With the ever-increasing demand for low power electronics, neuromorphic computing has garnered huge interest in recent times. Implementing neuromorphic computing in hardware will be a severe boost for applications involving complex processes such as image processing and pattern recognition. Artificial neurons form a critical part in neuromorphic circuits, and have been realized with complex complementary metal–oxide–semiconductor (CMOS) circuitry in the past. Recently, metal-insulator-transition materials have been used to realize artificial neurons. Although memristors have been implemented to realize synaptic behavior, not much work has been reported regarding the neuronal response achieved with these devices. In this work, we use the volatile threshold switching behavior of a vertical-MoS2/graphene van der Waals heterojunction system to produce the integrate-and-fire response of a neuron. We use large area chemical vapor deposited (CVD) graphene and MoS2, enabling large scale realization of these devices. These devices can emulate the most vital properties of a neuron, including the all or nothing spiking, the threshold driven spiking of the action potential, the post-firing refractory period of a neuron and strength modulated frequency response. These results show that the developed artificial neuron can play a crucial role in neuromorphic computing.
Understanding the complex and overwhelming functioning of the human brain has always fascinated scientists and researchers for biological fields and beyond. The way the human brain can process huge amounts of data and handle pattern recognition with relative ease is immensely compelling and its complexity is continuously evolving. The building blocks in the brain consist of interconnected neurons and synapses, which cooperate efficiently to process incoming signals and decide on outgoing actions. Inspired by the operation of the human brain, various neuromorphic devices, circuits, and systems have been developed that can work analogous to the brain. Owing to the low power dissipation and characteristics that are similar to biological neurons, spiking neural networks (SNN) have garnered huge interests for mimicking and closely resembling the neuro-biological system1. SNNs, the third generation of neural network models, have been found to be more hardware friendly and energy efficient; thus making them more biologically realistic compared to other neural networks2. The key components of an SNN are artificial neurons and synapses where the synapses connect the pre-neurons and the post-neurons. SNN uses discrete rather than continuous spikes along with the incorporation of the concept of time. It involves efficient transfer of information based on precise timing of a sequence of spikes. Important synaptic behaviors such as synaptic plasticity, long term potentiation and depression (LTP and LTD), and Spike Time dependent Plasticity (STDP) have been studied using emerging devices such as memristors for information processing, pattern recognition and learning methods of SNN3,4,5. But, neuronal response has mostly been realized using complex CMOS circuitry, which requires several transistors to mimic a single neuron. These circuits involve a large number of active components, increasing the power dissipation and making high density integration difficult5,6,7. To overcome these issues, various emerging devices have been used to emulate a biological neuron behavior. Insulator to metal transition (IMT) in materials such as vanadium dioxide (VO2)8,9 and niobium dioxide (NbO2)10, chalcogenide-based phase change materials11 and magnetoelectric switching of ferromagnets such as bismuth ferrite (BiFeO3)1, have been considered to develop various types of artificial neurons. VO2 has a very low critical temperature of ~340 K above which its switching behavior disappears, severely limiting the operational range of devices and making them unsuitable for on-chip integration8,9,12. In case of phase change materials-based neurons, the degree to which the neuronal characteristics can be tuned with nominal circuitry is limited by the fact that switching properties arise from the physics of crystallization11. For the same reason, the switching speed in phase change neuron is slow. Threshold switching in memristors can be a natural choice for realizing artificial neurons. However, the exploitation of threshold switching in memristors to realize artificial neurons is relatively unexplored. Recently, a Ag/SiO2/Au threshold switching memristor (TSM) was used to demonstrate an integrate-and-fire neuron13. The observation of volatile threshold switching in MoS2 stimulates the possibility of employing this phenomenon for the realization of artificial neurons14. However, the switching in a lateral MoS2 film mediated by the grain boundaries occludes scaling of lateral device dimensions. Hence, realizing such characteristics using a vertical structure can play a critical role in improving scaling opportunities.
