Abstract
This paper describes a nickelbased cellular material, which has the strength of titanium and the density of water. The material’s strength arises from sizedependent strengthening of loadbearing nickel struts whose diameter is as small as 17 nm and whose 8 GPa yield strength exceeds that of bulk nickel by up to 4X. The mechanical properties of this material can be controlled by varying the nanometerscale geometry, with strength varying over the range 90–880 MPa, modulus varying over the range 14–116 GPa, and density varying over the range 880–14500 kg/m^{3}. We refer to this material as a “metallic wood,” because it has the high mechanical strength and chemical stability of metal, as well as a density close to that of natural materials such as wood.
Introduction
Cellular materials with spatially organized and repeating pore geometries can have dramatic strength improvements as structural elements shrink to the nanometer scale^{1,2,3,4}. This paper describes a nanostructured cellular material based on electroplated nickel (8,900 kg/m^{3} bulk density), which has the strength of titanium and the density of water (1,000 kg/m^{3}). The high strength arises from sizedependent strengthening of loadbearing nickel struts whose diameter is as small as 17 nm and whose strength is as high as 8 GPa. We refer to this material as a “metallic wood,” because it has the high mechanical strength and chemical stability of metal, as well as a density close to that of natural materials such as wood.
Cellular materials with nanometerscale structural elements exhibit remarkable material properties^{5}, for example high strength^{3,6,7,8,9,10}, high energy absorption^{4}, ultralow density^{1,11,12,13,14}, and high specific strength^{1,15,16}. To understand the origin of these enhanced properties, we can look at the performance of single nanopillars which approximate a single strut in a nanostructured cellular material. Compression tests on nanopillars made from single crystal metals showed that reducing pillar diameter increased pillar strength by up to an order of magnitude more than the bulk material’s strength^{17,18,19}. This sizedependent strength enhancement has been widely studied in single crystals^{17,18,20,21,22}. In nanopillars made from nanocrystalline metals, however, both an increase in strength (for Ni and Au)^{23,24} and decrease in strength (for Ni and Pt)^{25,26} have been observed as geometric dimensions were reduced to the size of a single grain diameter. When nanocrystalline gold was used in the struts of a nanostructured cellular material, the cellular solid showed dramatic strength enhancement as the strut diameter decreased^{3,6}, but the conflicting results in nanopillars make it difficult to predict if nanostructured cellular materials made from nanocrystalline metals will exhibit a strength enhancement or reduction.
In addition to nanoscale enhancement, the macroscopic properties of nanostructured cellular materials are important when considering them for engineering applications. Most articles on nanostructured cellular materials report specific strength below 100 MPa/(Mg m^{3}), which is comparable to polymers and common metals^{1,3,4,6,7,8,9,10,11,12,13,14,15,16,27,28,29}. Materials with specific strength above 100 MPa/(Mg/m^{3}) are attractive because their strength approaches that of engineering metals and ceramics^{1,15,16}. However, the density of these materials can be low, in the range of 6–410 kg/m^{3}, which prohibits their use in some applications. Consider, for example, a metal panel modeled as a simply supported beam with length 1 m, crosssectional thickness 1 mm, specific strength 100 MPa/(Mg/m^{3}), and density 100 kg/m^{3}. For an application in which the panel supports a 100 N load at the center, the sheet would require a minimum width of 15 m. In contrast, a panel with specific strength 100 MPa/(Mg/m^{3}) and density 1,000 kg/m^{3} would require a minimum width of 1.5 m, which is in general a more reasonable solution. Many structural materials have density near 1,000 kg/m^{3}, including engineering polymers and naturally occurring materials such as wood. Only a few articles report nanostructured cellular materials with density near 1,000 kg/m^{3}, and these articles focus on ceramics and carbon based materials rather than metals^{4,16,29,30}. In general, there is a lack of published research on strong nanostructured cellular materials that have enough mass to support loads found in industrial applications.
Here we report a cellular material based on nanostructured nickel inverse opal materials. The mechanical properties of this material are governed by the sizedependent strengthening of nanometerscale structural elements, allowing large specific strengths up to 230 MPa/(Mg/m^{3}) in porous nickel. This specific strength is larger than most high strength metals including high strength stainless steel and Ti6Al4V^{31,32}. The mechanical properties of this material can be varied between natural materials and high strength metal alloys by controlling the geometric parameters within the cellular architecture; we demonstrate materials with yield strengths over the range 90–880 MPa, specific moduli 7–25 GPa/(Mg/m^{3}), and densities 880–14500 kg/m^{3}. Using finite element simulations and well established micropillar compression and nanoindentation testing, we find that the material strength increases as the nanometerscale strut diameter decreases. The strut yield strengths increase from 3.8 to 8.1 GPa as the strut diameter decreases from 115 to 17 nm, which is a 4X increase over the 2 GPa bulk deposited nickel yield strength.
Results
Figure 1a shows the fabrication of the inverse opal material. First, monodisperse polystyrene (PS) particles of diameter 260–930 nm were selfassembled onto a gold/chromium coated substrate in a face centered cubic (FCC) orientation. The PS was sintered at 96 °C to improve stability and increase the interconnect diameter between PS spheres. Nickel, 99.9%, was electrodeposited into the voids of the PS structure, followed by PS etching in tetrahydrofuran. The result was an open cell inverse opal material having interconnected spherical pores in a facecentered cubic orientation. For some samples, conformal electrodeposition of either additional nickel or rheniumnickel alloy (80 wt% rhenium) increased the solids volume fraction, strut diameter, and mass. The additional deposited nickel had the same composition as the nickel used to fabricate the inverse opal structure. Mechanically tested samples with rhenium are labeled Re. The average grain sizes of the nickel film and nickel inverse opals were 12.4 nm and 15.1 nm, calculated from the XRD data shown in the supplementary information using the Scherrer equation. The grain size was similar for coated and uncoated nickel samples. A 15 nm grain size in pure nickel corresponded to a ≈6.4 GPa hardness^{33,34}, near the peak hardness values of pure nickel, which agreed well with our electrodeposited nickel thin film nanoindentation hardness measurements of 5.8 GPa. The selfassembly based fabrication method can produce material samples larger than 100 mm^{2}, while allowing ~10 nm control of structure and chemistry by altering the polystyrene diameter, processing temperature, and electroplating parameters. In comparison, most methods for fabricating nanostructured cellular solids with controlled and repeated unit cell morphologies are limited to sample sizes with areas smaller than about 5 mm^{2} ^{1,11,12,15,27,28,35}. Figure 1b–g show SEM images of the material with 500 nm pores fractured on the (111) plane. Figure 1b,c show the inverse opal material with no coating and 0.16 solids volume fraction. Figure 1d,e show the material uniformly coated with 21 nm of nickel, which increased the solids volume fraction from 0.16 to 0.35. Figure 1f,g show the nickel inverse opal material uniformly coated with 25 nm of rheniumnickel alloy, which increased the solids volume fraction to 0.46. Figure 1h shows a material with 500 nm pores, 2 cm^{2} area, and 15 µm thickness fabricated on a gold/chromium coated glass slide. Figure 1i shows a material with 300 nm pores and 20 µm thickness fabricated on gold/chromiumcoated polyimide. The material is flexible and when prepared on a polyimide sheet could be bent past a 0.5 cm radius (Fig. 1i). Table 1 shows the fabricated materials and their geometric attributes such as coating thickness and volume fraction.
