Loading of AgNPs onto the surface of boron nitride nanosheets for determination of scopoletin in Atractylodes macrocephala

In this work, silver nanoparticles prepared by a molten salt method were deposited onto the surface of hexagonal boron nitride nanosheet (NS/AgNP) to from a composite. The synthesized nanocomposite was applied for surface modification of screen-printed electrode (SPE). The modified electrode showed a superior performance for electrochemical detection of scopoletin. The electrochemical behaviour of NS/AgNP/SPE was studied in detail. An electrocatalytic oxidation was observed and used for analytical determination of scopoletin concentration. The response of the proposed electrochemical sensing platform was linear over a wide detection range of 2 μM to 0.45 mM with a low limit of detection (LOD) of 0.89 μM. The NS/AgNP/SPE also showed excellent reproducibility and anti-interference property. In addition, the proposed scopoletin sensor was successfully used for the determination of scopoletin in Atractylodes macrocephala herb samples.

avoid this drawback, AgNPs are often loaded onto the surface of other materials to study their catalytic activity. In this study, h-BN nanosheets were first prepared as the substrate, and sodium citrate was used as a reducing agent to prepare h-BN nanosheet/silver nanoparticle (NS/AgNP) composites. The prepared NS/AgNP composite was used to produce surface-modified screen-printed electrodes (SPEs), which were subsequently applied for electrochemical sensing. The synthetic method for this material was simple, the raw materials were inexpensive and easy to obtain, and the preparation conditions were mild.
Scopoletin is widely found in the roots of Atractylodes macrocephala. Studies have shown that scopoletin has pharmacological properties, such as analgesic, anti-inflammatory, antihypertensive and spasmolytic effects, especially in anti-tumour and hyperuricaemia treatments. Scopoletin has attracted wide attention both in China and abroad. To date, several methods have been developed for the determination of scopoletin, including fluorometry 23 , liquid chromatography 24 , spectrofluorimetry 25 and HPLC-UV 26 methods. Although these methods have good sensitivities and selectivities, most of them require time-consuming and complex sample pretreatment processes and expensive, large-scale equipment. Electrochemical sensing has the characteristics of rapid analysis, high sensitivity, and simple and portable instrumentation; thus, the study of convenient, fast and sensitive modified electrode materials for detection applications has attracted increasing attention. In this work, we demonstrate the first use of the prepared NS/AgNP composite for the electrochemical sensing of scopoletin. After optimization, a NS/AgNP-modified screen-printed electrode could linearly detect scopoletin over the concentration range of 2 to 450 μM with a lower detection limit of 0.89 μM. In addition, the proposed approach was successfully used to determine the scopoletin content in an Atractylodes macrocephala extract. experiments Materials. Atractylodes macrocephala roots were purchased from a local supermarket in Suzhou, China.
Borax was purchased from the Sinopharm Chemical Reagent Co., Ltd. Melamine, sodium citrate and silver nitrite were purchased from Tianjin Tyrande Chemical Reagent Co., Ltd. All other chemicals were analytical grade reagents and were used without further purification.

Preparation of the h-BN nanosheets.
The h-BN nanosheets were prepared using NaCl and KCl as the molten salt medium and melamine and borax as the reactants. The mass ratio of NaCl to KCl was 44:56. The mass ratios of nitrogen to boron were 1:1, 2:1, and 4:1. The components were mixed evenly and put into an alumina crucible. The mixture was dried at 80 °C for 5 h. The mixture was then reacted for 3 h in a GSL-1600X corundum tube furnace at 900-1200 °C under a circulating nitrogen atmosphere. The product was washed and filtered with deionized water and then dried.
preparation of the Ns/AgNp nanocomposite. The h-BN nanosheets (30 mg) and AgNO 3 (30 mg) were dispersed into 100 mL and 50 mL of water for 20 min, respectively. After mixing the two dispersions, 30 mL of a sodium citrate solution (3%) was added quickly and stirred for 20 min. After the reaction was completed, the upper layer of the solution was left in static stratification, and the remaining portion was filtered and cleaned repeatedly with ethanol and deionized water. The NS/AgNP composite was then obtained by vacuum drying at 50 °C.
Characterization. The morphology of the as-synthesized AuNPs was observed using field emission scanning electron microscopy (FESEM) on a ZEISS SUPRA 55. The crystal phase of the sample was characterized by XRD over the 2θ range of 6° to 80° with Cu Kα (λ = 0.1546 nm) radiation (D8-Advanced, Bruker).