In this paper, we have constructed an integrate-and-fire artificial neuron by exploiting the threshold switching behavior in CVD-grown vertical MoS2 (v-MoS2) layers. A novel device structure was fabricated by growing v-MoS2 on a CVD-graphene monolayer as the bottom electrode and with Ni as the top contact to v-MoS2. The key characteristics of a biological neuron including an all or nothing spiking, a threshold driven spiking, a post firing refractory period and an input strength modulated frequency response were observed. The developed v-MoS2/graphene TSM artificial neuron can operate over a wide range of temperature and can potentially be scaled down to nanometer scale cross bar structures. This platform provides an attractive prospect for neuromorphic circuits, which can be seamlessly integrated with existing fabrication technologies enabling large scale realization of such devices.
The schematic of a biological neuron connected to multiple synapses is shown in Fig. 1a. Biological neurons are connected to each other through synapses. Depending upon the input signals received by the dendrites, an action potential (also referred to as a neuron spike) is generated by the soma of the neuron, which is then passed by the axon to other neurons through synapses. The electrical equilibrium is maintained by the movement of various ions such as Na+, K+, Cl− and Ca2+ in and out of the neuron cell. The potential difference between the interior and the exterior of the neuron is referred to as the membrane potential1. As the membrane potential (VM) builds up, the neuron produces an output spike (Iout) when the potential reaches a particular threshold voltage (Vth)15,16. This phenomenon of neuron spiking is shown in Fig. 1b. The neuron does not fire immediately after producing a spike even if it keeps receiving input signals. This period is known as the refractory period of a neuron8,17. After the refractory period, the neuron starts integrating the input again and prepares for the following spike.
One of the most commonly used neuron models in computational neuroscience is the integrate-and-fire (IF) model18. An IF artificial neuron fires as a function of the electrical potential developed across it, thus mimicking the crucial behavior of a biological neuron. Here, this behavior has been realized with a v-MoS2/graphene TSM as shown in the conceptual scheme in Fig. 1c. The v-MoS2/graphene neuron integrates the input signals received with the help of a capacitor. The capacitor integrates the charge and as soon as the voltage across the capacitor increases beyond the threshold value of the TSM, the neuron fires and an output spike is produced.
The device schematic of the v-MoS2/graphene device is shown in Fig. 2a. It consists of a CVD-grown monolayer graphene, wet transferred on the Si/SiO2 substrate19, followed by patterned growth of v-MoS2 on graphene. Nickel contacts were deposited on the graphene and on the v-MoS2. The optical image of the device is shown in Fig. 2b. A representative image of a block of a single chip with ~200 MoS2/graphene Threshold Switching Memristors (TSMs) is shown in Fig. 2c. The composition of the two layers was confirmed by Raman spectroscopy with excitation wavelength of 532 nm laser in ambient conditions. The spectrum in Fig. 2d was obtained on the as-grown v-MoS2 film over graphene in the device. Two bands corresponding to the in-plane E12g mode and the out-of-plane A1g mode were observed at 383 cm−1 and 411 cm−1 respectively. The presence of these two distinct high intensity peaks and the difference of about 28 cm−1 between their two positions signifies the presence of good quality multilayer MoS220. On pristine graphene, as shown in the inset of Fig. 2e, the Raman spectrum yielded two major distinct peaks, viz. the G band at 1590 cm−1, and the 2D band at 2690 cm−1. The peak intensity ratio I2D/IG is about ~2, indicating that the monolayer graphene used for our devices is of good quality21. After sulfurization, the spectrum, presented in Fig. 2e, exhibits three distinct peaks: The D band at 1350 cm−1, the G band at 1590 cm−1 and the 2D band at 2690 cm−1. A significant decrease in intensity of the 2D band with respect to the G band is revealed. This reduced value of the peak intensity ratio of the G and 2D peak and the large D band indicate the introduction of defects in the graphene layer during sulfurization22. The detailed analysis of the v-MoS2/graphene 2D-2D van der Waal’s heterojunction was carried out by High Resolution Transmission Electron Microscopy (HRTEM). Figure 2f shows the cross-section HRTEM image of 2D MoS2 on graphene/Si/SiO2. It can be clearly observed that MoS2 grows vertically on the graphene surface with high density of exposed edge planes. The vertical orientation of 2D MoS2 atomic layers was obtained by the sulfurization of thick Mo films, which essentially minimizes the strain energy arising as a result of volume expansion during Mo to MoS2 conversion23. This eventually leads to the formation of polycrystalline MoS2 structure with vertically orientated grains perpendicular to the substrate. The thickness of the CVD grown v-MoS2, as determined by using Atomic force microscopy (AFM) (Fig. 2g), was 21 nm, which is in agreement with the thickness observed in the cross-section TEM analysis of Fig. 2f.