The high specific strength of the inverse opal material results from two mechanical processes: porositybased weakening, which is independent of size, and strengthening of the pore struts, which is sizedependent at the nanometerscale. Porositybased weakening is the reduction in load that the material can support due to reduced volume fraction of solid material, and mediated by bending dominated deformation of the material struts^{36}. Sizedependent strengthening increases the local strength of the constituent material because of dislocation starvation in the struts, for strut widths smaller than about 1 µm^{2,9,19,37}. The inverse opal material yield strength, σ^{*}, is related to the solids volume fraction, (ρ^{*}/ρ_{s}), and strut yield stress, σ_{y}, by
where σ_{y} depends on the effective strut diameter, d, and can be greater than the bulk material strength due to sizedependent strengthening, ρ^{*} is the density of the porous inverse opal, and ρ_{s} is the density of the bulk solid^{8,36}. The geometric coefficients, C_{1} and C_{2}, are unique to the inverse opal geometry and independent of both pore size and solid chemistry. Once C_{1} and C_{2} are known for a given lattice geometry, the sizedependent strengthening effect σ_{y}(d) can be determined by measuring σ^{*}, d, and ρ^{*}/ρ_{s}^{3,8,9}.
We used finite element simulations of an inverse opal unit cell to understand how the geometry relates to the material modulus and yield strength and to solve for C_{1} and C_{2} (Fig. 2). Finite element simulations improved upon previous work, which used idealized relationships to calculate the sizedependent strengthening in nanoporous gold^{3,8,9}, by more accurately relating the applied load to the deformation and stress distribution in the inverse opal geometry. The simulations considered an inverse opal unit cell with isotropic elasticity and J2 plasticity loaded in the [111] direction. In order to mimic the experiments and control the solids volume fraction, the simulations included 0–33 nm nickel coatings, where the coating has the same material properties as the base nickel. Figure 2a shows repeat unit cells used in the finite element simulations; the colors correspond to Von Mises stresses at 1.2% engineering strain. The maximum stress occurs in the narrow region of the struts parallel to the displacement direction. Figure 2b shows corresponding stressstrain curves for nickel inverse opals with various coating thicknesses. The yield strengths, σ^{*}, were calculated at a 0.2% strain offset and compared to the solids volume fraction to solve for the coefficients in Eq. 1 ^{38}. The cellular solid yield strength is
For each material, the elastic modulus, E^{*}, was calculated from the initial slope of the linear stressstrain region in Fig. 2b. The elastic modulus is related to the solids volume fraction and bulk nickel elastic modulus, E = 171 GPa, by
The polynomial relationship between the mechanical properties and solids volume fraction indicates that the cellular solid deforms primarily through bending^{39}. This bendingdominated deformation is expected, since the inverse opal cell, with 32 struts and 21 joints, does not satisfy the Maxwell criterion^{40}. The stress and modulus relations compare closely with measurements described below, and are valid for coated and uncoated inverse opals made from any one material.
We measured mechanical properties of the fabricated materials using nanoindentation and micropillar compression measurements, which are well established techniques for measuring nanostructured cellular material compressive strengths and moduli^{1,3,4,6,7,8,9,10,11,12,13,14,15,16,17,18,19}. The micropillar compression tests measured the yield strength, σ^{*}^{17}, while nanoindentation measurements allowed us to determine elastic modulus, E^{*}, and hardness for all materials. Figure 3 shows micropillar compression test results for materials made from 500 nm diameter PS particles and 0, 19, and 33 nm nickel coatings. Figure 3a shows SEM images of 4 µm diameter micropillars before and after compression tests. Failure predominately occurred at the narrowest region of the struts and in the [111] direction parallel to the micropillar axis, consistent with the finite element simulations, which are orientated in the same geometry. Figure 3b shows the measured engineering stressstrain data for several inverse opal and solid nickel micropillars loaded to an engineering strain of about 20%. Table 1 shows the measured yield strength, which was measured using the 0.2% offset method.
The measured micropillar yield strength, σ^{*}, provides insight into the sizedependent strength of the inverse opal struts, σ_{y}(d). The supplementary methods section describes measurements of effective strut diameter, d, and solids volume fraction, (ρ^{*}/ρ_{s}), which are combined with Eqn. 2 for this analysis. Figure 3c shows strut yield strength, σ_{y}, as a function of effective strut diameter at the narrowest region of the strut, approximately where the failure occurred, for nickel inverse opals with 260, 500, and 930 nm pores. Blue data points show the strength of nickel inverse opals measured with micropillar compression. Green data points are nickel inverse opals measured with nanoindentation, where the yield strength was approximated by the hardness. Orange data points are 500 nm pore nickel inverse opals coated with 19 and 33 nm of additional nickel and measured with micropillar compression. In general, the strut strength increased as the effective strut diameter decreased. The largest value of strut yield strength measured by micropillar compression was 8.07 GPa for the nickel inverse opal material with 260 nm pore size, 0.10 solids volume fraction, and 17 nm effective strut diameter. This strength was a 4X increase over the yield strength of bulk electrodeposited nickel, which is 1.98 GPa^{33}. Importantly, the 1.98 GPa yield strength of the bulk nanocrystalline nickel was near the maximum reported for pure nickel^{33,34}, so the large strength enhancement must be due to the pore structure introduced by the inverse opal geometry. Similar strengthening has previously been reported in solid single crystal micro and nanopillar compression experiments, where the strength of subμm diameter pillars approached the theoretical strength of the material^{2,9,19,20,23,37,41,42}, as well as in nanoporous gold and mesoporous copper lattices with nanocrystalline and polycrystalline microstructure^{3,8,28}. The −0.6 slope of the best fit line for the uncoated nickel samples agreed remarkably well with the approximately −0.6 slope experimentally measured in multiple single crystal FCC metals including nickel, aluminum, gold, and copper^{17}, as well as with the −0.66 slope measured in nanocrystalline nickel nanopillars^{24}. This good agreement indicates that the strengthening mechanism and initial dislocation density in the nickel inverse opal samples were similar to previous single crystal and nanocrystalline nanopillar samples. The strengthening is derived from the small grain or feature size, which leaves no mechanism for dislocation build up and the dominant form of dislocation nucleation becomes surface nucleation^{24}. Similar to single crystal materials, the smaller strut diameters are stronger because the decreased probability of a critical dislocation compared to larger struts and bulk materials^{24}. The results in Fig. 3c show a clear sizedependent strength enhancement in inverse opal materials.
