng total RNA. Real time PCR was performed using ABI PRISM 7700 Sequence Detection System (Applied Biosystems,Monza, Italy). Expression of Glyceraldehyde 3-phosphate dehydrogenase (Gapdh) was used as internal control. Experiments were performed in duplicate from three independent samples. The mean normalized fold expression ± SEM are plotted. Oligonucleotides used are listed in Table 1.
Statistical analysis
Biological data are presented as the mean ± standard error of the mean (SEM). Differences in the mean beween experimental groups were tested using Student’s t-test or one-way ANOVA analysis followed by Bonferroni multicomparison post hoc test. A p value of 0.05 or less was considered statistical significant. Statistical analyses were performed using GraphPad Prism 3.03 software (GraphPad, San Diego, CA).
Experimental Protocols
Animal experiments were approved by the Animal Care and Use Committee of the University of Padova under license from the Italian Ministry of Health (244/2015-PR). All animal procedures were carried out in accordance with the National and European guidelines for handling and use of experimental animals.
References
Frantz, C., Stewart, K. M. & Weaver, V. M. The extracellular matrix at a glance. J. Cell Sci. 123, 4195–200 (2010).
Edmondson, R., Broglie, J. J., Adcock, A. F. & Yang, L. Three-dimensional cell culture systems and their applications in drug discovery and cell-based biosensors. Assay Drug Dev. Technol. 12, 207–18 (2014).
Lin, X., Shi, Y., Cao, Y. & Liu, W. Recent progress in stem cell differentiation directed by material and mechanical cues. Biomed. Mater. 11, 014109 (2016).
Zhang, S., Holmes, T., Lockshin, C. & Rich, A. Spontaneous assembly of a self-complementary oligopeptide to form a stable macroscopic membrane. Proc. Natl. Acad. Sci. 90, 3334–3338 (1993).
Zhang, S. Emerging biological materials through molecular self-assembly. Biotechnol. Adv. 20, 321–39 (2002).
Zhang, S. In Amino Acids, Peptides and Proteins. 40–65 doi:10.1039/9781849734677-00040 (RSC Publishing, 2012).
Tibbitt, M. W. & Anseth, K. S. Hydrogels as extracellular matrix mimics for 3D cell culture. Biotechnol. Bioeng. 103, 655–63 (2009).
Caplan, M. R., Schwartzfarb, E. M., Zhang, S., Kamm, R. D. & Lauffenburger, D. A. Control of self-assembling oligopeptide matrix formation through systematic variation of amino acid sequence. Biomaterials 23, 219–227 (2002).
Zhang, S., Gelain, F. & Zhao, X. Designer self-assembling peptide nanofiber scaffolds for 3D tissue cell cultures. Semin. Cancer Biol. 15, 413–420 (2005).
Gelain, F., Bottai, D., Vescovi, A. & Zhang, S. Designer Self-Assembling Peptide Nanofiber Scaffolds for Adult Mouse Neural Stem Cell 3-Dimensional Cultures. PLoS One 1, e119 (2006).
Wang, X., Horii, A. & Zhang, S. Designer functionalized self-assembling peptide nanofiber scaffolds for growth, migration, and tubulogenesis of human umbilical vein endothelial cells. Soft Matter 4, 2388 (2008).
Chau, Y. et al. Incorporation of a matrix metalloproteinase-sensitive substrate into self-assembling peptides – A model for biofunctional scaffolds. Biomaterials 29, 1713–1719 (2008).
Gelain, F. et al. Transplantation of Nanostructured Composite Scaffolds Results in the Regeneration of Chronically Injured Spinal Cords. ACS Nano 5, 227–236 (2011).
Ellis-Behnke, R. G. et al. Nano neuro knitting: Peptide nanofiber scaffold for brain repair and axon regeneration with functional return of vision. Proc. Natl. Acad. Sci. 103, 5054–5059 (2006).
Conconi, M. T. et al. Effects on in vitro and in vivo angiogenesis induced by small peptides carrying adhesion sequences. J. Pept. Sci. 16, 349–57 (2010).
Gilmore, J. M., Scheck, R. A., Esser-Kahn, A. P., Joshi, N. S. & Francis, M. B. N-terminal protein modification through a biomimetic transamination reaction. Angew. Chem. Int. Ed. Engl. 45, 5307–11 (2006).
Scheck, R. A., Dedeo, M. T., Iavarone, A. T. & Francis, M. B. Optimization of a Biomimetic Transamination Reaction. J. Am. Chem. Soc. 130, 11762–11770 (2008).
Zamuner, A. et al. Design of decorated self-assembling peptide hydrogels as architecture for mesenchymal stem cells. Materials (Basel). 9 (2016).
Zamuner, A., Sica, G. & Dettin, M. Insertion of a flexible spacer increases the yield of site-specific bioconjugation through n-terminal transamination. Lett. Org. Chem. 14 (2017).
Kulkarni, S. et al. Advances in Enteric Neurobiology: The “Brain” in the Gut in Health and Disease. J. Neurosci. 38, 9346–9354 (2018).
lomax, A. E., Fernandez, E. & Sharkey, K. A. Plasticity of the enteric nervous system during intestinal inflammation. Neurogastroenterol. Motil. 17, 4–15 (2005).
Dettin, M. et al. Effect of synthetic peptides on osteoblast adhesion. Biomaterials 26, 4507–4515 (2005).