Results and Discussion
To assess the switching characteristics with respect to the current compliance, the v-MoS2/graphene TSM was tested at various current compliances of 100 nA, 500 nA, and 1 µA as shown in Fig. 3a–c. The I-V characteristics of the same device were recorded by sweeping the voltage on the graphene electrode while keeping the MoS2 electrode at 0 V first with a current compliance of 100 nA repeatedly over 3 cycles. This process is then repeated with a current compliance of 500 nA and 1 µA. In all the cases, it is observed that the device is initially in its high resistance state (HRS) until a voltage higher than the threshold voltage is applied. At the onset of the threshold voltage (V1), the device undergoes an abrupt transition from the HRS to a low resistance state (LRS). During the reverse sweep, the device reverts to HRS as the voltage reduces below a particular value (V2). It is interesting to note that the device retains the volatile threshold switching behavior for all the applied current compliances.
After confirming the volatile threshold switching behavior of v-MoS2/graphene device, we now concentrate on the demonstration of an artificial neuron exploiting the volatile switching. The schematic of the circuit used for realizing the artificial neuron with the v-MoS2/graphene TSM is shown in Fig. 4a. The TSM device is connected in parallel with a resistor, Rp = 1 MΩ and a capacitor Co = 100 nF, which are connected in series to a resistor Ro = 10 kΩ. A load resistor RL = 1 MΩ is connected in series with the TSM to measure the output voltage. The resistors and the capacitor are connected to the device externally through a breadboard. The parallel resistor ‘Rp’ is connected to drain excessive current away from the device, thereby protecting the device. Its value is chosen to be 1 MΩ which is less than the RLRS = ~3 MΩ and greater than Ro such that Co does not discharge through Rp. The input source is a train of constant amplitude voltage pulses applied to the left node of the circuit with frequency 5 kHz and TON = 100 µs. The output voltage is measured across the RL. In Fig. 4b, when a series of input pulses (blue line) of an amplitude of 8 V with TON = 100 µs are applied to the circuit, the capacitor starts charging and the voltage starts increasing at node A (black line) till the capacitor gets completely charged. Initially, the TSM is in its HRS and the device resistance ‘RHRS’ is high (~10 MΩ) compared to Ro. The charging time constant (RoC) is ~100 times lower than that for the discharging time constant [(RP||RHRS|| RL) Co], hence the leakage through the device is almost negligible. Therefore, on application of the input pulses to the circuit, the capacitor (Co) gets charged. As the charge across the capacitor increases and the voltage at node A reaches the threshold voltage of the TSM, the device switches from the HRS to the LRS. Since the TSM is now in the LRS state, the capacitor starts discharging through the device and an abrupt increase in the current appears at the rightmost node (output). This corresponds to the increase in voltage at t ≈ 300 ms, observed in Fig. 4c. Now, the capacitor starts discharging and consequently the voltage at node A starts dropping down. Once the voltage at node A decreases, the TSM device reverts to the HRS. This results in the output current and voltage to reduce as well, causing a spike in the output voltage (Fig. 4c). The capacitor starts charging again signifying commencement of the integration period of the neuron as shown in Fig. 4c. The process gets repeated to produce the subsequent spikes shown in the figure at t > 320 ms. The charging and discharging of the capacitor, manifested through the voltage at node A, are shown in Figs S1 and S2 (Supplementary Information) for different spiking events.