Figure 3b and Table 1 show that the inverse opal strength increased in nickel inverse opals coated with additional nickel. The inverse opal strength increase is due to the strong dependence of the material strength on relative density (Eqn. 2), despite the strut yield strength decreasing as the strut diameter increased (Fig. 3c). Interestingly, the strut yield strength exceeds the strength predicted by the fit line in Fig. 3c, which indicates that coatings could provide a method for enhancing the total strength of inverse opal composites. Currently, the exact mechanism for the strength enhancement and the interaction between coated layers is not clear.
The high strength of the inverse opal struts combined with the regular porous architecture imparts unique macroscopic material properties including high hardness, high strength at a given weight, and a controllable modulus while maintaining high specific strength. Figure 4 shows inverse opal material properties and compares them to other high strength engineering materials. Figure 4a shows hardness as a function of solids volume fraction for nickel and nickelcoated nickel inverse opal materials. Hardness measures the resistance to local plastic deformation and is important for several applications including tribology. The hardness was measured with nanoindentation and increased from 0.082 to 2.4 GPa as the solids volume fraction increased from 0.1 to 0.48. The most dramatic hardness increase, from 0.3 to 2.4 GPa, occurred between 0.28 and 0.48 solids volume fractions, where the inverse opal hardness approached the linear scaling of the bulk hardness and solids volume fraction. The hardness predicted from finite element simulations of the nanoindentation tests are shown in black and have good agreement with the measured hardness at 0.2 to 0.3 solids volume fractions^{41,43}; however, the simulations under predict the hardness at low (less than 0.2) and high (greater than 0.3) solids volume fractions. Nanoindentation simulation details can be found in the supplementary methods section. The larger than predicted material hardness at high solids volume fractions results from a larger than predicted plastic Poisson’s ratio. This can be seen by comparing the measured and calculated nominal hardness, hardness normalized by yield strength, which depends strongly on the plastic Poisson’s ratio (Fig. S2d). Figure 4b shows that the measured and predicted nominal hardness both increase with solids volume fraction, but the measured nominal hardness increases dramatically at greater than 0.35 solids volume fractions while the predicted nominal hardness remained ~1.3. This jump in the measured nominal hardness is likely due to rapid densification of the inverse opal geometry during large plastic strains, which would increase the plastic Poisson’s ratio and increase the nominal hardness. Interestingly, the dramatic hardness increase in inverse opal materials with greater than 0.3 solids volume fractions corresponds to the same volume fractions where previous simulations of inverse opal materials predicted a rapid increase of modulus towards the Hashin and Shtrikman upper bound for isotropic materials^{29,44,45}. At greater than 0.3 solids volume fraction, simulations show that the inverse opal structure can outperform the stateoftheart octet and isotropictruss geometries in isotropic Young’s modulus, shear and bulk modulus, as well as in structural efficiency (total stiffness)^{16,29}. At smaller than 0.3 solids volume fraction, the inverse opal hardness is a good predictor of the yield strength.
Figure 4c shows the strength versus density of our materials along with data from other materials for comparison purposes, including high strength Ti, Ni, Al, and steel alloys. The nickel inverse opal materials with no coatings had the strength of aluminum alloys and titanium (σ^{*} = 90–240 MPa), and density close to that of water (ρ^{*} = 880 to 1400 kg m^{−3}), filling a new material space in the strengthdensity relationship. The two lightest inverse opal materials had the same average solids volume fractions ((ρ^{*}/ρ_{s}) = 0.1); however, the sample with smaller effective strut diameters (d = 17 vs. 59 nm) had an increased strut yield strength (σ_{y}(d) = 10 vs. 4.6 GPa) that more than doubled the material yield strength (σ^{*} = 194 vs. 90 MPa). The presence of a coating further increased the material strength. The strength and density of the coated inverse opal materials was comparable to highstrength, lightweight alloys such as 7075T6 aluminum, Ti6Al4V titanium, and Ti10V2Fe3Al titanium. These material properties were achieved despite the inverse opal material being fabricated from dense engineering materials (Ni = 8,900 kg m^{−3} and Re = 21,020 kg m^{−3}).
The unique relationship between the strut strength and inverse opal geometry enables independent control of the specific modulus and specific strength. Figure 4d shows the specific strengths versus specific moduli of the nickel inverse opal materials. The average specific strengths varied between 102–230 MPa/(Mg/m^{3}) and the average specific elastic moduli varied between 9–25 GPa/(Mg/m^{3}). Uncoated nickel inverse opal materials had solid volume fractions between 0.10 and 0.28 and average specific moduli between 15 and 20 GPa/(Mg/m^{3}). Coating additional layers of nickel onto the inverse opal materials increased the solids volume fractions up to 0.48 and increased the average specific moduli to 25 GPa/(Mg/m^{3}). In some cases, the specific moduli exceeded the bulk nickel specific modulus (19.2 GPa/(Mg/m^{3})), likely due to the nonnegligible contribution of the stiff native oxide. As additional layers of nickel were coated, the specific strengths remained near 200 MPa/(Mg/m^{3}) because an increased solids volume fraction increased the geometric strength but also increased the strut diameter, which reduced the benefit of sizebased strengthening. As described by the arrows in Fig. 4d, the specific modulus can be controlled independent of the specific strength by increasing the total solids volume fraction; whereas, the specific strength can be independently controlled by changing the strut effective diameter while maintaining a constant solids volume fraction.