Electrode modification and electrochemical measurements.
For the electrochemical investigation, a screen-printed electrode (SPE) was rinsed with water. For the electrode surface modification, 5 μL of a catalyst dispersion (0.5 mg/mL) was dropwise added onto the SPE surface and dried at room temperature. Electrochemical measurements were performed on a CH Instruments 660 A electrochemical workstation (CHI-660 A, CH Instruments, Texas, USA). The following conditions were used for the chronocoulometric analysis: initial E(V) = 0.5, final E (V) = 0.25, pulse width (s) = 0.25, step size = 1, and sample time (s) = 2.5 × 10 −4 .

Results and Discussion
The effects of various h-BN nanosheet preparation parameters were studied. Figure 1A shows the effect of the reaction temperature on the phase composition of the product. When the reaction temperature was 900 °C or 1000 °C degrees, the product was mainly composed of the h-BN phase with a small amount of impurities. When the reaction temperature was increased to 1100 °C and 1200 °C, the product was in the h-BN phase, and no phase impurities could be detected. Compared to the traditional borax-melamine solid-state reaction method, the reaction temperature necessary for obtaining the pure h-BN phase by the molten salt nitriding method was decreased by approximately 100 °C, which is in good agreement with the results of a previous report 20 . The effects of the salt-to-reactant ratio on the phase composition of the products are shown in Fig. 1B. When the ratio of nitrogen to boron was 2:1 and the reaction temperature was 1000 °C, the h-BN phase was present in the products of the reactions with different salt-to-reactant ratios. When the ratio of salt to reactants was increased from 0:1 to 1:1, the diffraction peaks of the phase impurities were still present in the reaction products, but the intensities of the impurity diffraction peaks decreased, indicating that the purity of the h-BN phase increased. When the ratio of salt to reactants was increased to 2:1, the diffraction peaks of the phase impurities disappeared, and only the h-BN phase was observed in the product, which indicates that an increase in the molten salt content promotes the formation of h-BN 27 . This phenomenon happens because complete dissolution of the reactants into the molten salts is conducive to their diffusion and interaction, thus promoting the formation of h-BN. Therefore, the h-BN nanosheets synthesized using a 2:1 ratio of salt to material, a 2:1 ratio of N to B and a temperature of 1100 °C were used for the composite synthesis.
www.nature.com/scientificreports www.nature.com/scientificreports/ Electrochemical impedance spectroscopy (EIS) was used to investigate the electrochemical properties of a bare SPE, an NS/SPE and an NS/AgNP/SPE using 5 mM [Fe(CN) 6 ] 3−/4− in 0.1 M KCl as the electrolyte. As shown in Fig. 3A, the EIS spectrum of the NS/SPE shows a slightly larger semicircle than that of the bare SPE due to the insulating nature of the h-BN nanosheets. In contrast, the NS/AgNP/SPE shows a much smaller semicircle, indicating that the surface modification improves the electron transfer rate on the SPE surface.   www.nature.com/scientificreports www.nature.com/scientificreports/   The CV and DPV curves of scopoletin with the different modified electrodes in a PBS solution at pH 7 were compared to study the effects of the composite on the electrocatalytic activity. Figure 4A shows the CV comparison of a 50 μM scopoletin solution obtained with the different modified electrodes. The oxidation peak current of scopoletin increases gradually from the bare SPE to the NS/SPE and to the NS/AgNP/SPE, indicating that the electrochemical activity toward scopoletin is enhanced by the presence of the silver nanoparticles and h-BN nanosheets. A comparison of the SWV data (Fig. 4B) shows that the NS/AgNP/SPE exhibits a superior electrocatalytic activity toward scopoletin and that its peak current was significantly greater than those of the other electrodes, which improved the detection sensitivity.