During the timeframe when the neuron is firing, the net charge integration across the capacitor is essentially zero. This is because any input voltage pulse applied is being directly drained by the TSM device (it being turned on). This period emulates the post firing refractory period of a biological neuron1,8,13. Once the refractory period is over, the device reverts from the LRS state to its HRS and the capacitor ‘Co’ starts integrating again. The refractory period from the v-MoS2/graphene TSM is shown in Fig. 4d and it is further corroborated in terms of the voltage at Node A as shown in Fig. S3.
Another key characteristic of a biological neuron is that the frequency of spiking increases with higher strength of the input13. To emulate this behavior using the developed artificial neurons, a train of pulses with the same frequency 5 kHz (Ton = 100 µs) but two different amplitudes are applied to the v-MoS2/graphene neurons. On application of input pulses of 7.5 V to the circuit (Fig. 5a), a potential drop across Ro occurs, leading to a voltage of ~4 V at the node A and a single output voltage spike is observed. On the other hand, increasing the amplitude of the input pulses to 8.5 V (Fig. 5b), three spikes are recorded in a shorter time range. The spiking frequency increases for input with a higher amplitude as seen in Fig. 5. In case of input pulses with a lower voltage, the capacitor requires a higher number of pulses to trigger the output spike than in case of input pulses with a higher voltage. Hence, the input strength modulated frequency dependence characteristics can be emulated by the developed v-MoS2/graphene artificial neurons.
Stochastic switching behavior
We studied the DC characteristics of the TSM for over 40 cycles to shed light on the nature of the switching voltages. It is observed that the device retained the abrupt transition from the HRS to the LRS over this period as shown in Fig. 6a. The threshold voltage at which the device switches from the HRS to the LRS (V1) and from the LRS to the HRS (V2) are plotted over the 40 cycles shown in Fig. 6b. It is evident from Fig. 6c that the window between V1 and V2 is maintained over the cycling period. Also, it is observed that V1 and V2 are probabilistic in nature and follow a stochastic distribution. Figure 6d shows the cumulative distribution function for the switching probability of the v-MoS2/graphene TSM, which, in turn, produces the neuron spiking probability. Additionally, the stochastic switching behavior of the v-MoS2/graphene TSM originating from device level stochasticity makes these probabilistic spiking neurons viable for applications in the field of hardware security, such as Random Number Generators (RNGs)24,25.
Recent reports have shown that the switching mechanism in single-layer MoS2 can be attributed to the grain boundaries (GBs)14. The switching behavior of our v-MoS2/graphene devices can be attributed to the multiple grain boundaries in the polycrystalline films of v-MoS2. To further comprehend the switching mechanism in the v-MoS2/graphene devices, the DC measurements were carried out in vacuum. It is interesting to note that in the absence of oxygen, the fabricated devices do not show the volatile switching behavior (Fig. S4, supporting information) that was observed in the presence of oxygen. It can be further noted that the switching window disappears and the device does not reset to its HRS during the reverse voltage sweep. Hence, the migration of oxygen ions facilitated by the grain boundaries in the v-MoS2 is the probable reason the switching mechanism in the realized v-MoS2/graphene devices. The vacuum ambient removes the oxygen ions from the system completely.