Discussion
The inverse opal geometry enables unique mechanical properties. The specific strengths reported here and by Do Rosario et al.^{16,29} are greater than the specific strengths reported for nanoscale octettruss architectures at similar volume fractions (10–150 MPa/(Mg/m^{3})), which ideally deform with no bending^{1,12,27}. We hypothesize that the high specific strength of inverse opal materials arises from the large concentration of ultrahigh strength struts that bear the majority of the stress concentrations, and the smooth transitions between struts that constrain bending modes and reduce stress concentrations where the struts connect. For example, and inverse opal material with 500 nm pores has 32 struts in every 0.35 µm^{3}. The high strength narrow regions in the struts support a majority of the stress concentrations and are smoothly connected to each other at ~100 nm thick nodes that prevent twisting and stress concentrations where the struts connect (Fig. S1). This pore geometry resembles closedcell foams with small interconnected openings between pores; closedcell foams outperform opencell materials because the cell faces constrain the bending modes of cell edges^{29,44}. Defects or nonclosedpacking of particles in the selfassembly process caused disorder and increased the strut diameters and solids volume fraction, which decreased specific strength. Wellordered inverse opal materials have a unique geometry that enables high specific strengths.
The specific strength of these materials could be further improved by fabricating smaller struts at increased volume fractions, and also with fewer defects in the crystal structure. For example, a perfectly ordered nickel inverse opal with 0.3 solids volume fraction and <10 nm effective strut diameters could achieve a specific strength of 520 MPa/(Mg/m^{3}) because the strut strengths would be close to the ~10.5 GPa theoretical yield strength of nickel^{46}. By using lightweight metal inverse opals such as titanium and aluminum, it might be possible to achieve 1,463 and 770 MPa/(Mg/m^{3}) specific strengths at 0.3 solids volume fractions as their theoretical yield strengths are ~15 and ~4.7 GPa^{47,48}.
Conclusion
In conclusion, we present metallic wood fabricated from nickel inverse opals, which has the strength of titanium and the chemical properties of a metal, while having the density of water and the cellular nature of natural materials like wood. The high strength of the metallic wood results from the sizedependent strengthening of the inverse opal struts, which have up to 4X the yield strength of bulk electrodeposited nickel and enable high specific strengths of 230 MPa/(Mg/m^{3}). The cellular structure can be controlled to tune the modulus and strength each by a factor of 10X.
The metallic wood can be easily fabricated over 100 mm^{2} areas, can be processed at room temperature, and can be combined with additional functional materials, as demonstrated with the rhenium coatings^{49}. The high strength continuous metallic architecture with isotropic elasticity, high hardness, and high strain energy storage could be important for a variety of applications such as energy storage^{50,51,52}, heat transport^{53}, and sensors^{54,55}. Future work could explore improvements in specific strength above 230 MPa/(Mg/m^{3}) by incorporating lightweight metals such as titanium or aluminum and developing rolltotoll processing of high strength porous metals from selfassembly^{56,57,58}.
Methods
Fabrication
The inverse opal cellular solids were fabricated by selfassembling polystyrene (PS) opals onto a goldcoated glass slide, electrodepositing nickel, and etching the remaining PS. The gold coated glass slide was fabricated by sputtering 8 nm of chromium followed by 50 nm of gold on a 1 mmthick soda lime glass slide. The glass slide with a gold film was cut into smaller samples, piranha cleaned for ten minutes, immersed in Millipore water with 3mercapto1propanesulfonic acid and sodium salt (2.2% by weight) for 4 hours and rinsed. Polystyrene (PS) opals were selfassembled onto the gold coated substrates by placing the substrates vertically in a 1 inch diameter plastic container filled with a colloidal solution of PS spheres. The plastic container was set on a hot plate at 55 °C, covered, and left for 24 to 30 hours until the solution was dry. The PS diameters were varied between 200–2,000 nm to change the cellular solid strut size. The substrates were then sintered at 96 °C for 30 minutes to 6 hours depending on the PS diameter. Longer sinter times increased the interconnect diameter between spheres and reduced the nickel volume fraction. The PS colloidal solution was made by combining 8 wt% PS sphere solution (1.2 grams), purchased from Invitrogen, with ultrapure water (40 grams). Nickel was then electrodeposited through the PS opal at a constant −1.8 volts versus a nickel reference electrode for 32 minutes in commercial plating solution, Technic RTU Mechanical Agitation. PS was removed by immersing the substrates in a tetrahydrofuran bath for 24 hours followed by a tetrahydrofuran and toluene rinse. The resulting cellular solids were about 15–20 µm thick. Additional nickel was coated on the inverse opal cellular solids using the same electroplating solution, but pulsing −1.7 volts for 30 seconds in between 20 second intervals of 0 amperage current for 15–90 cycles. Pulsed plating allowed for uniform nickel coating throughout the inverse opal depth^{52}. The nickel coating had a standard deviation between 10 and 30 percent of the average coating thickness for all samples. This variation was measured and accounted for in all calculations.
Rheniumnickel alloy was used as a coating because of its high ductility, strength, and creep resistance at high temperatures^{59}, which has made it an interesting material for thermophotovoltaics^{49}. The rheniumnickel alloy coating was deposited galvanostatically with a 5 mA cm^{−2} current density in a pH 5 electroplating bath with 34 mM NH_{4}ReO_{4}, 93 mM Ni(NH_{2}SO_{3})_{2}•4H_{2}O, and 300 mM C_{6}H_{8}O_{7} modified from ref.^{60}. NaOH was used to adjusted the pH. ReO_{4}^{−} is the most stable form of rhenium ion in solution. Citric acid, a tribasic acid, deprotonates gradually as the pH is increased and is a complexing agent. The plating bath was immersed in silicone oil at 75 °C. A platinum reference and counter electrode was used. Varying the precursor concentration changed the alloy composition. The plated alloy was about 80 weight percent rhenium measured with energydispersive Xray spectroscopy.
Material characterization
The mechanical properties of the bulk materials depend on their crystal structure. Figure S1f shows XRD data for a solid nickel film, a nickel inverse opal, and a solid rhenium film deposited on tungsten. The average grain sizes of the nickel film and nickel inverse opals were 12.4 nm and 15.1 nm, calculated from the XRD data using the Scherrer equation. A 15 nm grain size in pure nickel corresponded to a ≈6.4 GPa hardness^{33,34}, near the peak hardness values of pure nickel, which agreed well with our electrodeposited nickel thin film nanoindentation hardness measurements of 5.8 GPa. The deposited rheniumnickel alloy was amorphous with some polycrystallinity detected in transmission electron microscopy diffraction patterns.