Gandaglia, A. et al. Cardiomyocytes In Vitro Adhesion Is Actively Influenced by Biomimetic Synthetic Peptides for Cardiac Tissue Engineering. Tissue Eng. Part A 18, 725–736 (2012).
Bagno, A. et al. Human osteoblast-like cell adhesion on titanium substrates covalently functionalized with synthetic peptides. Bone 40, 693–699 (2007).
Brun, P. et al. Mechanisms underlying the attachment and spreading of human osteoblasts: from transient interactions to focal adhesions on vitronectin-grafted bioactive surfaces. Acta Biomater. 9, 6105–15 (2013).
Tashiro, K. et al. A synthetic peptide containing the IKVAV sequence from the A chain of laminin mediates cell attachment, migration, and neurite outgrowth. J. Biol. Chem. 264, 16174–82 (1989).
Wilkins, A., Chandran, S. & Compston, A. A role for oligodendrocyte-derived IGF-1 in trophic support of cortical neurons. Glia 36, 48–57 (2001).
Bitar, K. N. & Zakhem, E. Bioengineering the gut: future prospects of regenerative medicine. Nat. Rev. Gastroenterol. Hepatol. 13, 543–556 (2016).
Zakhem, E., Raghavan, S. & Bitar, K. N. Neo-innervation of a bioengineered intestinal smooth muscle construct around chitosan scaffold. Biomaterials 35, 1882–1889 (2014).
Cheng, T.-Y., Chen, M.-H., Chang, W.-H., Huang, M.-Y. & Wang, T.-W. Neural stem cells encapsulated in a functionalized self-assembling peptide hydrogel for brain tissue engineering. Biomaterials 34, 2005–2016 (2013).
Geisbauer, C. L., Wu, B. M. & Dunn, J. C. Y. Transplantation of Enteric Cells into the Aganglionic Rodent Small Intestines. J. Surg. Res. 176, 20–28 (2012).
Gambaretto, R., Tonin, L., Di Bello, C. & Dettin, M. Self-assembling peptides: sequence, secondary structure in solution and film formation. Biopolymers 89, 906–15 (2008).
Canet-Ferrer, J., Coronado, E., Forment-Aliaga, A. & Pinilla-Cienfuegos, E. Correction of the tip convolution effects in the imaging of nanostructures studied through scanning force microscopy. Nanotechnology 25, 395703 (2014).
Forte, G. et al. Surface-driven first-step events of nanoscale self-assembly for molecular peptide fibers: An experimental and theoretical study. Colloids Surfaces B Biointerfaces https://doi.org/10.1016/j.colsurfb.2018.01.016 (2018).
Aubé, A.-C. et al. Changes in enteric neurone phenotype and intestinal functions in a transgenic mouse model of enteric glia disruption. Gut 55, 630–7 (2006).
Rozario, T. & DeSimone, D. W. The extracellular matrix in development and morphogenesis: A dynamic view. Dev. Biol. 341, 126–140 (2010).
Letourneau, P., Condic, M. & Snow, D. Interactions of developing neurons with the extracellular matrix. J. Neurosci. 14, 915–928 (1994).
Bagley, C. J. et al. A key functional role for the insulin-like growth factor 1 N-terminal pentapeptide. Biochem. J. 259, 665–71 (1989).
Nieto-Estévez, V., Defterali, Ç. & Vicario-Abejón, C. IGF-I: A Key Growth Factor that Regulates Neurogenesis and Synaptogenesis from Embryonic to Adult Stages of the Brain. Front. Neurosci. 10 (2016).
Razavi, S. et al. Neurotrophic factors and their effects in the treatment of multiple sclerosis. Adv. Biomed. Res. 4, 53 (2015).
Lakhan, S. E. & Kirchgessner, A. Neuroinflammation in inflammatory bowel disease. J. Neuroinflammation 7, 37 (2010).
Brun, P. & Akbarali, H. I. Culture of Neurons and Smooth Muscle Cells from the Myenteric Plexus of Adult Mice. Neurotrophic Factors. 1727, 119–125, https://doi.org/10.1007/978-1-4939-7571-6_9 (2018).
Sato, Y. & Heuckeroth, R. O. Retinoic acid regulates murine enteric nervous system precursor proliferation, enhances neuronal precursor differentiation, and reduces neurite growth in vitro. Dev. Biol. 320, 185–198 (2008).
Brun, P. et al. Toll-Like Receptor 2 Regulates Intestinal Inflammation by Controlling Integrity of the Enteric Nervous System. Gastroenterology 145, 1323–1333 (2013).
Acknowledgements
This work has been supported by University of Padova (www.unipd.it) SID 2017 (DETT_SID17_01). The authors thank Raveena Bhodi (King’s College London) and Giulia Bernabè (University of Padova) for their excellent assistance in revising the English edition of this manuscript, and Prof. Gabriella D’Auria (University of Naples “Federico II”) for NMR characterization.
Author information
Authors and Affiliations
Contributions
P.B. and M.D. wrote the main text. P.B., A.Z., A.P., J.C., G.M.L.M. and G.M. performed experiments and discussed their results. M.D. coordinated the research groups.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Brun, P., Zamuner, A., Peretti, A. et al. 3D Synthetic Peptide-based Architectures for the Engineering of the Enteric Nervous System. Sci Rep 9, 5583 (2019). https://doi.org/10.1038/s41598-019-42071-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-42071-7
This article is cited by
-
Synthetic extracellular matrices with function-encoding peptides
Nature Reviews Bioengineering (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.