In summary, we have demonstrated a novel 2D material-based TSM comprising v-MoS2 layers grown on a monolayer graphene template. The device mimics the characteristics of a biological neuron via volatile resistive threshold switching behavior. The developed IF artificial neuron exhibits the key behaviors of a biological neuron which include an all or nothing spiking, a threshold driven spiking of the action potential, a post-firing refractory period of a neuron and a strength modulated frequency response. These properties coupled with the stochastic threshold switching behavior mediated by oxygen ion migration along the vertical grains of MoS2 make these artificial neurons viable for applications in real time computing systems based on event spiking such as pattern recognition, neuromorphic vision sensors, and hardware security. While the current through the v-MoS2/graphene TSM is presently low (~1 μA) demanding high input voltages for the circuit operation, the v-MoS2 stack can be engineered in the future by modifying its thickness and growth conditions to allow larger currents to flow through the circuit. This will consequently reduce the voltage requirements of the circuit as well.
First, commercially purchased CVD-grown monolayer graphene was wet transferred over a Si/SiO2 (300 nm SiO2) substrate. The graphene was then patterned by photolithography and etched by oxygen plasma. The sample was again patterned and 10 nm thick Mo films were deposited on the etched graphene using an electron beam (e-beam) evaporation system (Temescal FC-2000). The Mo films were subsequently sulfurized to MoS2 in a low-pressure CVD furnace. 50 nm Ni contacts on both graphene and MoS2 were patterned, e-beam evaporated and lifted off.
The patterned Mo film on graphene/Si/SiO2 substrate were loaded in the center of a quartz tube CVD furnace with a ceramic boat having sulfur powder at the upstream of Mo sample. The furnace was pumped down to a base pressure of ≤1 mTorr and then purged with argon (Ar) gas. The furnace was heated up to a temperature of ∼650−700 °C with a constant flow of 100 SCCM (standard cubic centimeters per minute) Ar gas at a pressure of ∼100 mTorr. After a 30-min reaction time, the furnace was naturally cooled down and the substrate was taken out of the furnace. The change of color of the substrate from blue to dark green, indicates the sulfurization of Mo on the graphene.
Raman, AFM and TEM characterization
The Raman spectra were obtained using a confocal Raman system (WITEC Alpha 300RA) in ambient conditions with a 532 nm laser source for excitation. The laser was focused with a Zeiss 50× objective lens (numerical aperture of 0.7) with power ~5.7 mW and integration time 5 s. Each raman spectra were taken over 10 scans. The AFM topography was acquired on an Anasys NanoIR2 system in tapping mode using Anasys tapping mode AFM probes (Model No. PR-EX-T125-10). The TEM imaging was carried out using JEOL ARM-200F equipped with an aberration corrector which provides spatial resolution down to ~1 Å at an operating voltage of 200 kV.
The electrical measurements were carried at room temperature in Micromanipulator 6200 probe station using a Keysight B1500A semiconductor device analyzer along with WGFMUs for pulse I-V measurements. The vacuum measurements were carried out in a Janis cryo-probe station. A Tektronix DPO 2024B oscilloscope was used to measure the node voltage.
All data generated and analyzed during this study are either included in the published article itself (or available within the Supplementary Information files).
Jaiswal, A., Roy, S., Srinivasan, G. & Roy, K. Proposal for a Leaky-Integrate-Fire Spiking Neuron Based on Magnetoelectric Switching of Ferromagnets. IEEE Trans. Electron Devices 64, 1818–1824 (2017).
Tavanaei, A., Ghodrati, M., Kheradpisheh, S. R., Masquelier, T. & Maida, A. S. Deep Learning in Spiking Neural Networks. arXiv preprint arXiv:1804.08150 (2018).
Prezioso, M. et al. Training and operation of an integrated neuromorphic network based on metal-oxide memristors. Nature 521, 61 (2015).
Tian, H. et al. A novel artificial synapse with dual modes using bilayer graphene as the bottom electrode. Nanoscale 9, 9275–9283 (2017).
Seo, J.-S. et al. In Custom Integrated Circuits Conference (CICC), 2011 1–4 (IEEE, 2011).
Indiveri, G., Chicca, E. & Douglas, R. A VLSI array of low-power spiking neurons and bistable synapses with spike-timing dependent plasticity. IEEE Trans. Neural Netw. 17, 211–221 (2006).