The nickel inverse opal solids volume fraction, (ρ^{*}/ρ_{s})_{Ni}, and coating volume fraction, (ρ^{*}/ρ_{s})_{coat}, are the independent variables for calculating the effective mechanical properties of cellular solids. (ρ^{*}/ρ_{s})_{Ni} and (ρ^{*}/ρ_{s})_{coat} are calculated from SEM measurements of PS radius, R, interconnect diameter, b, and coating thickness, t, combined with a geometric model of selfassembled PS spheres organized in a FCC unit cell, details of which are in the supplementary methods.
Mechanical simulations
Uniaxial compression tests were simulated using the implicit version of the commercial finite element package ABAQUS by modeling a threedimensional unit cell of the inverse opal material with tennode nonlinear tetrahedron elements. Since the inverse opal material was subjected to a macroscopically homogeneous stress state during the uniaxial compression test, it was sufficient to consider a unit cell to evaluate the effective mechanical properties. Figure S2a shows the hexagonal unit cell orientation, chosen to best represent the inverse opal geometry in the nanoindentation and micropillar compression tests. The unit cell was modeled with isotropic elasticity and J2 plasticity using the measured properties of the electrodeposited nickel. A displacement boundary condition was applied normal to the top surface and the average reaction force at the displaced boundary was recorded at each displacement increment^{61,62}. The elastic modulus of cellular structures was calculated at the first increment of simulations. The flow stress at 0.2% offset plastic deformation was chosen as the yield strength. Additional details on the simulation setup and boundary conditions are provided in the supplementary methods.
We used a numerical method for simulating the Berkovich nanoindentation test. The main aim of the nanoindentation study was to determine the nominal hardness, \(\frac{H}{Y}\), which is the ratio of the hardness, H, to the flow strength, Y. Figure S2b shows the simplified indentation problem. We represented the threedimensional Berkovich tip as a conical indenter with half cone angle θ = 70.3°^{63}, so that the nominal contact area A_{n} was the same as the Berkovich tip. The conical indenter was forced into the center of a cellular solid material block of size L at the center (Fig. S2b). As a result, only the axisymmetric mode of deformation was considered, and the corresponding boundary value problem was solved in cylindrical coordinates (r, z).
The cellular solid block bottom was fixed in the z direction, u_{z}_{z = 0} = 0, while a symmetric boundary condition was imposed on the center line, u_{r}_{r = 0} = 0. The indenter was assumed to be rigid and frictionless, and was statically driven into the block with displacement h. We evaluated the reaction force, F(h), and the nominal contact area, A_{n}(h) = πa(h)^{2}. The hardness, H, at indentation depth h was calculated as
The boundary value problem was solved using the implicit version of the commercial Finite Element Package ABAQUS, with 4 nodes axisymmetric elements. To determine the nominal hardness, \(\frac{H}{Y}\), the flow strength, Y, was chosen as the flow strength at 10% axial strain and kept as a constant. We chose the flow strength at 10% axial strain because, as shown in Fig. 3b, the uniaxial compression response of the cellular solid showed a mild strain hardening behavior after reaching the yield stress, σ_{Y}.
We considered the cellular solid as a homogenized continuum during the indentation process, as the contact radii was large compared to the unit cell size over most of the range of indentation depth h. Isotropic elasticity was used to model the elastic behavior of the cellular solid, with Young’s modulus, E, and elastic Poisson’s ratio, υ^{e}, calculated from the unit cell compression simulations. Following Khaderi et al.^{41}, the plastic deformation of the cellular solid was described by the isotropic crushable foam model of Deshpande and Fleck^{43}.
The isotropic yield surface of the cellular solid is specified by
The equivalent stress, \(\hat{\sigma }\), was composed of the mean stress, σ_{m}, and the Mises effective stress, σ_{e}, by
where \({\sigma }_{m}=\frac{1}{3}{\sigma }_{kk}\), and \({\sigma }_{e}^{2}=\frac{3}{2}{\sigma ^{\prime} }_{ij}{\sigma ^{\prime} }_{ij}\) with \({\sigma ^{\prime} }_{ij}={\sigma }_{ij}\frac{1}{3}{\sigma }_{kk}\). The typical compressive response of a cellular solid is characterized by a plateau stress \({\sigma }_{Y}^{pl}\) followed by densification due to the contact between the cell walls at large deformation. Following Khaderi et al. we assumed the yield surface \(Y({\hat{\varepsilon }}_{P})\) to have the following form^{41}
where the hardening rate h_{d} after densification was assumed to be equal to the effective Young’s modulus, E, of the inverse opal cellular solid. The parameter α determined the plastic compressibility by specifying the ratio of deviatoric stress to hydrostatic strength. Assuming the associate flow rule, α was determined by evaluating the plastic Poisson’s ratio, v_{p}, through the following relationship,
With v_{p} = 0.5, plastic incompressibility was maintained, and v_{p} < 0.5 means the plastic flow was compressible. We thus calculate the plastic Poisson’s ratio from the uniaxial compression simulations with
and hence the corresponding α value is obtained. Figure S2c shows the finite element prediction of the plastic Poisson’s ratio, v_{p}, as a function of solids volume fraction, (ρ^{*}/ρ_{s}), from the unit cell calculations. The plastic Poisson’s ratio, v_{p}, increased from 0.075 to 0.2 as (ρ^{*}/ρ_{s}) increased from 0.17 to 0.43.
Figure S2d shows finite element predictions of the nominal hardness, \(\frac{H}{Y}\), versus v_{p} for an inverse opal material with 0.17 total solids volume fraction. The nominal hardness, \(\frac{H}{Y}\), remained at approximately 1.3 when v_{p} was smaller than 0.3, and increased to 2.7 as v_{p} reached 0.5.
Mechanical measurements
The inverse opal cellular solids were mechanically characterized using nanoindentation and micropillar compression. An Agilent G200 Nanoindenter with a diamond Berkovich tip measured the hardness and elastic modulus of the samples through continuous stiffness measurements. The continuous stiffness technique provided mechanical properties as a function of indentation depth. The indentation depths were limited to 7.5 μm of displacement or the maximum peak load of 600 mN. Figure S4 shows hardness measurements for various nickel cellular solids with 500 nm diameter pores coated with nickel and rheniumnickel alloy. The data has a large standard deviation due to the surface roughness inherent to the porous structure at indentation depths below 500 nm. Material aggregation and substrate mechanical properties affect the measurements at indentation depths comparable to the sample thickness^{64,65}. In between these extremes, the data has a plateau typically near 2000 nm depth. The hardness and elastic modulus from each indentation were determined by the average value in this plateau range. For each sample, the reported values were the average of 10 indentations or more.