The CV curves of 50 a μM scopoletin solution obtained with the NS/AgNP/SPE at different scanning rates are shown in Fig. 5. The peak current (I p ) of scopoletin increased linearly with increasing scanning rates (v) from 25 mV/s to 400 mV/s and followed the equation I p = 3.3418 + 3.42006 v (R 2 = 0.996), indicating that the oxidation of scopoletin at the NS/AgNP/SPE surface was an adsorption-controlled process. The effect of the scanning rate on E p is shown in the inset of Fig. 5. Both E p and v conform to the following equation: Because the process at the electrode surface is controlled by adsorption, the relationship between E p and v follows the equation: where K 0 is the standard rate constant of the surface reaction, E 0 is the standard electrode potential, and α is the transfer coefficient for scopoletin oxidation. E p shows a linear relationship with v, and the value of α can be obtained from the slope, which is 0.021. Given that α = 0.5 is obtained, the n value of scopoletin is 2. Therefore, the oxidation process of scopoletin involves two electrons. Accumulation is a very useful pretreatment process in electrochemical sensing. Figure 6A shows the effects of the oxidation of a 50 μM solution of scopoletin at the NS/AgNP/SPE with different accumulation potentials. The results suggests that the oxidation response increases when the accumulation potential decreases from 0.4 to −0.2 V. The maximum performance was observed at an accumulated potential of −0.2 V. Additionally, further lowering the accumulation potential decreased the sensing performance. Therefore, −0.2 V was selected as the www.nature.com/scientificreports www.nature.com/scientificreports/ optimal accumulation potential for scopoletin oxidation. The accumulation time is another crucial parameter during accumulation pretreatment. As shown in Fig. 6B, the current response of scopoletin oxidation increases with increasing accumulation time. A significant current increase can be observed over the accumulation times of 30 to 100 s. The enhancement rate of the current response decreases after 100 s, especially after 140 s. Therefore, 100 s was selected as the accumulation time.
The analytical sensing ability of the NS/AgNP/SPE towards scopoletin was investigated using differential pulse voltammetry (DPV) due to the high sensitivity of this method. Figure 7 shows the DPV curves of the NS/ AgNP/SPE towards scopoletin at concentrations ranging from 2 μM to 0.45 mM. The inset shows the plots of the current response against the scopoletin concentration. A linear response was observed and can be expressed as I(μA) = 0.07144 C + 4.57122 (R 2 = 0.993). The lower limit of detection was calculated to be 0.89 μM based on a signal-to-noise ratio of 3. Based on the above results, the NS/AgNP/SPE exhibits excellent electrochemical sensing capabilities and can be used for scopoletin detection in herb samples. Table 1 summarizes the detection performance of our work compared with those of previous reports.
Dry Atractylodes macrocephala was used as a real sample for investigating the practical performance of the NS/AgNP/SPE towards scopoletin detection. A standard addition process was used, and the results are shown in Table 2. The results show that the average scopoletin concentration in Atractylodes macrocephala was 5.478 μM. HPLC (Agilent 1100) was used to confirm the electrochemical sensing performance.
The anti-interference properties of the NS/AgNP/SPE were also investigated. An I-T experiment was conducted with the successive additions of 50 μM scopoletin, glucose, tartaric acid (TA), uric acid (UA), ascorbic acid (AA), dopamine (DA), saccharose and fructose (Fig. 8). All interference species showed negligible effects on  Table 2. Electrochemical detection of scopoletin in Atractylodes macrocephala and the recovery results. www.nature.com/scientificreports www.nature.com/scientificreports/ scopoletin detection (current changes of less than 5%). The results indicate that the proposed NS/AgNP/SPE has excellent anti-interference properties for scopoletin detection.
The reproducibility of the NS/AgNP/SPE was investigated with eight individually prepared NS/AgNP/SPEs. Figure 9A shows the current responses of the eight NS/AgNP/SPEs towards a 50 μM solution of scopoletin. The RSD for the electrodes was calculated to be 5.11%, suggesting that the proposed electrode has a stable performance. The long-term stability of the electrodes was also tested. As shown in Fig. 9B, the electrode retained more than 90% of its original performance after 1 month of storage at room temperature, suggesting its acceptable long-term stability.

Conclusions
In conclusion, h-BN nanosheets were first prepared using a molten salt method using borax and melamine as the raw materials. Then, the NS/AgNP composite was prepared by a mild citric acid-assisted reduction process. The prepared NS/AgNPs were used for SPE surface medication and subsequently applied for the electrochemical determination of scopoletin. Under optimal conditions, the NS/AgNPs/SPE showed a linear detection capability towards scopoletin over a concentration range of 2 μM to 0.45 mM with a lower detection limit of 0.89 μM. In addition, the proposed NS/AgNPs/SPE was used for the determination of scopoletin in dry Atractylodes macrocephala samples.