Indiveri, G. et al. Neuromorphic silicon neuron circuits. Front. Neurosci. 5, 73 (2011).
Lin, J. et al. In International Electron Devices Meeting (IEDM), 2016 34.35. 31-34.35. 34 (IEEE, 2011).
Jerry, M. et al. In 74th Annual Device Research Conference (DRC), 2016 1–2 (IEEE).
Pickett, M. D., Medeiros-Ribeiro, G. & Williams, R. S. A scalable neuristor built with Mott memristors. Nat. Mater. 12, 114 (2013).
Tuma, T., Pantazi, A., Le Gallo, M., Sebastian, A. & Eleftheriou, E. Stochastic phase-change neurons. Nat. Nanotechnol. 11, 693 (2016).
Chen, P.-Y., Seo, J.-S., Cao, Y. & Yu, S. In Proceedings of the 35th International Conference on Computer-Aided Design. 15 (ACM).
Zhang, X. et al. An Artificial Neuron Based on a Threshold Switching Memristor. IEEE Electron Device Lett. 39, 308–311 (2018).
Sangwan, V. K. et al. Gate-tunable memristive phenomena mediated by grain boundaries in single-layer MoS2. Nat. nanotechnol. 10, 403 (2015).
Bean, B. P. The action potential in mammalian central neurons. Nat. Rev. Neurosci. 8, 451 (2007).
Dayan, P. & Abbott, L. F. Theoretical Neuroscience (Cambridge, MA: MIT Press, 2001).
Vreeken, J. Spiking Neural Network, An Introduction (Utrecht University: Information and Computing Sciences, 2003).
Izhikevich, E. M. Which model to use for cortical spiking neurons? IEEE Trans. Neural Netw. 15, 1063–1070 (2004).
Chan, J. et al. Reducing extrinsic performance-limiting factors in graphene grown by chemical vapor deposition. ACS Nano 6, 3224–3229 (2012).
Li, H. et al. From bulk to monolayer MoS2: evolution of Raman scattering. Adv. Funct. Mater. 22, 1385–1390 (2012).
Childres, I., Jauregui, L. A., Park, W., Cao, H. & Chen, Y. P. Raman spectroscopy of graphene and related materials. New Dev. Photon Mater. Res. 1 (2013).
Joiner, C. A. et al. Graphene-Molybdenum Disulfide-Graphene Tunneling Junctions with Large-Area Synthesized Materials. ACS Appl. Mater. Interfaces. 8, 8702–8709 (2016).
Choudhary, N. et al. Strain‐Driven and Layer‐Number‐Dependent Crossover of Growth Mode in van der Waals Heterostructures: 2D/2D Layer‐By‐Layer Horizontal Epitaxy to 2D/3D Vertical Reorientation. Adv. Mater. Interfaces, 1800382 (2018).
Jerry, M., Parihar, A., Raychowdhury, A. & Datta, S. In 75th Annual Device Research Conference (DRC), 2017 1–2 (IEEE).
Jerry, M., Parihar, A., Grisafe, B., Raychowdhury, A. & Datta, S. In 2017 Symposium on VLSI Circuits. T186-T187 (IEEE).
This work was supported by UCF startup fund for T.R. N.C. acknowledges partial support from the Preeminent Postdoctoral Program (P3) at the University of Central Florida.
The authors declare no competing interests.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
About this article
Cite this article
Kalita, H., Krishnaprasad, A., Choudhary, N. et al. Artificial Neuron using Vertical MoS2/Graphene Threshold Switching Memristors. Sci Rep 9, 53 (2019). https://doi.org/10.1038/s41598-018-35828-z
This article is cited by
npj 2D Materials and Applications (2023)
Atomically resolved electronic properties in single layer graphene on α-Al2O3 (0001) by chemical vapor deposition
Scientific Reports (2022)
Nano Research (2021)