Micropillar specimens were prepared by using an FEI Helios Nanolab 600i focused ion beam. Annular milling in three steps using beam currents of 21 nA, 2.5 nA and 80 pA resulted in cylindrical specimens of ≈3.6 μm diameter and ≈8 μm height. A final 100 nmwide ring milling facilitated adjusting the height of the micropillars and minimizing their taper to less than two degrees from vertical. The Agilent G200 Nanoindenter with a 10 μm diameter flat diamond punch compressed the micropillars at an average strain rate of ≈1e4 s^{−1}. The nanoindenter deformed the micropillars to a total strain of about 20%. SEMmeasured micropillar diameter, taken at the micropillar center, and height allowed the calculation of stressstrain behavior. The stress at 0.2% strain offset was used as the yield strength. The loading and unloading moduli were corrected to account for the substrate thickness using the method described in ref.^{66}. The Poisson’s ratio of the inverse opal cellular solids was taken as zero for nanoindentation and micropillar compression calculations based on previous testing of nanoporous opencell foams and qualitative experimental observations^{3,8}. The micropillar unloading moduli were 2–5X greater than the loading moduli and were similar to moduli measured with nanoindentation.
Availability of Materials and Data
The datasets generated during and/or analyzed during the current study are available from the corresponding author on reasonable request.
References
 1.
Meza, L. R., Das, S. & Greer, J. R. Strong, lightweight, and recoverable threedimensional ceramic nanolattices. Science 345, 1322–1326, https://doi.org/10.1126/science.1255908 (2014).
 2.
Shan, Z., Mishra, R. K., Asif, S. S., Warren, O. L. & Minor, A. M. Mechanical annealing and sourcelimited deformation in submicrometrediameter Ni crystals. Nat. Mater. 7, 115–119 (2008).
 3.
Biener, J., Hodge, A. M., Hamza, A. V., Hsiung, L. M. & Satcher, J. H. Nanoporous Au: A high yield strength material. Journal of Applied Physics 97, 024301, https://doi.org/10.1063/1.1832742 (2005).
 4.
Lee, J.H., Wang, L., Boyce, M. C. & Thomas, E. L. Periodic Bicontinuous Composites for High Specific Energy Absorption. Nano Letters 12, 4392–4396, https://doi.org/10.1021/nl302234f (2012).
 5.
Bauer, J. et al. Nanolattices: An Emerging Class of Mechanical Metamaterials. Advanced Materials, 1701850n/a, https://doi.org/10.1002/adma.201701850.
 6.
Biener, J., Hodge, A. M. & Hamza, A. V. Microscopic failure behavior of nanoporous gold. Appl. Phys. Lett. 87, 121908, https://doi.org/10.1063/1.2051791 (2005).
 7.
Biener, J. et al. Size Effects on the Mechanical Behavior of Nanoporous Au. Nano Letters 6, 2379–2382, https://doi.org/10.1021/nl061978i (2006).
 8.
Hodge, A. M. et al. Scaling equation for yield strength of nanoporous opencell foams. Acta Materialia 55, 1343–1349, https://doi.org/10.1016/j.actamat.2006.09.038 (2007).
 9.
Volkert, C., Lilleodden, E., Kramer, D. & Weissmuller, J. Approaching the theoretical strength in nanoporous Au. Appl. Phys. Lett. 89, 061920061920061923 (2006).
 10.
Lee, D. et al. Microfabrication and mechanical properties of nanoporous gold at the nanoscale. Scripta Materialia 56, 437–440, https://doi.org/10.1016/j.scriptamat.2006.08.069 (2007).
 11.
Jang, D., Meza, L. R., Greer, F. & Greer, J. R. Fabrication and deformation of threedimensional hollow ceramic nanostructures. Nat Mater 12, 893–898, https://doi.org/10.1038/nmat3738, http://www.nature.com/nmat/journal/v12/n10/abs/nmat3738.html#supplementaryinformation (2013).
 12.
Zheng, X. et al. Ultralight, ultrastiff mechanical metamaterials. Science 344, 1373–1377, https://doi.org/10.1126/science.1252291 (2014).
 13.
Zheng, X. et al. Multiscale metallic metamaterials. Nat Mater 15, 11001106, https://doi.org/10.1038/nmat4694, http://www.nature.com/nmat/journal/v15/n10/abs/nmat4694.html#supplementaryinformation (2016).
 14.
Schaedler, T. A. et al. Ultralight Metallic Microlattices. Science 334, 962–965, https://doi.org/10.1126/science.1211649 (2011).
 15.
Bauer, J., Hengsbach, S., Tesari, I., Schwaiger, R. & Kraft, O. Highstrength cellular ceramic composites with 3D microarchitecture. Proceedings of the National Academy of Sciences, https://doi.org/10.1073/pnas.1315147111 (2014).
 16.
do Rosário, J. J. et al. SelfAssembled Ultra High Strength, Ultra Stiff Mechanical Metamaterials Based on Inverse Opals. Adv. Eng. Mater., https://doi.org/10.1002/adem.201500118 (2015).
 17.
Uchic, M. D., Shade, P. A. & Dimiduk, D. M. Plasticity of MicrometerScale Single Crystals in Compression. Annual Review of Materials Research 39, 361–386, https://doi.org/10.1146/annurevmatsci082908145422 (2009).
 18.
Greer, J. R. & De Hosson, J. T. M. Plasticity in smallsized metallic systems: Intrinsic versus extrinsic size effect. Progress in Materials Science 56, 654–724, https://doi.org/10.1016/j.pmatsci.2011.01.005 (2011).
 19.
Frick, C. P., Clark, B. G., Orso, S., Schneider, A. S. & Arzt, E. Size effect on strength and strain hardening of smallscale [111] nickel compression pillars. Materials Science and Engineering: A 489, 319–329, https://doi.org/10.1016/j.msea.2007.12.038 (2008).
 20.
Uchic, M. D., Dimiduk, D. M., Florando, J. N. & Nix, W. D. Sample Dimensions Influence Strength and Crystal Plasticity. Science 305, 986–989, https://doi.org/10.1126/science.1098993 (2004).
 21.
ElAwady, J. A. et al. Prestraining effects on the powerlaw scaling of sizedependent strengthening in Ni single crystals. Scripta Materialia 68, 207–210 (2013).
 22.
Rao, S. I. et al. Athermal mechanisms of sizedependent crystal flow gleaned from threedimensional discrete dislocation simulations. Acta Materialia 56, 3245–3259 (2008).
 23.
An, B. H. et al. Ultrahigh Tensile Strength Nanowires with a Ni/Ni–Au Multilayer Nanocrystalline Structure. Nano Letters 16, 3500–3506, https://doi.org/10.1021/acs.nanolett.6b00275 (2016).
 24.
Rinaldi, A., Peralta, P., Friesen, C. & Sieradzki, K. Samplesize effects in the yield behavior of nanocrystalline nickel. Acta Materialia 56, 511–517 (2008).
 25.
Jang, D. & Greer, J. R. Sizeinduced weakening and grain boundaryassisted deformation in 60 nm grained Ni nanopillars. Scripta Materialia 64, 77–80, https://doi.org/10.1016/j.scriptamat.2010.09.010 (2011).
 26.
Gu, X. W. et al. Sizedependent deformation of nanocrystalline Pt nanopillars. Nano Letters 12, 6385–6392 (2012).
 27.
Meza, L. R. et al. Resilient 3D hierarchical architected metamaterials. Proceedings of the National Academy of Sciences, https://doi.org/10.1073/pnas.1509120112 (2015).
 28.
Wendy, G. X. & Greer, J. R. Ultrastrong architected Cu mesolattices. Extreme Mechanics Letters 2, 7–14, https://doi.org/10.1016/j.eml.2015.01.006 (2015).
 29.
do Rosário, J. J., Berger, J. B., Lilleodden, E. T., McMeeking, R. M. & Schneider, G. A. The stiffness and strength of metamaterials based on the inverse opal architecture. Extreme Mechanics Letters 12, 86–96, https://doi.org/10.1016/j.eml.2016.07.006 (2017).
 30.
Worsley, M. A. et al. Toward Macroscale, Isotropic Carbons with Graphene‐Sheet‐Like Electrical and Mechanical Properties. Advanced Functional Materials 24, 4259–4264 (2014).
 31.
Kim, S.H., Kim, H. & Kim, N. J. Brittle intermetallic compound makes ultrastrong lowdensity steel with large ductility. Nature 518, 77–79, https://doi.org/10.1038/nature14144 (2015).
 32.
Welsch, G., Boyer, R. & Collings, E. Materials properties handbook: titanium alloys. (ASM international, 1993).
 33.
ElSherik, A. M., Erb, U., Palumbo, G. & Aust, K. T. Deviations from hallpetch behaviour in asprepared nanocrystalline nickel. Scripta Metallurgica et Materialia 27, 1185–1188, https://doi.org/10.1016/0956716X(92)905967 (1992).
 34.
Seo, B. B., Gu, J., Jahed, Z. & Tsui, T. Y. Influence of grain boundary modifier on the strength sizedependence displayed by complexshaped nanocrystalline nickel pillars. Thin Solid Films 621, 178–183, https://doi.org/10.1016/j.tsf.2016.12.005 (2017).
 35.
Montemayor, L. C., Meza, L. R. & Greer, J. R. Design and Fabrication of Hollow Rigid Nanolattices via TwoPhoton Lithography. Adv. Eng. Mater. 16, 184–189, https://doi.org/10.1002/adem.201300254 (2014).
 36.
Gibson, L. J. & Ashby, M. F. Cellular Solids: Structure and Properties. Second edn, (Cambridge University Press, 1997).
 37.
Greer, J. R., Oliver, W. C. & Nix, W. D. Size dependence of mechanical properties of gold at the micron scale in the absence of strain gradients. Acta Materialia 53, 1821–1830, https://doi.org/10.1016/j.actamat.2004.12.031 (2005).
 38.
Callister, W. D. & Rethwisch, D. G. Materials science and engineering: an introduction. Vol. 7 (Wiley New York, 2007).
 39.
Ashby, M. F. The properties of foams and lattices. Philosophical Transactions of the Royal Society A: Mathematical, Physical and Engineering Sciences 364, 15–30, https://doi.org/10.1098/rsta.2005.1678 (2006).
 40.
Deshpande, V. S., Ashby, M. F. & Fleck, N. A. Foam topology: bending versus stretching dominated architectures. Acta Materialia 49, 1035–1040, https://doi.org/10.1016/S13596454(00)003797 (2001).
 41.
Khaderi, S. N. et al. The indentation response of Nickel nano double gyroid lattices. Extreme Mechanics Letters 10, 15–23, https://doi.org/10.1016/j.eml.2016.08.006 (2017).
 42.
Bauer, J., Schroer, A., Schwaiger, R. & Kraft, O. Approaching theoretical strength in glassy carbon nanolattices. Nat Mater 15, 438–443, https://doi.org/10.1038/nmat4561, http://www.nature.com/nmat/journal/v15/n4/abs/nmat4561.html#supplementaryinformation (2016).
 43.
Deshpande, V. & Fleck, N. Isotropic constitutive models for metallic foams. Journal of the Mechanics and Physics of Solids 48, 1253–1283 (2000).
 44.
Berger, J. B., Wadley, H. N. G. & McMeeking, R. M. Mechanical metamaterials at the theoretical limit of isotropic elastic stiffness. Nature 543, 533–537, https://doi.org/10.1038/nature21075, http://www.nature.com/nature/journal/v543/n7646/abs/nature21075.html#supplementaryinformation (2017).
 45.
Pikul, J. H. et al. Micromechanical devices with controllable stiffness fabricated from regular 3D porous materials. Journal of Micromechanics and Microengineering 24, 105006 (2014).
 46.
YueLin, L., Ying, Z., HongBo, Z., GuangHong, L. & Masanori, K. Theoretical strength and charge redistribution of fcc Ni in tension and shear. Journal of Physics: Condensed Matter 20, 335216 (2008).
 47.
Song, Y., Yang, R., Li, D. & Guo, Z. A firstprinciples study of the theoretical strength and bulk modulus of hcp metals. Philosophical Magazine A 81, 321–330 (2001).
 48.
Ogata, S., Li, J. & Yip, S. Ideal Pure Shear Strength of Aluminum and Copper. Science 298, 807 (2002).
 49.
Zhang, R., Cohen, J., Fan, S. & Braun, P. V. Electrodeposited high strength, thermally stable spectrally selective rhenium nickel inverse opals. Nanoscale 9, 11187–11194 (2017).
 50.
Pikul, J. H., Gang Zhang, H., Cho, J., Braun, P. V. & King, W. P. Highpower lithium ion microbatteries from interdigitated threedimensional bicontinuous nanoporous electrodes. Nat. Commun. 4, 1732, https://doi.org/10.1038/ncomms2747 (2013).
 51.
Zhang, H., Yu, X. & Braun, P. V. Threedimensional bicontinuous ultrafastcharge and discharge bulk battery electrodes. Nat. Nanotechnol. 6, 277–281, http://www.nature.com/nnano/journal/v6/n5/abs/nnano.2011.38.html#supplementaryinformation (2011).
 52.
Pikul, J. H., Liu, J., Braun, P. V. & King, W. P. Integration of high capacity materials into interdigitated mesostructured electrodes for high energy and high power density primary microbatteries. J. Power Sources 315, 308–315, https://doi.org/10.1016/j.jpowsour.2016.03.034 (2016).
 53.
Yoonjin, W., Barako, M. T., Agonafer, D. D., Asheghi, M. & Goodson, K. E. In Thermal and Thermomechanical Phenomena in Electronic Systems (ITherm), 2014 IEEE Intersociety Conference on. 326–332.
 54.
You, X., Pikul, J. H., King, W. P. & Pak, J. J. Zinc oxide inverse opal enzymatic biosensor. Appl. Phys. Lett. 102, 253103–253105 (2013).
 55.
Stein, A., Wilson, B. E. & Rudisill, S. G. Design and functionality of colloidalcrystaltemplated materialschemical applications of inverse opals. Chemical Society Reviews 42, 2763–2803, https://doi.org/10.1039/c2cs35317b (2013).
 56.
Li, X. & Gilchrist, J. F. Largearea nanoparticle films by continuous automated langmuir–blodgett assembly and deposition. Langmuir 32, 1220–1226 (2016).
 57.
Hatton, B., Mishchenko, L., Davis, S., Sandhage, K. H. & Aizenberg, J. Assembly of largearea, highly ordered, crackfree inverse opal films. Proceedings of the National Academy of Sciences 107, 10354–10359, https://doi.org/10.1073/pnas.1000954107 (2010).
 58.
Weldon, A. L., Kumnorkaew, P., Wang, B., Cheng, X. & Gilchrist, J. F. Fabrication of macroporous polymeric membranes through binary convective deposition. ACS Applied Materials & Interfaces 4, 4532–4540 (2012).
 59.
Reed, R. C. The superalloys: fundamentals and applications. (Cambridge university press, 2006).
 60.
Naor, A., Eliaz, N. & Gileadi, E. Electrodeposition of rhenium–nickel alloys from aqueous solutions. Electrochim. Acta 54, 6028–6035, https://doi.org/10.1016/j.electacta.2009.03.003 (2009).
 61.
Li, J. R., Cheng, H. F., Yu, J. L. & Han, F. S. Effect of dualsize cell mix on the stiffness and strength of opencell aluminum foams. Materials Science and Engineering: A 362, 240–248, https://doi.org/10.1016/S09215093(03)005707 (2003).
 62.
Kou, D. P., Li, J. R., Yu, J. L. & Cheng, H. F. Mechanical behavior of opencell metallic foams with dualsize cellular structure. Scripta Materialia 59, 483–486, https://doi.org/10.1016/j.scriptamat.2008.04.022 (2008).
 63.
Min, L., WeiMin, C., NaiGang, L. & LingDong, W. A numerical study of indentation using indenters of different geometry. Journal of Materials Research 19, 73–78 (2004).
 64.
Tsui, T. Y. & Pharr, G. M. Substrate effects on nanoindentation mechanical property measurement of soft films on hard substrates. Journal of Materials Research 14, 292–301, https://doi.org/10.1557/JMR.1999.0042 (1999).
 65.
Oliver, W. C. & Pharr, G. M. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. Journal of Materials Research 7, 1564–1583, https://doi.org/10.1557/JMR.1992.1564 (1992).
 66.
Fei, H., Abraham, A., Chawla, N. & Jiang, H. Evaluation of MicroPillar Compression Tests for Accurate Determination of ElasticPlastic Constitutive Relations. Journal of Applied Mechanics 79, 061011–061011, https://doi.org/10.1115/1.4006767 (2012).
 67.
Ledbetter, H. Physical Properties Data Compilations Relevant to Energy Storage. (National Bureau of Standards, 1982).
 68.
Donachie, M. J. & Donachie, S. J. Superalloys: a technical guide. (ASM international, 2002).
Acknowledgements
This research was supported by the Department of Energy Office of Science Graduate Fellowship Program (DOE SCGF), made possible in part by the American Recovery and Reinvestment Act of 2009, administered by ORISEORAU under contract no. DEAC0506OR23100.
Author information
Affiliations
Contributions
J.H.P., P.V.B. and W.P.K. conceived of the idea. J.H.P., S.O. and R.Z. carried out experiments. J.H.P., S.O., B.L., V.S.D. and W.P.K. developed the theory and B.L. and V.S.D. performed the simulations. P.V.B. and W.P.K. supervised the project. All authors discussed the results and contributed to the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Pikul, J.H., Özerinç, S., Liu, B. et al. High strength metallic wood from nanostructured nickel inverse opal materials. Sci Rep 9, 719 (2019). https://doi.org/10.1038/s41598018369013
Received:
Accepted:
Published:
Further reading

Effect of fused deposition modeling process parameters on the mechanical properties of recycled polyethylene terephthalate parts
Journal of Applied Polymer Science (2021)

Fabrication of TiO2coated nanostructured Ni foams for improved mechanical properties
Ceramics International (2020)

Nondestructive Measurements of the Mechanical and Structural Properties of Nanostructured Metalattices
Nano Letters (2020)

Temperaturedependent mechanical behavior of threedimensionally ordered macroporous tungsten
Journal of Materials Research (2020)

Conformal Electrodeposition of Co–Ni to Improve the Mechanical Properties of ThreeDimensional Ordered Macroporous Ni Films
Journal of The Electrochemical Society (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.